MgB2 coated conductors directly grown on flexible metallic Hastelloy tapes by hybrid physical–chemical vapor deposition

MgB₂ coated conductors (CCs), which can avoid the low packing density problem of powder-in-tube (PIT) processed wires, can be a realistic solution for practical engineering applications. Here we report on the superior superconducting properties of MgB₂ CCs grown directly on the flexible metallic Hastelloy tapes without any buffer layer at various deposition temperatures from 520 to 600 °C by using hybrid physical–chemical vapor deposition (HPCVD) technique. The superconducting transition temperatures (T_c) are in the range of 38.5–39.4 K, comparable to bulk samples and high quality thin films. Clear (101) and (002) reflection peaks of MgB₂ are observed in the X-ray diffraction patterns without any indication of chemical reaction between MgB₂ and Hastelloy tapes. From scanning electron microscopy, it was found that connection between MgB₂ grains and voids strongly depend on the growth temperature. A systematic increase in the flux pinning force density and thereby the critical current density with decreasing growth temperature was observed for the MgB₂ CCs. The critical current density (J_c) of J_c(5 K, 0 T) ～10⁷ A/cm² and J_c(5 K, 2.5 T) ～10⁵ A/cm² has been obtained for the sample fabricated at a low growth temperature of 520 °C. The enhanced J_c (H) behavior can be understood on the basis of the variation in the microstructure of MgB₂ CCs with growth temperature.     

钛离子辐照对MgB2超导薄膜的载流能力和磁通钉扎能力的影响

利用混合物理化学气相沉积法(hybrid physical-chemical vapor deposition, HPCVD)可以制备出高性能的MgB₂超导薄膜, 再对薄膜进行钛(Ti)离子辐照处理.经过辐照处理后的样品被掺入了Ti元素, 与未处理的干净MgB₂样品相比,其超导转变温度没有出现大幅度的下降, 而在外加磁场下的临界电流密度得到了明显的提高,同时样品的上临界磁场也得到了提高. 在温度5 K, 外加垂直磁场为4 T的情况下, Ti离子辐照剂量为1× 10¹³/cm²的样品的临界电流密度达到了1.72× 10⁵ A/cm², 比干净的MgB₂要高出许多,而其超导转变温度仍能维持在39.9 K的较高水平.     

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

We report the achievement of transport critical currents in Sr_0.6K_0.4Fe₂As₂ wires and tapes with a T_c = 34 K. The wires and tapes were fabricated through an in situ powder-in-tube process. Silver was used as a chemical addition as well as a sheath material. All the wire and tape samples have shown the ability to transport superconducting current. Critical current density J_c was enhanced upon silver addition, and at 4.2 K, a largest J_c of ～1200 A/cm² (I_c = 9 A) was achieved for 20% silver added tapes, which is the highest in iron-based wires and tapes so far. The J_c is almost field independent between 1 T and 10 T, exhibiting a strong vortex pinning. Such a high transport critical current density is attributed to the weak reaction between the silver sheath and the superconducting core, as well as an improved connectivity between grains. We also identify a weak-link behavior from the apparent drop of J_c at low fields and a hysteretic phenomenon. Finally, we found that compared to Fe, Ta and Nb tubes, Ag was the best sheath material for the fabrication of high-performance 122 type pnictide wires and tapes.     

MgB2 thick films with remarkable ductility on stainless steel substrate

We fabricated several superconducting MgB₂ thick films on stainless steel (SS) substrates by using hybrid physical-chemical vapor deposition (HPCVD) technique. The thickness was in the 10μm to 20μm range, and the onset critical transition temperature T _c (onset) and the width of the superconducting transition (ΔT) were about 37.8 and 1.2 K. They were dense and textured along (101) direction with high tenacity, despite the existence of a little amount of MgO and Mg. We bent the films at different degrees and studied the ductility and transport properties of these MgB₂ thick films under applied force. The results demonstrated that the superconducting properties of these thick films, prepared by HPCVD, stay almost unaffected even with the films bent to a large degree with a curvature of 0.5 mm. This indicated that the superconducting wires or tapes of MgB₂ with a core of SS had the advantages of avoiding rigidity and brittleness in industrial handling. The technique of HPCVD has, therefore, a high application potential. __________ Translated from Chinese Journal of Low Temperature Physics, 2005, 27(2) (in Chinese)     

On the superconductivity in in situ synthesized MgB2 tapes

Single core stainless steel (SS) sheathed MgB₂ tapes have been made by the powder-in-tube (PIT) method using commercial Mg and B powders in two series, one with nominal composition and the other with excess Mg. The electrical resistivity and susceptibility measurements have been carried out to evaluate residual resistivity ratio (RRR), the coherence length ξ(0) and critical current density J_C(T) in these tapes. Detailed structural analysis of the core material has been carried out to correlate the superconducting properties with the crystallinity. In the optimized growth condition the MgB₂ tapes exhibited an estimated J_C of ∼1.4×10⁷ A/m² at 39.45 K in zero field and the zero temperature coherence length is found to be ∼68 Å. MgB₂ tapes fabricated from starting powders having nominal Mg-composition have been shown to exhibit higher J_C than those fabricated from excess magnesium composition of the starting powders. The strained lattice together with the presence of nanosized MgO inclusion having size smaller than the coherence length, are shown to be responsible for the observed higher J_C.     

Role of processing in improving the critical current of Ag/BPSCCO tapes

Silver-clad tapes of highT _c Bi-Pb-Sr-Ca-Cu-O superconductors have been fabricated through the powder-in-tube method. The critical current density, J _c , of a thick tape was 534 A.cm⁻² (77 K, 0 T). Subsequent rolling and sintering of the tapes led to a gradual decrease inJ _c, instead of the expected increase. This was caused by the microcracks developed in the core material by a rather drastic reduction during the rolling of the tapes. A modified and well controlled rolling technique, on the other hand, resulted in much improvedJ _c values. Repeated rolling and sintering resulted in a good grain alignment and no microcracks were observed. In the present studies, maximumJ _c of 1846 A.cm⁻² (77 K, 0 T) and 2.43 × 10⁴ A.cm⁻² (4.2 K, 0 T) have been obtained Optimization of the processing and sintering parameters are expected to lead to still higherJ _c values.     

Transport properties of long monofilamentary Bi(2223) tapes

Summary Monofilamentary Bi(2223) tapes withJ _c(77 K, 0 tesla) up to 30 000 A/cm² have been prepared by cold rolling using the powder-in-tube method. An optimization of the precursor powders has led to a higher phase purity after the reaction heat treatment. The deformation process has been optimized in order to increase the oxide density and to reduce sausaging effects on the oxide thickness. The transport properties of these tapes have been studied in a wide range of temperature (4.2K-T _c) and magnetic fields (up to 28 tesla). The critical-current values at 77 K fields of 0.5 T and 1 T parallel to the tape surface are 10 000 A/cm² and 5400 A/cm², respectively. At 4.2 K theJ _c value decreases from 1.6·10⁵ A/cm² at 0 T to 6·10⁴ A/cm² at 15 T. At fields higher than 15 tesla a very low field dependence ofJ _c has been found, regardless of the tape orientation. Transport properties have also been studied by cutting small sections of the tape in order to investigate the local critical-current distribution. It has been found that, even in rolled tapes of good quality (J _c (77 K, 0 T)>20000 A/cm²), theJ _c distribution is homogeneous: the critical current density increases gradually from the centre of the tape to the sides, the latter exhibiting much higherJ _c (46000 A/cm²) than in the centre (18000 A/cm²). Paper presented at the ?VII Congresso SATT?, Torino, 4–7 October 1994.     

Deposition of Gd2Zr2O7 single buffer layers with different thickness for YBa2Cu3O7−δ coated conductors on metallic substrates

A series of Gd₂Zr₂O₇ (GZO) single buffer layers with different thicknesses were epitaxially grown on highly textured Ni–5 at.% W tapes using pulsed laser deposition. These allow the subsequent growth of high-quality superconducting YBa₂Cu₃O_7?δ layers. The superconducting transition temperature T_c reaches a maximum value of 92.4 K as well as a narrow transition width of 0.8 K for the optimized GZO layer thickness. The inductive measurements show the critical current density as high as 1.2 MA/cm² at 77 K in self-field, indicating that a GZO single buffer layer is a suitable alternative for simplifying the second generation high T_c superconducting coated conductors architecture.     

Superconductivity in porous MgB2

Porous magnesium diboride samples have been prepared by the heat treatment of a pressed mixture of Mg and MgB₂ powders. It was found that linked superconducting structure is formed down to the minimum normalized density γ_c=d/d₀≅0.16 (percolation threshold), where d is the density of MgB₂ averaged over the sample, d₀=2.62 g/cm³ is the X-ray density. Lattice parameters and critical temperature of the porous sample decrease with increasing porosity (decreasing γ) and T_c2≅32 K is minimal at γ_c. The grain boundaries in the porous samples are transparent for the current and J_c∼3×10⁵ A/cm² in self field at T=20 K in the samples with γ∼0.24.     

高性能MgB2长线材制备及性能表征

采用原位粉末装管工艺，分别以Mg粉(99.5%)，无定形B粉(99.9%)为原料，以纳米SiC(10—30nm)作为掺杂材料制备铁基MgB₂线.首先将已混合的原料在丙酮介质中球磨，真空干燥后，将粉末填入铁管内，然后通过孔型轧制、旋锻和拉拔等冷加工工艺得到11m长外径Ф1.75mm铁基MgB₂超导线.用扫描电镜，电子能谱，X射线衍射仪和超导量子干涉仪测试发现，样品微观结构整齐，晶粒大小均匀，内部仅含微量MgO，T_C(onset)=35.1K，ΔT_C＝5.3K.纳米SiC掺杂后，其中C造成MgB₂晶格畸变，形成有效磁通钉扎中心，C元素在MgB₂中分布均匀.标准四引线测试结果表明，11m线均分10段后，各点的J_c(4.2K,10T)均超过1.0×10⁴A/cm^{2，最高值达到1.2×104A/cm2.在10—18T范围各点临界电流值分布均匀，变化率小于10%.}     

Properties of Nb3Ge tapes for high field magnets

A laboratory process for long Nb₃Ge tapes fabrication by chemical vapor deposition (CVD) has been set up. The Nb₃Ge tapes which were fabricated offer the possibility of high current and high field operation at 4.2 K since the values of critical current densities, J_c, measured in high magnetic fields at 20T and 4.2K exceed 5 × 10⁴ A cm^?2 which is the generally accepted criterion for producing a superconducting magnet.     

Effect of processing temperature on the superconducting properties of acetone doped MgB2 tapes

Correlation of phase formation, critical transition temperature T_c, microstructure, and critical current density J_c with sintering temperature has been studied for acetone doped MgB₂/Fe tapes. Sintering was performed at 600–850 °C for 1 h in a flowing Ar atmosphere. High boron substitution by carbon was obtained with increasing the sintering temperature; however, the acetone doped samples synthesized at 800 °C contain large size MgB₂ grains and more MgO impurities. Incomplete reaction for the acetone doped samples heated at 600 °C result in bad intergrain connectivity. At 4.2 K, the best J_c value was achieved in the acetone doped sample sintered at 700 °C, which reached 24,000 A/cm² at 10 T and 10,000 A/cm² at 12 T, respectively. Our results indicate that the small grain size and less impurity were also important for the improvement of J_c–B properties besides the substitutions of B by C.     

Critical current density in MgB2 bulk samples after co-doping with nano-SiC and poly zinc acrylate complexes

The co-doped MgB₂ bulk samples have been synthesized using an in situ reaction processing. The additives is 8 wt.% SiC nano powders and 10 wt.% [(CH₂CHCOO)₂Zn]_n poly zinc acrylate complexes (PZA). A systematic study was performed on samples doped with SiC or PZA and samples co-doped with both of them. The effects of doping and co-doping on phase formation, microstructure, and the variation of lattice parameters were studied. The amount of substituted carbon, the critical temperature (T_c) and the critical current density (J_c) were determined. The calculated lattice parameters show the decrease of the a-axis, while no obvious change was detected for c-axis parameter in co-doped samples. This indicates that the carbon was substituted by boron in MgB₂. The amount of substituted carbon for the co-doped sample shows an enhancement compared to that of the both single doped samples. The co-doped samples perform the highest J_c values, which reaches 3.3 × 10⁴ A/cm² at 5 K and 7 T. It is shown that co-doping with SiC and organic compound is an effective way to further improve the superconducting properties of MgB₂.     

R&D of coated conductors for applications in Japan

On the research and development of coated conductors in Japan, the I_c characteristics and the length have been remarkably improved in the national project. Five hundred meter-long tapes with higher I_c values than 300 A/cm-width were realized by the pulsed laser deposition (PLD) and the metal organic deposition using trifluoroacetates (TFA-MOD) processings for the superconducting layer on the IBAD-GZO buffered substrates. In order to realize the low cost by the increasing the production rate of the ion beam assisted deposition (IBAD) layer, the process of IBAD-MgO was developed and a 1000 m-long IBAD buffer tape was fabricated at an extremely high production rate of 1 km/h. On the other hand, the artificial pinning center has been introduced in both PLD and MOD processing. The BaZrO₃ nano-rods were aligned along the c-axis of GdBCO superconducting films by the PLD process. The J_c value in the magnetic field parallel to the c-axis was remarkably improved. Additionally, the BaZrO₃ nano-particles were uniformly dispersed in YGdBCO films by the TFA-MOD process and the J_c–B–θ property was confirmed to be isotropic.     

Superconductivity and x—ray photoemission study of MgB2 thin films

Highly c-axis oriented MgB2 thin films with Tc^onset of 39.6K were fabricated by magnesium diffusing into pulsedlaser-deposited boron precursors.The estimation of critical current density Jc,using hysteresis loops and the Bean model,has given the value of 10^7A/cm^2(15K,0T),which is one of the highest values ever reported.The x-ray photoemission study of the MgB2 thin films has revealed that the binding energies of Mg 2p and B 1s are at 49.4eV and 186.9eV,which are close to those of metallic Mg and transition-metal diborides,respectively.     

Coated conductors containing grains with big aspect ratios

It is shown that the critical currents of high‐T_csuperconducting tapes fabricated by the coated conductor technologies are enhanced considerably if grain arrangements with large effective grain boundary areas are used. Increasing the aspect ratios of the grains reduces the deleterious effects of the grain boundaries. A practical road to competitive high‐T_ccables is proposed.     

Physical property characterization of bulk MgB<Subscript>2</Subscript> superconductor

We report synthesis, structure/micro-structure, resistivity under magnetic field [ρ(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity κ(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples of MgB₂, processed under identical conditions. The compound crystallizes in hexagonal structure with space group P6/mmm. Transmission electron microscopy (TEM) reveals electron micrographs showing various types of defect features along with the presence of 3–4 nm thick amorphous layers forming the grain boundaries of otherwise crystalline MgB₂. Raman spectra of the compound at room temperature exhibited characteristic phonon peak at 600 cm^-1. Superconductivity is observed at 37.2 K by magnetic susceptibility χ(T), resistivity ρ(T), thermoelectric power S(T), and thermal conductivity κ(T) measurements. The power law fitting of ρ(T) give rise to Debye temperature (Θ_D) at 1400 K which is found consistent with the theoretical fitting of S(T), exhibiting Θ _D of 1410 K and carrier density of 3.81 × 10²⁸/m³. Thermal conductivity κ(T) shows a jump at 38 K, i.e., at T_c, which was missing in some earlier reports. Critical current density (J_c) of up to 10⁵ A/cm² in 1–2 T (Tesla) fields at temperatures (T) of up to 10 K is seen from magnetization measurements. The irreversibility field, defined as the field related to merging of M(H) loops is found to be 78, 68 and 42 kOe at 4, 10 and 20 K respectively. The superconducting performance parameters viz. irreversibility field (H_irr) and critical current density J_c(H) of the studied MgB₂ are improved profoundly with addition of nano-SiC and nano-diamond. The physical property parameters measured for polycrystalline MgB₂ are compared with earlier reports and a consolidated insight of various physical properties is presented.     

High-speed deposition of RE123 film with large current capacity by hot-wall type PLD system

We have studied a hot-wall heating system to produce GdBa₂Cu₃O_y (GdBCO) films with large critical currents (I_c) at a high production rate by a pulsed-laser-deposition (PLD) method. GdBCO films fabricated at a production rate of 30 m/h under the optimized conditions, especially a distance of 95 mm between the target and the substrate (T–S), exhibited high critical current densities (J_c) of about 3 MA/cm² and I_c over 300 A at a thickness of 1–2 μm. Furthermore, long GdBCO tapes prepared by repeated depositions at each tape-passing speed of 80 m/h showed uniform I_c distribution along the longitudinal direction, because the hot-wall system enabled to stabilize temperature within a few degrees at 800 °C. A 170 m long tape with I_c over 600 A was successfully fabricated at a production rate of 16 m/h using a laser power of 360 W.     

Microstructural and superconducting properties of C6H6 added bulk MgB2 superconductor

The effect of aromatic hydrocarbon (benzene, C₆H₆) addition on lattice parameters, microstructure, critical temperature (T_c), critical current density (J_c) of bulk MgB₂ has been studied. In this work only 2 mol% C₆H₆ addition was found to be very effective in increasing the J_c values, while resulting in slight reduction of the T_c. J_c values of 2 mol% C₆H₆ added MgB₂ bulks reached to 1.83×10⁶ A/cm² at 15 K and 0 T. Microstructural analyses suggest that J_c enhancement is associated with the substitution of carbon with boron and which also results in the smaller MgB₂ grain size. The change in the lattice parameters or the lattice disorder is claimed as a cause of the slight reduction in the T_c by carbon addition. We note that our results show the advantages of C₆H₆ addition include homogeneous mixing of precursor powders, avoidance of expansive nanoadditives, production of highly reactive C, and significant enhancement in J_c of MgB₂, compared to un-doped samples.     

High-Jc GdBa2Cu3O7−δ films fabricated by the metal–organic deposition process

We report a successful fabrication of high-J_c GdBa₂Cu₃O_7−δ (GdBCO) films by the metal–organic deposition process on the LaAlO₃ (LAO) (0 0 1) substrates. The coating solution was prepared by mixing Gd, Cu fluorine-free sources with Ba trifluoroacetate. Samples were dip-coated, pyrolized within 3 h at the temperature up to 400 °C in a humid oxygen atmosphere, and finally fired at various high temperatures in 100 ppm Ar/O₂ atmosphere. The GdBCO films fired at 775 and 800 °C exhibited J_c values of ∼2.1 MA/cm² at 77 K in a self-field, which are attributable to both high T_c,zero values of ∼89 K and high in-plane textures of 1.3–1.4°. Above 800 °C, however, the superconducting properties of GdBCO films are degraded due to the thermal decomposition of GdBCO film in 100 ppm Ar/O₂ atmosphere.