Thermal conductivity of Na<Subscript>2</Subscript>W<Subscript>2</Subscript>O<Subscript>7</Subscript> crystal

The thermal conductivity of Na₂W₂O₇ single crystal has been studied along the main crystallographic directions at temperatures of 50–573 K. A low thermal conductivity is found to correlate with a significant difference in the cation weight.     

Synthesis,characterization, and thermal stability of SiO<Subscript>2</Subscript>/TiO<Subscript>2</Subscript>/CR-Ag multilayered nanostructures

The controllable synthesis and characterization of novel thermally stable silver-based particles are described. The experimental approach involves the design of thermally stable nanostructures by the deposition of an interfacial thick, active titania layer between the primary substrate (SiO₂ particles) and the metal nanoparticles (Ag NPs), as well as the doping of Ag nanoparticles with an organic molecule (Congo Red, CR). The nanostructured particles were composed of a 330-nm silica core capped by a granular titania layer (10 to 13 nm in thickness), along with monodisperse 5 to 30 nm CR-Ag NPs deposited on top. The titania-coated support (SiO₂/TiO₂ particles) was shown to be chemically and thermally stable and promoted the nucleation and anchoring of CR-Ag NPs, which prevented the sintering of CR-Ag NPs when the structure was exposed to high temperatures. The thermal stability of the silver composites was examined by scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM). Larger than 10 nm CR-Ag NPs were thermally stable up to 300 °C. Such temperature was high enough to destabilize the CR-Ag NPs due to the melting point of the CR. On the other hand, smaller than 10 nm Ag NPs were stable at temperatures up to 500 °C because of the strong metal-metal oxide binding energy. Energy dispersion X-ray spectroscopy (EDS) was carried out to qualitatively analyze the chemical stability of the structure at different temperatures which confirmed the stability of the structure and the existence of silver NPs at temperatures up to 500 °C.     

Casimir friction force between a SiO<Subscript>2</Subscript> probe and a graphene-coated SiO<Subscript>2</Subscript> substrate

The possibility of mechanical detection of Casimir friction with the use of a noncontact atomic force microscope is discussed. A SiO₂ probe tip located above a graphene-coated SiO₂ substrate is subjected to the frictional force caused by a fluctuating electromagnetic field produced by a current in graphene. This frictional force will create the bend of a cantilever, which can be measured by a modern noncontact atomic force microscope. Both the quantum and thermal contributions to the Casimir frictional force can be measured using this experimental setup. This result can also be used to mechanically detect Casimir friction in micro- and nanoelectromechanical systems.     

Laser-induced thermal effects on Si/SiO<Subscript>2</Subscript> free-standing superlattices

The thermal effects produced by continuous-wave laser radiation on free-standing Si/SiO₂ superlattices are studied. We compare two samples with different SiO₂ layer thicknesses (2 and 6 nm) and the same Si layer thickness (2 nm). The as-prepared free-standing superlattices contain some amount of Si nanocrystals (Si-nc). Intense laser irradiation at 488 nm of the as-prepared samples enhances the Raman scattering of Si-nc by two orders of magnitude. This laser-induced crystallization originates from melting of Si nanostructures in silica, which makes Si-nc better ordered and better isolated from the oxide surrounding. Continuous-wave laser control of Si-nc stress was achieved in these samples. In the proposed model, intense laser radiation melts Si-nc, and Si crystallization upon cooling down from the liquid phase in a silica matrix leads to compressive stress. The Si-nc stress can be tuned in the ∼3 GPa range using laser annealing below the Si melting temperature. The high laser-induced temperatures were verified with Raman spectroscopy. The laser-induced heat leads to a strongly nonlinear rise of light emission. The light emission is also observed in the anti-Stokes region, and its temperature dependence is practically the same for the two studied samples. The laser-induced temperature is essentially controlled by the absorbed laser power. PACS 78.55.-m; 78.20.-e; 68.55.-a; 78.30.-j     

Friction and wear properties of ZrO<Subscript>2</Subscript>/SiO<Subscript>2</Subscript> composite nanoparticles

In this article, the lubrication properties of ZrO₂/SiO₂ composite nanoparticles modified with aluminum zirconium coupling agent as additives in lubricating oil under variable applied load and concentration fraction were reported. It was demonstrated that the modified nanoparticles as additives in lubrication can effectively improve the lubricating properties. Under an optimized concentration of 0.1 wt%, the average friction coefficient was reduced by 16.24%. This was because the nanoparticles go into the friction zone with the flow of lubricant, and then the sliding friction changed to rolling friction with a result of the reduction of the friction coefficient.     

Preparation and investigation of composite SiO<Subscript>2</Subscript>-TiO<Subscript>2</Subscript> films

SiO₂-TiO₂ films [Si:Ti = 1:(0.06–2.3)] are obtained by the sol-gel method. The structural and photoluminescent properties of the films and powders heat-treated at different temperatures are studied. It is shown that after 700°C the composite consists of TiO₂ crystallites that are structurally similar to anatase and distributed in an amorphous SiO₂ matrix. The photoluminescence spectra have maxima at 450–500 nm. The photoluminescence intensity depends on the treatment temperature and TiO₂ content. __________ Translated from Zhurnal Prikladnoi Spektroskopii Vol. 74, No. 3, pp. 357–361, May–June, 2007.     

RETRACTED ARTICLE: Refractive-index tailoring and morphological evolutions in Gd<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> and ZrO<Subscript>2</Subscript>–SiO<Subscript>2</Subscript> composite thin films

Refractive-index tailoring and morphological evolutions in two different thin film composite systems of gadolinia–silica (Gd₂O₃:SiO₂) and zirconia–silica (ZrO₂:SiO₂) deposited through reactive electron-beam codeposition processes are discussed in this research paper. For Gd₂O₃:SiO₂ the refractive-index tuning has been achieved from 1.45 to 2.18, whereas in the case of ZrO₂:SiO₂ the achieved tunable range is from 1.45 to 2.45 in the ultraviolet region. Under certain compositional mixings with lower silica fractions both the systems demonstrated relative microstructural and morphological densifications. Such evolutions were very successfully derived through phase-modulated ellipsometry and atomic force microscopy. The composition-dependent refractive-index tailoring and microstructural densifications have been investigated by adopting Tauc–Lorentz and single-effective-oscillator models. The morphological correlation functions have also very aptly supported such evolutions in these composite films. These experimental results indicate their favourable properties and applicability down to the extreme ultraviolet wavelength region of the electromagnetic spectrum. PACS 42.79.Wc; 78.66.-w; 78.20.Ci; 61.16.Ch; 42.70.-a;68.55.-a; 68.35.Bs; 81.15.Ef     

Mössbauer studies of magnetic Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>/SiO<Subscript>2</Subscript> nanocomposites

A large variety of glass and glass ceramics may be obtained by sol-gel process from hydrolysis of tetraethoxysilane. The transformation involves hydrolysis and polycondensation reactions leading to the growth of clusters that eventually collide together to form a gel. The structure and properties of the final product have been found to be strongly dependent on the initial conditions of preparation. Silica nanocomposites based on Fe₂O₃/SiO₂ were prepared with the help of ultrasonic activation and subsequent annealing in nitrogen atmosphere or air with concentrations of iron oxide of about 20 to 30wt.%.     

Electrical conductivity and dielectric properties of SiO<Subscript>2</Subscript> nanoparticles dispersed in conducting polymer matrix

Electrical and dielectric properties of conducting polypyrrole–wide band gap silica (PPY–SiO₂) nanocomposites have been investigated as a function of temperature and frequency for different concentrations of polypyrrole. The average grain size of the nanocomposites is in the range of 40–80 nm. Impedance spectra reveal two distorted semicircles corresponding to grain and grain boundary effects. The magnitude of conductivity and its temperature variation are significantly different from polypyrrole and silica. A very large dielectric constant of about 4800 at 30 kHz and at room temperature has been observed for the highest concentration of silica. Inhomogeneous behavior of nanocomposites gives rise to high dielectric constant.     

Synthesis and nanostructural investigation of TiO<Subscript>2</Subscript> nanorods doped by SiO<Subscript>2</Subscript>

TiO₂ Nano rods can be used as dye-sensitized solar cells, various sensors and photocatalysts. These nanorods are synthesized by a hydrothermal corrosion process in NaOH solution at 200°C using TiO₂ powder as the source material. In the present work, the synthesis of TiO₂ nanorods in anatase, rutile and Ti₇O₁₃ phases and synthesis of TiO₂ nanorods by incorporating SiO₂ dopant, using the sol–gel method and alkaline corrosion are reported. The morphologies and crystal structures of the TiO₂ nanorods are characterized using field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD) study. The obtained results show not only an aggregation structure at high calcination temperatures with spherical particles but also Ti–O–Si bonds having four-fold coordination with oxygen in SiO^4 −.     

Fabrication and structural characterization of Mg<Subscript>2</Subscript>SiO<Subscript>4</Subscript> nanowires

This article demonstrates the first reported successful synthesis of Mg₂SiO₄ nanowires. We have thermally heated Au-coated Si substrates, using a quartz tube with its inner surface pre-coated with MgO nanostructures. We have characterized the sample morphologies by using scanning electron microscopy and transmission electron microscopy (TEM). X-ray diffraction analysis and high-resolution TEM observation coincidentally revealed that the nanowires were crystalline with an orthorhombic Mg₂SiO₄ structure. We have discussed the possible growth mechanism of Mg₂SiO₄ nanowires. PACS 81.07.-b; 81.05.Zx; 61.10.Nz; 68.37.Hk; 68.37.Lp     

Facile growth of monolayer MoS<Subscript>2</Subscript> film areas on SiO<Subscript>2</Subscript>

Areas of single-layer MoS₂ film can be prepared in a tube furnace without the need for temperature control. The films were characterized by means of Raman spectroscopy, photoluminescence, low-energy electron diffraction and microscopy, and X-ray photoelectron spectroscopy and mapping. Transport measurements show n-doped material with a mobility of 0.26 cm² V^-1 s^-1.     

A computer study of the Raman spectra of the (GaN)<Subscript>129</Subscript>, (SiO<Subscript>2</Subscript>)<Subscript>86</Subscript>, and (GaN)<Subscript>54</Subscript>(SiO<Subscript>2</Subscript>)<Subscript>50</Subscript> nanoparticles

The Raman spectra of the (GaN)₁₂₉, (SiO₂)₈₆, and (GaN)₅₄(SiO₂)₅₀ nanoparticles were calculated using the molecular dynamics method. The spectrum of (SiO₂)₈₆ had three broad bands only, whereas the Raman spectrum of (GaN)₁₂₉ contained a large number of overlapping bands. The form of the Raman spectrum of (GaN)₅₄(SiO₂)₅₀ was determined by the arrangement of the GaN and SiO₂ components in it. The nanoparticle with a GaN nucleus had a continuous fairly smooth spectrum over the frequency range 0 ≤ ω ≤ 600 cm⁻¹, whereas the spectrum of the nanoparticle with a SiO₂ nucleus contained well-defined bands caused by vibrations of groups of atoms of different kinds and atoms of the same kind.     

Ferroelectrical properties of SiO<Subscript>2</Subscript>-TGS nanocomposite

Dielectric properties of the composites based on nanodisperse silica hydrosol and ferroelectric triglycinesulfate (TGS) are investigated. The studies allow us to expect the presence of the ferroelectric state in the composites.     

Coaxial ZnO/SiO<Subscript>2</Subscript> nanocables fabricated by thermal evaporation/oxidation

ZnO/SiO₂ coaxial nanocables have been synthesized on silicon substrates by simply evaporating zinc powder under an argon and argon/oxygen mixed atmosphere sequentially. The diameters of these nanocables vary from 50 to 100 nm and the lengths up to several millimeters. Electron microscopy and chemical composition investigations reveal that the nanocable consists of a crystalline ZnO core surrounded by an amorphous silica sheath. The electron diffraction pattern proves that the long-axis direction of ZnO cores grows along the [0001] direction. Silica nanotubes with wall structures have been obtained by the selective dissolution of the cores with hydrochloric acid. PACS 81.10.Bk; 81.05.Hd     

The enhanced catalytic degradation of SiO<Subscript>2</Subscript>/Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>/C@TiO<Subscript>2</Subscript> photo-Fenton system on p-nitrophenol

Heterogeneous photo-Fenton SiO₂/Fe₃O₄/C@TiO₂ (SFCT) catalyst with a core-multishell structure and a diameter of about 550 nm was successfully prepared and was characterized by scanning electron microscopy (SEM), TEM, XRD, Raman, and Fourier transform infrared (FT-IR). The results illustrated that anatase TiO₂ coexisted with rutile TiO₂, in which the anatase phase was the main crystal phase. In addition, the catalytic activity of SFCT catalyst had been evaluated in the catalytic degradation on p-nitrophenol (PNP). The influence factors on the PNP degradation, including SFCT component ratio (m _SFC/ m _TiO2), H₂O₂ dosage, solution pH, and PNP concentration, had been investigated. And the contrast experiments about the photo-Fenton catalytic mechanism revealed that the SFCT-2 catalyst possessed a superior activity in the neutral environment due to the optimal activity matching between Fe₃O₄ and TiO₂, and it exhibited the stable catalytic performance after five successive recycles. Therefore, the SFCT-2 catalyst had a promising application for the photo-Fenton degradation of organic contaminant.