Effect of substrate bias voltages on the diffusion barrier properties of Zr-N films in Cu metallization

Zr-N diffusion barriers were deposited on the Si substrates by rf reactive magnetron sputtering under various substrate bias voltages. Cu films were subsequently sputtered onto the Zr-N films by dc pulse magnetron sputtering without breaking vacuum. The Cu/Zr-N/Si specimens were then annealed up to 650 °C in N₂ ambient for an hour. The effects of deposition bias on growth rate, film resistivity, microstructure, and diffusion barrier properties of Zr-N films were investigated. An increase in negative substrate bias resulted in a decrease in deposition rate together with a decrease in resistivity. It was found that the sheet resistances of Cu/Zr-N(−200 V)/Si contact system were lower than those of Cu/Zr-N(−50 V)/Si specimens after annealing at 650 °C. Cu/Zr-N(−200 V)/Si contact systems showed better thermal stability so that the Cu₃Si phase could not be detected.     

Ultrathin amorphous Ni-Ti film as diffusion barrier for Cu interconnection

5-nm-thick amorphous Ni-Ti films deposited on Si by magnetron sputtering, annealed at various temperatures in high vacuum, have been studied as diffusion barriers for Cu interconnection using X-ray diffraction, atomic force microscopy and four-probe methods. Although no Cu silicide peaks are found from X-ray diffraction patterns of the samples annealed up to 750 °C, it is found that the sheet resistance of Cu/Ni-Ti/Si decreases with the increase of annealing temperature and then slightly increases when the annealing temperature is higher than 700 °C. Root mean square roughness of Cu/Ni-Ti/Si increases with the increase of annealing temperature and many island-like grains present on the surface of the 750 °C annealed sample, which is ascribed to dewetting and agglomeration.     

Formation of copper islands on a native SiO2 surface at elevated temperatures

A combination of in situ X-ray photoelectron spectroscopy analysis and ex situ scanning electron- and atomic force microscopy has been used to study the formation of copper islands upon Cu deposition at elevated temperatures as a basis for the guided growth of copper islands. Two different temperature regions have been found: (I) up to 250 °C only close packed islands are formed due to low diffusion length of copper atoms on the surface. The SiO₂ film acts as a barrier protecting the silicon substrate from diffusion of Cu atoms from oxide surface. (II) The deposition at temperatures above 300 °C leads to the formation of separate islands which are (primarily at higher temperatures) crystalline. At these temperatures, copper atoms diffuse through the SiO₂ layer. However, they are not entirely dissolved in the bulk but a fraction of them forms a Cu rich layer in the vicinity of SiO₂/Si interface. The high copper concentration in this layer lowers the concentration gradient between the surface and the substrate and, consequently, inhibits the diffusion of Cu atoms into the substrate. Hence, the Cu islands remain on the surface even at temperatures as high as 450 °C.     

Failure behavior of ITO diffusion barrier between electroplating Cu and Si substrate annealed in a low vacuum

A structure of Cu/ITO(10 nm)/Si was first formed and then annealed at various temperatures for 5 min in a rapid thermal annealing furnace under 10⁻² Torr pressure. In Cu/ITO(10 nm)/Si structure, the ITO(10 nm) film was coated on Si substrate by sputtering process and the Cu film was deposited on ITO film by electroplating technique. The various Cu/ITO(10 nm)/Si samples were characterized by a four-point probe, a scanning electron microscope, an X-ray diffractometer, and a transmission electron microscope. The results showed that when the annealing temperature increases near 600 °C the interface between Cu and ITO becomes unstable, and the Cu₃Si particles begin to form; and when the annealing temperature increases to 650 °C, a good many of Cu₃Si particles about 1 μm in size form and the sheet resistance of Cu/ITO(10 nm)/Si structure largely increases.     

Ultrathin Mo/MoN bilayer nanostructure for diffusion barrier application of advanced Cu metallization

Ultrathin Mo (5 nm)/MoN (5 nm) bilayer nanostructure has been studied as a diffusion barrier for Cu metallization. The Mo/MoN bilayer was prepared by magnetron sputtering and the thermal stability of this barrier is investigated after annealing the Cu/barrier/Si film stack at different temperatures in vacuum for 10 min. The failure of barrier structure is indicated by the abrupt increase in sheet resistance and the formation of Cu₃Si phase proved by X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDS). High resolution transmission electron microscopy (HRTEM) examination suggested that the ultrathin Mo/MoN barrier is stable and can prevent the diffusion of Cu at least up to 600 °C.     

Epitaxial growth of uniform NiSi2 layers with atomically flat silicide/Si interface by solid-phase reaction in Ni-P/Si(1 0 0) systems

As metal-oxide-semiconductor field-effect transistor (MOSFET) devices are shrunk to the nanometer scale, flat shallow metal/Si electrical contacts must be formed in the source/drain region. This work demonstrates a method for the formation of epitaxial NiSi₂ layers by a solid-phase reaction in Ni-P(8 nm)/Si(1 0 0) samples. The results show that the sheet resistance remained low when the samples were annealed at temperatures from 400 to 700 °C. P atoms can be regarded as diffusion barriers against the supply of Ni to the Si substrate, which caused the formation of Si-rich silicide (NiSi₂) at low temperature. Furthermore, elemental P formed a stable capping layer with O, Ni and Si during the annealing process. A uniform NiSi₂ layer with an atomically flat interface was formed by annealing at 700 °C because of the formation of a Si-Ni-P-O capping layer and a reduction in the total interface area.     

Effect of tin-doped indium oxide film as capping layer on the agglomeration of copper film and the appearance of copper silicide

In this work, the effect of tin-doped indium oxide (ITO) film as capping layer on the agglomeration of copper film and the appearance of copper silicide was studied. Both samples of Cu 100 nm/ITO 10 nm/Si and ITO 20 nm/Cu 100 nm/ITO 10 nm/Si were prepared by sputtering deposition. After annealing in a rapid thermal annealing (RTA) furnace at various temperatures for 5 min in vacuum, the samples were characterized by four probe measurement for sheet resistance, X-ray diffraction (XRD) analysis for phase identification, scanning electron microscopy (SEM) for surface morphology and transmission electron microscopy (TEM) for microstructure.The results show that the sample with ITO capping layer is a good diffusion barrier between copper and silicon at least up to 750 °C, which is 100 °C higher than that of the sample without ITO capping layer. The failure temperature of the sample with ITO capping layer is about 800 °C, which is 100 °C higher than that of the sample without ITO capping layer. The ITO capping layer on Cu/ITO/Si can obstacle the agglomeration of copper film and the appearance of Cu₃Si phase.     

Defects in nanocrystalline Nb films: Effect of sputtering temperature

Thin niobium (Nb) films (thickness 350-400 nm) were prepared on (1 0 0)Si substrate in a UHV chamber using the cathode beam sputtering. The sputtering temperature T_s was varied from 40 up to 500 °C and the influence of the sputtering temperature on the microstructure of thin Nb films was investigated. Defect studies of the thin Nb films sputtered at various temperatures were performed by slow positron implantation spectroscopy (SPIS) with measurement of the Doppler broadening of the annihilation line. SPIS was combined with transmission electron microscopy (TEM) and X-ray diffraction (XRD). We have found that the films sputtered at T_s = 40 °C exhibit elongated, column-like nanocrystalline grains. No significant increase of grain size with T_s (up to 500 °C) was observed by TEM. The thin Nb films sputtered at T_s = 40 °C contain a high density of defects. It is demonstrated by shortened positron diffusion length and a high value of the S parameter for Nb layer compared to the well-annealed (defect-free) bulk Nb reference sample. A drastic decrease of defect density was found in the films sputtered at T_s ≥ 300 °C. It is reflected by a significant increase of the positron diffusion length and a decrease of the S parameter for the Nb layer. The defect density in the Nb layer is, however, still substantially higher than in the well-annealed reference bulk Nb sample. Moreover, there is a layer at the interface between the Nb film and the substrate with very high density of defects comparable to that in the films sputtered at T_s < 300 °C. All the Nb films studied exhibit a strong (1 1 0) texture. The films sputtered at T_s < 300 °C are characterized by a compressive macroscopic in-plane stress due to lattice mismatch between the film and the substrate. Relaxation of the in-plane stress was observed in the films sputtered at T_s ≥ 300 °C. The width of the XRD profiles of the films sputtered at T_s ≥ 300 °C is significantly smaller compared to the films sputtered at lower temperatures. This is most probably due to a lower defect density which results in reduced microstrains in the films sputtered at higher temperatures.     

Effects of deposition temperature on the structural and morphological properties of SnO2 films fabricated by pulsed laser deposition

Tin oxide (SnO₂) thin films were grown on Si (1 0 0) substrates using pulsed laser deposition (PLD) in O₂ gas ambient (10 Pa) and at different substrate temperatures (RT, 150, 300 and 400 °C). The influence of the substrate temperature on the structural and morphological properties of the films was investigated using X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). XRD measurements showed that the almost amorphous microstructure transformed into a polycrystalline SnO₂ phase. The film deposited at 400 °C has the best crystalline properties, i.e. optimum growth conditions. However, the film grown at 300 °C has minimum average root mean square (RMS) roughness of 3.1 nm with average grain size of 6.958 nm. The thickness of the thin films determined by the ellipsometer data is also presented and discussed.     

Thermal stability and electrical characteristics of NiSi films with electroplated Ni(W) alloy

In this study, an electroplating method to deposited Ni, crystalline NiW(c-NiW), amorphous NiW (a-NiW) films on P-type Si(1 0 0) were used to form Ni-silicide (NiSi) films. After annealed at various temperatures, sheet resistance of Ni/Cu, c-NiW/Cu and a-NiW/Cu was measured to observe the performance of those diffusion barrier layers. With W added in the barrier layer, the barrier performance was improved. The results of XRD and resistance measurement of the stacked Si/Ni(W)/Cu films reveal that Cu atom could diffuse through Ni barrier layer at 450 °C, could diffuse through c-NiW at 550 °C, but could hardly diffuse through a-NiW barrier layer. c-NiW layer has a better barrier performance than Ni layer, meanwhile the resistance is lower than a-NiW layer.     

Crystallization and surface morphology of Au/SiO2 thin films following furnace and flame annealing

A crystallization and surface evolution study of Au thin film on SiO₂ substrates following annealing at different temperatures above the eutectic point of the Au/Si system are reported. Samples were prepared by conventional evaporation of gold in a high vacuum (10⁻⁷ mbar) environment on substrates at room temperature. Thermal treatments were performed by both furnace and flame annealing techniques. Au thin films can be crystallized on SiO₂ substrates by both furnace and flame annealing. Annealing arranges the Au crystallites in the (1 1 1) plane direction and changes the morphology of the surface. Both, slow and rapid annealing result in a good background in the XRD spectra and hence clean and complete crystallization which depends more on the temperature than on the time of annealing. The epitaxial temperature for the Au/SiO₂ system decreases in the range of 350-400 °C. Furnace and flame annealing also form crystallized gold islands over the Au/SiO₂ surface. Relaxation at high temperatures of the strained Au layer, obtained after deposition, should be responsible for the initial stages of clusters formation. Gold nucleation sites may be formed at disordered points on the surface and they become islands when the temperature and time of annealing are increased. The growth rate of crystallites is highest around 360 °C. Above this temperature, the layer melts and gold diffuses from the substrate to the nucleation sites to increase the distance between islands and modify their shapes. Well above the eutectic temperature, the relaxed islands have hexagonally shaped borders. The mean crystallite diameters grow up to a maximum mean size of around 90 nm. The free activation energy for grain boundary migration above 360 °C is 0.2 eV. Therefore the type of the silicon substrate changes the mechanism of diffusion and growth of crystallites during annealing of the Au/Si system. Epitaxial Au(1 1 1) layers without formation of islands can be prepared by furnace annealing in the range of 300-310 °C and by flame annealing of a few seconds and up to 0.5 min.     

An XPS study and electrical properties of Pb1.1Zr0.53Ti0.47O3/PbO/Si (MFIS) structures according to the substrate temperature of the PbO buffer layer

PbO and PZT thin films were deposited on the p-type (1 0 0) Si substrate by the rf magnetron sputtering method with PbO and Pb_1.1Zr_0.53Ti_0.47O₃ targets for the application of the metal-ferroelectric-insulator-semiconductor (MFIS) structure. The MFIS structures with the PbO buffer layer show the good electric properties including a high memory window and a low leakage current density. The maximum value of the memory window is 2.0 V under the applied voltage of 9 V for the Pt/PZT (200 nm, 400 °C)/PbO (80 nm)/Si structures with the PbO buffer layer deposited at the substrate temperature of 300 °C. From the X-ray photoelectron spectroscopy (XPS) results, we could confirm that the substrate temperature of PbO affects the chemical states of the interface between the PbO buffer layer and Si substrate, which results in the inter-diffusion of Pb and the formation of the intermediate phases (PbSiO₃). And the existence of the undesired SiO₂ layer, which is the low dielectric layer, was confirmed at the surface region of the Si substrate by the XPS depth profile analysis.     

Effects of deposition temperature and thickness on the structural properties of thermal evaporated bismuth thin films

Bismuth (Bi) thin films of different thicknesses were deposited onto Si(1 0 0) substrate at various substrate temperatures by thermal evaporation technique. Influences of thickness and deposition temperature on the film morphologies, microstructure, and topographies were investigated. A columnar growth of hexahedron-like grains with bimodal particle size distribution was observed at high deposition temperature. The columnar growth and the presence of large grains induce the Bi films to have large surface roughness as evidenced by atomic force microscopy (AFM). The dependence of the crystalline orientation on the substrate temperature was analyzed by X-ray diffraction (XRD), which shows that the Bi films have completely randomly oriented polycrystalline structure with a rhombohedral phase at high deposition temperature (200 °C) and were strongly textured with preferred orientation at low deposition temperatures (30 and 100 °C).     

Effect of substrate temperature on the surface and interface oxidation of NiTi thin films

NiTi shape memory alloy thin films are deposited on pure Cu substrate at substrate ambient temperatures of 300 °C and 450 °C. The surface and interface oxidation of NiTi thin films are characterized by X-ray photoelectron spectroscopy (XPS). After a subsequent annealing treatment the crystallization behavior of the films deposited on substrate at different temperatures is studied by X-ray diffraction (XRD). The effects of substrate temperature on the surface and interface oxidation of NiTi thin films are investigated. In the film surface this is an oxide layer composed of TiO₂. The Ni atom has not been detected on surface. In the film/substrate interface there is an oxide layer with a mixture Ti₂O₃ and NiO in the films deposited at substrate temperatures 300 °C and 450 °C. In the films deposited at ambient temperature, the interface layer contains Ti suboxides (TiO) and metallic Ni.     

CTAB assisted growth and characterization of nanocrystalline CuO films by ultrasonic spray pyrolysis technique

An aqueous solution of cupric nitrate trihydrate (Cu(NO₃)₂·3H₂O) modified with cetyltrimetylammonium bromide (CTAB) is used to deposit CuO films on glass substrate by chemical spray pyrolysis technique. The thermal analysis shows that the dried CTAB doped precursor decomposes by an exothermic reaction and suggests that minimum substrate temperature for film deposition should be greater than 270 °C. X-ray diffraction (XRD) studies indicate the formation of monoclinic CuO with preferential orientation along (0 0 2) plane for all film samples. The CTAB used as cationic surfactant in precursor results in the suppression of grain growth in films along the (1 1 0), (0 2 0) and (2 2 0) crystal planes of CuO. Surfactant modified films showed an increase in crystallite size of 14 nm at substrate temperature of 300 °C. The scanning electron micrographs (FESEM) confirm the uniform distribution of facets like grains on the entire area of substrate. CTAB modified films show a significant reduction in the particle agglomeration. Electrical studies of the CuO films deposited at substrate temperature of 300 °C with and without surfactant reveal that the CTAB doping increase the activation energy of conduction by 0.217 eV and room temperature response to ammonia by 9%. The kinetics of the ammonia gas adsorption on the film surface follows the Elovich and Diffusion models.     

Transmission electron microscopy studies of HfO2 thin films grown by chloride-based atomic layer deposition

Detailed transmission electron microscopy characterization of HfO₂ films deposited on Si(1 0 0) using atomic layer deposition has been carried out. The influence of deposition temperature has been investigated. At 226 °C, a predominantly quasi-amorphous film containing large grains of cubic HfO₂ (a₀ = 5.08 Å) was formed. Grain morphology enabled the nucleation sites to be determined. Hot stage microscopy showed that both the cubic phase and the quasi-amorphous phase were very resistant to thermal modification up to 500 °C. These observations suggest that nucleation sites for the growth of the crystalline cubic phase form at the growing surface of the film, rather homogeneously within the film. The films grown at higher temperatures (300-750 °C) are crystalline and monoclinic. The principal effects of deposition temperature were on: grain size, which coarsens at the highest temperature; roughness with increases at the higher temperatures due to the prismatic faceting, and texture, with texturing being strongest at intermediate temperatures. Detailed interfacial characterization shows that interfacial layers of SiO₂ form at low and high temperatures. However, at intermediate temperatures, interfaces devoid of SiO₂ were formed.     

In situ growth stresses during the phase separation of immiscible FeCu thin films

This paper addresses the in situ growth stress evolution and post-growth stress relaxation during the phase separation of immiscible Fe_0.51Cu_0.49 thin films at various in situ deposition temperatures. Each film was sputter-deposited onto a 10 nm Si₃N₄ underlayer that was grown on top of Si [0 0 1] substrate at 25 °C, 145 °C, 205 °C, 265 °C or 325 °C. The thin film stress was measured using a wafer curvature technique. The in situ growth stress increased in compression with increasing substrate temperature. The stress relaxation of the Fe_0.51Cu_0.49 was found to have a linear increase with the inverse grain size for films deposited at temperatures greater than 205 °C. The stress state was correlated to the films’ phase and morphology by X-ray diffraction, (scanning) transmission electron microscopy and atomic force microscopy techniques.     

Evolution of magnetic and microstructural properties of thick sputtered NdFeB films with processing temperature

Ta (100 nm)/NdFeB (5 μm)/Ta (100 nm) films have been deposited onto Si substrates using triode sputtering (deposition rate ∼18 μm/h). A 2-step procedure was used: deposition at temperatures up to 400 °C followed by ex-situ annealing at higher temperatures. Post-deposition annealing temperatures above 650 °C are needed to develop high values of coercivity. The duration of the annealing time is more critical in anisotropic samples deposited onto heated substrates than in isotropic samples deposited at lower temperatures. For a given set of annealing conditions (750 °C/10′), high heating rates (?2000 °C/h) favour high coercivity in both isotropic and anisotropic films. The shape and size of Nd₂Fe₁₄B grains depend strongly on the heating rate.     

Heavy atomic-layer doping of B in low-temperature Si epitaxial growth on Si(1 0 0) by ultraclean low-pressure chemical vapor deposition

Electrical characteristics of B atomic-layer doped Si epitaxial films on Si(1 0 0) formed by B atomic-layer formation on Si(1 0 0) at 180 °C and subsequent capping Si deposition at 500 °C using ultraclean low-pressure chemical vapor deposition were investigated. From evaluation results of carrier concentration in the films, by low-temperature SiH₄ exposure at 180-300 °C before the capping Si deposition at 500 °C, 70% improvement of B electrical activity was confirmed, and it is suggested that lowering the temperatures for B atomic-layer formation on Si(1 0 0) as well as SiH₄ exposure before the capping Si deposition is effective to suppress B clustering and to achieve B atomic-layer doped Si films with extremely high carrier concentration.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.