Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.     

Synthesis and characterization of La2Mo2O9 obtained from freeze-dried precursors

La₂Mo₂O₉ ceramics have been prepared from freeze-dried precursors and their properties compared to those of lantanum molybdate obtained by conventional solid state (SS) reaction. All materials have been characterized by X-ray diffraction, scanning electron microscopy and thermal analysis (TGA/DTA/DSC and dilatometry) to characterize the phase formation and phase transition. When the freeze-dried method was applied, the synthesis temperature required to obtain dense samples was much lower than that for powders obtained by SS reaction. The morphology and structure of the oxide particle are significantly dependent on the synthesis method. The grain size is smaller, whereas the density of sintered pellets is higher for the freeze-dried precursor powder when compared with the SS reaction method. Impedance spectroscopy was used to measure the electrical conductivity of La₂Mo₂O₉ from 548 to 1123 K, in air, and to characterize the blocking effects of grain boundaries.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Local environment in Ba2In2−xWxO5+3x/2 oxide ion conductors

The actual oxygen environment of the tungsten dopant in the Ba₂In_2−xW_xO_5+3x/2 solid solution was revealed by combining X-ray absorption spectroscopy at the tungsten L_I and L_III edges and at the indium L_I edge. Whatever the substitution ratio, the tungsten atoms exhibit a regular octahedral environment. When the substitution ratio increases, the oxygen vacancies are progressively filled until their total occupancy for x=2/3. For x?0.3, the perovskite structure is stabilised; the tungsten atoms are randomly distributed in the structure. Although X-ray diffraction revealed a cubic symmetry for these compositions, a local distortion of the indium environment is observed when a tungsten atom is in its surrounding.     

Interactions of Ba2YCu3O6+y with the Gd3NbO7 buffer layer in coated conductors

A systematic study of the chemical interaction of Ba₂YCu₃O_6+y and Gd₃NbO₇ was conducted under two processing conditions: purified air (21% p_o2), and 100 Pa p_o2 (0.1% p_o2). Phases present along the pseudo-binary join Ba₂YCu₃O_6z and Gd₃NbO₇ were found to be in two five-phase volumes within the system. Three common phases that are present in all samples are (Y,Gd)₂Cu₂O₅, Ba(Y,Gd)₂CuO₅ and Cu₂O or CuO (depending on the processing conditions). The assemblies of phases can be categorized in three regions, with Ba₂YCu₃O_6+y: Gd₃NbO₇ ratios of (I)<5.5:4.5; (II)=5.5:4.5; and (III)>5.5:4.5. The lowest melting temperature of the system was determined to be ≈938 °C in air, and 850 °C at 100 Pa p_o2. Structure determinations of two selected phases, Ba₂(Gd_xY_1−x)NbO₆ (Fm3¯m, No. 225), and (Gd_xY_3−x)NbO₇ (C222₁, No. 20 and Ccmm, No. 63), were completed using the X-ray Rietveld refinement technique. Reference X-ray powder diffraction patterns for selected phases of Ba₂(Gd_xY_1−x)NbO₆ (x=0.2, 0.4, 0.6, and 0.8) and (Gd_xY_3−x)NbO₇ (x=0.6, 1.2, 1.8, 2.4 and 3) have been prepared for inclusion in the Powder Diffraction File (PDF).     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Thermal stability and crystal structure of β-Ba3YB3O9

A new compound, β-Ba₃YB₃O₉, has been attained through solid phase transition from α-Ba₃YB₃O₉ at high temperatures. Differential thermal analysis (DTA) revealed the phase transition at about 1120°C, the melting temperature at about 1253°C. Its crystal structure has been determined from powder X-ray diffraction data. The refinement was carried out using the Rietveld method and the final refinement converged with R_p=10.5% and R_wp=13.7%. This compound belongs to the hexagonal space group R-3, with lattice parameters a=13.0441(1) Å and c=9.5291(1) Å. There are 6 formulas per unit cell and 7 atoms in the asymmetric unit. The structure of β-Ba₃YB₃O₉ is built up from Ba(Y)O₈, BaO₆ and YB₆O₁₈ units formed by one YO₆ octahedron and six BO₃ triangles with shared O atoms.     

Hydrothermal synthesis and magnetic properties of RMn2O5 (R=La, Pr, Nd, Tb, Bi) and LaMn2O5+δ

RMn₂O₅ (R=La, Pr, Nd, Tb, Bi) crystallites were prepared by a mild hydrothermal method and characterized by powder X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy (XPS) and magnetic measurement. The formation of manganates was sensitive to the alkalinities and Mn-containing precursors of the reaction mixtures. This family of manganates is isostructural and has a space group of Pbam. The magnetic measurements for RMn₂O₅ showed an antiferromagnetic transition. The strong irreversibility between the ZFC and FC curves indicated a helicoidally magnetic structure below 40 K. The max d.c. susceptibilities of LaMn₂O_5+δ (δ=0.01, 0.06, 0.08, 0.16, 0.17) were found to be variable and the excess oxygen (δ) in the compounds was influenced by the alkalinity used in the hydrothermal synthesis.     

Synthesis and characterization of n=5, 6 members of the La4Srn−4TinO3n+2 series with layered structure based upon perovskite

Layered compounds have been synthesized and structurally characterized for the n=5 and 6 members of the perovskite-related family La₄Sr_n−4Ti_nO_3n+2 by combining X-ray diffraction and transmission electron microscopy. Their structure can be regarded as comprising [(La,Sr)₅Ti₅O₁₇] and [(La,Sr)₆Ti₆O₂₀] perovskite blocks joined by crystallographic shears along the a-axis, with consecutive blocks shifted by 1/2 [100]_p. The n=5 member is similar to the previously reported n=5 member of other A_nB_nO_3n+2-related series. The n=6 member, which has only been briefly reported in other systems previously, is also a well-behaved member of this A_nB_nO_3n+2 series.     

Synthesis, structure and physical properties of Ru ferrites: BaMRu5O11 (M=Li and Cu) and BaM′2Ru4O11 (M′=Mn, Fe and Co)

The synthesis, structure, and physical properties of five R-type Ru ferrites with chemical formula BaMRu₅O₁₁ (M=Li and Cu) and BaM′₂Ru₄O₁₁ (M′=Mn, Fe and Co) are reported. All the ferrites crystallize in space group P6₃/mmc and consist of layers of edge sharing octahedra interconnected by pairs of face sharing octahedra and isolated trigonal bipyramids. For M=Li and Cu, the ferrites are paramagnetic metals with the M atoms found on the trigonal bipyramid sites exclusively. For M′=Mn, Fe and Co, the ferrites are soft ferromagnetic metals. For M′=Mn, the Mn atoms are mixed randomly with Ru atoms on different sites. The magnetic structure for BaMn₂Ru₄O₁₁ is reported.     

Preparation and photoluminescence properties of RE:Na3La9O3(BO3)8 (RE=Er, Yb) crystals

Using Na₂CO₃-H₃BO₃-NaF as fluxes, transparent RE:Na₃La₉O₃(BO₃)₈ (abbr. RE:NLBO, RE=Er, Yb) crystals have been grown by the top seed solution growth (TSSG) method. The X-ray powder diffraction analysis shows that the RE:NLBO crystals have the same structure with NLBO. The element contents were determined by molar to be 0.64% Er³⁺ in Er:NLBO, 2.70% Yb³⁺ in Yb:NLBO, respectively. The polarized absorption spectra of RE:NLBO have been measured at room temperature and show that both Er:NLBO and Yb:NLBO have a strong absorption bands near 980 nm with wide FWHM (Full Wave at Half Maximum) (21 nm for Er:NLBO and 25 nm for Yb:NLBO). Fluorescence spectra have been recorded. Yb:NLBO has the emission peaks at 985 nm, 1028 nm and 1079 nm and the emission peak of Er:NLBO is at 1536 nm. Spectral parameters have been calculated by the Judd-Ofelt theory for Er:NLBO and the reciprocity method for Yb:NLBO, respectively. The calculated values show that Er:NLBO is a candidate of 1.55 μm laser crystals and Yb:NLBO is a candidate for self-frequency doubling crystal.     

Synthesis of layered cathode material Li[CoxMn1−x]O2 from layered double hydroxides precursors

Cathode materials Li[Co_xMn_1−x]O₂ for lithium secondary batteries have been prepared by a new route—precursor method of layered double hydroxides (LDHs). In situ high-temperature X-ray diffraction (HT-XRD) and thermogravimetric analysis coupled with mass spectrometry (TG-MS) were used to monitor the structural transformation during the reaction of CoMn LDHs and LiOH·H₂O: firstly the layered structure of LDHs transformed to an intermediate phase with spinel structure; then the distortion of the structure occurred with the intercalation of Li⁺ into the lattice, resulting in the formation of layered Li[Co_xMn_1−x]O₂ with α-NaFeO₂ structure. Extended X-ray absorption fine structure (EXAFS) data showed that the Co-O bonding length and the coordination number of Co were close to those of Mn in Li[Co_xMn_1−x]O₂, which indicates that the local environments of the transitional metals are rather similar. X-ray photoelectron spectroscopy (XPS) was used to measure the oxidation state of Co and Mn. The influences of Co/Mn ratio on both the structure and electrochemical property of Li[Co_xMn_1−x]O₂ have been investigated by XRD and electrochemical tests. It has been found that the products synthesized by the precursor method demonstrated a rather stable cycling behavior, with a reversible capacity of 122.5 mAh g⁻¹ for the layered material Li[Co_0.80Mn_0.20]O₂.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Thermoelectric properties of Ag-doped n-type (Bi2Te3)0.9-(Bi2−xAgxSe3)0.1 (x=0-0.4) alloys prepared by spark plasma sintering

Ag-doped n-type (Bi₂Te₃)_0.9-(Bi_2−xAg_xSe₃)_0.1 (x=0-0.4) alloys were prepared by spark plasma sintering and their physical properties evaluated. When at low Ag content (x=0.05), the temperature dependence of the lattice thermal conductivity follows the trend of (Bi₂Te₃)_0.9-(Bi₂Se₃)_0.1; while at higher Ag content, a relatively rapid reduction above 400 K can be observed due possibly to the enhancement of scattering of phonons by the increased defects. The Seebeck coefficient increases with Ag content, with some loss of electrical conductivity, but the maximum dimensionless figure of merit ZT can be obtained to be 0.86 for the alloy with x=0.4 at 505 K, about 0.2 higher than that of the alloy (Bi₂Te₃)_0.9-(Bi₂Se₃)_0.1 without Ag-doping.     

Intercalation behavior of n-alkylamines into an A-site defective layered perovskite H2W2O7

Intercalation behavior of n-alkylamines into a protonated form of an A-site defective layered perovskite H₂W₂O₇ has been investigated. Results from XRD indicate these materials are layered with the corresponding interlayer spacing governed by the n-alkylamine chain length, and a reversible intercalation and deintercalation property is observed among these intercalation compounds. The IR spectra of the intercalation compounds with n-alkylamines clearly show that n-alkyl chains possess an all-trans conformation, and H₂W₂O₇ accommodate n-alkylamines (C_nH_2n+1NH₂: n=3, 4, 7, 8, 12, 16) to form intercalation compounds via an acid-base mechanism. A linear relationship between the interlayer distance and the number of carbon atoms in n-alkyl chains is observed to show a bilayer arrangement of the n-alkyl chains with a tilt angle of ∼71.6°. Elemental analysis studies reveal that the amounts of intercalated n-alkylamines are about 2.0 mol per [W₂O₇]. Despite the surface geometry of H₂W₂O₇ is almost identical to those of layered perovskites H₂[A_n−1B_nO_3n+1], the amounts of intercalated n-alkylamines of them are different. A reasonable explanation is given through our research.     

Effect of boron non-stoichiometry on B-site in perovskite type structure ScBxRh3 and CeBxRh3 on charges of atoms on A-site: study by X-ray photoelectron and nuclear magnetic resonance spectroscopies

The solid solutions of ScBRh₃-ScRh₃ and CeBRh₃-CeRh₃ are synthesized by the arc melting method, where RBRh₃ and RRh₃ (R=rare earth element) have perovskite and AuCu₃ type structures, respectively. The binding energy of Sc 2p_3/2 for ScB_xRh₃ increases with the boron concentration. The Knight shift of ⁴⁵Sc observed by nuclear magnetic resonance spectroscopy decreases with increase of boron concentration. The decrement of the Knight shift corresponds the Sc 4s electron density at the Fermi level. The intensity ratio of f²: f¹: f⁰ of Ce 3d XPS spectrum changes with boron concentration of CeB_xRh₃. It is concluded that in both cases of ScB_xRh₃ and CeB_xRh₃ the charge on the atoms on A-site changes with the concentration of the atoms on B-site, where the atoms are not directly bound.     

Electronic structure and photocatalytic properties of ABi2Ta2O9 (A=Ca, Sr, Ba)

A new series of layered perovskite photocatalysts, ABi₂Ta₂O₉ (A=Ca, Sr, Ba), were synthesized by the conventional solid-state reaction method and the crystal structures were characterized by powder X-ray diffraction. The results showed that the structure of ABi₂Ta₂O₉ (A=Ca, Sr) is orthorhombic, while that of BaBi₂Ta₂O₉ is tetragonal. First-principles calculations of the electronic band structures and density of states (DOS) revealed that the conduction bands of these photocatalysts are mainly attributable to the Ta 5d+Bi 6p+O 2p orbitals, while their valence bands are composed of hybridization with O 2p+Ta 5d+Bi 6s orbitals. Photocatalytic activities for water splitting were investigated under UV light irradiation and indicated that these photocatalysts are highly active even without co-catalysts. The formation rate of H₂ evolution from an aqueous methanol solution is about 2.26 mmol h^-1 for the photocatalyst SrBi₂Ta₂O₉, which is much higher than that of CaBi₂Ta₂O₉ and BaBi₂Ta₂O₉. The photocatalytic properties are discussed in close connection with the crystal structure and the electronic structure in details.     

Structural, spectroscopic and photoluminescence studies of LiEu(WO4)2−x(MoO4)x as a near-UV convertible phosphor

A series of lithium europium double tungsto-molybdate phosphors LiEu(WO₄)_2−x(MoO₄)_x (x=0, 0.4, 0.8, 1.2, 1.6, 2.0) have been synthesized by solid-state reactions and their crystal structure, optical and luminescent properties were studied. As the molybdate content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm was found to increase and reach a maximum when the relative ratio of Mo/W is 2:0. These changes were found to be accompanied with the changes in the spectral feature, which can be attributed to the crystal field splitting of the ⁵D₀→⁷F₂ transition. As the molybdate content increases the emission intensity of the 615 nm peak also increases. The intense red-emission of the tungstomolybdate phosphors under near-UV excitation suggests them to be potential candidate for white light generation by using near-UV LEDs. In this study the effect of chemical compositions and crystal structure on the photoluminescent properties of LiEu(WO₄)_2−x(MoO₄)_x is investigated and discussed.     

Direct syntheses of Lan+1NinO3n+1 phases (n=1, 2, 3 and ∞) from nanosized co-crystallites

A new direct route for the “bottom up” syntheses of phases in the La_n+1Ni_nO_3n+1 series (n=1, 2, 3 and ∞) has been achieved via single-step heat treatments of nanosized co-crystallized precursors. The co-crystallized precursors were prepared using a continuous hydrothermal flow synthesis system that uses a superheated water flow at ca. 400 °C and 24.1 MPa to produce nanoparticulate slurries. Overall, a significant reduction in time and number of steps for the syntheses of La₃Ni₂O₇ and La₄Ni₃O₁₀ was achieved compared with more conventional synthesis methods, which typically require multiple homogenization and reheating steps over several days.