Crystal structure, magnetic susceptibility and Mössbauer spectroscopy of the mixed-valence iron phosphate Na1/2Cu4/3Fe2(PO4)3

Single crystals of a new mixed-valent iron phosphate Na_1/2Cu_4/3Fe₂(PO₄)₃ have been synthesized by a flux method and structurally characterized from X-ray diffraction data. Crystal data: space group ; ; ; ; α=105.881(1)°; β=107.202(1)°; γ=101.467(1)°; Z=2; R₁=0.03; wR₂=0.093. The three-dimensional structure was found to be closely related to that of the well known Howardevansite structural type. It results from infinite chains of CuO₅ and FeO₆ polyhedra, joined together by (Cu,□)O₆ octahedra and PO₄ tetrahedra by corner-sharing. The large cavities in framework are occupied by Na⁺ ions. The magnetic susceptibility study revealed an antiferromagnetic behavior with Neel temperature of approximately 40 K. The Mössbauer spectroscopy confirmed the presence of iron in both +2 and +3 oxidation states.     

[Zn(H2PO4)4] clusters and ∞[Zn2(HPO4)3(H2PO4)2] layers in two new zinc phosphates templated by [H2(4-amino-2.2.6.6-tetramethylpiperidine)] cations

Two zinc phosphates (ZnPO), [H₂(N₂C₉H₂₀)]·[Zn(H₂PO₄)₄] (I) and [H₂(N₂C₉H₂₀)]₂·[Zn₂(HPO₄)₃(H₂PO₄)₂]·H₂O (II), are synthesized under hydrothermal conditions using 4-amino-2.2.6.6-tetramethylpiperidine as organic template. I crystallizes in space group with , , , α=92.57(1)°, β=89.76(1)°, γ=102.16(2)°, and Z=2. Its structure, refined to R=0.029 and R_w=0.076 for 4279 independent reflections, consists of [Zn(H₂PO₄)₄]²⁻ clusters held together through strong hydrogen bonds to form pseudo-layers between which the doubly protonated amine molecules are inserted. II is monoclinic, C2, with , , , β=103.72(5)°, and Z=4 (R=0.079, R_w=0.268, 2477 independent reflections). The structure of II consists of _∞[Zn₂(HPO₄)₃(H₂PO₄)₂]⁴⁻ inorganic (2D) layers built up from vertex-sharing [ZnO₄] and [(H₂/H)PO₄] tetrahedra. Organic cations and water molecules ensure the connection between these layers via hydrogen bonds. It is shown that numerous (1D), (2D), e.g., [H₂(N₂C₉H₂₀)]₂·[Zn₂(HPO₄)₃(H₂PO₄)₂]·H₂O, and (3D) (ZnPO) result from the condensation of the [Zn(H₂PO₄)₄]²⁻ clusters.     

Synthesis, crystal structure and vibrational spectra characterization of MLa(PO3)4 (M=Na, Ag)

The single crystals of lanthanum metaphosphate MLa(PO₃)₄ (M=Na, Ag) have been synthesized and studied by a combination of X-ray crystal diffraction and vibrational spectroscopy. The sodium and silver compounds crystallize in the same monoclinic P2₁/n space group ( factor group) with the following respective unit cell dimensions: a=7.255(2), b=13.186(3), , β=90.40(2)°, , Z=4 and a=7.300(5), b=13.211(9), , β=90.47(4)°, , Z=4. This three-dimensional framework is built of twisted zig-zag chains running along a direction and made up of PO₄ tetrahedra sharing two corners, connected to the LaO₈ and NaO₇ or AgO₇ polyhedra by common oxygen atoms to the chains. The infrared and Raman vibrational spectra have been investigated. A group factor analysis leads to the determination of internal modes of (PO₃)⁻ anion in the phosphate chain.     

Synthesis, structure, and characterization of a new one-dimensional tellurite phosphate, Ba2TeO(PO4)2

A new one-dimensional tellurite phosphate, Ba₂TeO(PO₄)₂ has been synthesized by standard solid-state reaction techniques using BaCO₃, TeO₂, and (NH₄)H₂PO₄ as reagents. The structure of Ba₂TeO(PO₄)₂ was determined by single-crystal X-ray diffraction. Ba₂TeO(PO₄)₂ crystallizes in the triclinic space group P-1 (No. 2), with , , , α=76.843(4)°, β=79.933(4)°, γ=75.688(4)°, , and Z=2. Ba₂TeO(PO₄)₂ has a novel one-dimensional chain structure that is composed of PO₄ tetrahedra and TeO₅ polyhedra. Te⁴⁺ cations are in asymmetric coordination environments attributable to their lone pairs. The lone pairs on the Te⁴⁺ cations point in the [100] and [−100] direction and interact with the Ba²⁺ cations. Infrared, Raman, and UV-Vis diffuse reflectance spectroscopy, thermogravimetric analysis, and dipole moment calculations are also presented.     

Crystal growth, characterization and physical properties of PrNiSb3, NdNiSb3 and SmNiSb3

The crystal structures of three new intermetallic ternary compounds in the LnNiSb₃ (Ln=Pr, Nd and Sm) family have been characterized by single crystal X-ray diffraction. PrNiSb₃, NdNiSb₃ and SmNiSb₃ all crystallize in an orthorhombic space group, Pbcm (No. 57), Z=12, with , , , and ; , , , and ; and , , , and , for Ln=Pr, Nd and Sm, respectively. These compounds consist of rare-earth atoms located above and below layers of nearly square, buckled Sb nets, along with layers of highly distorted edge- and face-sharing NiSb₆ octahedra. Resistivity data indicate metallic behavior for all three compounds. Magnetization measurements show antiferromagnetic behavior with (PrNiSb₃), 4.6 K (NdNiSb₃), and 2.9 K (SmNiSb₃). Effective moments of 3.62 μ_B, 3.90 μ_B and 0.80 μ_B are found for PrNiSb₃, NdNiSb₃ and SmNiSb₃, respectively, and are consistent with Pr³⁺ (f ²), Nd³⁺ (f ³), and Sm³⁺ (f ⁴).     

Hydrothermal synthesis and characterization of (enH2)3.5[As8V14O42(PO4)]·2H2O

The compound (enH₂)_3.5[As₈V₁₄O₄₂(PO₄)]·2H₂O 1 (en=ethylenediamine) has been synthesized and characterized by means of elemental analysis, IR spectrum, ESR spectrum, XPS spectrum, TG analysis and single crystal X-ray diffraction analysis. The compound 1 crystallizes in monoclinic system, space group C2/c, β=105.59(3), Z=8 and R₁(wR₂)=0.0398(0.0885). The compound 1 is constructed from [As₈V₁₄O₄₂(PO₄)]⁷⁻ anions and H₂en cations linked through hydrogen bonds into a network. The [As₈V₁₄O₄₂(PO₄)]⁷⁻ cluster consists of 14 VO₅ square pyramids linked by 4 As₂O₅ handle-like units, and includes at its center an ordered PO₄³⁻ anion.     

Synthesis and crystal structures of the layered uranyl tellurites A2[(UO2)3(TeO3)2O2] (A=K, Rb, Cs)

The reactions of UO₃ and TeO₃ with KCl, RbCl, or CsCl at 800 °C for 5 d yield single crystals of A₂[(UO₂)₃(TeO₃)₂O₂] (A=K (1), Rb (2), and Cs (3)). These compounds are isostructural with one another, and their structures consist of two-dimensional sheets arranged in a stair-like topology separated by alkali metal cations. These sheets are comprised of zigzagging uranium(VI) oxide chains bridged by corner-sharing trigonal pyramidal TeO₃²⁻ anions. The chains are composed of dimeric, edge-sharing, pentagonal bipyramidal UO₇ moieties joined by edge-sharing tetragonal bipyramidal UO₆ units. The lone-pair of electrons from the TeO₃ groups are oriented in opposite directions with respect to one another on each side of the sheets rendering each individual sheet non-polar. The alkali metal cations form contacts with nearby tellurite oxygen atoms as well as with oxygen atoms from the uranyl moieties. Crystallographic data (193 K, MoKα, ): 1, triclinic, space group , , , , α=101.852(1)°, β=102.974(1)°, γ=100.081(1)°, , Z=2, R(F)=2.70% for 98 parameters and 1697 reflections with I>2σ(I); 2, triclinic, space group , , , , α=105.590(2)°, β=101.760(2)°, γ=99.456(2)°, , Z=2, R(F)=2.36% for 98 parameters and 1817 reflections with I>2σ(I); 3, triclinic, space group , , , , α=109.301(1)°, β=100.573(1)°, γ=99.504(1)°, , Z=2, R(F)=2.61% for 98 parameters and 1965 reflections with I>2σ(I).     

Long-range magnetic ordering of S=1/2 linear trimers in A3Cu3(PO4)4 (A=Ca, Sr, and Pb)

Magnetic properties of S=1/2 linear trimer cluster compounds A₃Cu₃(PO₄)₄ (A=Ca, Sr, and Pb) were investigated. Magnetic susceptibility data for the three compounds showed that paramagnetic copper spins form trimers with the total spin of 1/2 below about 45 K. Specific heat and magnetization measurements indicated that the trimer clusters undergo ferromagnetic long-range ordering at for A=Ca and antiferromagnetic long-range ordering at for A=Sr and for A=Pb. A₃Cu₃(PO₄)₄ exhibited 1/3-magnetization plateau at least up to magnetic field of 55 T at 1.3 and 4.2 K. A₃Cu₃(PO₄)₄ with A=Sr and Pb showed a spin-flop transition near 0.03 T in the antiferromagnetic state at 0.08 K. Specific heat data at magnetic fields clearly showed broad maxima at low temperatures due to the finite intra-chain interaction in one-dimensional arrays of the trimers.     

[Zn2(HPO3)2(H2PO3)][C3H5N2] and [Zn2(HPO3)3][C4H7N2]2·2H2O: Two new layered zinc phosphites with double 12-membered rings templated by imidazole and 2-methylimidazole

Two new zinc phosphites [Zn₂(HPO₃)₂(H₂PO₃)][C₃H₅N₂] 1 and [Zn₂(HPO₃)₃][C₄H₇N₂]₂·2H₂O 2 have been hydrothermally synthesized templated by imidazole and 2-methylimidazole. Single-crystal X-ray diffraction analysis reveals that the two compounds have the similar inorganic framework structures, which both exhibit 2D double layer structures with double 12-membered rings. Due to the different space-filling effect of the guest molecules, the stacking mode of adjacent layers and the arrangement mode of the organic amines are distinct. In 1, the adjacent layers are stacked in an -ABAB- sequence and monoprotonated imidazole molecules sit in the middle of 12MR windows, while in 2, the layers are stacked in an -AAAA- pattern. Monoprotonated 2-methylimidazole molecules occupy two different sites, one inserts into 12MR and the other resides in the interlayer region. Crystal data for 1: triclinic, P-1, , , , α=114.71(3)°, β=92.78(3)°, γ=113.04(3)°, , Z=2; for 2: triclinic, P-1, , , , α=68.244(7)°, β=76.143(7)°, γ=63.113(6)°, , Z=2.     

Preparation, structures, and band gaps of RbInS2 and RbInSe2

The two compounds RbInS₂ and RbInSe₂ have been synthesized at 773 K by means of the reactive flux method. These isostructural compounds crystallize in space group C2/c of the monoclinic system with 16 formula units in a cell at 153 K of dimensions , , , and β=100.244(1)° for RbInS₂, and , , , and β=100.16(2)° for RbInSe₂. The In atoms are four-coordinated. The structure consists of two-dimensional (Q=S, Se) layers perpendicular to [001] separated from the Rb⁺ cations. Adamantane-like In₄Q₁₀ units are connected by common corners to form the layers. Band structure calculations indicate that these compounds are direct band-gap semiconductors with the smallest band gap at the Γ point. The calculated band gaps are 2.8 eV for RbInS₂ and 2.0 eV for RbInSe₂, values that are consistent with the colors of the compounds.     

Single crystal structure and Raman spectrum of Ba3Na2(CN2)4

The synthesis, single crystal structure determination, and Raman spectrum are reported for colorless transparent tribarium disodium tetracyanamide, Ba₃Na₂(CN₂)₄. The title compound crystallizes in the space group C_2h⁵-P2₁/c (#14, , , , β=110.454(4)°, , Z=4, R/wR=0.0266/0.0543). Each sodium atom is surrounded by six nitrogen atoms in octahedral geometry. Sodium centered nitrogen octahedra are linked through face-sharing along the [100] direction to form one-dimensional (1D) chains. These chains are connected to each other through the carbon atoms of cyanamide and make a three-dimensional (3D) network with 1D channels along the [100] direction. Barium atoms and additional cyanamide anions reside in the channels. Each barium atom is irregularly coordinated with nitrogen and carbon from the cyanamide anions. The Raman spectrum shows symmetric vibrations of [NCN]²⁻ corresponding to ν_sym (1241.5 cm⁻¹) and 2δ (1356.4 cm⁻¹).     

Structural and conductivity studies of CsKSO4Te(OH)6 and Rb1.25K0.75SO4Te(OH)6 materials

The crystal structures of the title compounds were solved using the single-crystal X-ray diffraction technique. At room temperature CsKSO₄Te(OH)₆ was found to crystallize in the monoclinic system with Pn space group and lattice parameters: ; ; ; β=106.53(2)°; ; Z=4 and . The structural refinement has led to a reliability factor of R₁=0.0284 (wR₂=0.064) for 7577 independent reflections. Rb_1.25K_0.75SO₄Te(OH)₆ material possesses a monoclinic structure with space group P2₁/a and cell parameters: ; ; ; β=106.860(10)°; ; Z=4 and . The residuals are R₁=0.0297 and wR₂=0.0776 for 3336 independent reflections. The main interest of these structures is the presence of two different and independent anionic groups (TeO₆⁶⁻ and SO₄²⁻) in the same crystal.Complex impedance measurements (Z^*=Z^′—iZ^″) have been undertaken in the frequency and temperature ranges 20-10⁶ Hz and 400-600 K, respectively. The dielectric relaxation is studied in the complex modulus formalism M^*.     

Molten salt flux synthesis and structure of the new layered uranyl tellurite, K4[(UO2)5(TeO3)2O5]

The reaction of UO₃ and TeO₃ with a KCl flux at 800 °C for 3 days yields single crystals of K₄[(UO₂)₅(TeO₃)₂O₅]. The structure of the title compound consists of layered, two-dimensional sheets arranged in a stair-like topology separated by potassium cations. Contained within these sheets are one-dimensional uranium oxide ribbons consisting of UO₇ pentagonal bipyramids and UO₆ tetragonal bipyramids. The ribbons are in turn linked by corner-sharing with trigonal pyramidal TeO₃ units to form sheets. The lone-pair of electrons from the TeO₃ groups are oriented in opposite directions with respect to one another on each side of the sheets rendering each individual sheet nonpolar. The potassium cations form contacts with nearby tellurite units and axial uranyl oxygen atoms. Crystallographic data (193 K, MoKα, ): triclinic, space group , , , , α=99.642(1)°, β=93.591(1)°, γ=100.506(1)°, , Z=1,R(F)=4.19% for 149 parameters and 2583 reflections with I>2σ(I).     

Synthesis, structure, band gap, and electronic structure of CsAgSb4S7

The compound CsAgSb₄S₇ has been synthesized by the reaction of the elements in a Cs₂S₃ flux at 773 K. The compound crystallizes in a new structure type with eight formula units in space group C2/c of the monoclinic system in a cell at 153 K of dimensions , , , β=97.650(1)°, and . The structure contains two-dimensional layers separated by Cs atoms. Each layer is built from edge-sharing one-dimensional and chains. Each Ag atom is tetrahedrally coordinated to four S atoms. Each Sb³⁺ center is pyramidally coordinated to three S atoms to form an SbS₃ group. CsAgSb₄S₇ is insulating with an optical band gap of 2.04 eV. Extended Hückel calculations indicate that the band gap in CsAgSb₄S₇ is dominated by the Sb 5s and S 3p states above and below the Fermi level.     

Structures of the reduced niobium oxides Nb12O29 and Nb22O54

The crystal structure of Nb₂₂O₅₄ is reported for the first time, and the structure of orthorhombic Nb₁₂O₂₉ is reexamined, resolving previous ambiguities. Single crystal X-ray and electron diffraction were employed. These compounds were found to crystallize in the space groups P2/m (, , , β=102.029(3)^°) and Cmcm (, , ), respectively and share a common structural unit, a 4×3 block of corner sharing NbO₆ octahedra. Despite different constraints imposed by symmetry these blocks are very similar in both compounds. Within a block, it is found that the niobium atoms are not located in the centers of the oxygen octahedra, but rather are displaced inward toward the center of the block forming an apparent antiferroelectric state. Bond valence sums and bond lengths do not show the presence of charge ordering, suggesting that all 4d electrons are delocalized in these compounds at the temperature studied, T=200 K.     

Crystal structure, phase transition and anisotropic thermal expansion of barium zirconium diorthophosphate, BaZr(PO4)2

The crystal structure of BaZr(PO₄)₂ at 298 K was determined from conventional X-ray powder diffraction data using direct methods, and it was further refined by the Rietveld method. The structure was monoclinic (space group C2/m, Z=2) with , , , β=93.086(1)° and . Final reliability indices were R_wp=8.21%, R_p=5.64% and R_B=2.92%. The atom arrangement is similar to that of yavapaiite (KFe(SO₄)₂), however, these crystal structures differ distinctly in the coordination numbers of barium and potassium atoms; the former is tenfold coordinated, whereas the latter is sixfold coordinated. The powder specimens were also examined by high-temperature XRD and DTA to reveal the occurrence of a phase transition from monoclinic to orthorhombic at 732 K during heating. Upon cooling the reverse transition occurred at 710 K. The monoclinic crystal expanded almost one-dimensionally along [503] during the heating process. The orthorhombic phase also showed a tendency to expand one-dimensionally along the c-axis above 732 K.     

Synthesis, structural determination and magnetic properties of layered hybrid organic-inorganic, iron (II) propylphosphonate, Fe[(CH3(CH2)2PO3)(H2O)], and iron (II) octadecylphosphonate, Fe[(CH3(CH2)17PO3)(H2O)]

Fe[(CH₃(CH₂)₂PO₃)(H₂O)] (1) and Fe[(CH₃(CH₂)₁₇PO₃)(H₂O)] (2) were synthesized by reaction of FeCl₂·6H₂O and the relevant phosphonic acid in water in presence of urea and under inert atmosphere. The compounds were characterized by elemental and thermogravimetric analyses, UV-visible and IR spectroscopy. The crystal structure of (1) was determined from X-ray single crystal diffraction studies at room temperature: monoclinic symmetry, space group P2₁, , , , and β=98.62(3)°. The compound is lamellar and the structure is hybrid, made of alternating inorganic and organic layers along the c direction. The inorganic layers consist of Fe(II) ions octahedrally coordinated by five phosphonate oxygen atoms and one from the water molecule, separated by bi-layers of propyl groups. A preliminary structure characterization of compound (2) suggests a similar layered structure, but with an interlayer spacing of 40.3 Å. The magnetic properties of the compounds were both studied by a dc and ac SQUID magnetometer. Fe[(CH₃(CH₂)₂PO₃)(H₂O)] (1) obeys the Curie-Weiss law at temperatures above 50 K (, ), indicating a Fe +II oxidation state, a high-spin d⁶ (S=2) electronic configuration and an antiferromagnetic exchange couplings between the near-neighbouring Fe(II) ions. Below , Fe[(CH₃(CH₂)₂PO₃)(H₂O)] exhibits a weak ferromagnetism. The critical temperature of has been determined by ac magnetic susceptibility measurements. Compound (2) shows the same paramagnetic behaviour of the iron (II) propyl derivative. The values of C and θ were found to be and −44 K, respectively, thus suggesting the presence of Fe +II ion in the S=2 spin state and antiferromagnetic interactions between Fe(II) ions at low temperatures. Zero-field and field cooled magnetic susceptibility vs. T plots do not overlap below , suggesting the presence of an ordered magnetic state. The critical temperature, T_N, has been located by the peaks at from the ac susceptibility (χ′and χ″) vs. T plots. Below T_N hysteresis loops recorded in the temperature region show an S-shape, while below 15 K assume an ellipsoid form. They reveal that compound (2) is a weak ferromagnet. The critical temperature T_N in these layered Fe(II) alkylphosphonates is independent of the distance between the inorganic layers.     

X-ray powder diffraction studies and thermal behaviour of NaK2B9O15, Na(Na.17K.83)2B9O15, and (Na.80K.20)K2B9O15

The crystal structures of NaK₂B₉O₁₅ (, , , β=94.080(1)°, R_p=0.047, R_wp=0.059, R_B=0.026), Na(Na_.17K_.83)₂B₉O₁₅ (, , , β=94.228(2)°, R_p=0.053, R_wp=0.068, R_B=0.026), and (Na_.80K_.20)K₂B₉O₁₅ (, , , β=94.071(1)°, Z=4, R_p=0.041, R_wp=0.052, R_B=0.023) were refined in the monoclinic space groups P2₁/c(Z=4) using X-ray powder diffraction data and the Rietveld method. These nonaborates are isostructural to K₃B₉O₁₅. Their crystal structure consists of a three-dimensional open framework built up from three crystallographically independent triborate groups. The alkali metal cations are located on three different sites in the voids of the framework. High-temperature X-ray diffraction studies show that NaK₂B₉O₁₅ decomposes at about 700 °C in accordance with the peritectic reaction NaK₂B₉O₁₅↔K₅B₁₉O₃₁+liquid. The thermal expansion of NaK₂B₉O₁₅ and Na(Na_.17K_.83)₂B₉O₁₅ is highly anisotropic. A similarity of the thermal and compositional (Na-K substitution) deformations of NaK₂B₉O₁₅ is revealed: heating of NaK₂B₉O₁₅ by 1 °C leads to the same deformations of the crystal structure as increasing the amount of K atoms in (Na_1−xK_x)₃B₉O₁₅ by 0.04 at% K.