过渡金属Fe，Co，Ni居里点附近热电势的实验研究

测量了纯金属Fe，Co，Ni的热电势发现，在居里点附近热电势随温度的变化关系曲线均呈现先凹后凸的反常现象.由曲线的转折处可确定三个居里温度，即铁磁态居里点T_f，居里点T_C和顺磁居里点θ_p.由曲线可见，金属由铁磁态到顺磁态的相转变，存在一定温度间隔的转变过程，居里温度是这一过程的中间温度.分析曲线表明，温度在T_f与T_C范围有空穴参与导电，说明磁性负载者是d带中的空穴.对于温度在T_C与θ_p范围可能存在短程有序进行了讨论. 关键词： Fe Co Ni 热电势 居里温度     

非晶态Fe87-xSixB13合金的磁化强度、电阻与温度的关系

本文研究了非晶态Fe_87-xSi_xB₁₃(x=0,9.6,14.5)合金的饱和磁化强度、电阻率与温度的关系。得到样品的居里温度T_C和晶化温度T_cr随Si含量的增加而明显提高。低温下的热磁关系符合布洛赫的T^3/2定律,计算出自旋波劲度系数D从x=0时的62meV·A²增加到x=14.5时的111meV·A²。从D值和Handrich理 关键词：     

哈斯勒合金Ni-Mn-Ga的马氏体相变和磁增强双向形状记忆效应

通过研究铁磁性金属间化合物Ni_2+xMn_1-xGa(x=-0.1,0,0.08,0.13,0.18,0.2)和Ni_2-xMn_1+x/2Ga_1+x/2(x=-0.1,0,0.04,0.06,0.1)两个系列多晶样品的交流磁化率随温度的变化行为,得到了化合物在不同组分下的马氏体相变温度TM和居里温度T_C.发现随着Ni成分的增加,前者的马氏体相变温度T_m增加,而居里温度T_C降低,后者的马氏体相变温度T_m和居里温度T_C均是先增大后减小.报道了T_m在室温附近的单晶样品Ni₅₂Mn₂₄Ga₂₄的磁场增强双向形状记忆效应.发现伴随着马氏体相变,样品在[001]方向可产生1.2%的收缩.如果在该方向施加1.2T的偏磁场可以使该应变值增大到4.0%.而垂直于[001]方向施加1.2T的偏磁场时,在[001]方向产生1.6%的膨胀.阐明了产生大应变的原因并非相界移动,而是单晶的杂散内应力小和外加磁场通过孪晶界移动使马氏体变体重组的共同结果. 关键词： 形状记忆效应 马氏体相变 2MnGa')" href="#">Ni₂MnGa     

Mn的价态对La0.8Ba0.2MnO3电磁性能的影响

在2—390K温度之间研究了La_0.8Ba_0.2MnO₃的 磁矩、磁电阻与温度的关系.发 现以不同价态的Mn元素引入得到的La_0.8Ba_0．2MnO₃ ，性能虽然都存在金属 —绝缘体转变，以及在磁场作用下居里温度附近电阻率变化非常显著的特点，但是价态对磁 性转变温度T_C，金属—绝缘体转变温度T_mi，以及磁电阻极大 值温度T_MR的影 响都非常显著.三种价态相比较，使用二价Mn的电阻率最低以及磁性转变温度更接近室温.认 为影响材料性能的主要因素是材料制备时引进的Mn元素的价态，由于原料价态的不同而形成 的氧空位浓度变化，进而影响了Mn⁴⁺/Mn³⁺的比. 关键词： 价态 磁电阻 居里温度 金属—绝缘体转变     

钙钛矿Mn基氧化物的电子顺磁共振行为的实验研究

借助电子顺磁共振技术,对Mn³⁺/Mn⁴⁺=2∶1和1∶1的两个典型体系 在居里温度T_C以上温区的顺磁行为进行了实验研究.实验表明,存在一特征温度 T_min,通过该温度将T_C以上的磁行为分成两个明显可区分的温区： 在T_min以上,共振谱由一对称的单线构成,Lande 因子g值与温度无关且接近 自由电子的值(～20023),线宽随温度呈线性变化等;而在T_{min关键词： 稀土锰氧化物 电子顺磁共振 交换变窄 自旋-自旋相互作用 自旋-晶格相互作用}     

R3(Fe,Mo)29Nx的晶体学特性和内禀磁性

研究了R₃(Fe,Mo)₂₉(R=Ce,Nd,Sm,Gd,Tb,Dy,Y)氮化物的晶体学特性和内禀磁性.主要研究内容为：氮化对R₃(Fe,Mo)₂₉金属间化合物的点阵参数、居里温度T_C、饱和磁化强度σ_s和各向异性场B_a的影响. 关键词：     

LaxZnxBa1-xFe12-xO19铁氧体高温相组成

La_xZn_xBa_1-xFe_12-xO₁₉在高温相区将存在X相和W相,x=0时其居里温度分别为518℃和534℃,x<0.6范围内La,Zn可以在W相中固溶,随x的增加,产生W相的相变温度下降,居里温度θ_f和各向异性场H_A降低,而饱和比磁化强度σ_s增加,各向异性常数基本不变。 关键词：     

Heusler合金Cu2VAl磁性及输运性质的研究

对Heusler 合金Cu₂VAl多晶甩带样品进行了磁性与输运性质方面的研究. 实验 发现Cu₂VAl在温度T为210K附近发生铁磁—顺磁相变，为弱铁磁体. 输运性质的 测量表 明在72K时电阻因局域杂质超导相变而发生突变，电子和声子之间的散射是主要的散射机 理. 居里温度T_C以下存在侧跃导致的反常霍尔效应，并且7K附近的相变导致霍 尔电阻率发生异常. 关键词： 磁性 输运 2VAl')" href="#">Cu₂VAl     

Fe/SnO2非晶多层膜的磁特性

研究了高频溅射制备的Fe/SnO₂非晶多层膜的磁特性.当SnO₂层厚度d_s固定为5nm时，样品的饱和磁化强度M_s随Fe层厚度d_m的减小而降低，这主要受样品的死层效应和维度效应的影响.另外，在d_m很小时，样品呈现准二维磁性.样品居里温度T_C随d_m的减小单调下降.样品矫顽力H_c随d_m的变化呈现 关键词：     

二元掺杂镧锰氧化物La-Ca-Ba-Mn-O的庞磁电阻特性

用固相反应法制备了二元掺杂的镧锰氧化物La_0.67(Ca_0.6Ba_0.4)_0.33MnO_z(LCBMO)立方多晶体材料,研究了其磁特性和庞磁电阻特性,并与用类似方法制备的一元掺杂的La_0.67Ca_0.33MnO_z(LCMO)及La_0.67Ba_0.33MnO_z(LBMO)的庞磁电阻特性进行了比较.研究表明,LCBMO的居里温度T_C为312K,介于LCMO和LBMO的T_C（分别为280,362K）之间,其金属-半导体转变温度T_p和μ₀H=0.6T下的磁电阻（MR）峰值温度T_m分别为306,298K,接近于其T_C,也介于LCMO和LBMO的T_p和T_m之间.μ₀H=0.6T下,在各自的T_m处,LCMO,LCBMO和LBMO的庞磁电阻值分别达到41%,24.7%和8%,但在室温（300K）处,LCBMO的MR值仍达到20％,远大于LCMO和LBMO的值（分别为2.0％和2.4％）.研究还发现,在温度远低于T_m时,LCMO仍保持一定的磁电阻效应,而LCBMO和LBMO的磁电阻温度降低而增加,这些低温磁电阻特性与材料的结构特征（如晶界和致密度）有关. 关键词：     

Electron transport properties of Co71−xFexCr7Si8B14 (x=0, 2, 3.2, 4, 6,8 and 12 at%) amorphous alloys during devitrification

The investigation addresses the electron transport properties of Co_71−xFe_xCr₇Si₈B₁₄ (x=0, 2, 3.2, 4, 6, 8 and 12 at%) amorphous alloys. The variation in electrical resistivity of as-cast amorphous materials with thermal scanning from room temperature to 1000 K was measured. The CoFe-based alloys revealed an initial decrease in temperature coefficient of resistivity (TCR), a characteristic of spin-wave phenomena in glassy metallic systems. This behaviour in the present alloys was in a sharp contrast to the Co-based amorphous materials that indicate the drop in resistivity much below room temperature. In the studied alloys, the variation in initial TCR values and the full-width at half-maxima determined from X-ray diffraction of as-quenched materials exhibited a similar trend with increasing Fe content, indicating the compositional effect of near neighbouring atoms. After the initial decrease in resistivity, all the alloys indicated a subsequent increase at T_min. The Curie temperature (T_C), which was measured from thermal variation of ac susceptibility showed non-monotonic change with Fe content. In the temperature range between T_min and T_C the relative scattering by electron-magnon and electron-phonon resulted in the non-monotonic change in Curie temperature. At crystallization onset (T_X1) all the alloys except there with X=6, showed a sharp decrease in electrical resistivity which was attributed to ordering phenomena. In contrast to this resistivity decrease, X=6 alloy exhibited a drastic increase in resistivity around T_X1 observed during amorphous to nanocrystalline transformation. Such nanocrystalline state was observed by Transmission electron microscopy.     

Fe基非晶态合金的低温电阻研究

本文报道Fe_100-xB_x,Fe_87-xSi_xB₁₃,(Fe_1-xCo_x)₇₈Si_9.5B_12.5,(Fe_1-xM_x)_80-84B_16-20(M=Zr,V,Nb,Ta,Cr,Mo,W,Mn)非晶态合金的 关键词：     

非晶态Fe90-xBxZr10合金的磁性、电性和晶化

本文研究了部分B元素替代Fe对非晶态FeZr基合金磁性、电性和晶化的影响,并与非晶态FeB合金作了比较。解释了样品中每个FeZr原子的平均磁矩μ_FeZr和居里温度T_c随B含量x的增加而增加的原因,讨论了在不同的温区样品中可能存在的散射机制对电阻率的贡献以及影响晶化温度的因素。 关键词：     

非晶态(Fe1-xWx)84.5B15.5合金的低温电阻率反常

研究了(Fe_1-xW_x)_84.5B_15.5(x=0—0.1)非晶态合金的电阻率ρ与温度T(4.2—300K)的关系。实验结果表明,在所研究浓度区域内均出现电阻率与温度关系的极小值,电阻率极小值的温度T_min在x=0.06时出现峰值。用x=0.02—0.1浓度区域内,当Tmin时,又出现了电阻率与温度关系的极大值,电阻率极大值的温度T_max在26—35K之间。低温电阻率反常现象与类Kondo效应及局域磁矩之间RKKY相互作用有关。 关键词：     

Invar-type new ferromagnetic amorphous Fe-B alloys

Measurements of magnetization, electrical resistivity, thermal expansion and differential thermal change were made on amorphous Fe_100-xB_x (9 ≦ X ≦ 21) alloys prepared by rapid quenching from the liquid state.With decreasing boron content in the alloys, the Curie temperature falls remarkably, while the magnetic moment increases sluggishly. The thermal expansion curves exhibit the invar characteristics below the Curie temperature due to a large positive spontaneous volume magnetostriction, and the reduced magnetization curves decrease much more rapidly with increasing temperature than those of other ferromagnetic amorphous alloys.     

非晶态(Fe1-xCox)77.5Nd4B18.5合金的电阻率的压力系数和压力弛豫研究

在０．０００１－２．４ＧＰａ流体静压力范围详细研究了非晶(Fe_1-xCo_x)_77.5Nd₄B_18.5（０≤ｘ≤１．０）合金的电阻率与压力的关系，得到该非晶合金电阻率的压力系数随组分ｘ变化的规律。结果表明：用少量的钴（ｘ＝０．２）替代铁，不会影响其硬磁性和热稳定性，同时却可减小电阻率的压力系数，从而增强电磁性能在压力下的稳定性。此外还观测到在０．５１ＧＰａ保压３－２４h的结构弛豫，进一步求出该非晶台金电阻率的压力弛豫时间对组分ｘ的依赖关系。 关键词：     

成分和过渡金属对FeZr基非晶态合金晶化温度的影响

本文系统研究了Fe_100-xZr_x,(Fe_1-xZr_x)₈₄B₁₆和Fe_90-xM_xZr₁₀(M=V,Cr,Mn,Co,Ni,Si,B)非晶态合金的晶化温度与成分的关系。主要结果有:用Zr替代Fe使晶化温度明显提高;在FeMZr非晶态合金系列中,晶化温度依M=Mn,Cr,V元素的顺序和M含量x的增大而提高,而依 关键词：     

Curie temperatures and crystallization behavior of amorphous Fe81−xNixZr7B12 (x=10, 20, 30, 40, 50, 60) alloys

Curie temperature, crystal structure and crystallization behavior of amorphous alloys with the stoichiometry Fe_81−xNi_xZr₇B₁₂ (x=10–60) have been studied by X-ray diffractometry (XRD), differential scanning calorimetry (DSC) and AC-magnetization (TMAG) measurements as functions of temperature. The thermal stability of long-range magnetic order, T_C vs. Ni content in as-quenched amorphous alloys exhibits maximum at 352 °C for x=40. The primary crystallization has been detected during annealing at the first crystallization stage of all ribbons investigated.     

非晶态Fe86M4Zr10合金的磁性和电性

本文研究了非晶态Fe₈₆M₄Zr₁₀(M=V,Cr,Mn,Fe,CO,Ni,Cu,B,Si)合金的基本磁性和低温电性,讨论了不同元素M的掺杂对FeZr合金居里温度和磁矩的影响,并用相干交换散射模型解释了样品在居里温度附近出现的电阻率极小。 关键词：