可磁分离二氧化钛光催化剂的制备及其光催化性能

通过液相催化相转化的方法制备了一种可磁分离的光催化剂TiO₂/SiO₂/NiFe₂O₄(TSN),这种光催化剂显示出了超顺磁性,能够通过外加磁场方便的实现催化剂在水中的分离与回收。该光催化剂的X-射线衍射和TEM结果表明：纳米TiO₂颗粒包裹在磁性颗粒-SiO₂/NiFe₂O₄(SN)的周围形成TiO₂层。利用光催化降解甲基橙的效果来考察了这种光催化剂的活性,结果表明：在NiFe₂O₄和TiO₂之间包覆一层无定型的SiO₂,可以显著的提高催化剂的脱色效果,3次循环后,仍能保持良好的催化活性。     

In Situ Confined Growth Based on a Self‐Templating Reduction Strategy of Highly Dispersed Ni Nanoparticles in Hierarchical Yolk–Shell Fe@SiO2 Structures as Efficient Catalysts

Ni‐based magnetic catalysts exhibit moderate activity, low cost, and magnetic reusability in hydrogenation reactions. However, Ni nanoparticles anchored on magnetic supports commonly suffer from undesirable agglomeration during catalytic reactions due to the relatively weak affinity of the magnetic support for the Ni nanoparticles. A hierarchical yolk–shell Fe@SiO₂/Ni catalyst, with an inner movable Fe core and an ultrathin SiO₂/Ni shell composed of nanosheets, was synthesized in a self‐templating reduction strategy with a hierarchical yolk–shell Fe₃O₄@nickel silicate nanocomposite as the precursor. The spatial confinement of highly dispersed Ni nanoparticles with a mean size of 4 nm within ultrathin SiO₂ nanosheets with a thickness of 2.6 nm not only prevented their agglomeration during catalytic transformations but also exposed the abundant active Ni sites to reactants. Moreover, the large inner cavities and interlayer spaces between the assembled ultrathin SiO₂/Ni nanosheets provided suitable mesoporous channels for diffusion of the reactants towards the active sites. As expected, the Fe@SiO₂/Ni catalyst displayed high activity, high stability, and magnetic recoverability for the reduction of nitroaromatic compounds. In particular, the Ni‐based catalyst in the conversion of 4‐nitroamine maintained a rate of over 98 % and preserved the initial yolk–shell structure without any obvious aggregation of Ni nanoparticles after ten catalytic cycles, which confirmed the high structural stability of the Ni‐based catalyst.     

Hierarchical Fe3O4@TiO2 Yolk–Shell Microspheres with Enhanced Microwave‐Absorption Properties

A facile and efficient strategy for the synthesis of hierarchical yolk–shell microspheres with magnetic Fe₃O₄ cores and dielectric TiO₂ shells has been developed. Various Fe₃O₄@TiO₂ yolk–shell microspheres with different core sizes, interstitial void volumes, and shell thicknesses have been successfully synthesized by controlling the synthetic parameters. Moreover, the microwave absorption properties of these yolk–shell microspheres, such as the complex permittivity and permeability, were investigated. The electromagnetic data demonstrate that the as‐synthesized Fe₃O₄@TiO₂ yolk–shell microspheres exhibit significantly enhanced microwave absorption properties compared with pure Fe₃O₄ and our previously reported Fe₃O₄@TiO₂ core–shell microspheres, which may result from the unique yolk–shell structure with a large surface area and high porosity, as well as synergistic effects between the functional Fe₃O₄ cores and TiO₂ shells.     

Evaluating the efficiency of the GO‐Fe3O4/TiO2 mesoporous photocatalyst for degradation of chlorpyrifos pesticide under visible light irradiation

In this work, the photocatalytic activity of the synthesized graphene oxide (GO)‐Fe₃O₄/TiO₂ mesoporous photocatalysts was evaluated using chlorpyrifos (CP) as a contaminant. The nano‐photocatalyst was characterized by X‐ray diffraction, field emission scanning electron microscopy with energy‐dispersive X‐ray spectroscopy, transmission electron microscopy, and specific surface area by the Brunauer–Emmett–Teller method. Using visible light, the GO‐Fe₃O₄/TiO₂ mesoporous photocatalyst was investigated on the degradation of CP pesticide. The GO‐Fe₃O₄/TiO₂ photocatalyst displayed a good photocatalytic activity, which was achieving 97% of CP degradation after 60 min. Finally, experiments were performed to evaluate GO‐Fe₃O₄/TiO₂ mesoporous nanocatalyst activity on repeated applications; after several uses, its photocatalytic activity was retained, which indicated stability.     

Synthesis,characterization and photocatalytic application of TiO2/magnetic graphene for efficient photodegradation of crystal violet

A magnetized nano‐photocatalyst based on TiO₂/magnetic graphene was developed for efficient photodegradation of crystal violet (CV). Scanning electron microscopy, X‐ray diffraction, energy‐dispersive X‐ray spectroscopy and elemental mapping were used to characterize the prepared magnetic nano‐photocatalyst. The photocatalytic activity of the synthesized magnetic nano‐photocatalyst was evaluated using the decomposition of CV as a model organic pollutant under UV light irradiation. The obtained results showed that TiO₂/magnetic graphene exhibited much higher photocatalytic performance than bare TiO₂. Incorporation of graphene enhanced the activity of the prepared magnetic nano‐photocatalyst. TiO₂/magnetic graphene can be easily separated from an aqueous solution by applying an external magnetic field. Effects of pH, magnetized nano‐photocatalyst dosage, UV light irradiation time, H₂O₂ amount and initial concentration of dye on the photodegradation efficiency were evaluated and optimized. Efficient photodegradation (>98%) of the selected dye under optimized conditions using the synthesized nano‐photocatalyst under UV light irradiation was achieved in 25 min. The prepared magnetic nano‐photocatalyst can be used in a wide pH range (4–10) for degradation of CV. The effects of scavengers, namely methanol (OH^? scavenger), p‐benzoquinone (O₂^?? scavenger) and disodium ethylenediaminetetraacetate (hole scavenger), on CV photodegradation were investigated.     

Synthesis and properties of magnetically separable Fe3O4/TiO2/Bi2O3 photocatalysts

The Fe₃O₄/TiO₂/Bi₂O₃ composites were synthesized by a sol–gel method and used as improved photocatalysts for the degradation of methyl orange (MO) under simulated sunlight at room temperature. The as-prepared Fe₃O₄/TiO₂/Bi₂O₃ composites were characterized by X-ray diffraction, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and diffuse reflectance spectroscopy (DRS). TEM analysis reveals that the composite has a core–shell structure and diameters of Fe₃O₄ core is about 200 nm. DRS results reveal that all composites showed red shift in optical absorption. TiO₂, Fe₃O₄, and Bi₂O₃ exist mainly as separate phases in the Fe₃O₄/TiO₂/Bi₂O₃ composites based on XPS analysis. The photocatalytic degradation of MO with the prepared photocatalysts was studied under simulated sunlight illumination. Photocatalytic reactivity test indicated that the removal efficiency of MO with the Fe₃O₄/TiO₂/Bi₂O₃ photocatalyst was higher than that of pure TiO₂ and Fe₃O₄/TiO₂. Recovery rate of Fe₃O₄/TiO₂/Bi₂O₃ photocatalysts achieved 80 % after five times reuse.     

Preparation and characterization of rapid magnetic recyclable Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript>@TiO<Subscript>2</Subscript>–Sn photocatalyst

Effective procedure to synthesize Fe₃O₄@SiO₂@TiO₂–Sn magnetically separable photocatalyst by a combination of co-precipitation, sol–gel and photodeposition methods was introduced. Products were characterized by XRD, SEM, VSM, EDS, DRS, TEM, ICP-OES and IR techniques. The dimensions of catalyst particle size were evaluated by scanning electron microscopy, and results approved nanoscale size for product. In addition, studying the magnetic nature by VSM analysis showed superparamagnetic properties for all samples. XRD pattern indicates that TiO₂ coated on Fe₃O₄@SiO₂ core well crystallized at 400 °C in anatase phase. Synthesized photocatalyst shows good photocatalytic performance in decolorization of rhodamine B aqueous solution. The composite nanoparticles showed high recycling efficiency and stability over five separation cycles.     

Synthesis of nanostructured magnetic photocatalyst by colloidal approach and spray-drying technique

Nanostructured particles with a magnetic core and a photocatalytic shell are very interesting systems for their properties to be magnetically separable (and so reusable) in photocatalytic water depuration implant. Here, a robust, low time-consuming, easily scale up method to produce Fe₃O₄/SiO₂/TiO₂ hierarchical nanostructures starting from commercial precursors (i.e. Fe₃O₄, SiO₂) by employing a colloidal approach (i.e. heterocoagulation) coupled with the spray-drying technique is presented. In particular, a self-assembled layer-by-layer methodology based on the coagulation of dissimilar colloidal particles was applied. First, a passive layer of silica (SiO₂, amorphous) was created on magnetite in order to avoid detrimental phenomena arising from the direct contact between magnetite and titania, then the deposition of titania onto silica-coated-magnetite was promoted. TiO₂, SiO₂ and Fe₃O₄ nanosols were characterized in terms of zeta potential, optimized and a self-assembled layer-by-layer approach was followed in order to promote the heterocoagulation of silica onto magnetite surface and of titania onto silica coated magnetite. Once optimized the colloidal route, the mixture was then spray-dried to obtain a granulated powder with nano-scale reactivity, easier to handle and re-disperse in comparison to starting nanopowders with the same surface properties. The nanostructured particles have been characterized by different techniques such as SEM, TEM, XDR and their magnetic properties have been investigated. Moreover, preliminary photocatalytic texts have been performed.     

Photodegradation of Direct Blue-199 in carpet industry wastewater using iron-doped TiO2 nanoparticles and regenerated photocatalyst

Fe-doped TiO_2, Ti_1–xFe_xO₂ (x = 0.00, 0.02, 0.04, 0.06, 0.08, and 0.10), photocatalysts have been successfully synthesized via citric acid–assisted autocombustion method. The synthesized photocatalysts were characterized using different characterization techniques, such as X-ray diffraction (XRD), diffuse reflectance spectroscopy (DRS), Fourier transform infrared (FT-IR), transmission electron microscopy (TEM), energy dispersive x-ray spectroscopy (EDX), and x-ray photoelectron spectroscopy (XPS). The XRD diffraction patterns revealed that synthesized photocatalysts have the anatase phase of TiO₂. The DRS analysis indicates a slight increment in absorbance in the visible light region by the Fe doping in TiO₂. The FT-IR spectra reveal the various stretching and bending vibrational bands of the Ti–O lattice. The XPS spectra confirm the presence of elements titanium, oxygen, and iron in the synthesized samples and determine binding energy of elements. TEM analysis shows the shape of the synthesized photocatalyst, and it was used to calculate the average particle sizes of undoped and Fe-doped TiO₂ (Ti_0.96Fe_0.04O₂) photocatalysts using a histogram. The photocatalytic activities of synthesized photocatalysts were determined by photodegradation of dye (Direct Blue 199), contaminating carpet industry wastewater in the photochemical reactor and open pan reactor. The maximum photodegradation activity was shown by the Ti_0.96Fe_0.04O₂ photocatalyst among all the synthesized undoped and Fe-doped photocatalysts. The synthesized photocatalyst (Ti_0.96Fe_0.04O₂) had better photocatalytic activity when compared to both, undoped TiO₂ and Aeroxide (Degussa) P-25. The used Fe-doped TiO₂ photocatalyst (Ti_0.96Fe_0.04O₂) was regenerated five times and investigated for its photocatalytic activity.     

Highly selective and recyclable hydrogenation of α‐pinene catalyzed by ruthenium nanoparticles loaded on amphiphilic core–shell magnetic nanomaterials

A multifunctional nanomaterial (Fe₃O₄@SiO₂@C_X@NH₂) comprising a magnetic core, a silicon protective interlayer, and an amphiphilic silica shell is successfully prepared. Ru nanoparticles catalyst loaded on Fe₃O₄@SiO₂@C_X@NH₂ is used in hydrogenation of α‐pinene for the first time. The novel nanomaterial with amphipathy can be used as a solid foaming agent to increase gas–liquid–solid three‐phase contact and accelerate the reaction. Under the mild conditions (40 °C, 1 MPa H₂, 3 h), 99.9% α‐pinene conversion and 98.9% cis‐pinane selectivity are obtained, which is by far the best results reported. Furthermore, the magnetic nanocomposite catalyst can be easily separated by an external magnet and reused nine times with high selectivity maintaining.     

Synthesis of a new magnetic nano-island titania photocatalyst and investigation of its photocatalytic activity

In this study, a new magnetic nano-island titania photocatalyst (Fe₃O₄@SiO₂·TiO₂) was designed and fabricated. Precipitation, sol-gel, and hydrothermal methods were utilized to synthesize the magnetite, silica shell, and titania islands, respectively. Characterization of the synthesized catalyst was carried out by XRD, EDS, FTIR, SEM, TEM, and VSM analysis. The TEM analysis revealed that the overall size of the catalyst is about 490 nm, and titania island on the magnetic core was about 50 nm. VSM analysis showed that the photocatalyst has a fantastic paramagnetic property with magnetic saturation of 52 emu g^?1. Furthermore, photocatalytic activity of the synthesized catalyst was evaluated in the removal of p-nitrophenol as a typical pollutant of nitro-aromatic compounds such that its degradation and mineralization efficiency were obtained at 82 and 45% after 100 and 200 min of the process, respectively, using 100 ppm of the photocatalyst in pH = 6.5.     

Mesoporous Core–Shell Fenton Nanocatalyst: A Mild,Operationally Simple Approach to the Synthesis of Adipic Acid

Mesoporous nanoparticles composed of γ‐Al₂O₃ cores and α‐Fe₂O₃ shells were synthesized in aqueous medium. The surface charge of γ‐Al₂O₃ helps to form the core–shell nanocrystals. The core–shell structure and formation mechanism have been investigated by wide‐angle XRD, energy‐dispersive X‐ray spectroscopy, and elemental mapping by ultrahigh‐resolution (UHR) TEM and X‐ray photoelectron spectroscopy. The N₂ adsorption–desorption isotherm of this core–shell materials, which is of type IV, is characteristic of a mesoporous material having a BET surface area of 385 m² g^?1 and an average pore size of about 3.2 nm. The SEM images revealed that the mesoporosity in this core–shell material is due to self‐aggregation of tiny spherical nanocrystals with sizes of about 15–20 nm. Diffuse‐reflectance UV/Vis spectra, elemental mapping by UHRTEM, and wide‐angle XRD patterns indicate that the materials are composed of aluminum oxide cores and iron oxide shells. These Al₂O₃@Fe₂O₃ core–shell nanoparticles act as a heterogeneous Fenton nanocatalyst in the presence of hydrogen peroxide, and show high catalytic efficiency for the one‐pot conversion of cyclohexanone to adipic acid in water. The heterogeneous nature of the catalyst was confirmed by a hot filtration test and analysis of the reaction mixture by atomic absorption spectroscopy. The kinetics of the reaction was monitored by gas chromatography and ¹H NMR spectroscopy. The new core–shell catalyst remained in a separate solid phase, which could easily be removed from the reaction mixture by simple filtration and the catalyst reused efficiently.     

Stable aqueous dispersion of magnetic iron oxide core–shell nanoparticles prepared by biocompatible maleate polymers

A new method is applied to prepare stable aqueous dispersion of magnetic iron oxide nanoparticles (MNPs) by biocompatible maleate polymers. Fe₃O₄ magnetic core–shell nanoparticles are obtained via forming an inclusion complex between carboxylic acid groups of maleated biocompatible polymers shell and Fe₃O₄ MNPs core surface. Maleate polymers are synthesized via esterification of poly(ethylene glycol), poly(vinyl alcohol) and starch with maleic anhydride (MA). The Fe₃O₄ magnetic core–shell nanoparticles are characterized by Fourier transform infrared spectroscopy, X‐ray diffraction, transmission electron microscopy and vibrating sample magnetometer. The obtained magnetic core–shell nanoparticles exhibit superparamagnetic property and reveal long‐term aqueous stability. This work represents a valid methodology to produce highly stable aqueous dispersion of Fe₃O₄ MNPs ferrofluids which can be expected to have great potential as contrast agent for magnetic resonance imaging. Furthermore, the shell composition of biocompatible maleate polymers with double bond of MA as crosslinker agent allows the polymerization with other monomers to design preferred drug delivery systems. Copyright © 2014 John Wiley & Sons, Ltd.     

Superparamagnetic Fe3O4@SiO2 core–shell composite nanoparticles for the mixed hemimicelle solid‐phase extraction of benzodiazepines from hair and wastewater samples before high‐performance liquid chromatography analysis

Magnetic Fe₃O₄/SiO₂ composite core–shell nanoparticles were synthesized, characterized, and applied for the surfactant‐assisted solid‐phase extraction of five benzodiazepines diazepam, oxazepam, clonazepam, alprazolam, and midazolam, from human hair and wastewater samples before high‐performance liquid chromatography with diode array detection. The nanocomposite was synthesized in two steps. First, Fe₃O₄ nanoparticles were prepared by the chemical co‐precipitation method of Fe(III) and Fe(II) as reaction substrates and NH₃/H₂O as precipitant. Second, the surface of Fe₃O₄ nanoparticles was modified with shell silica by Stober method using tetraethylorthosilicate. The Fe₃O₄/SiO₂ composite were characterized by X‐ray diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy, and vibrating sample magnetometry. To enhance their adsorptive tendency toward benzodiazepines, cetyltrimethylammonium bromide was added, which was adsorbed on the surface of the Fe₃O₄/SiO₂ nanoparticles and formed mixed hemimicelles. The main parameters affecting the efficiency of the method were thoroughly investigated. Under optimum conditions, the calibration curves were linear in the range of 0.10–15 μgmL^?1. The relative standard deviations ranged from 2.73 to 7.07%. The correlation coefficients varied from 0.9930 to 0.9996.     

Surface Modification of a Magnetic SiO2 Support and Immobilization of a Nano-TiO2 Photocatalyst on It

This study presented an effective method to modify the surface chemical reactivity of a SiO₂/Fe₃O₄ support. The unmodified SiO₂/Fe₃O₄ support was prepared by the hydrolysis and condensation of tetraethoxysilane on the surface of hydrophilic Fe₃O₄ nanoparticles. These were then modified by a heat treatment in an ethanol/water solution under reflux. The resulting samples were characterized by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and transmission/scanning electron microscopy. The immobilization of a TiO₂ nanocatalyst on both unmodified and modified supports was performed to investigate the effects of the modification of the magnetic silica support on the loading of a TiO₂ nanocatalyst and the photocatalytic activity. The loading of TiO₂ and the photocatalytic activity were both improved.     

Catalytic Properties of TiO<Subscript>2</Subscript>/Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> Nanoparticles in Plasma Chemical Treatment

We proposed here a new process coupling dielectric barrier discharge (DBD) plasma with magnetic photocatalytic material nanoparticles for improving yield in DBD degradation of methyl orange (MO). TiO₂ doped Fe₃O₄ (TiO₂/Fe₃O₄) was prepared by the sol-gel method and used as a new type of magnetic photocatalyst in DBD system. It was found that the introduction of TiO₂/Fe₃O₄ in DBD system could effectively make use of the energy generated in DBD process and improve hydroxyl radical contributed by the main surface Fenton reaction, photocatalytic reaction and catalytic decomposition of dissolved ozone. Most part of MO (88%) was degraded during 30 min at peak voltage of 13 kV and TiO₂/Fe₃O₄ load of 100 mg/L, with a rate constant of 0.0731 min^?1 and a degradation yield of 7.23 g/(kW h). The coupled system showed higher degradation efficiency for MO removal.     

Preparation of Magnetic Photocatalyst TiO2 Supported on NiFe2O4 and Effect of Magnetic Carrier on Photocatalytic Activity

A magnetic photocatalyst TiO₂/NiFe₂O₄ (TN) with typical ferromagnetic hysteresis was prepared by a sol‐gel method, which is easy to be separated from a slurry‐type photoreactor under the application of an external magnetic field, being one of promising photocatalysts for wastewater treatment. The analysis of XRD indicated that the highly dispersed NiFe₂O₄ nanoparticles prevented the formation of rutile phase to some extent. A transmission electron microscope (TEM) was used to characterize the structure of the photocatalyst, indicating that the NiFe₂O₄ nanoparticles highly dispersed among TiO₂ nanoparticles. The prepared photocatalyst showed high photocatalytic activity for the degradation of methyl orange in water. The degradation results revealed that the NiFe₂O₄ nanoparticles played the role of recombination centre of photogenerated electrons and holes for the TN photocatalyst, which gave rise to the decrease in photocatalytic activity. Moreover, the experiment on recycled use of TN demonstrated a good repeatability of the photocatalytic activity.     

Controlled Synthesis of Fe3O4/ZIF‐8 Nanoparticles for Magnetically Separable Nanocatalysts

Fe₃O₄/ZIF‐8 nanoparticles were synthesized through a room‐temperature reaction between 2‐methylimidazolate and zinc nitrate in the presence of Fe₃O₄ nanocrystals. The particle size, surface charge, and magnetic loading can be conveniently controlled by the dosage of Zn(NO₃)₂ and Fe₃O₄ nanocrystals. The as‐prepared particles show both good thermal stability (stable to 550 °C) and large surface area (1174 m²g^?1). The nanoparticles also have a superparamagnetic response, so that they can strongly respond to an external field during magnetic separation and disperse back into the solution after withdrawal of the magnetic field. For the Knoevenagel reaction, which is catalyzed by alkaline active sites on external surface of catalyst, small Fe₃O₄/ZIF‐8 nanoparticles show a higher catalytic activity. At the same time, the nanocatalysts can be continuously used in multiple catalytic reactions through magnetic separation, activation, and redispersion with little loss of activity.     

Synthesis of pH‐responsive magnetic yolk–shell nanoparticles: A comparison between conventional etching and new deswelling approaches

Iron oxide (Fe₃O₄) magnetic nanoparticles as movable cores were used to synthesize yolk–shell nanoparticles with pH‐responsive shell composed of ethylene glycol dimethacrylate (EGDMA)‐crosslinked poly(acrylic acid) (PAA) via two different routes. In the first more common route, Fe₃O₄ nanoparticles were coated with silica layer via the Stöber process to yield Fe₃O₄@SiO₂ core–shell nanoparticles, subsequently used as seeds in the distillation precipitation copolymerization of AA and EGDMA to yield Fe₃O₄@SiO₂@P(AA‐EGDMA). The silica layer was selectively removed through alkali etching to yield Fe₃O₄@air@P(AA‐EGDMA). In the second route, Fe₃O₄ nanoparticles without any stabilization were used as seeds in the distillation precipitation copolymerization of AA and EGDMA to yield Fe₃O₄@P(AA‐EGDMA) core–shell nanoparticles. The nanoparticles were subsequently dispersed in acidic medium of pH = 2. Yolk–shell Fe₃O₄@air@P(AA‐EGDMA) nanoparticles were formed through deswelling of crosslinked PAA because of protonation of carboxyl groups at low pH values. Various techniques were utilized to investigate the characteristics of the synthesized core–shell nanoparticles. Formation of yolk–shell nanostructure was observed for both synthesis routes, namely etching of silica layer and deswelling approaches, from vibrating sample magnetometry and transmission electron microscopy results. Both types of nanoparticles showed pH‐responsive behaviour, i.e. decrease in absorption with increase in pH, as examined using UV–visible spectroscopy.     

Preparation of magnetic Fe3O4/TiO2/Ag composite microspheres with enhanced photocatalytic activity

The novel three-component Fe₃O₄/TiO₂/Ag composite mircospheres were prepared via a facile chemical deposition route. The Fe₃O₄/TiO₂ mircospheres were first prepared by the solvothermal method, and then Ag nanoparticles were anchored onto the out-layer of TiO₂ by the tyrosine-reduced method. The as-prepared magnetic Fe₃O₄/TiO₂/Ag composite mircospheres were applied as photocatalysis for the photocatalytic degradation of methylene blue. The results indicate that the photocatalytic activity of Fe₃O₄/TiO₂/Ag composite microspheres is superior to that of Fe₃O₄/TiO₂ due to the dual effects of the enhanced light absorption and reduction of photoelectron–hole pair recombination in TiO₂ with the introduction of Ag NPs. Moreover, these magnetic Fe₃O₄/TiO₂/Ag composite microspheres can be completely removed from the dispersion with the help of magnetic separation and reused with little or no loss of catalytic activity.