在有机发光器件中,掺杂染料分子是改变发光颜色,提高发光性能的有利手段.在掺杂体系中,主体材料向掺杂剂的能量传递是主要的激发态弛豫过程.在LEC器件中,利用掺杂手段改变发光颜色的方法报道很少.研究了以发射绿光(峰值550 nm)的共聚物Poly[(BEHP-PPV)-co-(MEH-PPV)]中掺杂DCJTB作为功能层的LEC器件的发光特性.器件的结构为ITO/Poly[(BEHP-PPV)-co-(MEH-PPV)]∶DCJTB+PEO+LiCF3SO3/Al.共聚物的光致发光光谱几乎覆盖了整个DCJTB吸收光谱的范围,满足能量传递的要求.通过光致发光与电致发光光谱的研究,发现掺杂后的薄膜不论是光致发光还是电致发光,都以DCJTB的发射为主,说明二者之间的确存在能量传递.     

Poly ∶ DCJTB 为功能层LEC器件的能量传递

在有机发光器件中,掺杂染料分子是改变发光颜色,提高发光性能的有利手段。在掺杂体系中,主体材料向掺杂剂的能量传递是主要的激发态弛豫过程。在LEC器件中,利用掺杂手段改变发光颜色的方法报道很少。研究了以发射绿光(峰值550 nm)的共聚物Poly 中掺杂DCJTB作为功能层的LEC器件的发光特性。器件的结构为ITO/Poly ∶ DCJTB+PEO+LiCF₃SO₃/Al。共聚物的光致发光光谱几乎覆盖了整个DCJTB吸收光谱的范围,满足能量传递的要求。通过光致发光与电致发光光谱的研究,发现掺杂后的薄膜不论是光致发光还是电致发光,都以DCJTB的发射为主,说明二者之间的确存在能量传递。     

TBPe与MEH-PPV共掺杂的有机电致发光器件的优化研究

采用有机小分子TBPe(2,5,8,11-tetratertbutylperylene)以不同比例掺入MEH-PPV(poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene])作为发光层,研究了TBPe不同掺杂比例对器件性能的影响,进而对发光强度进行优化。对于所制备的ITO/PEDOT∶PSS/MEH-PPV/TBPe/Al有机电致发光器件,TBPe的最优蒸镀厚度为0.5 nm,其发光强度相对于标准器件提高了325%。ITO/PEDOT∶PSS/MEH-PPV∶TBPe/TBPe/Liq/Al有机电致发光器件的最优掺杂比例为MEH-PPV∶TBPe=100∶30(质量比),其发光亮度相比于未掺杂器件提高了44%。在上述器件的基础上增加Alq3层提高电子注入,分别制作了Liq和LiF作为修饰层的ITO/PEDOT∶PSS/MEH-PPV∶TBPe/TBPe/Alq3/Liq/Al和ITO/PEDOT∶PSS/MEH-PPV∶TBPe/TBPe/Alq3/LiF/Al多层器件,发光亮度分别达到4 162 cd/m2和4 701 cd/m2。所有器件的电致发光波长均为580 nm,为MEH-PPV的发光,TBPe的掺杂对MEH-PPV的发光起到了增强作用。     

利用级联式能量传递的有机电致发光器件

为了提高掺杂型有机电致发光器件(OLED)中主体发光材料与客体荧光染料间能量传递的效率,2-对联苯-8-羟基喹啉锌(Zn ₂)作为NPB : DCJTB掺杂体系的能量助传递剂,制备了结构如:ITO/NPB/NPB : DCJTB/Zn ₂/BCP/Al的有机电致发光器件。助传递剂Zn ₂的加入,能够两次利用Frster能量转移,实现NPB向DCJTB级联式的能量传递过程,提高低浓度时掺杂染料DCJTB红光发射的纯度;此外,还探讨了三者间能量传递的有效距离,即当助传递剂与掺杂体系的距离在小于10 nm的范围内,其参与能量传递的效率随着距离的增加而逐渐下降。     

TBPe与MEH-PPV共掺杂的有机电致发光器件的优化研究

采用有机小分子TBPe（2,5,8,11-tetratertbutylperylene）以不同比例掺入MEH-PPV（poly ）作为发光层,研究了TBPe不同掺杂比例对器件性能的影响,进而对发光强度进行优化。对于所制备的ITO/PEDOT：PSS/MEH-PPV/TBPe/Al有机电致发光器件,TBPe的最优蒸镀厚度为0.5 nm,其发光强度相对于标准器件提高了325%。ITO/PEDOT：PSS/MEH-PPV：TBPe/TBPe/Liq/Al有机电致发光器件的最优掺杂比例为MEH-PPV：TBPe=100：30（质量比）,其发光亮度相比于未掺杂器件提高了44%。在上述器件的基础上增加Alq₃层提高电子注入,分别制作了Liq和LiF作为修饰层的ITO/PEDOT：PSS/MEH-PPV：TBPe/TBPe/Alq₃/Liq/Al和ITO/PEDOT：PSS/MEH-PPV：TBPe/TBPe/Alq₃/LiF/Al多层器件,发光亮度分别达到4 162 cd/m²和4 701 cd/m²。所有器件的电致发光波长均为580 nm,为MEH-PPV的发光,TBPe的掺杂对MEH-PPV的发光起到了增强作用。     

电场变化对有机磷光器件中激子形成影响的研究

激子形成区域随电场变化的移动会使得有机电致发光器件(OLEDs)的效率和色度发生改变,从而影响器件的性能。文章首先制备了两种OLED器件,器件1为ITO/PEDOT∶PSS/PVK∶Ir(ppy)₃∶DCJTB (100∶2∶1 wt)/BCP(10 nm)/Alq₃(15 nm)/Al,器件2为ITO/PEDOT∶PSS/PVK∶Ir(ppy)₃(100∶2 wt)/BCP(10 nm)/Alq₃(15 nm)/Al,研究了电场强度对单层多掺杂结构器件激子形成的影响。实验发现在多掺杂发光层中,随着电压的增加,Ir(ppy)₃,PVK和DCJTB的发光均增强,PVK和DCJTB发光增强更快。对其发光机制进行分析,认为较高电场下,载流子获得较高能量,更容易形成高能量激子,产生宽禁带材料PVK的发光;另一方面,从能级结构分析DCJTB的带隙较窄, 俘获更多的载流子发光更强。同时,在器件的电致发光(EL)光谱发现在460 nm处一新的发射峰, 发光随着电压的增大相对减弱。为了研究460 nm发光的来源,制备了器件：ITO/PEDOT∶PSS/PVK∶BCP∶Ir(ppy)₃(x∶y∶2 wt)/Alq₃(15 nm)/Al, 改变x, y的比值研究发现,460 nm处的发光依然存在,推测此发光峰应与PVK及BCP之间有关。     

掺杂型红色有机电致发光显示器件

全色显示是有机电致发光显示(OLED)器件发展的目标,而高性能红色发光器件一直是制约全彩色OLED器件实用化的瓶颈,也是目前有机电致发光显示研究的热点。制作了掺杂DCJTB和不同浓度的rubrene两种荧光染料的红色有机电致发光显示器件,以NPB和Alq₃分别作为空穴传输层和电子传输层,发现器件性能与只掺杂DCJTB的器件相比有明显提高,发光效率提高到2～3倍。通过Frster理论和能带理论分析了器件的能量转移机理,研究发现Frster能量转移不是掺杂器件能量转移的主要形式,载流子俘获机制才是器件效率提高的主要原因;rubrene的引入使得能量能够更有效地从Alq₃转移到DCJTB,从而显著地提高了器件的发光效率和性能。     

掺杂PVK薄膜中两种组分相互作用的光谱及形貌研究

将两种荧光材料Alq₃和DCJTB 同时掺杂到聚合物PVK中,通过混合薄膜的光学及电学性质研究了能量传递过程及电荷陷阱作用。同时用AFM分析了不同掺杂浓度下混合薄膜的相分离现象。发现随着DCJTB染料比例的增加,两种染料在PVK中的分散越来越均匀,说明在双掺杂体系中存在Alq₃和DCJTB 的某种作用,这种作用打散了混合物中Alq₃的聚集,但随着掺杂浓度的进一步增加,DCJTB形成了自己独立的电荷传输通道,从而降低了电致发光器件的启亮电压。     

蓝色发光材料DPVBi掺杂DCJTB发光性质的研究

对蓝光材料DPVBi掺杂红光染料DCJTB的发光性质进行了研究。首先研究了DPVBi掺杂不同质量浓度DCJTB的光致发光，当掺杂质量浓度为0.1％时，光致发光得到白光(色度x=0．36，y=0．34)。基于光致发光的实验结果，以DPVBi掺杂不同质量浓度DCJTB作发光层，制备了结构为ITO／CuPc／NPB／DPVBi：DCJTB/Alq3／LiF／Al的器件，当掺杂质量浓度为0．08％时器件实现了白色发光(色度为x=0．25，y=0．32)。研究了该白光器件的电致发光性质，白光器件在14V时达到最高亮度7822cd／m^2。在20mA／cm^2电流密度驱动下的亮度为489cd/m^2，最大流明效率为1．75lm／W。     

以蓝色发光材料DPVBi为基质的白色发光器件

白色有机发光器件是实现彩色平板显示的重要方案之一。利用蓝色发光材料DPVBi[4，4′—(2，2—苯乙烯基)—1，1′—联苯]掺杂红光染料DCJTB[4—氰甲烯基—2—叔丁基—6—(1，1，7，7—四甲基久洛尼定基—9—烯炔基—4H—吡喃)]作发光层制备了白色发光器件。研究了DPVBi掺杂不同浓度IDCJTB薄膜的光致发光性质，根据光致发光结果，制备了以DPVBi掺杂不同浓度DCJTB作发光层的电致发光器件，其结构为ITO／GuPc／NPB／DPVBi：DCJTB／Alq3／LiF／Al。当DCJTB质量分数为0．0008时，器件实现了白色发光(色度x=0．25，y=0．32)，电致发光和光致发光的掺杂比例基本相符，表明器件的白色发光主要是由基质DPVBi向掺杂剂DCJTB的能量传递产生的。研究还发现：白色器件随电压升高，光谱中蓝色成分相对于红色成分的比例略有增加，文章对此现象进行了分析。该白光器件在14V时达到最高亮度7822cd／cm^2，在20mA／cm^2电流密度下的亮度为-489cd／cm^2，最大流明效率为1．75lm／W。     

荧光染料和磷光染料激子形成截面的比较

为了比较单线态激子与三线态激子形成截面的大小,作者将荧光染料4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) 和磷光材料factris-(2-phenylpyridine) iridium [Ir(ppy)₃]共掺杂在N-vinylcarbazole (PVK)中作为发光层,制作了多层有机电致发光器件。通过对其光致发光及电致发光特性的研究,计算出Ir(ppy)₃激子的形成截面比DCJTB激子的形成截面大得多。     

Enhanced quantum efficiency in polymer electroluminescence devices by inserting an ultrathin PMMA layer

We report an increase of electroluminescence (EL) efficiency by about two times for poly(2-methoxy-5-(2′-ethylhexyloxy)-1,4-phenylene vinylene) (MEH-PPV) based polymer light-emitting diodes (PLED) while employing an ultrathin layer of poly(methyl methacrylate) (PMMA) between a hole injection layer, polyethylenedioxythiophenne:polystyrenesulfonate (PEDOT:PSS) and an emitting layer, MEH-PPV. The peak power efficiency of the control device (ITO/MEH-PPV/LiF/Al) was 0.42 lm/W with a current efficiency of 0.66 cd/A. The device with the optimized thickness of PMMA interface layer shows the highest power efficiency of 1.15 lm/W at a current efficiency exceeding 1.83 cd/A. The significant improvement in the device performance is attributed to the decrease of holes injection and the promotion of electrons injection, which cause the balance of the carriers within the emitting layer.     

Spectral Characteristics of White Organic Light-emitting Diodes Based on Novel Phosphorescent Sensitizer

采用新型贵金属铱的配合物bis(1,2-dipheny1-1H-benzoimida-zole)iridium (acetylacetonate)作为磷光敏化剂,与荧光染料4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9-en-yl)-4H-pyran共同掺杂到聚合物主体材料poly(N-vinylcarbazole)中,以N,N'-diphenyl-N,N'-bis(1-naphthyl) (1,1'-biphenyl)-4,4'-diami-ne作为蓝光发光层,制备了白色有机电致发光器件. 通过对掺杂体系的紫外-可见吸收光谱、光致发光光谱以及电致发光光谱的表征,分析了该磷光敏化体系的能量转移机制. 结果表明,在该聚合物磷光荧光双掺杂体系中,由于磷光与荧光材料之间的不完全的F?rster能量传递过程,导致电致发光光谱中同时存在磷光材料三线态到基态与荧光材料单线态到基态的辐射衰减发光. 该掺杂体系成功实现了白光发射,随着偏置电压的升高,器件的CIE色坐标有微小的红移,但都非常接近等能白光点,器件表现出了很好的色纯度.     

Non-doped red to yellow organic light-emitting diodes with an ultrathin 4-(dicyanomethylene)-2-t-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) layer

In this letter, bright non-doped red to yellow organic light-emitting diodes (OLEDs) with ultrathin 4-(dicyanomethylene)-2-t-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) layer as the emitting layer were fabricated. It was investigated that the effect of the ultrathin DCJTB layer on the electroluminescent (EL) performance of OLEDs. The DCJTB layer was incorporated at different positions in the conventional tris(8-quinolinolato)-aluminum (AlQ)-based devices (ITO/NPB/AlQ/LiF/Al). The emission of DCJTB was dominative in the EL spectra of the devices, in which the position of 0.3 nm DCJTB layer was less than 10 nm from the NPB/AlQ interface. The EL peak emission of DCJTB shifted to blue side as DCJTB position moved gradually from AlQ to NPB layer. The highest brightness of the device with 0.3 nm DCJTB layer inserted into NPB reached 16,200 cd/m² at 15 V, with the CIE coordinates of (0.522, 0.439).     

Single-layered light-emitting diodes possessing methoxy-modified pyrazoloquinoline dyes in poly-N-vinylcarbazole matrix

A principal opportunity to operate by current-voltage and electroluminescent-current dependences for the single-layered light-emitting diodes (LED) on the basis of the polyvinylcarbazole (PVK) polymers doped by methoxy-substituted pyrazoloquinoline (PQ) emitting dye chromphore is demonstrated. The principal light-emitting parameters in the architecture ITO/PQ: PVK/Ca (Al) were investigated. The maximally achieved quantum efficiency of the investigated LED was equal to about 0.87% and corresponded to the brightness about the 44 Cd/m². The absence of blue shift for the electroluminescence (EL) compared to PL may indicate on an absence of near-the-surface exciton diffusion for the methoxy-PQ contrary to the phenyl-methyl-substituted PQ. The quantum chemical calculations have shown principal role of the dye chromophore state dipole moments in the observed carrier kinetics determining the EL.     

红色有机发光二极管

制备了以芳香族二胺类衍生物TPD为空穴传输层、8－羟基喹啉铝Alq3掺杂红光染料DCJTB作为发光层LiF/Al为复合电极的红色发光二极管。研究了不同掺杂质量分数对器件发光光谱、亮度电流电压特性的影响。发现由于DCJTB的自极化作用,发光峰值位置有30nm的移动,当掺杂质量分数为0.2％和3％时,器件的最高亮度分别为17400cd/m^2和2900cd/m^2,20mA/cm^2时其亮度又分别为1080cd/m^2和150cd/m^2,量子效率分别为2％和0.5％。     

有机薄膜晶体管驱动聚合物发光二极管研究

研究了有机薄膜晶体管(OTFT)与聚合物发光二极管(PLED)集成制备技术和相关物理问题.OTFT结构为栅极钽(Ta)/绝缘层五氧化二钽(Ta2O5)/有源层并五苯(Pentacene)/源漏极金(Au);PLED器件结构为ITO/PEDOT:PEO(polyethylene oxide)/P-PPV或MEH-PPV/Ba/Al.PEDOT:PEO,P-PPV和MEH-PPV薄膜层均采用丝网印刷技术,实现了OTFT与PLED器件集成发光.其中OTFT器件的阈值电压为-7V,迁移率为0.91cm2/(V.s),并通过OTFT驱动得到以P-PPV和MEH-PPV为发光层的PLED器件的发光亮度分别达到124和26cd/m2,电流效率分别为12.4和1.1cd/A.利用丝网印刷技术可以有效控制高分子薄膜的沉积区域,实现功能器件的集成.