Ultra-thin films and surface alloying of Pd on Cu(1 1 1) investigated by medium energy ion scattering

The structure of Pd films on Cu(1 1 1) and the alloying between the films and the substrate have been investigated by medium energy ion scattering (MEIS) using 100 keV H⁺ ions. Data are presented for the and alignments (nominal one- and three-layer alignments, respectively). It is found that beyond 1 ML the Pd grows in a twinned fcc structure, the incommensurate nature of which increases the visibility of the Cu(1 1 1) substrate to MEIS. Deposition of 0.2 ML of Pd produces a structure in which Pd mostly occupies the top two layers which have interlayer distances d₁₂ = 208 ± 4 pm and d₂₃ = 211 ± 4 pm. Some twinning is also present in this structure. Upon annealing 1.6 ML of Pd to 600 K for 1 min, the copper and palladium interdiffuse leaving around 0.4 ML of visible palladium. Energy plots show that there are several layers with an altered structure present over at least part of the surface. This may be due to large scale interdiffusion or alloy island formation. Incremental annealing to successively higher temperatures shows that the structural transformation begins around 500 K.     

The growth of ultrathin Au films on Ni{1 1 1}: A study with medium energy ion scattering

The initial growth of Au on Ni{1 1 1} is strongly influenced by the 15.7% difference in bulk lattice parameter between the two fcc metals. At 400 K, the first monolayer of Au grows on the Ni{1 1 1} surface as a (9 × 9) overlayer with 8 Au-Au spacings being equivalent to 9 Ni-Ni spacings. Umezawa et al. [Physical Review B 57 (1998) 8842; Surface Science 426 (1999) 225] reported that the growth of Au overlayers can occur either via a reverse (R)-mode (i.e., incorporating a stacking fault at the Au-Ni interface) or a normal (N)-mode—the relative proportion of each mode being strongly sensitive to growth temperature. Using the technique of medium energy ion scattering, we examine the growth of Au on Ni{1 1 1} at 400 K. We conclude that, at this deposition temperature, there is a preference for growth via the R-mode (74 ± 9%). In addition, we find that the Au overlayer has a considerably higher density than bulk Au being contracted isotropically by 3.1% in the {1 1 1} plane and also by ∼7% perpendicular to the {1 1 1} plane. We discuss possible explanations for our findings.     

Alloy formation in the Au{1 1 1}/Ni system - An investigation with scanning tunnelling microscopy and medium energy ion scattering

Using the techniques of scanning tunnelling microscopy (STM) and medium energy ion scattering (MEIS), we examine the growth and annealing behaviour of ultrathin Ni films on Au{1 1 1} at 300 K. As has been shown previously, submonolayer growth of Ni on Au{1 1 1} is strongly influenced by the presence of the herringbone reconstruction with two-dimensional clusters nucleating at herringbone elbows. Second layer growth commences prior to the completion of the monolayer. After multiple layers have been deposited, the surface morphology retains a similar cluster-like appearance. Annealing produces surfaces exhibiting long range Moiré structures and, at higher temperature, triangular misfit dislocations. We use MEIS to examine the composition and structure of these surface alloy phases and conclude that in each case, they consist of an essentially pure Au surface layer on a bimetallic second layer.     

Hyperthermal scattering of Cs from Pt(1 1 1): the effect of image charge on the ion-surface energy transfer

We have studied the energy exchange between hyperthermal (5-100 eV) Cs⁺ projectiles and a Pt(1 1 1) surface by measuring the kinetic energy of the scattered ions. The scattering geometry was chosen to be in-plane with specular scattering angles, and the energy of the scattered ions was analyzed as functions of incidence energy and angle. For low incidence energy (<40 eV), the energy transfer to the Pt surface is substantially enhanced due to the attractive image charge force between Cs⁺ and the surface. The image charge effects are highlighted by the different energy transfer on Pt(1 1 1) and Si(1 1 1) surfaces. Analysis of the experimental results using two- and three-dimensional theoretical models revealed a well depth of 1 eV for the image charge potential. Hyperthermal Cs⁺ ions scatter from Pt(1 1 1) predominantly via double collisions with Pt atoms, though the scattering phenomena are insensitive to the impact site at the surface.     

Surface and subsurface oxide formation on Ni(1 0 0) and Ni(1 1 1)

The oxidation of Ni(1 0 0) and Ni(1 1 1) at elevated temperatures and large oxygen exposures, typical of the methods used in the preparation of NiO(1 0 0) films for surface studies, has been investigated by medium energy ion scattering (MEIS) using 100 keV H⁺ incident ions. Oxide film growth proceeds significantly faster on Ni(1 1 1) than on Ni(1 0 0), but on both surfaces oxide penetration occurs to depths significantly greater than 100 Å with total exposures of 1200 and 6000 L respectively. The metal/oxide interface is extremely rough, with metallic Ni extending to the surface, even for much thicker oxide films on Ni(1 1 1). On Ni(1 1 1), NiO growth occurs with the (1 0 0) face parallel to the Ni(1 1 1) surface and the close-packed 〈1 1 0〉 directions parallel. On Ni(1 0 0) the MEIS blocking curves cannot be reconciled with a single orientation of NiO(1 0 0) (with the 〈1 1 0〉 directions parallel) on the surface, but is consistent with the substantial orientational disorder (including tilt) previously identified by spot-profile analysis LEED.     

(6 × 2) Reconstruction of the Ag/Si(1 1 1) surface at 77 K

The ground state of the Ag/Si(1 1 1)-(3 × 1) has been investigated by low temperature scanning tunneling microscopy (STM) and density-functional theory. The Fourier transform of the STM image reveals a (6 × 2) reconstruction, which is theoretically found to yield a reconstruction with lower energy than the (3 × 1). The most stable (6 × 2) structural model leads to excellent correspondence between experimental and simulated STM images, and reveals a dimerization of the silver atoms in the channels formed by neighbouring honeycomb Si chains.     

Ab initio density functional study of O on the Ag(0 0 1) surface

The adsorption of oxygen on the Ag(1 0 0) is investigated by means of density functional techniques. Starting from a characterization of the clean silver surfaces oxygen adsorption in several modifications (molecularly, on-surface, sub-surface, Ag₂O) for varying coverage was studied. Besides structural parameters and adsorption energies also work-function changes, vibrational frequencies and core level energies were calculated for a better characterization of the adsorption structures and an easier comparison to the rich experimental data.     

Structures and stability of Ag clusters on Ag(1 1 1) and Ni(1 1 1) surfaces

The structures of the lowest total energy for small Ag_N clusters with N = 2-20, which are grown on Ag(1 1 1) and Ni(1 1 1) surfaces, have been determined using a combination of the embedded-atom method and the basin-hopping algorithm. It is found that the particularly stable Ag clusters with N<18 have similar geometries on both surfaces when comparing clusters of the same size. On the other hand, the geometries of the less stable Ag clusters in the same size range differ for the two surfaces. From N?18, the sizes of the particularly stable structures are different for the two different substrates. Due to the large size mismatch of the two types of atoms it is energetically unfavorable for Ag to form a pseudomorphic monolayer structures on Ni(1 1 1) and there is considerable strain produced at the interface. The effect of this strain and the increased adatom-substrate interactions lead to irregular and elongated structures of the adsorbed Ag clusters.     

The CuGaSe2(0 0 1) surface: A (4 × 1) reconstruction

We report on the formation of a stable (4 × 1) reconstruction of the chalcopyrite CuGaSe₂(0 0 1) surface. Using Ar⁺ ion-bombardment and annealing of epitaxial CuGaSe₂ films grown on GaAs(0 0 1) substrates it was possible to obtain flat, well-ordered surfaces showing a clear (4 × 1) reconstruction. The cleanliness and structure were analyzed in situ by AES and LEED. AES data suggest a slight Se-enrichment and Cu-depletion upon surface preparation. Our results demonstrate that (0 0 1) surfaces of the Cu-III-VI₂(0 0 1) material can show stable, unfacetted surfaces.     

A surface X-ray diffraction study of TiO2(1 1 0)(3 × 1)-S

Surface X-ray diffraction has been used to investigate the structure of TiO₂(1 1 0)(3 × 1)-S. In concert with existing STM and photoemission data it is shown that on formation of a (3 × 1)-S overlayer, sulphur adsorbs in a position bridging 6-fold titanium atoms, and all bridging oxygens are lost. Sulphur adsorption gives rise to significant restructuring of the substrate, detected as deep as the fourth layer of the selvedge. The replacement of a bridging oxygen atom with sulphur gives rise to a significant motion of 6-fold co-ordinated titanium atoms away from the adsorbate, along with a concomitant rumpling of the second substrate layer.     

LCAO study of the Cu(1 1 0)-p(2 × 1)O surface

We have performed semi-empirical LCAO calculations of the electronic structure of the Cu(1 1 0)-p(2 × 1)O surface. This has been done accounting for the Cu-Cu interactions by means of a recently proposed set of parameters, which give very good results for the bulk as well as for the surfaces of lowest Miller indices. Furthermore, the O-O interactions, which have been neglected in the preceding similar studies, have been taken into account. The resulting surface bands are in very good agreement with the overall set of the available experimental data. Several issues concerning the physical properties of this surface are addressed in the present paper: the changes induced on the clean surface bands by the adsorption and the reconstruction; the arrangement of the Cu and O atoms in the added rows; the position of the p_y antibonding band of the oxygen. In particular, we have found that the latter has an energy of −0.2 eV at the point. This result confirms an experimental indication in the same direction previously reported by Courths et al. [R. Courths, S. Hüfner, P. Kemkes, G. Wiesen, Surf. Sci. 376 (1997) 43].     

Determination of deuterium adsorption site on palladium(1 0 0) using low energy ion recoil spectroscopy

Ion beam analysis has been recently applied to study the adsorption phenomena of some adsorbates on metal surfaces. In this paper, surface recoils created by low energy Ne⁺ ions are employed to study the adsorption site of deuterium (D) atoms on Pd(1 0 0). This technique is extremely surface sensitive with the capacity for atomic layer depth resolution. From azimuthal angle observations of Pd(1 0 0) specimen, it was found that at room temperature, D was adsorbed in the fourfold hollow site of Pd(1 0 0) at a height of 0.25 ± 0.05 Å above the surface. The adsorbate remains in the hollow site at all temperatures to 383 K though the vertical height above the surface is found to depend on coverage and for the first time evidence is found of a transition to a p(2 × 2) structure for the adsorbate. There is no evidence of D sitting in the Pd(1 0 0) subsurface at room and higher temperatures.     

Surface structure of sphalerite studied by medium energy ion scattering and XPS

The reactivity of high-Fe containing sphalerite (Zn_1−xFe_xS), the major source of Zn, is of great interest for industrial applications. Since the initial reactivity depends on the physical and chemical properties of the surface, it is important to understand the structure of cleaved and fractured surfaces. Zn_1−xFe_xS zincblende (1 1 0) oriented samples cleaved in air and in vacuum were studied with medium energy ion scattering (MEIS) in order to study surface relaxation and reconstruction associated with the possible formation of S dimers. The experimental results are presented together with ion scattering Monte Carlo simulations that have been performed using the different models of the surface structure. The MEIS blocking patterns are different for the air- and vacuum-cleaved specimens. Models for the air-cleaved samples found S atoms in the first layer that are relaxed outwards by 0.08 Å and Zn(Fe) atoms relaxed inwards by 0.51 Å, with some lateral translation of both species. Results for the vacuum-cleaved sample indicate S atoms have been displaced laterally by 0.5 Å at the surface. X-ray photoelectron spectroscopic (XPS) measurements provide evidence for a high binding energy species indicative of S-S bonds in the near-surface region that are consistent with the ion scattering structural data for both cleaving protocols.     

Electron and lattice structure of ultra thin Ag films on Si(1 1 1) and Si(0 0 1)

We studied the low temperature (T ? 130 K) growth of Ag on Si(0 0 1) and Si(1 1 1) flat surfaces prepared by Si homo epitaxy with the aim to achieve thin metallic films. The band structure and morphology of the Ag overlayers have been investigated by means of XPS, UPS, LEED, STM and STS. Surprisingly a (√3 × √3)R30° LEED structure for Ag films has been observed after deposition of 2-6 ML Ag onto a Si(1 1 1)(√3 × √3)R30°Ag surface at low temperatures. XPS investigations showed that these films are solid, and UPS measurements indicate that they are metallic. However, after closer STM studies we found that these films consists of sharp Ag islands and (√3 × √3)R30°Ag flat terraces in between. On Si(0 0 1) the low-temperature deposition yields an epitaxial growth of Ag on clean Si(0 0 1)-2 × 1 with a twinned Ag(1 1 1) structure at coverage’s as low as 10 ML. Furthermore the conductivity of few monolayer Ag films on Si(1 0 0) surfaces has been studied as a function of temperature (40-300 K).     

Growth of Si nanostructures on Ag(0 0 1)

The first stages of the growth of silicon on Ag(0 0 1) at moderate temperatures start by the formation of a p(3 × 3) superstructure, which continuously evolves with increasing coverage toward a more complex superstructure. In this paper, the atomic arrangement of the p(3 × 3) and of the “complex” superstructure has been investigated using scanning tunnelling microscopy, surface X-ray diffraction and low energy electron diffraction. The atomic model retained for the p(3 × 3) reconstruction consists in four silicon atoms (tetramers) adsorbed near hollow and bridge sites of the top most Ag(0 0 1) surface layer. For higher coverages, i.e., when the “complex” superstructure starts to develop, the silicon overlayer forms periodic stripes, most probably bi-layers, with a graphitic like structure.     

NO dissociation pathways on Rh(1 0 0), (1 1 0), and (1 1 1) surfaces: A comparative density functional theory study

The chemisorption and dissociation pathways of NO on the Rh(1 0 0), (1 1 0), and (1 1 1) surfaces are studied by the plane-wave density functional theory (DFT) with CASTEP program. In addition, the electronic and geometrical effects that affect the NO dissociation reactions have been investigated in detail. The calculation results are presented as following: The effective activation energies of the best NO dissociation pathways on the Rh(1 0 0), the Rh(1 1 0), and the Rh(1 1 1) are 0.63, 0.66 and 1.77 eV, respectively. The activity of the Rh planes for NO dissociation is in the order of Rh(1 0 0) ≈ Rh(1 1 0) > Rh(1 1 1). The low dissociation barrier for Rh(1 0 0) and Rh(1 1 0) is associated with the existence of a lying-down NO structure which acts as a precursor for dissociation. By Mulliken population analysis and structure analysis, both electronic and geometrical effects are found to affect the NO dissociation reactions, but the geometrical effect exceed the electronic. The energy decomposition scheme has been used to provide further insight into the NO dissociation reactions. Based on the calculations, the interaction energy between N and O in the transition state on the Rh(1 1 1) is found much larger than that on the Rh(1 0 0) and the Rh(1 1 0). The major differences of should originate from the variation of the bonding competition effect.     

Quantitative determination of the local structure of thymine on Cu(1 1 0) using scanned-energy mode photoelectron diffraction

The local adsorption structures of the surface species formed by interaction of thymine with a Cu(1 1 0) surface at room temperature, and after heating to ∼530 K, have been investigated. Initial characterisation by soft-X-ray photoelectron spectroscopy and O K-edge near-edge X-ray absorption fine structure (NEXAFS) indicates the effect of sequential dehydrogenation of the NH species and provides information on the molecular orientation. O 1s and N 1s scanned-energy mode photoelectron diffraction shows the species at both temperatures bond to the surface through both carbonyl O atoms and the deprotonated N atom between them, each bonding atom adopting near-atop sites on the outermost Cu surface layer. The associated bondlengths are 1.96 ± 0.03 Å for Cu-N and 1.91 ± 0.03 Å and 2.03 ± 0.03 Å for the two inequivalent Cu--O bonds. The molecular plane lies almost exactly in the close-packed azimuth, but with a tilt relative to the surface normal of approximately 20°. Heating to ∼530 K, or deposition at this temperature, appears to lead to dehydrogenation of the second N atom in the ring, but no significant change in the adsorption geometry.     

Density functional theory investigation of CN on Cu(1 1 1), Ni(1 1 1) and Ni(1 0 0)

The adsorption of CN on Cu(1 1 1), Ni(1 1 1) and Ni(1 0 0) has been investigated using density functional theory (DFT). While experimental studies of CN on Cu(1 1 1) show the molecular axis to be essentially parallel to the surface, the normally-preferred DFT approach using the generalised gradient approximation (GGA) yields a lowest energy configuration with the C-N axis perpendicular to the surface, although calculations using the local density approximation (LDA) do indicate that the experimental geometry is energetically favoured. The same conclusions are found for CN on Ni(1 1 1); on both surfaces bonding through the N atom is always unfavourable, in contrast to some earlier published results of ab initio calculations for Ni(1 1 1)/CN and Ni(1 0 0)/CN. The different predictions of the GGA and LDA approaches may lie in subtly different relative energies of the CN 5σ and 1π orbitals, a situation somewhat similar to that for CO adsorbed on Pt(1 1 1) which has proved challenging for DFT calculations. On Ni(1 0 0) GGA calculations favour a lying-down species in a hollow site in a geometry rather similar to that found experimentally and in GGA calculations for CN on Ni(1 1 0).     

Electronic structure and surface reconstruction of adsorbed oxygen on copper(0 0 1)

The electronic structure of the c(2 × 2) and the missing row phases of chemisorbed O on Cu(0 0 1) at a coverage of 0.5 monolayers has been calculated using a full-potential semi-infinite embedding technique. Calculations are made over a range of Cu-O layer spacings, and from the change in the work function, the effective charge on O is obtained. The effective charge is the same for both phases of the O/Cu(0 0 1) surface with a value of −0.3|e| on O, and consequently too small to drive any surface instability. The angular momentum-resolved density of states and energy-resolved charge densities are used to describe the binding and the spatial electronic overlap at the surfaces. In the reconstructed phase the O and the surface Cu atoms undergo displacements, which optimises the bonding.     

Theoretical study of Ni adsorption on the GaN(0 0 0 1) surface

First-principles pseudo-potential calculations within density-functional theory framework are performed in order to study the structural and electronic properties of nickel adsorption and diffusion on a GaN(0 0 0 1)-2×2 surface. The adsorption energies and potential energy surfaces are investigated for a Ni adatom on the Ga-terminated (0 0 0 1) surface of GaN. This surface is also used to study the effect of the nickel surface coverage. The results show that the most stable positions of a Ni adatom on GaN(0 0 0 1) are at the H₃ sites and T₄ sites, for low and high Ni coverage respectively. In addition, confirming previous experimental results, we have found that the growth of Ni monolayers on the GaN(0 0 0 1) surface is possible.