Synthesis of molybdenum silicide by both ion implantation and ion beam assisted deposition

Two groups of Mo/Si films were deposited on surface of Si(1 0 0) crystal. The first group of the samples was prepared by both ion beam assisted deposition (IBAD) and metal vapor vacuum arc (MEVVA) ion implantation technologies under temperatures from 200 to 400 °C. The deposited species of IBAD were Mo and Si, and different sputtering Ar ion densities were selected. The mixed Mo/Si films were implanted by Mo ion with energy of 94 keV, and fluence of Mo ion was 5 × 10¹⁶ ions/cm². The second group of the samples was prepared only by IBAD under the same test temperature range. The Mo/Si samples were analyzed by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), sheet resistance, nanohardness, and modulus of the Mo/Si films were also measured. For the Mo/Si films implanted with Mo ion, XRD results indicate that phase of the Mo/Si films prepared at 400 and 300 °C was pure MoSi₂. Sheet resistance of the Mo/Si films implanted with Mo ion was less than that of the Mo/Si films prepared without ion implantation. Nanohardness and modulus of the Mo/Si films were obviously affected by test parameters.     

Comparing the chemical properties of evaporated and sputtered niobium films on oxidized Si(1 0 0) wafers - preparation of oxynitride films

Five hundred nanometers of niobium films have been deposited on silicon(1 0 0) wafers with 100 or 300 nm thermally grown oxide by electron beam evaporation and DC magnetron sputtering. SEM and AFM investigations revealed smaller crystallites and rougher surfaces for the evaporated films. The differences in film morphology resulted in lower reflection intensities in XRD for the as-deposited evaporated films. In order to investigate the influence of the structural properties on their chemical reactivities, in a first set of experiments the films were nitrided with molecular nitrogen by rapid thermal processing (RTP) at varying temperatures. In another set of experiments after nitridation in nitrogen at 1000 °C an oxidation step in molecular oxygen at varying temperatures followed. The films showed different reactivities, leading to different rates of nitridation and oxidation. Sputtered films were less reactive than the evaporated films, deduced from the sequence of reaction products dependent on reaction temperature. XRD data indicated that oxynitrides have formed. Elemental depth profiles were measured by secondary ion mass spectrometry (SIMS).     

Efficient field emission from coiled carbon nano/microfiber on copper substrate by dc-PECVD

Crystalline coiled carbon nano/micro fibers in thin film form have been synthesized via direct current plasma enhanced chemical vapor deposition (PECVD) on copper substrates with acetylene as a carbon precursor at 10 mbar pressure and 750 °C substrate temperature. The as-prepared samples were characterized by X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). XRD pattern as well as selected area electron diffraction (SAED) pattern showed that the samples were crystalline in nature. SEM and HRTEM studies showed that as synthesized coiled carbon fibers are having average diameter ∼100 nm and are several micrometers in length. The as-prepared samples showed moderately good electron field emission properties with a turn-on field as low as 1.96 V/μm for an inter-electrode distance 220 μm. The variation of field emission properties with inter-electrode distance has been studied in detail. The field emission properties of the coiled carbon fibrous thin films are compared with that of crystalline multiwalled carbon nanotubes and other carbon nanostructures.     

Preparation of nanocone ZnO thin film and its aging effect of photoluminescence

In this work, a nanocone ZnO thin film was prepared by electron beam evaporation on a Si (1 0 0) substrate. The structural properties of the film were investigated by X-ray diffraction (XRD), atomic force microscopy and laser Raman scattering, respectively. The aging effect of the nanocone ZnO thin film was studied by photoluminescence spectra. The structural analyses show that the prepared ZnO thin film has a hexagonal wurtzite structure and is preferentially oriented along the c-axis perpendicular to the substrate surface. The photoluminescence spectra show that with the increase of aging time, the green emission of the nanocone ZnO thin film gradually decreases while the ultraviolet emission somewhat increases. The reason for this phenomenon is likely that the green-emission-related oxygen vacancies in the film are gradually filled up. The Raman scattering analyses also suggest that the intensity of the Raman peak related to oxygen vacancies in the nanocone ZnO thin film declines after the film is aged in air for a year. Therefore, the authors think the green emission is mainly connected with oxygen vacancy defects.     

Synthesis of silicon carbide films by combined implantation with sputtering techniques

Silicon carbide (SiC) films were synthesized by combined metal vapor vacuum arc (MEVVA) ion implantation with ion beam assisted deposition (IBAD) techniques. Carbon ions with 40 keV energy were implanted into Si(1 0 0) substrates at ion fluence of 5 × 10¹⁶ ions/cm². Then silicon and carbon atoms were co-sputtered on the Si(1 0 0) substrate surface, at the same time the samples underwent assistant Ar-ion irradiation at 20 keV energy. A group of samples with substrate temperatures ranging from 400 to 600 °C were used to analyze the effect of temperature on formation of the SiC film. Influence of the assistant Ar-ion irradiation was also investigated. The structure, morphology and mechanical properties of the deposited films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and nanoindentation, respectively. The bond configurations were obtained from IR absorption and Raman spectroscopy. The experimental results indicate that microcrystalline SiC films were synthesized at 600 °C. The substrate temperature and assistant Ar-ion irradiation played a key role in the process. The assistant Ar-ion irradiation also helps increasing the nanohardness and bulk modulus of the SiC films. The best values of nanohardness and bulk modulus were 24.1 and 282.6 GPa, respectively.     

Study on the composition and phase change of BaO/Hf/Mo under high temperature

Hafnium films were deposited onto the molybdenum grids by radio-frequency magnetron sputtering from an Hf target in argon gas. Emission current of Mo grids coated with and without Hf film during the lifetime testing, which were contaminated by active electron-emission substances (i.e. Ba or BaO) from the cathode, were measured using an analogous-diode method. The results show that emission current from the Mo grid coated with Hf film is much less than that from the Mo grid without Hf film. The BaO layer was deposited on Hf/Mo substrates by chemical method in order to simulate the working conditions of the grids contaminated by electron-emission substances from the cathode. The suppression mechanism of electron emission from the Mo grid coated with Hf film is discussed according to the experimental results and the calculation of the reaction free energy.     

The influence of Mn content on luminescence properties in Mn-doped ZnO films deposited by ultrasonic spray assisted chemical vapor deposition

Mn-doped ZnO (Zn_1−xMn_xO, 0 ≤ x ≤ 0.1) films are prepared by an ultrasonic spray assisted chemical vapor deposition method. X-ray diffraction and Raman scattering show that all the Zn_1−xMn_xO films are good wurtzite structures without any impurity phases. Cathodoluminescence spectra show that ultraviolet emission and green luminescence can be observed. The intensity of ultraviolet emission decreases with the increment of x, while the intensity of green luminescence increases with the increment of x when x ≤ 0.02. However, when x (x > 0.02) is further increased, the intensity of green luminescence decreases gradually, and the green luminescence disappears when x is above 0.075. We consider that the change of the luminescence is related to the competition between the radiative recombination and the non-radiative recombination.     

Microstructural characterization of Ti-C-N thin films prepared by reactive crossed beam pulsed laser deposition

In this work, Raman spectroscopy has been used to characterize Ti-C-N thin films in order to obtain information about the microstructure of the deposited materials, and in particular to study the effects due to the carbon incorporation into the TiN lattice. Ti-C-N thin films were prepared using a crossed plasma configuration in which the ablation of two different targets, titanium and carbon, in a reactive atmosphere was performed. With this configuration, the carbon content in the films was varied in an easy way from 5.0 at% to 40.0 at%. Thin film composition was determined from Non-Rutherford Backscattering Spectroscopy (NRBS) measurements. X-ray photoelectron spectroscopy and X-Ray diffraction measurements were also carried out in order to characterize the films in more detail, with this being used to give support to the interpretation of the Raman spectra. The Raman results revealed that at lower carbon concentrations a solid solution Ti(C, N) is formed, whilst at higher carbon concentrations a nanocomposite, consisting of nanocrystalline TiCN and TiC immersed in an amorphous carbon matrix is obtained.     

Structural and optical characterization of Ce-doped Gd2SiO5 films by sol-gel technique

Cerium-doped Gd₂SiO₅ (GSO:Ce) films have been prepared on (1 1 1) silicon substrates by the sol-gel technique. Annealing was performed in the temperature range from 400 to 1000 °C. X-ray diffraction (XRD), and atomic force microscopy (AFM) were used to investigate the structure and morphology of GSO:Ce films. Results showed that GSO:Ce film starts to crystallize at about 600 °C, GSO:Ce films have a preferential (0 2 1) orientation, as the annealing temperature increase, the (0 2 1) peak intensity increases, the full width of half maximum (FWHM) decreases, and the grain size of GSO:Ce films increases. Emission spectra of GSO:Ce films were measured, results exhibit the characteristic blue emission peak at 427 nm.     

Heavy atomic-layer doping of B in low-temperature Si epitaxial growth on Si(1 0 0) by ultraclean low-pressure chemical vapor deposition

Electrical characteristics of B atomic-layer doped Si epitaxial films on Si(1 0 0) formed by B atomic-layer formation on Si(1 0 0) at 180 °C and subsequent capping Si deposition at 500 °C using ultraclean low-pressure chemical vapor deposition were investigated. From evaluation results of carrier concentration in the films, by low-temperature SiH₄ exposure at 180-300 °C before the capping Si deposition at 500 °C, 70% improvement of B electrical activity was confirmed, and it is suggested that lowering the temperatures for B atomic-layer formation on Si(1 0 0) as well as SiH₄ exposure before the capping Si deposition is effective to suppress B clustering and to achieve B atomic-layer doped Si films with extremely high carrier concentration.     

Characterization of CdTe films with in situ CdCl2 treatment grown by a simple vapor phase deposition technique

A unique vapor phase deposition (VPD) technique was designed and built to achieve in situ CdCl₂ treatment of CdTe film. The substrate temperature was 400 °C, and the temperature of CdTe mixture with CdCl₂ source was 500 °C. The structural and morphological properties of CdTe have been studied as a function of wt.% CdCl₂ concentration by using X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), scanning electron microscopy (SEM) and atomic force microscopy (AFM). XRD measurements show that the presence of CdCl₂ vapor induces (1 1 1)-oriented growth in the CdTe film. SEM measurements have shown enhance growth of grains, in the presence of CdCl₂. From AFM the roughness of the films showed a heavy dependence on CdCl₂ concentration. In the presence of 4% CdCl₂ concentration, the CdTe films roughness has a root mean square (rms) value of about 275 Å. This value is about 831 Å for the non-treated CdTe films.     

Spin-deposited nanocrystalline lithium ferrite thin films: Fabrication and characterization

Thin films of lithium ferrite (with general composition Li_0.5Fe_2.5O₄) were fabricated at low temperatures (up to 650 °C) by citrate-route using spin-deposition technique. Deposited films consisted of nanometer-sized grains as evidenced by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques. XRD patterns for annealed films showed broad peaks exhibiting a spinel phase. Size of nanocrystallites is estimated to be 3-7 nm using Scherrer's equation. Average grain size ∼8.5 nm is observed from TEM images of films annealed at 650 °C. Scanning electron micrographs show the formation of spherical aggregates of around 130 nm in diameter. The AFM analysis clearly evidenced the development of nanograins even at low (∼500 °C) annealing temperatures. Significant decrease in complex dielectric permittivity (∈′ − j∈″) with frequency is observed in the low frequency (100 Hz-1 MHz) as well as in X-band microwave frequency (8-12 GHz) region. ∈′ is found to be in the range of 15.7-33.9 in low frequency region, whereas in X-band microwave frequency region, it is found to lie between 3.9 and 4.9. Similarly, ∈″ is found to be 0.16-5.9 in the low frequency region, and 0.002-0.024 in the X-band microwave frequency region. Room temperature dc resistivity of these films is estimated to lie in the range of 10⁶-10⁸ Ω cm. These results strongly suggest that citrate-route processed nanocrystalline lithium ferrite thin films are promising candidates for monolithic microwave integrated circuits (MMICs).     

Crystallization and surface morphology evolution of erbium fluoride films on different substrates

Erbium fluoride (ErF₃) films were thermally deposited on Ge(1 1 1), Si(0 0 1) and copper mesh grid with different substrate temperature. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the structure and morphology of the films. The structure of ErF₃ films deposited on germanium and silicon changed from amorphous to crystalline with increasing the substrate temperature, while the crystallization temperature of the films on silicon is higher than that of on germanium. The infrared optical properties of the films change greatly with the evolution of crystal structure. It is also found that the morphology of ErF₃ film on Ge(1 1 1) at 200 °C is modulated by the stress between the substrate and film. The SEM and TEM results confirmed that the ErF₃ films on copper mesh grid were crystalline even at 100 °C. Interestingly, the ErF₃ films show flower-like surface morphology when deposited on copper mesh at 200 °C. The crystallization temperature (T_c) of ErF₃ films on the three substrates has the relation which is which is induced by the wetting angle of ErF₃ films on different substrates.     

Growth of thin Fe(0 0 1) films for terahertz emission experiments

The electrical and magnetic properties of thin iron (Fe) films have sparked significant scientific interest. Our interest, however, is in the fundamental interactions between light and matter. We have discovered a novel application for thin Fe films. These films are sources of terahertz (THz) radiation when stimulated by an incident laser pulse. After intense femtosecond pulse excitation by a Ti:sapphire laser, these films emit picosecond, broadband THz frequencies. The terahertz emission provides a direct measure of the induced ultrafast change in magnetization within the Fe film. The THz generation experiments and the growth of appropriate thin Fe films for these experiments are discussed. Several criteria are used to select the substrate and film growth conditions, including that the substrate must permit the epitaxial growth of a continuous, monocrystalline or single crystal film, yet must also be transparent to the emitted THz radiation. An Fe(0 0 1) film grown on the (0 0 1) surface of a magnesium oxide (MgO) substrate makes an ideal sample. The Fe films are grown by physical vapor deposition (PVD) in an ultrahigh vacuum (UHV) system. Low energy electron diffraction (LEED) and Auger electron spectroscopy (AES) are used to characterize the Fe(0 0 1) films. Two substrate surface preparation methods are investigated. Fe(0 0 1) films grown on MgO(0 0 1) substrates that are used as-received and films grown on MgO(0 0 1) substrates that have been UV/ozone-cleaned ex vacuo and annealed in vacuo produce the same results in the THz generation experiments. Either substrate preparation method permits the growth of samples suitable for the THz emission experiments.     

Photoluminescence properties of nitrogen-doped ZnO films deposited on ZnO single crystal substrates by the plasma-assisted reactive evaporation method

Photoluminescence (PL) spectra of nitrogen-doped ZnO films (ZnO:N films) grown epitaxially on n-type ZnO single crystal substrates by using the plasma-assisted reactive evaporation method were measured at 5 K. In PL spectra, free exciton emission at about 3.375 eV was very strong and emissions at 3.334 and 3.31 eV were observed. These two emissions are discussed in this paper. The nitrogen concentration in ZnO:N films measured by secondary ion mass spectroscopy was 10^19-20 cm⁻³. Current-voltage characteristics of the junction consisting of an n-type ZnO single crystal substrate and ZnO:N film showed good rectification. Also, ultraviolet radiation and visible light were emitted from this junction under a forward bias at room temperature. It is therefore thought that ZnO:N films have good crystallinity and that doped nitrogen atoms play a role as acceptors in ZnO:N films to form a good pn junction. From these phenomena and the excitation intensity dependency of PL spectra, emissions at 3.334 and 3.31 eV were assigned to neutral acceptor-bound exciton (A⁰X) emission and a donor-acceptor pair (DAP) emission due to doped nitrogen, respectively.     

Pulsed laser deposition of polyhydroxybutyrate biodegradable polymer thin films using ArF excimer laser

We demonstrated the pulsed laser deposition (PLD) of high quality films of a biodegradable polymer, the polyhydroxybutyrate (PHB). Thin films of PHB were deposited on KBr substrates and fused silica plates using an ArF (λ = 193 nm, FWHM = 30 ns) excimer laser with fluences between 0.05 and 1.5 J cm⁻². FTIR spectroscopic measurements proved that at the appropriate fluence (0.05, 0.09 and 0.12 J cm⁻²), the films exhibited similar functional groups with no significant laser-produced modifications present. Optical microscopic images showed that the layers were contiguous with embedded micrometer-sized grains. Ellipsometric results determined the wavelength dependence (λ ∼ 245-1000 nm) of the refractive index and absorption coefficient which were new information about the material and were not published in the scientific literature. We believe that our deposited PHB thin films would have more possible applications. For example to our supposal the thin layers would be applicable in laser induced forward transfer (LIFT) of biological materials using them as absorbing thin films.     

Influence of complexing agent on the electrodeposited Co-Pt-W magnetic thin films

Complexing agents are often used to improve the quality of electrodeposited alloys. Influence of different complexing agents with hydroxycarboxylic acid group on the electrodeposited Co-Pt-W thin films has been investigated. Cathodic polarization curves show that the polarization behaviors of electroplating bath with different complexing agents are very different. Surface morphology, phase composition and magnetic properties are observed by means of FESEM, XRD and vibrating sample magnetometer (VSM), respectively. It has been found out that, if citrate was used as complexing agent, the Co-Pt-W thin films were homogeneous and the granular crystals with the average grain size of 2 μm have been observed. Co-Pt-W thin films exhibited hexagonal close packed (hcp) lattice and strong perpendicular anisotropic magnetic behavior (H_c⊥ = 215.5 kA/m; H_c∥ = 55.4 kA/m). In the presence of gluconate, needle-like deposits were obtained and a strong face centered cubic (fcc(1 1 1)) texture was measured. The Co-Pt-W thin films showed isotropic magnetic behavior. In the case of tartate and malate, the coexistence of needle-like deposits and cellular deposits appeared. The XRD patterns showed that the mixed fcc and hcp phase formed. Perpendicular anisotropic magnetic behaviors of thin films, from malate or tartate baths, were not obvious.     

Spatially resolved Raman spectroscopy evaluation of residual stresses in 3C-SiC layer deposited on Si substrates with different crystallographic orientations

Raman scattering studies were performed on hot-wall chemical vapor deposited (heteroepitaxial) silicon carbide (SiC) films grown on Si substrates with orientations of (1 0 0), (1 1 1), (1 1 0) and (2 1 1), respectively. Raman spectra suggested that good quality cubic SiC single crystals could be obtained on the Si substrate, independent of its crystallographic orientation. Average residual stresses in the epitaxially grown 3C-SiC films were measured with the laser waist focused on the epilayer surface. Tensile and compressive residual stresses were found to be stored within the SiC film and in the Si substrate, respectively. The residual stress exhibited a marked dependence on the orientation of the substrate. The measured stresses were comparable to the thermal stress deduced from elastic deformation theory, which demonstrates that the large lattice mismatch between cubic SiC and Si is effectively relieved by initial carbonization. The confocal configuration of the optical probe enabled a stress evaluation along the cross-section of the sample, which showed maximum tensile stress magnitude at the SiC/Si interface from the SiC side, decreasing away from the interface in varied rate for different crystallographic orientations. Defocusing experiments were used to precisely characterize the geometry of the laser probe in 3C-SiC single crystal. Based on this knowledge, a theoretical convolution of the in-depth stress distribution could be obtained, which showed a satisfactory agreement with stress values obtained by experiments performed on the 3C-SiC surface.     

A comparative study of field-emission from different one dimensional carbon nanostructures synthesized via thermal CVD system

Different one dimensional (1D) carbon nanostructures, such as carbon nanonoodles (CNNs), carbon nanospikes (CNSs) and carbon nanotubes (CNTs) have been synthesized via thermal chemical vapour deposition (TCVD) technique. The different 1D morphologies were synthesized by varying the substrate material and the deposition conditions. The as-prepared samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). FESEM and TEM images showed that the diameters of the CNNs and CNTs were ∼40 nm while the diameters of the CNSs were around 100 nm. Field emission studies of the as-prepared samples showed that CNSs to be a better field emitter than CNNs, whereas CNTs are the best among the three producing large emission current. The variation of field emission properties with inter-electrode distance has been studied in detail. Also the time dependent field emission studies of all the nanostructures have been carried out.     

Synthesis of bamboo-leaf-shaped ZnO nanostructures by oxidation of Zn/SiO2 composite films deposited with radio frequency magnetron co-sputtering

Bamboo-leaf-shaped ZnO nanostructures were synthesized by oxidation of metal Zn/SiO₂ matrix composite thin films deposited on Si(1 1 1) substrates with radio frequency magnetron co-sputtering. The synthesized bamboo-leaf-shaped ZnO are single crystalline in nature with widths ranging from 30 to 60 nm and lengths of up to 5-10 μm, room temperature photoluminescence spectrum of the nanostructures shows a strong and sharp UV emission band at 372 nm and a weak and broad green emission band at about 520 nm which indicates relatively excellent crystallization and optical quality of the ZnO nanostructures synthesized by this novel method.