Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.     

Local environment in Ba2In2−xWxO5+3x/2 oxide ion conductors

The actual oxygen environment of the tungsten dopant in the Ba₂In_2−xW_xO_5+3x/2 solid solution was revealed by combining X-ray absorption spectroscopy at the tungsten L_I and L_III edges and at the indium L_I edge. Whatever the substitution ratio, the tungsten atoms exhibit a regular octahedral environment. When the substitution ratio increases, the oxygen vacancies are progressively filled until their total occupancy for x=2/3. For x?0.3, the perovskite structure is stabilised; the tungsten atoms are randomly distributed in the structure. Although X-ray diffraction revealed a cubic symmetry for these compositions, a local distortion of the indium environment is observed when a tungsten atom is in its surrounding.     

Interactions of Ba2YCu3O6+y with the Gd3NbO7 buffer layer in coated conductors

A systematic study of the chemical interaction of Ba₂YCu₃O_6+y and Gd₃NbO₇ was conducted under two processing conditions: purified air (21% p_o2), and 100 Pa p_o2 (0.1% p_o2). Phases present along the pseudo-binary join Ba₂YCu₃O_6z and Gd₃NbO₇ were found to be in two five-phase volumes within the system. Three common phases that are present in all samples are (Y,Gd)₂Cu₂O₅, Ba(Y,Gd)₂CuO₅ and Cu₂O or CuO (depending on the processing conditions). The assemblies of phases can be categorized in three regions, with Ba₂YCu₃O_6+y: Gd₃NbO₇ ratios of (I)<5.5:4.5; (II)=5.5:4.5; and (III)>5.5:4.5. The lowest melting temperature of the system was determined to be ≈938 °C in air, and 850 °C at 100 Pa p_o2. Structure determinations of two selected phases, Ba₂(Gd_xY_1−x)NbO₆ (Fm3¯m, No. 225), and (Gd_xY_3−x)NbO₇ (C222₁, No. 20 and Ccmm, No. 63), were completed using the X-ray Rietveld refinement technique. Reference X-ray powder diffraction patterns for selected phases of Ba₂(Gd_xY_1−x)NbO₆ (x=0.2, 0.4, 0.6, and 0.8) and (Gd_xY_3−x)NbO₇ (x=0.6, 1.2, 1.8, 2.4 and 3) have been prepared for inclusion in the Powder Diffraction File (PDF).     

Synthesis and characterization of La2Mo2O9 obtained from freeze-dried precursors

La₂Mo₂O₉ ceramics have been prepared from freeze-dried precursors and their properties compared to those of lantanum molybdate obtained by conventional solid state (SS) reaction. All materials have been characterized by X-ray diffraction, scanning electron microscopy and thermal analysis (TGA/DTA/DSC and dilatometry) to characterize the phase formation and phase transition. When the freeze-dried method was applied, the synthesis temperature required to obtain dense samples was much lower than that for powders obtained by SS reaction. The morphology and structure of the oxide particle are significantly dependent on the synthesis method. The grain size is smaller, whereas the density of sintered pellets is higher for the freeze-dried precursor powder when compared with the SS reaction method. Impedance spectroscopy was used to measure the electrical conductivity of La₂Mo₂O₉ from 548 to 1123 K, in air, and to characterize the blocking effects of grain boundaries.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Synthesis and characterization of n=5, 6 members of the La4Srn−4TinO3n+2 series with layered structure based upon perovskite

Layered compounds have been synthesized and structurally characterized for the n=5 and 6 members of the perovskite-related family La₄Sr_n−4Ti_nO_3n+2 by combining X-ray diffraction and transmission electron microscopy. Their structure can be regarded as comprising [(La,Sr)₅Ti₅O₁₇] and [(La,Sr)₆Ti₆O₂₀] perovskite blocks joined by crystallographic shears along the a-axis, with consecutive blocks shifted by 1/2 [100]_p. The n=5 member is similar to the previously reported n=5 member of other A_nB_nO_3n+2-related series. The n=6 member, which has only been briefly reported in other systems previously, is also a well-behaved member of this A_nB_nO_3n+2 series.     

Synthesis, structure, and magnetism of Tb4PdGa12 and Tb4PtGa12

Single crystals of Tb₄MGa₁₂ (M=Pd, Pt) have been synthesized. The isostructural compounds crystallize in the cubic space group , with Z=2 and lattice parameters: a=8.5940(5) and 8.5850(3) Å for Tb₄PdGa₁₂ and Tb₄PtGa₁₂, respectively. The crystal structure consists of corner-sharing MGa₆ octahedra and TbGa₃ cuboctahedra. Magnetic measurements suggest that Tb₄PdGa₁₂ is an antiferromagnetic metamagnet with a Néel temperature of 16 K, while the Pt analog orders at T_N=12 K.     

Structure and properties of a novel cobaltate La0.30CoO2

The layered cobaltate La_0.30CoO₂ was prepared from Na_xCoO₂ precursor by a solid-state ionic exchange and was characterized by means of X-ray and neutron diffraction, magnetic, thermal and electric transport measurements. The compound consists of hexagonal sheets of edge-sharing CoO₆ octahedra interleaved by lanthanum monolayers. Compared to Na⁺ in the parent system, the La³⁺ ions occupy only one-third of available sites, forming a 2-dimensional superstructure. The deviation from the ideal stoichiometry La_1/3CoO₂ introduces extra hole carriers into the diamagnetic LS Co³⁺ matrix making the sample Pauli paramagnetic. The temperature dependence of the electrical conductivity in La_0.30CoO₂ follows Mott's T^−1/3 law up to about 400 K, which is in contrast with the standard metallic behavior in the Na⁺ homolog possessing the same formal doping. The experiments are complemented by electronic structure calculations for La_0.30CoO₂ and related Na_xCoO₂ systems.     

Structural, spectroscopic and photoluminescence studies of LiEu(WO4)2−x(MoO4)x as a near-UV convertible phosphor

A series of lithium europium double tungsto-molybdate phosphors LiEu(WO₄)_2−x(MoO₄)_x (x=0, 0.4, 0.8, 1.2, 1.6, 2.0) have been synthesized by solid-state reactions and their crystal structure, optical and luminescent properties were studied. As the molybdate content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm was found to increase and reach a maximum when the relative ratio of Mo/W is 2:0. These changes were found to be accompanied with the changes in the spectral feature, which can be attributed to the crystal field splitting of the ⁵D₀→⁷F₂ transition. As the molybdate content increases the emission intensity of the 615 nm peak also increases. The intense red-emission of the tungstomolybdate phosphors under near-UV excitation suggests them to be potential candidate for white light generation by using near-UV LEDs. In this study the effect of chemical compositions and crystal structure on the photoluminescent properties of LiEu(WO₄)_2−x(MoO₄)_x is investigated and discussed.     

Thermochemistry of Li1+xMn2−xO4 (0?x?1/3) spinel

Lithium substituted Li_1+xMn_2−xO₄ spinel samples in the entire solid solution range (0?x?1/3) were synthesized by solid-state reaction. The samples with x<0.25 are stoichiometric and those with x?0.25 are oxygen deficient. High-temperature oxide melt solution calorimetry in molten 3Na₂O·4MoO₃ at 974 K was performed to determine their enthalpies of formation from constituent binary oxides at 298 K. The cubic lattice parameter was determined from least-squares fitting of powder XRD data. The variations of the enthalpy of formation from oxides and the lattice parameter with x follow similar trends. The enthalpy of formation from oxides becomes more exothermic with x for stoichiometric compounds (x<0.25) and deviates endothermically from this trend for oxygen-deficient samples (x?0.25). This energetic trend is related to two competing substitution mechanisms of lithium for manganese (oxidation of Mn³⁺ to Mn⁴⁺ versus formation of oxygen vacancies). For stoichiometric spinels, the oxidation of Mn³⁺ to Mn⁴⁺ is dominant, whereas for oxygen-deficient compounds both mechanisms are operative. The endothermic deviation is ascribed to the large endothermic enthalpy of reduction.     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Direct syntheses of Lan+1NinO3n+1 phases (n=1, 2, 3 and ∞) from nanosized co-crystallites

A new direct route for the “bottom up” syntheses of phases in the La_n+1Ni_nO_3n+1 series (n=1, 2, 3 and ∞) has been achieved via single-step heat treatments of nanosized co-crystallized precursors. The co-crystallized precursors were prepared using a continuous hydrothermal flow synthesis system that uses a superheated water flow at ca. 400 °C and 24.1 MPa to produce nanoparticulate slurries. Overall, a significant reduction in time and number of steps for the syntheses of La₃Ni₂O₇ and La₄Ni₃O₁₀ was achieved compared with more conventional synthesis methods, which typically require multiple homogenization and reheating steps over several days.     

Enzyme mimics of spinel-type CoxNi1−xFe2O4 magnetic nanomaterial for eletroctrocatalytic oxidation of hydrogen peroxide

A series of spinel-type Co_xNi_1−xFe₂O₄ (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) magnetic nanomaterials were solvothermally synthesized as enzyme mimics for the eletroctrocatalytic oxidation of H₂O₂. X-ray diffraction and scanning electron microscope were employed to characterize the composition, structure and morphology of the material. The electrochemical properties of spinel-type Co_xNi_1−xFe₂O₄ with different (Co/Ni) molar ratio toward H₂O₂ oxidation were investigated, and the results demonstrated that Co_0.5Ni_0.5Fe₂O₄ modified carbon paste electrode (Co_0.5Ni_0.5Fe₂O₄/CPE) possessed the best electrocatalytic activity for H₂O₂ oxidation. Under optimum conditions, the calibration curve for H₂O₂ determination on Co_0.5Ni_0.5Fe₂O₄/CPE was linear in a wide range of 1.0 × 10⁻⁸–1.0 × 10⁻³ M with low detection limit of 3.0 × 10⁻⁹ M (S/N = 3). The proposed Co_0.5Ni_0.5Fe₂O₄/CPE was also applied to the determination of H₂O₂ in commercial toothpastes with satisfactory results, indicating that Co_xNi_1−xFe₂O₄ is a promising hydrogen peroxidase mimics for the detection of H₂O₂.     

Crystal Structure of Pseudorhombohedral InFe1−xTixO3+x/2 (x=2/3)

The structure of pseudorhombohedral-type InFe_1−xTi_xO_3−x/2 (x=2/3) was refined by Rietveld profile fitting. The crystal is a commensurate member of a series in a solution range on InFeO₃-In₂Ti₂O₇ including incommensurate structures. The structure with the unit cell of a=5.9188(1), b=10.1112(2), and c=6.3896(1) Å, β=108.018(2)°, and a space group P2₁/a is the alternate stacking of an edge-shared InO₆ octahedral layer and an Fe/Ti-O plane along c^*. Metal sites on the Fe/Ti-O plane are surrounded by four oxygen atoms on the Fe/Ti-O plane and two axial ones. Electric conductivities of the order 10⁻⁴ S/cm were observed for the samples at 1000 K, while the oxide ion transport number is almost zero as no electromotive force was detected by an oxygen concentration cell.     

Structure and magnetic properties of RE2Cu2Cd

The ternary intermetallic compounds RE₂Cu₂Cd (RE=Y, Sm, Gd-Tm, Lu) were synthesized by induction-melting of the elements in sealed tantalum tubes. The samples were characterized by X-ray powder diffraction. The structure of Gd₂Cu₂Cd was refined from single crystal X-ray diffractometer data: Mo₂FeB₂ type, space group P4/mbm, a=756.2(3), c=380.2(3) pm, wR2=0.0455, 321 F² values, 12 variables. The structures are 1:1 intergrowth variants of slightly distorted CsCl and AlB₂ related slabs of compositions RECd and RECu₂. The copper and cadmium atoms build up two-dimensional [Cu₂Cd] networks (257 pm Cu-Cu and 301 pm Cu-Cd in Gd₂Cu₂Cd) which are bonded to the rare earth atoms via short RE-Cu contacts (290 pm in Gd₂Cu₂Cd). Temperature dependent susceptibility measurements of RE₂Cu₂Cd with RE=Gd, Tb, Dy, and Tm show experimental magnetic moments which are close to the free RE³⁺ ion values. The four compounds show ferromagnetic ordering at T_C=116.7(2), 86.2(3), 48.4(1), and 14.5(1) K, respectively, as confirmed by heat capacity measurements. Dy₂Cu₂Cd shows a spin reorientation at T_N=16.9(1) K.     

Intercalation behavior of n-alkylamines into an A-site defective layered perovskite H2W2O7

Intercalation behavior of n-alkylamines into a protonated form of an A-site defective layered perovskite H₂W₂O₇ has been investigated. Results from XRD indicate these materials are layered with the corresponding interlayer spacing governed by the n-alkylamine chain length, and a reversible intercalation and deintercalation property is observed among these intercalation compounds. The IR spectra of the intercalation compounds with n-alkylamines clearly show that n-alkyl chains possess an all-trans conformation, and H₂W₂O₇ accommodate n-alkylamines (C_nH_2n+1NH₂: n=3, 4, 7, 8, 12, 16) to form intercalation compounds via an acid-base mechanism. A linear relationship between the interlayer distance and the number of carbon atoms in n-alkyl chains is observed to show a bilayer arrangement of the n-alkyl chains with a tilt angle of ∼71.6°. Elemental analysis studies reveal that the amounts of intercalated n-alkylamines are about 2.0 mol per [W₂O₇]. Despite the surface geometry of H₂W₂O₇ is almost identical to those of layered perovskites H₂[A_n−1B_nO_3n+1], the amounts of intercalated n-alkylamines of them are different. A reasonable explanation is given through our research.     

Synthesis, X-ray crystal structure and vibrational spectroscopy of the acidic pyrophosphate KMg0.5H2P2O7·H2O

The hydrated potassium hemimagnesium dihydrogen pyrophosphate KMg_0.5H₂P₂O₇·H₂O was synthesized. It crystallizes in the triclinic system, space group (n. 2), Z=2, with the following unit-cell parameters: a=6.8565(2) Å, b=7.3621(3) Å, c=7.6202(3) Å, α=81.044(2)°, β=72.248(2)°, γ=83.314(3)°, V=360.90(2) Å³. The structure was obtained by single-crystal X-ray diffractometry, and a full-matrix least-squares refinement based on F² gave a final R index of =0.0368 (wR=0.0975), utilizing 1446 observed reflections with I>2σ(I). The crystal packing consists in a three-dimensional network made by layers parallel to ab plane of PO₄ double tetrahedra and MgO₆ octahedra, linked by hydrogen bonds, while K atoms form complex coordination within cavities between tetrahedra and octahedra. The dihydro-pyrophosphate anion (H₂P₂O₇)²⁻ shows bent eclipsed conformation and the Mg²⁺ ion lies on inversion center. No coincidences observed between most of infrared and Raman spectral bands confirmed the centrosymmetric structure of the title compound; the vibrational spectra point to a bent POP bridge angle.     

Composition-induced structural phase transitions in the (Ba1−xLax)2In2O5+x (0?x?0.6) system

Composition-induced structural phase changes across the high temperature, fast oxide ion conducting (Ba_1−xLa_x)₂In₂O_5+x, 0?x?0.6, system have been carefully analysed using hard mode infrared (IR) powder absorption spectroscopy, X-ray powder diffraction and electron diffraction. An orthorhombic brownmillerite to three-dimensionally disordered cubic perovskite phase transition in this system is signalled by a drastic change in slope of both wavenumber and average line widths of IR spectra as a function of composition. Some evidence is found for the existence of an intermediate tetragonal phase (previously reported to exist from electron diffraction data) around x∼0.2. The new spectroscopic data have been used to compare microscopic and macroscopic strain parameters arising from variation in composition. The strain and spectroscopic data are consistent with first-order character for the tetragonal→orthorhombic transition, while the cubic→tetragonal transition could be continuous. Differences between the variation with composition of spectral parameters and of macroscopic strain parameters are consistent with a substantial order/disorder component for the transitions. There is also evidence for precursor effects within the cubic structure before symmetry is broken.