Magnetic properties of Gd2(Fe1−x−yCoyTix)17

Serial single-phase Gd₂(Fe_1−x−yCo_yTi_x)₁₇ compounds have been synthesized. These compounds have a crystal structure belonging to rhombohedral lattice with space group. The lattice parameters of compounds decrease with cobalt content and increase with titanium content, respectively. The saturation magnetization decreases with increasing cobalt and titanium contents. The anisotropy fields increase to maximum then decrease with cobalt concentration. The magnetocrystalline anisotropy constants increase with cobalt content from negative to positive maximum and then decrease with Co concentration. The saturation moment of the compounds decreases linearly with cobalt concentration and decreases nonlinearly with titanium concentration.     

Thermal and magnetothermal properties of La0.5Pr0.5Mn2Si2

The thermal and magnetothermal properties of La_0.5Pr_0.5Mn₂Si₂ and isostructural LaFe₂Si₂ intermetallic compounds in the temperature range 4.5-303 K are reported with and without applied magnetic field. The electronic, lattice, and magnetic contributions to the heat capacity of La_0.5Pr_0.5Mn₂Si₂ are determined and analyzed. We have determined and from heat capacity experiments; the values are in line with those from the magnetization measurements. We conclude that in order to observe the anomaly in the heat capacity data around in the system, the transition around should occur in a narrow temperature interval.     

Magnetic and magnetocaloric properties of Pr0.6−xEuxSr0.4MnO3 manganese oxides

Studies of the structural, magnetic and magnetocaloric properties of polycrystalline Pr_0.6−xEu_xSr_0.4MnO₃ (0≤x≤0.15) perovskite manganites were carried out. Substitution for praseodymium with europium, with smaller ionic radius, induces local distortion in the 〈Mn–O–Mn〉 bonds and consequently causes a random distribution in the magnetic exchange interactions. The competition between magnetic interactions leads to the appearance of an inhomogeneous magnetic state in our samples. Pr_0.6−xEu_xSr_0.4MnO₃ (x=0, 0.05, 0.1 and 0.15) polycrystalline samples were prepared using the solid–solid reaction method at high temperature. The compounds yielded are single phase and crystallize in the orthorhombic system with the Pnma space group. The substitution of Eu for Pr leads to a decrease of the Curie temperature T_C from 303 K for x=0.00 to 260 K for x=0.15. All of our compounds exhibit a large magnetic entropy change with a maximum around 2.2 J/kg K under a magnetic applied field change of 2 T for all compounds.     

Characterization of Ce1−xZrxO2 thin films prepared by pyrolytic spray technique

It was demonstrated that spray pyrolysis can be used to prepare Ce_1−xZr_xO₂ thin films with x between 0 and 1. The composition of these films was determined by electron probe microanalysis (EPMA), and the crystalline structure by X-ray diffraction (XRD) and Raman spectroscopy (RS). Cyclic voltammetry (CV) was performed in an electrolyte of propylene carbonate with 1 M LiClO₄. Films with high Zr content were incapable of charge exchange of Li⁺ ions. In the contrast, films with high Ce content were found to be able to insert/extract large charge densities of Li⁺ ions. They also remained transparent during Li⁺ intercalation.     

The static and dynamic lattice effects in La1−xCaxMnO3

The structural and magnetic behavior of the perovskite insulator La_0.9Ca_0.1MnO₃ were studied as a function of temperature from 15 to 300 K by neutron powder diffraction. Although this compound shows an anomalous response of the lattice parameters around T_c (150 K), the behavior of the oxygen/manganese Debye-Waller factors is in clear contrast to its “colossal magnetoresistance” (CMR) counterpart La_0.65Ca_0.35MnO₃. We speculate that the difference is intimately associated with the metal-insulator transition in the latter compound.     

Heat capacity and thermal expansion of CdCr2Se4 and CdCr2S4

The thermodynamic properties of the spinel ferromagnetic compounds CdCr₂Se₄ and CdCr₂S₄ have been investigated by making heat capacity and thermal expansion measurements on single crystals. For both compounds, the ferromagnetic transition is marked by λ-type thermal anomalies, and the results provide a pressure dependence of the transition temperatures that is in agreement with direct measurements. Below the transition, CdCr₂S₄ shows an anomalous heat-capacity contribution and negative thermal expansion, which are in contrast to the conventional behavior found in CdCr₂Se₄.     

Normal-state transport properties of Ba1−xKxBiO3 crystals

The normal-state transport properties of Ba_1−xK_xBiO₃ crystals with a wide range of potassium compositions (0≤x≤0.62) were studied. Although the host material BaBiO₃ has a monoclinic structure, the system changes from a monoclinic to an orthorhombic structure with a small doping of potassium (0≤x<0.35) and behaves similar to a doped semiconductor, without exhibiting superconductivity. In the composition range, holes are majority carriers in the transport phenomena. When x exceeds a critical value (0.35), the system goes into a cubic superconducting phase with a single metallic band. The vicinity of the critical composition transport phenomena is easy to understand assuming the existence of two conducting channels that are made up of metallic and semiconducting phases. Maximum T_c exceeding 30 K was observed at x0.4, where carrier density was at its maximum. Overdoping with potassium suppresses superconductivity. In the metallic composition of x>0.45, transport seems to correlate with the phonon mode with an energy distribution of 15–43 meV.     

Vortex core physics in the cuprate superconductor Nd2−xCexCuOy

Flux-flow voltage steps and negative differential resistivity in the cuprate Nd_2−xCe_xCuO_y are explained in terms of subbands between the Fermi energy and the energy gap affecting the quasiparticle dynamics.     

Synthesis and dielectric properties of Bi1−xNdxFeO3 perovskites

Single-phase polycrystalline samples of Bi_1−xNd_xFeO₃ were prepared by standard solid state reaction method. X-ray diffraction (XRD) patterns of the powder samples were recorded and analyzed for the confirmation of crystal structure lattice parameters. Further, these samples were characterized by IR technique to identify and understand the aspect of bonding in the present samples. The dielectric measurements were carried out on the samples as a function of frequency in the range 100 Hz to 1 MHz at room temperature and also as a function of temperature in the range 300–750 K at certain fixed frequencies. The DC and AC electrical resistivity studies were carried out in order to understand conduction mechanism in the samples.     

Electrochemical behaviour of oxygen at nickel nest cathodic material with catalyst La1−xSrxCoO3

The reduction of oxygen in the three phases gas–liquid–solid using a nickel nest as electrode with a La_1−xSr_xCoO₃ (x=0, 0.3, 0.5, 0.7, 1) series of combined oxides as a catalyst in different electrolytes of acidic H₃PO₄ or alkaline KOH, NaOH or LiOH solution at a fixed optimum oxygen flow-rate at room temperature was studied by the electrochemical method. The electrochemical parameters, such as electron transfer coefficient and exchange current density, were also determined. The La_1−xSr_xCoO₃ series of catalysts was synthesized by a solid-state reaction. XRD was used to confirm the structure of the catalyst. BET, EDS and resistivity measurements were used to investigated the electrochemical behaviour of the cathodic reduction of oxygen in the presence of the catalyst. SEM was also used to inspect the change before and after the reaction with the catalyst. The electron transfer coefficients, β, from the experiments with the various catalysts in the different alkaline electrolytes were determined as follows:

β(in KOH)>β(in NaOH)>β(in LiOH).

It was discovered that La_0.7Sr_0.3CoO₃ as a catalyst has a higher catalytic activity, a higher specific surface area, lower electrical resistivity, better stability and less agglomeration. Therefore, the above catalyst is the best catalyst for oxygen reduction of those studied.     

Structural and lithium intercalation studies of Mn(0.5−x)CaxTi2(PO4)3 phases (0≤x≤0.50)

Materials from the Mn_(0.5−x)Ca_xTi₂(PO₄)₃ (0≤x≤0.50) solid solution were obtained by solid-state reaction in air at 1000 °C. Selected compositions were investigated by powder X-ray diffraction analysis, ³¹P nuclear magnetic resonance (NMR) spectroscopy and electrochemical lithium intercalation. The structure of all samples determined by Rietveld analysis is of the Nasicon type with the R space group. Mn²⁺/Ca²⁺ ions occupy only the M1 sites in the Ti₂(PO₄)₃ framework. The divalent cations are ordered in one of two M1 sites, except for the Mn_0.50Ti₂(PO₄)₃ phase, where a small departure from the ideal order is observed by XRD and ³¹P MAS NMR. The electrochemical behaviour of Mn_0.50Ti₂(PO₄)₃ and Mn_(0.5−x)Ca_xTi₂(PO₄)₃ phases was characterised in Li cells. Two Li ions can be inserted without altering the Ti₂(PO₄)₃ framework. In the 0≤y≤2 range, the OCV curves of Li//Li_yMn_0.50Ti₂(PO₄)₃ cells show two main potential plateaus at 2.90 and 2.50–2.30 V. Comparison between the OCV curves of Li//Li_(1+y)Ti₂(PO₄)₃ and Li//Li_yMn_0.50Ti₂(PO₄)₃ shows that the intercalation occurs first in the unoccupied M1 site of Mn_0.50Ti₂(PO₄)₃ at 2.90 V and then, for compositions y>0.50, at the M2 site (2.50–2.30 V voltage range). The effect of calcium substitution in Mn_0.50Ti₂(PO₄)₃ on the lithium intercalation is also discussed from a structural and kinetic viewpoint. In all systems, the lithium intercalation is associated with a redistribution of the divalent cation over all M1 sites. In the case of Mn_0.50Ti₂(PO₄)₃, the stability of Mn²⁺ either in an octahedral or tetrahedral environment facilitates cationic migration.     

Electrical conduction and optical properties of amorphous (Sb2Se3)100−xSnx thin films

The variation of DC electrical conductivity and the optical properties of thermally evaporated a- (Sb₂Se₃)_100−xSn_x thin films with temperature have been studied. It is found that the thermal activation energy decreases, while the optical gap first increases (up to x=1) and then decreases, with the increase in Sn content. These results have been explained by taking into consideration the structural modifications induced by the incorporation of Sn into the parent alloy. The variation in the conductivity prefactor (σ_o) with Sn addition indicates a change in the dominant conduction transport mechanism from extended states to localized states. An experimental correlation between the activation energy and the pre-exponential factor has been observed, indicating the validity of Meyer–Neldel rule in the studied samples.     

The first-principle study on the electronic structure and magnetic properties of polymer Cu(HCO 2 )(NO 3 )(pyz) {pyz = Pyrazine}

The first principle method was applied to study the electronic structure and magnetic properties of the compound of Cu(HCO₂)(NO₃)(pyz). The density of states, the electronic structure and the spin magnetic moments are calculated. The results reveal that the compound has a ferromagnetic interaction arising from the bridging μ- HCO₂⁻ and pyz ligands, and the ferromagnetic properties come from the spin delocalization effect. The spin magnetic moment per molecule mainly comes from the Cu ion, but has little contribution from O, N and C anion.     

Kondo behaviour of the solid solution (Ce1−xLax)PtGa

The solid solution (Ce_1−xLa_x)PtGa has been studied through X-ray diffraction, magnetization (σ(B)), magnetic susceptibility (χ(T)), electrical resistivity (ρ(T)), magnetoresistivity (MR) and heat capacity (C_P(T)) measurements. The Néel temperature (T_N=3.3 K) for CePtGa is lowered upon La substitution as observed from χ(T) and ρ(T) measurements. The Kondo temperature T_K as calculated from MR measurements is comparable to T_N and also decreases with La substitution. The volume dependence of T_K is in accordance with the compressible Kondo lattice model and a Doniach diagram of the results is presented. C_P(T) measurements are presented for CePtGa, Ce_0.2La_0.8PtGa and LaPtGa and the results are discussed in terms of the electronic and magnetic properties. Other features of interest are anomalies in ρ(T) and C_P(T) due to crystalline electric field effects and metamagnetism as observed in σ(B) studies for samples with 0≤x≤ 0.3.     

Structural and vibrational properties of dilute GaNxAs1−x(P1−x)

We report a comprehensive analyzes of the Fourier transform infrared (FTIR) absorption and Raman scattering data on the structural and vibrational properties of dilute ternary GaAs_1−xN_x,[GaP_1−xN_x] (x<0.03) alloys grown on GaAs [GaP] by metal organic chemical vapor deposition (MOCVD) and solid source molecular beam epitaxy (MBE). By using realistic total energy and lattice dynamical calculations, the origin of experimentally observed N-induced vibrational features are characterized. Useful information is obtained about the structural stability, vibrational frequencies, lattice relaxations and compositional disorder in GaNAs (GaNP) alloys. At lower composition (x<0.015) most of the N atoms occupy the As [P] sublattice {N_As[N_P]}—they prefer moving out of their substitutional sites to more energetically favorable locations at higher x. Our results for the N-isotopic shifts of local mode frequencies compare favorably well with the existing FTIR data.     

Structural properties and Raman spectroscopy of orthorhombic (Eu1−xPrx)0.6Sr0.4MnO3 (0≤x≤1.0)

The effect of Pr doping on structural properties and room temperature Raman spectroscopy measurements is investigated in manganites (Eu_1−xPr_x)_0.6Sr_0.4MnO₃ (0≤x≤1.0) with fixed carrier concentration. The result of the Rietveld refinement of x-ray powder diffraction shows that these compounds crystallize in an orthorhombic distorted structure with a space group Pnma. It is evident that, with increasing Pr substitution, three types of orthorhombic structures can be distinguished. The phonon frequencies of the three main peaks, in room temperature Raman-scattering measurements, have been discussed together with their structural characteristics, such as bond-length, bond-angles, and the change of orthorhombic structure type. With the increase of Pr content, the mode at 491  cm⁻¹ also shows a corresponding change. A step effect becomes evident, which seems to indicate the close dependence between the frequency shift of this mode and the change in crystal symmetry. This further supports the notion that the mode at 491  cm⁻¹ is closely correlated with the Jahn–Teller distortion. Moreover, we have found that the lowest frequency peak (assigned as an A_1g phonon mode) depends linearly on the tolerance factor t.     

Enhanced ferroelectric, magnetic and magnetoelectric properties of Bi1−xCaxFe1−xTixO3 solid solutions

We report on the enhanced electromechanical, magnetic and magnetoelectric properties of Bi_1−xCa_xFe_1−xTi_xO₃ solid solutions. The crystal structure of the x≈0.25 compounds are close to the rhombohedral-orthorhombic phase boundary, and the solid solutions are characterized by increased electromechanical properties due to the polarization extension near the polar-nonpolar border. The homogenous weakly ferromagnetic state is established at x>0.15 doping. The chemical doping shifts the magnetic transition close to room temperature, thus enlarging the magnetic susceptibility of the compounds. The solid solutions at the morphotropic phase boundary exhibit a nearly twofold increase in piezoelectric response, whereas the magnetoelectric coupling shows five times enhancement in comparison with the parent bismuth ferrite.     

Very strong interlayer exchange coupling in epitaxial Fe/Fe1−xSix/Fe trilayers (x=0.4–1.0)

Fe/Fe_1−xSi_x/Fe (x=0.4–1.0) wedge-type epitaxial trilayers with improved homogeneity are grown by co-evaporation from two electron-beam sources. The coupling strengths of the bilinear (J₁) and biquadratic (J₂) coupling terms are derived from Brillouin light scattering (BLS) spectra and longitudinal MOKE hysteresis loops. The total coupling strength J=J₁+J₂ increases dramatically with increasing x and reaches values in excess of 6 mJ/m².     

Field-induced pinning effect of Nd(Ba1−xNdx)2Cu3O7−δ single crystals grown by the traveling-solvent floating-zone method

We have studied the superconducting properties of Nd(Ba_1−xNd_x)₂Cu₃O_7−δ (Nd123, x ≈ 0.1) single crystals grown by the traveling-solvent floating-zone method under 0.1% O₂ in Ar atmosphere. The enhancement of the magnetization with increasing field is observed in the hysteresis (M-H) loop in fields both parallel and perpendicular to the c-axis of the Nd123 single crystals as well as in the bulk crystals prepared by the oxygen-controlled-melt-growth (OCMG) method. The composition variation of Ba/Nd is observed in the matrix of Nd123 crystals by an analytical TEM equipped with a cold field-emission gun. It turns out that the enhancement is due to the field-induced pinning effect ascribed to the weak superconducting Nd---Ba substitution regions in the Nd123 matrix.     

Non-Fermi liquid regimes in U1−xMxPd2Al3(M=Y,Th)

The temperature-composition (T–x) phase diagram and NFL characteristics in the electrical resistivity ρ(T), specific heat C(T), and magnetic susceptibility χ(T) at low temperatures for the systems U_1−xM_xPd₂Al₃ (M=Y,Th) are described. The T–x phase diagram, the NFL characteristics, and the underlying mechanism for the NFL behavior are distinctly different for M=Y³⁺ and Th⁴⁺, apparently reflecting the difference in valence of the M atom substituents, and suggesting that U is tetravalent in these two systems.