Li2Mg2Si4O10F2、H2Mn8O16·1.4H2O和Li1.3Ti1.7Al0.3(PO4)3在高浓度LiCl水溶液中的离子交换行为

研究了用功能材料 Li2Mg2Si4O10F2(LHT)、 H2Mn8O16@ 1.4H2O(CRYMO)和 Li1.3Ti1.7Al0.3(PO4)3(LTAP)分别去除高浓度氯化锂水溶液中的杂质 Fe3+、 K+和 Na+ .实验结果表明,这几种功能材料分别对溶液中的杂质 Fe3+、 K+和 Na+有很高的选择性,除杂效果明显 .分析和研究了这几种功能材料在高浓度氯化锂水溶液中分别与 Fe3+、 K+和 Na+的交换行为 .结果表明,在高浓度氯化锂溶液中这几种功能材料与杂质交换的动力学行为可近似用 JMAK方程描述.     

Li1.3Ti1.7Al0.3(PO4)3与Na+的离子交换

锂离子传导材料Li_1.3Ti_1.7Al_0.3(PO₄)₃是具有NASICON结构的功能材料, 与Na⁺进行离子交换具有选择性高的特性. 研究了在不同温度条件下NaCl和LiCl水溶液中Li_1.3Ti_1.7Al_0.3(PO₄)₃上的Na/Li离子交换行为. 实验结果表明, 升高温度能显著提高Li_1.3Ti_1.7Al_0.3(PO₄)₃的Na/Li交换反应速率, 提高LiCl中杂质Na的分离效果.     

Li1.3Zr1.7Al0.3(PO4)3的离子交换特性

锂作为21世纪推动科学技术发展的重要元素之一,被誉为“工业味精”、“能源之星”。目前锂及其相关盐类材料已成为信息产业、核能源、航空航天技术、新型材料及军事科技等行业重点开发领域,具有极高科学价值和广阔商业前景[1￣4]。氯化锂是电解制金属锂的主要原料,它的纯度是电     

PEO与Li1.3Al0.3Ti1.7(PO4)3络合的离子导体聚合物电解质

将实验室经固相反应的精细Li1．3Al0．3Ti1．7(PO4)3盐与聚氧化乙烯(PEO)按照不同，nEO／nLi摩尔比，通过溶液浇铸法制备了固态聚合物电解质。红外光谱分析表明Li1．3Al0．3Ti1．7(PO4)3盐与PEO之间有络合产生。SEM照片显示PEO晶体外层为无定形相所包覆形成的胞状结构。经电化学阻抗(简称EIS)法测试发现聚合物电解质膜的室温阻抗谱图是由高频处一压缩的半圆和低频下一条直线组成，而高温时的阻抗谱主要为一条直线。离子电导率的测试结果得到：当nEO／nLi=16时，聚合物电解质室温下电导率约为10^-6／cm，343K时达到10^-4s／cm。离子迁移率的数据表明聚合物电解质为离子和电子共混的导体，但在聚合物电解质体系中电荷的迁移主要是由离子作为载流子导电造成的，由测试结果可得此电解质为离子导体。     

无机离子交换剂Mg1.5Mn0.5Ti0.75O4对Li 的交换选择性实验

利用共沉淀,固相反应热结晶法,合成具有尖晶石型的复合金属氧化物Mg1.5Mn0.5Ti0.75O4。具有尖晶石型结构的物质,可以插入大量的替代离子并且改变自身锂和氧的化学计量数,与此同时,还保持了结构的稳定。这种特性能够使得它们被用于离子交换研究,用来满足提取锂的需求。通过检测该复合氧化物的饱和交换能力值,分配系数值等,从而确定出该物质具体特性。实验表明,经过酸化的Mg1.5Mn0.5Ti0.75O4,其Mg2 的抽出比率能够达到72%,Mn4 和Ti4 的溶解比率低于8.2%。实验分析得出,Li 能够从无机离子交换剂Mg1.5Mn0.5Ti0.75O4中抽出以及插入,主要是归因于离子交换机理。被酸化的样品对Li 有一个10.6mmol?g-1的离子交换能力,并且对Li 还具有记忆性的离子筛性能。     

Influence of MgHPO4·3H2O and Mg3(PO4)2·8H2O on Thermal Reactions (20°-1000°C) in Solid Solutions with Al2(SO4)3·16H2O

Abstract

The following binary systems were studied: AI₂(SO₄)₃·16H₂0 - MgHPO₄·3H₂O and AI₂(SO₄)₃·16H₂O - Mg₃(P0₄)₂·8H₂0.     

Li1.3Al0.3Ti1.7(PO4)3 filler effect on (PEO)LiClO4 solid polymer electrolyte

Composite polymer electrolyte (CPE) films consisting of PEO, LiClO₄, and Li_1.3Al_0.3Ti_1.7(PO₄)₃ with fixed EO/Li = 8 but different relative compositions of the two lithium salts were prepared by the solution casting method. The CPE films were characterized using SEM, DSC, electrical impedance spectroscopy (EIS), and ion transference number measurement. It was found that the incorporation of LiClO₄ and Li_1.3Al_0.3Ti_1.7(PO₄)₃ into PEO by keeping EO/Li = 8 reduced the crystallinity of PEO from 50.34% to the range of 3.57–15.63% depending upon the relative composition of the two salts. The room temperature impedance spectra of the CPE films all exhibited a shape of depressed semicircle in the high frequency range and inclined line in the low frequency range, but the high temperature ones were mainly inclined lines. The Li⁺ ionic conductivity of the CPE films mildly increased and then decreased with increasing Li_1.3Al_0.3Ti_1.7(PO₄)₃ content, and the maximum conductivities were obtained at Li_1.3Al_0.3Ti_1.7(PO₄)₃ content of 15 wt % for all measuring temperatures, for example, 1.378 × 10^?3 S/cm at 100 °C and 1.387 × 10^?5 S/cm at 25 °C. The temperature dependence of the ionic conductivity of the CPE films follows the Vogel–Tamman–Fulcher (VTF) equation The pseudo activation energies (E_a) were rather low, 0.053–0.062 eV, indicating an easy migration of Li⁺ in the amorphous phase dominant PEO. The pre‐exponent constant A and ion transference number t_Li+ were found to have a similar variation tendency with increasing Li_1.3Al_0.3Ti_1.7(PO₄)₃ content and reached their maximums also at Li_1.3Al_0.3Ti_1.7(PO₄)₃ content of 15 wt %. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 743–751, 2005     

Li_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3,Na_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3的离子交换研究

研究了在不同温度下的NaNO3和AgNO3水溶液中Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3离子交换行为.实验表明Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3均显示出了高选择性与Na+和Ag+进行离子交换的特征,且对Ag+的选择性高于Na+.升高温度可显著提高Ag/Li和Ag/Na的交换反应速度.     

Water-stable high lithium-ion conducting Li1.4Al0.4Ge0.2Ti1.4(PO4)3-TiO2-LiCl•H2O–epoxy resin composite film with high mechanical strength as separator for Li-air batteries

Journal of Solid State Electrochemistry - Aqueous rechargeable lithium-air batteries are candidates for next-generation high energy and power density batteries. The key material of this type...     

仲钨酸盐A柱撑化合物Mg12Al6(OH)36(W7O24)·4H2O的合成及其光催化性能研究

光催化降解水中有机污染物并使之矿化为无机物的技术正在引起众多学者的关注[1～3]. 目前, 两类主要的光催化剂为半导体金属氧簇和多金属氧酸盐簇(POM). 然而, 这两类催化剂在使用过程中都存在着催化剂难以回收的缺点. 将POM嵌入层柱双氢氧化物(LDH)中制备POM柱撑化合物是固载POM的有效途径之一[4]. 均相体系中仲钨酸盐A(W7O6-24)的光化学活性已有研究, 它可使22种卤代烃完全降解和矿化[5]. 本文通过阴离子交换反应制备了水不溶性的仲钨酸盐A柱撑化合物Mg12Al6(OH)36(W7O24)*4H2O(缩为Mg2Al-W7), 所用前躯体为Mg4Al2(OH)12TA*xH2O (简写为Mg2Al-TA, TA2-= 对苯二甲酸根离子). Mg2Al-W7在非均相体系中的光化学行为通过水溶液中有机氯杀虫剂六六六(C6H6Cl6, 用HCH表示)的降解与矿化进行了研究. 据报道, 由于六六六非常稳定和难于降解, 目前农田中仍存在数以千吨计的残留的六六六, 国外文献近期仍在报道TiO2光催化降解六六六的方法[6,7]. 我们的研究表明, Mg2Al-W7对降解及矿化六六六有活性, 且催化剂易于分离回收, 并可用于再循环. 这些特点为Mg2Al-W7光催化降解水中其它有机污染物的研究与应用奠定了基础.