Yb3+: Sr3Gd(BO3)3激光晶体的生长和光谱特性

采用提拉法(Czochralski)生长出了掺Yb3+的Sr3Gd(BO3)3晶体,晶体尺寸达到:25 mm×30 mm.测量了Yb3+: Sr3Gd(BO3)3晶体的吸收谱、荧光谱以及荧光寿命.Yb3+: Sr3Gd(BO3)3晶体在975 nm有一半峰宽为7 nm的强吸收峰,π谱的吸收跃迁截面σa=7.28×10-21 cm2,在1040 nm的发射跃迁截面σe=1.43×10-21 cm2.辐射寿命为1.46 ms, Yb3+浓度为13 at;时的荧光寿命f=2.14 ms,Yb3+浓度为0.5 at;时的荧光寿命f=1.21 ms.     

Er∶LaAl3(BO3)4晶体的生长和光谱性质研究

采用助熔剂法生长了Er: LaAl3(BO3)4晶体.LaAl3(BO3)4晶体属正交晶系,晶胞参数a=0.93586(4) nm,b=0.79904(3) nm,c=0.43626 (6) nm,V=0.34595 nm3.测量了晶体在室温的吸收光谱和荧光光谱.该晶体吸收光谱能级丰富;在1533 nm波长处有较强的荧光光谱,对应于4I13/2→4I15/2的能级跃迁;晶体的荧光寿命为2.72ms.研究了晶体的热学性质,室温时的比热容大约为0.595 J/g·℃.     

GdAl3（BO3）4及其Yb^3＋激活激光晶体的研究

采用顶部籽晶法从K2Mo3O10-B2O3助熔剂体系中生长出尺寸达到20 mm的GdAl3(BO3)4(简称GAB)和Yb3 激活的晶体.测试了GAB晶体的<100>和(001)轴向热膨胀系数,确定了透光波长范围,计算了有效倍频系数和相位匹配角随波长的变化,结果表明GAB晶体在整个透光范围内均可实现相位匹配.测定了Yb3 :GAB晶体在室温下的偏振吸收和荧光光谱,进行了光谱计算,测试了晶体的激光性能,在1046 nm处实现了2.1 W激光输出,斜率效率达到58%.     

Nd3+∶NaGd(MoO4)2晶体的生长及XRD-Rietveld结构精修

使用Cz提拉法生长了Nd3+∶NaGd(MoO4)2晶体,利用电感耦合等离子体光谱仪(ICP-AES)测试了晶体中Nd3+的浓度为1.98×1020 cm3,计算了分凝系数为0.84.通过XRD测定了Nd3+∶NaGd(MoO4)2(x=0.01)的晶体的结构,计算晶胞参数及晶胞体积,并进行Rietveld精修.结果表明:Rietveld拟合分析结果具有很好的一致性,NaGd(MoO4)2为四方晶系,空间群同为I41/a(88),a=b=0.5243 nm,c=1.1480 nm,V=0.3145 nm3,z=4,ρcalc=5.260,具有MoO4四面体及GdO8多面体结构,Na和Gd原子位于各自的晶体学位置,Mo-O键长主要在0.1712(2) ～0.1856(3) nm之间变化,Gd-O键长主要在0.2328(3)～0.2513(4) nm之间变化.     

Nd3+∶Gd0.2Y0.8Al3(BO3)4激光晶体的研究

测定了Nd3+∶Gd 0.2Y0.8Al3(BO3)4-K2MO3O10-B2O3生长体系的生长温度曲线,生长出尺寸达32mm的Nd3+∶Gd0.2Y0.8Al3(BO3)4激光晶体,并从中切割出尺寸为4mm×5mm×6mm的优质激光器件,采用钛宝石模拟LD泵浦,在1.06μm处得到48mW的激光输出,激光阈值17mW,光-光转换效率为20%.     

Er~(3 ),Yb~(3 )∶YAl_3(BO_3)_4晶体的光谱性质研究

采用助熔剂法生长了Er3 ,Yb3 共掺的YAl3 (BO3 ) 4 晶体 ,测量了晶体的室温吸收谱。由此吸收谱 ,根据Judd Ofelt理论计算了Er3 在Er3 ,Yb3 ∶YAl3 (BO3 ) 4 晶体中的强度参数、自发辐射几率、积分发射截面等参数。强度参数为Ω2 =2 .4 4× 10 -2 0 cm2 、Ω4=2 .0 0× 10 -2 0 cm2 、Ω6=6 .10× 10 -2 0 cm2 。研究了晶体的荧光特性 ,并在 976nm激光泵浦下得到了上转换绿色荧光。     

Er3+,Yb3+:YAl3(BO3)4晶体的光谱性质研究

采用助熔剂法生长了Er3+,Yb3+共掺的YAl3(BO3)4晶体,测量了晶体的室温吸收谱.由此吸收谱,根据JuddOfelt理论计算了Er3+在Er3+,Yb3+:YAl3(BO3)4晶体中的强度参数、自发辐射几率、积分发射截面等参数.强度参数为Ω2=2.44×10-20cm2、Ω4=2.00×10-20cm2、Ω6=6.10×10-20cm2.研究了晶体的荧光特性,并在976nm激光泵浦下得到了上转换绿色荧光.     

Ba3(VO4)2晶体的生长和拉曼性质的研究

采用提拉法生长了尺寸为φ22mm×50 mm的Ba3(VO4):晶体.室温下测试了Ba3(VO4)2晶体不同激发配置下自发拉曼散射光谱.另外测试了该晶体在532 nm、25 ps脉冲下的受激拉曼散射,观察到3阶斯托克斯线(625.5 am)和1阶反斯托克斯线(506.8 nm),并估算了Ba3(VO4)2晶体的稳态拉曼增益系数.     

高温超导衬底材料SrLaAlO4晶体的生长及特性

用提拉法生长了不开裂的高温超导衬底材料SrLaAlO4晶体,晶体尺寸为(25～30)mm×(50～60)mm.该晶体具有K2NiF4型结构,晶格常数为a=0.375nm,c=1.263nm.生长的晶体颜色随着生长时炉膛内氧气氛的含量的增加而逐渐加深.测量了晶体的室温下的介电常数及介电损耗分别为20及8×10-4.     

Ce:YVO4晶体的生长及其电荷迁移发光

为探索新型的白光LED荧光粉材料,采用提拉法生长了Ce2(CO3)3掺杂的Ce3+∶YVO4晶体,并对生长晶体的结构和光谱性能进行了表征。通过XRD测试,确定了由提拉法生长的Ce3+∶YVO4晶体的晶相没有发生变化。Ce3+∶YVO4晶体在450 nm处有一个较宽的发射带,在620 nm处有一个明显的发射峰。分析表明,在Ce3+掺杂的YVO4晶体中,铈离子主要以三价离子的形式存在,但在激发光照射下出现的620 nm发射表明有Ce4+存在,并且Ce4+与配位O2-形成了电荷迁移态(CTS)。     

助熔剂法生长非线性光学晶体Cd3Zn3B4O12及其性质研究

本文以PbO-0.25B2O3为助熔剂,利用顶部籽晶法获得了较大块的Cd3Zn3B4O12单晶.透过率测试结果显示该晶体的紫外截止波长位于310 nm处.利用Kurtz-Perry的方法对晶体的倍频效应进行了测试,结果显示该晶体的粉末倍频效应约为KDP的5倍,且能实现相位匹配.晶体的光损伤阈值约为840 MW(1064 nm,10 ns).该晶体的热分析结果显示Cd3Zn3B4O12晶体在熔点温度以上会产生分解,这也是阻碍高质量大块Cd3Zn3B4O12晶体生长最主要的因素.     

不同晶体结构Gd2(MoO4)3:Eu3+荧光粉的合成及其发光性能研究

采用溶胶凝胶-燃烧法,柠檬酸为络合剂合成出系列Gd₂(MoO₄)₃:Eu³⁺荧光粉.利用X射线衍射(XRD)、扫描电子显微镜(SEM)和荧光光谱对样品的结构、形貌和发光性能进行了研究.XRD分析表明:稀土离子与柠檬酸为1:0.5时,800℃热处理获得单斜结构的Gd₂(MoO₄)₃:Eu³⁺荧光粉.单斜结构的Gd₂(MoO₄)₃:Eu³⁺荧光粉到正交结构的Gd₂(MoO₄)₃:Eu³⁺荧光粉的转换可以通过改变稀土离子与柠檬酸摩尔比和热处理温度等合成条件实现.Gd₂(MoO₄)₃:Eu³⁺荧光粉的形貌受合成条件的影响.荧光光谱研究表明:Gd₂(MoO₄)₃:Eu³⁺荧光粉的主发射峰位于616 nm处来自于Eu³⁺的⁵D₀→⁷F₂电偶极跃迁.正交结构的Gd₂(MoO₄)₃:Eu³⁺荧光粉发射强度明显高于单斜结构的荧光粉.计算⁵D₀→⁷F₂与⁵D₀→⁷F₁跃迁发射的相对强度比值表明:正交结构的Gd₂(MoO₄)₃:Eu³⁺中Eu³⁺局域环境的对称性较高。     

Preparation and Properties of a Novel Nonlinear Optical Crystal: MnHg(SCN)4(H2O)2.2(C3H6CONCH3)

In this article, diaquatetrakis (thiocyanato) manganese(II) mercury(II)‐N‐methyl‐2‐pyrrolidone, MnHg(SCN)₄(H2O)₂.2(C₃H₆CONCH₃), (abbreviated as MMTWMP), a new organometallic nonlinear optical crystal material is reported. The structure, optical and thermal characterizations were determined by elemental analysis, infrared and Raman spectroscopy, X‐ray powder diffraction, thermogravimetric analysis, differential scanning calorimetry, special heat, SHG measurements and UV/Vis/NIR optical transmission spectra. It belongs to the tetragonal crystallographic system, with cell parameters: a = 12.1294, c = 8.2238Å, V = 1211.27ų. Single crystals with dimensions up to 8 × 7 × 5 mm³ have been obtained. The morphology of the crystals was indexed. The MMTWMP crystal exhibits good physicochemical stability at normal temperature and pressure. Its UV transparency cutoff is 360 nm, which is shifted to the violet by 13 nm, as compared with MnHg(SCN)₄ (MMTC); the optical transmission is 44.82% at 404 nm, which is by 17.46% higher than that of MMTC.     

Yb3+:YVO4晶体的生长及光谱性能研究

采用提拉法生长出光学质量优良的Yb3+:YVO4晶体,研究生长过程中工艺参数的控制.测得掺杂浓度为18.1;Yb3+:YVO4晶体中Yb3+离子的有效分凝系数Keff为0.96.测定了不同Yb3+离子掺杂浓度晶体的吸收光谱和荧光光谱,并分别计算了不同掺杂浓度下Yb3+:YVO4晶体的光谱参数.本文总结和解释了掺杂浓度影响其性能的规律,讨论了Yb3+:YVO4晶体作为激光晶体的优点.     

零声表面波频率温度系数方向的硅酸镓镧晶体生长

采用提拉法生长了高质量、大尺寸、结构完整的声表面波零温度系数切向LGS晶体.XRD图谱显示,生长的晶体为单一相LGS晶体,晶格常数为a=0.816274 nm,c=0.509253 nm,密度为5.7463 g/cm3.压电常数、介电常数、热膨胀性能等与传统方向生长的晶体一致.用此方向生长的LGS晶体制作声表面波频率温度性能优化的切片,只需要垂直生长方向进行切割,可以大大简化晶体的加工工艺、提高LGS晶体的利用率,节省材料成本.     

非线性光学晶体δ-LiZnPO4的制备、结构及光学性能

研究了LiF为助熔剂体系下的δ-LiZnPO4的结晶特性,通过自发结晶得到了尺寸为1~3 mm的透明块状δ-LiZnPO4和Li4Zn(PO4)2共晶体,通过PXRD衍射分析和元素分析确定了共晶体的相组成,并对从共晶体中分离出的δ-LiZnPO4晶体结构进行了分析.结果表明:δ-LiZnPO4晶体具有非中心对称结构,属于正交晶系,空间群为Pna21,晶格常数a=1.00085 nm,b=0.49390 nm,c=0.66545 nm,Z=4;δ-LiZnPO4是由PO4、ZnO4和LiO4四面体构筑成的具有类似ABW型分子筛结构的化合物.采用水热法制备了尺寸约为10 μm的纯相透明的δ-LiZnPO4晶体.粉末倍频测试表明,δ-LiZnPO4晶体倍频效应约为KDP的1.7倍,紫外截止边约为218 nm,是一种有潜在应用价值的紫外非线性光学晶体.     

白光LED用红色荧光粉SrMoO4: Eu3+,Gd3+的制备与表征

采用共沉淀法合成了红色荧光粉Sr1-x-yMoO4∶ Eu3+x,Gd3+y,分别对样品进行了X射线衍射(XRD)分析、扫面电镜(SEM)和荧光光谱(PL)的测定.结果表明:所合成的样品均为单一纯相四方晶系结构,添加Gd3+(为0.35mol时)使主衍射峰的位置右移了0.35°;SEM照片显示:SrMoO4∶ Eu3+和SrMoO4∶Eu3+,Gd3+颗粒尺寸分布相对均匀,为类方块状,颗粒大小约为1～3μm;Gd3+和Eu3+的共掺得到的SrMoO4∶ Eu3+,Gd3+在616 nm处主发射峰的发光强度约是SrMoO4∶Eu3+的2.09倍;当掺杂x=0.25 mol和y=0.35 mol时,在近紫外光(395 nm)激发下,SrMoO4Eu3+,Gd3+得到616 nm处红光发射极峰.     

Na3La2(BO3)3的晶体结构

以Na2CO3-H3BO3-NaF为助熔剂,使用顶部籽晶法生长出Na3La2(BO3)3透明单晶.测定了Na3La2(BO3)3的晶体结构,该晶体属正交晶系,空间群:mm2(No.38),晶胞参数为a＝0.51580(10)nm,b=1.1350(2)nm,c=0.73230(15)nm,α＝β＝γ＝90°,V＝0.42871(15)nm3,密度:.053g/cm3.晶体结构中的硼氧基团是平面的BO3基团,BO3基团相互独立,且与Na(1)O6、Na(2)O8、Na(3)O6和La(1)O9配位多面体连结形成三维网络骨架结构.讨论了Na3La2(BO3)3的晶体结构与倍频效应的关系.     

Zn,Co双掺杂近化学计量比LiNbO_3晶体的生长及性能

以K_2O为助熔剂,应用坩埚下降法生长出了Co~(2+) 初始浓度为0.5 mol;,以及ZnO分别为3 mol;与6 mol;的单掺与双掺杂SLN晶体(分别用SLN0, SLN3, SLN6表示).测定了晶体上下部位的吸收与发射光谱.在晶体的吸收光谱中均可观察到520 nm,549 nm,612 nm,1447 nm四个吸收峰,表明Co~(2+)处于晶体的八面体场中.ZnO的掺入明显地改变了吸收峰的相对强度.在520 nm光的激发下,观察到776 nm的荧光发射,其荧光强度的相对强弱也与ZnO的掺杂量有明显的联系.从吸收边带估算出SLN0, SLN3, SLN6晶体中Li2O的含量分别为49.06 mol;,49.28 mol;, 49.10 mol;.ZnO的掺杂量对Co~(2+)在铌酸锂晶体中的浓度分布有很大的影响作用,当ZnO的掺入量为3 mol;时,明显地抑制了Co~(2+)在LiNbO_3晶体中的掺入,当ZnO掺杂量达到6 mol;时,抑制作用减弱.本文从Zn~(2+)在LiNbO_3中随浓度变化的分凝情况以及对Co~(2+)的排斥作用解释了Co~(2+)在晶体中的分布特性以及光谱的变化情况.