Effects of deposition parameters on laser-induced damage threshold of Ta2O5 films

Ta₂O₅ films were deposited on BK7 substrates by e-beam evaporation with different deposition parameters such as substrate temperature (323-623 K), oxygen pressure (0.5-3.0×10⁻² Pa) and deposition rate (0.2-0.5 nm/s). Absorption, scattering and chemical composition were investigated by surface thermal lensing (STL) technique, total integrated scattering (TIS) measurement and X-ray photoelectron spectroscopy (XPS), respectively. The laser-induced damage threshold (LIDT) was assessed using pulsed Nd:YAG 1064 nm laser at a pulse length of 12 ns. The results showed that optical properties, absorption and LIDT were influenced by the deposition parameters and annealing. However, scattering was little correlated with the deposition parameters. On the whole, the LIDT increased with increasing substrate temperature and oxygen pressure, whereas it increased firstly and then decreased upon increasing deposition rate. After annealing at 673 K for 12 h, the LIDT of films improved significantly. The dependence of possible damage mechanism on deposition parameters was discussed.     

High temperature annealing effect on structure, optical property and laser-induced damage threshold of Ta2O5 films

Ta₂O₅ films were deposited by conventional electron beam evaporation method and then annealed in air at different temperature from 873 to 1273 K. It was found that the film structure changed from amorphous phase to hexagonal phase when annealed at 1073 K, then transformed to orthorhombic phase after annealed at 1273 K. The transmittance was improved after annealed at 873 K, and it decreased as the annealing temperature increased further. The total integrated scattering (TIS) tests and AFM results showed that both scattering and root mean square (RMS) roughness of films increased with the annealing temperature increasing. X-ray photoelectron spectroscopy (XPS) analysis showed that the film obtained better stoichiometry and the O/Ta ratio increased to 2.50 after annealing. It was found that the laser-induced damage threshold (LIDT) increased to the maximum when annealed at 873 K, while it decreased when the annealing temperature increased further. Detailed damaged models dominated by different parameters during annealing were discussed.     

Influence of overcoat on laser-induced damage threshold of 532 and 800 nm TiO2/SiO2 high reflectors

TiO₂/SiO₂ high reflectors with and without a SiO₂ overcoat are deposited by electron-beam evaporation. The film properties are characterized by visible spectrometry measures, structure analysis, roughness and laser-induced damage threshold (LIDT) tests, surface defects and damage morphology observation. The effects of overcoats on LIDT at 532 nm, 8 ns and 800 nm, 220 ps laser pulses are investigated. The relations between film structure, roughness, surface defects, electric field and LIDT are discussed. It is found that overcoats can increase the LIDT at these two laser wavelengths. The reduction of peak temperature, the low defects density and roughness, the low intrinsic absorption of SiO₂ and its amorphous structure are the main reasons for LIDT improvement by overcoats.     

Optical properties of In2O3 oxidized from InN deposited by reactive magnetron sputtering

Unintentionally doped and zinc-doped indium nitride (U-InN and InN:Zn) films were deposited on (0 0 0 1) sapphire substrates by radio-frequency reactive magnetron sputtering, and all samples were then treated by annealing to form In₂O₃ films. U-InN and InN:Zn films have similar photon absorption characteristics. The as-deposited U-InN and InN:Zn film show the absorption edge, ∼1.8-1.9 eV. After the annealing process at 500 °C for 20 min, the absorption coefficient at the visible range apparently decreases, and the absorption edge is about 3.5 eV. Two emission peaks at 3.342 eV (371 nm) and 3.238 eV (383 nm) in the 20 K photoluminescence (PL) spectrum of In₂O₃:Zn films were identified as the free-exciton (FE) or the near band-to-band (B-B) and conduction-band-to-acceptor (C-A) recombination, respectively.     

Effects of annealing on laser-induced damage threshold of TiO2/SiO2 high reflectors

The mechanism of improving 1064 nm, 12 ns laser-induced damage threshold (LIDT) of TiO₂/SiO₂ high reflectors (HR) prepared by electronic beam evaporation from 5.1 to 13.1 J/cm² by thermal annealing is discussed. Through optical properties, structure and chemical composition analysis, it is found that the reduced atomic non-stoichiometric defects are the main reason of absorption decrease and LIDT rise after annealing. A remarkable increase of LIDT is found at 300 °C annealing. The refractive index and film inhomogeneity rise, physical thickness decrease, and film stress changes from compress stress to tensile stress due to the structure change during annealing.     

Deposition and characterization of layer-by-layer sputtered AgGaSe2 thin films

Sputtering technique has been used for the deposition of AgGaSe₂ thin films onto soda-lime glass substrates using sequential layer-by-layer deposition of GaSe and Ag thin films. The analysis of energy dispersive analysis of X-ray (EDXA) indicated a Ga-rich composition for as-grown samples and there was a pronounce effect of post-annealing on chemical composition of AgGaSe₂ thin film. X-ray diffraction (XRD) measurements revealed that Ag metallic phase exists in the amorphous AgGaSe₂ structure up to annealing temperature 450 °C and then the structure turned to the single phase AgGaSe₂ with the preferred orientation along (1 1 2) direction with the annealing temperature at 600 °C. The surface morphology of the samples was analyzed by scanning electron microscopy (SEM) measurements. The structural parameters related to chalcopyrite compounds have been calculated. Optical properties of AgGaSe₂ thin films were studied by carrying out transmittance and reflectance measurements in the wavelength range of 325-1100 nm at room temperature. The absorption coefficient and the band gap values for as-grown and annealed samples were evaluated as 1.55 and 1.77 eV, respectively. The crystal-field and spin-orbit splitting levels were resolved. These levels (2.03 and 2.30 eV) were also detected from the photoresponse measurements almost at the same energy values. As a result of the temperature dependent resistivity and mobility measurements in the temperature range of 100-430 K, it was found that the decrease in mobility and the increase in carrier concentration following to the increasing annealing temperature attributed to the structural defects (tetragonal distortion, vacancies and interstitials).     

Calculation of temperature fields with a film-substrate interfacial layer model to discuss the layer-pair number effects on the damage thresholds of LaF3/MgF2 high reflectors at 355 nm

Laser induced damage thresholds (LIDT) of LaF₃/MgF₂ high reflectors at 355 nm were measured and investigated as a function of layer-pair number. Generally, LaF₃/MgF₂ coatings with more layer pairs possessed higher LIDT, but coatings with too high layer-pair number crazed because of high tensile stress, so the LIDT of them decreased badly. The temperature rise in the coatings was calculated based on a film-substrate interfacial absorption model, and the depth of the damage in the coatings were measured by a Veeco optical profilograph. The two characterization methods together were used to interpret the effects of layer-pair number on LIDT, and the damage mechanism of coatings at laser wavelength of 355 nm was also discussed.     

Preparation of sol-gel ZrO2-SiO2 highly reflective multilayer films and laser-induced damage threshold characteristic

Sol-gel (ZrO₂/SiO₂)¹² ZrO₂ films were prepared by spin coating method. The reflectivity spectrum of the films was measured with a Lambda 900 spectrometer. In order to investigate laser-induced damage threshold (LIDT) characteristic of highly reflective films, one-layer ZrO₂ and SiO₂ films, two-layer ZrO₂/SiO₂ and SiO₂/ZrO₂ films were also prepared by spin coating method. LIDT of each film was measured. Damage morphology after laser irradiation was characterized by optical microscopy (Nikon E600K). The experimental results showed that the reflectivity of (ZrO₂/SiO₂)¹² ZrO₂ film at 1064 nm and 355 nm wavelength is 99.7%. The LIDT results decreases as the number of layer of films increases. All the films have similar damage morphology. The experimental results are explained by the different temperature profiles of the films.     

The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Characterization of chemically deposited ZnSe/SnO2/glass films: Influence of annealing in Ar atmosphere on physical properties

The Zinc Selenide (ZnSe) thin films have been deposited on SnO₂/glass substrates by a simple and inexpensive chemical bath deposition (CBD). The structural, optical and electrical properties of ZnSe films have been characterized by X-ray diffraction (XRD), Energy Dispersive X-ray Analysis (EDAX), optical absorption spectroscopy, and four point probe techniques, respectively. The films have been subjected to different annealing temperature in Argon (Ar) atmosphere. An increase in annealing temperature does not cause a complete phase transformation whereas it affects the crystallite size, dislocation density and strain. The optical band gap (E_g) of the as-deposited film is estimated to be 3.08 eV and decreases with increasing annealing temperature down to 2.43 eV at 773 K. The as-deposited and annealed films show typical semiconducting behaviour, dρ/dT > 0. Interestingly, the films annealed at 373 K, 473 K, and 573 K show two distinct temperature dependent regions of electrical resistivity; exponential region at high temperature, linear region at low temperature. The temperature at which the transition takes place from exponential to linear region strongly depends on the annealing temperature.     

Creation of nanoparticles and luminescence in Al2O3 crystal by Zn ion implantation

Single crystal α-Al₂O₃ wafers were implanted with 45 keV Zn ions up to a fluence of 1×10¹⁷ ions/cm², and were then subjected to furnace annealing in oxygen atmosphere at different temperatures. Various techniques have been applied to study the creation of nanoparticles (NPs), defects and their thermal evolutions, as well as their effects on optical properties of Al₂O₃. Our results clearly show that Zn NPs have been synthesized in the as-implanted sample and they begin to be oxidized at 500 °C. Two broad photoluminescence bands appear in the Zn ion-implanted samples and their intensities depend on the annealing temperatures. The results have been interpreted in view of creation of the defects and NPs, Zn atoms diffusion as well as their thermal evolution during annealing.     

Investigations on co-evaporated Cu2SnSe3 and Cu2SnSe3-ZnSe thin films

Cu₂SnSe₃ is an important precursor material for the growth of Cu₂ZnSnSe₄, an emerging solar cell absorber layer via solid state reaction of Cu₂SnSe₃ and ZnSe. In this study, we have grown Cu₂SnSe₃ (CTSe) and Cu₂SnSe₃-ZnSe (20%) films onto soda-lime glass substrates held at 573 K by co-evaporation technique. The effect of annealing of these films at 723 K for an hour in selenium atmosphere is also investigated. XRD studies of as-deposited Cu₂SnSe₃ and Cu₂SnSe₃-ZnSe films indicated SnSe as secondary phase which disappeared on annealing. The direct optical band gap of annealed Cu₂SnSe₃ and Cu₂SnSe₃-ZnSe films were found to be 0.90 eV and 0.94 eV respectively. Raman spectroscopy studies were used to understand the effect of ZnSe on the properties of Cu₂SnSe₃.     

Synthesis and characterization of thermoluminescent Li2B4O7 nanophosphor

Lithium borate (Li₂B₄O₇) is a low Z_eff, tissue equivalent material that is commonly used for medical dosimetry using the thermoluminescence (TL) technique. Nanocrystals of lithium borate were synthesized by the combustion method for the first time in the laboratory. TL characteristics of the synthesized material were studied and compared with those of commercially available microcrystalline Li₂B₄O₇. The optimum pre-irradiation annealing condition was found to be 300 °C for 10 min and that of post-irradiation annealing was 300 °C for 30 min. The synthesized Li₂B₄O₇ nanophosphor has very poor sensitivity for low doses of gamma up to 10¹ Gy whereas from 10¹ to 4.5×10² Gy this phosphor exhibits a linear response and then from 4.5×10² to 10³ Gy it shows supralinearity. Thermoluminescence properties of Li₂B₄O₇ nanophosphor doped with Cu has also been investigated in this paper. It shows low fading and a linear response over a wide range of gamma radiation from 1×10² to 5×10³ Gy. Therefore the synthesized lithium borate nanophosphor doped with Cu may be used for high dose measurements of gamma radiations.     

A study of the properties and microstructure of Ni81Fe19 ultrathin films with MgO

The anisotropic magnetoresistance (AMR) of a Ta (5 nm)/MgO (3 nm)/Ni₈₁Fe₁₉ (10 nm)/MgO (2 nm)/Ta (3 nm) film with MgO-Nano Oxide Layer (NOL) increases dramatically from 1.05% to 3.24% compared with a Ta (5 nm)/Ni₈₁Fe₁₉ (10 nm)/Ta (3 nm) film without the MgO-NOL layer after annealing at 380 °C for 2 h. Although the MgO destroys the NiFe (1 1 1) texture, it enhances the specular electron scattering of the conduction electrons at the NOL interface and suppresses the interface reactions and diffusion at the Ta/NiFe and NiFe/Ta interfaces. The NiFe (1 1 1) texture was formed after the annealing, resulting in a higher AMR ratio. X-ray photoelectron spectroscope results show that Mg and Mg²⁺ were present in the MgO_x films.     

Synthesis, structural and magnetic properties of the nanocomposite Fe63B23Nd7Y3Nb3Cr1 magnets

The Fe₆₃B₂₃Nd₇Y₃Nb₃Cr₁ nanocomposite magnets in the form of sheets have been prepared by copper mold casting technique. The phase evolution, crystal structure, microstructural and magnetic properties have been investigated in the as-cast and annealed states. The as-cast sheets show magnetically soft behaviors which become magnetically hard by thermal annealing. The optimal annealed microstructure was composed of nanosize soft magnetic α-Fe (19-29 nm) and hard magnetic Nd₂Fe₁₄B (45-55 nm) grains. The best hard magnetic properties such as intrinsic coercivity, _jH_c of 1119 kA/m, remanence, B_r of 0.44 T, magnetic induction to saturation magnetization ratio, M_r/M_s=0.61 and maximum energy product, (BH)_max of 55 kJ/m³ was obtained after annealing at 680 °C for 15 min. The annealing treatment above 680 °C results in non-ideal phase grains growth, which degrade the magnetic properties.     

Surface characterization and luminescent properties of SrAl2O4:Eu,Dy nano thin films

SrAl₂O₄:Eu²⁺, Dy³⁺ thin films were grown on Si (1 0 0) substrates in different atmospheres using the pulsed laser deposition (PLD) technique. The effects of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological and photoluminescence (PL) properties of the films were investigated. The films were ablated using a 248 nm KrF excimer laser. Improved PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres compared to those prepared in vacuum. A stable green emission peak at 520 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions was obtained. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The diffusion of adventitious C into the nanostructured layers deposited in the Ar and O₂ atmospheres was most probably responsible for the quenching of the PL intensity after annealing.     

Annealing effect on CdS/SnO2 films grown by chemical bath deposition

The extensive investigation of the annealing effect in nitrogen atmosphere on the structural optical and electrical properties of chemically deposited CdS films on SnO₂ has been performed. The as-deposited film shows 2.45 eV band gap (E_g) and decreases with increasing annealing temperature. The film annealed at 623 K having pure hexagonal phase (a = 4.14 Å, c = 6.71 Å for [1 0 0] plane) and E_g = 2.36 eV shows 10 times higher conductivity for all temperature range, and shows two different activation energies E_a = 0.114 eV and E_a = 0.033 eV for the temperature range 395 K ≤ T ≤ 515 K and 515 K ≤ T ≤ 585 K, respectively. The structural parameters such as dislocation density, strain and optical parameters such as absorption and extinction coefficient are calculated and compared for all the films.     

Influences of CO2 laser annealing on mechanical and laser-induced damage properties of ZrO2 thin films

Zirconium dioxide (ZrO₂) thin films were deposited on BK7 glass substrates by the electron beam evaporation method. A continuous wave CO₂ laser was used to anneal the ZrO₂ thin films to investigate whether beneficial changes could be produced. After annealing at different laser scanning speeds by CO₂ laser, weak absorption of the coatings was measured by the surface thermal lensing (STL) technique, and then laser-induced damage threshold (LIDT) was also determined. It was found that the weak absorption decreased first, while the laser scanning speed is below some value, then increased. The LIDT of the ZrO₂ coatings decreased greatly when the laser scanning speeds were below some value. A Nomarski microscope was employed to map the damage morphology, and it was found that the damage behavior was defect-initiated both for annealed and as-deposited samples. The influences of post-deposition CO₂ laser annealing on the structural and mechanical properties of the films have also been investigated by X-ray diffraction and ZYGO interferometer. It was found that the microstructure of the ZrO₂ films did not change. The residual stress in ZrO₂ films showed a tendency from tensile to compressive after CO₂ laser annealing, and the variation quantity of the residual stress increased with decreasing laser scanning speed. The residual stress may be mitigated to some extent at proper treatment parameters.     

Collision-induced first overtone band of D2 in binary mixtures D2-X where X is Ar, Kr, and Xe

Enhancement spectra of the collision-induced absorption in the first overtone region 5500-6750 cm⁻¹ of D₂ in the D₂-Ar, D₂-Kr, and D₂-Xe binary mixtures were studied at 298 K for base densities of D₂ in the range 55-251 amagat and for partial densities of Ar, Kr, and Xe in the range 46-384 amagat. The observed spectra consist of the following quadrupolar transitions: O₂(3), O₂(2), Q₂ (J), J = 1-5 and S₂ (J), J = 0-5 of D₂. Binary and ternary absorption coefficients were determined from the integrated absorption coefficients of the band. Profile analyses of the spectra were carried out using the Birnbaum-Cohen (BC) lineshape function and characteristic lineshape parameters were determined from the analyses.     

Magnetotransport properties of epitaxial Pr0.5Ca0.5MnO3 films grown by a solution technique

Epitaxial Pr_0.5Ca_0.5MnO₃ films have been synthesized on (0 0 1) SrTiO₃ substrate using a chemical solution deposition technique and two-step post-annealing process. The zero field resistivity of the films shows semiconducting behavior and a characteristic of charge ordering is observed at 230 K. The resistivity of the 10 nm film did not show any effect with the magnetic field. However, melting of charge ordering was observed for the 120 nm film at an applied magnetic field of 4 T. Large decrease in the resistivity of the 120 nm film (<100 K) resulted in magnetoresistance of nearly −100% at 75 K.