自复合材料xLiFePO4·yLi3V2（PO4）3的合成及电化学性能

用固相法合成了不同比例的xLiFePO4.yLi3V2（PO4）3复合物.XRD、SEM和电化学测试仪等分析方法表征了所有样品的特性.结果表明,样品0.95LiFePO4.0.05Li3V2（PO4）3以0.2C的充放电倍率放电时具有162.7 mAh.g-1的电化学容量.同时该样品表现出了较其它样品更优异的循环稳定性...     

锂离子电池正极材料Li_3V_2(PO_4)_3的制备及性能研究

应用碳热还原法制备了表面碳包覆的Li3V2(PO4)3材料.X射线衍射、红外光谱和透射电镜表征样品的结构及形貌.结果表明,该合成样品为纯相的Li3V2(PO4)3晶体,颗粒尺寸100nm左右.电化学阻抗谱测试表明,该材料在3.0～4.3V电位区间的锂离子扩散系数比它在3.0～4.8V区间的高约3个数量级.另外,前者的电荷转移电阻也明显低于后者.因而,其循环性能也明显优于后者的循环性能.     

钒改性锂离子电池正极材料LiFe0.5Mn0.5PO4/C电化学性能

采用高温固相反应,以NH4VO3为钒源合成了化学计量式为(1-x)LiFe0.5Mn0.5PO4-xLi3V2(PO4)3/C (x=0,0.1,0.2,0.25,1)的钒改性磷酸锰铁锂正极材料.电化学测试表明钒改性能明显提高磷酸锰铁锂材料的充放电性能,其中x=0.2时得到的0.8LiFe0.5Mn0.5PO4-0.2Li3V2(PO4)3/C(标记为LFMP-LVP/C)材料电化学性能最好,其0.1C倍率时的放电比容量为141 mAh·g-1.X射线衍射(XRD)分析指出LFMP-LVP/C材料的微观结构为橄榄石型LiFe0.5Mn0.5PO4/C和NASICON型Li3V2(PO4)3组成的双相结构.能量色射X射线谱(EDS)分析结果指出,Fe、Mn、V、P元素在所合成材料中的分布非常均匀,表明所制备材料成分的均一性.Li3V2(PO4)3改性使材料的电导率明显提高.LiFe0.5Mn0.5PO4的电导率为1.9×10-8 S· cm-1,而LFMP-LVP材料电导率提高到2.7×10-7 S·cm-1.与纯Li3V2(PO4)3的电导率(2.3×10-7 S·cm-1)相近.电化学测试表明钒改性使LFMP-LVP/C材料充放电过程电极极化明显减小,从而电化学性能得到显著提高.本文工作表明Li3V2(PO4)3改性可成为提高橄榄石型磷酸盐锂离子电池正极材料电化学性能的一种有效方法.     

钒改性锂离子电池正极材料LiFe0.5Mn0.5PO4/C 电化学性能

采用高温固相反应,以NH4VO3为钒源合成了化学计量式为(1-x)LiFe0.5Mn0.5PO4-xLi3V2(PO4)3/C(x=0,0.1,0.2,0.25,1)的钒改性磷酸锰铁锂正极材料.电化学测试表明钒改性能明显提高磷酸锰铁锂材料的充放电性能,其中x=0.2时得到的0.8LiFe0.5Mn0.5PO4-0.2Li3V2(PO4)3/C(标记为LFMP-LVP/C)材料电化学性能最好,其0.1C倍率时的放电比容量为141mAh·g-1.X射线衍射(XRD)分析指出LFMP-LVP/C材料的微观结构为橄榄石型LiFe0.5Mn0.5PO4/C和NASICON型Li3V2(PO4)3组成的双相结构.能量色射X射线谱(EDS)分析结果指出,Fe、Mn、V、P元素在所合成材料中的分布非常均匀,表明所制备材料成分的均一性.Li3V2(PO4)3改性使材料的电导率明显提高.LiFe0.5Mn0.5PO4的电导率为1.9×10-8S·cm-1,而LFMP-LVP材料电导率提高到2.7×10-7S·cm-1.与纯Li3V2(PO4)3的电导率(2.3×10-7S·cm-1)相近.电化学测试表明钒改性使LFMP-LVP/C材料充放电过程电极极化明显减小,从而电化学性能得到显著提高.本文工作表明Li3V2(PO4)3改性可成为提高橄榄石型磷酸盐锂离子电池正极材料电化学性能的一种有效方法.     

Ti4+离子掺杂对Li3V2(PO4)3晶体结构与性能的影响

采用溶胶凝胶/碳热还原法合成了锂离子电池正极材料Li3V2(PO4)3及其掺Ti化合物Li3-2x(V1-xTix)2-(PO4)3. 电化学测试结果表明, 经Ti4+离子掺杂后材料的充放电性能及循环性能明显提高. 与纯相Li3V2(PO4)3在3.58、3.67和4.08 V出现三个平台相比, 掺杂后材料的前两个平台发生简并且平台趋于模糊的倾斜状态. 这种趋势随掺杂量的增大而增强. 差热分析(DTA)表明掺杂生成了稳定的酌相产物. 采用X射线衍射和Rietveld方法表征了化合物的晶体结构, 结果表明, 三个不同位置Li的不完全占据导致晶体中产生阳离子空穴, 使材料在常温下的离子电导率提高了3个数量级. 锂离子混排提高了样品的电导率和充放电比容量.     

三元掺杂改性锂离子电池正极材料Li3V2(PO4)3

以柠檬酸为螯合剂和还原剂, NH₄VO₃为钒源,通过溶胶-凝胶法制备了锂离子电池正极材料Li₃V₂(PO₄)₃及其三元掺杂体系Li_2.85Na_0.15V_1.9Al_0.1(PO₄)_2.9F_0.1.分别采用X射线衍射(XRD)、高分辨透射电子显微镜(HRTEM)、能量损失谱(EELS)、拉曼(Raman)光谱、扫描电子显微镜(SEM)、X射线能谱(EDS)、恒流充放电、循环伏安(CV)和交流阻抗谱(EIS)等技术对材料的微观结构、颗粒形貌和电化学性能进行分析.结果表明:在残余碳包覆的基础上, Na、Al、F三元掺杂有利于稳定Li₃V₂(PO₄)₃的晶体结构,进一步减少颗粒团聚和提升材料导电特性,促进第三个锂离子的脱出和嵌入,从而显著改善Li₃V₂(PO₄)₃的实用电化学性能.未经掺杂的Li₃V₂(PO₄)₃原粉在1/9C、1C和6C倍率下的可逆比容量分别为141、119和98 mAh·g^-1,而三元掺杂改性材料在1/9C、1C、8C和14C倍率下的比容量分别为172、139、119和115 mAh·g^-1.在1C倍率下循环300圈后,掺杂体系的比容量依然高达118 mAh·g^-1,比原粉高出32.6%.值得注意的是,这种三元掺杂还使Li₃V₂(PO₄)₃的多平台放电曲线近似转变为一条斜线,显示出可能不同的储锂机制.     

不同碳源对Li_3V_2(PO_4)_3/C复合正极材料性能的影响

以甲基纤维素、壳聚糖及葡萄糖分别作为碳源,应用碳热还原法合成正极Li3V2(PO4)3/C复合材料.XRD、SEM等方法分析、表征材料的结构、形貌和电化学性能.结果表明,碳源的选择对产物的比容量、循环寿命和倍率性能等均有较大的影响.以甲基纤维素为碳源制备的单斜Li3V2(PO4)3正极材料具有较好的电化学性能,在3.0～4.5V,0.2C倍率下,其初始容量为130.6mAh·g-1,30次循环后放电比容量仍可达到108mAh·g-1.     

Li3V2(PO4)3电极过程及其锂离子脱嵌动力学研究(Ⅰ)

采用溶胶凝胶法合成了Nasicon化合物Li3V2(PO4)3,采用X射线衍射(XRD)对产品进行了物相分析.采用充放电测试,循环伏安(CV)研究了化合物的电化学性能和锂离子的脱嵌过程,计算出Li+在固相中的扩散系数(10-8 cm2·s-1);采用交流阻抗测试(EIS)研究了Li3V2(PO4)3的电极过程;对两种类型的阻抗图谱提出不同等效电路模型并对结果进行了拟合;研究了Li3V2(PO4)3电极过程动力学以及新鲜电极界面在充放电过程中的变化特性.     

Li3V2-xMgx(PO4)3/C正极材料的制备及电化学性能研究

通过溶胶-凝胶法制备出Mg~(2+)掺杂Li_3V_(2-x)Mg_x(PO_4)_3/C(x=0,0.01,0.05,0.09)正极材料。采用X-射线衍射(XRD)、透射电镜(TEM)对材料的结构和形貌进行了表征和分析,通过恒流测试、循环伏安和交流阻抗测试对样品的电化学性能进行了表征,结果表明适量的掺杂能够显著提高材料的电化学性能。当倍率为0.2 C,充放电电压为2-4.3 V,材料Li_3V_(1.95)Mg_(0.05)(PO_4)_3/C表现出最优的电化学性能,首次放电容量达到162.1 mAh·g~(-1)。经过不同倍率的充放电循环后,其初始容量保持率可达98.5%,表现出优异的电化学稳定性。     

锂离子电池正极材料Na3V2（PO4）2F3的原位XRD及固体核磁共振研究

采用溶胶凝胶法制备Na3V2（PO4）2F3/C复合材料,该材料具有优异的电化学循环性能和倍率性能.利用电化学原位同步辐射X射线衍射（XRD）及魔角旋转固体核磁共振（MASSS-NMR）技术研究了Na3V2（PO4）2F3材料充放电过程中结构变化过程及Li/Na嵌入-脱出反应.研究结果表明,Na3V2（PO4）2F3的电极反应按嵌入-脱出反应机理进行,充放电过程中材料具有优异的结构稳定性.我们还发现Na3V2（PO4）2F3与电解液接触后与电解液中的Li＋发生部分交换反应形成LixNa3-xV2（PO4）2F3.在首次充电时,Li＋和结构中Na1位置的Na＋共同从晶格中脱出;而首次放电过程中,Na＋和Li＋共同嵌入到晶格中;充放电过程中发生的是Li＋和Na＋的共嵌入-脱出反应.     

碳包覆Li3V2(PO4)3正极材料在LiPF6电解液中的表面/界面行为

利用碳热还原法成功制备了碳包覆Li3V2(PO4)3正极材料。X射线衍射研究表明材料具有纯相单斜结构。高分辨透射电子显微镜观察到材料表面存在5～10 nm的包覆碳层。碳包覆Li3V2(PO4)3材料在3.0～4.3 V电压区间内可提供120 mA.h/g(C/4倍率)、115 mA.h/g(1C倍率)和110 mA.h/g(2C倍率)的可逆容量,并且在循环300次后容量保持率超过97%,显示出良好的应用前景。该材料在充放电循环初期经历了不可逆容量损失。高分辨透射电子显微镜研究表明,该不可逆容量损失来源于材料表面生成的固体电解质中间相(SEI膜),红外光谱分析表明,SEI膜的成份主要包括ROCO2Li和RCO2Li等有机物,以及Li2CO3、LixPFy和LixPOyFz等无机物。表面SEI膜经历初期电化学循环后趋于稳定,从而保证碳包覆Li3V2(PO4)3正极材料优良的电化学性能。     

快离子导体Li3V2(PO4)3包覆LiFePO4的结构和性能

通过机械活化将快离子导体Li3 V2(PO4)3包覆在LiFePO4 表面, 制备了性能优异的复合正极材料9LiFePO4@Li3 V2(PO4)3. 用XRD, SEM, HRTEM, EDS和电化学测试等手段研究了材料的物理化学性能. 结果表明, 包覆后的材料含有橄榄石结构的LiFePO4、单斜晶系的Li3 V2(PO4)3 和正交晶系的Li3 PO4; LiFePO4颗粒表面包覆了一层Li3 V2(PO4)3, 且部分V3+进入LiFePO4晶格内部, 使其晶格参数减小, 包覆后的LiFePO4的交换电流密度和锂离子扩散系数均提高了1个数量级. 电化学测试结果表明, 包覆后的LiFePO4的倍率性能及循环性能都得到显著改善, 在1C和2C倍率下, 包覆后的LiFePO4的首次放电比容量较包覆前分别提高了34.09%和78.97%, 经150次循环后容量保持率分别提高了27.77%和65.54%; 并且5C时容量为121.379 mA·h/g(包覆前LiFePO4在5C下几乎没有容量), 循环350次后的容量保持率高达94.03%.     

Conducting Graphene Decorated Li3V2(PO4)3/C for Lithium‐Ion Battery Cathode with Superior Rate Capability and Cycling Stability

In this study, core‐shell structured Li₃V₂(PO₄)₃/C wrapped in graphene nanosheets has been successfully prepared. The reduction of graphene oxide and the synthesis of Li₃V₂(PO₄)₃/C are carried out simultaneously using a chemical route followed by a solid‐state reaction. The effects of conducting graphene are studied by X‐ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectra and electrochemical measurements. The results reveal that the graphene sheets not only form a compact and uniform coating layer throughout the Li₃V₂(PO₄)₃/C, but also stretch out and cross‐link into a conducting network around the Li₃V₂(PO₄)₃/C particles. Thus, the graphene decorated Li₃V₂(PO₄)₃/C electrode exhibits superior high‐rate capability and long‐cycle stability. It delivers a reversible discharge capacity of 178.2 mAh·g^?1 after 60 cycles at a current density of 0.1 C, and the rate performances of 176, 169.3, 156.1 and 135.7 mAh·g^?1 at 1, 2, 5 and 10 C, respectively. The superior electrochemical properties make the graphene decorated Li₃V₂(PO₄)₃/C composite a promising cathode material for high‐performance lithium‐ion battery.     

流变相法制备海藻酸基碳包覆Li3V2(PO4)3材料的电化学性能

Li₃V₂(PO₄)₃/C (LVP/C) cathode materials were successfully prepared by a rheological phase method using alginic acid as the carbon source. The X-ray diffraction (XRD) patterns demonstrate that all the samples contain pure LVP with the same monoclinic structure. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images show that LVP/C materials have a uniform particle size. The LVP/C sample with 10% (w) alginic acid shows the best cycling stability. It delivers a discharge capacity of 117.5 mAh·g^-1 (3.0-4.3 V), which can be maintained at 116.5 mAh·g^-1 after 50 cycles at a rate of 0.1C. Its capacity retentions of 99.1% (3.0-4.3 V) and 76.8% (3.0-4.8 V) after 50 cycles are prominently higher than those of pristine Li₃V₂(PO₄)₃, which are 89.7% (3.0-4.3 V) and 62.39% (3.0-4.8 V). These outstanding electrochemical performances are mainly attributed to the alginic acid-based carbon coating, which can increase the electronic conductivity of materials and buffer the mechanical damage of the active materials during the Li ion insertion/extraction process, thus improving the electrochemical performance of the LVP/C samples.     

Design and Construction of 3D Porous Na3V2(PO4)3/C as High Performance Cathode for Sodium Ion Batteries

An easy and delicate approach using cheap carbon source as conductive materials to construct 3D sequential porous structural Na3V2(PO4)3/C(NVP/C)with high performance for cathode materials of sodium ion battery is highly desired.In this paper,the NVP/C with 3D sequential porous structure is constructed by a delicate approach named as“cooking porridge”including evaporation and calcination stages.Especially,during evaporation,the viscosity of NVP/C precursor is optimized by controlling the adding quantity of citric acid,thus leading to a 3D sequential porous structure with a high specific surface area.Furthermore,the NVP/C with a 3D sequential porous structure enables the electrolyte to interior easily,providing more active sites for redox reaction and shortening the diffusion path of electron and sodium ion.Therefore,benefited from its unique structure,as cathode material of sodium ion batteries,the 3D sequential porous structural NVP/C exhibits high specific capacities(115.7,88.9 and 74.4 mA·h/g at current rates of 1,20 and 50 C,respectively)and excellent cycling stability(107.5 and 80.4 mA·h/g are remained at a current density of 1 C after 500 cycles and at a current density of 20 C after 2200 cycles,respectively).     

Na3V2(PO4)2O2F的合成及其在钠离子电池中的应用

目前,合成Na3V2(PO4)2O2F(NVPF)材料的方法包括高温固相法、水热法、溶剂热法等,这些方法均不利于该材料的大规模工业化生产.本文开发了温和的低温共沉淀法合成NVPF材料,该材料首次放电容量为105.6 mAh·g-1,首次效率为90.16％.经过简单的热处理过程,可以有效去除由于液相合成带来的结晶水以及吸...     

Nitrogen-doped Carbon Coated Na3V2(PO4)3 with Superior Sodium Storage Capability

Cathodes with high cycling stability and rate capability are required for ambient temperature sodium ion batteries in renewable energy storage application. Na₃V₂(PO₄)₃ is an attractive cathode material with excellent electrochemical stability and fast ion diffusion coefficient within the 3D NASICON structure. Nevertheless, the practical application of Na₃V₂(PO₄)₃ is seriously hindered by its intrinsically poor electronic conductivity. Herein, solvent evaporation method is presented to obtain the nitrogen-doped carbon coated Na₃V₂(PO₄)₃ cathode material, delivering enhanced electrochemical performances. N-Doped carbon layer coating serves as a highly conducting pathway, and creates numerous extrinsic defects and active sites, which can facilitate the storage and diffusion of Na⁺. Moreover, the N-doped carbon layer can provide a stable framework to accommodate the agglomeration of the electrode upon electrode cycling. N-Doped carbon coated Na₃V₂(PO₄)₃(NC-NVP) exhibits excellent long cycling life and superior rate performances than bare Na₃V₂(PO₄)₃ without carbon coating. NC-NVP delivers a stable capacity of 95.9 mA·h/g after 500 cycles at 1 C rate, which corresponds to high capacity retention(94.6%) with respect to the initial capacity(101.4 mA·h/g). Over 91.3% of the initial capacity is retained after 500 cycles at 5 C, and the capacity can reach 85 mA·h/g at 30 C rate.     

磷酸钒锂溶胶-凝胶制备及电化学性能研究

以柠檬酸为螯合剂和碳源,应用溶胶-凝胶法制备锂离子电池正极Li3V2(PO4)3/C.XRD、SEM及恒电流充放电等测试表明,所得样品经800℃、12 h焙烧后具有单一晶相结构,粒度相对较小,分布均匀.0.1C、0.5C和1C放电首次比容量分别为153.0、143.1和130.6 mAh.g-1,50次循环容量效率分别为93.1%,85.4%和77.3%,充电效率达80%,放电电压较高.