超细粉Pb_(0.75)Ca_(0.25)[(Ni_(1/3)Nb_(2/3))_(0.08)Ti_(0.912)Mn_(0.008)]O_3的制备与表征

报道了用化学共沉淀法制备掺杂 Ca、Ni、Nb、Mn钛酸铅超细陶瓷粉末的方法。制得的粉料化学式为 :Pb0 .75Ca0 .2 5[(Ni1 / 3 Nb2 / 3 ) 0 .0 8Ti0 .91 2 Mn0 .0 0 8] O3 ,粒径小于 0 .1μm,所有的掺杂元素均能定量掺入。     

La0.6Sr0.4Co1-yFeyO3(y=0.2,0.8)复合氧化物混合导电性能研究

采用甘氨酸-硝酸盐（GNP）法制备了La0．6Sr0．4Co1-yFeyO3（y=0．2，0．8）g合氧化物，研究了材料的结构、电子-离子混合导电性能及其相关性。结果表明，La0.6Sr0.4Co1-yFeyO3（y=0．2，0．8）合成粉料的颗粒细小均匀（～100nm），陶瓷形成菱形六面体钙钛矿结构。与La0．6Sr0．4Co0．2Fe0．8O3（y=0．8）陶瓷相比，La0.6Sr0.4Co0．8Fe0．2O3（y=0．2）陶瓷的晶粒尺寸大、致密度较高。在La0.6Sr0.4Co0．8Fe0．2O3（y=0．2）陶瓷中观察到Co^3＋离子歧化对电子导电性能的影响。与La0.6Sr0.4Co0.2Fe0.8O3（y=0．8）陶瓷相比，La0.6Sr0.4Co0.8Fe0．2O3（y=0．2）陶瓷具有更优异的电子-离子混合导电性能，材料在混合导电性能上的差异与其电子结构和显微结构紧密相关。     

铌元素改性V2O5-WO3/TiO2催化剂降低脱硝过程SO2的氧化率

本文采用浸渍法制备了Nb改性的V₂O₅-WO₃/Ti O₂催化剂,研究了脱硝反应中Nb负载量对催化剂SO₂氧化活性的影响。结果表明,在350℃下,Nb2O5负载量为2%的Nb₂O₅-V₂O₅-WO₃/Ti O₂催化剂上的SO₂氧化率最低（0.6%）,而同时NOx的转化率仍能达到95%。采用TGA、氮吸附、XRD、H2-TPR、CO₂-TPD、XPS和in-situ DRIFTS等对催化剂进行了表征分析,结果显示,Nb改性后V2O5-WO₃/Ti O₂催化剂的晶体结构没有发生明显改变,但是其比表面积小幅度下降,有助于减少对SO₂的吸附;同时,改性后催化剂表面的吸附氧含量下降,氧化还原性能也稍微减弱,这有利于降低其对SO₂...     

La2O3掺杂对CaO—MgO—Nb2O5-TiO2系陶瓷微观结构及微波介电性能的影响

用固相法制备了La2O3掺杂的CaO—MgO—Nb2O5-TiO2系微波介质陶瓷，通过改变La^3 离子的含量以调整改变CaO—MgO—Nb2O5-TiO2-La2O3系陶瓷的微观结构与微波介电性能。研究结果表明：通过A位La^3 离子取代Ca^2 离子可以提高该体系的品质因素Qf值、改善频率温度系数，同时降低了该体系的介电常数。随着La^3 离子取代量的提高，该体系的介电常数从57降低至35，Qf值从33400GHz上升至35000GHz(7．6GHz)，同时该体系的频率温度系数得到了改善。微波介电性能的变化与其微观结构变化密切相关，主要原因是在于A位空位缺陷引起氧八面体的畸变。     

NiO在γ-Al_2O_3及 TiO_2/γ-Al_2O_3载体上的表面存在状态

本文采用 LRS, XRD, UV-DRS, TPR考查了γ-Al2O3上 TiO2的分散容量,分散态 Ti4＋离子的配位环境; NiO在经 TiO2改性后的γ-Al2O3载体上的分散容量。结果表明：（ 1） TiO2在γ-Al2O3表面的分散容量约为 0.62 mmol/100m2γ-Al2O3,当 TiO2含量低于该分散容量时 Ti4＋在γ-Al2O3载体表面以嵌入形式呈离子态分布;而含量高于分散容量时还有结晶态的 TiO2出现。（ 2） NiO在 TiO2/γ-Al2O3载体表面的分散容量约为 1.1 mmol/100m2γ-Al2O3,比之在γ-Al2O3载体表面的分散容量 (1.5mmol/100m2γ-Al2O3)要低,这是由于γ-Al2O3表面上部分空位被 Ti4＋离子占据。用表面相互作用的“嵌入模型” (Incorporation Model）讨论了这些结果。     

A位取代对(Ca0.61Nd0.26)TiO3陶瓷烧结特性和介电性能的影响

采用常规固相反应法,以(Ca0.61Nd0.26)TiO3体系为基体成分,研究了A位取代对(Ca0.61Nd0.26)TiO3陶瓷的烧结特性和介电性能的影响规律。结果表明:Zn,Mg的A位取代,促使(Ca0.61Nd0.26)TiO3陶瓷烧结温度从1350℃降至1250℃。Zn,Mg在一定范围内A位取代(Ca0.61Nd0.26)TiO3中的Ca可形成钙钛矿结构的固溶体,Zn、Mg最大固溶度(x(Zn),y(Mg))分别不超过0.1和0.15mol。当取代量超过固溶度后,分别形成Ca2Zn4Ti15O36和MgTi2O5第二相。随Zn和Mg取代量的增加,陶瓷介电常数(εr)和谐振频率温度系数(τf)减小。陶瓷品质因数(Qf)值随Zn取代量先增后减,而随Mg取代量增加,其Qf值一直增大。Zn,Mg最佳取代分别为x(Zn)=0.15和y(Mg)=0.25,在1250℃烧结2h,[(Ca0.85Zn0.15)0.61Nd0.26]TiO3的介电性能:εr=93.60,Qf=12454GHz,τf= 150.3ppm·℃-1,[(Ca0.75Mg0.25)0.61Nd0.26]TiO3的介电性能:εr=72.48,Qf=14622GHz,τf= 108ppm·℃-1。     

2,2′-(1,2-亚苯基二氧)二(N-苯基乙酰胺)及其稀土配合物的合成、表征与荧光性质

合成了一种新的芳香族酰胺配体2，2’-（1，2-亚苯基二氧）二（N-苯基乙酰胺）及其稀土（La，Eu，Tb，Dy，Sm，Gd）硝酸盐配合物，通过核磁共振谱、元素分析、摩尔电导、红外光谱、差热等测试技术对其进行了结构表征。结果表明，稀土配合物的可能结构为：[REL（NO3）3]·H2O（RE：La^3＋、Sm^3＋、Eu^3＋、Gd^3＋、Tb^3＋、Dy^3＋）．配合物产率约为78％。在稀土配合物中，作为抗衡阴离子的3个硝酸根均以双齿的配位方式与稀土配位，稀土配位数为10，并且还有1个结晶水。在298K下对配合物[EuL（NO3）3]·H2O和[TI）L（N03）3]·H2O的固体荧光性质进行了研究。结果发现，它们分别发射Eu^3＋和Tb^3＋稀土离子的特征荧光，且配合物[TbL（NO3）3]·H2O的荧光比[EuL（NO3）3]·H2O的荧光强。说明此芳香族酰胺配体敏论Tb^3＋发光比敏化Eu^3＋发光程度大。     

Bi4(Ti1/3Sn2/3)3O12掺杂BaTiO3基X8R陶瓷微观结构与介电性能

研究了Bi4(Ti1/3Sn2/3)3O12掺杂对钛酸钡基陶瓷微观结构和介电性能影响。结果表明,掺杂Bi4(Ti1/3Sn2/3)3O12后钛酸钡基陶瓷晶粒明显长大,同时烧结温度可由1 280℃降低至1 180℃。系统的介电性能和Bi4(Ti1/3Sn2/3)3O12的掺杂量有密切关系。当Bi4(Ti1/3Sn2/3)3O12的掺杂量从0.5mol%增加到2mol%,体系的居里峰被明显压低和展宽,当掺杂量为2mol%时居里峰变得不明显。当Bi4(Ti1/3Sn2/3)3O12的掺杂量从0.5mol%增加到2mol%,系统的居里温度由131℃升高至139℃。当Bi4(Ti1/3Sn2/3)3O12的掺杂量为1mol%时,钛酸钡基陶瓷介电常数为1 930,介电常数温度变化率为5%(-55℃),13%(134℃),-8%(150℃),满足X8R标准。     

含纳米晶颗粒的Yb3+/Er3+共掺透明碲酸盐玻璃陶瓷的光谱性质研究

在组成为15Li2O-15Nb2O5-70TeO2-0.1Er2O3-0.4Yb2O3（%, 摩尔分数）的碲酸盐玻璃基础上, 采用两步热处理法制备了透明的含纳米晶颗粒碲酸盐玻璃陶瓷. 通过X射线衍射（XRD）测试表明, 玻璃陶瓷中的晶体颗粒组成为Yb6Te5O19.2或Er6Te5O19.2, 晶粒尺寸约为55 nm. 根据Judd-Ofelt理论计算了Er^3＋离子在基质玻璃和玻璃陶瓷中的光谱参数Ωt（t＝2, 4, 6）以及Er^3＋：4I15/2→4I13/2跃迁自发辐射几率, 根据McCumber理论计算了Er^3＋：4I13/2→4I15/2跃迁的发射截面. 测试了基质玻璃和玻璃陶瓷的拉曼光谱, 对比研究了铒离子在基质玻璃和玻璃陶瓷中1.5 μm处荧光和上转换光谱特性.     

类钙钛矿新铌酸盐Ba5LaTi2Nb3O18的合成、结构与介电特性

为满足现代通信技术小型化、集成化与高可靠性的迫切要求,探索具有高介电常数、低介电损耗与低温度系数的微波介电材料引起了材料科学、化学、物理和电子科学等领域科学工作者的广泛关注,并已开发出复合钙钛矿结构的Ba(Mg1/3Ta2/3)O3、Ba(Zn1/3Ta2/3)O3和钨青铜结构的Ba6-3xLn8+2x·Ti18O54及Ba2Ti9O20等实用化的高性能材料[1～7].这类材料均由氧八面体共顶连接,而且氧八面体内(B位)、外(A位)阳离子比例等于或略大于1,由此,我们推测在B位与A位阳离子比例略小于1的类钙钛矿结构中也极有可能存在具有优良介电性能的新材料,因此对通式为AnBn-1O3n(n=5,6,7,8)的系列新化合物进行了系统的合成、结构与介电性能研究[8,9].本文报道在BaO-La2O3-TiO2-Nb2O5体系中合成的具有5层类钙钛矿结构的新铌酸盐Ba5LaTi2Nb3O18,发现该材料具有较好的介电性能.     

沉淀法合成蓝色长余辉发光材料Sr_2MgSi_2O_7:Eu~(2+),Dy~(3+)

采用沉淀法制备了高亮度的长余辉发光材料Sr_2MgSi_2O_7:Eu~(2+),Dy~(3+).通过XRD、荧光光谱和热释光谱对其进行表征.XRD测试表明所制备的Sr_2MgSi_2O_7:Eu~(2+),Dy~(3+),四方晶.荧光光谱测试表明,λ_(em)=467 nm作为监控波长,在275～450 nm之间有宽的激发光谱,峰值位于399 nm.用λ=399 nm激发样品,其发射光谱为一宽带,峰值位于467 nm.1050℃煅烧前躯体所制备的Sr_2MgSi_2O_7:Eu~(2+),Dy~(3+)发光性能最好.热释光谱峰值位于357 K,适合长余辉现象的产生.对Sr_2MgSi_2O_7:Eu~(2+),Dy~(3+)长余辉发光机理进行了讨论.     

Doping Effect of Bi~(3+) on the Properties of YAG:Ce~(3+),Mn~(2+) Phosphor Ceramics for Warm WLEDs

A series of Bi³⁺-doped YAG:Ce³⁺, Mn²⁺ ceramics was synthesized successfully by gel-casting method and structurally characterized by XRD and SEM. The doping effect and related mechanism of Bi³⁺ upon the luminescent property were studied. It can be assigned to the energy transfer of multipolar interaction from Bi³⁺ to Ce³⁺, leading to the improvement of emission intensity about 58% for 0.0001 Bi³⁺ and 0.05 Mn²⁺ doping. In addition, the emission is significantly red-shifted with the peak at 590 nm for the Y2.9939 Ce0.006 Bi0.0001 Al4.96 Mn0.02 Si0.02 O12 ceramic specimen with in-line transmittance 81.6% at 1100 nm. The LED module assembled from Y2.9939 Ce0.006 Bi0.0001 Al4.96 Mn0.02 Si0.02 O12 ceramic owns correlated color temperature(CCT) of 3960 K and luminous efficiency(LE) of 92 lm/W, implying that doping Bi³⁺ shows a good sensitization effect in the YAG:Ce³⁺, Mn²⁺ ceramic system and further serving as an attracting phosphor candidates for warm WLEDs applications.     

高价离子掺入Bi(Pb)-Sr-Ca-Cu-O体系对成相和结构的影响

The effects of high valence cations M~(n+) (n≥4) doped on the phase formation and the structure stability have been investigated. In the crystal structure X_2Sr_2Ca_2Cu_3O_(10)(X = Bi_(1-x-y)Pb_xM_y), the high valence cations M~(n+), Bi~(3+), and Pb~(2+) were deter-mined to statistically distribute at the bismuth positions. The bismuth valence is raised and the positions of oxygen atoms in the (XO_2X) double layers are fully occupied. Conseqently, The structural stability is increased. The phase 2223 was found to form more rapidly by doping and the single phase with T_c(0)>110 K can be obtained more easily.     

镧离子掺杂纳米TiO2光催化降解聚乙烯薄膜的研究

La3 掺杂纳米TiO2光催化剂后,用于固相光催化降解聚乙烯(PE)薄膜。在紫外线辐射288h后,0.1%La2O3/TiO2使薄膜失重14.5%,产生更多石蜡和CO2,SEM表明其对PE的光氧化腐蚀能力更强,在薄膜表面形成更大更多的凹坑和空洞,红外光谱表明PE薄膜中的-CH2和支链-CH3基团的吸收明显减少,0.1%La2O3/TiO2光催化剂使PE的C=O的吸收增大。La3 掺杂后,提高了纳米TiO2的光催化活性。     

微波等离子体法合成SrAl_2O_4:Eu~(2+),Dy~(3+)中激活剂的浓度猝灭研究

采用微波等离子体法合成SrAl_2O_4:Eu~(2+),Dy~(3+)长余辉发光材料,通过对掺杂不同激活剂浓度的产物的光谱性能、余辉性能、相组成结构的分析以及晶胞常数的计算,探讨了微波等离子体法合成srAl_2O_4:Eu~(2+),Dy~(3+)时,激活剂Eu~(2+)的浓度猝灭特性.XRD测试结果表明,Eu~(2+)离子的掺入对基质晶格畸变影响很小;光谱和余辉性能测试表明Eu~(2+)的掺杂浓度对产物的瞬时发光强度影响较大,相对而言对余辉性能的影响程度不大.产物的发光性能随Eu~(2+)摩尔浓度的增大呈现先增强后减弱的趋势,发光中心Eu~(2+)离子的猝灭浓度为4%.结合EDX结果说明,与高温固相法以及其他一些方法相比,采用微波等离子体合成技术可在一定程度上提高Eu~(2+)离子的临界猝灭浓度,从而为进一步提高长余辉发光材料的发光性能提供了可能.     

Sc~(3+)掺杂LiMn_xSc_(1-x)O_2材料的合成及电化学性能研究

采用水热反应的方法,以LiOH·H_2O,MnOOH和Sc_2O_3为原料,合成了一系列Sc~(3+)掺杂的锂离子电池正极材料LiSc_xMn_(1-x)O_2(x=0.01,0.02,0.03,0.05).利用X射线衍射和X光电子能谱测试研究了材料的结构和元素的化学状态.掺杂后的LiSc_xMn_(1-x)O_2材料仍保持正交相结构.电化学测试结果表明,掺杂后材料表现出较好的电化学性能,Sc~(3+)的掺入使材料的循环稳定性能大幅度提高,掺杂量为2%时LiMn_(0.981)Sc_(0.019)O_2材料的初次放电容量为140.5 mAh·g~(-1),60次循环后放电容量高达169.6 mAJl·g-.,远高于未掺杂的LiMnO_2材料的放电容量107.7 mAh·g~(-1).这种提高源于Sc~(3+)的加入,很好地起到了稳定晶体结构、有效抑制Jahn-Teller效应的作用.电化学阻抗测试结果表明,Sc~(3+)的掺人能改善材料的导电性能.     

静电纺丝技术制备Y_2O_3∶Yb~(3+),Er~(3+)上转换纳米纤维及其表征

采用静电纺丝技术制备了PVA/[Y(NO3)3+Yb(NO3)3+Er(NO3)3]复合纳米纤维,将其在适当的温度下进行热处理,得到Y2O3∶Yb3+,Er3+上转换纳米纤维.XRD分析表明,复合纳米纤维为无定形,Y2O3∶Yb3+,Er3+上转换纳米纤维属于体心立方晶系,空间群为Ia3.SEM分析表明,复合纳米纤维的平均直径约为150nm;随着焙烧温度的升高,纤维直径逐渐减小.经过600℃焙烧后,获得了直径约60nm的Y2O3∶Yb3+,Er3+上转换纳米纤维.TG-DTA分析表明,当焙烧温度高于600℃时,复合纳米纤维中水分、有机物和硝酸盐分解挥发完毕,样品不再失重,总失重率为83%.FTIR分析表明,复合纳米纤维与纯PVA的红外光谱一致,当焙烧温度高于600℃时,生成了Y2O3∶Yb3+,Er3+上转换纳米纤维.该纤维在980nm的半导体激光器激发下发射出中心波长为521,562nm的绿色和656nm的红色上转换荧光,分别对应于Er3+离子的2H11/2/4S3/2→4Il5/2跃迁和4F9/2→4Il5/2跃迁.对Y2O3∶Yb3+,Er3+上转换纳米纤维的形成机理进行了讨论.     

氧化热处理对聚苯胺/V2O5杂化材料结构和性能的影响

采用原位氧化聚合法将聚苯胺分子链插入层状V2O5的片层中,制得了聚苯胺／五氧化二钒(PAn／V2O3)纳米杂化材料,并用氧气对杂化材料进行氧化热处理,用WAXD、FTIR、TGA、电导率及循环伏安测试等手段研究了氧化热处理对杂化材料结构与性能的影响。结果表明：氧化热处理对杂化材料的层状结构几乎没有影响,但将导致层闯客体聚苯胺分子链上醌式结构的比重略有增加,降低了电子的离域能力,从而使得电导率略有下降,同时伴随着部分V^4 氧化为V^5 ,使得嵌锂能力得到明显改善。     

The effect of Al~(3+) coordination structure on the propane dehydrogenation activity of Pt/Ga/Al_2O_3 catalysts

The effect of the Al_2O_3 structure on the performance of Pt/Ga/Al_2O_3 catalysts is investigated for the direct dehydrogenation of propane. The study unveils that the structure of Al~(3+)determines the bulk structure of catalysts, particularly a high content of coordinatively unsaturated Al~(3+)sites(penta-coordinated Al~(3+),denoted as Al~(3+)penta) could lead to a remarkably improved dehydrogenation activity of the catalyst. The bulk characterization reveals that the sufficient amount of Al~(3+)pentain Al_2O_3 benefit the dispersion of Pt and Ga_2O_3 on the Al_2O_3 support. At the same time, TPR results reveal that the presence of Pt facilitates the reduction of Ga_2O_3, likely due to the hydrogen spillover between the well dispersed Pt and Ga_2O_3,which consequently enhances the synergistic function between Pt and Ga_2O_3 in the dehydrogenation of propane. Recyclability tests demonstrate that the dehydrogenation activity stabilizes after three cycles over the Pt/Ga/Al_2O_3 catalyst.     

腐殖酸对La~(3+),Nd~(3+)等重金属离子混合体系吸附的研究

对含有La~(3+),Nd~(3+)的重金属混合体系进行吸附选择性试验,筛选出腐殖酸浓度为1.2 g·L~(-1)时吸附La~(3+),Nd~(3+)的最佳条件(pH=5.4,温度313 K,振荡时间8 h,重金属离子初始浓度0.15 mmol·L~(-1)),得出此条件下吸附优先顺序为:La~(3+)>Pb~(2+)>Cu~(2+)>Nd~(3+)>Cd~(2+)>Zn~(2+)>Co~(2+)>Cr~(3+);HA的吸附总量在室温下拟合二级动力学方程的效果最好;Langmuir方程则能更好地描述HA对重金属离子的等温吸附过程,并且随着温度的升高,HA的最大吸附量逐渐增加;HA对La~(3+),Nd~(3+)等重金属离子的吸附优先顺序受到pH值、温度、振荡时间、重金属离子初始浓度和本身性质的综合影响,且重金属的地球化学性质是主导因素.