A potential reddish orange emitting phosphor Ca2BO3Cl:Eu for white light-emitting diodes

A series of phosphors Ca₂BO₃Cl:Eu³⁺ were synthesized by using a high-temperature solid-state reaction technique, and their UV–vis luminescence properties were investigated. The f–f transitions of Eu³⁺ in the host lattice were assigned and discussed. The excitation and emission spectra indicate that this phosphor can be effectively excited by ultraviolet (394 nm), and exhibit reddish orange emission corresponding to the ⁵D₀→⁷F_J (J=0, 1, 2) transitions of Eu³⁺. The influence of the doping concentration and charge compensators on the relative emission intensity of Eu³⁺ was investigated, and the optimum doping concentration is 0.04. The critical distance R_c was estimated to be 17.1 Å in terms of the concentration quenching data. The present study suggests that Ca₂BO₃Cl:Eu³⁺ can be a potential candidate as an UV-convertible phosphor for white light-emitting diodes (LEDs).     

Synthesis and luminescence investigation of RE (Eu, Tb and Ce)-doped lithium silicate (Li2SiO3)

Synthesis and photoluminescence (PL) investigations of lithium metasilicate doped with Eu³⁺, Tb³⁺ and Ce³⁺ were carried out. PL spectra of Eu-doped sample showed peaks corresponding to the ⁵D₀→⁷F_j (j=1, 2, 3 and 4) transitions under ultraviolet excitation. Strong red emission coming from the hypersensitive ⁵D₀→⁷F₂ transition of Eu³⁺ ion suggested the presence of the dopant ion in structurally disordered environment. Tb³⁺-doped silicate sample showed blue-green emission corresponding to the ⁵D₄→⁷F_j (j=6, 5 and 4) transitions. Ce-doped sample under excitation from UV, showed a broad emission band in the region 350-370 nm with shoulders around 410 nm. The fluorescence lifetimes of Eu³⁺ and Tb³⁺ ions were found out to be 790 and 600 μs, respectively. For Ce³⁺, the lifetime was of the order of 45 ns. PL spectra of the europium- and terbium-doped samples were compared with commercial red (Y₂O₃:Eu³⁺) and green (LaPO₄:Tb³⁺) phosphors, respectively. It was found that the emission from the doped silicate sample was 37% of the commercial phosphor in case of the Tb-doped sample and 8% of the commercial phosphor in case of the Eu-doped sample.     

Synthesis and luminescent properties of europium-activated Ca2SnO4 phosphors by sol-gel method

In this paper, the Ca₂SnO₄:Eu³⁺ phosphor was prepared by low-temperature sol-gel method. The influence of calcined temperature and time on structure of Ca₂SnO₄:Eu³⁺ was investigated by using X-ray powder diffraction (XRD). The experimental results show that the dried gel was crystallized to the pure orthorhombic phase after calcination at 900 °C in air for 6 h. These phosphors have displayed bright red color under a UV source. The richness of the red color has been verified by determining their color coordination from the CIE standard charts, and this red emission has been assigned to ⁵D₀→⁷F₂ electric dipole transition at 616 and 620 nm. The excellent luminescence properties make it possible as a good candidate for plasma display panel (PDP) application.     

New red phosphors BaZr(BO3)2 and SrAl2B2O7 doped with Eu for PDP applications

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) characteristics of Eu³⁺ ion doped borate phosphors; BaZr(BO₃)₂:Eu³⁺ and SrAl₂B₂O₇:Eu³⁺ are studied. The excitation spectra show strong absorption in the VUV region with the absorption band edge at ca. 200 nm for BaZr(BO₃)₂:Eu³⁺ and 183 nm for SrAl₂B₂O₇:Eu³⁺, respectively, which ensures the efficient absorption of the Xe plasma emission lines. In BaZr(BO₃)₂:Eu³⁺, the charge transfer band of Eu³⁺ does not appear strongly in the excitation spectrum, which can be enhanced by co-doping Al³⁺ ion into the BaZr(BO₃)₂ lattices. The luminescence intensity of BaZr(BO₃)₂:Eu³⁺ is also increased by Al³⁺ incorporation into the lattices. The PL spectra show the strongest emission at 615 nm corresponding to the electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺ in both BaZr(BO₃)₂ and SrAl₂B₂O₇, similar to that in YAl₃(BO₃)₄, which results in a good color purity for display applications.     

Enhancement of red spectral emission intensity of Y3Al5O12:Ce phosphor via Pr co-doping and Tb substitution for the application to white LEDs

We have enhanced color-rendering property of a blue light emitting diode (LED) pumped white LED with yellow emitting Y₃Al₅O₁₂:Ce³⁺ (YAG:Ce) phosphor using addition of Pr and Tb as a co-activator and host lattice element, respectively. Pr³⁺ addition to YAG:Ce phosphor resulted in sharp emission peak at about 610 nm through ¹D₂→³H₄ transition. And when Tb³⁺ substituted Y³⁺ sites, Ce³⁺ emission band shifted to a longer wavelength due to larger crystal field splitting. Y₃Al₅O₁₂:Ce³⁺, Pr³⁺ and (Y_1−xTb_x)₃Al₅O₁₂:Ce³⁺ phosphors were coated on blue LEDs to fabricate white LEDs, respectively, and their color-rendering indices (CRIs, R_a) were measured. As a consequence of the addition of Pr³⁺ or Tb³⁺, CRI of the white LEDs improved to be R_a=83 and 80, respectively. Especially, blue LED pumped (Y_0.2Tb_0.8)₃Al₅O₁₂:Ce³⁺ white LED showed both strong luminescence and high color-rendering property.     

Potential tunable white-emitting phosphor LiSr4(BO3)3:Ce3+, Eu2+ for ultraviolet light-emitting diodes

A novel Ce³⁺/Eu²⁺ co-activated LiSr₄(BO₃)₃ phosphor has been synthesized by traditional solid-state reaction. The samples could display varied color emission from blue towards white and ultimately to yellow under the excitation of ultraviolet (UV) light with the appropriate adjustment of the relative proportion of Ce³⁺/Eu²⁺. The resonance-type energy transfer mechanism from Ce³⁺ to Eu²⁺ in LiSr₄(BO₃)₃:Ce³⁺, Eu²⁺ phosphors is dominant by electric dipole–dipole interaction, and the critical distance is calculated to be about 29.14 Å by the spectra overlap method. White light was observed from LiSr₄(BO₃)₃:mCe³⁺, nEu²⁺ phosphors with chromaticity coordinates (0.34, 0.30) upon 350 nm excitation. The LiSr₄(BO₃)₃:Ce³⁺, Eu²⁺ phosphor has potential applications as an UV radiation-converting phosphor for white light-emitting diodes.     

The concentration quenching and crystallographic sites of Eu2+ in Ca2BO3Cl

A yellow phosphor, Ca2BO3CI：Eu2＋, is prepared by the high-temperature solid-state method. Under the condition of excitation sources ranging from ultraviolet to visible light, efficient yellow emission can be observed. The emission spectrum shows an asymmetrical single intensive band centred at 573 nm, which corresponds to the 4f65dl→4f7 transition of Eu2＋. Eu2＋ ions occupy two types of Ca2＋ sites in the Ca2BO3C1 lattice and form two corresponding emission centres, respectively, which lead to the asymmetrical emission of Eu2＋ in Ca2BO3C1. The emission intensity of Eu2＋ in Ca2BO3C1 is influenced by the Eu2＋ doping concentration. Concentration quenching is discovered, and its mechanism is verified to be a dipole-dipole interaction. The value of the critical transfer distance is calculated to be 2.166 nm, which is in good agreement with the 2.120 nm value derived from the experimental data.     

Enhanced luminescence of GdTaO4:Eu thin-film phosphors by K doping

The effect of K⁺ ions on GdTaO₄:Eu³⁺ thin-film phosphors was investigated in order to improve their luminescent properties. The GdTaO₄:Eu_0.1, K_x thin films were synthesized by sol-gel process, and characterized through measuring their microstructure and luminescence. The results indicated that photoluminescence (PL) intensity of GdTaO₄:Eu³⁺ film was improved remarkably by K doping. There were two maxima in the curve of PL intensity against K⁺ dopant concentration, where one was improved up to 2.1 times at x = 0.001 and the other was enhanced up to 2.7 times at x = 0.05. The first maximum was regarded as the alteration of the local environment surrounding the Eu³⁺ activator by incorporation of K⁺ ions, and the second maximum was due to the flux effect. Additionally, the luminescence increased with the increase of firing temperature from 800 °C to 1200 °C.     

Photoluminescence studies of red-emitting NaEu(WO4)2 as a near-UV or blue convertible phosphor

Sodium europium double tungstate [NaEu(WO₄)₂] phosphor was prepared by the solid-state reaction method. Its crystal structure, photoluminescence properties and thermal quenching characteristics were investigated aiming at the potential application in the field of white light-emitting diodes (LEDs). The influences of Sm doping on the photoluminescence properties of this phosphor were also studied. It is found that this phosphor can be effectively excited by 394 or 464 nm light, which nicely match the output wavelengths of near-ultraviolet (UV) or blue LED chips. Under 394 or 464 nm light excitation, this phosphor exhibits stronger emission intensity than the Y₂O₂S:Eu³⁺ or Eu²⁺-activated sulfide phosphor. The introduction of Sm³⁺ ions can broaden the excitation peaks at 394 and 464 nm of the NaEu(WO₄)₂ phosphor and significantly enhance its relative luminance under 400 and 460 nm LEDs excitation. Furthermore, the relative luminance of NaEu(WO₄)₂ phosphor shows a superior thermal stability compared with the commercially used sulfide or oxysulfide phosphor, and make it a promising red phosphor for solid-state lighting devices based on near-UV or blue LED chips.     

Luminescence and chromaticity of alkaline earth aluminate MxSr1−xAl2O4:Eu (M: Ca,Ba)

In order to prepare fluorescent material for UV-LED used as illumination light source, two series of Eu²⁺ doped (1 mol%) alkaline earth aluminate phosphors Ca_xSr_1−xAl₂O₄ and Ba_xSr_1−xAl₂O₄ were prepared. The crystal structure, relative quantum efficiency(Qr), peak wavelength(λ_p), color tuning and chromaticity were investigated by XRD patterns and photoluminescence (PL) on samples prepared by solid solution system (s series) and powder mixing system (m series) respectively. For the s series, the synthesized Ca_xSr_1−xAl₂O₄:Eu²⁺ powders show that the structure transforms from monoclinic to hexagonal at x?0.5, and λ_p increases from 442.3 to 529.7 nm with decreasing x. For the Ba_xSr_1−xAl₂O₄:Eu²⁺ system, the structure transforms from monoclinic to hexagonal at x?0.3, and λ_p decreases from 520.5 to 502.2 nm continuously from x=0 to 1. The shift in λ_p could be explained by the crystal field effect, which is affected by different coulomb attractive forces due to the various fraction of alkaline earth cation in the host lattice. Different phosphor properties prepared by either solid solution or powder mixing methods were characterized by chromaticity measurements for both reflective and transmissive modes.     

Photoluminescence studies on Eu and Ce-doped Li2SrSiO4

The luminescence of Li₂SrSiO₄: 0.01Eu, xCe (x=0.0025, 0.005, 0.0075, and 0.01) is studied as a potential ultraviolet light-emitting diode (UV-LED) phosphor that is capable of converting the ultraviolet emission of a UV-LED into white light with good luminosity. There are broad blue and yellow emissions peaked at 413 and 575 nm, respectively. The two emissions come from d-f transitions of Ce³⁺ and Eu²⁺, respectively. The emission intensity of Li₂SrSiO₄: 0.01Eu, xCe reaches its maximum at x=0.0075. The energy transfer from Ce³⁺ to Eu²⁺ is demonstrated to be the type of electric dipole-dipole interaction with considerable spectral overlap and nonradiative transition is calculated to dominate. The Commission International de I’Eclairage (CIE) chromaticity coordinates of Ce³⁺/Eu²⁺ substituted compounds is also discussed.     

Photoluminescence of double-color-emitting phosphor Ca5(PO4)3Cl:Eu, Mn for near-UV LED

Eu²⁺ activated Ca₅(PO₄)₃Cl blue-emitting phosphors were prepared by the conventional solid state method using CaCl₂ as the chlorine source and H₃BO₃ as flux. The structure and luminescent properties of phosphors depend on the concentrations of Eu²⁺, the amount of CaCl₂ and the usage of the H₃BO₃ flux were investigated systematically. Eu²⁺ and Mn²⁺ Co-doped Ca₅(PO₄)₃Cl with blue and orange double-band emissions were also researched based on the optimal composition and synthesis conditions. The energy transfer between Eu²⁺ and Mn²⁺ was found in the phosphor Ca₅(PO₄)₃Cl:Eu²⁺, Mn²⁺, and the Co-doped phosphor can be efficiently excited by near-UV light, indicating that the phoshor is a potentional candidate for n-UV LED used phosphor.     

Thermally stable blue-emitting NaSrPO4:Eu phosphor for near UV white LEDs

A novel blue light emitting NaSr_1 − xPO₄:Eu²⁺_x (x = 0.001 to 0.02) phosphors were prepared by solid-state reaction method to investigate its optical properties and thermal stability for its application in white light-emitting diodes (w-LEDs). The excitation and emission spectra of the prepared phosphor reveal a broad emission peak centered at 460 nm which arises due to 4f-5d transitions of Eu²⁺ upon the near ultra-violet (n-UV) excitation wavelength at 380 nm. The effect of Eu²⁺ doping concentration and sintering temperature on the emission intensity of NaSrPO₄:Eu²⁺ was investigated along with its chromaticity coordinates. The temperature dependent luminescence properties of the prepared phosphor show better results than that of the commercial YAG:Ce³⁺phosphor. Besides, their XRD, FT-IR, SEM, TG, and DTA profiles have also been analyzed to explore its structural details.     

Ca₂BO₃Cl:Ce³⁺,Tb³⁺:A novel tunable emitting phosphor for white light-emitting diode

<正>Ca₂BO₃Cl:Ce³⁺,Ca₂BO₃Cl:Tb³⁺,and Ca₂BO₃Cl:Ce³⁺,Tb³⁺ phosphors are synthesized by a high temperature solid-state reaction.The emission intensity of Ce³⁺ or Tb³⁺ in Ca₂BO₃Cl is influenced by the Ce³⁺ or Tb³⁺ doping content,and the optimum concentrations of Ce³⁺ and Tb³⁺ are 0.03 mol and 0.05 mol,respectively.The concentration quenching effect of Ce³⁺ or Tb³⁺ in Ca₂BO₃Cl occurs,and the concentration quenching mechanism is d-d interaction for either Ce³⁺ or Tb³⁺.The Ca₂BO₃Cl:Ce³⁺,Tb³⁺ can produce colour emission from blue to green by properly tuning the relative ratio between Ce³⁺ and Tb³⁺,and the emission intensity of Tb³⁺ in Ca₂BO₃Cl can be enhanced by the energy transfer from Ce³⁺ to Tb³⁺.The results indicate that Ca₂BO₃Cl:Ce³⁺,Tb³⁺ may be a promising double emission phosphor for UV-based white light emitting diodes.     

Potential PDP phosphors with strong absorption around 172 nm: Rare earth doped NaLaP2O7 and NaGdP2O7

NaLaP₂O₇ and NaGdP₂O₇ powder samples are prepared by solid-state reactions at 750 and 600 °C, respectively, and the VUV-excited luminescence properties of Ln³⁺ (Ln=Ce, Pr, Tb, Tm, Eu) in both diphosphates are studied. Ln³⁺ ions in both hosts show analogous luminescence. For Ce³⁺-doped samples, the five Ce³⁺ 5d levels can be clearly identified. As for Pr³⁺ and Tb³⁺-doped samples, strong 4f-5d absorption band around 172 nm is observed, which matches well with Xe-He excimer in plasma display panel (PDP) devices. As a result, Pr³⁺ can be utilized as sensitizer to absorb 172 nm VUV photon and transfer energy to appropriate activators, and Tb³⁺-doped NaREP₂O₇(RE=La, Gd) are potential 172 nm excited green PDP phosphors. For Tm³⁺ and Eu³⁺-doped samples, the Tm³⁺-O²⁻ charge transfer band (CTB) is observed to be at 177 nm, but the CTB of Eu³⁺ is observed at abnormally low energy position, which might originate from multi-position of Eu³⁺ ions. The similarity in luminescence properties of Ln³⁺ in both hosts indicates certain structural resemblance of coordination environment of Ln³⁺ in the two sodium rare earth diphosphates.     

Spectral properties of Nd:Ca2Nb2O7 crystal

This paper reports the spectral properties of Nd³⁺:Ca₂Nb₂O₇. The spectral parameters of Nd³⁺ in Nd³⁺:Ca₂Nb₂O₇ crystal have been investigated based on Judd-Ofelt theory. The spectral parameters were obtained. The parameters of line strengths Ω_λ are Ω₂=4.967×10⁻²⁰ cm², Ω₄=5.431×10⁻²⁰ cm², Ω₆=5.693×10⁻²⁰ cm². The radiative lifetime, the fluorescence lifetime and the quantum efficiency are 122 μs, 103 μs and 84.4%, respectively. The fluorescence branch ratios calculated: β₁=0.425, β₂=0.479, β₃=0.091, β₄=0.004. The emission cross section at 1068 nm is 6.204×10⁻²⁰ cm².     

SrS:Ce/ZnS:Mn-A di-band phosphor for near-UV and blue LED-converted white-light emitting diodes

The SrS:Ce/ZnS:Mn phosphor blends with various combination viz 75:25, 50:50 and 25:75 were assign to generate the white-light emission using near-UV and blue-light emitting diodes (LED) as an excitation source. The SrS:Ce exhibits strong absorption at 427 nm and the corresponding intense emission occurs at 480 and 540 nm due to electron transition from 5d(²D)−4f(²F_5/2, _7/2) of Ce³⁺ ion as a result of spin-orbit coupling. The ZnS:Mn excited under same wavelength shows broad emission band with λ_max=582 nm originates due to 3d (⁴G−⁶S) level of Mn²⁺. Photoluminescence studies of phosphor blend excited using near-UV to blue light confirms the emitted radiation varies from cool to warm white light in the range 430-600 nm, applicable to LED lightings. The CIE chromaticity coordinate values measured using SrS:Ce/ZnS:Mn phosphor blend-coated 430 nm LED pumped phosphors in the ratio 75:25, 50:50 and 25:75 are found to be (0.235, 0.125), (0.280, 0.190) and (0.285, 0.250), respectively.     

Improved luminescent properties of red-emitting Ca0.54Sr0.16Eu0.08Gd0.12(MoO4)0.2(WO4)0.8 phosphor for LED application by charge compensation

The red-emitting Ca_0.54Sr_0.16Eu_0.08Gd_0.12(MoO₄)_0.2(WO₄)_0.8 phosphor is improved in the emission charateristics by charge compensation, of which chromaticity coordinates (CIE) are x=0.66 and y=0.33. Three approaches to charge compensation are investigated, namely (a) 3Ca²⁺/Sr²⁺→2Eu³⁺/Gd³⁺+vacancy, (b) 2Ca²⁺/Sr²⁺→Eu³⁺/Gd³⁺+M⁺(M⁺ is a monovalent cation like Li⁺, Na⁺ and K⁺ employed as a charge compensator) and (c) Ca²⁺/Sr²⁺→Eu³⁺/Gd³⁺+N⁻ (N⁻ is a monovalent anion like F⁻, Cl⁻, Br⁻ and I⁻ employed as charge compensation ions). Through photoluminescent spectra analyzing the radiative and non-radiative relaxation mechanisms of luminescent system are obtained. Under 20 mA forward-bias current, one red-emitting LED is made by combining 390-405 nm-emitting LED chip and the phosphor. The red-emitting phosphor has broad prospects in LED application field.     

Synthesis and photoluminescence of CeO2:Eu phosphor powders

The crystalline structure and photoluminescence (PL) properties of europium-doped cerium dioxide synthesized by the solid-state reaction method were analyzed. CeO₂:Eu³⁺ phosphor powders exhibit the pure cubic fluorite phase up to 10 mol% doping concentration of Eu³⁺. With indirect excitation of CeO₂ host at 373 nm, the PL intensity quickly increases with increasing Eu³⁺ concentration, up to about 1 mol%, and then decreases indicating the concentration quenching. While with direct excitation (467 nm), much more stronger PL emissions, especially the electric dipole emission ⁵D₀-⁷F₂ at 612 nm, are observed and no concentration quenching occurs up to 10 mol% doping concentration of Eu³⁺. The nature of this behavior and the cause of the concentration quenching were discussed.     

Eu-activated Ba2Mg(BO3)2 yellow-emitting phosphors for near ultraviolet-based light-emitting diodes

A series of Eu²⁺-activated Ba₂Mg(BO₃)₂ yellow phosphors were prepared by a high temperature solid-state reaction. The phosphor emits intense yellow light under near ultraviolet excitation. Large Stokes shift can be attributed to the asymmetric nature of the Eu site and the lack of rigidity in the host. The concentration self-quenching mechanism of Ba₂Mg(BO₃)₂:Eu²⁺ is d-d interaction and the critical transfer distance is calculated to be about 12.29 Å. Prototype light-emitting diodes were fabricated by coating the Ba₂Mg(BO₃)₂:0.07Eu²⁺ phosphor onto ∼370 nm-emitting InGaN chips. The LEDs exhibit intense yellow-emitting under a forward bias of 20 mA. The results indicate that Eu²⁺-activated Ba₂Mg(BO₃)₂ is a candidate as a yellow component for fabrication of near-UV white light-emitting diodes.