Two localized CO₂ laser treatment methods for mitigation of UV damage growth in fused silica

Two methods:high-power,short-time,single-shot irradiation(Method A) and low-power,long-time,multi-shot irradiation(Method B) are investigated to mitigate the UV damage growth in fused silica by using a 10.6-μm CO2 laser.To verify the mitigation effect of the two methods,the laser induced damage thresholds(LIDTs) of the mitigated sites are tested with a 355-nm,6.4-ns Nd:YAG laser,and the light modulation of the mitigation sites are tested with a 351-nm continuous Nd:YLF laser.The mitigated damaged sites treated with the two methods have almost the same LIDTs,which can recover to the level of pristine material.Compared with Method A,Method B produces mitigated sites with low crater depth and weak light modulation.In addition,there is no raised rim or re-deposited debris formed around the crater edge for Method B.Theoretical calculation is utilized to evaluate the central temperature of the CO2 laser beam irradiated zone and the radius of the crater.It is indicated that the calculated results are consistent with the experimental results.     

激光钝化对熔石英修复后损伤性能影响的实验研究

采用10.6 μupm 的 CO₂激光, 对单次激光脉冲辐照修复熔石英存在的烧蚀采用大光斑钝化去除. 经过辐照修复的区域置于前表面测试初始损伤阈值, 结果表明调制造成的损伤得到了一定程度的抑制; 辐照区域置于后表面修复后 熔石英的初始损伤阈值超过了基底的初始损伤阈值. 实验观察到了应力分布外扩, 同时明显减弱. 对损伤增长的测试说明, 经过激光熔融辐照后的损伤点, 当应力释放以后, 损伤扩展初期表现出指数增长趋势, 后期随着辐照次数的增加, 损伤增长不再明显, 并且趋于恒定值.     

激光钝化对熔石英修复后损伤性能影响的实验研究

采用10.6 μupm 的 CO₂激光, 对单次激光脉冲辐照修复熔石英存在的烧蚀采用大光斑钝化去除. 经过辐照修复的区域置于前表面测试初始损伤阈值, 结果表明调制造成的损伤得到了一定程度的抑制; 辐照区域置于后表面修复后 熔石英的初始损伤阈值超过了基底的初始损伤阈值. 实验观察到了应力分布外扩, 同时明显减弱. 对损伤增长的测试说明, 经过激光熔融辐照后的损伤点, 当应力释放以后, 损伤扩展初期表现出指数增长趋势, 后期随着辐照次数的增加, 损伤增长不再明显, 并且趋于恒定值.     

Surface evolution and laser damage resistance of CO2 laser irradiated area of fused silica

A 10.6 μm CO₂ laser has been reported to effectively mitigate the laser damage growth of fused silica. Two zones of the laser irradiated area are defined in this work: the distorted zone and the laser affected zone. The parameters of the two zones are studied at different CO₂ laser beam sizes, irradiation times, and powers by microscopy, profilometry, and photoelastic method. The results show that the diameter of laser affected zone is almost completely determined by the laser beam size and the distorted zone is associated with the mitigation range of CO₂ laser beam. The diameter and depth of the distorted zone increase as the laser power and irradiation time increase. The depth grows exponentially depending on the irradiation time. The maximum residual stress discrepancy is located near the boundary of the laser affected zone. The laser damage resistance test results show that the distorted zone and the laser affected zone have a better damage resistance than the original substrate.     

ATR-FTIR spectroscopic studies on density changes of fused silica induced by localized CO2 laser treatment

The surface density changes of the central region of the sites treated by using the CO_2 laser-based non-evaporative damage mitigation for fused silica are investigated by attenuated total reflectance-Fourier transform infrared spectroscopy(ATR-FTIR).The ATR-FTIR peak shifts of the treated sites of fused silica are monitored to determine the changes of the corresponding density.For the quenching treated sites,the surface density is increased by(0.24±0.01)%compared with the initial density but the laser annealing by the exposure of a power ramp down after damage mitigation effectively suppresses the structural changes of treated sites,which could reduce the increase of the corresponding density to(0.08±0.01)%.The results provide sufficient evidence that the laser annealing by a power ramp down after damage mitigation has a positive effect on the control of the structural change induced by CO_2 laser-based damage mitigation.     

CO2激光扫描辐照修复熔石英表面损伤

采用振镜系统结合10.6 m的CO2激光,对熔石英表面损伤点进行辐照,成功地修复了直径500 m的大尺寸损伤点,损伤修复后表面无烧蚀残留,损伤内部完全愈合,无气泡和残余裂纹。和定点修复方式相比,这种修复具有修复尺度大、面形影响区域小、应力分布范围小的优势。80%扫描辐照修复的损伤点的初始损伤阈值恢复甚至超过了基底的初始损伤阈值。     

Irradiation effects of CO2 laser parameters on surface morphology of fused silica

To understand the surface morphology evolution of fused silica induced by 10.6-μm CO2 laser irradiation at different parameters,this paper reports that optical microscopy,profilometry,and hydrophilicity tests are utilized to characterize the surface structure and roughness of the laser irradiated area. The results show that three typical surface morphologies and two typical hydrophilicity test images are observed at different laser powers and pulse durations. The correlations between surface temperature and surface morphology as well as hydrophilicity behaviours are presented. The different hydrophilicity behaviours are related to surface structures of the laser-induced crater and thermal diffusion area. The thermal diffusion length monotonously increases with increasing laser power and pulse duration. The crater width is almost determined by the laser beam size. The crater depth is more sensitive to the laser power and pulse duration than the crater width.     

CO2激光对熔石英表面小尺寸损伤的修复

利用10.6 μm的CO2激光对不同直径的点状损伤和不同宽度的划痕进行了修复。经过波长351 nm的紫外激光考核发现,对于直径小于80 μm的点状损伤和对于宽度小于40 μm的划痕,随着损伤点尺寸和划痕宽度的增加,修复后阈值提高程度逐渐降低。划痕的宽度在达到40 μm以后修复效果非常微弱。修复过程中,由于作用时间较短及温度分布不均产生了热应力导致样片损伤以后产生径向裂痕,后续的紫外激光会使裂痕明显扩展。当样品被置于高温退火炉内退火3 h以后,应力导致开裂的现象得到了解决。     

CO2激光局域辐照对熔石英损伤特性的影响

研究了CO₂激光局域辐照对熔石英损伤特性的影响, 发现当辐照中心温度较低时(1139 K), 辐照对损伤阈值没有明显影响, 但辐照中心温度较高时(1638 K), 辐照对损伤阈值有明显的影响, 损伤阈值随距离辐照中心间距的增大而减小, 在残余应力产生光程差最大处附近, 损伤阈值降到最小, 随着与辐照中心间距的进一步增加, 损伤阈值略有上升. 对导致此现象的原因做了分析. 由于残余应力的存在, 在辐照中心发生再损伤产生的裂纹后, 裂纹先沿径向扩展, 在残余应力产生光程差最大处附近, 裂纹转而向切向扩展, 这可能与径向和环向张应力随半径的变化有关. 在采用热处理炉退火消除残余应力时, 必须注意元件的洁净处理, 否则退火会出现析晶现象, 对损伤阈值和透射率造成不良影响. 关键词： 2激光局域辐照')" href="#">CO₂激光局域辐照 熔石英 损伤特性     

CO2激光对熔石英表面小尺寸损伤的修复

 利用10.6 μm的CO₂激光对不同直径的点状损伤和不同宽度的划痕进行了修复。经过波长351 nm的紫外激光考核发现,对于直径小于80 μm的点状损伤和对于宽度小于40 μm的划痕,随着损伤点尺寸和划痕宽度的增加,修复后阈值提高程度逐渐降低。划痕的宽度在达到40 μm以后修复效果非常微弱。修复过程中,由于作用时间较短及温度分布不均产生了热应力导致样片损伤以后产生径向裂痕,后续的紫外激光会使裂痕明显扩展。当样品被置于高温退火炉内退火3 h以后,应力导致开裂的现象得到了解决。     

Mitigation of laser damage growth in fused silica by using a non-evaporative technique

A non-evaporative technique is used to mitigate damage sites with lateral sizes in a range from 50 μm to 400 μm and depths smaller than 100 μm.The influence of the pulse frequency of a CO 2 laser on the mitigation effect is studied.It is found that a more symmetrical and smooth mitigation crater can be obtained by increasing the laser pulse frequency form 0.1 to 20 kHz.Furthermore,the sizes of laser-affected and distorted zones decrease with the increase of the laser pulse frequency,leading to less degradation of the wave-front quality of the conditioned sample.The energy density of the CO 2 laser beam is introduced for selecting the mitigation parameters.The damage sites can be successfully mitigated by increasing the energy density in a ramped way.Finally,the laser-induced damage threshold(LIDT) of the mitigated site is tested using 355 nm laser beam with a small spot(0.23 mm 2) and a large spot(3.14 mm 2),separately.It is shown that the non-evaporative mitigation technique is a successful method to stop damage re-initiation since the average LIDTs of mitigated sites tested with small or large laser spots are higher than that of pristine material.     

熔石英紫外激光初始损伤形态分析

采取355 nm激光脉冲辐照熔石英样品,利用Nomarski微分干涉差显微镜、原子力显微镜和扫描电子显微镜观测手段对前后表面产生的损伤点进行了观察分析。对前后表面损伤形态做出详细的描述和分类,从理论上对每种损伤类型产生的条件与机理做出推测。实验结果表明：熔石英前表面存在小麻点群损伤和星状裂纹损伤两种损伤形态,横向尺寸分别为0.8～2.5和1.0～5.5 μm;后表面存在小麻点群损伤、壳状剥离损伤和火山口3种损伤形态,损伤横向尺寸分别为0.48～1.33,4～20和12～30 μm。实验证明了1 μm尺度损伤点的产生与再沉积层密切相关。     

熔石英紫外激光初始损伤形态分析

 采取355 nm激光脉冲辐照熔石英样品,利用Nomarski微分干涉差显微镜、原子力显微镜和扫描电子显微镜观测手段对前后表面产生的损伤点进行了观察分析。对前后表面损伤形态做出详细的描述和分类,从理论上对每种损伤类型产生的条件与机理做出推测。实验结果表明：熔石英前表面存在小麻点群损伤和星状裂纹损伤两种损伤形态,横向尺寸分别为0.8～2.5和1.0～5.5 μm;后表面存在小麻点群损伤、壳状剥离损伤和火山口3种损伤形态,损伤横向尺寸分别为0.48～1.33,4～20和12～30 μm。实验证明了1 μm尺度损伤点的产生与再沉积层密切相关。     

激光诱导熔石英表面损伤修复中的气泡形成和控制研究

基于熔石英材料在CO_2激光作用下的温度分布和结构参数变化的计算结果,对熔石英损伤修复中的气泡形成和控制进行了研究.针对损伤尺寸介于150—250μm之间的损伤点,提出了一种能够有效控制气泡形成的长时间低温预热修复方法.基于低温下熔石英材料结构弛豫时间常数较长的特点,该方法在不引起熔石英材料结构发生显著变化的同时,能够解吸附表面和裂纹处所附着的气体和杂质,可有效降低裂纹闭合过程中气泡形成的概率.实验结果表明,长时间低温预热修复方法的成功修复概率可达到98%.     

Influences of CO2 laser annealing on mechanical and laser-induced damage properties of ZrO2 thin films

Zirconium dioxide (ZrO₂) thin films were deposited on BK7 glass substrates by the electron beam evaporation method. A continuous wave CO₂ laser was used to anneal the ZrO₂ thin films to investigate whether beneficial changes could be produced. After annealing at different laser scanning speeds by CO₂ laser, weak absorption of the coatings was measured by the surface thermal lensing (STL) technique, and then laser-induced damage threshold (LIDT) was also determined. It was found that the weak absorption decreased first, while the laser scanning speed is below some value, then increased. The LIDT of the ZrO₂ coatings decreased greatly when the laser scanning speeds were below some value. A Nomarski microscope was employed to map the damage morphology, and it was found that the damage behavior was defect-initiated both for annealed and as-deposited samples. The influences of post-deposition CO₂ laser annealing on the structural and mechanical properties of the films have also been investigated by X-ray diffraction and ZYGO interferometer. It was found that the microstructure of the ZrO₂ films did not change. The residual stress in ZrO₂ films showed a tendency from tensile to compressive after CO₂ laser annealing, and the variation quantity of the residual stress increased with decreasing laser scanning speed. The residual stress may be mitigated to some extent at proper treatment parameters.     

熔石英表面热致应力对激光损伤行为影响的研究

为了研究热致应力对光学元件损伤特性的影响,通过实验测试退火处理消除热应力和未消热应力石英基片的激光损伤特性,研究了热致应力对石英元件初始损伤阈值、损伤增长阈值以及损伤增长规律的影响.结果表明,热致应力对熔石英光学元件的初始损伤阈值有影响,初始损伤阈值随着热致应力增大而降低;热致应力会加剧激光引发的损伤增长,相同的激光通量下,表面应力越大的区域拥有越高的损伤增长因子,但损伤增长仍遵从指数增长规律.热致应力对损伤增长阈值没有明显的影响.本文的研究将为CO2激光预处理工艺能否被应用于大口径光学元件提供一个必要的技术参考.     

Gas breakdown with nanosecond CO2 laser radiation

The thresholds for CO₂ laser induced breakdown and their variation with pulse width have been measured at various pressures for Ar, N₂ and an 8/1/1 laser mixture of He/CO₂/N₂ using 3–40 ns duration pulses. These measurements indicate that excited state production plays a dominant role in determining the threshold for nanosecond duration pulses. This has been confirmed by the good agreement obtained between the measured and theoretical thresholds.     

酸蚀与紫外激光预处理结合提高熔石英损伤阈值

采用HF酸刻蚀和紫外激光预处理相结合的方式提升熔石英元件的负载能力,用质量分数为1%的HF缓冲溶液对熔石英刻蚀1~100 min,综合透过率、粗糙度和损伤阈值测试结果,发现刻蚀时间为10 min的熔石英抗损伤能力最佳。采用355 nm紫外激光对HF酸刻蚀10 min的熔石英进行预处理,结果表明：紫外预处理能量密度在熔石英零损伤阈值的60%以下时,激光损伤阈值单调递增;能量到达80%时,阈值反而低于原始样片的损伤阈值。适当地控制酸蚀时间和紫外激光预处理参数能有效提高熔石英的抗损伤能力。     

CO2激光扫描辐照修复熔石英表面损伤

采用振镜系统结合10.6 m的CO2激光,对熔石英表面损伤点进行辐照,成功地修复了直径500 m的大尺寸损伤点,损伤修复后表面无烧蚀残留,损伤内部完全愈合,无气泡和残余裂纹。和定点修复方式相比,这种修复具有修复尺度大、面形影响区域小、应力分布范围小的优势。80%扫描辐照修复的损伤点的初始损伤阈值恢复甚至超过了基底的初始损伤阈值。     

CO2激光预处理参数对石英基片表面粗糙度的影响

为研究CO2激光预处理参数对熔石英基片表面粗糙度的影响,采用频率为100 Hz,光斑面积为1 mm2的CO2激光对理想的熔石英基片进行辐照处理,根据处理后基片表面微观形貌特征将修复程度分别定义为轻度、中度和重度修复,并对3种修复程度下基片的表面粗糙度值进行了统计。研究了不同脉冲作用时间和不同占空比（激光功率）的激光束单点单次辐照基片后的表面粗糙度。结果表明：石英基片的表面粗糙度均方根值和处理造成的凹陷深度均随脉冲作用时间和功率的增加逐渐变大;均方根值的增幅逐渐增加,凹陷深度的增幅逐渐减小。