MoO3/SiO2催化剂的异丁烷选择氧化反应性能

分别采用浸渍法和溶胶－凝胶法制备了MoO3/SiO2催化剂，用XRD，TPR，IR，TPD和活性评价等手段对催化剂的影响，晶格氧活泼性，化学吸附性能和异丁烷选择氧化反应性能进行了研究。结果表明，催化剂表面由Lewis碱位Mo=M,Mo-O-Mo中的晶格氧和Lewis酸位Mo^6 构成，在MoO3/SiO2催化剂上，异丁烷主要通过甲基的H双位吸附在表面的Lewis碱位Mo=O上；在常压条件下，异丁烷选择氧化产物主要为异丁烷，甲基丙烯醛和甲基丙烯酸，其中深度氧化产物CO2主要由吸附的异丁烯继续反应生成；采用溶胶－凝胶法制备的MoO3/SiO2催化剂，可得到较高的异丁烷转化率和含氧有机物选择性。     

V2O5/SiO2催化剂的异丁烷选择氧化反应性能

 采用溶胶－凝胶法和浸渍法制备了V2O5／SiO2催化剂,并用XRD,IR,TPD和活性评价等手段对催化剂的表面构造、化学吸附性能和异丁烷选择氧化反应性能进行了研究．结果表明：催化剂表面由Lewis碱位V＝O双键的端氧和Lewis酸位V5＋构成,异丁烷分子主要通过甲基中的H双位吸附在催化剂表面的Lewis碱位上,异丁烯分子可通过甲基的H吸附在催化剂表面的Lewis碱位,也可通过C＝C双键吸附在催化剂表面的Lewis酸位上．在常压条件下,异丁烷选择氧化产物主要有异丁烯、甲基丙烯醛和甲基丙烯酸,其中深度氧化产物CO2主要由通过C＝C吸附的异丁烯继续反应生成．     

Fe-Al-P-O催化1,2-二氯丙烷与水环氧化制环氧丙烷反应机理

 采用溶胶-凝胶法制备了非晶态Fe-Al-P-O催化剂,并用IR,XRD,TEM,N2吸附及微反等技术对其组成、结构特性以及催化性能进行了表征和评价,通过IR和TPD-MS等技术着重研究了其化学吸附性能,探讨了表面催化反应的机理. 结果表明,Fe-Al-P-O催化剂是FePO4和AlPO4均匀混合形成的非晶态混合物,能够促进1,2-二氯丙烷和水反应高选择性地生成环氧丙烷,其Lewis酸位的Fe3+和Lewis碱位P=O的O2-是催化剂表面的主要活性位,能使水进行解离吸附并形成Fe-O-和P-OH 键. 1,2-二氯丙烷通过Cl-与P-OH键中的H+作用形成桥式吸附态是反应进行的关键.     

丙烯环氧化制环氧丙烷Fe-Al-P-O催化剂的研究

用溶胶-凝胶法制得了Fe-Al-P-O催化剂，采用IR、XRD、TEM、BET、TPR和微反等技术研究了催化剂的物化性质和反应性能。实验结果表明，Fe1/2-Al1/2-PO4由10 nm左右 FePO4和AlPO4微晶组合而成，其晶格氧的活泼性大于单纯FePO4，AlPO4在Fe1/2-Al1/2-PO4中起到分散FePO4微晶的作用；Fe1/2-Al1/2-PO4的反应性能与原料气组成密切相关，丙烯与O2的选择氧化产物主要是丙烯醛，原料气中加入H2后，反应产物以环氧丙烷为主，同时还有部分丙烯醛，原料气中引入水蒸气后，可进一步增加环氧丙烷的选择性及减少丙烯醛的产率；在0.1 MPa、200 ℃、C3H6/O2/H2/H2O/N2=1∶1∶1∶1∶6（mol比）和空速1 200 h－1条件下，丙烯的转化率为8.9％，环氧丙烷的选择性为81.0％。     

Te掺杂对MoPO/SiO2催化剂上丙烷选择氧化制丙烯醛反应的影响

 考察了Te的添加及Te含量对MoPO/SiO2催化剂催化丙烷选择氧化制丙烯醛反应性能的影响. MoPO/SiO2催化剂对丙烷选择氧化制丙烯醛反应的中间产物丙烯选择性较高,而Te的添加促进了丙烯向丙烯醛的转化. N2吸附、XRD、Raman、XPS、H2-TPR、丙烷脉冲、NH3-TPD和Py-IR等实验结果表明,催化剂添加Te后虽然比表面积有所下降,但单位比表面积上的酸量增加,催化剂低温可还原性得到改善,从而有利于丙烷的转化. Te可能有利于丙烯α-H的脱除和/或烯丙基的插氧反应.     

MOPO/SiO2催化剂上丙烷选择氧化制丙烯醛反应机理

 考察了丙烷以及丙烷选择氧化反应的有关中间体或其探针分子(如丙烯、烯丙醇、异丙醇和正丙醇)和产物(如丙烯醛、丙酮和丙醛)在MoPO/SiO2催化剂上的反应行为,用以探明该催化剂上丙烷选择氧化制丙烯醛反应的可能路径. 结果表明,异丙氧基是MoPO/SiO2催化剂上丙烷选择氧化制丙烯醛反应的主要中间体,异丙氧基脱β-H生成丙烯或脱α-H生成丙酮,而丙烯则经σ-氧烯丙基转化为丙烯醛.     

激光促进异丁烷选择氧化制甲基丙烯酸

用共沉淀法制备了Fe和Mo的复合氧化物.运用XRD、 IR、 TPD和LSSR技术研究了其晶体结构、表面构造、化学吸附特性和激光促进异丁烷选择氧化反应性能.结果表明: Fe-Mo-O的主体物相为Fe2(MoO4)3,并有少量的MoO3相;其表面上存在Lewis碱位(Mo=O和Mo-O-Fe键中的O)及Lewis酸位Fe3+;异丁烷的两个甲基H分别吸附在两个相邻的Lewis碱位(Mo=O)上形成双位分子吸附态;在常压和200℃条件下,用一定频率的激光激发Mo=O键1000次,异丁烷的转化率为5.8%,其反应产物是异丁烯、甲基丙烯醛和甲基丙烯酸,其中甲基丙烯酸的选择性为80%.根据实验结果,探讨了激光促进异丁烷选择氧化为甲基丙烯酸的表面反应机理.     

乙烷部分氧化制C2氧化物用Fe-A1-P-O催化剂的研究Ⅰ．超细Fe-A1-P-O催化剂的制备与表征

用溶胶-凝胶法制备了超细Fe-Al-P-O催化剂，并用DTA-TG，BET，TEM，XRD，TPR和IR等技术研究了催化剂的微观组成和结构及其晶格氧活性，探讨了催化剂的制备工艺，考察了溶胶．凝胶的形成机理、凝胶干燥及焙烧条件对催化剂微观组成和结构的影响规律．结果表明，Fe-Al-P-O催化剂呈非晶态，是具有均匀分布的超细粒子(10nm)，其比表面积大(238m2／g)，晶格氧活性高．FePO4和AlPO4间隔分布在催化剂表面，形成Lewis碱位(P=O，P-O-Fe)和Lewis颗粒(Fe3 ，Al3 )．     

乙烷部分氧化制C2氧化物用Fe-A1-P-O催化剂的研究 Ⅱ．Fe-A1-P-O催化剂的吸附及催化性能

用化学吸附-IR，化学吸附-TPD和微反技术研究了超细Fe-Al-P-O催化剂的化学吸附性能及对乙烷部分氧化反应的催化性能．结果表明，乙烷能够以-CH3中的H原子吸附于催化剂表面P=O键的端氧上形成分子吸附态，并且随着吸附温度的升高，对乙烷的吸附强度逐渐增大；乙烯则主要是以C=C双键吸附在催化剂的Lewis酸位：Fe3 上．乙烷部分氧化反应的主要产物为乙烯和COx，但在反应物中引入氢的条件下，乙烷部分氧化反应的性能大为改善，并可生成乙醇和乙醛等含氧化合物．     

杂多化合物膜催化异丁烯选择氧化反应

 以多孔钛片为支撑体,将组成为HxCu1．2PAs0．6Mo12Oy的杂多化合物与具有氧溢流效应的氧化物Sb2O4制成催化膜,在特制的膜催化反应器中进行异丁烯选择氧化反应．结果表明,杂多化合物－Sb2O4催化膜具有较高的催化活性;在适宜的条件下,甲基丙烯酸收率可达26.3％,甲基丙烯醛收率可达22.4％,液体产物（即可用产物,包括甲基丙烯酸、甲基丙烯醛、乙酸和丙酮）收率可达67.4％．     

负载型纳米金催化剂用于丙烯气相环氧化反应的研究进展

丙烯气相选择氧化制备环氧丙烷是催化领域的难题之一,负载型纳米金催化剂因在氢气和氧气共存条件下对环氧丙烷具有高选择性而被广泛研究,并在丙烯转化率、反应稳定性、氢气有效利用率上都取得了长足的进步。本文综述了负载型纳米金催化剂用于丙烯气相环氧化反应的研究结果和发展趋势。重点阐述了催化剂制备方法、载体材料、金粒径、催化助剂等对丙烯气相环氧化反应的影响。最后,综合各催化剂的优缺点,分析并展望了具有高转化率与高选择性的纳米金催化剂的前景和发展方向。     

钛硅分子筛中铝杂质对其性能的影响

 以四丙基溴化铵为模板剂,以硅溶胶为硅源,采用水热合成法制备了不同铝杂质含量的钛硅分子筛,并系统考察了铝杂质对钛硅分子筛性能的影响．结果表明,原料中的铝杂质可促进钛硅分子筛晶化,但同时也引入了酸性中心;在丙烯环氧化反应中,铝杂质形成的酸性中心会催化环氧丙烷与溶剂的副反应;加入少量碱性添加物可抑制铝杂质的酸催化作用,提高环氧丙烷的选择性,但过量碱性添加物会使钛硅分子筛失活．     

Copolymerization of carbon dioxide and propylene oxide using an aluminum porphyrin system and its components

The catalytic activities of tetraphenylporphinatoaluminum chloride (TPPAlCl) and its propylene oxide adduct (TPPAl(PO)₂Cl) were investigated in detail together with a quarternary salt Et₄NBr for the copolymerization of carbon dioxide and propylene oxide. In addition, for the components and starting raw materials of the catalyst systems, catalytic activities were examined for the copolymerization. The TPPAlCl catalyst delivered oligomers containing ether linkages to a large extent, regardless of its PO adduction. And cyclic propylene carbonate, as byproduct, was formed in a very small portion. Using the TPPAlCl coupled with Et₄NBr as a catalyst system, the formation of ether linkages was reduced significantly in the copolymerization; however, the obtained oligomer still contained ether linkages of 25.0 mol % in the backbone. On the other hand, the formation of cyclic carbonate was increased to 22.4 mol % relative to the oligomer product. The results indicate that the salt, which was coupled with the TPPAlCl catalyst, plays a key role in reducing the formation of ether linkage in the oligomer and, however, in enhancing the formation of cyclic carbonate. Similar results were obtained for the copolymerization catalyzed by the TPPAl(PO)₂Cl/Et₄NBr system. That is, the formation of ether linkages was not restricted further by the PO adduction of the TPPAlCl component in the catalyst system. Only oligomers with a relatively high molecular weight were produced. This indicates that the PO adduction of the TPPAlCl component contributes highly to the initiation and propagation step in the oligomerization, consequently leading to a relatively high molecular weight oligomer. In contrast, the Et₄NBr, as well as the Et₂AlCl, produced only cyclic carbonate in a very low yield. Furthermore, tetraphenylporphine exhibited no catalytic activity, regardless of using together with Et₄NBr. On the other hand, the Et₂AlCl coupled with Et₄NBr provided a low molecular weight oligomer having ether linkages of 92.3 mol % in addition to the cyclic carbonate. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 3329–3336, 1999     

丙烯环氧化反应用Au／TiO2系列催化剂的制备与表征

 用沉积－沉淀法制备了Au／TiO2系列催化剂，并用XRD，TG－DTA，BET，TEM和IR等技术对催化剂的物相、组成和表面结构进行了表征，利用微反对催化剂在丙烯环氧化反应中的活性进行了评价．结果表明，Au／TiO2催化剂的比表面积在100m2／g以上，Au粒子以纳米级超细颗粒均匀分散在锐钛矿型TiO2的表面．催化剂表面的活性相是Lewis酸位Tin＋与Au粒子，Au可以吸附氢与氧并将其转化为过氧化物．在50～150℃温度范围内，丙烯的转化率为0．56％～1．16％，环氧丙烷的选择性在87％以上．原料气中H2或O2的含量增大时，丙烯的转化率随之升高．在催化剂中引入碱金属或碱土金属的硝酸盐作为助剂，可以不同程度地提高催化剂的活性．     

Copolymerization of propylene oxide with carbon dioxide catalyzed by zinc adipate

Copolymerization of carbon dioxide with propylene oxide in the presence of zinc adipate was studied. The effects of the temperature, nature of the solvent, and catalyst concentration on the molecular weight, molecular-weight distribution, and yields of the copolymer and propylene carbonate were examined. The structure of the polymer obtained was studied by ¹³N and ¹I NMR spectroscopy.     

离子交换树脂催化合成碳酸亚丙酯

碘型离子交换树脂在某些偶极非质子性溶剂的作用下，能有效地催化二氧化碳与环氧丙烷合成碳酸亚丙酯，并能重复使用至少10次而仍能保持较高的催化活性。     

Catalytic Formation of Propylene Carbonate from Supercritical Carbon Dioxide/Propylene Oxide Mixture

TheuseofsupercriticalcarbondioxideasasubstitUtesolventforchemicalsynthesisisaveryattractiveareainviewofresourceutiIizationandenvironmentalproblems"'.SinceCO2,whichhasaneasilyaccessibIecriticalpointwithaTcof3l.l'CandaPcof7.3MPa,isnontoxic,nonflammableandinexpensive,itcanreplacehazardousorganicsolventandtherebyprovideavaluablepollutionpreventiontool.Assimilartoothersupercriticalfluids,SC-CO,hasgaslikediffusitivityandliquidIikedensity,andchangingpressureandtemperaturecanvaryitsphysicalpro…     

丙烯氨氧化Mo-Bi-Fe-P/海泡石负载型催化剂的研究

丙烯氨氧化Mo-Bi-Fe-P/海泡石负载型催化剂的研究     

聚苯乙烯负载聚乙二醇在合成碳酸亚丙酯上的应用

用金属钾、金属钠以及氢氧化钠水溶液等方法制备聚苯乙烯负载聚乙二醇，结果表明，采用金属钾比金属钢具有更好的接枝效果，并能使反应在较低的温度下较快进行。在氢氧化钠溶液中添加少量相转移剂，如Bu4NBr，接枝效果也有所提高。以聚苯乙烯负载聚乙二醇和KI一起为催化剂，研究了溶剂、温度等因素对CO2与环氧丙烷合成碳酸亚丙酯催化活性的影响。结果表明，以甲醇为溶剂催化活性较高。研究还表明，聚苯乙烯负载聚乙二醇具有较好的热稳定性，可以在150℃下重复使用至少5次。     

不同介质中热处理TS-1的表征及催化性能

 分别以水汽和空气为介质对TS－1进行热处理，并采用XRF，XRD，FT－IR，UV－Vis，27AlMASNMR，29SiMASNMR，31PMASNMR和NH3－TPD等手段对TS－1热处理后骨架结构变化及B酸中心和酸量变化进行了分析．以丙烯环氧化反应为探针，考察了酸中心变化对TS－1催化性能的影响．结果表明，TS－1中的微量铝随着热处理温度的升高而减少，导致B酸中心数量及总酸量减少，环氧丙烷选择性提高，以水汽为介质热处理时脱铝更明显．热处理温度达到750℃时，TS－1分子筛中的硅氧四面体发生变化，不同的介质对骨架钛产生不同的影响．