一步制备高比表面积介孔Co3O4-CeO2及其表征

以有序介孔二氧化硅KIT-6为硬模板,硝酸钴、硝酸铈为金属源,分别在真空辅助条件和普通搅拌条件下制备了介孔CoCeOx复合氧化物。采用XRD、SEM、TEM、N2吸脱附等技术表征了复合氧化物的物化性质,并评价其氧化甲苯的性能。结果表明,在真空辅助和搅拌条件下制备的CoCeOx氧化物是由Co3O4和CeO2组成的介孔Co3O4-CeO2复合氧化物,其比表面积分别为141和89 m^2·g^-1,平均孔径分别为8.7和9.6 nm。真空辅助纳米复制过程有利于金属盐的前驱体充分填充到模板的孔隙中,去除模板后,可以得到有序的介孔复合金属氧化物。所制备介孔钴铈复合氧化物具有孔道有序性好、比表面积大的特点,在挥发性有机化合物的氧化去除方面具有一定的应用前景。     

Preparation and formation mechanism of three-dimensionally ordered macroporous (3DOM) MgO, MgSO4, CaCO3, and SrCO3, and photonic stop band properties of 3DOM CaCO3

Three-dimensionally ordered macroporous (3DOM) magnesium (Mg) oxide (MgO), MgSO₄, calcium (Ca) carbonate (CaCO₃), and strontium (Sr) carbonate (SrCO₃) were prepared using a colloidal crystal of polymer spheres as a template. Ethanol or ethanol-water solution of metal salts (acetate or nitrate) and citric acid was infiltrated into the void of the colloidal crystal template of a monodispersed poly(methyl methacrylate) (PMMA) sphere. Heating of this PMMA-metal salt-citric acid composite produced the desired well-ordered 3DOM materials with a high pore fraction, which was confirmed by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and ultraviolet-visible (UV-vis) diffuse reflectance spectra. The presence of citric acid is crucial for production of the 3DOM structures. Reaction of citric acid with metal salt produces metal citrate solid in the void of PMMA spheres, which is necessary to maintain the 3DOM structure during the calcination process. 3DOM CaCO₃ shows opalescent colors because of it's photonic stop band properties.     

General synthesis of mesoporous spheres of metal oxides and phosphates

Monodisperse and high-surface-area mesoporous inorganic spheres of various compositions including metal oxides, mixed oxides, and metal phosphates are prepared by templating mesoporous carbon spheres which are replicated from spherical mesoporous silica. Due to the rigid and thermally stable framework of carbon template, the crystalline phases of the obtained metal oxide spheres can be readily tailored by controlling crystalline temperatures. Moreover, the sphere morphologies can be changed from solid structure to hollow structure in some cases by changing the polarity of the precursor, due to the hydrophobic nature of carbon template.     

Amphiphilic block copolymers directed synthesis of mesoporous nickel-based oxides with bimodal mesopores and nanocrystal-assembled walls

Mesoporous late-transition metal oxides have great potential in applications of energy,catalysis and chemical sensing due to their unique physical and chemical properties.However,their synthesis via the flexible and scalable soft-template method remain a great challenge,due to the weak organic-inorganic interaction between the frequently used surfactants(e.g.,Pluronic-type block copolymers) and metal oxide precursors,and the low crystallization temperature of metal oxides.In this study,ordered mesoporous NiO with dual mesopores,high surface area and well-interconnected crystalline porous frameworks have been successfully synthesized via the facile solvent evaporation-induced co-assembly(EICA) method,by using lab-made amphiphilic diblock copolymer polystyrene-b-poly(4-vinylpyridine)(PS-b-P4 VP) as both the structure-directing agent(the soft template) and macromolecular chelating agents for nickel species,THF as the solvent,and nickel acetylacetonate(Ni(acac)2) as inorganic precursor.Similarly,by using Ni(acac)2 and Fe(acac)3 as the binary precursors,ordered mesoporous Fedoped NiO materials can be obtained,which have bimodal mesopores of large mesopores(32.5 nm) and secondary mesopores(4.0-11.5 nm) in the nanocrystal-assembled walls,high specific surface areas(～74.8 m~2/g) and large pore value(～0.167 cm~3/g).The obtained mesoporous Fe-doped NiO based gas sensor showed superior ethanol sensing performances with good sensitivity,high selectivity and fast response-recovery dynamics.     

General Self‐Template Synthesis of Transition‐Metal Oxide and Chalcogenide Mesoporous Nanotubes with Enhanced Electrochemical Performances

The development of a general strategy for synthesizing hierarchical porous transition‐metal oxide and chalcogenide mesoporous nanotubes, is still highly challenging. Herein we present a facile self‐template strategy to synthesize Co₃O₄ mesoporous nanotubes with outstanding performances in both the electrocatalytic oxygen‐evolution reaction (OER) and Li‐ion battery via the thermal‐oxidation‐induced transformation of cheap and easily‐prepared Co‐Asp(cobalt–aspartic acid) nanowires. The initially formed thin layers on the precursor surfaces, oxygen‐induced outward diffusion of interior precursors, the gas release of organic oxidation, and subsequent Kirkendall effect are important for the appearance of the mesoporous nanotubes. This self‐template strategy of low‐cost precursors is found to be a versatile method to prepare other functional mesoporous nanotubes of transition‐metal oxides and chalcogenides, such as NiO, NiCo₂O₄, Mn₅O₈, CoS₂ and CoSe₂.     

Ordered mesoporous Pt/Fe3O4–CeO2 heterostructure gel particles with enhanced catalytic performance for the reduction of 4-nitrophenol

The unique physicochemical properties of ordered mesoporous transition metal oxides have attracted more and more attention. The hydrolysis process of metal oxide precursors is difficult to control, and it is difficult to synthesize an ordered mesoporous transition metal oxide material using the conventional template method. Ordered mesoporous Pt/Fe₃O₄–CeO₂ heterostructure gel materials with excellent catalytic properties were successfully prepared using aerogel technology and the chemical deposition method. The Pt/Fe₃O₄–CeO₂ material was an n–n combined heterostructured semiconductor material which consisted of a magnetic Fe₃O₄ layer, a CeO₂ core and Pt noble metal doped nanoparticles. A layer of Fe₃O₄ thin film was formed on the surface of ordered mesoporous Pt/CeO₂ gel matrix material using the chemical deposition method. The intriguing heterostructural features could facilitate reactant diffusion and exposure of active sites which could enhance synergistic catalytic effects between the Pt nanoparticles and CeO₂ nanoparticles. Compared with Pt/CeO₂, the prepared Pt/Fe₃O₄–CeO₂ showed enhanced catalytic activity in the reduction of 4-nitrophenol at room temperature. The catalytic activity of the heterostructure catalysts was systematically investigated using 4-nitrophenol reduction as a model reaction. The results showed that the Pt (0.1%)/Fe₃O₄–CeO₂ sample exhibited the optimal catalytic performance toward catalytic reduction of 4-nitrophenol to 4-aminophenol. The study provided a method for the preparation of heterostructure nanocatalysts with high efficiency, which would be effective for application in various catalytic reactions.     

介孔金属氧化物/复合物的合成方法

介孔金属氧化物及其复合物由于其特有的组成与结构, 在催化、传感、光、电、磁等领域有着广泛的应用, 是近年来国内外跨学科领域研究的热点。本文对近几年来介孔金属氧化物及其复合物的合成方法进行了归纳总结, 其合成途径大致可以分为软模板法、硬模板法及纳米晶粒组装法。     

真空辅助硬模板法制备三维有序介孔氧化钕

以介孔氧化硅KIT-6为硬模板,硝酸钕为金属源,分别在搅拌条件和真空条件下制备具有三维介孔结构的立方多晶氧化钕。采用XRD、TEM和氮气吸附-脱附技术对所得样品进行表征。结果表明,在真空辅助条件下制备所得的氧化钕较在搅拌条件下制备得到的氧化钕具有更规则的三维有序介孔结构,两者的比表面积分别为117和84 m.2g-1。     

Thermolytic formation and microstructure of IrO2 + Ta2O5 mixed oxide anodes from chloride precursors

The thermolytic formation of IrO₂+Ta₂O₅ mixed oxides from chloride precursors is studied by thermogravimetry (TGA) and differential thermal analysis (DTA). The structure and morphologies of the corresponding oxide films coated on titanium bases are determined by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM), respectively. The experimental results showed that, as a result of the interaction between Ir and Ta components, especially, the formation of solid solution phases during the thermolysis processes, the oxidative dissociation of the H₂IrCl₆+TaCl₅ mixture is facilitated. The catalytic effect reached the maximum at a nominal IrO₂ content of 70 mol% in the expected product, i.e. IrO₂+Ta₂O₅ mixed oxides, accompanied by the highest solid solubility between the two oxides and the finest rutile-structured crystalline grains in the oxides. For the mixed precursors with a low iridium content (e.g. 10 mol% nominal IrO₂ in IrO₂+Ta₂O₅) or a low tantalum content (e.g. 80 mol% nominal IrO₂), however, the decomposition of the major component is inhibited by the minor one at high temperatures (610-800 °C). The results show that the solid solution at low Ir contents (<30 mol% IrO₂) is unstable since it decomposes at high temperatures (≥750 °C). Two or more IrO₂ based rutile-constructed solid solution phases are thermolytically formed from the mixed precursors with nominal IrO₂ contents ≥30 mol%. The rutile-structured phases stably exist only in the case of IrO₂ contents ≥60 mol%.     

Photocatalytic hydrogen evolution over mesoporous TiO2/metal nanocomposites

Na⁺ complex with the dibenzo-18-crown-6 ester was used as a template to synthesize mesoporous titanium dioxide with the specific surface area 130–140 m²/g, pore diameter 5–9 nm and anatase content 70–90%. The mesoporous TiO₂ samples prepared were found to have photocatalytic activity in Cu^II, Ni^II and Ag^I reduction by aliphatic alcohols. The resulting metal–semiconductor nanostructures have remarkable photocatalytic activity in hydrogen evolution from water–alcohol mixtures, their efficiency being 50–60% greater than that of the metal-containing nano-composites based on TiO₂ Degussa P25.The effects of the thermal treatment of mesoporous TiO₂ upon its photocatalytic activity in hydrogen production were studied. The anatase content and pore size were found to be the basic parameters determining the photoreaction rate. The growth of the quantum yield of hydrogen evolution from TiO₂/Ag⁰ to TiO₂/Ni⁰ to TiO₂/Cu⁰ was interpreted in terms of differences in the electronic interaction between metal nanoparticles and the semiconductor surface. It was found that there is an optimal metal concentration range where the quantum yield of hydrogen production is maximal. A decrease in the photoreaction rate at further increment in the metal content was supposed to be connected with the enlargement of metal nanoparticles and deterioration of the intimate electron interaction between the components of the metal–semiconductor nanocomposites.     

Structured mesoporous Mn, Fe, and Co oxides: Synthesis, physicochemical, and catalytic properties

Structured mesoporous Mn, Fe, and Co oxides are synthesized using “soft” and “hard” templates; the resulting materials are characterized by XRD, SEM, TEM, BET, and TG. It is shown that in the first case, the oxides have high surface areas of up to 450 m²/g that are preserved after calcination of the material up to 300°C. Even though, the surface area of the oxides prepared by the “hard-template” method does not exceed 100 m²/g; it is, however, thermally stable up to 500°C. Catalytic activity of mesoporous oxides in methanol conversion was found to depend on both the nature of the transition metal and the type of template used in synthesis.     

Growth of Single‐Layered Two‐Dimensional Mesoporous Polymer/Carbon Films by Self‐Assembly of Monomicelles at the Interfaces of Various Substrates

Single‐layered two‐dimensional (2D) ultrathin mesoporous polymer/carbon films are grown by self‐assembly of monomicelles at the interfaces of various substrates, which is a general and common modification strategy. These unconventional 2D mesoporous films possess only a single layer of mesopores, while the size of the thin films can grow up to inch size in the plane. Free‐standing transparent mesoporous carbon ultrathin films, together with the ordered mesoporous structure on the substrates of different compositions (e.g. metal oxides, carbon) and morphologies (e.g. nanocubes, nanodiscs, flexible and patterned substrates) have been obtained. This strategy not only affords controllable hierarchical porous nanostructures, but also appends the easily modified and multifunctional properties of carbon to the primary substrate. By using this method, we have fabricated Fe₂O₃–mesoporous carbon photoelectrochemical biosensors, which show excellent sensitivity and selectivity for glutathione.     

陈化温度和pH值对氨基功能化介孔氧化硅吸附CO_2性能的影响

本研究采用溶胶-凝胶法,分别以十二烷基肌氨酸钠、氨丙基三甲氧基硅烷(APTMS)和正硅酸乙酯(TEOS)为结构导向剂(SDA)、共结构导向剂(CSDA)和硅源合成了氨基功能化的介孔氧化硅预产物。利用乙醇和乙醇胺混合液对预产物进行萃取后获得氨基功能化介孔氧化硅。利用红外光谱、元素分析、N2吸-脱附、透射电镜等手段对材料进行了表征。红外光谱结果证明通过萃取方法可较好地去除表面活性剂;N2吸附结果表明所有样品都具有介孔结构;元素分析和透射电镜结果说明反应陈化温度、pH值等合成条件对材料孔道内表面的氨基含量和材料结构有较大的影响。CO2吸附实验证明在低陈化温度、相对较低的pH值下合成的材料具有较高的CO2吸附量。     

介孔α-Fe2O3表面配合反应平衡常数测定

采用十二胺为模板剂、氨水做沉淀剂成功制备了介孔α-Fe₂O₃, 通过粉末X射线衍射(XRD)、透射电镜(TEM)、N₂吸附/脱附技术对样品晶相、形貌和比表面积进行了表征. 根据介孔α-Fe₂O₃悬浮液的酸碱滴定数据, 使用FITEQL软件, 采用双电层恒电容模型计算得出了介孔α-Fe₂O₃的表面酸碱反应平衡常数. 在此基础上研究了Cu^2＋, Pb^2＋, Zn^2＋在介孔氧化铁表面的吸附行为, 使用WinSGW软件模拟得出了相应的表面配合反应平衡常数并讨论了其吸附机理.     

Hydrothermal synthesis of the perovskite manganites Pr0.5Sr0.5MnO3 and Nd0.5Sr0.5MnO3 and alkali-earth manganese oxides CaMn2O4, 4H-SrMnO3, and 2H-BaMnO3

We report the synthesis of the perovskite manganites Pr_0.5Sr_0.5MnO₃ and Nd_0.5Sr_0.5MnO₃ using mild hydrothermal conditions. Both are formed as polycrystalline powders from solutions of metal salts in aqueous potassium hydroxide at 240 °C, and crystallise as a tetragonal polymorph (space group I4/mcm). Scanning electron microscopy shows both materials to contain cuboid-shaped crystallites several microns in dimension, and the average particle size is verified by light scattering measurements. We also report the first hydrothermal synthesis of 2H-BaMnO₃ and 4H-SrMnO₃, and the first subcritical hydrothermal synthesis of CaMn₂O₄ (marokite). Despite the formation of these alkali-earth manganese oxides at 240 °C, we have been unable to isolate rare-earth manganese oxides LnMnO₃ using similar conditions. We discuss the formation of perovskite manganites in hydrothermal reactions by relating our new results to those manganites already reported to form under hydrothermal conditions, and rationalise the trends seen by considering tolerance factor of the perovskite and the variance of the A-site metal radius.     

Breakthrough and future: nanoscale controls of compositions,morphologies, and mesochannel orientations toward advanced mesoporous materials

Currently, ordered mesoporous materials prepared through the self‐assembly of surfactants have attracted growing interests owing to their special properties, including uniform mesopores and a high specific surface area. Here we focus on fine controls of compositions, morphologies, mesochannel orientations which are important factors for design of mesoporous materials with new functionalities. This Review describes our recent progress toward advanced mesoporous materials. Mesoporous materials now include a variety of inorganic‐based materials, for example, transition‐metal oxides, carbons, inorganic‐organic hybrid materials, polymers, and even metals. Mesoporous metals with metallic frameworks can be produced by using surfactant‐based synthesis with electrochemical methods. Owing to their metallic frameworks, mesoporous metals with high electroconductivity and high surface areas hold promise for a wide range of potential applications, such as electronic devices, magnetic recording media, and metal catalysts. Fabrication of mesoporous materials with controllable morphologies is also one of the main subjects in this rapidly developing research field. Mesoporous materials in the form of films, spheres, fibers, and tubes have been obtained by various synthetic processes such as evaporation‐mediated direct templating (EDIT), spray‐dried techniques, and collaboration with hard‐templates such as porous anodic alumina and polymer membranes. Furthermore, we have developed several approaches for orientation controls of 1D mesochannels. The macroscopic‐scale controls of mesochannels are important for innovative applications such as molecular‐scale devices and electrodes with enhanced diffusions of guest species. © 2010 The Japan Chemical Journal Forum and Wiley Periodicals, Inc. Chem Rec 9: 321–339; 2009: Published online in Wiley InterScience ( www.interscience.wiley.com ) DOI 10.1002/tcr.200900022     

Original electrochemical mechanisms of CaSnO3 and CaSnSiO5 as anode materials for Li-ion batteries

Calcium stannate (CaSnO₃) and malayaite (CaSnSiO₅) were synthesized by means of a high temperature solid-state reaction. Their crystal structures and morphologies were characterized by X-ray diffraction (XRD) and Scanning Electron Microscopy; their electrochemical properties were analyzed by galvanostatic tests. The amorphization of the initial electrode materials was followed by XRD. The first discharge of the oxides CaSnO₃ and CaSnSiO₅ shows a plateau at low potential, which is due to the progressive formation of Li–Ca–Sn and/or Li–Sn alloys as shown by ¹¹⁹Sn Mössbauer spectroscopy. The results reveal similar electrochemical mechanisms for CaSnO₃ and CaSnSiO₅ but they completely differ from those related to SnO₂.     

Use of a porphyrin platform and 3,4-HPO chelating units to synthesize ligands with N4 and O4 coordination sites

Piperazine and 1,2-diaminobenzene have been previously used as anchoring molecules to synthesize 3-hydroxy-4-pyridinone (3,4-HPO) tetradentate ligands affording ligands with different flexibility and coordination properties. In order to have a relatively rigid and hindered structure, a porphyrin platform was selected to anchor one or two 3,4-HPO chelating units. This platform provides an additional N₄ coordination sphere and also very interesting optical properties to the synthesized conjugates. Depending on the metal ion present in the porphyrin core, conjugates with different spectroscopic properties are obtained. EPR spectroscopy has been used to characterize the copper(II) metalloporphyrins and to monitor and identify the species formed upon addition of copper(II) to solutions of two porphyrin conjugates with one and two 3,4-HPO arms. The porphyrin conjugates having two 3,4-HPO units are ligands that provide two separate binding sites with N₄ and O₄ coordination spheres, which allow accommodation of two metal ion centers that may be distinguished by spectroscopic methods.     

黄铜矿及其复合材料在电化学储能领域的研究进展

黄铜矿(CuFeS₂)是一种具有特殊金色光泽的天然矿物,具有四方结构,其中Fe、Cu离子与晶格中的硫形成四面体配位,相较于其他硫化物和其相对应的氧化物,CuFeS₂具有较高的电导率和优异的电化学性能,且拥有成本低廉、存在天然矿物且自然储量丰富、无毒等优势,使其具有应用于电化学储能体系电极材料的潜能。本文详细介绍了CuFeS₂的物理化学性质、几种简单的不同形貌的合成方法以及其作为电化学储能电极材料方面的研究,并对CuFeS₂材料未来的研究方向进行了展望。     

Hydrothermal synthesis of antimony oxychloride and oxide nanocrystals: Sb4O5Cl2, Sb8O11Cl2, and Sb2O3

We described herein a facile solution-phase route to three nanocrystals of antimony oxychlorides and oxides (Sb₄O₅Cl₂, Sb₈O₁₁Cl₂, and Sb₂O₃), whose morphologies and phases were varied with the pH value of a reaction mixture or composition of a mixed solvent. In particular, the solvent composition controlled the selective preparation of cubic Sb₂O₃ (senarmontite) and orthorhombic Sb₂O₃ (valentinite). Both cubic and orthorhombic Sb₂O₃ samples exhibited strong emission properties.