Crystal structures and magnetic properties of CeAu4Si2 and CeAu2Si2

Single crystals of CeAu₄Si₂ and CeAu₂Si₂ have been grown out of ternary fluxes rich in Au, and the former, also by sintering the stoichiometric composition at 750 °C. The single-crystal X-ray refinement result for CeAu₄Si₂ is orthorhombic, Cmmm (No. 65, Z=2), different from a tetragonal result found from an X-ray powder diffraction refinement [H. Nakashima, et al., J. Alloys Compds. 424 (2006) 7]. For CeAu₂Si₂, this is the first report of the stoichiometric crystalline phase, in the known tetragonal I4/mmm structure. The anisotropic field- and temperature-dependent magnetizations, as well as specific heat and resistivity data are compared. Although both compounds have related structural packing, they present unique magnetic features. CeAu₂Si₂ is a typical antiferromagnet with T_N=8.8(1) K and CeAu₄Si₂ features a ferromagnetic component below T_c=3.3(1) K. Both phases have effective moments close in value to that of free Ce³⁺.     

EuZn2Si2 and EuZn2Ge2 Grown from Zn or Ga(ln)/Zn Flux

Single crystals of the novel ternary compounds EuZn₂Si₂ and EuZn₂Ge₂ were grown from pure gallium, indium, or zinc metal used as a flux solvent. Crystal properties were characterized using X-ray single-crystal analyses via Gandolfi and Weissenberg film techniques and by four-circle X-ray single-crystal diffractometry. The new compounds crystallize with ternary derivative structures of BaAl₄, i.e., EuZn₂Si₂ with ThCr₂Si₂-type (a=0.42607(2) nm, c=1.03956(5) nm, I4/mmm, R₁=0.038) and EuZn₂Ge₂ with CaBe₂Ge₂-type (a=0.43095(2) nm, c=1.07926(6) nm, P4/nmm, R₁=0.067). XAS and magnetic measurements on EuZn₂Si₂ and EuZn₂Ge₂ revealed in both compounds the presence of Eu²⁺ ions carrying large magnetic moments, which order magnetically at low temperatures. The magnetic phase transition occurs at T_N=16 and 7.5 K for the silicide and the germanide, respectively. In EuZn₂Si₂ there occurs a spin reorientation at 13 K and furthermore some canting of antiferromagnetically ordered moments below about 10 K. In EuZn₂Ge₂ a canted antiferromagnetic structure is formed just at T_N.     

Long-range antiferromagnetic ordering in Cu2NiB2O6

Magnetic properties of peculiar structural-type borate Cu₂NiB₂O₆ are investigated by means of ac susceptibility, dc magnetization, and heat capacity measurements. This material is isostructural to Cu₂CoB₂O₆, of which the structural configuration is composed of quasi-one-dimensional six-columns ribbons. Our experimental results show that this material displays an antiferromagnetic phase transition at ∼15 K, which differs from Cu₂CoB₂O₆ showing spin-glass behavior below 5 K. The different magnetic ground states in these compounds may be attributed mainly to the subtle balance of the exchange energy in the scalene triangles.     

Magnetic and electronic structure of TlCo2S2

An extensive investigation of the ferromagnetic compound TlCo₂S₂ has resulted in new information on the electronic and magnetic structure. Electronic structure calculations showed that magnetic ordering is energetically favorable with a clear driving force for ferromagnetic coupling within the cobalt layers. TlCo₂S₂ is metallic and the conductivity is due to holes in the valence band. XPS single crystal measurements did not show evidence of mixed oxidation states of cobalt. Neutron powder diffraction resulted in a ferromagnetic structure with the magnetic moment in the ab-plane. The derived magnetic moment of the cobalt atom is at 10 K and is in very good agreement with the value, at 10 K, inferred from the magnetic hysteresis curve.     

A novel germanate, Cu2Fe2Ge4O13, with a four tetrahedra oligomer

The structure of Cu₂Fe₂Ge₄O₁₃, previously thought to be CuFeGe₂O₆, has been determined from single-crystal X-ray diffraction data to be monoclinic, P2₁/m, a=12.1050(6), b=8.5073(4), c=4.8736(2) Å, β=96.145(1)°, Z=2, with R1=0.0231 and wR2=0.0605. The unique structure has an oligomer of four germanate tetrahedra, cross-linked laterally by square-planar copper ions, joined end-to-end by a zigzag chain of edge-sharing iron oxide octahedra. Running along the a-direction the metal oxide chain consists of alternating Cu-Cu and Fe-Fe dimers. A hypothetical series of homologous structures (Cu_n−2Fe₂Ge_nO_3n+1 with n=3,4,…,∞) with different length germanate oligomers is proposed, where as n increases, the infinite chain of the CuGeO₃ is approached. In this context, Cu₂Fe₂Ge₄O₁₃ is viewed as being built from blocks of CuGeO₃ and the Fe oxide chains. This material has significance to the study of low-dimensional mixed-spin systems.     

Synthesis, structure and physical properties of the new uranium ternary phase U3Co2Ge7

A new ternary compound, U₃Co₂Ge₇, has been synthesized from the corresponding elements by a high temperature reaction using molten tin flux. It crystallizes in the orthorhombic La₃Co₂Sn₇-type (Pearson's symbol oC24, space group Cmmm, No. 65) with lattice parameters determined from single-crystal X-ray diffraction as follows: a=4.145(2) Å; b=24.920(7); c=4.136(2) Å, V=427.2(3) Å³. Structure refinements confirm an ordered structure having two crystallographically inequivalent uranium atoms, occupying sites with dissimilar coordination. U₃Co₂Ge₇ orders ferromagnetically below 40 K and undergoes a consecutive magnetic transition at 20 K. These results have been obtained from temperature- and field-dependent magnetization, resistivity and heat-capacity measurements. The estimated Sommerfeld coefficient γ=87 mJ/mol-U K² suggests U₃Co₂Ge₇ to be a moderately heavy-fermion material.     

Structure and Properties of Yb3Ge5

Single crystals of Yb₃Ge₅, grown from pure gallium or indium metal flux and investigated by means of CCD four-circle diffractometry, were consistent with the Th₃Pd₅-type of structure, displaying full order of vacancies and germanium atoms. From magnetic susceptibility and electrical resistivity measurements, performed on single-crystalline specimens, Yb₃Ge₅ was found to be an intermediate valent systems.     

Transport and optical properties of heavily hole-doped semiconductors BaCu2Se2 and BaCu2Te2

Experimental and theoretical studies of the electronic and optical properties of orthorhombic BaCu₂Se₂ and BaCu₂Te₂ are reported. Experimental data include the electrical resistivity, Hall coefficient, Seebeck coefficient, thermal conductivity, and lattice constants for , and optical transmission and diffuse reflectance data at room temperature. Nominally stoichiometric, polycrystalline samples form with hole concentrations inferred from Hall measurements of 2×10¹⁸ and 5×10¹⁹ cm⁻³ near room temperature for the selenide and telluride, respectively. The corresponding mobilities are near 15 cm² V⁻¹ s⁻¹ for both materials. Optical measurements reveal a transition near 1.8 eV in BaCu₂Se₂, while no similar feature was observed for BaCu₂Te₂. First principles calculations indicate both materials are direct or nearly direct gap semiconductors with calculated gaps near 1.0 eV and 1.3 eV for the telluride and selenide, respectively, and predict weak absorption below about 2 eV. Transport properties calculated from the electronic structure are also presented.     

The crystal structure determinations and refinements of K2S2O7, KNaS2O7 and Na2S2O7 from X-ray powder and single crystal diffraction data

The crystal structures of K₂S₂O₇, KNaS₂O₇ and Na₂S₂O₇ have been solved and/or refined from X-ray synchrotron powder diffraction data and conventional single-crystal data. K₂S₂O₇: From powder diffraction data, monoclinic C2/c, Z=4, a=12.3653(2), b=7.3122(1), , β=93.0792(7)°, R_Bragg=0.096. KNaS₂O₇: From powder diffraction data; triclinic , Z=2, a=5.90476(9), b=7.2008(1), , α=101.7074(9), β=90.6960(7), γ=94.2403(9)°, R_Bragg=0.075. Na₂S₂O₇: From single-crystal data; triclinic , Z=2, a=6.7702(9), b=6.7975(10), , α=116.779(2), β=96.089(3), γ=84.000(3)°, R_F=0.033. The disulphate anions are essentially eclipsed. All three structures can be described as dichromate-like, where the alkali cations coordinate oxygens of the isolated disulphate groups in three-dimensional networks. The K-O and Na-O coordinations were determined from electron density topology and coordination geometry. The three structures have a cation-disulphate chain in common. In K₂S₂O₇ and Na₂S₂O₇ the neighbouring chains are antiparallel, while in KNaS₂O₇ the chains are parallel. The differences between the K₂S₂O₇ and Na₂S₂O₇ structures, with double-, respectively single-sided chain connections and straight, respectively, corrugated structural layers can be understood in terms of the differences in size and coordinating ability of the cations.     

AlCl3(ZnCl2,MgCl2)对Sm2O3的氯化效果及电化学行为

研究了AlCl_3(ZnCl_2、MgCl_2)对Sm_2O_3的氯化效果以及Sm_2O_3在Li Cl-KCl-AlCl_3(ZnCl_2、MgCl_2)熔盐体系中的电化学行为。在Li Cl-KCl-Sm_2O_3熔盐中加入AlCl_3(ZnCl_2、MgCl_2)后,ICP测量结果表明,AlCl_3体系中Sm(Ⅲ)离子的浓度最高,并且在923 K时达到最大值;固相反应表明,AlCl_3氯化Sm_2O_3生成SmCl_3,而Sm_2O_3和ZnCl_2(MgCl_2)反应生成Sm OCl。电化学行为表明,AlCl_3体系中观察到了两种Al-Sm的合金峰,而ZnCl_2体系中只观察到Zn-Sm金属间化合物的形成峰,MgCl_2体系中没有形成合金。在-6.25 A·cm~(-2)下,W电极上恒电流电解2 h获得了Al-Li-Sm合金,经XRD分析,合金为Al_2Sm相。     

AlCl3(ZnCl2,MgCl2)对Sm2O3的氯化效果及电化学行为

研究了AlCl₃(ZnCl₂、MgCl₂)对Sm₂O₃的氯化效果以及Sm₂O₃在LiCl-KCl-AlCl₃(ZnCl₂、MgCl₂)熔盐体系中的电化学行为。在LiCl-KCl-Sm₂O₃熔盐中加入AlCl₃(ZnCl₂、MgCl₂)后,ICP测量结果表明,AlCl₃体系中Sm(Ⅲ)离子的浓度最高,并且在923 K时达到最大值;固相反应表明,AlCl₃氯化Sm₂O₃生成SmCl₃,而Sm₂O₃和ZnCl₂(MgCl₂)反应生成SmOCl。电化学行为表明,AlCl₃体系中观察到了两种Al-Sm的合金峰,而ZnCl₂体系中只观察到Zn-Sm金属间化合物的形成峰,MgCl₂体系中没有形成合金。在-6.25 A·cm^-2下,W电极上恒电流电解2 h获得了Al-Li-Sm合金,经XRD分析,合金为Al₂Sm相。     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

TiO2/SnO2复合光催化剂的耦合效应

采用改进的sol gel技术制备TiO2/SnO2耦合型半导体光催化剂,利用XRD、气相色谱 仪、粒度仪和表面光电压装置等研究了耦合型半导体光催化机理和光催化效率的影响因素, 并通过降解甲醛探讨其在空气污染治理中的作用.实验结果表明,添加20 ％(mol) SnO2的复 合半导体光催化剂,其光催化效率比纯TiO2高一倍以上.据实验结果和粒子紧密堆积原理,提 出强耦合效应和弱耦合效应的光催化反应模型,并用此模型较好地解释了TiO2/SnO2复合型半 导体光催化剂的光催化效率随SnO2含量变化规律.     

Conversion of NO in NO/N2, NO/O2/N2, NO/C2H4/N2 and NO/C2H4/O2/N2 Systems by Dielectric Barrier Discharge Plasmas

An experimental study on the conversion of NO in the NO/N₂, NO/O₂/N₂, NO/C₂H₄/N₂ and NO/C₂H₄/O₂/N₂ systems has been carried out using dielectric barrier discharge (DBD) plasmas at atmospheric pressure. In the NO/N₂ system, NO decomposition to N₂ and O₂ is the dominating reaction; NO conversion to NO₂ is less significant. O₂ produced from NO decomposition was detected by an on-line mass spectrometer. With the increase of NO initial concentration, the concentration of O₂ produced decreases at 298 K, but slightly increases at 523 K. In the NO/O₂/N₂ system, NO is mainly oxidized to NO₂, but NO conversion becomes very low at 523 K and over 1.6% of O₂. In the NO/C₂H₄/N₂ system, NO is reduced to N₂ with about the same NO conversion as that in the NO/N₂ system but without NO₂ formation. In the NO/C₂H₄/O₂/N₂ system, the oxidation of NO to NO₂ is dramatically promoted. At 523 K, with the increase of the energy density, NO conversion increases rapidly first, and then almost stabilizes at 93–91% of NO conversion with 61–55% of NO₂ selectivity in the energy density range of 317–550 J L⁻¹. It finally decreases gradually at high energy density. A negligible amount of N₂O is formed in the above four systems. Of the four systems studied, NO conversion and NO₂ selectivity of the NO/C₂H₄/O₂/N₂ system are the highest, and NO/O₂/C₂H₄/N₂ system has the lowest electrical energy consumption per NO molecule converted.     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

V2O5/TiO2催化剂表面结构FT-IR发射光谱研究(II)

用傅里哀变换红外发射光谱原位考察了V_2O_5/TiO_2催化剂在制备焙烧过程中担载偏钒酸铵的热分解步骤及其形成的表面活性相结构。偏钒酸铵在200 ℃左右分解, 在300 ℃之前完全转化为晶相V_2O_5。担载于TiO_2上的偏钒酸铵在100 ℃左右与TiO_2已产生强的化学作用, 在200 ℃之前已完全分解。对于10%(质量分数)V_2O_5/TiO_2催化剂其担载偏钒酸分解后在1020 cm~(-1)附近出现晶相V_2O_5的特征峰。但在500 ℃进一步焙烧后晶相V_5O_5的峰减弱并在1025—900 cm~(-1)区出现宽峰, 表明部分晶相V_2O_5可能转化为二维高分散的VO_x物种。2%(质量分数)V_2O_5/TiO_2催化剂在焙烧过程中也显示晶相V_2O_5的弱峰, 但同时也观察到属于VO_x物种的宽峰。进一步降低钒担载量, V_2O_5晶相特征峰逐渐消失, 而在1025—900 cm~(-1)区出现二维VO_x物种的宽峰。结果还表明傅里哀变换红外发射光谱是表征氧化物催化剂表面相结构的一种有力的方法。     

Mn-Na2WO4/SiO2催化剂表面活性中心结构的DFT研究

Mn Na2WO4/SiO2 is one of the best catalysts for oxidative coupling of methane.To investigate the nature of active centers and the reaction mechanism,the structure of possible metal sites formed by tungsten and manganese over the silica surface were studied using molecular simulation method and ab initio DFT calculations.Silica support exists in the catalyst as 岐瞔ristobalite and its (111) face exposes preferentially to the surface.The calculated results show that tungsten interacts with the silica surface by three or one bridge oxygen atoms to form tetrahedral [WO4],and manganese interacts with single bridge oxygen to form dispersed [MnO4] or exists as oxide clusters.The nature of the molecular orbitals and the electronic structure suggest that the tetrahedral [WO4] site with single bridge oxygen is the most probable active center responsible for methane activation.     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

Crystal structure and vibrational properies of Rb2MgWO2(PO4)2—A new framework phosphate

The new compound Rb₂MgWO₂(PO₄)₂ has been synthesized and characterized by a single-crystal X-structure determination, and IR and Raman spectroscopic studies. The crystal structure is orthorhombic, space group Pbca, with the unit cell dimensions a=9.891(2), b=12.641(2), , Z=8. Compared to the K₂M^IIWO₂(PO₄)₂ series, where M^II=Mg, Mn, Fe, Co, Ni, and Cd, the volume of the unit cell in the present compound is nearly doubled. The MgO₆ and WO₆ octahedra are arranged into polyhedral groups consisting of two edge sharing MgO₆ joined by corners with two WO₆ octahedra. These groups are interconnected through the PO₄ tetrahedra into layers in a×b plane. The Rb⁺ ions perform thermally activated displacements within the cavities formed between the polyhedral layers. The origin of various Raman and IR modes is discussed. These results indicate that a clear energy gap exists between the stretching and remaining modes. The most intense modes are shown to be due to vibrations of the W-O bonds.