Structural characterization of La0.9Ba0.1MnO3/Y-ZrO2 film by X-ray diffraction

Perovskite manganite La_0.9Ba_0.1MnO₃(LBMO) films were deposited on (0 0 1)-oriented single crystal yttria-stabilized zirconia (YSZ) substrate by 90° off-axis radio frequency magnetron sputtering. The film thickness ranged from 10 nm to 100 nm. Grazing incidence X-ray diffraction technique and high resolution X-ray diffraction were applied to characterize the structure of LBMO films. The LBMO film mainly consisted of (0 0 1)-orientated grain as well as weakly textured (1 1 0)-orientated grain. The results indicated that an amorphous layer with thickness of about 4 nm was formed at the LBMO/YSZ interface. The strain in LBMO film was small and averaged to be about -0.14%. The strain in the film was not lattice mismatch-induced strain but residual strain due to the difference in thermal expansion coefficient between film and substrate.     

Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Magnetotransport properties of epitaxial Pr0.5Ca0.5MnO3 films grown by a solution technique

Epitaxial Pr_0.5Ca_0.5MnO₃ films have been synthesized on (0 0 1) SrTiO₃ substrate using a chemical solution deposition technique and two-step post-annealing process. The zero field resistivity of the films shows semiconducting behavior and a characteristic of charge ordering is observed at 230 K. The resistivity of the 10 nm film did not show any effect with the magnetic field. However, melting of charge ordering was observed for the 120 nm film at an applied magnetic field of 4 T. Large decrease in the resistivity of the 120 nm film (<100 K) resulted in magnetoresistance of nearly −100% at 75 K.     

Characterization of Y2O3 gate dielectric on n-GaAs substrates

Physical and electrical properties of sputtered deposited Y₂O₃ films on NH₄OH treated n-GaAs substrate are investigated. The as-deposited films and interfacial layer formation have been analyzed by using X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). It is found that directly deposited Y₂O₃ on n-GaAs exhibits excellent electrical properties with low frequency dispersion (<5%), hysteresis voltage (0.24 V), and interface trap density (3 × 10¹² eV⁻¹ cm⁻²). The results show that the deposition of Y₂O₃ on n-GaAs can be an effective way to improve the interface quality by the suppression on native oxides formation, especially arsenic oxide which causes Fermi level pinning at high-k/GaAs interface. The Al/Y₂O₃/n-GaAs stack with an equivalent oxide thickness (EOT) of 2.1 nm shows a leakage current density of 3.6 × 10⁻⁶ A cm⁻² at a V_FB of 1 V. While the low-field leakage current conduction mechanism has been found to be dominated by the Schottky emission, Poole-Frenkel emission takes over at high electric fields. The energy band alignment of Y₂O₃ films on n-GaAs substrate is extracted from detailed XPS measurements. The valence and conduction band offsets at Y₂O₃/n-GaAs interfaces are found to be 2.14 and 2.21 eV, respectively.     

Optical properties of La2O3 doped diamond-like carbon films

A novel kind of La₂O₃ doped diamond-like carbon (DLC) films with thickness of 100-120 nm were deposited by unbalanced magnetron sputtering. Raman spectra and photoluminescence properties were measured by Raman spectrometer operated by 325 nm He-Cd laser and 514 nm Ar⁺ laser, respectively. The intensities of Raman spectra and photoluminescence are higher than those of pure DLC films. The La₂O₃ doped DLC films have the potential promising for the application of solar cell coatings.     

Exchange bias in thin-film (Co/Pt)3/Cr2O3 multilayers

We have fabricated exchange-biased Co/Pt layers ((0.3 nm/1.5 nm)×3) on (0 0 1)-oriented Cr₂O₃ thin films. The multilayered films showed extremely smooth surfaces and interfaces with root mean square roughness of ≈0.3 nm for 10 μm×10 μm area. The Cr₂O₃ films display sufficient insulation with a relative low leakage current (1.17×10⁻² A/cm² at 380 MV/m) at room temperature which allowed us to apply electric field as high as 77 MV/m. We find that the sign of the exchange bias and the shape of the hysteresis loops of the out-of-plane magnetized Co/Pt layers can be delicately controlled by adjusting the magnetic field cooling process through the Néel temperature of Cr₂O₃. No clear evidence of the effect of electric field and the electric field cooling was detected on the exchange bias for fields as high as 77 MV/m. We place the upper bound of the shift in exchange bias field due to electric field cooling to be 5 Oe at 250 K.     

Structural, magnetic and electric properties of HoMnO3 films on SrTiO3(001)

HoMnO₃ films were grown on pure and Nb-doped SrTiO₃ (001) substrates by pulsed laser deposition. The films grew epitaxially with the c-axis along the substrate normal. Varying the deposition temperature between 650 and 850 °C did not significantly affect the structural and magnetic properties of the films, whereas growth in oxygen partial pressures below 0.01 mbar lead to a degradation of the structural properties. Some of the films had a ferromagnetic-like magnetic phase transition at about 45 K, probably related to Mn₃O₄ precipitates; this magnetic response was isotropic. The Ho sublattice was found to be paramagnetic down to 5 K, but showing a pronounced anisotropy with the c-axis being the hard axis. The films showed a distinct dielectric anomaly at 16 K that depended on voltage and slightly on frequency in the range between 1 kHz and 1 MHz. The magnetoelectric effect was large with an in-plane field of 8 T suppressing the dielectric anomaly completely.     

Influence of epitaxial growth on phase competition in Pr0.5Sr0.5MnO3 films

A series of Pr_0.5Sr_0.5MnO₃ (PSMO) films with various thickness were epitaxially grown on substrates of (0 0 1)-oriented (LaAlO₃)_0.3(SrAl_0.5Ta_0.5O₃)_0.7 (LSAT), LaAlO₃ (LAO) and SrTiO₃ (STO), and (0 1 1)-oriented STO using pulse laser deposition. Influence of epitaxial growth on phase competition was investigated. A ferromagnetic metal to antiferromagnetic insulator (FMM-AFI) transition upon cooling is present in both largely compressed situations deposited on LAO (0 0 1) and tensile cases deposited on STO (0 0 1) but absent in little strained films grown on LSAT (0 0 1), indicating that the antiferromagnetic insulating state is favored by strains. On the other hand, the 400 nm films deposited on (0 1 1)-oriented STO as well as LAO substrates show FMM-AFI transition. These results reveal that both the orientation of epitaxial growth and substrate-induced strain affect the FMM-AFI transition.     

Microstructures and multiferroic properties of textured Bi0.8La0.2FeO3 thin films

La-substituted BiFeO₃, Bi_0.8La_0.2FeO₃, thin films were fabricated on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition. X-ray diffraction and high-resolution transmission electron microscope were used to analyze the structures of the films. The results show the films fabricated under optimized growth condition are (0 1 2) textured. X-ray photoemission spectroscopy results indicate that the oxidation state of Fe ion is Fe³⁺ in the films without detectable Fe²⁺. The films show low leakage current and excellent dielectric characters. Multiferroic properties with a remnant ferroelectric polarization of 5.2 μC/cm² and a remanent magnetization of 0.02 μ_B/Fe were established. These results have some implications for further research.     

VO2-WO3 nanocomposite thin films synthesized by pulsed laser deposition technique

Pure VO₂ and VO₂-WO₃ composite thin films were grown on quartz substrate by pulsed laser deposition (PLD) technique. The influence of varying WO₃ molar concentration in the range from x = 0.0 to x = 0.4 on structural, electrical and optical properties of VO₂-WO₃ nanocomposite thin films has been systematically investigated. X-ray diffraction studies reveal the single crystalline monoclinic VO₂ phase (m-VO₂) up to 10% of WO₃ content whereas both m-VO₂ as well as h-WO₃ (hexagonal WO₃) phases were present at higher WO₃ content (0.2 ≤ x ≤ 0.4). Optical transmittance spectra of the films showed blue shift in the absorption edge with increase in WO₃ content. Temperature dependence of resistivity (R-T) measurements indicates significant variation in metal-insulator transition temperature, width of the hysteresis, and shape of the hysteresis curve. Cyclic Voltammetry measurements were performed on VO₂-WO₃ thin films. A direct correlation between V/W ratio and structure-property relationship was established. The present investigations reveal that doping of WO₃ in VO₂ is effective to increase the optical transmittance and to reduce the semiconductor to metal phase transition temperature close to room temperature.     

Optical characterization and microstructure of BaTiO3 thin films obtained by RF-magnetron sputtering

BaTiO₃ thin films were deposited on Pt/Ti/SiO₂/Si by rf planar-magnetron sputtering. The films thickness increases with the decrease of both deposition pressure and sample-discharge centre distance. The films annealed at 900 °C, for 8 h, present direct band gap energy ranged between 3.57 and 3.59 eV. The dependence of the structure and microstructure (texture, degree of crystallinity), as well as of the optical characteristics on the deposition parameters, was analysed. Using spectroscopic ellipsometry (SE) measurements coupled with the Bruggeman Effective Medium Approximation (B-EMA), the layer structure and the surface roughness, were determined. The root mean square roughness values of the surface layer, estimated by atomic force microscopy (AFM) analyses, are ranged between 10 and 20 nm and were in good agreement with SE data.The obtained films have tetragonal unit cell and show densely packed, non-columnar morphology and hexagon-like crystallite shape.     

Characterization of TiO2/Au/TiO2 films deposited by magnetron sputtering on polycarbonate substrates

Transparent and conducting TiO₂/Au/TiO₂ (TAuT) films were deposited by reactive magnetron sputtering on polycarbonate substrates to investigate the effect of the Au interlayer on the optical, electrical, and structural properties of the films. In TAuT films, the Au interlayer thickness was kept at 5 nm. Although total thickness was maintained at 100 nm, the stack structure was varied as 50/5/45, 70/5/25, and 90/5/5 nm.In XRD pattern, the intermediate Au films were crystallized, while all TAuT films did not show any diffraction peaks for TiO₂ films with regardless of stack structure. The optical and electrical properties were dependent on the stack structure of the films. The lowest sheet resistance of 23 Ω/□ and highest optical transmittance of 76% at 550 nm were obtained from TiO₂ 90 nm/Au 5 nm/TiO₂ 5 nm films. The work function was dependent on the film stack. The highest work function (4.8 eV) was observed with the TiO₂ 90 nm/Au 5 nm/TiO₂ 5 nm film stack. The TAuT film stack of TiO₂ 90 nm/Au 5 nm/TiO₂ 5 nm films is an optimized stack that may be an alternative candidate for transparent electrodes in flat panel displays.     

Optical properties of In2O3 oxidized from InN deposited by reactive magnetron sputtering

Unintentionally doped and zinc-doped indium nitride (U-InN and InN:Zn) films were deposited on (0 0 0 1) sapphire substrates by radio-frequency reactive magnetron sputtering, and all samples were then treated by annealing to form In₂O₃ films. U-InN and InN:Zn films have similar photon absorption characteristics. The as-deposited U-InN and InN:Zn film show the absorption edge, ∼1.8-1.9 eV. After the annealing process at 500 °C for 20 min, the absorption coefficient at the visible range apparently decreases, and the absorption edge is about 3.5 eV. Two emission peaks at 3.342 eV (371 nm) and 3.238 eV (383 nm) in the 20 K photoluminescence (PL) spectrum of In₂O₃:Zn films were identified as the free-exciton (FE) or the near band-to-band (B-B) and conduction-band-to-acceptor (C-A) recombination, respectively.     

Structural and optical properties of Er, Yb co-doped Y2O3 thin films

Thin Er³⁺, Yb³⁺ co-doped Y₂O₃ films were grown on (1 0 0) YAG substrates by pulsed laser deposition. Ceramic targets having different active ion concentration were used for ablation. The influence of the rare-earth content and oxygen pressure applied during the deposition on the structural, morphological and optical properties of the films were investigated. The films deposited at the lower pressure, 1 Pa, and at 1/10 Er to Yb doping ratio are highly textured along the (1 1 1) direction of the Y₂O₃ cubic phase. In addition to the crystalline structure, these films possess smoother surface compared to those prepared at the higher pressure, 10 Pa. All other films are polycrystalline, consisting of cubic and monoclinic phases of Y₂O₃. The rougher surface of the films produced at the higher-pressure leads to higher scattering losses and different behavior of the reflectivity spectra. Optical anisotropy in the films of less than 0.004 was measured regardless of the monoclinic structure obtained. Waveguide losses of about 1 dB/cm at 633 nm were obtained for the films produced at the lower oxygen pressure.     

Annealing effects on the structural and electrical transport properties of n-type Bi2Te2.7Se0.3 thin films deposited by flash evaporation

N-type Bi₂Te_2.7Se_0.3 thermoelectric thin films with thickness 800 nm have been deposited on glass substrates by flash evaporation method at 473 K. Annealing effects on the thermoelectric properties of Bi₂Te_2.7Se_0.3 thin films were examined in the temperature range 373-573 K. The structures, morphology and chemical composition of the thin films were characterized by X-ray diffraction, field emission scanning electron microscope and energy dispersive X-ray spectroscopy, respectively. Thermoelectric properties of the thin films have been evaluated by measurements of the electrical resistivity and Seebeck coefficient at 300 K. The Hall coefficients were measured at room temperature by the Van der Pauw method. The carrier concentration and mobility were calculated from the Hall coefficient. The films thickness of the annealed samples was measured by ellipsometer. When annealed at 473 K, the electrical resistivity and Seebeck coefficient are 2.7 mΩ cm and −180 μV/K, respectively. The maximum of thermoelectric power factor is enhanced to 12 μW/cm K².     

Ferroelectric properties of bilayer structured Pb(Zr0.52Ti0.48)O3/SrBi2Ta2O9 (PZT/SBT) thin films on Pt/TiO2/SiO2/Si substrates

Pb(Zr_0.52Ti_0.48)O₃ (PZT) thin films with large remanent polarization and SrBi₂Ta₂O₉ (SBT) thin films with excellent fatigue-resisting characteristic have been widely studied for non-volatile random access memories, respectively. To combine these two advantages_, bilayered Pb(Zr_0.52Ti_0.48)O₃/SrBi₂Ta₂O₉ (PZT/SBT) thin films were fabricated on Pt/TiO₂/SiO₂/Si substrates by chemical solution deposition method. X-ray diffraction patterns revealed that the diffraction peaks of PZT/SBT thin films were completely composed of PZT and SBT, and no other secondary phase was observed. The electrical properties of the bilayered structure PZT/SBT films have been investigated in comparison with pure PZT and SBT films. PZT/SBT bilayered thin films showed larger remanent polarization (2P_r) of 18.37 μC/cm² than pure SBT and less polarization fatigue up to 1 × 10⁹ switching cycles than pure PZT. These results indicated that this bilayered structure of PZT/SBT is a promising material combination for ferroelectric memory applications.     

Magnetic properties of Ni-substituted BiFeO3

BiFe_1−xNi_xO₃ ceramic powders with x up to 0.10 have been prepared by the sol-gel technique. The band gap of BiFeO₃ is 2.23 eV, and decreases to 2.09 eV for BiFe_0.95Ni_0.05O₃ and BiFe_0.90Ni_0.10O₃. The Mössbauer spectra show sextet at room temperature, indicating the magnetic ordering and the presence of only Fe³⁺ ions. Superparamagnetism with blocking temperature of 31 K for BiFe_0.95Ni_0.05O₃ and 100 K for BiFe_0.90Ni_0.10O₃ was observed. Enhanced magnetization at room temperature have been observed (1.0 emu/g for BiFe_0.95Ni_0.05O₃ and 2.9 emu/g for BiFe_0.90Ni_0.10O₃ under magnetic field of 10,000 Oe), which is one order larger than that of BiFeO₃ (0.1 emu/g under magnetic field of 10,000 Oe). The enhanced magnetization was attributed to the suppression of the cycloidal spin structure by Ni³⁺ substitution and the ferrimagnetic interaction between Fe³⁺ and Ni³⁺ ions.     

Transverse laser induced thermoelectric voltage effect in tilted La0.5Sr0.5CoO3 thin films

The transverse laser induced thermoelectric voltage effect has been investigated in tilted La_0.5Sr_0.5CoO₃ thin films grown on vicinal cut LaAlO₃ (1 0 0) substrates when films are irradiated by pulse laser at room temperature. The detected voltage signals are demonstrated to originate from the transverse Seebeck effect as the linear dependence of voltage on tilted angle in the range of small tilted angle. The Seebeck coefficient anisotropy ΔS of 0.03 μV/K at room temperature is calculated and its distorted cubic structure is thought to be responsible for this. Films grown on a series of substrates with different tilted angles show the optimum angle of 19.8° for the maximum voltage. Film thickness dependence of voltage has also been studied.     

Laser synthesis of thin layers of In4Se3, In4Te3 and modification of their structure and characteristics

Trends of structural modifications and phase composition occurring in In₄Se₃ thin films and In₄Se₃-In₄Te₃ epitaxial heterojunctions under laser irradiations have been investigated. Dynamics of the layer structure modification, depending on laser modes, i.e. pulse duration τ = 2-4 ms, irradiation intensity I₀ = 10-50 kW/cm², number of pulses N = 5-50, was studied by electron microscopy. An increase in laser influence promotes enlargement of the layer grains and transformation of their polycrystalline structure towards higher degree of stoichiometry. As a result of laser solid restructuring heterojunctions of In₄Se₃-In₄Te₃, being photosensitive within 1.0-2.0 μm and showing fast time of response, have been obtained. Laser modification of structure enables one to optimize electrical and optical properties of functional elements on the base of thin films and layers of In₄Se₃, In₄Te₃, widely used as infrared detectors and filters.