Effect of Ⅲ/Ⅴ Ratio of HT-AIN Buffer Layer on Polarity Selection and Electrical Quality of GaN Films Grown by Radio Frequency Molecular Beam Epitaxy

We investigate the effect of A/N ratio of the high temperature （HT） AIN buffer layer on polarity selection and electrical quality of GaN films grown by radio frequency molecular beam epitaxy. The results show that low Al/N ratio results in N-polarity GaN films and intermediate Al/N ratio leads to mixed-polarity GaN films with poor electrical quality. GaN films tend to grow with Ga polarity on Al-rich AIN buffer layers. GaN films with different polarities are confirmed by in-situ reflection high-energy electron diffraction during the growth process. Wet chemical etching, together with atomic force microscopy, also proves the polarity assignments. The optimum value for room-temperature Hall mobility of the Ga-polarity GaN film is 703cm^2/V.s, which is superior to the N-polarity and mixed-polarity GaN films.     

Epitaxial growth of Al on Si(1 1 1) with Cu buffer layers

The structure of thin Al films grown on Si(1 1 1) with thin Cu buffer layers has been investigated using synchrotron radiation photoemission spectroscopy. A thin Cu(1 1 1) layer between the Si(1 1 1) substrate and an Al film may enhance quantum well effects in the Al film significantly. The strength of quantum well effects has been investigated qualitatively with respect to the thickness of the Cu buffer layer and to the Al film thickness. Deposition of Cu on Si(1 1 1)7 × 7 leads to formation of a disordered silicide layer in an initial regime before a well-ordered Cu(1 1 1) film is formed after deposition of the equivalent of 6 layers of Cu. In the regime below 6 layers of Cu the disorder is transferred to Al layers subsequently grown on top. The initial growth of up to 8 layers of Al on a well-ordered Si/Cu(1 1 1) layer leads to a disordered film due to the lattice mismatch between the two metals. When the Cu buffer layer and the Al over-layer are above 6 and 8 layers, respectively the Al film shows sharp low energy electron diffraction patterns and very sharp quantum well peaks in the valence band spectra signalling good epitaxial growth.     

Optical and structural investigation of a-plane GaN layers on r-plane sapphire with nucleation layer optimization

Nonpolar a-plane GaN epilayers are grown on several r-plane sapphire substrates by metal organic chemical vapour deposition using different nucleation layers:(A) a GaN nucleation layer deposited at low temperature(LT);(B) an AlN nucleation layer deposited at high temperature;or(C) an LT thin AlN nucleation layer with an AlN layer and an AlN/AlGaN superlattice both subsequently deposited at high temperature.The samples have been characterized by Xray diffraction(XRD),atomic force microscopy and photoluminescence.The GaN layers grown using nucleation layers B and C show narrower XRD rocking curves than that using nucleation layer A,indicating a reduction in crystal defect density.Furthermore,the GaN layer grown using nucleation layer C exhibits a surface morphology with triangular defect pits eliminated completely.The improved optical property,corresponding to the enhanced crystal quality,is also confirmed by temperature-dependent and excitation power-dependent photoluminescence measurements.     

Influence of AlN buffer layer thickness on structural properties of GaN epilayer grown on Si (111) substrate with AlGaN interlayer

We present the growth of GaN epilayer on Si (111) substrate with a single AlGaN interlayer sandwiched between the GaN epilayer and AlN buffer layer by using the metalorganic chemical vapour deposition. The influence of the AlN buffer layer thickness on structural properties of the GaN epilayer has been investigated by scanning electron microscopy, atomic force microscopy, optical microscopy and high-resolution x-ray diffraction. It is found that an AlN buffer layer with the appropriate thickness plays an important role in increasing compressive strain and improving crystal quality during the growth of AlGaN interlayer, which can introduce a more compressive strain into the subsequent grown GaN layer, and reduce the crack density and threading dislocation density in GaN film.     

Influence of substrate crystallography on the room temperature synthesis of AlN thin films by reactive sputtering

A pulsed DC reactive ion beam sputtering system has been used to synthesize aluminium nitride (AlN) thin films at room temperature by reactive sputtering. After systematic study of the processing variables, high-quality polycrystalline films with preferred c-axis orientation have been grown successfully on silicon and Au/Si substrates with an Al target under a N₂/(N₂ + Ar) gas flow ratio of 55%, 2 mTorr processing pressure and keeping the temperature of the substrate holder at room temperature. The crystalline quality of the AlN layer as well as the influence of the substrate crystallography on the AlN orientation has been characterized by high-resolution X-ray diffraction (HR-XRD). Best ω-FWHM (Full Width at Half Maximum) values of the (0 0 0 2) reflection rocking curve in the 1 μm thick AlN layers are 1.3°. Atomic Force Microscopy (AFM) measurements have been used to study the surface morphology of the AlN layer and Transmission Electron Microscopy (TEM) measurements to investigate the AlN/substrate interaction. AlN grew off-axis from the Si substrate but on-axis to the surface normal. When the AlN thin film is deposited on top of an Au layer, it grows along the [0 0 0 1] direction but showing a two-domain structure with two in-plane orientations rotated 30° between them.     

AlGaN插入层对InAlN/AlGaN/GaN异质结散射机制的影响

InAlN/AlN/GaN异质结中,名义上的AlN插入层实为Ga含量很高的AlGaN层, Al, Ga摩尔百分比决定了电子波函数与隧穿几率,因此影响与InAlN/AlGaN势垒层有关的散射机制.本文通过求解薛定谔-泊松方程与输运方程,研究了AlGaN层Al摩尔百分含量对InAlN组分不均匀导致的子带能级波动散射、导带波动散射以及合金无序散射三种散射机制的影响.结果显示:当Al含量由0增大到1,子带能级波动散射强度与合金无序散射强度先增大后减小,导带波动散射强度单调减小;在Al含量为0.1附近的小组分范围内,合金无序散射是限制迁移率的主要散射机制,该组分范围之外,子带能级波动散射是限制迁移率的主要散射机制;当Al摩尔百分含量超过0.52,三种散射机制共同限制的迁移率超过无插入层结构的迁移率, AlGaN层显示出对迁移率的提升作用.     

Influence of domain boundaries on polarity of GaN grown on sapphire

GaN films were grown on sapphire substrates by laser-induced reactive epitaxy. The domains in the films were determined to be the Ga-polarity by the convergent beam electron diffraction (CBED) technique, while the adjacent matrices had the N-polarity. The domain boundaries were characterized as inversion domain boundaries (IDBs). An atomic structure of the IDB is proposed based on high-resolution transmission electron microscopy (HRTEM) investigations. Control of the polarity of GaN/sapphire films was achieved by suppressing the formation of IDBs with an interlayer of AlGaN and a low-temperature GaN buffer layer.     

Role of Ge interlayer in the growth of high-quality strain relaxed SiGe layer with low dislocation density

High-quality strain relaxed SiGe layer has been fabricated on Si using a thin Ge interlayer grown at 330 °C. The properties of SiGe layers with and without the low-temperature Ge interlayer are compared. The results indicate that the Ge interlayer plays an important role in the preparation of SiGe layer. The strain relaxed low-temperature Ge interlayer with coalesced island surface, acting as a stable and compliant template, could remove the cross-hatch misfit dislocation lines on surface and promote the strain relaxation in the SiGe layer homogeneously.     

CMOS-compatible light-emitting devices based on thin aluminum nitride film containing Al nanocrystals

Electroluminescence (EL) from Al-rich AlN thin films grown on p-type Si substrate by radio frequency (RF) magnetron sputtering has been observed at room temperature. The light-emitting structure based on the thin films can be driven by an electrical pulse as short as 10⁻⁵ s. No obvious change in the light emission intensity was observed after 10⁶ pulse cycles. It has been found that the light emission intensity increases with the Al concentration. It is shown that the phenomenon is due to the enhancement of the percolative conduction via the Al nanocrystals distributed in the AlN matrix as a result of the increase in Al concentration.     

N极性GaN/AlGaN异质结二维电子气模拟

通过自洽求解薛定谔方程和泊松方程,较系统地研究了GaN沟道层、AlGaN背势垒层、Si掺杂和AlN插入层对N极性GaN/AlGaN异质结中二维电子气(2DEG)的影响,分析表明,GaN沟道层厚度、AlGaN背势垒层厚度及Al组分变大都能一定程度上提高二维电子气面密度,AlGaN背势垒层的厚度和Al组分变大也可提高二维电子气限阈性,且不同的Si掺杂形式对二维电子气的影响也有差异,而AlN插入层在提高器件二维电子气面密度、限阈性等方面表现都较为突出,在模拟中GaN沟道层厚度小于5nm时无法形成二维电子气,超过20nm后二维电子气面密度趋于饱和,而AlGaN背势垒厚度超过40nm后二维电子气也有饱和趋势,对均匀掺杂和delta掺杂而言AlGaN背势垒层Si掺杂浓度超过5×10~(19)cm~(-3)后2DEG面密度开始饱和,而厚度为2nmAlN插入层的引入会使2DEG面密度从无AlN插入层时的0.93×10~(13)cm~(-2)提高到1.17×10~(13)cm~(-2)。     

Buffer design for nitrogen polarity GaN on sapphire by RF-MBE and application to the nanostructure formation using KOH etching

GaN films were grown by radiofrequency plasma-assisted molecular beam epitaxy on a variety of sapphire substrates with different buffer layer and/or preparation processes, to show the controllability of lattice-polarity selection as well as their applicability to the nanostructure fabrication. Film polarities, which have been checked by reflection high-energy electron diffraction reconstructions and etched morphologies in KOH aqueous solution, were very sensitive to these preparation processes. Ga-polarity GaN could be obtained by an introduction of a high-temperature nitridation and an AlN interlayer deposition, and the N-polarity film with a flat surface and large grains could be grown on a low-temperature-nitrided sapphire in combination with a use of nitrogen-flux modulation sequence, while other pretreatment resulted in the mixed polarities. The resultant morphology of N-polarity GaN after KOH etching clearly reflects crystallographic orientation and the highly anisotropic-etching behavior show the usefulness of the low-temperature-nitrided sapphire for obtaining large-domain N-polarity GaN and the feasibility of nanostructure fabrication without the use of an expensive dry-etching process.     

The influence of AlN/GaN superlattice intermediate layer on the properties of GaN grown on Si（111） substrates

AlN/GaN superlattice buffer is inserted between GaN epitaxial layer and Si substrate before epitaxial growth of GaN layer. High-quality and crack-free GaN epitaxial layers can be obtained by inserting AlN/GaN superlattice buffer layer. The influence of AlN/GaN superlattice buffer layer on the properties of GaN films are investigated in this paper. One of the important roles of the superlattice is to release tensile strain between Si substrate and epilayer. Raman spectra show a substantial decrease of in-plane tensile strain in GaN layers by using AlN/GaN superlattice buffer layer. Moreover, TEM cross-sectional images show that the densities of both screw and edge dislocations are significantly reduced. The GaN films grown on Si with the superlattice buffer also have better surface morphology and optical properties.     

Properties of GaN on different polarity buffer layers by hydride vapour phase epitaxy

This paper reports on N-, mixed-, and Ga-polarity buffer layers are grown by molecular beam epitaxy (MBE) on sapphire (0001) substrates, with the GaN thicker films grown on the buffer layer with different polarity by hydride vapour epitaxy technique (HVPE). The surface morphology, structural and optical properties of these HVPE-GaN epilayers are characterized by wet chemical etching, scanning electron microscope, x-ray diffraction, and photoluminescence spectrum respectively. It finds that the N-polarity film is unstable against the higher growth temperature and wet chemical etching, while that of GaN polarity one is stable. The results indicate that the crystalline quality of HVPE-GaN epilayers depends on the polarity of buffer layers.     

GaAs(111)衬底上生长的GaN的极性与生长方法和生长条件的关系

研究了在GaAs(111)衬底上生长的六角相GaN的极性的相关关系.在高Ⅴ/Ⅲ比的条件下用MOVPE和MOMBE方法生长的GaN的极性和GaAs衬底的极性一致;在(111)A-Ga表面上的生长层呈现Ga的极性,而在(111)B-As表面上的生长层呈现N的极性.然而,在低的Ⅴ/Ⅲ比,或采用一个AIN中间层的条件下,用HVPE和MOMBE方法在GaAs(111)B表面上生长的GaN呈现出Ga的极性.目前,其原因尚不清楚,但是这些结果表明采用HVPE生长方法或用一高温AlN阻挡层可以得到高质量的GaN.     

Characterization of thick HVPE GaN films

The morphology of the top surface for HVPE GaN layers grown on a MOCVD GaN template with a thin LT-AlN interlayer was investigated. This surface is characterized by the formation of numerous hillocks associated with screw dislocations or nanopipes. Their size is large and may reach more than 1 mm. The rocking curves of the 002 and 102 reflections correspond to a relaxed layer. The HREM images of the as-deposited and annealed interlayers show a perfect atomic structure with a very abrupt AlN/HVPE GaN interface. Thus, the deposition of the LT-AlN layer has promoted the growth of an HVPE layer with an excellent crystalline quality.     

PEALD-deposited crystalline GaN films on Si(100) substrates with sharp interfaces

Polycrystalline gallium nitride(GaN) thin films were deposited on Si(100) substrates via plasma-enhanced atomic layer deposition(PEALD) under optimal deposition parameters. In this work, we focus on the research of the GaN/Si(100)interfacial properties. The x-ray reflectivity measurements show the clearly-resolved fringes for all the as-grown GaN films, which reveals a perfectly smooth interface between the GaN film and Si(100), and this feature of sharp interface is further confirmed by high resolution transmission electron microscopy(HRTEM). However, an amorphous interfacial layer(~ 2 nm) can be observed from the HRTEM images, and is determined to be mixture of Ga_xO_y and GaN by xray photoelectron spectroscopy. To investigate the effect of this interlayer on the GaN growth, an AlN buffer layer was employed for GaN deposition. No interlayer is observed between GaN and AlN, and GaN shows better crystallization and lower oxygen impurity during the initial growth stage than the GaN with an interlayer.     

Influence of double A1N buffer layers on the qualities of GaN films prepared by metal-organic chemical vapour deposition

<正>In this paper we report that the GaN thin film is grown by metal-organic chemical vapour deposition on a sapphire (0001) substrate with double AlN buffer layers.The buffer layer consists of a low-temperature(LT) AlN layer and a high-temperature(HT) AlN layer that are grown at 600℃and 1000℃,respectively.It is observed that the thickness of the LT-AlN layer drastically influences the quality of GaN thin film,and that the optimized 4.25-min-LT-AlN layer minimizes the dislocation density of GaN thin film.The reason for the improved properties is discussed in this paper.     

AlN缓冲层对Si基GaN外延薄膜性质的影响

采用金属有机化合物化学气相沉积（MOCVD）方法制备了不同AlN缓冲层厚度的GaN样品,研究了AlN缓冲层厚度对GaN外延层的应力、表面形貌和晶体质量的影响。研究结果表明：厚度为15 nm的AlN缓冲层不仅可以有效抑制Si扩散,而且还给GaN外延层提供了一个较大的压应力,避免GaN薄膜出现裂纹。在该厚度AlN缓冲层上制备的GaN薄膜表面光亮、无裂纹,受到的张应力为0.3 GPa,（0002）和（1012）面的高分辨X射线衍射摇摆曲线峰值半高宽分别为536 arcsec和594 arcsec,原子力显微镜测试得到表面粗糙度为0.2 nm。     

The influence of SixNy interlayer on GaN film grown on Si(111) substrate

A method to drastically reduce dislocation density in a GaN film grown on an Si(111) substrate is newly developed. In this method, the Si_xN_y interlayer which is deposited on an AlN buffer layer in situ is introduced to grow the GaN film laterally. The crack-free GaN film with thickness over 1.7 micron is grown on an Si(111) substrate successfully. Synthesized GaN epilayer is characterized by X-ray diffraction (XRD), atomic force microscope (AFM), and Raman spectrum. The test results show that the GaN crystal reveals a wurtzite structure with the <0001> crystal orientation and the full width at half maximum of the X-ray diffraction curve in the (0002) plane is as low as 403 arcsec for the GaN film grown on the Si substrate with an Si_xN_y interlayer. In addition, Raman scattering is used to study the stress in the sample. The results indicate that the Si_xN_y interlayer can more effectively accommodate the strain energy. So the dislocation density can be reduced drastically, and the crystal quality of GaN film can be greatly improved by introducing Si_xN_y interlayer.     

Introducing voids around the interlayer of AlN by high temperature annealing

Introducing voids into AlN layer at a certain height using a simple method is meaningful but challenging. In this work, the AlN/sapphire template with AlN interlayer structure was designed and grown by metal-organic chemical vapor deposition. Then, the AlN template was annealed at 1700 ℃ for an hour to introduce the voids. It was found that voids were formed in the AlN layer after high-temperature annealing and they were mainly distributed around the AlN interlayer. Meanwhile, the dislocation density of the AlN template decreased from 5.26×10⁹ cm^-2 to 5.10×10⁸ cm^-2. This work provides a possible method to introduce voids into AlN layer at a designated height, which will benefit the design of AlN-based devices.