Inexpensive and nonconventional fabrication of microfluidic devices in PMMA based on a soft-embossing protocol

This study describes an inexpensive and nonconventional soft-embossing protocol to produce microfluidic devices in poly(methyl methacrylate) (PMMA). The desirable microfluidic structure was photo-patterned in a poly(vinyl acetate) (PVAc) film deposited on glass substrate to produce a low-relief master. Then, this template was used to generate a high-relief pattern in stiffened PDMS by increasing of curing agent /monomer ratio (1:5) followed by thermal aging in a laboratory oven (200°C for 24 h). The stiffened PDMS masters were used to replicate microfluidic devices in PMMA based on soft embossing at 220–230°C and thermal sealing at 140°C. Both embossing and sealing stages were performed by using binder clips. The proposed protocol has ensured the replication of microfluidic devices in PMMA with great fidelity (>94%). Examples of MCE devices, droplet generator devices and spot test array were successfully demonstrated. For testing MCE devices, a mixture containing inorganic cations was selected as model and the achieved analytical performance did not reveal significant difference from commercial PMMA devices. Water droplets were successfully generated in an oil phase at rate of ca. 60 droplets/min (fixing the continuous phase flow rate at 100 μL/h) with size of ca. 322 ± 6 μm. Glucose colorimetric assay was performed on spot test devices and good detectability level (5 μmol/L) was achieved. The obtained results for two artificial serum samples revealed good agreement with the certified concentrations. Based on the fabrication simplicity and great analytical performance, the proposed soft-embossing protocol may emerge as promising approach for manufacturing PMMA devices.     

Thermoset polyester droplet-based microfluidic devices for high frequency generation

The vast majority of droplet-based microfluidic devices are made from polydimethylsiloxane (PDMS). Unfortunately PDMS is not suitable for high frequency droplet generation at high operating pressure due to its low shear modulus. In this paper, we report the fabrication and testing of microfluidic devices using thermoset polyester (TPE). The optical characteristics of the fabricated devices were assessed and substrate resistance to pressure also investigated. TPE devices bonded using an O(2) plasma treated PET substrate at 76 °C were shown to function efficiently at pressures up to 18 MPa. TPE material retains many of the attractive features of PDMS such as ease of fabrication but significantly, has superior mechanical properties. The improved resistance of TPE to high pressures enabled investigation of high frequency droplet generation as a function of a wide range of flow-rates with three different oils as continuous phase.     

Disposable roll-to-roll hot embossed electrophoresis chip for detection of antibiotic resistance gene mecA in bacteria

We present a high-throughput roll-to-roll (R2R) manufacturing process for foil-based polymethyl methacrylate (PMMA) chips of excellent optical quality. These disposable, R2R hot embossed microfluidic chips are used for the identification of the antibiotic resistance gene mecA in Staphylococcus epidermidis. R2R hot embossing is an emerging manufacturing technology for polymer microfluidic devices. It is based on continuous feeding of a thermoplastic foil through a pressurized area between a heated embossing cylinder and a blank counter cylinder. Although mass fabrication of foil-based microfluidic chips and their use for biological applications were foreseen already some years ago, no such studies have been published previously.     

A polymeric master replication technology for mass fabrication of poly(dimethylsiloxane) microfluidic devices

A protocol of producing multiple polymeric masters from an original glass master mold has been developed, which enables the production of multiple poly(dimethylsiloxane) (PDMS)-based microfluidic devices in a low-cost and efficient manner. Standard wet-etching techniques were used to fabricate an original glass master with negative features, from which more than 50 polymethylmethacrylate (PMMA) positive replica masters were rapidly created using the thermal printing technique. The time to replicate each PMMA master was as short as 20 min. The PMMA replica masters have excellent structural features and could be used to cast PDMS devices for many times. An integration geometry designed for laser-induced fluorescence (LIF) detection, which contains normal deep microfluidic channels and a much deeper optical fiber channel, was successfully transferred into PDMS devices. The positive relief on seven PMMA replica masters is replicated with regard to the negative original glass master, with a depth average variation of 0.89% for 26-microm deep microfluidic channels and 1.16% for the 90 mum deep fiber channel. The imprinted positive relief in PMMA from master-to-master is reproducible with relative standard deviations (RSDs) of 1.06% for the maximum width and 0.46% for depth in terms of the separation channel. The PDMS devices fabricated from the PMMA replica masters were characterized and applied to the separation of a fluorescein isothiocyanate (FITC)-labeled epinephrine sample.     

Poly(methyl methacrylate) CE microchips replicated from poly(dimethylsiloxane) templates for the determination of cations

A novel method for the rapid fabrication of poly(methyl methacrylate) (PMMA) microfluidic chips using poly(dimethylsiloxane) (PDMS) templates has been demonstrated. The PDMS molds were fabricated by soft lithography. The dense prepolymerized solution of methyl methacrylate containing thermal and UV initiators was allowed to polymerized between a PDMS template and a piece of a 1 mm thick commercial PMMA plate under a UV lamp. The images of microchannels on the PDMS template were precisely replicated into the synthesized PMMA substrates during the UV-initiated polymerization of the prepolymerized solution on the surface of the PMMA plate at room temperature. The polymerization could be completed within 10 min under ambient temperature. The chips were subsequently assembled by thermal bonding of the channel plate and the cover sheet. The new fabrication method obviates the need for specialized replication equipment and reduces the complexity of prototyping and manufacturing. Nearly 20 PMMA chips were replicated using a single PDMS mold. The attractive performance of the new microfluidic chips has been demonstrated by separating and detecting cations in connection with contactless conductivity detection. The fabricated PMMA microchip has also been successfully employed for the determination of potassium and sodium in environmental and biological samples.     

Thermoplastic elastomers for microfluidics: towards a high-throughput fabrication method of multilayered microfluidic devices

Multilayer soft lithography of polydimethylsiloxane (PDMS) is a well-known method for the fabrication of complex fluidic functions. With advantages and drawbacks, this technique allows fabrication of valves, pumps and micro-mixers. However, the process is inadequate for industrial applications. Here, we report a rapid prototyping technique for the fabrication of multilayer microfluidic devices, using a different and promising class of polymers. Using styrenic thermoplastic elastomers (TPE), we demonstrate a rapid technique for the fabrication and assembly of pneumatically driven valves in a multilayer microfluidic device made completely from thermoplastics. This material solution is transparent, biocompatible and as flexible as PDMS, and has high throughput thermoforming processing characteristics. We established a proof of principle for valving and mixing with three different grades of TPE using an SU-8 master mold. Specific viscoelastic properties of each grade allow us to report enhanced bonding capabilities from room temperature bonding to free pressure thermally assisted bonding. In terms of microfabrication, beyond classically embossing means, we demonstrate a high-throughput thermoforming method, where TPE molding experiments have been carried out without applied pressure and vacuum assistance within an overall cycle time of 180 s. The quality of the obtained thermoplastic systems show robust behavior and an opening/closing frequency of 5 Hz.     

Fabrication of microfluidic chip using micro‐hot embossing with micro electrical discharge machining mold

This study develops an improved method for generating aluminum mold inserts used in the replication of polymer‐based microfluidic chip. Since molding masters that are suitable for microfluidic chip replication must have features whose dimensions are of the order of tens to hundreds of microns, micro electrical discharge machining is employed herein to fabricate an aluminum mold insert of a microfluidic chip. The width and depth of the aluminum mold insert for the microfluidic chip are 61.50 and 49.61 µm, respectively. The surface roughness values of the microchannel and the sample reservoir in aluminum mold insert for the microfluidic chip are 53.9 and 34.3 nm, respectively. PMMA material is adopted as the molded microfluidic chip that is produced by micro‐hot embossing molding. The PMMA material can replicate the microchannel and sample reservoir very well when the aluminum mold insert is used in micro‐hot embossing molding. The results indicate that the most important parameter in the replication of molded microfluidic chip is the embossing pressure, which is also the most important parameter in determining the surface roughness of the molded microfluidic chip. Copyright © 2010 John Wiley & Sons, Ltd.     

Beyond PDMS: off-stoichiometry thiol-ene (OSTE) based soft lithography for rapid prototyping of microfluidic devices

In this article we introduce a novel polymer platform based on off-stoichiometry thiol-enes (OSTEs), aiming to bridge the gap between research prototyping and commercial production of microfluidic devices. The polymers are based on the versatile UV-curable thiol-ene chemistry but takes advantage of off-stoichiometry ratios to enable important features for a prototyping system, such as one-step surface modifications, tuneable mechanical properties and leakage free sealing through direct UV-bonding. The platform exhibits many similarities with PDMS, such as rapid prototyping and uncomplicated processing but can at the same time mirror the mechanical and chemical properties of both PDMS as well as commercial grade thermoplastics. The OSTE-prepolymer can be cast using standard SU-8 on silicon masters and a table-top UV-lamp, the surface modifications are precisely grafted using a stencil mask and the bonding requires only a single UV-exposure. To illustrate the potential of the material we demonstrate key concepts important in microfluidic chip fabrication such as patterned surface modifications for hydrophobic stops, pneumatic valves using UV-lamination of stiff and rubbery materials as well as micromachining of chip-to-world connectors in the OSTE-materials.     

Fabrication improvements for thermoset polyester (TPE) microfluidic devices

Thermoset polyester (TPE) microfluidic devices were previously developed as an alternative to poly(dimethylsiloxane) (PDMS) devices, fabricated similarly by replica molding, yet offering stable surface properties and good chemical compatibility with some organics that are incompatible with PDMS. This paper describes a number of improvements in the fabrication of TPE chips. Specifically, we describe methods to form TPE devices with a thin bottom layer for use with high numerical aperture (NA) objectives for sensitive fluorescence detection and optical manipulation. We also describe plasma-bonding of TPE to glass to create hybrid TPE-glass devices. We further present a simple master-pretreatment method to replace our original technique that required the use of specialized equipment.     

Polyurethane-based microfluidic devices for blood contacting applications

Protein adsorption on PDMS surfaces poses a significant challenge in microfluidic devices that come into contact with biofluids such as blood. Polyurethane (PU) is often used for the construction of medical devices, but despite having several attractive properties for biointerfacing, it has not been widely used in microfluidic devices. In this work we developed two new fabrication processes for making thin, transparent and flexible PU-based microfluidic devices. Methods for the fabrication and bonding of microchannels, the integration of fluidic interconnections and surface modification with hydrophilic polyethylene oxide (PEO) to reduce protein adsorption are detailed. Using these processes, microchannels were produced having high transparency (96% that of glass in visible light), high bond strength (326.4 kPa) and low protein adsorption (80% reduction in fibrinogen adsorption vs. unmodified PDMS), which is critical for prevention of fouling. Our findings indicate that PEO modified PU could serve as an effective alternative to PDMS in blood contacting microfluidic applications.     

New family of fluorinated polymer chips for droplet and organic solvent microfluidics

We present a new family of microfluidic chips hot embossed from a commercial fluorinated thermoplastic polymer (Dyneon THV). This material shares most of the properties of fluoro polymers (very low surface energy and resistance to chemicals), but is easier to process due to its relatively low melting point. Finally, as an elastic material it also allows easy world to chip connections. Fluoropolymer films can be imprinted by hot embossing from PDMS molds prepared by soft lithography. Chips are then sealed by an original technique (termed Monolithic-Adhesive-Bonding), using two different grades of fluoropolymer to obtain uniform mechanical, chemical and surface properties. This fabrication process is well adapted to rapid prototyping, but it also has potential for low cost industrial production, since it does not require any curing or etching step. We prepared microfluidic devices with micrometre resolution features, that are optically transparent, and that provide good resistance to pressure (up to 50 kPa). We demonstrated the transport of water droplets in fluorinated oil, and fluorescence detection of DNA within the droplets. No measurable interaction of the droplets with the channels wall was observed, alleviating the need for surface treatment previously necessary for droplet applications in microfluidic chips. These chips can also handle harsh organic solvents. For instance, we demonstrated the formation of chloroform droplets in fluorinated oil, expanding the potential for on chip microchemistry.     

Polymer microfabrication technologies for microfluidic systems

Polymers have assumed the leading role as substrate materials for microfluidic devices in recent years. They offer a broad range of material parameters as well as material and surface chemical properties which enable microscopic design features that cannot be realised by any other class of materials. A similar range of fabrication technologies exist to generate microfluidic devices from these materials. This review will introduce the currently relevant microfabrication technologies such as replication methods like hot embossing, injection molding, microthermoforming and casting as well as photodefining methods like lithography and laser ablation for microfluidic systems and discuss academic and industrial considerations for their use. A section on back-end processing completes the overview.     

Solvent-resistant photocurable liquid fluoropolymers for microfluidic device fabrication [corrected

We report the first fabrication of a solvent-compatible microfluidic device based on photocurable "Liquid Teflon" materials. The materials are highly fluorinated functionalized perfluoropolyethers (PFPEs) that have liquidlike viscosities that can be cured into tough, highly durable elastomers that exhibit the remarkable chemical resistance of fluoropolymers such as Teflon. Poly(dimethylsiloxane) (PDMS) elastomers have rapidly become the material of choice for many recent microfluidic device applications. Despite the advantages of PDMS in relation to microfluidics technology, the material suffers from a serious drawback in that it swells in most organic solvents. The swelling of PDMS-based devices in organic solvents greatly disrupts the micrometer-sized features and makes it impossible for fluids to flow inside the channels. Our approach to this problem has been to replace PDMS with photocurable perfluoropolyethers. Device fabrication and valve actuation were accomplished using established procedures for PDMS devices. The additional advantage of photocuring allows fabrication time to be decreased from several hours to a matter of minutes. The PFPE-based device exhibited mechanical properties similar to those of Sylgard 184 before and after curing as well as remarkable resistance to organic solvents. This work has the potential to expand the field of microfluidics to many novel applications.     

Electrochromatography in poly(dimethyl)siloxane microchips using organic monolithic stationary phases

This paper shows the in situ synthesis of an hexyl acrylate monolith in PDMS microfluidic devices and its subsequent use as stationary phase for electrochromatography on chip. To overcome the ability of PDMS material to absorb organic monomers, surface modification of the enclosed channels was realized by UV-mediated graft polymerization. This grafting procedure is based on the preliminary adsorption of a photoinitiator onto the PDMS surface and polymerization of charged monomers. Next, hexyl acrylate monoliths were cast in situ using photopolymerization process. The chromatographic behavior of the monolithic column was confirmed by the successful separation of derivatized catecholamines in the PDMS device using a 30 mm effective separation length (100 microm x 100 microm section). Efficiencies reached up to 200,000 plates per meter.     

Chemically resistant microfluidic valves from Viton® membranes bonded to COC and PMMA

We present a reliable technique for irreversibly bonding chemically inert Viton? membranes to PMMA and COC substrates to produce microfluidic devices with integrated elastomeric structures. Viton? is widely used in commercially available valves and has several advantages when compared to other elastomeric membranes currently utilised in microfluidic valves (e.g. PDMS), such as high solvent resistance, low porosity and high temperature tolerance. The bond strength was sufficient to withstand a fluid pressure of 400 kPa (PMMA/Viton?) and 310 kPa (COC/Viton?) before leakage or burst failure, which is sufficient for most microfluidic applications. We demonstrate and characterise on-chip pneumatic Viton? microvalves on PMMA and COC substrates. We also provide a detailed method for bonding fluorinated Viton? elastomer, a highly chemically compatible material, to PMMA and COC polymers. This allows the production of microfluidic devices able to handle a wide range of chemically harsh fluids and broadens the scope of the microfluidic platform concept.     

Three-dimensional interconnected microporous poly(dimethylsiloxane) microfluidic devices

This technical note presents a fabrication method and applications of three-dimensional (3D) interconnected microporous poly(dimethylsiloxane) (PDMS) microfluidic devices. Based on soft lithography, the microporous PDMS microfluidic devices were fabricated by molding a mixture of PDMS pre-polymer and sugar particles in a microstructured mold. After curing and demolding, the sugar particles were dissolved and washed away from the microstructured PDMS replica revealing 3D interconnected microporous structures. Other than introducing microporous structures into the PDMS replica, different sizes of sugar particles can be used to alter the surface wettability of the microporous PDMS replica. Oxygen plasma assisted bonding was used to enclose the microstructured microporous PDMS replica using a non-porous PDMS with inlet and outlet holes. A gas absorption reaction using carbon dioxide (CO(2)) gas acidified water was used to demonstrate the advantages and potential applications of the microporous PDMS microfluidic devices. We demonstrated that the acidification rate in the microporous PDMS microfluidic device was approximately 10 times faster than the non-porous PDMS microfluidic device under similar experimental conditions. The microporous PDMS microfluidic devices can also be used in cell culture applications where gas perfusion can improve cell survival and functions.     

Hot embossing of electrophoresis microchannels in PMMA substrates using electric heating wires

A simple method based on electric heating wires has been developed for the rapid fabrication of poly(methyl methacrylate) (PMMA) electrophoresis microchips in ordinary laboratories without the need for microfabrication facilities. A piece of stretched electric heating wire placed across the length of a PMMA plate along its midline was sandwiched between two microscope slides under pressure. Subsequently, alternating current was allowed to pass through the wire to generate heat to emboss a separation microchannel on the PMMA separation channel plate at room temperature. The injection channel was fabricated using the same procedure on a PMMA sheet that was perpendicular to the separation channel. The complete microchip was obtained by bonding the separation channel plate to the injection channel sheet, sealing the channels inside. The electric heating wires used in this work not only generated heat; they also served as templates for embossing the microchannels. The prepared microfluidic microchips have been successfully employed in the electrophoresis separation and detection of ions in connection with contactless conductivity detection.     

Thermoset polyester as an alternative material for microchip electrophoresis/electrochemistry

Microchip CE coupled with electrochemical detection (MCE-EC) is a good method for the direct detection of many small molecule analytes because the technique is sensitive and readily miniaturized. Polymer materials are being increasingly used with MCE due to their affordability and ease of fabrication. While PDMS has become arguably the most widely used material in MCE-EC due to the simplicity of microelectrode incorporation, it suffers from a lack of separation efficiency, lower surface stability, and a tendency for analyte sorption. Other polymers, such as poly(methylmethacrylate) (PMMA) and poly(carbonate) (PC), have higher separation efficiencies but require more difficult fabrication techniques for electrode incorporation. In this report, thermoset polyester (TPE) was characterized as an alternative material for MCE-EC. TPE microchips were characterized in their native and plasma oxidized forms and after coating with polyelectrolyte multilayers (PEMs). TPE provides higher separation efficiencies when compared to PDMS microchips, while still using simple fabrication protocols. In this work, separation efficiencies as high as 295,000 N/m were seen when using TPE MCE-EC devices. Furthermore, the EOF was higher and more consistent as a function of pH for both native and plasma-treated TPE than PDMS. Finally, TPE is amenable to modification using simple PEM coatings as another way to control surface chemistry and surface charge.     

Hybrid microfluidic cartridge formed by irreversible bonding of SU-8 and PDMS for multi-layer flow applications

SU-8 and polydimethylsiloxane (PDMS) are both transparent materials with properties very convenient for rapid prototyping of microfluidic systems. However, previous efforts of combining these two materials failed due to poor adhesion between them. Herein, we introduce a promising low-temperature technique (< 100 °C) to irreversibly bond two or more structured layers of SU-8 and PDMS to create hybrid stacks. This offers new possibilities in design and fabrication of enclosed three-dimensional microstructures and microchannels with simple soft-lithography techniques. The potential of this method is demonstrated by the fabrication of a new version of our microfluidic sensor cartridge that was reported recently¹.     

Fabrication, modification, and application of poly(methyl methacrylate) microfluidic chips

Poly(methyl methacrylate) (PMMA) is particularly useful for microfluidic chips with the features of low price, excellent optic transparency, attractive mechanical and chemical properties, ease of fabrication and modification, biocompatibility, etc. During the past decade, significant progress in the PMMA microfluidic chips has occurred. This review, which contains 120 references, summarizes the recent advances and the key strategies in the fabrication, modification, and application of PMMA microfluidic chips. It is expected that PMMA microchips should find a wide range of applications and will lead to the creation of truly disposable microfluidic devices.