Synthesis and eutectic behavior of liquid crystalline copolyesters

A series of liquid crystalline copolyesters, derived from 1,4‐hydroxy‐benzoic acid (HBA), 6‐hydroxy‐2‐naphthoic acid (HNA), terephthalic acid (TA), and hydroquinone (HQ), were prepared; crystallization, melting and solid‐state structure of the copolyesters were studied by using differential scanning calorimetry (DSC) and wide‐angle x‐ray diffraction (WAXD). It was found that the variation of melting point of the copolyesters with increasing HBA mol % exhibits eutectic melting behavior at a constant mole ratio of HNA, and the extrapolated eutectic temperature decreases linearly with increasing HNA mol %. WAXD analysis of the copolyesters indicates that the d‐spacing related to three‐dimensional order increases first and then decreases with increasing HBA mol %. The increase of the d‐spacing, consistent with looser packing of chains, leads to the reduction of melting point and most likely accounts for the eutectic behavior observed. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 2171–2177, 2009     

Synthesis and characterization of fully biobased poly(propylene succinate‐ran‐propylene adipate). Analysis of the architecture‐dependent physicochemical behavior

Fully biobased aliphatic random poly(1,3‐propylene succinate‐ran‐1,3‐propylene adipate) (PPSA) copolyesters with high molar mass were synthesized with different macromolecular architectures based on various succinic acid/adipic acid (SA/AA) molar ratio, by transesterification in melt. Titanium (IV) isopropoxide was used as an effective catalyst. All synthesized copolyesters were fully characterized by different chemical and physicochemical techniques including NMR, size exclusion chromatography, FTIR, wide angle X‐ray scattering, differential scanning calorimetry, and thermogravimetric analysis. The final copolyesters molar compositions were identical to the feed ones. The different sequences based on succinate and adipate segments were randomly distributed along the chains. All the corresponding copolyesters showed an excellent thermal stability with a degradation onset temperature higher than 290 °C, which increased with the adipate content. According to their compositions and architectures, PPSA copolyesters can exhibit or not a crystalline phase, at room temperature. T_g of copolyesters decreased with the adipate content due to the decrease in the chains mobility, following the Gordon–Taylor relation. PPSA showed a pseudo eutectic melting behavior characteristic of an isodimorphic character. Finally, PPSA copolyesters were not able to crystallize during the cooling or the second heating run, due to the 1,3‐propanediol chemical structure, which led to amorphous materials with the exception of the polyester based solely on AA. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55, 2738–2748     

Effects of comonomer sequential structure on thermal and crystallization behaviors of biodegradable poly(butylene succinate‐co‐butylene terephthalate)s

In this work, new investigations on the effect of comonomer sequential structure on the thermal and crystallization behaviors and biodegradability have been implemented for the biodegradable poly(butylene succinate‐co‐butylene terephthalate) (PBST) as well as aliphatic poly(butylene succinate) (PBS). At first, these copolyesters were efficiently synthesized from dimethyl succinate and/or dimethyl terephthalate and 1,4‐butanediol via condensation polymerization in bulk. Subsequently, their molecular weights and macromolecular chain structures were analyzed by gel permeation chromatography (GPC) and nuclear magnetic resonance (NMR) spectroscopy. By means of differential scanning calorimeter (DSC) and wide‐angle X‐ray diffractometer (WAXD), thermal and crystallization behaviors of these synthesized aromatic–aliphatic copolyesters were further explored. It was demonstrated that the synthesized copolyesters were revealed to have random comonomer sequential structures with thermal and crystallization properties strongly depending on their comonomer molar compositions, and that crystal lattice structures of the new crystallizable copolyesters shifted from the monoclinic crystal of semicrystalline PBS to triclinic lattice of the poly(butylene terephthalate) (PBT) with increasing the terephthalate comonomer composition, and the minor comonomer components were suggested to be trapped in the crystallizable component domains as defects. In addition, the enzymatic degradability was also characterized for the copolyesters film samples. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1635–1644, 2006     

New polymer syntheses. 102. Aspirin‐modified LC polyesters based on PET and 4‐hydroxybenzoic acid

Four series of liquid‐crystalline copolyesters were prepared by the transesterification of poly(ethylene terephthalate) (PET) with 4‐acetoxybenzoic acid (4‐ABA) or mixtures of 4‐ABA and acetylsalicylic acid (ASA). Two series consisted of 30 mol % PET, and the other two series consisted of 40 mol % PET. The molar ratio of 4‐HBA and ASA was varied in all four series from 0 to 25 mol %. One 30% PET series and one 40% PET series were prepared with the addition of acetic acid, which caused a more perfect randomization of the sequence but yielded slightly lower molecular weights. The incorporation of ASA reduced the crystallinity, which vanished completely at a salicylic acid (SA) content greater than 10 mol %. SA also reduced the stability of the nematic phase, but all the copolyesters were thermotropic up to a 20 mol % SA content. Furthermore, the molecular weights decreased with the increasing incorporation of ASA. Despite this negative trend, the melt viscosity and the storage and loss moduli passed a maximum between 5 and 10% SA. Obviously, the incorporation of SA favored the formation of entanglements. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 2013–2022, 2000     

Development of amorphous copolyesters based on 1,4‐cyclohexanedimethanol

The modification of poly(ethylene terephthalate) with 1,4‐cyclohexanedimethanol and the modification of poly(1,4‐cyclohexylenedimethylene terephthalate) with ethylene glycol or isophthalic acid retard the crystallization of the copolyester backbone, and over a wide range of comonomer concentrations, very slowly crystallizing, essentially amorphous copolyesters are formed. These amorphous copolyesters possess attractive physical properties such as toughness, low color, and chemical resistance, and since their first commercial introduction in 1977, these copolyesters have become the basis of a large and growing plastics business for Eastman Chemical Co. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5847–5852, 2004     

Poly(ethylene terephthalate) copolymers containing 5‐nitroisophthalic units. I. Synthesis and characterization

Poly(ethylene terephthalate‐co‐5‐nitroisophthalate) copolymers, abbreviated as PETNI, were synthesized via a two‐step melt copolycondensation of bis(2‐hydroxyethyl) terephthalate and bis(2‐hydroxyethyl) 5‐nitroisophthalate mixtures with molar ratios of these two comonomers varying from 95/5 to 50/50. Polymerization reactions were carried out at temperatures between 200 and 270 °C in the presence of tetrabutyl titanate as a catalyst. The copolyesters were characterized by solution viscosity, GPC, FTIR, and NMR spectroscopy. They were found to be random copolymers and to have a comonomer composition in accordance with that used in the corresponding feed. The copolyesters became less crystalline and showed a steady decay in the melting temperature as the content in 5‐nitroisophthalic units increased. They all showed glass‐transition temperatures superior to that of PET with the maximum value at 85 °C being observed for the 50/50 composition. PETNI copolyesters appeared stable up to 300 °C and thermal degradation was found to occur in two well‐differentiated steps. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1934–1942, 2000     

Synthesis,characterization, and enzymatic degradation of network aliphatic copolyesters

Network copolyesters were prepared from glycerol (Yg) and sebacic acid (10) with 10–90 mol % of either succinic acid (4), 1,12-dodecanedicarboxylic acid (14), 1,18-octadecanedicarboxylic acid (20), or terephthalic acid (T). Prepolymers prepared by melt-polycondensation were cast from dimethylformamide solution and postpolymerized at 230–250°C for various periods of time to form a network. The resultant films were transparent, flexible, and insoluble in organic solvents. The network copolyesters obtained were characterized by infrared absorption spectra, wide angle X-ray diffraction analysis, density measurement, thermomechanical analysis, differential scanning calorimetry, and tensile test. The enzymatic degradation was estimated by weight loss of the network copolyester films in a buffer solution with Rhizopus delemar lipase at 37°C. The weight loss due to the enzymatic degradation was decreased with increasing comonomer content, and the copolyesters with Yg4, Yg20 and YgT more than 50 mol % were not degraded by lipase enzyme at all. On the contrary, Yg-10/14 films were degraded appreciably over whole range of comonomer composition. With increasing comonomer content, the heat distortion temperature increased gradually, while the tensile strength and Young's modulus were not changed much. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 2005–2011, 1999     

New polymer syntheses. CIX. Biodegradable,alternating copolyesters of terephthalic acid,aliphatic dicarboxylic acids,and alkane diols

Copolyesters with an alternating sequence of terephthalic acid and aliphatic dicarboxylic acids were prepared with three different methods. First, dicarboxylic acid dichlorides were reacted with bis(2‐hydroxyethyl)terephthalate (BHET) in refluxing 1,2‐dichlorobenzene. Second, the same monomers were polycondensed at 0–20 °C in the presence of pyridine. Third, dicarboxylic acid dichlorides and silylated BHET were polycondensed in bulk. Only this third method gave satisfactory molecular weights. Matrix‐assisted laser desorption/ionization time‐of‐flight mass spectrometry revealed that the copolyesters prepared by the pyridine and silyl methods might have contained considerable fractions of cyclic oligoesters and polyesters despite the absence of transesterification and backbiting processes. The alternating sequences and thermal properties were characterized with ¹H NMR spectroscopy and differential scanning calorimetry measurements, respectively. In agreement with the alternating sequence, all copolyesters proved to be crystalline, but the crystallization was extremely slow [slower than that of poly(ethylene terephthalate)]. A second series of alternating copolyesters was prepared by the polycondensation of silylated bis(4‐hydroxybut‐ yl)terephthalate with various aliphatic dicarboxylic acid dichlorides. The resulting copolyesters showed significantly higher rates of crystallization, and the melting temperatures were higher than those of the BHET‐based copolyesters. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3371–3382, 2001     

Crystallization and melting behavior of liquid crystalline copolyesters based on poly(ethylene terephthalate)

A series of copolyesters were prepared by the incorporation of p‐hydroxybenzoic acid (HBA), hydroquinone (HQ), and terephthalic acid (TA) into poly(ethylene terephthalate) (PET). On the basis of viscosity measurements, high molar mass copolyesters were obtained in the syntheses, and ¹H‐NMR analyses indicated the total insertion of comonomers. They exhibit nematic phase above melting temperature, as observed by polarized light microscope (PLM). Their crystallization and melting behaviors were also studied by differential scanning calorimetry (DSC) and wide angle X‐ray diffraction (WAXD). It was found that these copolyesters are more crystalline than copolyesters prepared from PET and HBA. Introduction of HQ/TA disrupts longer rigid‐rod sequences formed by HBA, and thus enhances molecular motion and increases crystallization rate and crystallinity. Isothermal crystallization at solid phase polymerization conditions (up to 24 h at 200°C) resulted in increased copolymer randomness (by NMR) and higher melting point, the latter attributed to structural annealing. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 369–377, 1999     

Poly(ethylene terephthalate) copolyesters derived from (2S,3S)‐2,3‐dimethoxy‐1,4‐butanediol

Novel poly(ethylene terephthalate) (PET) copolyesters, abbreviated PEDMBT, containing optically active (2S,3S)‐2,3‐dimethoxy‐1,4‐butanediol (DMBD) as the second comonomer were investigated. Copolymers with ethylene glycol to DMBD ratios between 95/5 and 50/50 as well as the two parent homopolymers, PET and PDMBT, were prepared by a two‐step melt polycondensation. The resulting copolymers were found to approximately have the composition of the polymerization reaction feed and a random microstructure. Polymer intrinsic viscosities varied from 0.4 to 0.6 dL g^?1 with weight‐average molecular weights ranging from 16,000 to 44,000. PEDMBT copolyesters were distinguished in being much more soluble than PET and showing an increasing affinity for water with the content in dimethoxy groups. According to the asymmetric constitution of DMBD, they displayed optical activity in solution. Both melting and glass‐transition temperatures of the copolyesters were observed to steadily decrease with the content in DMBD. PEDMBTs were found to be crystalline for contents in DMBD up to 30 mol %. Both powder and fiber X‐ray diffraction revealed that the same crystalline structure is shared by PET and the crystalline copolyesters. The homopolyester PDMBT resulted in becoming a polymer with a crystallinity comparable to PET but with a significantly different crystalline structure. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3250–3262, 2001     

Ethylene copolymerization with cyclic dienes using rac‐Et[Ind]2ZrCl2–Methylaluminoxane

The effect of the copolymerization temperature and amount of comonomer in the copolymerization of ethylene with 1,3‐cyclopentadiene, dicyclopentadiene, and 4‐vinyl‐1‐cyclohexene and the rac‐Et[Ind]₂ZrCl₂–methylaluminoxane metallocene system was studied. The amount of comonomer present in the reaction media influenced the catalytic activity. Dicyclopentadiene was the most reactive comonomer among the cyclic dienes studied. In general, copolymers synthesized at 60 °C showed higher catalytic activities. Ethylene–dicyclopentadiene copolymers with high comonomer contents (>9%) did not show melting temperatures. 1,3‐Cyclopentadiene dimerized into dicyclopentadiene during the copolymerization, giving a terpolymer of ethylene, cyclopentadiene, and dicyclopentadiene. A complete characterization of the products was carried out with ¹H NMR, ¹³C NMR, heteronuclear chemical shift correlation, differential scanning calorimetry, and gel permeation chromatography. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 471–485, 2002; DOI 10.1002/pola.10133     

Polydispersity of ethylene sequence length in metallocene ethylene/α‐olefin copolymers. II. Influence on crystallization and melting behavior

In this work, crystallization and melting behavior of metallocene ethylene/α‐olefin copolymers were investigated by differential scanning calorimetry (DSC) and atomic force microscopy (AFM). The results indicated that the crystallization and melting temperatures for all the samples were directly related to the long ethylene sequences instead of the average sequence length (ASL), whereas the crystallization enthalpy and crystallinity were directly related to ASL, that is, both parameters decreased with a decreasing ASL. Multiple melting peaks were analyzed by thermal analysis. Three phenomena contributed to the multiple melting behaviors after isothermal crystallization, that is, the melting of crystals formed during quenching, the melting‐recrystallization process, and the coexistence of different crystal morphologies. Two types of crystal morphologies could coexist in samples having a high comonomer content after isothermal crystallization. They were the chain‐folded lamellae formed by long ethylene sequences and the bundlelike crystals formed by short ethylene sequences. The coexistence phenomenon was further proved by the AFM morphological observation. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 822–830, 2002     

One‐step synthesis of polycarbonates bearing pendant carboxyl groups by lipase‐catalyzed ring‐opening polymerization

The ring‐opening polymerization of a monomer containing a free carboxylic acid group is reported for the first time. The monomer, 5‐methyl‐5‐carboxyl‐1,3‐dioxan‐2‐one (MCC), was copolymerized with trimethylene carbonate (TMC) in an enzymatic ring‐opening polymerization conducted in bulk at 80 °C. The low‐melting TMC comonomer also solubilized the high‐melting MCC monomer, allowing for solvent‐free polymerizations. Six commercially available lipases were screened, and Candida antarctica lipase‐B (Novozym‐435) and Pseudomonas cepacia lipase were selected to catalyze the copolymerization because of their higher monomer conversions. Higher molecular weight polymers (weight‐average molecular weight = 7800–9200) were prepared when Novozym‐435 was used, with less MCC incorporated into the copolymer than used in the monomer feed. However, Pseudomonas cepacia lipase showed good agreement between the molar feed ratios and the molar composition, but the molecular weights (weight‐average molecular weight = 3600–4800) were lower than those obtained when Novozym‐435 was used. ¹³C NMR spectral data were used for microstructural analysis, which suggested the formation of random, linear, and pendant carboxylic acid groups containing polycarbonates with hydroxyl groups at both chain ends. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1267–1274, 2002     

Partially renewable copolyesters prepared from acetalized d‐glucitol by solid‐state modification of poly(butylene terephthalate)

The backbone of poly(butylene terephthalate) (PBT) was modified with 2,4:3,5‐di‐O‐methylene‐D ‐glucitol (Glux) using solid‐state modification (SSM). The obtained copolyesters proved to have a non‐random overall chemical microstructure. The thermal properties of these semicrystalline, block‐like, Glux‐based materials were extraordinary, showing higher melting points, and glass transition temperatures compared with other sugar‐based copolyesters prepared by SSM. These remarkable thermal properties were a direct result of the inherently rigid structure of Glux and the relatively slow randomization of the block‐like chemical microstructure of the Glux‐based copolyesters in the melt. SSM proved to be a versatile tool for preparing partially biobased copolyesters with superior thermal properties. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 164–177     

Morphology of poly(butylene terephthalate)–poly(ethylene terephthalate‐co‐isophthalate‐co‐sebacate) segmented copolyesters

Segmented copolyesters, namely, poly(butylene terephthalate)–poly(ethylene terephthalate‐co‐isophthalate‐co‐sebacate) (PBT‐PETIS), were synthesized with the melting transesterification processing in vacuo condition involving bulk polyester produced on a large scale (PBT) and ternary amorphous random copolyester (PETIS). Investigations on the morphology of segmented copolyesters were undertaken. The two‐phase morphology model was confirmed by transmission electron microscopy and dynamic mechanical thermal analysis. One of the phases was composed of crystallizable PBT, and the other was a homogeneous mixture of PETIS and noncrystallizable PBT. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 2257–2263, 2003     

Copolymerization of propylene with higher α‐olefins in the presence of the syndiospecific catalyst i‐Pr(Cp)(9‐Flu)ZrCl2/MAO

The catalyst system i‐Pr(Cp)(9‐Flu)ZrCl₂/methylaluminoxane was used for the synthesis of random syndiotactic copolymers of propylene with 1‐hexene, 1‐dodecene, and 1‐octadecene as comonomers. An investigation of the microstructure by ¹³C NMR spectroscopy revealed that the stereoregularity of the copolymers decreased because of an increase in skipped insertions in the presence of the higher 1‐olefin. The melting temperature of the copolymers, as measured by differential scanning calorimetry (DSC), decreased linearly with increasing comonomer content independently of the comonomer nature. During the DSC heating cycle, an exothermic peak indicating a crystallization process was observed. The decrease in the crystallization temperature with higher 1‐olefin content, measured by crystallization analysis fractionation, indicated a small but significant dependence on the nature of the comonomer. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 128–140, 2002     

Diels–Alder modification of poly(ethylene terephthalate‐co‐anthracene‐2,6‐carboxylate) with N‐substituted maleimides

Dimethyl 2,6‐anthracene dicarboxylate is used as a comonomer in the synthesis of functional copolymers that are subject to modification with Diels–Alder reactions. The formation of poly(ethylene terephthalate‐co‐2,6‐anthracenate), containing less than 20 mol % of the anthracene‐2,6‐dicarboxylate structural units, provides materials that are tractable and soluble. The anthracene units of the copolymers undergo Diels–Alder reactions with N‐substituted maleimides. The grafting of N‐alkylmaleimides affords soluble, hydrophobic polymers, whereas grafting with maleimide‐terminated poly(ethylene glycol) affords hydrophilic polymers. Because this reaction proceeds below the melting point of the copolymers, the procedure can be applied to thin films, whereby the surface properties are modified. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3256–3263, 2002     

Ethylene/1‐hexene copolymers synthesized with a single‐site catalyst: Crystallization analysis fractionation,modeling, and reactivity ratio estimation

A series of poly(ethylene‐co‐1‐hexene) samples made with rac‐ethylene bis(indenyl)zirconium dichloride/methylaluminoxane were analyzed by crystallization analysis fractionation (CRYSTAF). The nine samples had comonomer contents of 0–4.2 mol % 1‐hexene with a narrow range of molecular weights (34,000–39,000 g/mol). Because all the copolymer samples had narrow, unimodal chemical composition distributions, they were ideal as calibration standards for CRYSTAF. A linear calibration curve was constructed relating the peak crystallization temperature from CRYSTAF operated at a cooling rate of 0.1 °C/min and the comonomer content as determined by ¹³C NMR. Reactivity ratios for ethylene and 1‐hexene were estimated by the fitting of reactant liquid‐phase compositional data to the Mayo–Lewis equation. It was found that a value of the 1‐hexene reactivity ratio could not be unequivocally determined from the set of samples analyzed because the range of comonomer incorporation was too narrow. Stockmayer's bivariate distribution was used to model the fractionation process in CRYSTAF, and although a good fit to experimental CRYSTAF profiles was attained, the model did not fully describe the underlying crystallization phenomena. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2595–2611, 2002     

Cocrystallization in blends of random tetrafluoroethylene fluorinated copolymers: The effect of the chain structure and crystallization conditions

The possibility of the cocrystallization of random fluorinated tetrafluoroethylene copolymers was investigated with differential scanning calorimetry and wide‐angle X‐ray scattering. In particular, mixtures composed of poly(tetrafluoroethylene)‐co‐(hexafluoropropylene) containing 8 or 1 mol % comonomer or poly(tetrafluoroethylene)‐co‐perfluoromethylvinylether (2–10 mol % comonomer) were examined. The extent of cocrystallization was determined by the difference in the comonomer content, being higher when the difference was lower, and it was favored when quenching from the melt state was adopted. Nevertheless, a key to determining the extent of cocrystallization was the behavior of counits with respect to inclusion or exclusion from the crystal lattice: when the components were different with respect to this behavior, they were not likely to be miscible in the crystal state even if the difference in the comonomer content was low. Moreover, the similarity in the crystallization rates between the components played an important role: the cocrystallization decreased as the difference in the crystallization rate increased until, when the difference became high enough, the blend became immiscible. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1477–1489, 2002     

Application of SSA thermal fractionation and X‐ray diffraction to elucidate comonomer inclusion or exclusion from the crystalline phases in poly(butylene succinate‐ran‐butylene azelate) random copolymers

Poly(butylene succinate‐ran‐butylene azelate) random copolyesters were thermally fractionated by successive self‐nucleation and annealing (SSA). The samples before and after SSA were analyzed by differential scanning calorimetry (DSC) and X‐ray diffraction (WAXS and SAXS). WAXS results indicate that a small degree of comonomer inclusion is present in the crystalline phases that are formed in the copolymers depending on composition: a PBS‐like unit cell or/and a PBAz‐like unit cell, thus confirming the isodimorphic behavior of the samples. SSA on the other hand demonstrated that the degree of comonomer exclusion during crystallization is far larger than comonomer inclusion, as judged by the increase in fractionation degree with compositions leading to the pseudo‐eutectic point. Furthermore, WAXS, SAXS, and SSA results show that the isodimorphic behavior is not highly dependent on kinetic factors, as the degree of comonomer inclusion or exclusion in the samples was not significantly altered by SSA thermal fractionation, a thermal treatment that promotes annealing and molecular segregation of defects to the amorphous regions of the material. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 2346–2358