Raman scattering of the mixed chalcogenide glass system As2SxSe3-x

Polarized room temperature Raman spectra of glassy As₂S_xSe_3-x for 0≦×≦3 have been measured. Spectra for crystalline As₂S₁Se₂ are reported. The polarization and intensity dependence upon composition are consistent with mixed pyramids of composition As₂S_nSe_3-n and preclude phase separation in the glassy system.     

Growth and Raman spectroscopic characterization of As4S4 (II) single crystals

As described by Kutoglu (1976 [16]), single crystals of As₄S₄ (II) phase have been grown using a new two-step synthesis that drastically increases the reproducibility that is attainable in synthetic experiments. First, through photo-induced phase transformation, pararealgar powder is prepared as a precursor instead of AsS melt. Then it is dissolved and recrystallized from CS₂ solvent. Results show that single crystals of the As₄S₄ (II) phase were obtained reproducibly through the dissolution–recrystallization process. Single crystals of As₄S₄ (II) obtained using this method were translucent and showed a uniform yellow-orange color. The crystal exhibits a platelet-like shape as a thin film with well-developed faces (0 1 0) and (0 1¯ 0). The grown crystals are as large as 0.50×0.50×0.01 mm. They were characterized using powder and single crystal X-ray diffraction techniques to confirm the phase identification and the lattice parameters. The As₄S₄ (II) phase crystallizes in monoclinic system with cell parameters a=11.202(4) Å, b=9.954(4) Å, c=7.142(4) Å, β=92.81(4)°, V=795.4(6) Å³, which shows good agreement with the former value. Raman spectroscopic studies elucidated the behavior of the substance and the relation among phases of tetra-arsenic tetrasulfide.     

Vibrational properties of As2S3 glass

Vibrational densities of states and infrared and Raman spectra have been calculated for a structural model of As₂S₃ glass. The calculations are based on simple semi-empirical forms for interatomic potentials, electric dipole moment and Raman polarizability. The bands of the calculated spectra agree well with those of the observed infrared and Raman spectra of As₂S₃ glass in intensity and position, although a small concentration of the wrong SS bonds remains in the structural model and causes an additional peak in the higher frequency region. The calculated depolarization ratio of the Raman spectra is consistent with the observed one.     

Medium range order and optical properties of As2S3 glass

Low frequency Raman scattering and optical absorption edge were measured for As₂S₃ glasses quenched at temperature in the supercooling region of the glasses. It was found that both the Raman spectrum and the optical absorption edge shift to the lower energy side with the rise of the quenching temperature. The effects were interpreted in terms of the order of the arrangements of the layer-like clusters, which become more random as the quenching temperature goes higher.     

Preparation of mixed arsenic/antimony chalcogenide glasses and some optical and thermo-physical properties

The preparation of mixed glasses of As₂S_3−xSe_x (x = 0–3) and (1 − y) · As₂S₃y · Sb₂S₃ (y = 0–1) has been carried out by an in situ pouring technique. X-ray diffraction (XRD) was used to confirm the glassy nature of the materials and monitor devitrification. Visible-IR transmission, photoluminescence, refractive index and micro-Raman were measured as a function of composition. Microhardness (MH) and thermal expansion coefficient (TEC) were also measured. Raman peaks in As₂S₃ and As₂Se₃ were observed around 338 cm⁻¹ and 230 cm⁻¹, respectively in this first composition series in which S was replaced by Se. When As was replaced by Sb, in the case of second composition series, the As₂S₃ related Raman peak became broader and shifted to lower wave number, reflecting some structural change/devitrification. MH increased (1.31–1.50 GPa) with Se and Sb content while the TEC was found to decrease (2.5–1.4 × 10⁻⁵/K). The progressive increase in the content of either Se or Sb in As₂S₃ is anticipated to modify bond lengths and bond angles. The combined effect of these structural modifications would change the local structure of the glass forming a more rigid glass network thereby increasing the hardness and decreasing TEC.     

Structure and bonding in the mixed chalcogenide system As2SxSe3−x

⁷⁵As Nuclear Quadrupole Resonance (NQR) lineshape measurements for the amorphous mixed chalcogenide system As₂S_xSe_3?x are reported. The line-shapes are asymmetric and approximately 8 MHz in width (full width at half maximum). The peak resonance frequency is observed to increase approximately linearly with x. The NQR results indicate the presence of mixed As₂(S, Se)₃ pyramidal structural units and are thus not consistent with models that predict the occurrence of anion subsite segregation. NQR measurements performed on crystalline As₂SSe₂ lend support to the structural model proposed for the glasses.     

Effect of hydrostatic pressure on the elastic moduli of As2S3 and As2Se3 glasses at 195 and 296 K

Velocities of 30 MHz longitudinal and shear ultrasonic waves have been measured in As₂S₃ and As₂Se₃ glasses as a function of hydrostatic pressure up to 1.5 kbar at 195 K and 3 kbar at 296 K. The elastic stiffness moduli are found to have relatively large, positive, pressure dependences which are about the same at both temperatures for both glasses. This behavior is attributed to the weakness of bonding between layers comprised of AsS₃ and AsS₃ pyramids.Inspection of data for a variety of glasses reveals a correlation between the value of C_L/3C_T and whether the elastic moduli are increased or decreased by pressure. (C_L is the longitudinal modulus and C_T the shear modulus.)Using the pressure dependences of the elastic moduli obtained in the present work, it is found that volume change is responsible for most of the temperature dependences of the moduli. In addition elastic gammas are obtained which are consistent with thermal Grüneisen gammas at 12 K. The pressure dependence of the volume of As₂S₃ glass at 296 K is calculated using the present results in the Murnagham equation. Agreement with volumetric data of Weir is obtained.     

The kinetics of photodissolution of Ag in amorphous As2S3 films

A new technique, measurement of the electrical resistance change of the Ag layer, is developed to study the kinetics of photodissolution of Ag in amorphous As₂S₃. It is shown that the photodissolution rate is proportional to the light intensity absorbed in the As₂S₃ at the As₂S₃Ag interface, but photoelectrons ejected from the Ag into the As₂S₃ also contribute. The process is shown to be two-stage. Firstly a critical “radiation damage” dose must be accumulated in the As₂S₃. Secondly, the Ag atom is photon-assisted across the As₂S₃Ag interface activation barrier.     

A square-wave voltammetric study on the diffusivities of polyvalent elements in CaO/BaO/Al2O3/SiO2 glass melts

Diffusion coefficients of various polyvalent ions (Sn²⁺, As³⁺, As⁵⁺, Sb³⁺, Sb⁵⁺, Cr³⁺, Ti⁴⁺, V⁴⁺, V⁵⁺ and Fe³⁺) were measured in melts with the basic compositions of 10CaO·10 BaO·10Al₂O₃·70SiO₂ and 10CaO·10BaO·15Al₂O₃·65SiO₂ by means of square-wave voltammetry. At temperatures in the range of 1300-1600 °C, linear correlations between logD and 1/T were observed. At 1400 °C, the diffusion coefficients obtained are compared with those obtained from other glass melt compositions.     

Bulk and impurity infrared absorption in 0.5 As2Se30.5 GeSe2 glass

A study of infrared absorption in the 250–4000 cm^?1 region has been carried out for 0.5 As₂Se₃0.5 GeSe₂ glasses quantitatively doped with oxide impurity. The frequencies of the intrinsic 2- and 3-phonon absorption bands at 490 and 690 cm^?1 correspond well to those predicted from combinations of the high frequency bands in the first order IR and Raman spectra of As₂Se₃ and GeSe₂ glasses.Glasses doped with As₂O₃ exhibit the same oxide impurity absorptionbands as those doped with GeO₂. Unlike As₂Se₃ glass, at impurity concentrations up to 1000 ppm As₂O₃, 0.5 As₂Se₃0.5 GeSe₂ glass exhibits only one major oxide impurity species, characterized by absorption bands at 780 and 1260 cm^?1 and due to oxygen bonded to network Ge. The observation of a much weaker network AsO vibration band at 670 cm^?1 confirms that oxygen bonds preferentially to Ge in this glass. The same minor oxide species appears to determine excess IR absorption at the CO₂ laser wavelength of 10.6 μm in both As₂Se₃ and 0.5 As₂Se₃ 0.5 GeSe₂ glasses. The frequencies and intensities of absorption bands due to hydrogen impurities are also quite comparable for these two materials.     

Local structure and vibrational spectra of vAs2O3

We discuss the atomic displacements of the optically active vibrational modes of vitreous (v-)As₂O₃ through comparisons of the infrared (ir) and Raman response with the corresponding spectra of the two crystalline polymorphs, claudetite, a layer crystal similar to orpiment, and arsenolite, a molecular crystal based on the As₄O₆ molecule. We conclude from these comparisons that the structure of the glass is composed of $\text{AsO}{}_{\mathrm{<mtext>3</mtext><mtext>2</mtext>}}$ pyramidal units that are corner connected to form a continuous random network. The character of the strong ir and polarized Raman modes in the vitreous form, suggests that the interconnection of these pyramidal units cannot be described by a random distribution of dihedral angles, but rather has peaks at angles characteristic of the different ordering in two-dimensional macromolecular layer basis of claudetite, and the As₄O₆ molecule. The comparisons are extended to v-As₂S₃ and vAs₂Se₃ where we conclude the dihedral angle distributions characteristic of an As₄O₆-like local geometry are less prevalent.     

X-ray photoelectron spectroscopic studies on Se/As2S3 and Sb/As2S3 nanomultilayered film

Photoinduced diffusion in Se/As₂S₃ and Sb/As₂S₃ nanomultilayered thin films are studied by X-ray photoelectron spectroscopy (XPS). The XPS measurements show the atomic movements during photoinduced diffusion in Se/As₂S₃ and Sb/As₂S₃ nanomultilayered film. The analysis of experimental data describes the nature of light induced changes in different structural units.     

Plasma etching of As2S3 films for optical waveguides

Chalcogenide glasses are good candidate materials for ultra-fast non-linear optic devices. In this work, we present the photolithographic process and the plasma etching of arsenic tri-sulphide (As₂S₃) film. The films were deposited on thermally oxidized silicon substrates by ultra-fast pulsed laser deposition. To protect As₂S₃ film from photo-resist developer, thin resist layer ∼100-200 nm was remained on the UV exposed area by controlling resist development time. After removing the protective layer in oxygen plasma, As₂S₃ waveguides were patterned in inductively coupled plasma reactive ion etching (ICP-RIE) system using CF₄-O₂ gas mixture. We investigated the etch rate and the etch selectivity to photo-resist of As₂S₃ as a function of bias power, induction power, operating pressure, and gas flow rate ratio of CF₄ and O₂. The film is mainly etched by the chemical reaction with fluorine radicals. The content of oxygen in the plasma determines the etched sidewall profiles and nearly vertical profile was obtained at high oxygen content plasma.     

Stimulated interdiffusion and optical recording in Sb/As2S3 nanomultilayers

The role of the compositional modulation at nano-scale dimensions (2–10 nm) in the enhancement of optical recording parameters in nanomultilayers, which contain Sb as active, optical absorbing and diffusing layers and As₂S₃ as barrier (matrix) layers was investigated. Comparison was made with single homogeneous layers made of ternary (As₂S3)_xSb_1−x glasses and co-deposited from Sb and As₂S₃. It was shown that essential increase of the recording efficiency, sensitivity of the bleaching process, broadening of its spectral range occurs due to the stimulated interdiffusion of adjacent components in Sb/As₂S₃ nanomultilayers with optimized Sb layer thickness.     

Thermo-optic properties of B2O3 doped Li2O-Al2O3-SiO2 glass-ceramics

Reduction in the temperature coefficient of the optical path length, dS/dT of Li₂O-Al₂O₃-SiO₂ glass-ceramics with near-zero thermal expansion coefficient was attempted using control of the temperature coefficient of electronic polarizability, ?, and the thermal expansion coefficient, α. The dS/dT value of 2.6 mol% B₂O₃-doped glass-ceramic was 12.5  × 10⁻⁶/°C, which was 0.9 ×  10⁻⁶/°C smaller than that of B₂O₃-free glass-ceramic. On the other hand, reduction in dS/dT through B₂O₃ doping was not confirmed in precursor glasses. Results showed that reduction in dS/dT of the glass-ceramic through B₂O₃ doping is caused by the reduction in ?. The reduction in ? from B₂O₃ doping was probably attributable to numerical reduction in non-bridging oxide ions with larger ? value by the concentration of boron ions in the residual glass phase. In addition, application of hydrostatic pressure during crystallization was effective to inhibit precipitation of β-spodumene solid solution, which thereby decreases dS/dT. The dS/dT value of B₂O₃-doped glass-ceramic crystallized under 196 MPa was 11.7 ×  10⁻⁶/°C. That value was slightly larger than that of silica glass. The α value of this glass-ceramic was smaller than that of silica glass.     

Structural changes during the crystallization of the Bi4Ge3O12 glasses

Bismuth-germanate glass ceramics with the composition 40% Bi₂O₃-60% GeO₂ (in molar percents) were prepared through controlled crystallization of melt-quenched glass. The Raman and FTIR spectra recorded in the as-made glasses show broad bands at 240, 400, 780 cm^− 1 and 400, 745 cm^− 1 have been assigned Ge-O bonds which appear right after preparation. X-ray diffraction has shown that the as-made glasses are amorphous, but after annealing above the crystallization temperature at 558 °C, BGO nano-crystallites with a size of about 50 nm precipitate in the glass matrix. The Raman and FTIR spectra reveal sharp peaks associated to the “internal” and “external vibrations” of GeO₄ tetrahedral groups inside the BGO nano-crystallites. In the glass ceramic sample the transparency region is shifted at longer wavelengths compared to as-made glass, due to the Rayleigh scattering on the BGO nano-crystallites.     

Ac conductivity of Ag-doped bulk,glassy As2S3

Measurements of the electrical conductivity of Ag-doped bulk As₂S₃ glasses have been made as functions of temperature, pressure, frequency and Ag doping level. A Debye-like loss peak was observed near 10⁴ Hz. The frequency of the loss peak is dependent on temperature, pressure and doping level, but these dependences are different from those of the dc conductivity. The ac loss is attributed to the Maxwell-Wagner losses characteristic of inhomogeneous materials. The materials are presumed to be inhomogeneous mixtures of As₂S₃ and Ag₂S. We have also searched unsuccessfully for ac conductance in several bulk chalcogenide glasses.     

Durability of an As2S3 chalcogenide glass: Optical properties and dissolution kinetics

The durability of a As₂S₃ chalcogenide glass composition was studied in de-ionized water at different temperatures (60-90 °C) for different periods of time, up to 120 days. The evolutions of the chemical composition and the pH of the solutions as well as the optical transmission of bulk samples, in the 2-10 μm region, were measured as a function of corrosion time. Atomic force microscopy and optical microscopy were used to investigate the roughness of corroded surfaces and the evolution of surface defects. The water corrosion of As₂S₃ glass was found to follow a congruent dissolution mechanism, a possible glass-water reaction mechanism was proposed. The optical transmission of the glass was found to be affected by the corrosion. The optical loss increased from 4 to 21% with corrosion time, this variation was attributed to the texturation of the surface by the reaction of corrosion. Moreover, the experimental results show that high temperature value enhances the corrosion reaction: an activation energy of 103 ± 2 kJ/mol was computed from experimental measurements.     

Magnetic behaviour of 20Fe2O380[3B2O3(1−χ)PbOχAs2O3] glasses

The results of magnetic measurements performed on 20Fe₂O₃80[3B₂O₃(1?χ)PbOχAs₂O₃] glasses, in the temperature range 4.2 to 300 K are reported. By decreasing the temperature a downward curvature of reciprocal susceptibility is observed for T<50 K. The composition dependence of the paramagnetic Curie temperatures and Curie constants is discussed.