Synthesis of layered cathode material Li[CoxMn1−x]O2 from layered double hydroxides precursors

Cathode materials Li[Co_xMn_1−x]O₂ for lithium secondary batteries have been prepared by a new route—precursor method of layered double hydroxides (LDHs). In situ high-temperature X-ray diffraction (HT-XRD) and thermogravimetric analysis coupled with mass spectrometry (TG-MS) were used to monitor the structural transformation during the reaction of CoMn LDHs and LiOH·H₂O: firstly the layered structure of LDHs transformed to an intermediate phase with spinel structure; then the distortion of the structure occurred with the intercalation of Li⁺ into the lattice, resulting in the formation of layered Li[Co_xMn_1−x]O₂ with α-NaFeO₂ structure. Extended X-ray absorption fine structure (EXAFS) data showed that the Co-O bonding length and the coordination number of Co were close to those of Mn in Li[Co_xMn_1−x]O₂, which indicates that the local environments of the transitional metals are rather similar. X-ray photoelectron spectroscopy (XPS) was used to measure the oxidation state of Co and Mn. The influences of Co/Mn ratio on both the structure and electrochemical property of Li[Co_xMn_1−x]O₂ have been investigated by XRD and electrochemical tests. It has been found that the products synthesized by the precursor method demonstrated a rather stable cycling behavior, with a reversible capacity of 122.5 mAh g⁻¹ for the layered material Li[Co_0.80Mn_0.20]O₂.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Electron-poor SrAuxIn4−x (0.5?x?1.2) and SrAuxSn4−x (1.3?x?2.2) phases with the BaAl4-type structure

Solid solutions SrAu_xIn_4−x (0.5?x?1.2) and SrAu_xSn_4−x (1.3?x?2.2) have been prepared at 700 °C and their structures characterized by powder and single-crystal X-ray diffraction. They adopt the tetragonal BaAl₄-type structure (space group I4/mmm, Z=2; SrAu_1.1(1)In_2.9(1), a=4.5841(2) Å, c=12.3725(5) Å; SrAu_1.4(1)Sn_2.6(1), a=4.6447(7) Å, c=11.403(2) Å), with Au atoms preferentially substituting into the apical over basal sites within the anionic network. The phase width inherent in these solid solutions implies that the BaAl₄-type structure can be stabilized over a range of valence electron counts (vec), 13.0-11.6 for SrAu_xIn_4−x and 14.1-11.4 for SrAu_xSn_4−x. They represent new examples of electron-poor BaAl₄-type compounds, which generally have a vec of 14. Band structure calculations confirm that substitution of Au, with its smaller size and fewer number of valence electrons, for In or Sn atoms enables the BaAl₄-type structure to be stabilized in the parent binaries SrIn₄ and SrSn₄, which adopt different structure types.     

Structural, spectroscopic and photoluminescence studies of LiEu(WO4)2−x(MoO4)x as a near-UV convertible phosphor

A series of lithium europium double tungsto-molybdate phosphors LiEu(WO₄)_2−x(MoO₄)_x (x=0, 0.4, 0.8, 1.2, 1.6, 2.0) have been synthesized by solid-state reactions and their crystal structure, optical and luminescent properties were studied. As the molybdate content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm was found to increase and reach a maximum when the relative ratio of Mo/W is 2:0. These changes were found to be accompanied with the changes in the spectral feature, which can be attributed to the crystal field splitting of the ⁵D₀→⁷F₂ transition. As the molybdate content increases the emission intensity of the 615 nm peak also increases. The intense red-emission of the tungstomolybdate phosphors under near-UV excitation suggests them to be potential candidate for white light generation by using near-UV LEDs. In this study the effect of chemical compositions and crystal structure on the photoluminescent properties of LiEu(WO₄)_2−x(MoO₄)_x is investigated and discussed.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

Thermoelectric properties of p-type pseudo-binary (Ag0.365Sb0.558Te)x-(Bi0.5Sb1.5Te3)1−x (x=0-1.0) alloys prepared by spark plasma sintering

In this paper, pseudo-binary (Ag_0.365Sb_0.558Te)_x-(Bi_0.5Sb_1.5Te₃)_1−x (x=0-1.0) alloys were prepared using spark plasma sintering technique, and the composition-dependent thermoelectric properties were evaluated. Electrical conductivities range from 7.9×10⁴ to 15.6×10⁴ Ω⁻¹ m⁻¹ at temperatures of 507 and 318 K, respectively, being about 3.0 and 8.5 times those of Bi_0.5Sb_1.5Te₃ alloy at the corresponding temperatures. The optimal dimensionless figure of merit (ZT) of the sample with molar fraction x=0.025 reaches 1.1 at 478 K, whereas that of the ternary Bi_0.5Sb_1.5Te₃ alloy is 0.58 near room temperature. The results also reveal that a direct introduction of Ag_0.365Sb_0.558Te in the Bi-Sb-Te system is much more effective to the property improvement than naturally precipitated Ag_0.365Sb_0.558Te in the Ag-doped Ag-Bi-Sb-Te system.     

High-pressure synthesis and structural characterization of three new polyphosphides, α-SrP3, BaP8, and LaP5

Three novel metal polyphosphides, α-SrP₃, BaP₈, and LaP₅, were prepared in BN crucibles by the reaction of the respective stoichiometric mixtures under a high pressure of 3 GPa at 950-1000°C. Their crystal structures were determined from single-crystal X-ray data (α-SrP₃: space group C2/m, a=9.199(6) Å, b=7.288(3) Å, c=5.690(3) Å, β=113.45(4)°, Z=4, R₁/wR₂=0.0684/0.1180 for 471 observed reflections and 22 variables; BaP₈: space group P−1, a=6.762(2) Å, b=7.233(2) Å, c=8.567(2) Å, α=86.32(2)°, β=84.31(2)°, γ=70.40(2)°, Z=2, R₁/wR₂=0.0476/0.1255 for 2702 observed reflections and 82 variables; LaP₅: space group P2₁/m, a=4.885(1) Å, b=9.673(3) Å, c=5.577(2) Å, β=105.32(2)°, Z=2, R₁/wR₂=0.0391/0.1034 for 1272 observed reflections and 31 variables). α-SrP₃ is isostructural with SrAs₃ and the crystal structure consists of two-dimensional puckered polyanionic layers _∞²[P₃]²⁻ that stack along the c-axis yielding channels occupied by Sr²⁺ counterions. BaP₈ crystallizes in a new structure type which contains a three-dimensional infinite polyanionic framework _∞³[P₃]²⁻, with large channels hosting the barium cations. LaP₅ is a layered compound containing _∞²[P₅]³⁻ polyanionic layers separated by La³⁺ ions. All three compounds exhibit expected diamagnetic behaviors.     

Synthesis, optical properties and electronic structures of polyoxometalates K3P(Mo1−xWx)12O40 (0?x?1)

Various compositions of solid solutions K₃P(Mo_1−xW_x)₁₂O₄₀ (0?x?1) were prepared using two solid state synthetic routes. The crystallite size was determined by linewidth refinements of X-ray diffraction patterns using the Warren-Averbach method, and the grain size distribution by laser scattering experiments. Optical properties were determined by diffuse reflectance measurements in the UV-visible range. The optical gap E_g was found to increase exponentially from ∼2.5 to ∼3.30 eV with increasing x, and is systematically shifted to a higher energy when the grain size decreases. The relation between E_g and x was analyzed by calculating the HOMO-LUMO gaps of the [P(Mo_1−xW_x)₁₂O₄₀]³⁻ anions on the basis of tight-binding electronic structure calculations.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Thermoelectric properties of polycrystalline La1−xSrxCoO3

Thermoelectric properties of polycrystalline La_1−xSr_xCoO₃, where Sr²⁺ is substituted in La³⁺ site in perovskite-type LaCoO₃, have been investigated. Sr-doping increases the electrical conductivity (σ) of La_1−xSr_xCoO₃, and also decreases the Seebeck coefficient (S) for 0.01?x?0.40. A Hall coefficient measurement reveals that the increase in electrical conductivity arises from increases in both carrier concentration and the Hall mobility. The decrease in the Seebeck coefficient is caused by a decrease in carrier effective mass as well as increase in carrier concentration. The highest power factor (σS²) is 3.7×10⁻⁴ W m⁻¹ K⁻² at 250 K for x=0.10. The thermal conductivity (κ) is about 2 W m⁻¹ K⁻¹ at 300 K for 0?x?0.04, and increases for x?0.05 because of an increase in heat transport by conductive carrier. The thermoelectric properties of La_1−xSr_xCoO₃ are improved by Sr-doping, and the figure of merit (Z=σS² κ⁻¹) reaches 1.6×10⁻⁴ K⁻¹ for x=0.06 at 300 K (ZT=0.048). For heavily Sr-doped samples, the thermoelectric properties diminish mainly because of the decrease in the Seebeck coefficient and the increase in thermal conductivity.     

Hydrothermal synthesis, characterization and thermochemistry of Ca2[B2O4(OH)2]·0.5H2O

A pure calcium borate Ca₂[B₂O₄(OH)₂]·0.5H₂O has been synthesized under hydrothermal condition and characterized by XRD, FT-IR and TG as well as by chemical analysis. The molar enthalpy of solution of Ca₂[B₂O₄(OH)₂]·0.5H₂O in HC1·54.582H₂O was determined. From a combination of this result with measured enthalpies of solution of H₃BO₃ in HC1·54.561H₂O and of CaO in (HCl + H₃BO₃) solution, together with the standard molar enthalpies of formation of CaO(s), H₃BO₃(s) and H₂O(l), the standard molar enthalpy of formation of −(3172.5 ± 2.5) kJ mol⁻¹ of Ca₂[B₂O₄(OH)₂]·0.5H₂O was obtained.     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

Formation of crystalline TiO2−xNx and its photocatalytic activity

Amorphous precursors to nitrogen-doped TiO₂ (NTP) and pure TiO₂ (ATP) powders were synthesized by hydrolytic synthesis and sol-gel method (SGM), respectively. Corresponding crystalline phases were obtained by thermally induced transformation of these amorphous powders. From FT-IR and XPS data, it was concluded that a complex containing titanium and ammonia was formed in the precipitate stage while calcination drove weakly adsorbed ammonium species off the surface, decomposed ammonia bound on surface of precipitated powder and led to substitution of nitrogen atom into the lattice of TiO₂ during the crystallization. The activation energies required for grain growth in amorphous TiO_2−xN_x and TiO₂ samples were determined to be 1.6 and 1.7 kJ/mol, respectively. Those required for the phase transformation from amorphous to crystalline TiO_2−xN_x and TiO₂ were determined to be 129 and 142 kJ/mol, respectively. A relatively low temperature was required for the phase transformation in NTP sample than in ATP sample. The fabricated N-doped TiO₂ photocatalyst absorbed the visible light showing two absorption edges; one in UV range due to titanium oxide as the main edge and the other due to nitrogen doping as a small shoulder. TiO_2−xN_x photocatalyst demonstrated its photoactivity for photocurrent generation and decomposition of 2-propanol (IPA) under visible light irradiation ().     

Synthesis, crystal structure and optical properties of a novel sodium lead pentaborate, NaPbB5O9

A novel sodium lead pentaborate, NaPbB₅O₉, has been successfully synthesized by standard solid-state reaction. The single-crystal X-ray structural analysis showed that NaPbB₅O₉ crystallizes in the monoclinic space group P2₁/c with a=6.5324(10) Å, b=13.0234(2) Å, c=8.5838(10) Å, β=104.971(10)°, and Z=4. The crystal structure is composed of double ring [B₅O₉]³⁻ units, [PbO₇] and [NaO₇] polyhedra. [B₅O₉]³⁻ groups connect with each other forming two-dimensional infinite _∞[B₅O₉]³⁻ layers, while [PbO₇] and [NaO₇] polyhedra are located between the layers. [PbO₇] polyhedra linked together via corner-sharing O atom forming novel infinite _∞[PbO₆] chains along the c axis. The thermal behavior, IR spectrum and the optical diffuse reflectance spectrum of NaPbB₅O₉ were reported.     

Hydrothermal synthesis and structure of the first tin(II) squarate Sn2O(C4O4)(H2O)—comparison with Sn2[Sn2O2F4]

A tin(II) squarate Sn₂O(C₄O₄)(H₂O) was synthesized by hydrothermal technique. It crystallizes in the monoclinic system, space group C2/m (no. 12) with lattice parameters a=12.7380(9) Å, b=7.9000(3) Å, c=8.3490(5) Å, β=121.975(3)°, V=712.69(7) Å³, Z=4. The crystal structure determined with an R=0.042 factor, consists of [(Sn₄O₁₀)(H₂O)₂] units connected from one another in the [101] and [010] directions via squarate groups to form layers separated by Sn(II) lone pairs. This compound presents the same remarkable structural arrangement as observed in the tin-oxo-fluoride Sn₂[Sn₂O₂F₄] inorganic compound with Sn(II) lone pairs E(1) and E(2) concentrated in large rectangular-shape tunnels running along [001] direction.     

Thermochemistry of Li1+xMn2−xO4 (0?x?1/3) spinel

Lithium substituted Li_1+xMn_2−xO₄ spinel samples in the entire solid solution range (0?x?1/3) were synthesized by solid-state reaction. The samples with x<0.25 are stoichiometric and those with x?0.25 are oxygen deficient. High-temperature oxide melt solution calorimetry in molten 3Na₂O·4MoO₃ at 974 K was performed to determine their enthalpies of formation from constituent binary oxides at 298 K. The cubic lattice parameter was determined from least-squares fitting of powder XRD data. The variations of the enthalpy of formation from oxides and the lattice parameter with x follow similar trends. The enthalpy of formation from oxides becomes more exothermic with x for stoichiometric compounds (x<0.25) and deviates endothermically from this trend for oxygen-deficient samples (x?0.25). This energetic trend is related to two competing substitution mechanisms of lithium for manganese (oxidation of Mn³⁺ to Mn⁴⁺ versus formation of oxygen vacancies). For stoichiometric spinels, the oxidation of Mn³⁺ to Mn⁴⁺ is dominant, whereas for oxygen-deficient compounds both mechanisms are operative. The endothermic deviation is ascribed to the large endothermic enthalpy of reduction.     

Structural and physical properties of the new intermetallic compound Yb3Pd2Sn2

The crystal structure of the ternary intermetallic compound Yb₃Pd₂Sn₂ has been determined ab initio from powder X-ray diffraction data. The compound crystallizes as a new structure type in the orthorhombic space group Pbcm and lattice constants a=0.58262(3), b=1.68393(8), c=1.38735(7) nm. Yb₃Pd₂Sn₂ is composed of a complex _∞[Pd₂Sn₂]^δ− polyanionic network in which the Yb ions are embedded. A comparison between this structure and those of Eu₃Pd₂Sn₂ and Ca₃Pd₂Sn₂, other novel polar intermetallic compounds, was made. DC susceptibility and ¹⁷⁰Yb Mössbauer spectroscopic measurements indicate a close-to divalent Yb behavior. Moreover, a hybridization between 4f and conduction electrons is suggested by electronic structure calculations and heat capacity measurements.     

Evolution of structure and magnetic properties in electron-doped double perovskites, Sr2−xLaxMnWO6 (0?x?1)

Powder neutron and X-ray diffraction studies show that the double perovskites in the region 0?x?1 exhibit two crystallographic modifications at room temperature: monoclinic P2₁/n and tetragonal I4/m, with a boundary at 0.75<x<0.9. Magnetic susceptibility measurements indicate that for x=0 and 0.5 Sr_2−xLa_xMnWO₆ orders antiferromagnetically (AFM) at 15 and 25 K, respectively, for 0.75?x<1.0, a contribution of weak ferromagnetism (FM), probably due to canted-AFM order, increases with increasing x. The end point compound SrLaMnWO₆ shows the strongest FM cluster effect; however, no clear evidence of magnetic order is discernable down to 4.2 K. X-ray absorption spectroscopy (XAS) confirms Mn²⁺ and mixed-valent W^6+/5+ formal oxidation states in Sr_2−xLa_xMnWO₆.     

A facile high-yield solvothermal route to tin phosphide Sn4P3

An effective method of synthesis of tin phosphide Sn₄P₃ starting from metallic tin and amorphous red phosphorus by a low-temperature (200 °C) solvothermal reaction in ethylenediamine is offered. The key parameters of this process - duration, temperature, and the ratio of initial components (Sn/P) are studied. The structure, phase composition, and morphology of the products are investigated using powder X-ray diffraction and scanning electron microscopy. Different synthetic ways for tin phosphide are discussed and compared with the proposed one. The mechanism of solvothermal preparation of tin phosphide in ethylenediamine is discussed. It is shown that the proposed solvothermal method opens up the possibility of preparing other metal-rich phosphides.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.