Composition and structure of acid leached LiMn2−yTiyO4 (0.2≤y≤1.5) spinels

Lithium manganese titanium spinels, LiMn_2−yTi_yO₄, (0.2≤y≤1.5) have been synthesized by solid-state reaction between TiO₂ (anatase), Li₂CO₃ and MnCO₃. Li⁺ was leached from the powdered reaction products by treatment in excess of 0.2 N HCl at 85 °C for 6 h, under reflux. The elemental composition of the acidic solution and solid residues of leaching has been determined by complexometric titration, atomic absorption spectroscopy and X-ray fluorescence analysis. Powder X-ray diffraction was used for structural characterization of the crystalline fraction of the solid residues. It has been found that the amount of Li⁺ leached from LiMn_2−yTi_yO₄ decreases monotonically with increasing y in the interval 0.2≤y≤1.0 and abruptly drops to negligibly small values for y>1.0. The content of Mn and Li in the liquid phase and of Mn and Ti in the solid (amorphous plus crystalline) residue, were related to the composition and cation distribution in the pristine compounds. A new formal chemical equation describing the process of leaching and a mechanism of the structural transformation undergone by the initial solids as a result of Li⁺ removal has been proposed.     

Structure and phase composition of nanocrystalline Ce1−xLuxO2−y

The microstructure and phase stability of nanocrystalline mixed oxide Lu_xCe_1−xO_2−y (x=0-1) are described. Nano-sized (3-4 nm) oxide particles were prepared by the reverse microemulsion method. Morphological and structural changes upon heat treatment in an oxidizing atmosphere were studied by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman and Yb³⁺ emission spectroscopy, the latter ion being present as an impurity in the Lu₂O₃ starting material. Up to 950 °C, the samples were single phase, with structure changing smoothly with Lu content from fluorite type (F) to bixbyite type (C). For the samples heated at 1100 °C phase separation into coexisting F- and C-type structures was observed for 0.35<x<0.7. It was also found that addition of Lu strongly hinders the crystallite growth of ceria during heat treatment at 800 and 950 °C.     

Mixed conductivity, structural and microstructural characterization of titania-doped yttria tetragonal zirconia polycrystalline/titania-doped yttria stabilized zirconia composite anode matrices

Taking advantage of the fact that TiO₂ additions to 8YSZ cause not only the formation of a titania-doped YSZ solid solution but also a titania-doped YTZP solid solution, composite materials based on both solutions were prepared by solid state reaction. In particular, additions of 15 mol% of TiO₂ give rise to composite materials constituted by 0.51 mol fraction titania-doped yttria tetragonal zirconia polycrystalline and 0.49 mol fraction titania-doped yttria stabilized zirconia (0.51TiYTZP/0.49TiYSZ). Furthermore, Y₂(Ti_1−yZr_y)₂O₇ pyrochlore is present as an impurity phase with y close to 1, according to FT-Raman results. Lower and higher additions of titania than that of 15 mol%, i.e., x=0, 5, 10, 20, 25 and 30 mol% were considered to study the evolution of 8YSZ phase as a function of the TiO₂ content. Furthermore, zirconium titanate phase (ZrTiO₄) is detected when the titania content is equal or higher than 20 mol% and this phase admits Y₂O₃ in solid solution according to FE-SEM-EDX.The 0.51TiYTZP/0.49TiYSZ duplex material was selected in this study to establish the mechanism of its electronic conduction under low oxygen partial pressures. In the pO₂ range from 0.21 to 10^−7.5 atm. the conductivity is predominantly ionic and constant over the range and its value is 0.01 S/cm. The ionic plus electronic conductivity is 0.02 S/cm at 1000 °C and 10^−12.3 atm. Furthermore, the onset of electronic conductivity under reducing conditions exhibits a −1/4 pO₂ dependence. Therefore, it is concluded that the n-type electronic conduction in the duplex material can be due to a small polaron-hopping between Ti³⁺ and Ti⁴⁺.     

High-pressure synthesis, crystal structure and magnetic properties of a new cuprate (Nd,Ce)2+xCaCu2O6+y

New phase (Nd,Ce)_2+xCaCu₂O_6+y was prepared at a high-pressure/high-temperature condition of 6 GPa and 1300°C. It had a nonstoichiometric composition close to Nd_2.16Ce_0.225CaCu₂O_6+y. According to X-ray diffraction pattern, the Nd_2.16Ce_0.225CaCu₂O_6+y phase has a tetragonal lattice with a = 3.845(1) Å, c = 19.349(5) Å. However, electron microscopic observations revealed a complicated shear structure for this phase. Magnetic susceptibility and magnetic hysteresis measurements were performed for the Nd_2.16Ce_0.225CaCu₂O_6+y sample and it was found that the phase undergoes a weak ferromagnetic transition at 150 K. Below ≈40 K, complicated magnetic behavior was observed suggesting the presence of second weak ferromagnetic transition near 40 K.     

Transmission electron microscopy study of Ruddlesden-Popper Can+1MnnO3n+1n=2 and 3 compounds

Two Ruddlesden-Popper compounds Ca_n+1Mn_nO_3n+1 with n=2 and 3 synthesized by a citrate gel technique have been studied by TEM. The structure of Ca₄Mn₃O₁₀ is consistent with the previously determined structure having the space group Pbca and a⁻ a⁻ c⁺/a⁻ a⁻ c⁺ tilt system. The presence of defects suggests the possible high-temperature phase transition from untilted I4/mmm to Pbca. The structure of Ca₃Mn₂O₇ was found to be different from the previously suggested I4/mmm symmetry. Ca₃Mn₂O₇ forms with an orthorhombic structure with either Cmcm or Cmc2₁ space group. A structural model for Cmc2₁ based on the tilting of almost-rigid octahedra with a⁺ c⁻ c⁻/a⁺ c⁻ c⁻ tilt system is proposed. The lamellar defects were shown to be twin variants of the Cmc2₁ structure with the (001)_t interfaces, which suggests the possible tilting phase transition from the ideal I4/mmm to Cmc2₁ following the maximal group-subgroup symmetry tree: I4/mmm→Fmmm→Bbmm(Cmcm)→Bb2₁m(Cmc2₁).     

High-temperature neutron diffraction study of the cation ordered perovskites TbBaMn2O5+x and TbBaMn2O5.5−y

The miscibility of TbBaMn₂O_5+x and TbBaMn₂O_5.5−y has been investigated at 100-600 °C using in situ powder neutron diffraction. No miscibility is observed, and the two phases remain oxygen stoichiometric (x,y=0) at 600 °C. Structure refinement results show that neither material undergoes a phase transition in this temperature range. TbBaMn₂O₅ is Mn²⁺/Mn³⁺ charge ordered and any charge melting transition is >600 °C. This symmetry-broken charge ordering is remarkably robust in comparison to that in other oxides.     

High dielectric constant PrYxOy sensing films electrolyte-insulator-semiconductor pH-sensor for the detection of urea

In this paper, we describe the structural and sensing properties of high-k PrY_xO_y sensing films deposited on Si substrates through reactive co-sputtering. Secondary ion mass spectrometry and atomic force microscopy were employed to analyze the compositional and morphological features of these films after annealing at various temperatures. The electrolyte-insulator-semiconductor (EIS) device incorporating a PrY_xO_y sensing membrane that had been annealed at 800 °C exhibited good sensing characteristics, including a high sensitivity (59.07 mV pH⁻¹ in solutions from pH 2 to 12), a low hysteresis voltage (2.4 mV in the pH loop 7 → 4 → 7 → 10 → 7), and a small drift rate (0.62 mV h⁻¹ in the buffer solution at pH 7). The PrY_xO_y EIS device also showed a high selective response towards H⁺. This improvement can be attributed to the small number of crystal defects and the large surface roughness. In addition, the enzymatic EIS-based urea biosensor incorporating a high-k PrY_xO_y sensing film annealed at 800 °C allowed the potentiometric analysis of urea, at concentrations ranging from 1 to 16 mM, with a sensitivity of 9.59 mV mM⁻¹.     

Structure and magnetic order in the series BixRE1−xFe0.5Mn0.5O3 (RE=La,Nd)

The influence of Bi³⁺ on the structural and magnetic properties of the rare-earth-containing perovskites REFe_0.5Mn_0.5O₃ (RE=La,Nd) was studied, and the limit of bismuth substitution was determined to be x≤0.5 in Bi_xRE_1−xFe_0.5Mn_0.5O_3+δ (RE=La,Nd) at ambient pressure. Crystal structures in both La and Nd series were determined to be GdFeO₃-type Pnma with the exception of the Bi_0.3La_0.7Fe_0.5Mn_0.5O₃ sample, which is monoclinic I2/a in the a⁻b⁻b⁻ tilt scheme. The samples undergo a transition to G-type antiferromagnetic order along with a weak ferromagnetic component, mixed with cluster-glass type behavior. The substitution of bismuth into the lattice results in a drop in T_N relative to the lanthanide end-members. Long range ordering temperatures T_N in the range 240-255 K were observed, with a significantly lower ordered magnetic moment in the case of lanthanum (M∼1.7-1.9 μ_B) than in the case of neodymium (M∼2.1 μ_B).     

Investigation of the quasi-ternary system LaMnO3-LaCoO3-“LaCuO3”—I: the series La(Mn0.5Co0.5)1−xCuxO3−δ

The La(Mn_0.5Co_0.5)_1−xCu_xO_3−δ series with x=0, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8 and 1 was synthesized by the Pechini method to obtain insight into the phase formation in the quasi-ternary LaMnO₃-LaCoO₃-“LaCuO₃” system caused by the instability of LaCuO₃ under ambient conditions. After sintering at 1100°C some remarkable results were obtained: LaMn_0.3Co_0.3Cu_0.4O_3−δ crystallized as a single phase in the orthorhombic perovskite structure typical of LaCuO₃. Among the synthesized compositions this compound showed the highest electrical conductivity in air at 800°C (155 S cm⁻¹) and also the highest thermal expansion coefficient (α_30−800°C=15.4×10⁻⁶ K⁻¹). The LaCuO_3−δ composition also crystallized as a single phase but in a monoclinic structure although previous investigations have shown that other phases are preferably formed after sintering at 1100°C. The electrical conductivity and thermal expansion coefficient were the lowest within the series of compositions, i.e. 9.4 S cm⁻¹ and 11.9×10⁻⁶ K⁻¹, respectively.     

Synthesis and phase transition of Li-Mn-O spinels with high Li/Mn ratio by thermo-decomposition of LiMnC2O4(Ac)

LiMnC₂O₄(Ac) precursor in which Li⁺ and Mn²⁺ were amalgamated in one molecule was prepared by solid-state reaction at room-temperature using manganese acetate, lithium hydroxide and oxalic acid as raw materials. By thermo-decomposition of LiMnC₂O₄(Ac) at various temperatures, a series of Li_1+y[Mn_2−xLi_x]_16dO₄ spinels were prepared with Li₂MnO₃ as impurities. The structure and phase transition of these spinels were investigated by XRD, TG/DTA, average oxidation state of Mn and cyclic voltammeric techniques. Results revealed that the Li-Mn-O spinels with high Li/Mn ratio were unstable at high temperature, and the phase transition was associated with the transfer of Li⁺ from octahedral 16c sites to 16d sites. With the sintering temperature increasing from 450 to 850 °C, the phase structure varied from lithiated-spinel Li₂Mn₂O₄ to Li₄Mn₅O₁₂-like to LiMn₂O₄-like and finally to rock-salt LiMnO₂-like. A way of determining x with average oxidation state of Mn and the content of Li₂MnO₃ was also demonstrated.     

Anomalous octahedral distortion and multiple phase transitions in the metal-ordered manganite YBaMn2O6

By means of powder X-ray diffraction, powder neutron diffraction and transmission electron microscopy (TEM), we determined the crystal structures of a metal-ordered manganite YBaMn₂O₆ which undergoes successive phase transitions. A high-temperature metallic phase (T_c1=520 K<T) crystallizes in a triclinic P1 with the following unit cell: Z=2, a=5.4948(15) Å, b=5.4920(14) Å, c=7.7174(4) Å, α=89.804(20)°, β=90.173(20)°, γ=91.160(4)°. The MnO₆ octahedral tilting is approximately written as a⁰b⁻c⁻, leading to a significant structural anisotropy within the ab plane. The structure for T_c2<T<T_c1 is a monoclinic P2 (Z=2, a=5.5181(4) Å, b=5.5142(4) Å, c=7.6443(3) Å, β=90.267(4)°) with an a⁻b⁻c⁻ tilting. The structural features suggest a d_x²−y² orbital ordering (OO). Below T_c2=480 K, crystallographically inequivalent two octahedra show distinct volume difference, due to the Mn³⁺/Mn⁴⁺ charge ordering. The TEM study furthermore revealed a unique d_3x²−r²/d_3y²−r² OO with a modified CE structure. It was found that the obtained crystal structures are strongly correlated to the unusual physical properties. In particular, the extremely high temperature at which charge degree of freedom freezes, T_c2, should be caused by the absence of the structural disorder and by heavily distorted MnO₆ octahedra.     

Phase equilibria of the Ba-Sm-Y-Cu-O system for coated conductor applications

The complex phase relationships near the BaO-poor region of the quaternary Ba-Sm-Y-Cu-O oxide system prepared in pure air (O₂p=22 kPa, 950 °C) and in 0.1% O₂ (O₂p=100 Pa, 810 °C) have been determined. This investigation also included the subsolidus compatibilities in ten subsystems (Ba-Sm-Y-O, Ba-Sm-Cu-O, Ba-Y-Cu-O, Sm-Y-Cu-O, Ba-Sm-O, Ba-Y-O, Ba-Cu-O, Sm-Y-O, Sm-Cu-O, and Y-Cu-O), and the homogeneity range of five solid solutions (Ba(Sm_xY_2−x)CuO₅, (Sm,Y)₂O₃, (Sm,Y)₂CuO₄, (Y,Sm)₂Cu₂O₅, and Ba(Sm,Y)₂O₄). The single phase range of the superconductor solid solution, (Ba_2−xSm_x)(Sm_1−yY_y)Cu₃O_6+z, and the phase compatibilities in its vicinity, which are particularly important for processing, are described in detail. The phase equilibrium data of the Ba-Sm-Y-Cu-O system will enable the improvement of the intrinsic superconducting properties of second-generation wires, and facilitate the flux-pinning process.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

Systematic investigation on new SrCo1−yNbyO3−δ ceramic membranes with high oxygen semi-permeability

SrCo_1−yNb_yO_3−δ (y = 0.025–0.4) were synthesized for oxygen separation application. The crystal structure, phase stability, oxygen nonstoichiometry, electrical conductivity, and oxygen permeability of the oxides were systematically investigated. Cubic perovskite, with enhanced phase stability at higher Nb concentration, was obtained at y = 0.025–0.2. However, the further increase in niobium concentration led to the formation of impurity phase. The niobium doping concentration also had a significant effect on electrical conductivity and oxygen permeability of the membranes. SrCo_0.9Nb_0.1O_3−δ exhibited the highest electrical conductivity and oxygen permeability among the others. It reached a permeation flux of ∼2.80 × 10⁻⁶ mol cm⁻² s⁻¹ at 900 °C for a 1.0-mm membrane under an air/helium oxygen gradient. The further investigation demonstrated the oxygen permeation process was mainly rate-limited by the oxygen bulk diffusion process.     

Low temperature synthesis of Mn3O4 polyhedral nanocrystals and magnetic study

Manganese oxide (hausmannite) polyhedral nanocrystals were prepared by a microwave-assisted solution-based method using Mn(CH₃COO)₂ and (CH₂)₆N₄ at 80 °C. The as-prepared Mn₃O₄ nanocrystals were characterized by means of X-ray diffraction, field-emission transmission electron microscopy, field-emission scanning electron microscopy and Raman spectrum. Mn₃O₄ polyhedral nanocrystals prepared by microwave heating at 80 °C for 60 min were of cubic and rhombohedral shapes with the edge lengths in the range of 15-40 nm. Mn₃O₄ nanocrystals grew following the Ostwald ripening mechanism with increasing reaction time. High-resolution transmission electron microscopy and selected area electron diffraction confirm that the as-obtained polyhedral nanocrystals were single-crystalline. The magnetic behavior of Mn₃O₄ nanocrystals was studied. Mn₃O₄ nanocrystals show an obvious ferromagnetic behavior at low temperatures. The magnetic behavior of Mn₃O₄ nanocrystals was sensitive to crystal size. Ferromagnetic onset temperatures (T_c) of samples 1 and 3 are 40.6 and 41.1 K, respectively, lower than that observed for bulk Mn₃O₄ (42 K).     

High-temperature X-ray diffraction study of crystallization and phase segregation on spinel-type lithium manganese oxides

To study crystallization process of spinel-type Li_1+xMn_2−xO₄, in-situ high-temperature X-ray diffraction technique (HT-XRD) was utilized for the mixture consisting of Li₂CO₃ and Mn₂O₃ as starting material in the temperature range of 25-700 °C. In-situ HT-XRD analysis directly revealed that crystallization process of Li_1+xMn_2−xO₄ was significantly affected by the difference in the Li/Mn molar ratio in the precursor. Single phase of stoichiometric LiMn₂O₄ formed at 700 °C. The formation of single phase of spinel was achieved at the lower temperature than the stoichiometric sample as Li/Mn molar ratio in the precursor increased. Lattice parameter of the stoichiometric LiMn₂O₄ at 25 °C was 8.24 Å and expanded to 8.31 Å at 700 °C, which corresponds to the approximately 3% expansion in the unit cell volume. From the slope of the lattice parameter change as a function of temperatures, linear thermal expansion coefficient of the stoichiometric LiMn₂O₄ was calculated to be 1.2×10⁻⁵ °C⁻¹ in this temperature range. When the Li/Mn molar ratio in Li_1+xMn_2−xO₄ increased (x > 0.1), the spinel phase segregated into the Li_1+yMn_2−yO₄ (x > y) and Li₂MnO₃ during heating, which involved the oxygen loss from the materials. During the cooling process from 700 °C, and the segregated phase merged into Li_1+xMn_2−xO₄ with oxygen incorporation. Such trend directly observed by in-situ HT-XRD was supported by thermal gravimetric analysis as reversible weight (oxygen) loss/gain at higher temperature (500-700 °C).     

Hexaferrites and phase relations in the iron-rich part of the system Sr-La-Co-Fe-O

The iron rich part of the system was examined in the temperature range of 1200-1380 °C in air, with focus on the solid solutions of M-type hexaferrites. Samples of suitable compositions were studied by electronprobe microanalysis (EPMA). Substituted Sr-hexaferrites in the system Sr-La-Co-Fe-O do not follow the 1:1 substitution mechanism of La/Co in M-type ferrites. Due to the presence and limited Co²⁺-incorporation Fe³⁺-ions are reduced to Fe²⁺ within the crystal lattice to obtain charge balance. In all examined M-type ferrites divalent iron is formed, even at 1200 °C. The substitution principle Sr²⁺+Fe³⁺↔La³⁺+(Fe²⁺, Co²⁺) yields to the general substitution formula for the M-type hexaferrite Sr²⁺_1-xLa³⁺_xFe²⁺_x-yCo²⁺_yFe³⁺_12-xO¹⁹ (0≤x≤1 and 0≤y≤x). In addition Sr/La-perovskite_SS (_SS=solid solution), Co/Fe-spinel_SS, hematite and magnetite are formed. Sr-hexaferrite exhibits at 1200 °C a limited solid solution with small amounts of Fe²⁺ (SrFe₁₂O₁₉↔Sr_0.3La_0.7Co_0.5Fe²⁺_0.2Fe_11.3O₁₉). At 1300 and 1380 °C a continuous solid solution series of the M-type hexaferrite is stable. SrFe₁₂O₁₉ and LaCo_0.4Fe²⁺_0.6Fe₁₁O₁₉ are the end members at 1300 °C. The maximum Fe²⁺O content is about 13 mol% in the M-type ferrite at 1380 °C (LaCo_0.1Fe²⁺_0.9Fe₁₁O₁₉).     

Structural and physical properties evolution of BaIr1−xMnxO3 solid solutions synthesized by high-pressure sintering

The BaIr_1−xMn_xO₃ (0.0≤x≤1.0) solid solutions were synthesized by using the solid-state chemical method and high pressure sintering in the pressure range 0-5 GPa. According to the pressure-composition “phase diagram” at 1000 °C, the 9M BaIr_1−xMn_xO₃ transforms to the 6M form at 5 GPa and x≤1/6. In the x range 0.5-1.0, it transforms to the 9R form in a large pressure range. For the 9M BaIrO₃, the Mn ions substitution for Ir ions enhances the semiconducting property, and reduces the weak ferromagnetism. When x is larger than 1/3, the 9M/9R BaIr_1−xMn_xO₃ behave spin-glass-like state at low temperature, with the glass transition temperature T_g about 60 K. For the 6M BaIrO₃, the Mn ions doping results in that it transforms to insulator and spin-glass-like magnetism from the initial paramagnetic metal.     

Temperature-dependent structural study of microporous CsAlSi5O12

CsAlSi₅O₁₂ crystals were synthesized at high temperature by slow cooling of a vanadium oxide flux. Single-crystal X-ray diffraction structure analysis and electron microprobe analyses yielded the microporous CAS zeolite framework structure of Cs_0.85Al_0.85Si_5.15O₁₂ composition. High-temperature single-crystal and powder X-ray diffraction studies were utilized to analyze anisotropic thermal expansion. Rietveld refined cell constants from powder diffraction data, measured in steps of 25 °C up to 700 °C, show a significant decrease in expansion above 500 °C. At 500 °C, a displacive, static disorder-dynamic disorder-type phase transition from the acentric low-temperature space group Ama2 to centrosymmetric Amam (Cmcm in standard setting) was found. Thermal expansion below the phase transition is governed by rigid-body TO₄ rotations accompanied by stretching of T-O-T angles. Above the phase transition at 500 °C all atoms, except one oxygen (O6), are fixed on mirror planes. Temperature-dependent polarized Raman single-crystal spectra between −270 and 300 °C and unpolarized spectra between room temperature and 1000 °C become increasingly less resolved with rising temperature confirming the disordered static-disordered dynamic type of the phase transition.     

Solvothermal Synthesis of Superfine Li1−xMn2O4−σ Powders

Superfine Li_1−xMn₂O_4−σ powders were successfully synthesized by the alcohol-thermal method using 0.01 mol of MnO₂, 0.01mol of LiOH·H₂O, and 0.06mol of NaOH as starting materials at 160-200°C. The products are characterized by XRD, TEM, ED, BET, and ICP. Results show that the Li_0.74Mn₂O_3.74 powder prepared at 200°C has an average size of 180 nm with BET surface areas of 16.44 m²/g. A possible formation mechanism is proposed. It was concluded that the alcohol acts not only as the solvent but also as the reducing agent in the synthesis of Li_1−xMn₂O_4−σ powders. The effects of reaction temperature and the contents of NaOH and LiOH on the formation of single phase Li_1−xMn₂O_4−σ were investigated.