Growth, structural and optical properties of CdxZn1−xS thin films deposited using spray pyrolysis technique

Cd_xZn_(1−x)S (x = 0, 0.2, 0.4, 0.6, 0.8, and 1) thin films were deposited by the chemical spray pyrolysis technique using a less used combination of chemicals. Depositions were done at 573 K on cleaned glass substrates. The composition, surface morphology and structural properties of deposited films were studied using EDAX, SEM and X-ray diffraction technique. XRD studies reveal that all the films are crystalline with hexagonal (wurtzite) structure and inclusion of Cd into the structure of ZnS improved the crystallinity of the films. The value of lattice constant ‘a’ and ‘c’ have been observed to vary with composition from 0.382 to 0.415 nm and 0.625 to 0.675 nm, respectively. The band gap of the thin films varied from 3.32 to 2.41 eV as composition varied from x = 0.0–1.0. It was observed that presence of small amount of cadmium results in marked changes in the optical band gap of ZnS.     

The optical properties of CdxZn1−xS thin films on glass substrate prepared by spray pyrolysis method

A series of Cd_xZn_1−xS thin films have been deposited on glass substrates using spray pyrolysis technique. The crystallinity and microstructure of Cd_xZn_1−xS thin films have been investigated by X-ray diffraction (XRD). Based on the results of Hall measurements, the films obtained were an n-type semiconductor. The X-ray data analysis of Cd_xZn_1−xS thin films showed that the grain size of the Cd_xZn_1−xS increased with increase in Cd composition. It is observed that the band gap increases as the Cd composition decreases. The results also showed a blue shift of absorption edge of optical transmission spectra is increases as Zn ratio increases. The effects of Cd composition on the structural and optical properties of Cd_xZn_1−xS thin films were related to their grain size, stress and carrier concentration.     

Growth, structural and optical transport properties of nanocrystal Zn1−xCdS thin films deposited by solution growth technique (SGT) for photosensor applications

Solution Growth Technique (SGT) has been used for deposition of Zn_1−xCdS nanocrystalline thin films. Various parameters such as solution pH (10.4), deposition time, concentration of ions, composition and deposition and annealing temperatures have been optimized for the development of device grade thin film. In order to achieve uniformity and adhesiveness of thin film on glass substrate, 5 ml triethanolamine (TEA) have been added in deposition solution. The as-deposited films have been annealed in Rapid Thermal Annealing (RTA) system at various temperature ranges from 100 to 500 °C in air. The changes in structural formation and optical transport phenomena have been studied with annealing temperatures and composition value (x). As-deposited films have two phases of ZnS and CdS, which were confirmed by X-ray diffraction studies; further the X-ray analysis of annealed (380 °C) films indicates that the films have nanocrystalline size (150 nm) and crystal structure depends on the films stoichiometry and annealing temperatures. The Zn_0.4CdS films annealed at 380 °C in air for 5 min have hexagonal structure where as films annealed at 500 °C have represented the oxide phase with hexagonal structure. Optical properties of the films were studied in the wavelength range 350-1000 nm. The optical band gap (E_g=2.94-2.30 eV) decreases with the composition (x) value. The effect of air rapid annealing on the photoresponse has also been observed on Zn_1−xCdS nanocrystal thin films. The Zn_1−xCdS thin film has higher photosensitivity at higher annealing temperatures (380-500 °C), and films also have mixed Zn_1−xCdS/Zn_1−xCdSO phase with larger grain size than the as-deposited and films annealed up to 380 °C. The present results are well agreed with the results of other studies.     

Growth, structural and optical properties of non-stoichiometric CuIn(S1−xSex)2 thin films deposited by solution growth technique for photovoltaic application

Polycrystalline thin films of p-CuIn(S_1−xSe_x)₂ have been deposited by a solution growth technique. The deposition parameters such as pH, temperature and time have been optimized. In order to achieve uniformity of thin film, triethanolamine (TEA) has been used. As deposited films have been annealed at 450 °C in air for 5 min. The surface morphology, compositional ratio, structural properties have been studied by SEM, EDAX and XRD technique, respectively. It has been found that films have chalcopyrite structure with the lattice parameters a=5.28 Å and c=11.45 Å at composition x=0.5. The grain size of all composition x measured from SEM and XRD is varied in between 450 and 520 nm. The optical transmittance spectra have been recorded in the range 350-1000 nm. The absorption coefficient has been calculated at the absorption edge for each of the composition x and it is in the range of 10⁴ cm⁻¹. The material shows the direct allowed band gap, which varies from 1.07 to 1.44 eV with change in composition (0≤x≤1.0). These parameters are useful for the photovoltaic application.