Crystal field energy levels of the laser crystal Gd3Ga5O12: Nd

The crystal field energy levels of laser crystal Gd₃Ga₅O₁₂: Nd³⁺ are calculated using the diagonalization (of energy matrix) method. From the calculations, the 93 observed crystal field energy levels are explained reasonably and the root-mean-square (r.m.s.) deviation σ(≈25.6 cm⁻¹) and the scalar crystal-field strength parameter Nv (≈3847 cm⁻¹) are obtained. The results are discussed.     

Er3+/Yb3+共掺Gd3Sc2Ga3O12晶体的上转换发光

研究了提拉法生长的Er³⁺/Yb³⁺:Gd₃Sc₂Ga₃O₁₂和Er³⁺:Gd₃Sc₂Ga₃O₁₂晶体在室温下320—1700nm范围的吸收光谱和500—750nm范围内的上转换荧光谱,同时对其上转换荧光的可能发生机制、途径以及上转换过程可能对Er^{3+相似文献}   

Spectral properties of Nd-doped Sr3Ga2Ge4O14 crystal

Neodymium doped strontium gallogermanate crystals were grown successfully by the Bridgman technique. The linear thermal expansion coefficients for the c- and a-axes were measured as 5.8 × 10⁻⁶ °C⁻¹ and 6.5 × 10⁻⁶ °C⁻¹. Absorption spectra, and fluorescence spectra, as well as fluorescence decay curves of Nd³⁺-doped Sr₃Ga₂Ge₄O₁₄ crystal, have been recorded at room temperature and used to calculate the absorption and stimulated emission cross-sections. Based on the Judd-Ofelt theory, three intensity parameters were obtained. The luminescent quantum efficiency of the ⁴F_3/2 level was determined to be approximately 73.8% for this material. Compared with other Nd³⁺-doped laser crystals, Nd³⁺-doped Sr₃Ga₂Ge₄O₁₄ crystal displays special laser properties due to its disorder structure.     

Metal-like to insulator transition in Lu3Fe5O12

Polycrystalline Lu₃Fe₅O₁₂, prepared using the solid state reaction method, has Fe in the mixed valence state as inferred from the X-ray photoelectron spectroscopy. A spectral change in the impedance plot at 343 K is attributed to metal-like to insulator transition (MIT), which is analyzed in terms of localized and delocalized _eg$e_g$ electrons. The change in the slope at 343 K in the DC conductivity plot also proves the MIT. The dependence of Z^′${\mathrm{Z}}^{\prime }$ on temperature and Z^″${\mathrm{Z}}^{″}$ on frequency clearly substantiates the presence of localized electrons up to 343 K and delocalized electrons above 343 K.     

Conductivity and sintering property of LaNi1 − xFexO3 ceramics prepared by Pechini method

Preparation of LaNi_1 − xFe_xO₃, which is one of the candidate materials of solid oxide fuel cell cathode, current collecting layer and interconnect coating was examined with Pechini method and solid state reaction method. Single phase LaNi_1 − xFe_xO₃ with large Ni content has successfully been prepared by low temperature sintering as 750 °C with Pechini method, whereas large amount of raw materials has remained with solid state reaction method by sintering at the same temperature. It can be ascribed to more homogenous cation distribution in raw powder material prior to sintering with Pechini method. It has also been revealed that LaNi_1 − xFe_xO₃ with x lower than 0.3 is thermodynamically unstable in air above 1000 °C. LaNi_0.6Fe_0.4O₃ showed superior property as cathode material with high electrical conductivity, thermodynamic stability and appropriate sintering property.     

Adsorption of water on thin V2O3(0 0 0 1) films

V₂O₃(0 0 0 1) films have been grown epitaxially on Au(1 1 1) and W(1 1 0). Under typical UHV conditions these films are terminated by a layer of vanadyl groups as has been shown previously [A.-C. Dupuis, M. Abu Haija, B. Richter, H. Kuhlenbeck, H.-J. Freund, V₂O₃(0 0 0 1) on Au(1 1 1) and W(1 1 0): growth, termination and electronic structure, Surf. Sci. 539 (2003) 99]. Electron irradiation may remove the oxygen atoms of this layer. H₂O adsorption on the vanadyl terminated surface and on the reduced surface has been studied with thermal desorption spectroscopy (TDS), vibrational spectroscopy (IRAS) and electron spectroscopy (XPS) using light from the BESSY II electron storage ring in Berlin. It is shown that water molecules interact only weakly with the vanadyl terminated surface: water is adsorbed molecularly and desorbs below room temperature. On the reduced surface water partially dissociates and forms a layer of hydroxyl groups which may be detected on the surface up to T ∼ 600 K. Below ∼330 K also co-adsorbed molecular water is detected. The water dissociation products desorb as molecular water which means that they recombine before desorption. No sign of surface re-oxidation could be detected after desorption, indicating that the dissociation products desorb completely.     

Unified calculations of the optical and electron paramagnetic resonance spectral data for Ce ion in Y3Ga5O12 crystal

Seven crystal field energy levels (obtained from the optical spectra) and three g factors g_x, g_y and g_z (obtained from electron paramagnetic resonance (EPR) spectra) for Ce³⁺ ion in Y₃Ga₅O₁₂ crystal are calculated together by diagonalizing a complete energy matrix. The Hamiltonian of this energy matrix includes all the interactions for 4f¹ ion Ce³⁺ in rhombic crystal field and under an external magnetic field, and so the optical and EPR data can be studied in a unified way. The calculated crystal field energy levels are in better agreement with the experimental values than the calculated values in the previous paper, and the g factors (which have not been calculated previously) are explained reasonably. The results are discussed.     

Low temperature adsorption of oxygen on reduced V2O3(0 0 0 1) surfaces

Well ordered V₂O₃(0 0 0 1) films were prepared on Au(1 1 1) and W(1 1 0) substrates. These films are terminated by a layer of vanadyl groups under typical UHV conditions. Reduction by electron bombardment may remove the oxygen atoms of the vanadyl layer, leading to a surface terminated by vanadium atoms. The interaction of oxygen with the reduced V₂O₃(0 0 0 1) surface has been studied in the temperature range from 80 to 610 K. Thermal desorption spectroscopy (TDS), infrared reflection absorption spectroscopy (IRAS), high resolution electron energy loss spectroscopy (HREELS), X-ray photoelectron spectroscopy (XPS), and density functional theory (DFT) were used to study the adsorbed oxygen species. Low temperature adsorption of oxygen on reduced V₂O₃(0 0 0 1) occurs both dissociatively and molecularly. At 90 K a negatively charged molecular oxygen species is observed. Upon annealing the adsorbed oxygen species dissociates, re-oxidizing the reduced surface by the formation of vanadyl species. Density functional theory was employed to calculate the structure and the vibrational frequencies of the O₂ species on the surface. Using both cluster and periodic models, the surface species could be identified as η²-peroxo () lying flat on surface, bonded to the surface vanadium atoms. Although the O-O vibrational normal mode involves motions almost parallel to the surface, it can be detected by infrared spectroscopy because it is connected with a change of the dipole moment perpendicular to the surface.     

CO2 adsorption on Cr(1 1 0) and Cr2O3(0 0 0 1)/Cr(1 1 0)

We attempt to correlate qualitatively the surface structure with the chemical activity for a metal surface, Cr(1 1 0), and one of its surface oxides, Cr₂O₃(0 0 0 1)/Cr(1 1 0). The kinetics and dynamics of CO₂ adsorption have been studied by low energy electron diffraction (LEED), Aug er electron spectroscopy (AES), and thermal desorption spectroscopy (TDS), as well as adsorption probability measurements conducted for impact energies of E_i = 0.1-1.1 eV and adsorption temperatures of T_s = 92-135 K. The Cr(1 1 0) surface is characterized by a square shaped LEED pattern, contamination free Cr AES, and a single dominant TDS peak (binding energy E_d = 33.3 kJ/mol, first order pre-exponential 1 × 10¹³ s⁻¹). The oxide exhibits a hexagonal shaped LEED pattern, Cr AES with an additional O-line, and two TDS peaks (E_d = 39.5 and 30.5 kJ/mol). The initial adsorption probability, S₀, is independent of T_s for both systems and decreases exponentially from 0.69 to 0.22 for Cr(1 1 0) with increasing E_i, with S₀ smaller by ∼0.15 for the surface oxide. The coverage dependence of the adsorption probability, S(Θ), at low E_i is approx. independent of coverage (Kisliuk-shape) and increases initially at large E_i with coverage (adsorbate-assisted adsorption). CO₂ physisorbs on both systems and the adsorption is non-activated and precursor mediated. Monte Carlo simulations (MCS) have been used to parameterize the beam scattering data. The coverage dependence of E_d has been obtained by means of a Redhead analysis of the TDS curves.     

High power diode-pumped passively Q-switched and mode-locking Nd:GdVO4 laser at 912 nm

A high power diode-end-pumped passively Q-switched and mode-locking (QML) Nd:GdVO₄ laser at 912 nm was demonstrated for the first time, to the best of our knowledge. A Z-type laser cavity with Cr⁴⁺:YAG crystals as the intracavity saturable absorber were employed in the experiments. Influence of the initial transmission (T_U) of the saturable absorber on the QML laser performance was investigated. Using the T_U = 95% Cr⁴⁺:YAG, as much as an average output power of 2.0 W pulsed 912 nm laser was produced at an absorbed pump power of 25.0 W, then the repetition rates of the Q-switched envelope and the mode-locking pulse were ~ 224 kHz and ~ 160 MHz, respectively. Whereas the maximum output power was reduced to 1.3 W using the T_U = 90% Cr⁴⁺:YAG, we obtained a 100% modulation depth for the mode-locking pulses inside the Q-switched envelope.     

Growth of Al2O3 thin films on NiAl(1 0 0) by gas-phase oxidation and electro-oxidation

The growth and structures of aluminum oxides on NiAl(1 0 0) have been investigated by RHEED (reflection high energy electron diffraction), complemented by LEED (low energy electron diffraction), AES (Auger electron spectroscopy) and STM (scanning tunneling microscopy). Crystalline θ-Al₂O₃ phase grows through gas-phase oxidation on the NiAl(1 0 0) substrate with its a and b-axes parallel to [0 −1 0] and [0 0 1] direction of the substrate, respectively, forming a (2 × 1) unit cell. Whilst, three-dimensional nano-sized NiAl(1 0 0) protrusions and Al₂O₃, NiAl(0 1 1) clusters were found to co-exit at the surface, evidenced by extraordinary transmission spots superposed to the substrate reflection rods in the RHEED patterns. Particularly, the NiAl(0 1 1) clusters develop with their (0 1 1) plane parallel to the NiAl(1 0 0) surface, and [1 0 0] axis parallel to the [0 −1 1] direction of the substrate surface. STM observation combined with information from AES and TPD (temperature programmed desorption) suggest the formation of these 3D structures is closely associated with partial decomposition of the crystalline oxides during annealing. On the other hand, smoother (2 × 1) oxide islands with thickness close to a complete monolayer of θ-Al₂O₃ can be formed on NiAl(1 0 0) by electro-oxidation, in contrast with the large crystalline films formed by gas-oxidation.     

Multiplication of electronic excitations in nanophosphors Lu2O3:Eu and Lu2O3:Tb

Luminescence properties of Lu₂O₃:Eu³⁺ and Lu₂O₃:Tb³⁺ nanocrystalline powders with the particle size varying from 46 to 6 nm were studied under excitation by synchrotron radiation in the photon energy range (up to ∼22.5 eV) covering the region where the processes of multiplication of electronic excitation occur. It was found that the excitation spectra of Tb³⁺ emission from all Lu₂O₃:Tb³⁺ nanopowders have similar behavior, whereas the shape of the excitation spectra of Eu³⁺ emission from Lu₂O₃:Eu³⁺ nanopowders strongly depends on the particle size. The difference in the behavior of Lu₂O₃:Eu³⁺ and Lu₂O₃:Tb³⁺ nanophosphor systems was explained by different mechanisms of the energy transfer from the host to Eu³⁺ or Tb³⁺ ions (either the hole or electron recombination mechanism, respectively), which are differently influenced by losses of electronic excitations near the particle surface.     

The influence of Pr co-doping on the luminescent properties of Lu2O3:5 mol% Eu films

Uniform and crack free polycrystalline lutetium oxide (Lu₂O₃:(Eu,Pr)) films were fabricated by Pechini sol-gel method combined with the spin-coating technique. X-ray diffraction (XRD) and atomic force microscope (AFM) characterizations indicated that the obtained film was composed of polycrystalline cubic Lu₂O₃ phase with an average grain size around 30 nm. The photoluminescence(PL) spectra and decay performances of the Lu₂O₃:5 mol% Eu films co-doped by 0-0.5 mol% Pr³⁺ with different concentrations were characterized. It was found that the afterglow was reduced obviously due to the introduction of 0-0.5 mol% Pr³⁺ in the Lu₂O₃:5 mol% Eu films coupled by decrease in the emission intensity at 612 nm. The mechanism of afterglow diminishing was discussed based on the thermoluminescence measurements.     

Synthesis, characterization, and luminescent properties of Lu2O3:Eu phosphors

Eu-doped lutetia (Lu₂O₃:Eu) nano-phosphors were synthesized by the sol-gel combustion process from a mixed aqueous solution of europium and lutetium nitrates, using organic glycine as the fuel. Powder X-ray diffraction shows that cubic Lu₂O₃:Eu crystallites are directly obtained by the sol-gel combustion process without further calcination. Electron microscopy reveals that the as-prepared phosphors are agglomerated and have a fluffy, fine, and porous morphology, consisting of primary particle size of 8-10 nm. The excitation spectrum is characterized by three dominant bands centered at 395, 466, and 534 nm, respectively. Both the photoluminescent and radioluminescent spectra are very similar and exhibit intense emission peaks centered at 612 nm due to ⁵D₀→⁷F₂ transition of Eu³⁺ ions. The energy transfer from Lu₂O₃ host to Eu³⁺ activator is more efficient in the case of calcined phosphors than for the as-prepared phosphors due to their improved lattice perfection.     

High-throughput characterization of BixY3−xFe5O12 combinatorial thin films by magneto-optical imaging technique

Bi_xY_3−xFe₅O₁₂ thin films have been grown on GGG (Gd₃Ga₅O₁₂) (1 1 1) substrates by the combinatorial composition-spread techniques under substrate temperature (T_sub) ranging from 410 to 700 °C and O₂ pressure of 200 mTorr. In order to study the effect of substrates on the deposition of Bi_xY_3−xFe₅O₁₂ thin films, garnet substrates annealed at 1300 °C for 3 h were also used. Magneto-optical properties were characterized by our home-designed magneto-optical imaging system. From the maps of Faraday rotation angle θ_F, it was evident that the Faraday effect appears only when T_sub = 430-630 °C. θ_F reaches to the maximum value (∼6°/μm, λ = 632 nm) at 500 °C, and is proportional to the Bi contents. XRD and EPMA analyses showed that Bi ions are easier to substitute for Y sites and better crystallinity is obtained for annealed substrates than for commercial ones.     

Theoretical and experimental investigations of a diode-pumped high-power continuous-wave 912 nm Nd:GdVO4 laser operation at room temperature

Based on the rate equation of Nd³⁺-doped quasi-three-level lasers, a theoretical model of diode-end-pumped continuous-wave 912 nm Nd:GdVO₄ laser is presented. Lasing threshold and slope efficiency considering reabsorption effect are calculated and analyzed. It is found that the output performance of 912 nm laser operating at room temperature is influenced remarkably by the reabsorption loss and spatial distribution of the pump beam and laser beam. In experiments, the output power and average slope efficiency of 912 nm laser were investigated under different conditions. After optimization at the parameters of laser medium, working temperature and spatial distribution of the pump beam, up to 16.2 W continuous-wave 912 nm laser output was obtained at incident pump power of 67.0 W, with an average slope efficiency of 41.7%, to the best of our knowledge, this is the highest output power of diode-pumped 912 nm Nd:GdVO₄ laser by far.     

Structural, transport and electrochemical properties of LiNi1 − yCoyMn0.1O2 and Al, Mg and Cu-substituted LiNi0.65Co0.25Mn0.1O2 oxides

LiNi_{1 - y − z}Co_yMn_zO₂ (y = 0.25, 0.35, 0.5, 0.6; z = 0.1, 0.2), LiNi_0.63Cu_0.02Co_0.25Mn_0.1O₂, LiNi_0.65Co_0.25Mn_0.08Al_0.02O₂, LiNi_0.65Co_0.25Mn_0.08Mg_0.02O₂ and LiNi_0.65Co_0.25Mn_0.08Al_0.01Mg_0.01O₂ cathode materials were synthesized by a soft chemistry EDTA-based method. Structural and transport properties of pristine and delithiated materials (Li_xNi_0.65Co_0.25Mn_0.1O₂, Li_xNi_0.55Co_0.35Mn_0.1O₂ and LiNi_0.63Cu_0.02Co_0.25Mn_0.1O₂ oxides) are presented. In the considered group of oxides there is no correlation between electrical conductivity and the a parameter (M-M distance in the octahedra layers). The results of electrochemical performance of cathode materials are presented. The best stability during first 10 cycles was obtained for Li/Li_xNi_0.63Cu_0.02Co_0.25Mn_0.1O₂ cell due to enhanced kinetics of intercalation process.     

Gd3Ga5O12:Ag薄膜电致发光材料的制备及其发光性质

研究了Gd₃Ga₅O₁₂:Ag材料的制备及其发光性质.Gd₃Ga₅O₁₂:Ag材料通过固相反应法制得,采用X射线衍射法分 析了材料的结晶度及成分.用电子束蒸发将该材料制备成交流的薄膜电致发光器件,得到了 较好的蓝紫色发光,发光峰分别位于397和467nm.通过对材料的光致发光和激发光谱的研究 和比较,得出397和467nm分别来自于氧空位和Ag⁺的发光.     

Scanning tunneling microscopy study of growth of Pt nanoclusters on thin film Al2O3/NiAl(1 0 0)

The growth of Pt nanoclusters on thin film Al₂O₃ grown on NiAl(1 0 0) was studied by using scanning tunneling microscopy (STM). The samples were prepared by vapor depositing various amounts of Pt onto the Al₂O₃/NiAl(1 0 0) at different substrate temperatures in ultra high vacuum (UHV). The STM images show that sizeable Pt nanoclusters grow solely on crystalline Al₂O₃ surface. These Pt clusters appear to be randomly distributed and only a few form evident alignment patterns, contrasting with Co clusters that are highly aligned on the crystalline Al₂O₃. The size distributions of these Pt clusters are rather broader than those of the Co clusters on the same surface and the sizes are evidently smaller. With increasing coverage or deposition temperature, the number of larger clusters is enhanced, while the size of the majority number of the clusters remains around the same (0.4 nm as height and 2.25 nm as diameter), which differs drastically from the Pt clusters on γ-Al₂O₃/NiAl(1 1 0) observed earlier. These Pt cluster growth features are mostly attributed to smaller diffusion length and ease to form stable nucleus, arising from strong Pt-Pt and Pt-oxide interactions and the peculiar protrusion structures on the ordered Al₂O₃/NiAl(1 0 0). The thermal stability of Pt nanoclusters was also examined. The cluster density decreased monotonically with annealing temperature up to 1000 K at the expense of smaller clusters but coalescence is not observed.     

Magnetic properties of the Lu2Fe17−xMnx single crystals

Magnetic properties of the single-crystalline Lu₂Fe_17−xMn_x compounds, in which x=0, 0.5, and 2, with the Th₂Ni₁₇-type crystal structure are reported. The Lu₂Fe_17−xMn_x compounds with x=0 and 0.5 are ferromagnets at low temperatures and antiferromagnets at high temperatures. The compound with x=2 is always a ferromagnet. The easy-plane magnetic anisotropy in the Lu₂Fe_17−xMn_x ferromagnets drastically weakens with increase in Mn content up to x=2. The temperature dependence of the first magnetic anisotropy constant was obtained and compared with the single-ion model prediction.