Luminescence of CaGa<Subscript>2</Subscript>Se<Subscript>4</Subscript>:Eu crystals

We have studied photoluminescence and thermoluminescence (PL and TL) in CaGa₂Se₄:Eu crystals in the temperature range 77–400 K. We have established that broadband photoluminescence with maximum at 571 nm is due to intracenter transitions 4f⁶ 5d–4f⁷ (⁸S_7/2) of the Eu²⁺ ions. From the temperature dependence of the intensity (log I–10³/T), we determined the activation energy (E _a = 0.04 eV) for thermal quenching of photoluminescence. From the thermoluminescence spectra, we determined the trap depths: 0.31, 0.44, 0.53, 0.59 eV. The lifetime of the excited state 4f6 5d of the Eu²⁺ ions in the CaGa₂Se₄ crystal found from the luminescence decay kinetics is 3.8 μsec. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 76, No. 1, pp. 112–116, January–February, 2009.     

Structural and dehydriding properties of Ca(BH<Subscript>4</Subscript>)<Subscript>2</Subscript>

We have investigated the structural and dehydriding properties of Ca(BH₄)₂. It was found that Ca(BH₄)₂ undergoes a structural phase transformation from an orthorhombic low-temperature (LT) modification into a tetragonal high-temperature (HT) modification between 433 K and 523 K. The amount of hydrogen desorbed from Ca(BH₄)₂ during the pressure–composition (p–c) isotherm measurement was 5.9 mass%. This hydrogen desorption is caused by the partial dehydrogenation of Ca(BH₄)₂ accompanied by the formation of CaH₂ and orthorhombic intermediate phases.     

Nonlinear optical characterization of LaEr(MoO<Subscript>4</Subscript>)<Subscript>3</Subscript> thin films using the <Emphasis Type="BoldItalic">Z</Emphasis> -scan technique

The nonlinear optical properties of thin films of LaEr(MoO₄)₃ were studied using a ∼30 ps Nd:YAG laser at 532 nm with a repetition rate of 250 Hz. Closed aperture Z-scan measurement revealed a negative nonlinearity in the LaEr(MoO₄)₃. The nonlinear refractive index γ=1.38×10^-10 cm²/W and nonlinear absorption coefficient β=16.8×10^-6 cm/W were calculated from the Z-scan data. The fluorescent upconversion spectra were recorded with 980 nm excitation. An optical switching mechanism based on nonlinear absorption is also presented experimentally. PACS 81.15.Fg; 77.84.Bw; 33.50.Dq; 42.70.Mp     

Electron momentum density in Cu<Subscript>0.9</Subscript>Al<Subscript>0.1</Subscript>

A reconstruction technique based on the solution of the Radon transform in terms of Jacobi polynomials is used to obtain the 3D electron momentum density, ϱ(p), from nine high-resolution Compton profiles (CPs) for a Cu_0.9Al_0.1 disordered alloy single crystal. The method was also applied to theoretical CPs computed within the Korringa–Kohn–Rostoker coherent potential approximation (KKR-CPA) first-principles scheme for the same nine orientations of the crystal. The experimental ϱ(p) is in satisfactory agreement with the theoretical ϱ(p), shows most details of the Fermi surface (FS) and exhibits electron correlation effects. We comment on the map of the FS obtained by folding the reconstructed ϱ(p) into the first Brillouin zone, which yields the occupation number density, ϱ(k). A test of the validity of data via a consistency condition (within our reconstruction algorithm) as well as the propagation of experimental noise in the reconstruction of both ϱ(p) and ϱ(k) are investigated. Received: 24 October 2001 / Accepted: 20 January 2002 / Published online: 3 June 2002 RID="*" ID="*"Corresponding author. Fax: +48-71/344-10-29, E-mail: samsel@int.pan.wroc.pl     

Growth and spectral properties of self-frequency doubling crystal,Nd:Ca<Subscript>9.03</Subscript>Na<Subscript>1.08</Subscript>La<Subscript>0.62</Subscript>(VO<Subscript>4</Subscript>)<Subscript>7</Subscript>

The non-doped and doped Nd³⁺ of Ca_9.03Na_1.08La_0.62(VO₄)₇ crystals were grown by the Czochralski technique. The effective segregation coefficients of Na⁺ and Nd³⁺ ions in the crystal were measured to be about 0.5 and 1.1, respectively. The XPS analysis of Ca_9.03Na_1.08La_0.62(VO₄)₇ crystal indicates that the vanadium in the crystal is a mixture of V⁴⁺ (1.46 at. %) and V⁵⁺ (98.54 at. %). The hardness of Nd:Ca_9.03Na_1.08La_0.62(VO₄)₇ crystal is about 383.1 VDH. Nd:Ca_9.03Na_1.08La_0.62(VO₄)₇ crystal exhibits similar thermal expansion coefficients along the a (11.2×10^-6 K^-1) and c (13.7×10^-6 K^-1) axes, indicating a low thermal expansion anisotropy (α_c/α_a≈1.2). The qualitative frequency-doubling experiment shows that the doping of Na⁺ ion can help reduce the scattering of frequency-doubling light, and the intensity of SHG for Ca_9.03Na_1.08La_0.62(VO₄)₇ crystal is found to be about 3.5 times as large as that of KDP. The polarized absorption and fluorescence spectra are analyzed based on Judd–Ofelt theory, which exhibits that the π-polarized absorption and stimulated emission cross sections are 6.07×10^-20 cm² with an FWHM 12.0 nm at 810 nm and 1.42×10^-19 cm² at 1069 nm, respectively. The fluorescence lifetime is 115 μs at room temperature. All the results indicate that Nd:Ca_9.03Na_1.08La_0.62(VO₄)₇ crystal is a candidate of self-frequency doubling laser material. PACS 42.62.Fi; 42.70.Mp; 81.10.Fq     

Spectroscopic properties of Nd<Superscript>3+</Superscript>:CaNb<Subscript>2</Subscript>O<Subscript>6</Subscript> crystal

The absorption spectra, fluorescence spectrum and fluorescence decay curve of Nd³⁺ ions in CaNb₂O₆ crystal were measured at room temperature. The peak absorption cross section was calculated to be 6.202×10⁻²⁰ cm² with a broad FWHM of 7 nm at 808 nm for E//a light polarization. The spectroscopic parameters of Nd³⁺ ions in CaNb₂O₆ crystal have been investigated based on Judd-Ofelt theory. The parameters of the line strengths Ω _t are Ω ₂=5.321×10⁻²⁰ cm²,Ω ₄=1.734×10⁻²⁰ cm²,Ω ₆=2.889×10⁻²⁰ cm². The radiative lifetime, the fluorescence lifetime and the quantum efficiency are 167 μs, 152 μs and 91%, respectively. The fluorescence branch ratios are calculated to be β ₁=36.03%,β ₂=52.29%,β ₃=11.15%,β ₄=0.533%. The emission cross section at 1062 nm is 9.87×10⁻²⁰ cm².     

Negative thermo-optical coefficients and athermal directions in monoclinic KGd(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> and KY(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> laser host crystals in the visible region

The temperature dependence of three principal refractive indices of the biaxial KGd(WO₄)₂ and KY(WO₄)₂ crystals in the temperature range of 288–673 K was measured at wavelengths of 438.5 and 632.8 nm. Their thermo-optical coefficients (TOC) of the first and second orders were determined on the basis of the experimental data obtained. TOC were found to be negative for the n_g and n_p refractive indices of the KY(WO₄)₂ crystal and for the n_g refractive index of the KGd(WO₄)₂ crystal. It was established that in a fairly wide temperature range contributions of the positive and negative TOC to the refractive index of a light wave propagating in these crystals in certain directions compensate each other. Such athermal directions were determined for the index ellipsoid principal planes of these crystals on the basis of experimental data. PACS 78.20.Ci; 78.20.Nv     

Magnetic properties of the Nd<Subscript>0.5</Subscript>Gd<Subscript>0.5</Subscript>Fe<Subscript>3</Subscript>(BO<Subscript>3</Subscript>)<Subscript>4</Subscript> single crystal

The magnetic properties of the Nd_0.5Gd_0.5Fe₃(BO₃)₄ single crystal have been studied in principal crystallographic directions in magnetic fields to 90 kG in the temperature range 2–300 K; in addition, the heat capacity has been measured in the range 2–300 K. It has been found that, below the Néel temperature T _N = 32 K down to 2 K, the single crystal exhibits an easy-plane antiferromagnetic structure. A hysteresis has been detected during magnetization of the crystal in the easy plane in fields of 1.0–3.5 kG, and a singularity has been found in the temperature dependence of the magnetic susceptibility in the easy plane at a temperature of 11 K in fields B < 1 kG. It has been shown that the singularity is due to appearance of the hysteresis. The origin of the magnetic properties of the crystal near the hysteresis has been discussed.     

Electrical properties,equivalent circuit,and dielectric relaxation studies on [(C<Subscript>3</Subscript>H<Subscript>7</Subscript>)<Subscript>4</Subscript>N]<Subscript>2</Subscript>Cd<Subscript>2</Subscript>Cl<Subscript>6</Subscript> polycrystalline

The Ac electrical conductivity and the dielectric relaxation properties of the [(C₃H₇)₄N]₂Cd₂Cl₆ polycrystalline sample have been investigated by means of impedance spectroscopy measurements over a wide range of frequencies and temperatures, 209 Hz–5 MHz and 361–418 K, respectively. The purpose is to make a difference between the electrical and dielectric properties of the polycrystalline sample and single crystal. Besides, a detailed analysis of the impedance spectrum suggests that the electrical properties of the material are strongly temperature-dependent. Plots of (Z" versus Z') are well fitted to an equivalent circuit model consisting of a series combination of grains and grains boundary elements. Moreover, the temperature dependence of the electrical conductivity in the different phases follows the Arrhenius law and the frequency dependence of σ (ω) follows the Jonscher’s universal dynamic law. Furthermore, the modulus plots can be characterized by full width at half height or in terms of a nonexperiential decay function φ(t) = exp(t/t)^β. Finally, the imaginary part of the permittivity constant is analyzed with the Cole–Cole formalism.     

Electrical characterization of the [N(CH<Subscript>3</Subscript>)<Subscript>4</Subscript>][N(C<Subscript>2</Subscript>H<Subscript>5</Subscript>)<Subscript>4</Subscript>]ZnCl<Subscript>4</Subscript> compound

The [N(CH₃)₄][N(C₂H₅)₄]ZnCl₄ compound has been synthesized by a solution-based chemical method. The X-ray diffraction study at room temperature revealed an orthorhombic system with P2₁2₁2 space group. The complex impedance has been investigated in the temperature and frequency ranges 420–520 K and 200 Hz–5 MHz, respectively. The grain interior and grain boundary contribution to the electrical response in the material have been identified. Dielectric data were analyzed using the complex electrical modulus M ^* for the sample at various temperature. The modulus plots can be characterized by full width at half height or in terms of a non-exponential decay function ϕ(t) = exp[(−t/τ) ^β ]. The detailed conductivity study indicated that the electrical conduction in the material is a thermally activated process. The variation of the AC conductivity with frequency at different temperatures obeys the Almond and West universal law.     

EPR and optical absorption studies of Cu<Superscript>2+</Superscript> ions in [ZnPd(CN)<Subscript>4</Subscript>(C<Subscript>4</Subscript>H<Subscript>12</Subscript>N<Subscript>2</Subscript>O<Subscript>2</Subscript>)] single crystals

A Cu²⁺-doped single crystal of catena-trans-bis(N-(2-hydroxyethyl)-ethylenediamine) zinc(II)-tetra-m-cyanopaladate(II) [ZnPd(CN)₄(C₄H₁₂N₂O₂)] complex has been investigated by electron paramagnetic resonance (EPR) technique at room temperature. EPR spectra indicate that Cu²⁺ ions substitute for magnetically equivalent Zn²⁺ ions and form octahedral complexes in [ZnPd(CN)₄(C₄H₁₂N₂O₂)] hosts. The crystal field affecting the Cu²⁺ ion is nearly axial. The optical absorption studies show two bands at 322 nm (30864 cm⁻¹) and 634 nm (15337 cm⁻¹) which confirm the axial symmetry. The spin Hamiltonian parameters and the relevant wave function are determined.     

Polarized spectral properties of Er<Superscript>3+</Superscript> ions in NaGd(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

Polarized spectral properties of Er³⁺:NaGd(WO₄)₂ single crystal are reported. The crystal was grown by the Czochralski method. The Judd–Ofelt theory was applied to analyze the polarized absorption spectra and then calculate the spontaneous emission probabilities, radiative lifetimes, and branching ratios. Fluorescence decay curves of the ⁴ I _13/2, ⁴ I _11/2, and ⁴ S _3/2 multiplets for the Er³⁺ ions were measured. Stimulated emission cross-sections of the ⁴ I _13/2→⁴ I _15/2 transition obtained by the Fuchtbauer–Ladenberg formula and the reciprocity method were compared. Multi-phonon relaxation rates of the crystal were estimated. Green up-conversion fluorescence around 531 and 552 nm was observed, and the possible up-conversion mechanisms were proposed. PACS 78.20.-e; 42.70.Hj     

Thermal and optical properties of Tm<Superscript>3+</Superscript>:NaLa(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

A Tm³⁺-doped NaLa(WO₄)₂ single crystal with a dimension of Φ20 mm×40 mm was grown by the Czochralski method. Anisotropic thermal expansion coefficients of this crystal were investigated. Polarized absorption spectra, emission spectra and decay curve were recorded at room temperature. The absorption and emission cross-section were presented. Based on the Judd–Ofelt analysis, we obtained the three intensity parameters: Ω₂=10.21×10^-20, Ω₄=2.66×10^-20, and Ω₆=1.46×10^-20 cm². The radiative probabilities, radiative lifetimes, and branch ratios of Tm³⁺:NaLa(WO₄)₂ were calculated, too. Luminescence lifetime of the ³ H ₄ level was measured to be 220 μs. The stimulated emission cross-section for the ³ F ₄→³ H ₆ transition were determined using the reciprocity method, potential laser gain for this transition were also investigated, the gain curves implied that the tunable range is up to 200 nm. PACS 42.70.Hj; 78.20.-e     

Thulium doped monoclinic KLu(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> single crystals: growth and spectroscopy

This paper presents the crystal growth and optical characterization of thulium-doped KLu(WO₄)₂ (KLuW). Thulium-doped KLuW macrodefect-free monoclinic single crystals (a^*×b×c≈10×7×15 mm³) were grown by the top seeded solution growth slow cooling method with dopant concentrations of 0.5%, 1%, 3% and 5% atomic in solution. The evolution of unit cell parameters in relation with thulium doping was studied by X-ray powder patterns. Thulium energy levels in the KLuW host were determined by 6 K polarized optical absorption. The Judd–Ofelt parameters determined were Ω₂=9.01×10^-20 cm², Ω₄=1.36×10^-20 cm² and Ω₆=1.43×10^-20 cm². The maximum emission cross section for the 1.9 μm emission, calculated by Füchtbauer–Ladenburg method, is 1.75×10^-20 cm², at 1845 nm with E//N_m. The intensity decay time from the emitting levels ¹ G ₄ and ³ H ₄ levels in relation to the concentration were studied. For the lowest thulium concentration, the measured decay times from ¹ G ₄ and ³ H ₄ emitting levels are 140 μs and 230 μs, respectively. PACS 42.55.Rz; 78.20.-e; 78.55.-m     

Spectroscopy and laser properties of Tm<Superscript>3+</Superscript>:KY(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

The polarized absorption spectra of Tm³⁺-doped potassium yttrium tungstate (Tm:KY(WO₄)₂) crystal at room temperature were measured. The emission spectrum and lifetime of the ³ F ₄ excited state were determined. Using standard and modified Judd–Ofelt theories, the intensity parameters and the radiative lifetimes were calculated and good agreement with the experimental results was obtained for both theories. Continuous-wave laser operation in Tm:KYW crystal under laser diode pumping at 802 nm and 1750 nm was demonstrated with slope efficiency of 53% and 28% and output power of about 555 mW and 86 mW, respectively. PACS 42.55.Xi; 42.60.Pk; 42.70.Hj     

Thermally stimulated recombination processes and luminescence in Li<Subscript>6</Subscript>(Y,Gd,Eu)(BO<Subscript>3</Subscript>)<Subscript>3</Subscript> crystals

The thermally stimulated recombination processes and luminescence in crystals of the lithium borate family Li₆(Y,Gd,Eu)(BO₃)₃ have been investigated. The steady-state luminescence spectra under X-ray excitation (X-ray luminescence spectra), the temperature dependences of the X-ray luminescence intensity, and the glow curves for the Li₆Gd(BO₃)₃, Li₆Eu(BO₃)₃, Li₆Y_0.5Gd_0.5(BO₃)₃: Eu, and Li₆Gd(BO₃)₃: Eu compounds have been measured in the temperature range 90–500 K. In the X-ray luminescence spectra, the band at 312 nm corresponding to the ⁶ P _J → ⁸ S _7/2 transitions in the Gd³⁺ ion and the group of lines at 580–700 nm due to the ⁵ D ₀ → ⁷ F _J transitions (J = 0–4) in the Eu³⁺ ion are dominant. For undoped crystals, the X-ray luminescence intensity of these bands increases by a factor of 15 with a change in the temperature from 100 to 400 K. The possible mechanisms providing the observed temperature dependence of the intensity and their relation to the specific features of energy transfer of electronic excitations in these crystals have been discussed. It has been revealed that the glow curves for all the crystals under investigation exhibit the main complex peak with the maximum at a temperature of 110–160 K and a number of weaker peaks with the composition and structure dependent on the crystal type. The nature of shallow trapping centers responsible for the thermally stimulated luminescence in the range below room temperature and their relation to defects in the lithium cation sublattice have been analyzed.     

Physical property characterization of bulk MgB<Subscript>2</Subscript> superconductor

We report synthesis, structure/micro-structure, resistivity under magnetic field [ρ(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity κ(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples of MgB₂, processed under identical conditions. The compound crystallizes in hexagonal structure with space group P6/mmm. Transmission electron microscopy (TEM) reveals electron micrographs showing various types of defect features along with the presence of 3–4 nm thick amorphous layers forming the grain boundaries of otherwise crystalline MgB₂. Raman spectra of the compound at room temperature exhibited characteristic phonon peak at 600 cm^-1. Superconductivity is observed at 37.2 K by magnetic susceptibility χ(T), resistivity ρ(T), thermoelectric power S(T), and thermal conductivity κ(T) measurements. The power law fitting of ρ(T) give rise to Debye temperature (Θ_D) at 1400 K which is found consistent with the theoretical fitting of S(T), exhibiting Θ _D of 1410 K and carrier density of 3.81 × 10²⁸/m³. Thermal conductivity κ(T) shows a jump at 38 K, i.e., at T_c, which was missing in some earlier reports. Critical current density (J_c) of up to 10⁵ A/cm² in 1–2 T (Tesla) fields at temperatures (T) of up to 10 K is seen from magnetization measurements. The irreversibility field, defined as the field related to merging of M(H) loops is found to be 78, 68 and 42 kOe at 4, 10 and 20 K respectively. The superconducting performance parameters viz. irreversibility field (H_irr) and critical current density J_c(H) of the studied MgB₂ are improved profoundly with addition of nano-SiC and nano-diamond. The physical property parameters measured for polycrystalline MgB₂ are compared with earlier reports and a consolidated insight of various physical properties is presented.     

InTaO<Subscript>4</Subscript>-based nanostructures synthesized by reactive pulsed laser ablation

Nanostructured Ni-doped indium–tantalum–oxides (InTaO₄) were synthesized by a reactive pulsed laser ablation process, aiming at the final goal of direct splitting of water under visible sunbeam irradiation. The third harmonics beam of a Nd:YAG laser was focused onto a sintered In_0.9Ni_0.1TaO_4−δ target in pure oxygen background gases (0.05–1.00 Torr). Increasing the oxygen gas pressure, via thin films having nanometer-sized strong morphologies, single-crystalline nanoparticles were synthesized in the reactive vapor phases. The nanostructured deposited materials have the monoclinic layered wolframite-type structure of bulk InTaO₄, without oxygen deficiency.     

Characterization of Y<Subscript>2</Subscript>BaCuO<Subscript>5</Subscript> nanoparticles synthesized by nano-emulsion method

Nanoscale yttrium–barium–copper oxide (Y₂BaCuO₅, Y211) particles were synthesized using the emulsion method and the solution method. The basic water-in-oil (w/o) emulsion system consisted of n-octane (continuous oil phase), cetyltrimethylammonium bromide (cationic surfactant), butanol (cosurfactant) and water. The composition of the emulsion system was varied and characterized by measuring the conductivity of the solutions and droplet size. The droplet size of emulsion was determined by using the dynamic light scattering method. The water content, cosurfactant content, and surfactant/n-octane ratio affected the droplet size which was in the range of 3–8 nm, and hence the w/o emulsion system was referred to as a nano-emulsion system. A model was used to verify the droplet size. The influence of salt (Y₂(NO₃)₃) content on the droplet size was investigated and the addition of salt reduced the droplet size. The effects of reaction time and temperature on the Y211 particle sizes were also investigated. The particles were characterized using the TEM, SEM, and XRD. Nanoparticles produced by the nano-emulsion method were calcined at 850°C to form the Y211 phase as compared to solid state processing temperature of 1050°C. Based on the TEM analysis, the average diameter of the Y211 particles produced using the nano-emulsion method was in the range of 30–100 nm. The effect of adding 15% Y211 nanoparticles to the superconductor YBCO-123 as flux pinning centers, was investigated, and the transition temperature was reduced by 3 K.     

Spectral and kinetic characteristics of CdI<Subscript>2</Subscript> and CdI<Subscript>2</Subscript>:Pb scintillators

We have studied the effect of lead dopant on the optical absorption, photoluminescence, and x-ray luminescence spectra, and the scintillation characteristics of CdI₂ at room temperature. The crystals for the study were grown by the Stockbarger-Bridgman method. Activation of CdI₂ from the melt by the compound PbI₂ leads to the appearance in the absorption spectra in the near-edge region of an activator band at 395–405 nm, which is interpreted as an A band connected with electronic transitions from the ¹S₀ state to the ³P₁ levels in the Pb²⁺ ion. For x-ray excitation, CdI₂:Pb²⁺ crystals with optimal dopant concentration (∼1.0 mol%) are characterized by a light yield with maximum in the 570–580 nm region that is an order of magnitude higher than for CdI₂ crystals in the 490–500 nm band. For α excitation, the radioluminescence kinetics for cadmium iodide is characterized by a very short (∼0.3 nsec) rise time and fast decay of luminescence, with τ₁ ≈ 4 nsec and τ₂ = 10–76 nsec. Depending on the conditions under which the crystals were obtained, the fast component fraction is 95%–99%. The crystal is characterized by a similar scintillation pulse in the case of excitation by x-ray pulses. The radioluminescence pulse shape for CdI₂:Pb in the decay stage is predominantly exponential, with luminescence decay time constants τ₁ ≈ 10 nsec and τ₂ = 200–250 nsec. This system is characterized by low afterglow, at the level for the Bi₄G₃O₁₂ scintillator. We have demonstrated the feasibility of using CdI₂:Pb as a scintillator for detecting α particles. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 75, No. 6, pp. 825–830, November–December, 2008.