Structure and properties of the CaFe2O4-type cobalt oxide CaCo2O4

The calcium cobalt oxide CaCo₂O₄ was synthesized for the first time and characterized from a powder X-ray diffraction study, measuring magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power. CaCo₂O₄ crystallizes in the CaFe₂O₄ (calcium ferrite)-type structure, consisting of an edge- and corner-shared CoO₆ octahedral network. The structure of CaCo₂O₄ belongs to an orthorhombic system (space group: Pnma) with lattice parameters, a=8.789(2) Å, b=2.9006(7) Å and c=10.282(3) Å. Curie-Weiss-like behavior in magnetic susceptibility with the nearly trivalent cobalt low-spin state (Co³⁺, 3d, S=0), semiconductor-like temperature dependence of resistivity (ρ=3×10⁻¹ Ω cm at 380 K) with dominant hopping conduction at low temperature, metallic-temperature-dependent large thermoelectric power (Seebeck coefficient: S=+147 μV/K at 380 K), and Schottky-type specific heat with a small Sommerfeld constant (γ=4.48(7) mJ/Co mol K²), were observed. These results suggest that the compound possesses a metallic electronic state with a small density of states at the Fermi level. The doped holes are localized at low temperatures due to disorder in the crystal. The carriers probably originate from slight off-stoichiometry of the phase. It was also found that S tends to increase even more beyond 380 K. The large S is possibly attributed to residual spin entropy and orbital degeneracy coupled with charges by strong electron correlation in the cobalt oxides.     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

Magnetic and Mössbauer Study of the Novel FeIn2S2Se2 Layered Compound

The magnetic properties of the new polymorphic FeIn₂S₂Se₂ compound are presented. The system crystallizes in the α-FeGa₂S₄ structure at low temperatures, and undergoes a transition to a MgAl₂S₄-type structure at T>850°C. For this high-temperature phase, low-field magnetization data show a peak at T₁=12.5(5) K, below which magnetic irreversibility is observed. High-temperature susceptibility fits indicate the presence of antiferromagnetic interactions with a high degree of frustration. The effective magnetic moment μ_eff=4.54(3) μ_B agrees with the expected 3d⁶ (S=2) configuration for Fe²⁺. Mössbauer spectroscopy showed that Fe²⁺ ions are distributed in tetrahedral (A) and octahedral (B) sites with a B:A≈1 ratio. The ac susceptibility data were analyzed according to conventional power law dynamics, giving a freezing temperature T_g=12.5(2) K and critical exponent zν=6.5±1, in agreement with Monte Carlo simulations for 3D short-range Ising spin-glass systems.     

Structure Study of Bi2.5Na0.5Ta2O9 and Bi2.5Nam−1.5NbmO3m+3 (m=2-4) by Neutron Powder Diffraction and Electron Microscopy

The crystal structures of Bi_2.5Na_0.5Ta₂O₉ and Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=3,4) have been investigated by the Rietveld analysis of their neutron powder diffraction patterns (λ=1.470 Å). These compounds belong to the Aurivillius phase family and are built up by (Bi₂O₂)²⁺ fluorite layers and (A_m-1B_mO_3m+1)^2- (m=2-4) pseudo-perovskite slabs. Bi_2.5Na_0.5Ta₂O₉ (m=2) and Bi_2.5Na_2.5Nb₄O₁₅ (m=4) crystallize in the orthorhombic space group A2₁am, Z=4, with lattice constants of a=5.4763(4), b=5.4478(4), c=24.9710 (15) and a=5.5095(5), b=5.4783(5), c=40.553(3) Å, respectively. Bi_2.5Na_1.5Nb₃O₁₂ (m=3) has been refined in the orthorhombic space group B2cb, Z=4, with the unit-cell parameters a=5.5024(7), b=5.4622(7), and c=32.735(4) Å. In comparison with its isostructural Nb analogue, the structure of Bi_2.5Na_0.5Ta₂O₉ is less distorted and bond valence sum calculations indicate that the Ta-O bonds are somewhat stronger than the Nb-O bonds. The cell parameters a and b increase with increasing m for the compounds Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=2-4), causing a greater strain in the structure. Electron microscopy studies verify that the intergrowth of mixed perovskite layers, caused by stacking faults, also increases with increasing m.     

The synthesis and structural characterization of the new ternary nitrides: Ca4TiN4 and Ca5NbN5

The ternary nitrides, Ca₄TiN₄ and Ca₅NbN₅, were synthesized in sealed niobium tubes using lithium nitride as a flux at 900 and 1050 °C, respectively. The structures of both compounds were solved from single-crystal X-ray diffraction data. Ca₄TiN₄ is the first example of a calcium group IV nitride; it crystallizes in the triclinic space group (No. 2) with cell parameters a=5.9757(5) Å, b=6.0129(5) Å, c=6.0116(12) Å, α=71.565(4)°, β=79.471(4)°, γ=68.258(4)° and Z=2. Ca₄TiN₄ is isostructural with Na₄TiO₄ and contains tetrahedral TiN₄ units connected through edges and corners to CaN₄ tetrahedra and CaN₅ square pyramids. Ca₅NbN₅ crystallizes in the monoclinic space group C2/m (No. 12) with cell parameters a=11.922(7) Å, b=6.878(5) Å, c=8.936(7) Å, β=101.22(3)° and Z=4. Ca₅NbN₅ is isostructural with Ba₅NbN₅; the structure contains NbN₄ tetrahedra that share vertices with CaN₅ trigonal bipyramids.     

Crystal growth, structural characterization and magnetic properties of Ca3CuRhO6, Ca3Co1.34Rh0.66O6 and Ca3FeRhO6

Single crystals of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ were synthesized by high temperature flux growth in molten K₂CO₃ and structurally characterized by single crystal X-ray diffraction. While Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ crystallize with trigonal (rhombohedral) symmetry in the space group , Z=6: Ca₃Co_1.34Rh_0.66O₆a=9.161(1) Å, c=10.601(2) Å; Ca₃FeRhO₆a=9.1884(3) Å, c=10.7750(4) Å; Ca₃CuRhO₆ adopts a monoclinic distortion of the K₄CdCl₆ structure in the space group C2/c, Z=4: a=9.004(2) Å, b=9.218(2) Å, c=6.453(1) Å, β=91.672(5). All crystals of Ca₃CuRhO₆ examined were twinned by pseudo-merohedry. Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are structurally related and contain infinite one-dimensional chains of alternating face-sharing RhO₆ octahedra and MO₆ trigonal prisms. In the monoclinic modification, the copper atoms are displaced from the center of the trigonal prism toward one of the rectangular faces adopting a pseudo-square planar configuration. The magnetic properties of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are discussed.     

Structure and magnetism of rare-earth-substituted Ca3Co2O6

Yttrium- and rare-earth-substituted derivatives of Ca_3−vR_vCo₂O₆ (RY, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Yb, and Lu) have been synthesized and structurally characterized by powder X-ray and neutron diffraction. All phases adopt the K₄CdCl₆-type structure with space group R3¯c), in which the trivalent R³⁺ substituents randomly occupy the Ca²⁺ site. The homogeneity range of Ca_3−vR_vCo₂O₆ extends to v≈0.90 for the substituents concerned. A significant increase in the Co2-O distances within the trigonal-prismatic Co2O₆ co-ordination polyhedra upon introduction of R³⁺ confirms that extra electrons from the R³⁺-for-Ca²⁺ substitution exclusively enter the Co2 site of the quasi-one-dimensional Ca_3−vR_vCo₂O₆ structure, thereby formally reducing its oxidation state. This is furthermore supported by magnetic susceptibility and low-temperature neutron diffraction measurements. The long-range ferrimagnetic ordering temperature is reduced upon R substitution and appears to vanish for v>∼0.30.     

The effect of element substitution on high-temperature thermoelectric properties of Ca3Co2O6 compounds

Polycrystalline Ca₃Co_1.8M_0.2O₆ (M=Mn, Fe, Co, Ni, Cu) and Ca_2.7Na_0.3Co₂O₆ were synthesized by solid-state reaction to evaluate the effect of substitution on the thermoelectric properties of Ca₃Co₂O₆. Substitution by Mn, Cu and Na appears to increase carrier density, given that electrical resistivity (ρ) and the Seebeck coefficient (S) were simultaneously reduced. Conversely, Fe substitution seems to reduce carrier density, resulting in a simultaneous increase in S and ρ. Cu and Na substitution resulted in a significant decrease in ρ due to enhancement of grain size and grain boundary connectivity, which could have a strong impact on ρ. Not only the intrinsic substitution effect on the electronic state but also this modification of the microstructure plays an important role in improvement of the thermoelectric power factor, particularly in the case of the Na-substituted sample.     

Composition-induced phase transition in Ca14Zn6−xGa10+xO35+x/2 (x=0.0 and 0.5)

Novel complex oxides Ca₁₄Zn₆Ga₁₀O₃₅ and Ca₁₄Zn_5.5Ga_10.5O_35.25 were prepared in air at 1200 °C, 72 h. Refinements of their crystal structures using X-ray powder diffraction data showed that Ca₁₄Zn₆Ga₁₀O₃₅ is ordered (S.G. F23, =0.0458, R_p=0.0485, R_wp=0.0659, χ²=1.88) and Ca₁₄Zn_5.5Ga_10.5O_35.25 disordered (S.G. F432, =0.0346, R_p=0.0601, R_wp=0.0794, χ²=2.82) variants of the crystal structure of Ca₁₄Zn₆Al₁₀O₃₅. In the crystal structure of Ca₁₄Zn₆Ga₁₀O₃₅, there are large empty voids, which could be partially occupied by additional oxygen atoms upon substitution of Zn²⁺ by Ga³⁺ as in Ca₁₄Zn_5.5Ga_10.5O_35.25. These oxygen atoms are introduced into the crystal structure of Ca₁₄Zn_5.5Ga_10.5O_35.25 only as a part of four tetrahedra (Zn, Ga)O₄ groups sharing common vertex. This creates a situation where even a minor change in the chemical composition leads to considerable anion and cation disordering resulting in a change of space group from F23 (no. 196) to F432 (no. 209).     

Synthesis, structure and physical properties of the new Zintl phases Eu11Zn6Sb12 and Eu11Cd6Sb12

Reported are the syntheses, crystal structure determinations from single-crystal X-ray diffraction, and magnetic properties of two new ternary compounds, Eu₁₁Cd₆Sb₁₂ and Eu₁₁Zn₆Sb₁₂. Both crystallize with the complex Sr₁₁Cd₆Sb₁₂ structure type—monoclinic, space group C2/m (no. 12), Z=2, with unit cell parameters a=31.979(4) Å, b=4.5981(5) Å, c=12.3499(14) Å, β=109.675(1)° for Eu₁₁Zn₆Sb₁₂, and a=32.507(2) Å, b=4.7294(3) Å, c=12.4158(8) Å, β=109.972(1)° for Eu₁₁Cd₆Sb₁₂. Their crystal structures are best described as made up of polyanionic and ribbons of corner-shared ZnSb₄ and CdSb₄ tetrahedra and Eu²⁺ cations. A notable characteristic of these structures is the presence of Sb-Sb interactions, which exist between two tetrahedra from adjacent layers, giving rise to unique channels. Detailed structure analyses shows that similar bonding arrangements are seen in much simpler structure types, such as Ca₃AlAs₃ and Ca₅Ga₂As₆ and the structure can be rationalized as their intergrowth. Temperature-dependent magnetization measurements indicate that Eu₁₁Cd₆Sb₁₂ orders anti-ferromagnetically below 7.5 K, while Eu₁₁Zn₆Sb₁₂ does not order down to 5 K. Resistivity measurements confirm that Eu₁₁Cd₆Sb₁₂ is poorly metallic, as expected for a Zintl phase.     

Single-crystal synthesis, structure analysis, and physical properties of the calcium ferrite-type NaxTi2O4 with 0.558<x<1

Single crystals of calcium ferrite CaFe₂O₄-type NaTi₂O₄ having millimeter-sized needle shapes were synthesized by a reaction of Na metal and TiO₂ in a sealed iron vessel at 1473 K. Sodium-deficient Na_xTi₂O₄ single crystals with 0.558<x<1 were successfully synthesized by a topotactic oxidation reaction using NaTi₂O₄ single crystals as parent materials. The crystal structures of Na_xTi₂O₄ with x=0.970, 0.912, 0.799, 0.751, 0.717, 0.686, 0.611, and 0.558 were determined by the single-crystal X-ray diffraction method. The basic framework constructed by the Ti1O₆ and Ti2O₆ double rutile chains was maintained in these Na_xTi₂O₄ compounds. Based on the results of bond valence analysis, we speculated that the Ti1 sites are preferentially occupied by Ti³⁺ cations over the compositional range of 0.8<x<1, while both the Ti1 and Ti2 sites are randomly occupied by Ti³⁺ and Ti⁴⁺ cations at x=0.558. Magnetic susceptibility data indicated that the broad maximum around 40 K observed in as-grown NaTi₂O₄ is suppressed by an Na deficiency and vanishes in Na_0.717Ti₂O₄. The electrical resistivity increased with the Na deficiency; however, it was still semiconductive in Na_0.799Ti₂O₄.     

Structure and magnetic properties of Ca14MnP11

The compound Ca₁₄MnP₁₁ crystallizes in the Ca₁₄AlSb₁₁ structure type with the tetragonal space group I4₁/acd (Z=8) and lattice parameters of , c=20.7565(9) at 90 K. The structure consists of MnP₄⁹⁻ tetrahedron, P₃⁷⁻ trimer, 4 P³⁻ isolated anions and 14 Ca²⁺ cations. Similar to other compounds of this structure type containing phosphorous, the P₃⁷⁻ trimer has a central P atom that is best modeled in the structure as being equally split between two sites. In addition, there is no additional distortion of the manganese-containing tetrahedron compared with the main group analog, Ca₁₄GaP₁₁, suggesting that the Mn oxidation state is Mn²⁺. Temperature-dependent magnetic susceptibility shows that the compound is paramagnetic over the entire temperature range measured (2-300 K). The data can be fit with a modified Curie-Weiss law and provide an effective magnetic moment of 5.80 (2) B.M. with a Weiss constant of −2.13(2) K and . This moment is significantly higher than those measured for any of the Mn-containing analogs and is consistent with Mn²⁺. This result will be discussed in light of the electron counting scheme for Mn compounds of the Ca₁₄AlSb₁₁ structure-type.     

The crystal structure determinations and refinements of K2S2O7, KNaS2O7 and Na2S2O7 from X-ray powder and single crystal diffraction data

The crystal structures of K₂S₂O₇, KNaS₂O₇ and Na₂S₂O₇ have been solved and/or refined from X-ray synchrotron powder diffraction data and conventional single-crystal data. K₂S₂O₇: From powder diffraction data, monoclinic C2/c, Z=4, a=12.3653(2), b=7.3122(1), , β=93.0792(7)°, R_Bragg=0.096. KNaS₂O₇: From powder diffraction data; triclinic , Z=2, a=5.90476(9), b=7.2008(1), , α=101.7074(9), β=90.6960(7), γ=94.2403(9)°, R_Bragg=0.075. Na₂S₂O₇: From single-crystal data; triclinic , Z=2, a=6.7702(9), b=6.7975(10), , α=116.779(2), β=96.089(3), γ=84.000(3)°, R_F=0.033. The disulphate anions are essentially eclipsed. All three structures can be described as dichromate-like, where the alkali cations coordinate oxygens of the isolated disulphate groups in three-dimensional networks. The K-O and Na-O coordinations were determined from electron density topology and coordination geometry. The three structures have a cation-disulphate chain in common. In K₂S₂O₇ and Na₂S₂O₇ the neighbouring chains are antiparallel, while in KNaS₂O₇ the chains are parallel. The differences between the K₂S₂O₇ and Na₂S₂O₇ structures, with double-, respectively single-sided chain connections and straight, respectively, corrugated structural layers can be understood in terms of the differences in size and coordinating ability of the cations.     

A new structure type of phosphate: Crystal structure of Na2Zn5(PO4)4

A new compound, Na₂Zn₅(PO₄)₄, was identified in the system ZnONa₂OP₂O₅ and high-quality crystal was obtained by the melt method. The crystal structure of this compound was solved by direct method from single crystal X-ray diffraction data. The structure was then refined anisotropically using a full-matrix least square refinement on F² and the refinement converged to R₁=0.0233 and wR₂=0.0544. This compound crystallizes in the orthorhombic system with space group Pbcn, lattice parameters a=10.381(2) Å, b=8.507(1) Å, c=16.568(3) Å and Z=4. The structure is made up of 3D [Zn₅P₄O₁₆]_n²ⁿ⁻ covalent framework consisting of [Zn₄P₄O₁₆]_n⁴ⁿ⁻ layers. The powder diffraction pattern of Na₉Zn₂₁(PO₄)₁₇ is explained by simulating a theoretical pattern with NaZnPO₄ and Na₂Zn₅(PO₄)₄ in the molar ratio of 1:4 and then by Rietveld refinement of experimental pattern. Na₂Zn₅(PO₄)₄ melts congruently at 855 °C and its conductivity is 5.63×10⁻⁹ S/cm.     

Preparation and structural study from neutron diffraction data of Pr5Mo3O16

The title compound has been prepared as polycrystalline powder by thermal treatments of mixtures of Pr₆O₁₁ and MoO₂ in air. In the literature, an oxide with a composition Pr₂MoO₆ has been formerly described to present interesting catalytic properties, but its true stoichiometry and crystal structure are reported here for the first time. It is cubic, isostructural with CdTm₄Mo₃O₁₆ (space group Pn-3n, Z=8), with a=11.0897(1) Å. The structure contains MoO₄ tetrahedral units, with Mo-O distances of 1.788(2) Å, fully long-range ordered with PrO₈ polyhedra; in fact it can be considered as a superstructure of fluorite (M₈O₁₆), containing 32 MO₂ fluorite formulae per unit cell, with a lattice parameter related to that of cubic fluorite (a_f=5.5 Å) as a≈2a_f. A bond valence study indicates that Mo exhibits a mixed oxidation state between 5+ and 6+ (perhaps accounting for the excellent catalytic properties). One kind of Pr atoms is trivalent whereas the second presents a mixed Pr³⁺-Pr⁴⁺ oxidation state. The similarity of the XRD pattern with that published for Ce₂MoO₆ suggests that this compound also belongs to the same structural type, with an actual stoichiometry Ce₅Mo₃O₁₆.     

Crystal structure and magnetic properties of the UFe7Al5 uranium-iron aluminide

The ternary compound UFe₇Al₅ was synthesized by arc melting, followed by annealing at 850°C. The crystal structure was determined by single-crystal X-ray diffraction and refined to a residual value of R=0.039 (S=1.030), with lattice parameters a=8.581(2) Å and c=4.946(1) Å. This compound is a new extreme composition in the family of intermetallics with general formula UFe_xAl_12−x crystallizing in the tetragonal ThMn₁₂-type structure, space group I4/mmm. In contrast to UFe_xAl_12−x within the composition range 4?x?6, in UFe₇Al₅ the additional iron atom is found in the 8i equipositions. Magnetization measurements versus temperature show two magnetic transitions at 363 and 275 K, respectively, with a ferromagnetic behavior below the highest temperature transition. ⁵⁷Fe Mössbauer data indicate that the high-temperature transition is related to the ordering of the iron atoms. The dependence of the isomer shifts and magnetic hyperfine fields on the crystallographic site and on the number of the iron nearest neighbors is similar to that observed in the other UFe_xAl_12−x and rare-earth analogues. The magnetic hyperfine field values of iron atoms on 8i sites is larger than in the other sites, in agreement with previous data obtained for other ThMn₁₂-type compounds.     

Synthesis, crystal structures, magnetic and electric transport properties of Eu11InSb9 and Yb11InSb9

Two new rare-earth metal containing Zintl phases, Eu₁₁InSb₉ and Yb₁₁InSb₉ have been synthesized by reactions of the corresponding elements in molten In metal to serve as a self-flux. Their crystal structures have been determined by single crystal X-ray diffraction—both compounds are isostructural and crystallize in the orthorhombic space group Iba2 (No. 45), Z=4 with unit cell parameters a=12.224(2) Å, b=12.874(2) Å, c=17.315(3) Å for Eu₁₁InSb₉, and a=11.7886(11) Å, b=12.4151(12) Å, c=16.6743(15) Å for Yb₁₁InSb₉, respectively (Ca₁₁InSb₉-type, Pearson's code oI84). Both structures can be rationalized using the classic Zintl rules, and are best described in terms of discrete In-centered tetrahedra of Sb, [InSb₄]⁹⁻, isolated Sb dimers, [Sb₂]⁴⁻, and isolated Sb anions, Sb³⁻. These anionic species are separated by Eu²⁺ and Yb²⁺ cations, which occupy the empty space between them and counterbalance the formal charges. Temperature-dependent magnetic susceptibility and resistivity measurements corroborate such analysis and indicate divalent Eu and Yb, as well as poorly metallic behavior for both Eu₁₁InSb₉ and Yb₁₁InSb₉. The close relationships between these structures and those of the monoclinic α-Ca₂₁Mn₄Sb₁₈ and Ca₂₁Mn₄Bi₁₈ are also discussed.     

Structural and magnetic properties of the quaternary oxides Ba6Ln2Fe4O15 (Ln=Pr and Nd)

The crystal structures and magnetic properties of the quaternary lanthanide oxides Ba₆Ln₂Fe₄O₁₅ (Ln=Pr and Nd) are reported. They crystallize in a hexagonal structure with space group P6₃mc and have the “Fe₄O₁₅ cluster” consisting of one FeO₆ octahedron and three FeO₄ tetrahedra. Measurements of the magnetic susceptibility, specific heat, and powder neutron diffraction reveal that this cluster behaves as a spin tetramer with a ferrimagnetic ground state of S_T=5 even at room temperature. The cluster moments show a long-range antiferromagnetic ordering at 23.2 K (Ln=Pr) and 17.8 K (Nd), and the magnetic moments of the Ln³⁺ ions also order cooperatively. By applying the magnetic field (∼2 T), this antiferromagnetic ordering of the clusters changes to a ferromagnetic one. This result indicates that there exists a competition in the magnetic interaction between the clusters.     

EuZn2Si2 and EuZn2Ge2 Grown from Zn or Ga(ln)/Zn Flux

Single crystals of the novel ternary compounds EuZn₂Si₂ and EuZn₂Ge₂ were grown from pure gallium, indium, or zinc metal used as a flux solvent. Crystal properties were characterized using X-ray single-crystal analyses via Gandolfi and Weissenberg film techniques and by four-circle X-ray single-crystal diffractometry. The new compounds crystallize with ternary derivative structures of BaAl₄, i.e., EuZn₂Si₂ with ThCr₂Si₂-type (a=0.42607(2) nm, c=1.03956(5) nm, I4/mmm, R₁=0.038) and EuZn₂Ge₂ with CaBe₂Ge₂-type (a=0.43095(2) nm, c=1.07926(6) nm, P4/nmm, R₁=0.067). XAS and magnetic measurements on EuZn₂Si₂ and EuZn₂Ge₂ revealed in both compounds the presence of Eu²⁺ ions carrying large magnetic moments, which order magnetically at low temperatures. The magnetic phase transition occurs at T_N=16 and 7.5 K for the silicide and the germanide, respectively. In EuZn₂Si₂ there occurs a spin reorientation at 13 K and furthermore some canting of antiferromagnetically ordered moments below about 10 K. In EuZn₂Ge₂ a canted antiferromagnetic structure is formed just at T_N.     

Structure and magnetism of NaRu2O4 and Na2.7Ru4O9

The structures of NaRu₂O₄ and Na_2.7Ru₄O₉ are refined using neutron diffraction. NaRu₂O₄ is a stoichiometric compound consisting of double chains of edge sharing RuO₆ octahedra. Na_2.7Ru₄O₉ is a non-stoichiometric compound with partial occupancy of the Na sublattice. The structure is a mixture of single, double and triple chains of edge-shared RuO₆ octahedra. NaRu₂O₄ displays temperature independent paramagnetism with . Na_2.7Ru₄O₉ is paramagnetic, χ₀= with and a Curie constant of 0.0119 emu/mol Oe K. Specific heat measurements reveal a small upturn at low temperatures, similar to the upturn observed in La₄Ru₆O₁₉. The electronic contribution to the specific heat (γ) for Na_2.7Ru₄O₉ was determined to be15 mJ/mole_Ru K².