Oxygen ordering and superconductivity in YBa2Cu3O7-δ

Samples of YBa₂Cu₃O_7-δ in which concentration of oxygen was varied by annealing at different temperatures between 200 and 900C followed by quenching to 77 K have been investigated by carrying out measurements of oxygen stoichiometry, room temperature resistivity, superconductivity and crystal structure. It is shown that the overall oxygen stoichiometry alone does not adequately characterize the superconducting and normal state behaviour;T _c, ΔT _cand room temperature resistivity also vary with the heat treatment conditions. This implies a dependence of the physical properties on the details of the distribution of the oxygen atoms. The results show a definite correlation betweenT _cand resistivity hitherto not reported.     

Effect of strontium substitution on superconductivity in YBa 2 Cu 4 O 8

Superconducting powders with the composition Y(Ba 1 mx Sr x ) 2 Cu 4 O 8 ( x = 0.00-0.50) have been prepared by an aqueous sol-gel method. The effects of strontium substitution on the properties of compounds were studied by resistivity measurements, X-ray powder diffraction, thermogravimetric analysis, electron microscopy and elemental analysis. The data indicate that single-phase Y(Ba 1 mx Sr x ) 2 Cu 4 O 8 superconducting samples were obtained. They also show that doping with strontium has a strong effect on the superconducting properties of the YBa 2 Cu 4 O 8 phase. The critical temperature is enhanced from 78 K (for a non-substituted sample) to 88 K (for Y(Ba 1 mx Sr x ) 2 Cu 4 O 8 ). Elemental analysis data clearly indicate that small amounts of strontium enter the copper sites in the Y(Ba 1 mx Sr x ) 2 Cu 4 O 8 compounds. A point-defect chemistry approach, which explains the enhancement of T c by substituting strontium for barium, is presented.     

Theory of high temperature superconductivity in YBa2Cu3O7_δ

A theory of high temperature superconductivity in YBa₂Cu₃O₇__δ compound has been developed on the basis of the momentum pairing of electrons through the relativistic Darwin interaction. The transport behaviour of electrons is explained in terms of a mechanism of correlated electron transfer arising from the electron-phonon coupling. A model Hamiltonian has been developed to describe the superconducting properties of the system. This gives an energy gap which is higher than the BCS value. Attempts have been made to explain the absence of isotope effect, the linear dependence of specific heat, the presence of larger temperature-independent paramagnetism in the normal phase and the softening of some of the optic phonon modes observed in this system.     

Ac-Josephson effect in YBa2Cu3O7/YBa2Cu3O7 point contact junctions

The ac-Josephson effect could be demonstrated up to dc voltages of 20 mV on the I–V characteristic of adjustable YBa₂Cu₃O₇/YBa₂Cu₃O₇ point contacts at 4.2 K. A detailed analysis of the rf power dependence of the size of microwave-induced constant voltage steps is given for microwave frequencies of 70 and 90 GHz. The results prove that electron pairing is responsible for the superconductivity in YBa₂Cu₃O₇.     

HighT c superconductivity in YBa2Cu3O7−x studied by PAC and PAS

HighT _c superconductivity has been investigated in YBaCuO by both perturbed angular correlation and positron annihilation spectroscopy techniques as a function of temperature from 77 to 300 K. An abrupt change has been observed in the positron lifetime and Doppler broadening and the electric field gradient and its asymmetry parameter acrossT _c, indicating a transition of two- to one-dimensional Cu-O-Cu chain structure and a charge transfer from CuO layers to CuO chains. An anomaly of the normal state has been demonstrated around 125 K, which is attributed to the structural instability.     

Magnetic field dependence of critical current density in YBa2Cu3O7

We have measured the transport critical current densityJ _cof sintered YBa₂Cu₃O₇, in various applied fields up to 185 Oe at 77 K. We find a sharp decay ofJ _cwith magnetic field. We show that this sharp decay is consistent with the low field hysteresis results of Groveret al. We argue that the observed field dependence is not caused by intragranular weak links.     

Vortex-creep activation energy in YBa2Cu3O7/PrBa2Cu3O7 superlattices

YBa₂Cu₃O₇/PrBa₂Cu₃O₇ (YBCO/PBCO) superlattices with a different ratio of the superconducting and insulating layer thicknesses were prepared by high pressure dc sputtering. The vortex-creep activation energy U₀ was determined by analyzing the in-plane resistive transition of 200 μm wide bridges with the external magnetic field B oriented along the c axis. It was found that U₀ is proportional to the thickness of the YBCO layers, and does only weakly depend on the PBCO layer thickness, when the latter exceeds two unit cells. We observed a change in the variation of U₀ with the current I in the specimen: U₀ exhibits a plateau in the low-I region, then decreases significantly with increasing I. This behaviour is explained in terms of a crossover plastic vortex creep – elastic (collective) creep induced by the transport current.