Glass-forming ability and crystallization of bulk metallic glass (HfxZr1−x)52.5Cu17.9Ni14.6Al10Ti5

We have produced a series of bulk metallic glasses of composition (Hf_xZr_1−x)_52.5Cu_17.9Ni_14.6Al₁₀Ti₅ (with x=0-1) by an arc melting/suction casting method. The density of these alloys increases by nearly 67% with increasing Hf content from 6.65 g/cm³ (x=0) to 11.09 g/cm³ (x=1). Over the same composition range the glass-forming ability decreases, as demonstrated by the size of the largest amorphous ingots that can be cast without crystallization. Although both the glass transition temperature and the melting temperature increase linearly with increasing Hf content, the reduced glass transition temperature (T_g/T_m) decreases, from 0.64 (x=0) to 0.62 (x=1), which suggests that the `confusion principle' correlating increased glass-forming ability with increased number of components, does not apply in this case due to the chemical similarity between Zr and Hf. A different crystallization behavior is observed for Zr-based and Hf-based glasses. The final crystalline phases are CuZr₂ and Zr₂Ni for Zr-based alloys, and Al₁₆Hf₆Ni₇ and CuHf₂ for Hf-based alloys.     

Non-isothermal crystallization kinetics study on new amorphous Ga20Sb5S75 and Ga20Sb40S40 chalcogenide glasses

Bulk glasses of the system Ga₂₀Sb_xS_80−x (x = 5 and 40) were prepared for the first time by the known melt quenching technique. Non-isothermal differential scanning calorimetric (DSC) measurements of as-quenched Ga₂₀Sb_xS_80−x (x = 5 and 40) chalcogenide glasses reveal that the characteristic temperatures e.g. the glass transition temperature (T_g), the temperature corresponding to the maximum crystallization rate (T_p) recorded in the temperature range 400-650 K for x = 5 and 480-660 K for x = 40 are strongly dependent on heating rate and Sb content. Upon heating, these glasses show a single glass transition temperature (T_g) and double crystallization temperatures (T_p1 and T_p2) for x = 5 which overlapped and appear as a single crystallization peak (T_p) for x = 40. The activation energies of crystallization E_c were evaluated by three different methods. The crystallization data were examined in terms of recent analysis developed for non-isothermal conditions. The crystalline phases resulting from (DSC) have been identified using X-ray diffraction.     

Elasticity, thermal expansion and compressive behavior of Mg65Cu25Tb10 bulk metallic glass

The existence of special covalently bonded short-range ordering structures in a Mg₆₅Cu₂₅Tb₁₀ bulk metallic glass (BMG) is confirmed by thermal expansion and compression behavior. Under ambient conditions the linear thermal expansion coefficient obtained is almost constant in the glassy state with a value of 4.0 × 10⁻⁵ K⁻¹. By fitting the static equation of state at room temperature under ambient conditions we find the value for bulk modulus B of 48.7 GPa, which is in excellent agreement with the experimental study by pulse-echo techniques of 44.7 GPa. Unlike many bulk metallic glasses, such as Zr- and Pd-based, which bulk modulus is much larger than 100 GPa, the value B of Mg₆₅Cu₂₅Tb₁₀ BMG falls into the range of SiO₂ and fluorozirconate glass ZBLAN. Moreover, the elastic constant of the Mg₆₅Cu₂₅Tb₁₀ BMG is almost the same as those of ZBLAN. No evidence for the high-pressure phase transitions of the Mg₆₅Cu₂₅Tb₁₀ BMG has been found up to 31.19 GPa at room temperature.     

Crystallization of amorphous Ni35Zr65 and Fe40Ni40P14B6 under proton irradiation

Two amorphous alloys, Ni₃₅Zr₆₅ and Fe₄₀Ni₄₀P₁₄B₆, were irradiated using 400 keV protons at several temperatures below the crystallization temperature, T_x, to peak doses in the neighborhood of 3.5 to 4.5 dpa. Irradiation at 250°C resulted in the crystallization of both alloys, which were examined by transmission electron microscopy of samples electrolytically polished to various distances from the irradiated surface to study the effect of dose. Samples masked from the proton beam remained amorphous during irradiation. In the Ni₃₅Zr₆₅ alloy crystallization of the equilibrium phases propagated throughout the entire sample, while the in the Fe₄₀Ni₄₀P₁₄B₆ alloy crystallization was observed only in those parts of the samples lying within the proton range. Neither alloy crystallized during irradiation at 100°C. In both these alloys the amorphous phase is therefore evidently stable at irradiation temperatures below approximately 0.6 T_x. An examination of the literature on irradiation damage of binary alloys and intermetallic compounds suggests that there is a tendency for initially amorphous alloys to remain amorphous at irradiation temperatures, T_irr < 0.3 T_L, where T_L (≈T_x) is the “melting” temperature (either a eutectic, peritectic or congruent melting temperature). Also, these same alloys, even when they are initially crystalline, transform to the amorphous state during irradiation at T < 0.3 T_L. Some other crystalline alloys have also been shown to transform to the amorphous state at T_irr < 0.3 T_L even though they have never been prepared in this condition by rapid quenching techniques. The temperature 0.3 T_L appears to be a lower limit, however, since the crystalline to amorphous transformation occurs in many of these alloys at temperatures greater than 0.3 T_L. It is suggested, by analogy with results on void formation in irradiated metals, that this low temperature limit is related to the low mobility of vacancies in these materials, although the mechanism of crystallization, or conversely amorphization, is not fully understood.     

Combined in-situ SAXS/WAXS and HRTEM study on crystallization of (Cu60Co40)1 − xZrx metallic glasses

CuZr as well as CoZr are well known metallic glass-formers in a wide compositional range. Since the binary Cu-Co system exhibits a metastable liquid-liquid miscibility gap, i.e. Cu and Co tend to separate from each other, the ternary Cu-Co-Zr system is a promising candidate to form phase separated glass-glass composites. In this work (Cu₆₀Co₄₀)_1 − xZr_x metallic glasses with relatively low Zr contents of x = 37 and x = 32 were prepared by melt spinning and investigated by in-situ small-angle and wide-angle X-ray scattering (SAXS/WAXS) and differential scanning calorimetry (DSC). Certain heat treated samples were additionally investigated by high-resolution transmission electron microscopy (HRTEM). Even for x = 32 there are no indications for any kind of phase separation in the as-quenched state within experimental resolution, i.e. the critical temperature T_c for a liquid-liquid phase separation has already decreased from 1556 K for binary Cu₆₀Co₄₀ to a temperature below the glass transition temperature T_g = 762(5)K found for (Cu₆₀Co₄₀)₆₈Zr₃₂. Combined in-situ SAXS/WAXS and HRTEM investigations reveal that thermal annealing also does not induce an amorphous-amorphous phase separation. Instead the formation of nano crystallites of a so far unknown Cu-rich/Zr-poor phase with relatively low activation energy for crystallization E_a = 116(7) kJ/mol at temperatures far below the crystallization temperature deduced from DSC measurements is observed.     

Potentiodynamic polarization studies on amorphous Zr46.75Ti8.25Cu7.5Ni10Be27.5, Zr65Cu17.5Ni10Al7.5, Zr67Ni33 and Ti60Ni40 in aqueous HNO3 solutions

Potentiodynamic polarization studies were carried out on virgin specimens of Zr-based bulk amorphous alloys Zr_46.75Ti_8.25Cu_7.5Ni₁₀Be_27.5 and Zr₆₅Cu_17.5Ni₁₀Al_7.5, and conventional-type binary amorphous alloys Zr₆₇Ni₃₃ and Ti₆₀Ni₄₀ in solutions of 0.2 M, 0.5 M and 1.0 M HNO₃ at room temperature. The values of the corrosion current density (I_corr) for the bulk amorphous alloy Zr_46.75Ti_8.25Cu_7.5Ni₁₀Be_27.5 were found to be comparable with those of Zr₆₅Cu_17.5Ni₁₀Al_7.5 in 0.2 M and 0.5 M HNO₃, but the value of I_corr for the former was almost three times more than that of the latter in 1.0 M HNO₃. In the case of conventional binary amorphous alloys, Ti₆₀Ni₄₀ showed lower value of I_corr as compared to Zr₆₇Ni₃₃ in 0.5 M and 1.0 M HNO₃ and a comparable value of I_corr in 0.2 M HNO₃. In general, the binary Ti₆₀Ni₄₀ displayed the best corrosion resistance among all the alloys in all the cases and the corrosion current density (I_corr) for all the alloys was found to increase with the increasing concentration of nitric acid. It is noticed that the bulk amorphous alloys do not possess superior corrosion resistance as compared to conventional binary amorphous alloys in aqueous HNO₃ solutions. The observed differences in their corrosion behavior are attributed to different alloy constituents and composition of the alloys investigated.     

Crystallization kinetics of Fe73.5−xMnxCu1Nb3Si13.5B9 (x = 0, 1, 3, 5, 7) amorphous alloys

In this study, we have investigated the effect of substituting Mn for Fe on the crystallization kinetics of amorphous Fe_73.5−xMn_xCu₁Nb₃Si_13.5B₉ (x = 1, 3, 5, 7) alloys. The samples were annealed at 550 °C and 600 °C for 1 h under an argon atmosphere. The X-ray diffraction analyses showed only a crystalline peak belonging to the α-Fe(Si) phase, with the grain size ranging from 12.2 nm for x = 0 to 16.7 nm for x = 7. The activation energies of the alloys were calculated using Kissinger, Ozawa and Augis-Bennett models based on differential thermal analysis data. The Avrami exponent n was calculated from the Johnson-Mehl-Avrami equation. The activation energy increased up to x = 3, then decreased with increasing Mn content. The values of the Avrami exponent showed that the crystallization is typical diffusion-controlled three-dimensional growth at a constant nucleation rate.     

Influence of TM and RE elements on glass formation of the ternary Al-TM-RE systems

The effects of TM and RE elements on glass formation ability (GFA) of the Al-TM-RE systems are studied systematically. The TM elements show distinct differences: critical sizes of the Al-TM-Ce systems are in the order of Ni > Co > Fe > Cu. However, the RE elements show similar effect on glass formation. These results are discussed in terms of the GFA-related factors, i.e., reduced glass transition temperature (T_rg = T_g (T_x)/T_L, where T_g, T_x and T_L are the glass transition temperature, onset crystallization temperature and liquidus temperature, respectively) and the mixing enthalpy ΔH_Al-TM. A new parameter of T_L − T_g (T_x) is potentially proposed and used to evaluate the GFA of the Al-based alloys, as well as bulk glass-formers.     

Effect of carbon on the microstructural evolution of Zr66.7−xNi33.3Cx (x = 0, 1, 3) alloys during mechanical alloying

In the present paper, the effect of carbon on the microstructural evolution of Zr_66.7−xNi_33.3C_x (x = 0, 1, 3) alloys during mechanical alloying has been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that these three alloys undergo similar amorphization and crystallization processes, and the final milling product is a metastable fcc-Zr_66.7−xNi_33.3C_x phase. The carbon addition can shorten the milling time for the complete amorphization reaction and enhance the stability of the formed amorphous alloy, which can suppress the mechanically induced amorphous-crystalline phase transformation with further increasing milling time.     

Effects of Sn addition on the glass forming ability and crystallization behavior in Ni-Zr-Ti-Si alloys

The effect of Sn substitution for Si on the glass forming ability (GFA) and crystallization behavior has been studied in Ni₅₉Zr₂₀Ti₁₆Si_5 − xSn_x (x=0, 3, 5) alloys. A bulk amorphous Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ alloy with diameter up to 3 mm can be fabricated by injection casting. Partial substitution of Si by Sn in Ni₅₉Zr₂₀Ti₆Si_5 − xSn_x alloys improves the glass forming ability. The improved GFA of the Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ alloy is can be explained based on the lowering of liquidus temperature. The crystallization sequence becomes completely different with addition of Sn. The amorphous Ni₅₉Zr₂₀Ti₁₆Si₅ alloy crystallizes via precipitation of only a cubic NiTi phase in the first crystallization step, whereas the amorphous Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ alloy crystallizes via simultaneous precipitation of orthorhombic Ni₁₀(Zr,Ti)₇ and cubic NiTi phases. Addition of Sn in the Ni₅₉Zr₂₀Ti₁₆Si₅ alloy suppresses the formation of the primary cubic NiTi phase. The bulk amorphous Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ alloy exhibits high compressive fracture strength of about 2.7 GPa with a plastic strain of about 2%.     

Boron content dependance of magnetoimpedance in Fe91−xZr5BxNb4 alloys

A systematic investigation of the influence of B content on the magnetoimpedance (MI) effect in melt-spun Fe_91−xZr₅B_xNb₄ (FZBN, 0 ? x ? 30) ribbons has been performed within a frequency range, f ∼ 310-1110 kHz and under a varying dc magnetic field (H_dc) up to 70 Oe. The MI effect is not observed in the sample with x ? 5 but within the range 8 ? x ? 30. A distinct MI effect has been observed with a maximum change of 180% at around 1.1 MHz in the sample with x = 20, coincident with a saturation magnetic field of 66 Oe and a field sensitivity of about 7%/Oe. Magnetic measurements reveal that the MI effect and B content dependence of the effect are closely related to coercivity of the FZBN alloy series, except for the sample with 20 at.%. The drastic MI ratio observed in the sample with x = 20 is ascribed to its special microstructure. The mechanism of the MI effect in FZBN alloys and of the significant MI value appearing at a B content of x = 20 is discussed in this paper.     

Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti₄₀Cu₄₀Zr₁₀Ni₁₀ alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples. The 2 mm single glassy rod sample exhibited a large supercooled liquid region ΔT_x = 58 K and γ = T_x/(T_g + T_l) is 0.390, which indicated that the alloy possessed a good glass-forming ability. The bulk samples also exhibited good mechanical properties. The 2 mm rod sample showed the highest yield strength of about 2086 MPa. The 3 mm rod sample not only showed high yield strength of about 2000 MPa, but also enhanced plastic strain of about 0.71%.     

Glass formation and crystallization behavior in Mg65Cu25Y10−xGdx (x=0, 5 and 10) alloys

The glass forming ability and crystallization behavior of Mg₆₅Cu₂₅Y_10−xGd_x (x=0, 5 and 10) alloys have been investigated. The glass forming ability (GFA) is significantly improved when Y in Mg₆₅Cu₂₅Y₁₀ is substituted with Gd. Ternary Mg₆₅Cu₂₅Gd₁₀ bulk metallic glass (BMG) with diameter of at least 8 mm was successfully fabricated by conventional Cu-mold casting method in air atmosphere. Mg₂(Y, Gd) is the first competing crystalline phase against the glass formation in the Mg₆₅Cu₂₅Y_10−xGd_x (x=0, 5) alloys, while Mg₂Cu and Cu₂Gd are the competing crystalline phases in the Mg₆₅Cu₂₅Gd₁₀ alloy. Therefore, the suppression of the formation of Mg₂(Y, Gd) during cooling from the liquid improves the GFA significantly.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Thermal and some physical properties of glasses in the La2O3−CaO−B2O3 ternary system

Glasses in the La₂O₃−CaO−B₂O₃ ternary system were studied. The glass forming range as determined by the appearance of the annealed cast was found to match previously published findings. Clear glasses were formed in the composition range of 5.7−19.1 mol% La₂O₃ with constant B₂O₃ content of 71.4 mol%, and in glasses of constant La₂O₃:CaO ratio of 1:4 with B₂O₃ content in the range of 71.4-55.0 mol%. The non-linear optical crystalline phase La₂Ca₂B₁₀O₁₉ was crystallized from the clear glasses after heat treatments, as determined by powder XRD. Two types of the LaBO₃ crystalline phases were detected in the partially and the fully crystallized glass compositions outside the glass forming range. Data are reported for the glass transition temperature (T_g), dilatometric softening point (T_d), linear coefficient of expansion (α), onset crystallization temperature (T_x), exothermal peak temperature (T_P), density (ρ) and index of refraction (n_D) in the clear glasses.     

Electronegativity difference, atomic size parameter and widths of supercooled liquid regions of Sb2S3-As2S3-Sb2Te3 glasses

Electronegativity difference Δ_x, atomic size parameter δ and width of supercooled liquid region (ΔT_x = T_x − T_g, where T_x is the onset crystallization temperature and T_g the glass transition temperature) are analysed for glasses of the ternary system Sb₂S₃-As₂S₃-Sb₂Te₃ as a function of arsenic atomic percentage.Correlation is investigated between the two bonds parameters (Δ_x and δ) and the width of supercooled liquid region ΔT_x (which is generally reliable in estimating the stability against the crystallization of the glasses). It is found that this width of supercooled liquid region of the glasses in Sb₂S₃-As₂S₃-Sb₂Te₃ system depends on electronegativity difference and atomic size parameter.     

Crystallization processes in amorphous Zr54Cu46 alloy

The crystallization of amorphous Zr₅₄Cu₄₆ alloy was investigated by using X-ray diffraction (XRD), differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) techniques. The experimental results show that an endothermic peak in DSC traces for amorphous Zr₅₄Cu₄₆ alloy exists at about 1006 K, indicating following eutectoid reaction occurs, namely, Cu₁₀Zr₇+CuZr₂↔CuZr in amorphous Zr₅₄Cu₄₆ alloy during heating. With increasing the heating rate, the glass transition temperature T_g and onset crystallization temperature T_x of amorphous Zr₅₄Cu₄₆ alloy increase in parallel, and the supercooled liquid region ΔT_x (=T_x−T_g) holds almost constant with an average value of 44 K. Both XRD and TEM results prove that Cu₁₀Zr₇ and CuZr₂ are main crystallization products for amorphous Zr₅₄Cu₄₆ alloy under continuous heating conditions. No CuZr phase is identified because of its small precipitation amount. Finally, the crystallization processes of amorphous Zr₅₄Cu₄₆ alloy were summarized.     

Structural transformation on Se0.8Te0.2 chalcogenide glass

Using X-ray diffraction and differential scanning calorimetry (DSC), the structure and the crystallization mechanism of Se_0.8Te_0.2 chalcogenide glass has been studied. The structure of the crystalline phase has been refined using the Rietveld technique. The crystal structure is hexagonal with lattice parameter a = 0.443 nm and c = 0.511 nm. The average crystallite size obtained using Scherrer equation is equal 16.2 nm, so it lies in the nano-range. From the radial distribution function, the short range order (SRO) of the amorphous phase has been discussed. The structure unit of the SRO is regular tetrahedron with (r₂/r₁) = 1.61. The Se_0.8Te_0.2 glassy sample obeys the chemical order network model, CONM. Some amorphous structural parameters have been deduced. The crystallization mechanism of the amorphous phase is one-dimensional growth. The calculated value of the glass transition activation energy (E_g) and the crystallization activation energy (E_c) are 159.8 ± 0.3 and 104.3 ± 0.51 kJ/mol, respectively.     

Viscosity of (GeSe2)x(Sb2Se3)1−x undercooled melts

Viscosity of (GeSe₂)_x(Sb₂Se₃)_1−x undercooled melts (x = 0.4-0.8) was measured using parallel-plate method and penetration method. By using these two techniques viscosity of the whole measurable region of undercooled melt and of the part of glass region can be measured. In this relatively broad viscosity interval (seven orders of magnitude) all measured samples show Newtonian behavior and the dependence of their viscosity on temperature can be described by a simple Arrhenius equation. The kinetic fragilities calculated from these dependencies show similar compositional dependence as heat capacity changes at glass transition measured by DSC.