Electrodeposition and magnetic properties of Ni nanowire arrays on anodic aluminum oxide/Ti/Si substrate

Ni nanowire arrays with different diameters have now been extended to directly fabricate in porous anodic alumina oxide (AAO) templates on Ti/Si substrate by direct current (DC) electrodeposition. An aluminum film is firstly sputter-deposited on a silicon substrate coated with a 300 nm Ti film. AAO/Ti/Si substrate is synthesized by a two-step electrochemical anodization of the aluminum film on the Ti/Si substrate and then used as template to grow Ni nanowire arrays with different diameters. The coercivity and the squareness in parallel direction of Ni nanowires with about 10 nm diameters are 664 Oe and 0.90, respectively. The Ni nanowire arrays fabricated on AAO/Ti/Si substrates should lead to practical applications in ultrahigh-density magnetic storage devices because of the excellent properties.     

Fabrication and magnetic properties of amorphous Co0.71Pt0.29 nanowire arrays

Highly ordered Co_0.71Pt_0.29 alloy nanowire arrays have been fabricated successfully by direct current electro-deposition into the pores of a porous anodic aluminum oxide (AAO) template. SEM and TEM images reveal that the nanowires of array are uniform, well isolated, and parallel to one another. The aspect ratio of nanowires is over 200. XRD and EDS pattern indicates that amorphous Co_0.71Pt_0.29 structure was formed during electro-deposition. In amorphous sample, magnetocrystal anisotropy is very small, therefore, shape anisotropy plays a dominant role which leads to strong perpendicular anisotropy. High coercivity (Hc=1.7 kOe) and squareness (Mr/Ms) around 0.7 were obtained in the samples when the field was applied parallel to the axis of the nanowires. However, when it changed to polycrystalline structure after annealing, due to the competition of magnetocrystal anisotropy and shape anisotropy, the sample did not display perpendicular anisotropy.     

Influence of partial rare-earth substitution for Sm in the giant intrinsic magnetic hardness compound SmCo2Ni3

The phenomenon of giant intrinsic magnetic hardness is investigated in compounds R_1−x Sm _x Co₂Ni₃ with R=Y, Pr, Gd, Tb, Er. Partial Er substitution for Sm actually increases magnetic hardness while all other substitutions decrease magnetic hardness. The strength of coercivity is thus dependent on both the sign and magnitude of the crystal field interaction. The temperature dependence of coercivity is complex in the case of Pr substitution as a result of competing effects from thermal activation and a decrease in anisotropy at low temperatures. This study has been supported by a grant from the National Science Foundation.     

Giant intrinsic magnetic hardness in RFe5−x Ni x (R=rare earth,x=4 to 5)

Giant low temperature intrinsic magnetic hardness is observed in structurally homogeneous CaCu₅ type compounds RFe_5−x Ni _x . In SmFe_5−x Ni _x , this magnetic hardness peaks approximately at a composition SmFe_0.2Ni_4.8, with an extrapolated coercive force of 230 kOe at absolute zero. The transition metal sublattice is not anisotropic. Thus, the rare earth alone creates giant coercivity. Only compounds withc-axis preference exhibit substantial magnetic hardness (Sm, Er, Tm). Partial substitution of a tetravalent rare earth to produce crystal field anisotropy fluctuations apparently increases coercivity somewhat in the axis-preference compound SmFeNi₄, but has no effect in the plane-preferred compound TbFeNi₄.     

Magnetic Force Microscopy Study of Alternate Sputtered （001） Oriented L1o Phase FePt Films

We present a magnetic force microscopy study of alternate sputtered （001） oriented L1o phase FePt films. It is found that the root-mean-square value of phase shift of magnetic force images, （ △Ф）rms, can be used to characterize the perpendicular anisotropy for a series of specimens. Therefore, the considerable improvement of the perpendicular anisotropy after post-annealing can be characterized. In addition, the magnetic properties, magnetic and crystalline microstructures before and after post-annealing are compared for the typical [Fe5nm Pt5 nm]10 film with substrate temperature T8 = 500℃, single layer thickness d = 5 nm and total layer thickness D=100 nm to confirm the effect of post-annealing on improving the perpendicular anisotropy for Fe-Pt films.     

Magnetic and magneto-optical properties of FeRh thin films

The magnetic and magneto-optical properties of FeRh thin films epitaxially deposited onto MgO(1 0 0) substrates by RF sputter-deposition system have been investigated in conjunction with the structure. An intriguing virgin effect has been found in the M–T curves of the as-deposited FeRh thin films, which is presumably interpreted in term of a change in structural phase when heating. Also, a (negative) maximum peak of Kerr rotation at around 3.8 eV has been observed when FeRh thin films are in ferromagnetic state. The polar Kerr rotation angle is found to increase at temperatures above 100 °C, which corresponds to the antiferromagnet (AF)–ferromagnet (FM) transition of FeRh thin films.     

Structural and magnetic properties of SmCo5.6Ti0.4 alloy

Three series of SmCo_5.6Ti_0.4 samples were prepared by quenching, melt spinning, and ball milling, respectively. Annealing at different temperatures was carried out for the three series. The influence of the processing routes on the structural and magnetic properties was systematically investigated for this alloy. The as-quenched bulk sample consisted of three phases with a rather coarse grain microstructure. Low intrinsic coercivity (_iH_c) of 0.12 T was obtained in this sample. While the as-spun ribbons and as-milled/annealed powders showed the CaCu₅-type phase (1:5) plus Th₂Zn₁₇-type phase (2:17), and the 1:5 phase plus TbCu₇-type phase (1:7), respectively, with nanograin microstructure. The _iH_c of as-spun ribbons and as-milled/annealed (700 °C for 2 h) powders was found to be 0.59 and 2.23 T, respectively. Coercivity mechanism of these as-spun ribbons is mainly of nucleation type. In the as-milled/annealed powders, the network of the nanograin boundaries is believed to provide strong pinning sites for the domain wall movement.     

Hard magnetic properties of ErCo7−xCux [0.3⩽x⩽1] system

We report the observation of excellent hard magnetic properties on purely single phase ErCo_7−xCu_x compounds with x=0.3, 0.5, 0.8 and 1. Cu substitution leads to a decrease in the saturation magnetization, but enhances the uniaxial anisotropy in this system. The large anisotropy field (∼100 kOe) is attributed to the Er and the Co sublattices. Domain wall pinning effect seems to play a crucial role in determining the temperature and field dependences of magnetization in these compounds. The hard magnetic properties obtained at room temperature (RT) are comparable to the best results obtained in other RCo₇ based materials.     

Structure and magnetic properties of SmCoxTi0.4-1:7 ribbons

SmCo_xTi_0.4 (x=6.6, 7.1, 7.6, 8.1) ribbons have been prepared by melt spinning at a wheel speed of 42 m/s, followed by annealing at 750 °C for 2 h. Both as-spun and as-annealed ribbons possess the disordered TbCu7-type (1:7) phase even when the Sm/(Co,Ti) atomic ratio deviates from 1/7. The c/a ratio increases with increasing Co concentration x, but the unit cell volume decreases. The Curie temperatures show above 700 °C, increasing from 707 °C for x=6.6 to 782 °C for x=8.1. The saturation magnetizations increase almost linearly with increasing Co content. The observed magnetic hardening is believed to arise from the high magnetocrystalline anisotropy of the 1:7 phase and the fine nanograin structure. The intrinsic coercivity of 9797 Oe has been obtained in the melt-spun SmCo_7.1Ti_0.4 ribbons.     

Structural and magnetic properties of SmCo7−xMox alloys

Phase structure and magnetic properties of the as-cast and as-milled/annealed SmCo_7−xMo_x (x=0, 0.1, 0.2, 0.3, 0.4) alloys have been systematically studied. It is found that all the as-cast series alloys are composed of the CaCu₅-type and Th₂Zn₁₇-type phases. Saturation magnetization of the samples decreases with the Mo content increasing. Intrinsic coercivities (_iH_c) of no more than 0.06 T are observed in these as-cast samples, due to their rather coarse grain microstructures with an average grain size of 50 μm. The as-milled/annealed SmCo_7−xMo_x powders crystallize in the disordered TbCu₇-type (1:7) structure with very fine nanograins, and a minor Co₃Mo phase appears in the samples with x=0.1-0.4. High _iH_c (?0.95 T) are achieved in these samples, with a maximum of 1.26 T located at x=0.2, which can be primarily attributed to strong pinning of the domain wall motion at the nanograin boundaries. The temperature coefficient (β) of the _iH_c is about −0.22%/°C in the temperature range of 25-400 °C for the as-milled/annealed samples.     

On the correlation between microstructure and magnetic losses in electrical steel

The magnetic properties of electrical steel such as magnetization curves, magnetization behavior and specific magnetic losses are related to the microstructure and the texture of the steel. A quantitative model, which describes the effect of microstructure and texture and their interplay on the magnetic losses P, is still missing. Based on experimental data for nonoriented electrical steels and FeSi-samples with high (Si, Al)-content, a more general formula is proposed for the dependence of P, at a given value of magnetic induction B, as a function of the mean value of the grain size d of the material and of the intensities of the relevant magnetic texture components.     

The growth of soft magnetic FeNiN thin films under different experimental procedures

FeNiN thin films with good soft magnetic properties were synthesized on Si (1 0 0) substrates at 473 K by RF magnetron sputtering. The dependence of phase structure and magnetic properties on nitrogen partial pressure, nickel concentrations, film thickness and substrate temperature were systematically investigated. The phase evolution from α-(Fe,Ni)N to ξ-(Fe,Ni)₂N with increase of nitrogen partial pressure was seen. The addition of Ni caused FeNiN films to turn from BCC structure to FCC structure. Clear reproducible striped domains appeared at the film surfaces when X_Ni=19.6%, which is explained by the high enough perpendicular anisotropy and the small stress in the film. All films show smooth surfaces and good soft magnetic properties compared to corresponding FeN compounds. The magnetic properties depended dramatically on the phase structure. Optimum soft magnetic properties with H_C of <1 Oe are obtained between 5.0%?X_Ni?10.0%.     

Magnetic anisotropy-induced spin-reorientation in spinel FeCr2S4

In this paper, the low-field magnetic behavior of polycrystalline FeCr₂S₄ was investigated by thermal circling the sample from 5 to 200 K at a constant magnetic field. We show that, upon cooling the sample at 50 Oe to a temperature below the Curie temperature then warming back, the magnetization displays irreversibility between cooling and warming sequence. The irreversible behavior was suppressed gradually with increasing magnetic field. By considering spin-reorientation due to the increase of magnetic anisotropy upon cooling, the irreversible behavior has been explained qualitatively.     

Magnetic properties of Nd–Fe–B film magnets prepared by RF sputtering

Highly oriented films of ∼6 μm in thickness consisting of the Nd₂Fe₁₄B compound phase were obtained by a three-dimensional sputtering method at room temperature and the subsequent crystallization by annealing. The c-axis orientation and coercivity of film samples were sensitive to the sputtering parameters and annealing conditions. The optimum temperature and time for annealing were 650 °C and 30 min to show the highest coercivity without any deterioration for the orientation of Nd₂Fe₁₄B grains, and furthermore the degree of c-axis orientation was increased by decreasing the Ar gas pressure or input power for sputtering. The resultant film magnets with good magnetic properties of B_r=∼1.06 T, H_C=∼371 kA/m, and (BH)_max=∼160 kJ/m³ were obtained under the optimized parameters for sputtering.     

Investigation of magneto-anisotropy field for system of particles with near superparamagnetic volume

We obtained the temperature dependence for low-field boundary of the anisotropy field distribution in a system of barium hexaferrite nanocrystals in the temperature range from 300 to 700 K. We treated the experimental data taking into account the influence of thermal fluctuations on the anisotropy field and the transition of particles into the paramagnetic state, stimulated by external magnetic field. We showed that the dependence under consideration is formed by particles of different volume, which increased from 3.5×10⁻¹⁸ to 40×10⁻¹⁸ cm³ while the particles lost their magnetic stability with the temperature growth.     

Measurement of the coupling strength distribution in ferromagnetic (F)/antiferromagnetic (AF) exchange bias systems

We propose a method for determination of the distribution function P(j) of the coupling energy density j in polycrystalline textured ferromagnetic (F)/antiferromagnetic (AF) film systems. P(j) governs the entire film coupling J and the exchange bias field H_e and was not measurable until now. The method is verified by torquemetry in a high magnetic field and by reversing its rotation sense. The transition to a new magnetic steady state after rotation reversal is analyzed within a Stoner–Wohlfarth model including thermal relaxation. This transition is completed earlier for strongly coupled grains than for grains with smaller j, which is reflected in the torque curves. We determined P(j) for a sputtered NiFe(16 nm)/IrMn(0.8 nm) film at T=50 K in the hysteretic range of coupling energies and found that P strongly decreases for increasing j.     

Low-temperature first-order reversal curves and interaction effects on assemblies of iron oxide nanoparticles

We present the synthesis and magnetic properties of high quality uncoated and gold-coated iron oxide magnetic nanoparticles. The structural properties of these nanoparticles are investigated by transmission electron microscopy, UV-visible spectroscopy and X-ray diffraction. Experimental results and theoretical simulations indicate that the synthesized nanoparticles present a very good monodispersity, and well defined size and shape. The coercive field of these particles is identified by low-temperature first-order reversal curves and the results used in order to fit zero-field-cooled magnetization processes with theoretical models. The identification of the parameters in this analysis suggests that the coating process hardly affects the morphology and the overall magnetic properties of the cores inside coated particles.     

Effect of C layer on the structures and magnetic properties of (0 0 1)-oriented [C/CoPt]n/Ag films

CoPt/Ag and [C/CoPt]n/Ag thin films have been prepared onto the glass substrates by magnetron sputtering. We investigated the evolution of texture and magnetic properties of CoPt/Ag and [C/CoPt]n/Ag films. The results show that C-doping plays an important role in improving (0 0 1) texture, improving the order parameter S, reducing the intergrain interactions, and making the magnetization reversal mechanism more close to Stoner-Wolfarth rotational mechanism. The growth mechanism of (0 0 1) texture also seems to be related strongly to the films thickness. Our results show that the highly (0 0 1)-oriented films with ordered fct phase have a significant potential for the perpendicular media of extremely high-density recording.