Mechanical alloying of Ni<Subscript>80</Subscript>Ta<Subscript>20</Subscript> and Ni<Subscript>80</Subscript>Nb<Subscript>20</Subscript>. Crystallization of the amorphous phase

The sequence and crystallization kinetics of the amorphous phase have been analyzed by differential scanning calorimetry and X-ray diffraction for mechanochemically activated Ni₈₀Ta₂₀ and Ni₈₀Nb₂₀ samples. The formation of equilibrium products from the amorphous phase occurs through the formation of metastable products of the A3 type. The kinetic parameters (activation energy and reaction order) and thermodynamic characteristics of this process are determined. Crystallization of the amorphous phase for the Ni₈₀Ta₂₀ and Ni₈₀Nb₂₀ systems occurs due to the growth of existing nuclei through the polymorphic and eutectic mechanisms, respectively. The thermal effects of the synthesis of equilibrium products from a mechanochemically activated mixture of components are identified.     

Formation and structure of nanocrystals in bulk Zr<Subscript>50</Subscript>Ti<Subscript>16</Subscript>Cu<Subscript>15</Subscript>Ni<Subscript>19</Subscript> metallic glass

The possible formation of a nanocrystalline structure in controlled crystallization of a bulk Zr₅₀Ti₁₆Cu₁₅Ni₁₉ amorphous alloy has been studied using differential scanning calorimetry, transmission and high-resolution electron microscopy, and x-ray diffraction. It was established that crystallization of the alloy at temperatures above the glass formation point occurs in two stages and brings about the formation of a nanocrystalline structure consisting of three phases. Local spectral x-ray analysis identified the composition and structure of the phases formed.     

Structural transformations in the Al<Subscript>85</Subscript>Ni<Subscript>6.1</Subscript>Co<Subscript>2</Subscript>Gd<Subscript>6</Subscript>Si<Subscript>0.9</Subscript> amorphous alloy during multiple rolling

The effect of multiple rolling at room temperature on the structure and crystallization of the Al₈₅Ni_6.1Co₂Gd₆Si_0.9 amorphous alloy has been studied using transmission electron microscopy, differential scanning calorimetry, and X-ray diffraction. The total plastic strain is 33%. It has been shown that the deformation results in the formation of aluminum nanocrystals with the average size that does not exceed 10–15 nm. The nanocrystals are formed in regions of localization of plastic deformation. The deformation decreases the thermal effect of nanocrystallization (∼15%) as compared to the heat release at the first stage of crystallization of the unstrained sample. The morphology, structure, and distribution of precipitates have been investigated. Possible mechanisms of the formation of nanocrystals during the deformation have been discussed.     

The influence of crystalline grain size on the thermal stability of the Er<Subscript>0.45</Subscript>Ho<Subscript>0.55</Subscript>Fe<Subscript>2</Subscript> compound

The phase composition and the temperature dependence of the magnetization of the Er_0.45Ho_0.55Fe₂ compound in coarse-grained, microcrystalline, and submicrocrystalline states are investigated experimentally. It is found that, upon heating under vacuum, the Er_0.45Ho_0.55Fe₂ microcrystalline powder with a crystalline grain size of ∼1 μm undergoes decomposition into pure iron and rare-earth (erbium and holmium) oxides and nitrides at a temperature of 500 K. The changes observed in the phase composition of the microcrystalline powder due to annealing are confirmed by x-ray diffraction analysis. Heating of the Er_0.45Ho_0.55Fe₂ submicrocrystalline sample leads to a partial change in the phase composition. The phase composition of a large crystal (∼1 mm in size) remains unchanged upon heating to 1080 K. It is shown that the thermal stability of the Er_0.45Ho_0.55Fe₂ compound depends on the crystalline grain size. __________ Translated from Fizika Tverdogo Tela, Vol. 44, No. 6, 2002, pp. 1060–1063. Original Russian Text Copyright ? 2002 by Mulyukov, Sharipov, Korznikova.     

Effect of heat treatment on the structure and elastic properties of a bulk Pd<Subscript>40</Subscript>Cu<Subscript>30</Subscript>Ni<Subscript>10</Subscript>P<Subscript>20</Subscript> metallic glass

The effect of heat treatment over the range from room temperature to 500°C on the elastic properties of a bulk amorphous Pd₄₀Cu₃₀Ni₁₀P₂₀ alloy was studied. It is shown that the increase in the shear modulus under crystallization of the alloy is two-staged and that the most significant increase in the modulus occurs at the second stage. The obtained results are compared to the x-ray structural data. It is also found that the density characteristics of the as-cast material change very slightly during the transformation from the amorphous to the crystal state, with the density decreasing slightly due to crystallization.     

Laser performance of holmium-doped Lu<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript> and (Lu,Y)<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript> crystals pumped by Tm:fiber laser

Optical properties of Ho³⁺-doped Lu₃Al₅O₁₂ and (Lu,Y)₃Al₅O₁₂ crystals were investigated and compared. Substitution of Y for Lu in the host garnet Lu₃Al₅O₁₂ results in broad absorption and emission spectra, and improvements in the laser behavior of Ho³⁺. Pumped by Tm:fiber laser, a maximum output power of 5.02 and 5.73 W of Ho-doped Lu₃Al₅O₁₂ and (Lu,Y)₃Al₅O₁₂ have been obtained, respectively. The center lasing wavelength are 2124.5 and 2123.0 nm for Lu₃Al₅O₁₂ and (Lu,Y)₃Al₅O₁₂, respectively.     

Field-induced magnetic transition in a mixed rare-earth aluminum garnet Er<Subscript>2</Subscript>HoAl<Subscript>5</Subscript>O<Subscript>12</Subscript>

The temperature dependence of the ac magnetic susceptibility of a single-crystal mixed rare-earth garnet Er₂HoAl₅O₁₂ has been investigated within the range from 1.8 to 300 K in a zero constant field and in applied bias fields of up to 9 T. In the absence of a constant magnetic field the magnetic susceptibility followed the Curie–Weiss law. The application of a constant magnetic field caused a magnetic phase transition, the temperature of which increased with increasing magnetic field. The temperature of the maximum of the ac magnetic susceptibility, which is a characteristic of the phase transition, did not show a noticeable dependence on the frequency of the alternating magnetic field.     

Vibrational and electronic properties of the amorphous systems Ni<Subscript>44</Subscript>Nb<Subscript>56</Subscript>, Ni<Subscript>62</Subscript>Nb<Subscript>38</Subscript>, and Cu<Subscript>33</Subscript>Zr<Subscript>67</Subscript> as derived from specific heat measurements

The specific heats of the amorphous systems Ni₄₄Nb₅₆, Ni₆₂Nb₃₈, and Cu₃₃Zr₆₇ were studied in the temperature range 3–273 K. The data obtained allow one to isolate the contribution due to atomic vibrations from the experimentally measured specific heat, to determine the density of electronic states at the Fermi level and the temperature dependence of the characteristic Debye parameter Θ over a broad temperature range, and to calculate a few frequency moments that characterize the vibrational spectrum. The information derived on the average characteristics of vibrational spectra is in good agreement with earlier data on inelastic neutron scattering. In transferring from Ni₄₄Nb₅₆ to Ni₆₂Nb₃₈, the density of electronic states at the Fermi level decreases and the characteristic vibrational frequencies increase. The density of electronic states at the Fermi level for Cu₃₃Zr₆₇ is close to that for Ni₆₂Nb₃₈. The characteristic frequencies of the vibrational spectrum of the Cu₃₃Zr₆₇ system are substantially lower (by 30%) than those of the Ni₄₄Nb₅₆ and Ni₆₂Nb₃₈ systems.     

Magnetic and Magnetodielectric Properties of Ho<Subscript>0.5</Subscript>Nd<Subscript>0.5</Subscript>Fe<Subscript>3</Subscript>(BO<Subscript>3</Subscript>)<Subscript>4</Subscript>

The magnetic and magnetodielectric properties of Ho_0.5Nd_0.5Fe₃(BO₃)₄ ferroborate with the competing Ho–Fe and Nd–Fe exchange couplings have been experimentally and theoretically investigated. Step anomalies in the magnetization curves at the spin-reorientation transition induced by the magnetic field B ║ c have been found. The spontaneous spin-reorientation transition temperature T_SR ≈ 8 K has been refined. The measured magnetic properties and observed features are interpreted using a single theoretical approach based on the molecular field approximation and calculations within the crystal field model of the rare-earth ion. Interpretation of the experimental data includes determination of the crystal field parameters for Ho³⁺ and Nd³⁺ ions in Ho_0.5Nd_0.5Fe₃(BO₃)₄ and parameters of the Ho–Fe and Nd–Fe exchange couplings.     

Effect of thermal annealing on the structure of ZnSe/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocomposite films

The ZnSe/Al₂O₃ nanocomposite films synthesized by laser evaporation followed by heat treatment are studied. X-ray diffraction and electron-microscopic investigations of the as-deposited films demonstrate the presence of ZnSe crystallites in an Al₂O₃ amorphous matrix. Annealing changes the structures of ZnSe and Al₂O₃, increases the ZnSe crystallite size, and causes the appearance of the ZnSeO₄ phase. The presence of aluminum oxide layers decreases the phase transformation temperature of zinc selenide.     

Magnetic properties of LiNi<Subscript>0.5</Subscript>Mn<Subscript>0.47</Subscript>Al<Subscript>0.03</Subscript>O<Subscript>2</Subscript> as positive electrode for Li-ion batteries

The layered LiNi_0.5Mn_0.47Al_0.03O₂ was synthesized by wet chemical method and characterized by X-ray diffraction and analysis of magnetic measurements. The powders adopted the α-NaFeO₂ structure. This substitution of Al for Mn promotes the formation of Li(Ni_0.47²⁺Ni_0.03³⁺Mn_0.47⁴⁺Al_0.03³⁺)O₂ structures and induces an increase in the average oxidation state of Ni, thereby leading to the shrinkage of the lattice unit cell. The concentration of antisite defects in which Ni²⁺ occupies the (3a) Li lattice sites in the Wyckoff notation has been estimated from the ferromagnetic Ni²⁺(3a)–Mn⁴⁺(3b) pairing observed below 140 K. The substitution of 3% Al for Mn reduces the amount of antisite defects from 7% to 6.4–6.5%. The analysis of the magnetic properties in the paramagnetic phase in the framework of the Curie–Weiss law agrees well with the combination of Ni²⁺ (S = 1), Ni³⁺ (S = 1/2) and Mn⁴⁺ (S = 3/2) spin-only values. Delithiation has been made by the use of K₂S₂O₈. According to this process, known to be softer than the electrochemical one, the nickel ions in the (3b) sites are converted into Ni⁴⁺ in the high spin configuration, while Ni²⁺(3a)–Mn⁴⁺(3b) ferromagnetic pairs remain, as the Li⁺(3b) ions linked to the Ni²⁺(3a) ions in the antisite defects are not removed. The results show that the antisite defect is surrounded by Mn⁴⁺ ions, implying the nonuniform distribution of the cations in agreement with previous NMR and neutron experiments.     

High-resolution spectroscopy of HoFe<Subscript>3</Subscript>(BO<Subscript>3</Subscript>)<Subscript>4</Subscript> crystal: a study of phase transitions

The transmission spectra of HoFe₃(BO₃) multiferroic single crystals are studied by optical Fourier-transform spectroscopy at temperatures of 1.7–423 K in polarized light in the spectral range 500–10 000 cm^–1 with a resolution up to 0.1 cm^–1. A new first-order structural phase transition close to the second-order transition is recorded at T_c = 360 K by the appearance of a new phonon mode at 976 cm^–1. The reasons for considerable differences in T_c for different samples of holmium ferroborate are discussed. By temperature variations in the spectra of the f–f transitions in the Ho³⁺ ion, we studied two magnetic phase transitions, namely, magnetic ordering into an easy-plane structure as a second-order phase transition at T_N = 39 K and spin reorientation from the ab plane to the c axis as a first-order phase transition at T_SR = 4.7 ± 0.2 K. It is shown that erbium impurity in a concentration of 1 at % decreases the spin-reorientation transition temperature to T_SR = 4.0 K.     

Atomic and magnetic structures of Fe<Subscript>70</Subscript>Al<Subscript>5</Subscript>B<Subscript>25</Subscript> amorphous alloys

The short-range order around boron, aluminum, and iron atoms in Fe₇₅B₂₅ and Fe₇₀Al₅B₂₅ amorphous alloys has been studied by ¹¹B and ²⁷Al nuclear magnetic resonance at 4.2 K and ⁵⁷Fe Mössbauer spectroscopy at 87 and 295 K. The average magnetic moment of iron atoms μ(Fe) in these alloys has been measured by a vibrating sample magnetometer. It has been revealed that the substitution of aluminum atoms for iron atoms does not disturb μ(Fe) in the Fe₇₀Al₅B₂₅ alloy, gives rise to an additional contribution to the ¹¹B NMR spectrum in the low-frequency range, and shifts maxima of the distribution of hyperfine fields at the ⁵⁷Fe nuclei. In the Fe₇₀Al₅B₂₅ amorphous alloy, the aluminum atoms substitute for iron atoms in the nearest coordination shells of boron and iron atoms. This alloy consists of nanoclusters in which boron and iron atoms have a short-range order of the tetragonal Fe₃B phase type.     

Phase transition in Pd<Subscript>40</Subscript>Ni<Subscript>10</Subscript>Cu<Subscript>30</Subscript>P<Subscript>20</Subscript> bulk metallic glass under HP &; HT

The phase transitions in Pd₄₀Ni₁₀Cu₃₀P₂₀ bulk metallic glass (BMG) have been studied under high pressure and high temperature (HP & HT) by X-ray diffaction measurements with synchrotron radiation source. We found that the BMG underwent a phase transitions of amorphous-crystalline-amorphous at 10 GPa upon heating. The parallel experiments were carried out at 7 GPa, while we did not observe the amorphous-crystalline-amorphous transitions by increasing temperature. Quenching the melted BMG at 7 GPa, it was found that the phase crystallized from the melt differed from the primary phase crystallized from the starting amorphous solid upon heating suggesting there existed a distinct mechanism in two cases.     

Magnetic and magnetoelectric properties of the Tb<Subscript>0.75</Subscript>Ho<Subscript>0.25</Subscript>Fe<Subscript>3</Subscript>(BO<Subscript>3</Subscript>)<Subscript>4</Subscript> ferroborate

Single crystals of the Tb_0.75Ho_0.25Fe₃(BO₃)₄ ferroborate have been grown by the group method from a solution–melt based on bismuth trimolybdate. The magnetic and magnetoelectric properties of the ferroborate single crystals have been investigated in the temperature range from 4.2 to 300 K and in magnetic fields up to 9 T. Magnetically, this material is an antiferromagnet with the Néel temperature T _N = 38.8 K and easy-axis anisotropy. The magnitude of the magnetoelectric polarization has been found to be more than 1.5–2.0 times greater than the sum of the polarizations induced by the magnetic field for the ferroborates TbFe₃(BO₃)₄ and HoFe₃(BO₃)₄ taken in the corresponding shares.     

Nanocrystallization of an amorphous Fe<Subscript>80</Subscript>B<Subscript>20</Subscript> alloy during severe plastic deformation

The structural evolution of an amorphous Fe₈₀B₂₀ alloy subjected to severe plastic deformation at room temperature or at 200°C was studied. Deformation leads to the formation of α-Fe nanocrystals in an amorphous phase. After room-temperature deformation, nanocrystals are localized in shear bands. After deformation at 200°C, the nanocrystal distribution over the alloy is more uniform. Possible causes of the crystallization of the amorphous phase during severe plastic deformation are discussed.     

On the Coexistence of Chemically Similar Stable and Metastable Phases in the BeO–MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> System

The joint crystallization of the stable phase (a number of solid solutions of chromium-containing beryllian indialite) and metastable phases (crystalline modifications) of the compound with β-quartz structure (Si_0.64Al_0.28Mg_0.21Be_0.09)^IVO₂ ~ Mg_1.89Be_0.81Al_2.52Si_5.76O₁₈ admixed with Cr₂O₃ phases of khmaralite Mg_1.21Cr_0.01Be_0.46Al_1.78Si_3.38O₂₀ and spinel {(Mg_0.95Be_0.045Si_0.005)^IV(Al_1.31Cr_0.67Mg_0.02)^VI}O₄ is performed using melted chromium–beryllian indialite preliminarily obtained by solid-phase synthesis as a precursor. Simultaneously, the residual X-ray amorphous melt of composition Mg_1.83Cr_0.01Be_1.04Al_2.64Si_5.57O₁₈ is hardened. Thus, a reconstructive transition from the beryllian indialite melt to a phase with the β-quartz structure is implemented, and the chemical similarity of these compounds is demonstrated. The rate of change in the crystallization isotherm of 2°С/h and increased heat outflow through the highly heat-conducting walls of the Pt–Rh crucible (taper) contribute to this process.     

Effect of site disorder on the magnetic properties of weak itinerant ferromagnet Ni<Subscript>75</Subscript>Al<Subscript>25</Subscript>

Detailed study of Ni₇₅Al₂₅ samples with varying degree of site disorder reveals that site disorder promotes magnetic excitations such as spin waves and local spin-density fluctuations and thereby reduces both spin-wave stiffness and Curie temperature. Irreversibility lines in theT-H phase diagram of the weak itinerant ferromagnet Ni₇₅Al₂₅ have been determined for the first time and the effect of site disorder on them has been ascertained Article presented at the International Symposium on Advances in Superconductivity and Magnetism: Materials, Mechanisms and Devices, ASMM2D-2001, 25–28 September 2001, Mangalore, India.     

The transport and thermal properties of glassy LiPO<Subscript>3</Subscript>/crystalline Al<Subscript>2</Subscript>O<Subscript>3</Subscript> (ZrO<Subscript>2</Subscript>) composite electrolytes

Glassy LiPO₃/crystalline Al₂O₃ and glassy LiPO₃/crystalline ZrO₂ (0–12.5 vol.% of oxide fillers) composite solid electrolytes have been prepared by glass matrix softening. Their thermal and transport properties have been investigated by differential scanning calorimetry (DSC) and impedance spectroscopy methods. The addition of ZrO₂ leads to a decrease in the crystallization temperature of LiPO₃ glass. It was found that the conductivity behavior depends on the nature of the dispersed addition. In the case of the Al₂O₃ addition, the increase in the electrical conductivity is observed. The ionic conductivity of the LiPO₃/10% Al₂O₃ composite reaches 5.8 × 10^?8 S/cm at room temperature. In contrast, the conductivity in the LiPO₃/ZrO₂ composite system decreases.