Compositional dependence of ferroelectric properties of highly c-axis oriented Bi4−xNdxTi3O12 film capacitors

Highly c-axis oriented neodymium-modified bismuth titanate (Bi_4−xNd_xTi₃O₁₂) films having a variety of neodymium (Nd) contents were successfully grown on Pt/TiO₂/SiO₂/Si(100) substrates using metal-organic sol decomposition. After systematically examining ferroelectric properties of the c-axis oriented Bi_4−xNd_xTi₃O₁₂ film capacitors as a function of the Nd-content, we concluded that the capacitor with x=0.85 had the largest remanent polarization. The Bi_3.15Nd_0.85Ti₃O₁₂ capacitor fabricated using a top Pt electrode showed well-saturated polarization-electric field (P-E) switching curves with the remanent polarization (P_r) of 51 μC/cm² and the coercive field (E_c) of 99 kV/cm at an applied voltage of 10 V. More importantly, the Pt/Bi_3.15Nd_0.85Ti₃O₁₂/Pt capacitor exhibited fatigue-free behavior up to 4.5×10¹⁰ read/write switching cycles at a frequency of 1 MHz. The capacitor also demonstrated an excellent charge-retaining ability and a strong resistance against the imprinting failure.     

Sunlight photocatalytic activity of CdS modified TiO2 loaded on activated carbon fibers

To improve the photocatalytic application performances of TiO₂, in this work, firstly CdS modified Degussa P25 TiO₂ (CdS/TiO₂) composites were prepared by two methods, sol-gel method and precipitation method. Next they, sol-gel-CdS/TiO₂ (sg-CdS/TiO₂) and precipitation-CdS/TiO₂ (pp-CdS/TiO₂), were loaded on activated carbon fibers (ACFs) by dip-coating method using the sodium carboxymethyl cellulose as adhesives. The composites were characterized by XRD, UV-vis absorbance spectra, SEM, EDS and BET. The photocatalytic activities under sunlight were investigated by the degradation of methylene blue. The results showed that CdS/TiO₂ composites were mainly composed of anatase-TiO₂ and little CdS cubic phases. The absorption wavelengths of sg-CdS/TiO₂ and pp-CdS/TiO₂ composites were extended to 590 nm and 740 nm, respectively. The absorption edge had a pronounced ‘red shift’. From EDS analysis, the elemental contents of CdS/TiO₂ were mainly Ti and O and a small quantity of S and Cd. CdS/TiO₂ loaded on ACFs were in the form of small clusters, but not very uniform; compared with the original ACFs, the surface area and pore volume of CdS/TiO₂/ACFs decreased slightly, respectively, while the average pore diameter was not changed. The photodegradation rate of methylene blue under sunlight with CdS/TiO₂/ACFs composites was markedly higher than that of P25-TiO₂/ACFs, and the effect of pp-CdS/TiO₂/ACFs composites was better than that of sg-CdS/TiO₂/ACFs, when irradiated for 180 min, and the photodegradation rate of methylene blue reached to 90.1%. The photodegradation kinetics of the methylene blue fitted with the Langmuir-Hinshelwood equation. The apparent reaction rate constants of sg-CdS/TiO₂/ACFs and pp-CdS/TiO₂ were 0.0105 min⁻¹ and 0.0146 min⁻¹, respectively, which were about 1.3-1.7 times as large as that of P25-TiO₂/ACFs.     

Ferroelectric properties of highly c-axis oriented Bi4−xLaxTi3O12 film-based capacitors

Highly c-axis oriented lanthanum-modified bismuth titanate (Bi_4−xLa_xTi₃O₁₂) films having a variety of lanthanum (La) contents were grown on Pt/TiO₂/SiO₂/Si(100) substrates using metal-organic sol deposition and subsequent annealing at 650 °C for 1 h. After systematically examining the ferroelectric properties of Bi_4−xLa_xTi₃O₁₂ films as a function of the La-content, it was concluded that the film with x=0.85 had the largest remanent polarization in the direction parallel to the c-axis. The Pt/Bi_3.15La_0.85Ti₃O₁₂/Pt capacitor showed a well-saturated polarization-electric field (P-E) switching curve with the switching remanent polarization (2P_r) value of 33 μC/cm² and the coercive field (E_c) of 68 kV/cm at an applied voltage of 10 V. More importantly, the capacitor exhibited fatigue-free behavior up to 6.5×10¹⁰ read/write switching cycles at a frequency of 1 MHz. The capacitor also demonstrated an excellent charge-retaining ability and a strong resistance against the imprinting failure.     

X-ray photoelectron spectroscopic investigations on cubic BaTiO3, BaTi0.9Fe0.1O3 and Ba0.9Nd0.1TiO3 systems

X-ray photoelectron spectroscopic (XPS) studies were carried out on wet-chemically synthesized cubic BaTiO₃, Ba_0.9Nd_0.1TiO₃ and BaTi_0.9Fe_0.1O_3−δ powders. The compounds were prepared by hydrothermal and gel to crystallite conversion technique; and phases formed readily at 420 K. The phase purity of the powders was confirmed from X-ray diffractometry. Chemical state and chemical environment of the constituent elements in the compositions were examined by XPS. Ba²⁺ was found to exist in two different chemical environments in these titanates. The Ti 2p_3/2 photoelectron peak in BaTi_0.9Fe_0.1O_3−δ was found to be broadened after Fe³⁺ substitution. Any resolvable broadening was not observed distinctly in the Ti 2p peak for Ba_0.9Nd_0.1TiO₃, unsintered BaTiO₃ and BaTiO₃ annealed in hydrogen (8% H₂ + Ar) at 1000 K. The prevalence of mixed-valent titanium and iron in BaTi_0.9Fe_0.1O_3−δ composition was evident from the XPS results and was further supported by the enhanced electrical conductivity at 298-550 K for BaTi_0.9Fe_0.1O_3−δ in comparison to BaTiO₃ and Ba_0.9Nd_0.1TiO₃. Hydroxyl incorporation was facilitated by substituting Nd³⁺ in Ba-sublattice. The presence of hydroxyls was observed from the broadening of the O 1s peak in XPS studies of the compounds.     

Reduced dielectric loss and leakage current in CaCu3Ti4O12/SiO2/CaCu3Ti4O12 multilayered films

The CaCu₃Ti₄O₁₂/SiO₂/CaCu₃Ti₄O₁₂ (CCTO/SiO₂/CCTO) multilayered films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition method. It has been demonstrated that the dielectric loss and the leakage current density were significantly reduced with the increase of the SiO₂ layer thickness, accompanied with a decrease of the dielectric constant. The CCTO film with a 20 nm SiO₂ layer showed a dielectric loss of 0.065 at 100 kHz and the leakage current density of 6×10⁻⁷ A/cm² at 100 kV/cm, which were much lower than those of the single layer CCTO films. The improvement of the electric properties is ascribed to two reasons: one is the improved crystallinity; the other is the reduced free carriers in the multilayered films.     

Reactivity of (H)(e) color centers at the MgO surface: formation of O2 and N2 radical anions

We have considered the interaction of O₂ and N₂ molecules with electrons trapped at the surface of MgO by performing embedded cluster DFT calculations. Trapped electrons at the surface of MgO react instantaneously with O₂ and N₂ leading to the formation of the corresponding O₂⁻ and N₂⁻ molecular anions stabilized at specific surface sites. So far, the atomistic model for this process was based on the idea that the electrons are trapped at oxygen vacancies, the F_S⁺ centers. Recently, it has been shown that morphological sites at the MgO surface like a reverse corner, a step or a corner, can adsorb hydrogen and stabilize (H⁺)(e⁻) pairs giving rise to a new class of paramagnetic color centers. Here we show that these centers exhibit reactivity towards O₂ and N₂, which is fully consistent with the experimental observations, providing further support to the new model of electron traps at the MgO surface.     

Photocatalytic oxidation of natural organic adsorbates on anatase TiO2 films observed by infrared adsorption spectroscopy with a multiple internal reflection geometry

Photocatalytic oxidation of organic adsorbates on anatase TiO₂ films has been examined in different atmospheres of humid air, dry air and vacuum. The photocatalytic oxidation was observed by IR absorption spectroscopy (IRAS) with a multiple-internal-reflection (MIR) geometry. The photocatalytic oxidation is the fastest in the air at a humidity of 70% where oxygen and water vapor are consuming to produce OH radicals and O₂⁻ anions on the TiO₂ surface with the UV exposure. In the dry air, a rate of the photocatalytic oxidation is almost 30% of that in the humid air, where only O₂⁻ anions oxidize the organic adsorbates. In vacuum, on the other hand, it is negligible, which suggests that adsorbed H₂O molecules do not play an important role in the photocatalytic reaction. It is suggested that an addition of the water vapor is necessary to achieve the higher catalytic activity.     

Ferroelectric properties of bilayer structured Pb(Zr0.52Ti0.48)O3/SrBi2Ta2O9 (PZT/SBT) thin films on Pt/TiO2/SiO2/Si substrates

Pb(Zr_0.52Ti_0.48)O₃ (PZT) thin films with large remanent polarization and SrBi₂Ta₂O₉ (SBT) thin films with excellent fatigue-resisting characteristic have been widely studied for non-volatile random access memories, respectively. To combine these two advantages_, bilayered Pb(Zr_0.52Ti_0.48)O₃/SrBi₂Ta₂O₉ (PZT/SBT) thin films were fabricated on Pt/TiO₂/SiO₂/Si substrates by chemical solution deposition method. X-ray diffraction patterns revealed that the diffraction peaks of PZT/SBT thin films were completely composed of PZT and SBT, and no other secondary phase was observed. The electrical properties of the bilayered structure PZT/SBT films have been investigated in comparison with pure PZT and SBT films. PZT/SBT bilayered thin films showed larger remanent polarization (2P_r) of 18.37 μC/cm² than pure SBT and less polarization fatigue up to 1 × 10⁹ switching cycles than pure PZT. These results indicated that this bilayered structure of PZT/SBT is a promising material combination for ferroelectric memory applications.     

Antiferromagnetic phase transition in garnet-type AgCa2Co2V3O12 and AgCa2Ni2V3O12

Antiferromagnetic phase transition in two vanadium garnets AgCa₂Co₂V₃O₁₂ and AgCa₂Ni₂V₃O₁₂ has been found and investigated extensively. The heat capacity exhibits sharp peak due to the antiferromagnetic order with the Néel temperature T_N=6.39 K for AgCa₂Co₂V₃O₁₂ and 7.21 K for AgCa₂Ni₂V₃O₁₂, respectively. The magnetic susceptibilities exhibit broad maximum, and these T_N correspond to the inflection points of the magnetic susceptibility χ a little lower than T(χ_max). The magnetic entropy changes from zero to 20 K per mol Co²⁺ and Ni²⁺ ions are 5.31 J K⁻¹ mol-Co²⁺-ion⁻¹ and 6.85 J K⁻¹ mol-Ni²⁺-ion⁻¹, indicating S=1/2 for Co²⁺ ion and S=1 for Ni²⁺ ion. The magnetic susceptibility of AgCa₂Ni₂V₃O₁₂ shows the Curie-Weiss behavior between 20 and 350 K with the effective magnetic moment μ_eff=3.23 μ_B Ni²⁺-ion⁻¹ and the Weiss constant θ=−16.4 K (antiferromagnetic sign). Nevertheless, the simple Curie-Weiss law cannot be applicable for AgCa₂Co₂V₃O₁₂. The complex temperature dependence of magnetic susceptibility has been interpreted within the framework of Tanabe-Sugano energy diagram, which is analyzed on the basis of crystalline electric field. The ground state is the spin doublet state ²E(t₂⁶e) and the first excited state is spin quartet state ⁴T₁(t₂⁵e²) which locates extremely close to the ground state. The low spin state S=1/2 for Co²⁺ ion is verified experimentally at least below 20 K which is in agreement with the result of the heat capacity.     

Synthesis and electronic behaviors of TiO2/carbon clusters/Cr2O3 composite materials

Nano-structured TiO₂/carbon clusters/Cr₂O₃ composite material has been successfully obtained by the microwave treatment of a TiO(acac)/Cr(acac)₃/epoxy resin complex. The compositions of the composite materials were determined using ICP, elemental analysis and surface characterization by SEM-EDX, TEM and XRD. ESR spectral examinations suggest the possibility of an electron transfer in the process of TiO₂ → carbon clusters → Cr₂O₃ with an oxidation site at TiO₂ particles and a reduction site at Cr₂O₃ particles. The preliminary experimental results show that the calcined materials could decompose methylene blue under visible-light irradiation.     

Luminescence spectroscopy of Ti ions in Li2O-CaF2-P2O5 glass ceramics

Li₂O-CaF₂-P₂O₅ glasses mixed with different concentrations of TiO₂ (ranging from 0 to 0.8 mol%) were crystallized at 500 °C. The photo luminescence spectra of these samples excited with the wavelengths corresponding to their absorption edges have been recorded at room temperature. The spectra exhibited an emission band in the wavelength region 470-500 nm. The emission band is identified due to the charge transfer from O²⁻ ion in to empty 3d orbital of octahedrally positioned Ti⁴⁺ ions. The analysis of the results further indicates the highest luminescence efficiency for the glass ceramic sample crystallized with 0.6 mol% of TiO₂.     

Structural, vibrational and dielectric properties of new potassium hydrogen sulfate arsenate: K4(SO4)(HSO4)2(H3AsO4)

A new compound, K₄(SO₄)(HSO₄)₂(H₃AsO₄) was synthesized from water solution of KHSO₄/K₃H(SO₄)₂/H₃AsO₄. This compound crystallizes in the triclinic system with space group P1¯ and cell parameters: a=8.9076(2) Å, b=10.1258(2) Å, c=10.6785(3) Å; α=72.5250(14)°, β=66.3990(13)°, γ=65.5159(13)°, V=792.74(3) Å³, Z=2 and ρ_cal=2.466 g cm⁻³. The refinement of 3760 observed reflections (I>2σ(I)) leads to R₁=0.0394 and wR₂=0.0755. The structure is characterized by SO₄²⁻, HSO₄⁻ and H₃AsO₄ tetrahedra connected by hydrogen bridge to form two types of dimer (H(16)S(3)O₄⁻?S(1)O₄²⁻ and H(12)S(2)O₄⁻?H₃AsO₄). These dimers are interconnected along the [1¯ 1 0] direction by the hydrogen bonds O(3)-H(3)?O(6). They are also linked by the hydrogen bridge assured by the hydrogen atoms H(2), H(3) and H(4) of the H₃AsO₄ group to build the chain S(1)O₄?H₃AsO₄ which are parallel to the “a” direction. The potassium cations are coordinated by eight oxygen atoms with K-O distance ranging from 2.678(2) to 3.354(2) Å.Crystals of K₄(SO₄)(HSO₄)₂(H₃AsO₄) undergo one endothermic peak at 436 K. This transition detected by differential scanning calorimetry (DSC) is also analyzed by dielectric and conductivity measurements using the impedance spectroscopy techniques. The obtained results show that this transition is protonic by nature.     

Preparation of transparent conductive TiO2:Nb thin films by pulsed laser deposition

This study investigated the optical and electrical properties of Nb-doped TiO₂ thin films prepared by pulsed laser deposition (PLD). The PLD conditions were optimized to fabricate Nb-doped TiO₂ thin films with an improved electrical conductivity and crystalline structure. XRD analyses revealed that the deposition at room temperature in 0.92 Pa O₂ was suitable to produce anatase-type TiO₂. A Nb-doped TiO₂ thin film attained a resistivity as low as 6.7 × 10⁻⁴ Ω cm after annealing at 350 °C in vacuum (<10⁻⁵ Pa), thereby maintaining the transmittance as high as 60% in the UV-vis region.     

Synthesis and characterization of TiO2/Fe2O3 core-shell nanocomposition film and their photoelectrochemical property

TiO₂/Fe₂O₃ core-shell nanocomposition film has been fabricated via two-step method. TiO₂ nanorod arrays are synthesized by a facile hydrothermal method, and followed by Fe₂O₃ nanoparticles deposited on TiO₂ nanorod arrays through an ordinary chemical bath deposition. The phase structures, morphologies, particle size, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer. The results confirm that Fe₂O₃ nanoparticles of mean size ca. 10 nm coated on the surface of TiO2 NRs. After depositing Fe₂O₃, UV-vis absorption property is induces the shift to the visible-light range, the annealing temperature of 600 °C is the best condition for UV-vis absorption property of TiO₂/Fe₂O₃ nanocomposite film, and increasing Fe content, optical activity are enhanced one by one. The photoelectrochemical (PEC) performances of the as-prepared composite nanorods are determined by measuring the photo-generated currents under illumination of UV-vis light. The TiO₂ NRs modified by Fe₂O₃ show the photocurrent value of 1.36 mA/cm² at 0 V vs Ag/AgCl, which is higher than those of unmodified TiO₂ NRs.     

Role of Cl ions in photooxidation of propylene on TiO2 surface

The effect of Cl⁻ ions on photooxidation of propylene on TiO₂ semiconductor was investigated. Cl⁻/TiO₂ catalysts were prepared by annealing Degussa P25 TiO₂ in the gas flow of N₂ and Cl₂ under 100-400 °C. The photocatalytic oxidation of propylene was carried out in a continuous flow system, with the chromatograph to analyze the products on line. The experimental results showed that the activity of Cl⁻/TiO₂ catalysts increased as heat-treated temperature decreased. The activity of the sample heat-treated at 100 °C was about two times higher than that of pure TiO₂. Moreover, as to TiO₂, the main product of the propylene photocatalytic oxidation was CO₂, but with Cl⁻/TiO₂ catalysts, not only CO₂ but also trace CO was determined. The adsorbed species on TiO₂ surface before and after reaction were analyzed by X-ray photoelectron spectroscopy (XPS) and thermogravimetric/differential thermal analyses (TG-DTA) coupled to a mass spectrometer (MS). XPS analysis showed that there was Cl⁻ absorbed on the Cl⁻/TiO₂ surface, and the absorption amount of Cl⁻ decreased after the photooxidation reaction of propylene. TG-DTA-MS analysis confirmed chlorine absorbed on the surface of TiO₂ in the form of Cl⁻ ion. These results illuminated that absorbed Cl⁻ on the surface of TiO₂ formed a weak physical absorption on TiO₂ at low temperature, and subsequently participated in the photooxidation of propylene, finally removed from TiO₂ surface.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Photocatalytic abilities of gel-derived P-doped TiO2

P-doped TiO₂ nanoparticles were synthesized through hydrolysis and condensation of Ti(OC₂H₅)₄ with H₃PO₄ additions. Effects of [H₃PO₄]/[Ti(OC₂H₅)₄] molar ratios on the anatase-to-rutile phase transformation, crystallite sizes, surface areas, and photocatalytic abilities of the gel-derived P-doped TiO₂ were investigated. The P-doped TiO₂ nanoparticles prepared by [H₃PO₄]/[Ti(OC₂H₅)₄]=0.03 were composed of anatase monophase even at 900 ^oC and possessed very strong photocatalytic ability. Kinetic studies on the P-doped TiO₂ to photocatalytically decompose methylene blue under irradiation of 365 nm UV light found that the P-doped TiO₂ prepared by [H₃PO₄]/[Ti(OC₂H₅)₄]=0.03 and calcined at 800 ^oC had the specific reaction rates, at 25 °C, k_A,m=0.76 m³/(kg min) (based on the mass of P-doped TiO₂) and k_A,BET=46.2×10⁻⁶ m/min (based on the BET surface area of P-doped TiO₂), which is superior to the performance of a commercial product, P25 (k_A,m=0.22 m³/(kg min) and k_A,BET=4.8×10⁻⁶ m/min).     

Adsorption CO2 on the perfect and oxygen vacancy defect surfaces of anatase TiO2 and its photocatalytic mechanism of conversion to CO

The adsorption energies for physisorption and the most stable chemisorption of CO₂ on the neutral charge of perfect anatase [TiO₂] (0 0 1) are −9.03 and −24.66 kcal/mol on the spin-unpolarized and −12.98 and −26.19 kcal/mol on the spin-polarized surface. The small activation barriers of 1.67 kcal/mol on the spin-unpolarized surface and of 6.66 kcal/mol on the spin-unpolarized surface were obtained. The adsorption mechanism of CO₂ on the oxygen vacancy defect [TiO₂ + V_O] surface of anatase TiO₂ using density functional theory calculations was investigated. The energetically preferred conversion of CO₂ to CO was found either on the spin-unpolarized or spin-polarized surfaces of oxygen vacancy defect surface [TiO₂ + V_O] as photocatalyst.     

The roles of Li and F ions in Li-F-codoped TiO2 system

An overall comparative study was carried out on Li-doped, F-doped, and Li-F-codoped TiO₂ powders in order to elucidate the roles of Li⁺ and F⁻ ions in photocatalyst. The characteristic data were based on the analysis of XRD, XPS, and PL spectra. The effects of atomic ratio of Li/Ti and F/Ti on the photocatalytic activity were also investigated. As the results, Li doping accelerated the phase formation of rutile in lower temperature while F doping prevented the phase transition from anatase to rutile. Li doping inducted a large amount of O_OH on the surface of TiO₂, while F doping consumed much of O_OH. Li⁺ ions acted as the roles of recombination center of electron-hole pairs while F doping could restrain the recombination of electron-hole pairs on the center of Li⁺ ions. The roles of Li⁺ and F⁻ ions were also confirmed in the experimental section, where the photocatalytic activity of TiO₂ was improved greatly by synergistic reaction of Li⁺ and F⁻ ions.     

Response improvement for In2O3-TiO2 thick film gas sensors

In₂O₃ is introduced into TiO₂ by sol-gel method to improve the response/recovery rate and expand the operating temperature, when the In₂O₃-TiO₂ mixed system is exposed to H₂/O₂. The sensor is fabricated by thick film technology. Influence of In₂O₃ on the film phase composition, microstructure and sensing characteristics is discussed. Dynamic response properties show that the operating temperature of the mixed system is at 500-800 °C, which is about 600-800 °C for pure TiO₂. Response time of the sensor is about 200-260 ms (millisecond) while recovery time is in a narrow range of 60-280 ms at 600-800 °C. The promoting mechanism is suggested to arise from the introduction of In₂O₃ and grain size effect of the sensing film. Then In₂O₃-TiO₂ thick films are surface-modified by Pt using chloroplatinic acid. The promoting effect of Pt dispersed on the mixed system is also investigated.