New synthesis of excellent visible-light TiO2−xNx photocatalyst using a very simple method

An excellent visible-light-responsive (from 400 to 550 nm) TiO_2−xN_x photocatalyst was prepared by a simple wet method. Hydrazine was used as a new nitrogen resource in this paper. Self-made amorphous titanium dioxide precursor powders were dipped into hydrazine hydrate, and calcined at low temperature (110 °C) in the air. The TiO_2−xN_x was successfully synthesized, following by spontaneous combustion. The photocatalyst was characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), transmission electron microscope (TEM), UV-Vis diffuse reflectance spectrometer (DRS), and X-ray photoelectron spectroscopy (XPS). Analysis of XPS indicated that N atoms were incorporated into the lattice of the titania crystal during the combustion of hydrazine on the surface of TiO₂. Ethylene was selected as a target pollutant under visible-light excitation to evaluate the activity of this photocatalyst. The newly prepared TiO_2−xN_x photocatalyst with strong photocatalytic activity and high photochemical stability under visible-light irradiation was firstly demonstrated in the experiment.     

Visible light-sensitive yellow TiO2−xNx and Fe-N co-doped Ti1−yFeyO2−xNx anatase photocatalysts

Nitrogen substituted yellow colored anatase TiO_2−xN_x and Fe-N co-doped Ti_1−yFe_yO_2−xN_x have been easily synthesized by novel hydrazine method. White anatase TiO_2−δ and N/Fe-N-doped samples are semiconducting and the presence of ESR signals at g ∼1.994-2.0025 supports the oxygen vacancy and g∼4.3 indicates Fe³⁺ in the lattice. TiO_2−xN_x has higher conductivity than TiO_2−x and Fe/Fe-N-doped anatase and the UV absorption edge of white TiO_2−x extends in the visible region in N, Fe and Fe-N co-doped TiO₂, which show, respectively, two band gaps at ∼3.25/2.63, ∼3.31/2.44 and 2.8/2.44 eV. An activation energy of ∼1.8 eV is observed in Arrhenius log resistivity vs. 1/T plots for all samples. All TiO₂ and Fe-doped TiO₂ show low 2-propanol photodegradation activity but have significant NO photodestruction capability, both in UV and visible regions, while standard Degussa P-25 is incapable in destroying NO in the visible region The mid-gap levels that these N and Fe-N-doped TiO₂ consist may cause this discrepancy in their photocatalytic activities.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Preparation and photocatalytic activity of high-efficiency visible-light-responsive photocatalyst SnSx/TiO2

Visible-light-responsive composite photocatalysts SnS₂/TiO₂ and SnS/TiO₂ with different mass ratios were prepared by in-situ synthesis technology in solution with commercial TiO₂. The junction-based materials SnS_x (x=1, 2)/TiO₂ were found to have high visible-light photocatalytic performance and possess much better activity than the single-phase SnS_x or TiO₂. The greatly enhanced photocatalytic activity of the SnS_x/TiO₂ composites was mainly attributed to the matching band potentials and efficient charge transfer and separation at the tight-bonding interface between SnS_x and TiO₂. The fact was confirmed by the comparison of photocatalytic activities of the SnS₂/TiO₂ samples prepared by physical mixing method and in-situ synthesis technique.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Synthesis and characterization of Ti1−2xNbxNixO2−x/2 solid solutions

Doped-rutile has been traditionally used in ceramic pigments for its intense optical properties. In this paper, we compare the classical ceramic synthesis of Ti_1−2xNb_xNi_xO_2−x/2 system with the sol-gel methodology, which allows a reduction of the anatase-rutile transformation temperature. The composition was optimised in order to obtain a unique rutile phase with the minimum amount of pollutant Ni(II) and enhanced chromatic coordinates. Incorporation of the doping ions in the rutile structure was corroborated by XRD and Rietveld refinements. The species responsible for the colour mechanism were studied by different techniques. UV-VIS spectroscopy showed the characteristic features of Ni²⁺ ions, whose existence was corroborated by EPR and magnetic measurements. From these results, (Ni,Nb)doped-TiO₂ powder samples can be now shaped as thin films, monoliths, etc. by using sol-gel methodology without modifying their properties. This study introduces new possibilities of coloured TiO₂-based solid solutions in new combined advanced applications (colouring agent and photocatalyst, etc.).     

Interactions of Ba2YCu3O6+y with the Gd3NbO7 buffer layer in coated conductors

A systematic study of the chemical interaction of Ba₂YCu₃O_6+y and Gd₃NbO₇ was conducted under two processing conditions: purified air (21% p_o2), and 100 Pa p_o2 (0.1% p_o2). Phases present along the pseudo-binary join Ba₂YCu₃O_6z and Gd₃NbO₇ were found to be in two five-phase volumes within the system. Three common phases that are present in all samples are (Y,Gd)₂Cu₂O₅, Ba(Y,Gd)₂CuO₅ and Cu₂O or CuO (depending on the processing conditions). The assemblies of phases can be categorized in three regions, with Ba₂YCu₃O_6+y: Gd₃NbO₇ ratios of (I)<5.5:4.5; (II)=5.5:4.5; and (III)>5.5:4.5. The lowest melting temperature of the system was determined to be ≈938 °C in air, and 850 °C at 100 Pa p_o2. Structure determinations of two selected phases, Ba₂(Gd_xY_1−x)NbO₆ (Fm3¯m, No. 225), and (Gd_xY_3−x)NbO₇ (C222₁, No. 20 and Ccmm, No. 63), were completed using the X-ray Rietveld refinement technique. Reference X-ray powder diffraction patterns for selected phases of Ba₂(Gd_xY_1−x)NbO₆ (x=0.2, 0.4, 0.6, and 0.8) and (Gd_xY_3−x)NbO₇ (x=0.6, 1.2, 1.8, 2.4 and 3) have been prepared for inclusion in the Powder Diffraction File (PDF).     

Charge compensation and oxidation in NaxCoO2−δ and LixCoO2−δ studied by XANES

A comparative study on the oxidation and charge compensation in the A_xCoO_2−δ systems, A=Na (x=0.75, 0.47, 0.36, 0.12) and Li (x=1, 0.49, 0.05), using X-ray absorption spectroscopy at O 1s and Co 2p edges is reported. Both the O 1s and Co 2p XANES results show that upon removal of alkali metal from A_xCoO_2−δ the valence of cobalt increases more in Li_xCoO_2−δ than in Na_xCoO_2−δ. In addition, the data of O 1s XANES indicate that charge compensation by oxygen is more pronounced in Na_xCoO_2−δ than in Li_xCoO_2−δ.     

Synthesis of layered cathode material Li[CoxMn1−x]O2 from layered double hydroxides precursors

Cathode materials Li[Co_xMn_1−x]O₂ for lithium secondary batteries have been prepared by a new route—precursor method of layered double hydroxides (LDHs). In situ high-temperature X-ray diffraction (HT-XRD) and thermogravimetric analysis coupled with mass spectrometry (TG-MS) were used to monitor the structural transformation during the reaction of CoMn LDHs and LiOH·H₂O: firstly the layered structure of LDHs transformed to an intermediate phase with spinel structure; then the distortion of the structure occurred with the intercalation of Li⁺ into the lattice, resulting in the formation of layered Li[Co_xMn_1−x]O₂ with α-NaFeO₂ structure. Extended X-ray absorption fine structure (EXAFS) data showed that the Co-O bonding length and the coordination number of Co were close to those of Mn in Li[Co_xMn_1−x]O₂, which indicates that the local environments of the transitional metals are rather similar. X-ray photoelectron spectroscopy (XPS) was used to measure the oxidation state of Co and Mn. The influences of Co/Mn ratio on both the structure and electrochemical property of Li[Co_xMn_1−x]O₂ have been investigated by XRD and electrochemical tests. It has been found that the products synthesized by the precursor method demonstrated a rather stable cycling behavior, with a reversible capacity of 122.5 mAh g⁻¹ for the layered material Li[Co_0.80Mn_0.20]O₂.     

The clathrate Ba8CuxGe46−x−y□y: Phase equilibria and crystal structure

Phase relations at 700 °C, 800 °C and solidus temperatures have been derived for the clathrate system Ba₈Cu_xGe_46−x−y□_y via X-ray single crystal and powder diffractometry combined with electron probe micro analysis and differential thermal analysis. The ternary clathrate phase derives from binary Ba₈Ge₄₃□₃ and extends up to x=6. Structure investigations define cubic primitive symmetry with the space group type consistent with a clathrate type I structure throughout the entire homogeneity region 0<x?6 but defect-free Ba₈Cu_xGe_46−x exists for x?5.5.     

The crystal structure of the LiAg2In compound

The newly established intermetallic compound LiAg₂In crystallizes in the MnCu₂Al-type structure (Fm-3m, Heusler phase) with . The homogeneity range of this phase in the ternary Li-Ag-In phase diagram along the adjacent quasibinary cut Li_0.25(Ag_1−xIn_x)_0.75 was determined by X-ray powder diffraction and extends from x∼0.33, Li_0.25Ag_0.50In_0.25, up to x∼0.44, Li_0.25Ag_0.42In_0.33. The homogeneity ranges of Heusler- and Zintl-type phases in the Li-Ag-In system are separated from each other by a broad heterogeneous region.     

Neutron diffraction study of the crystal structure and structural phase transition of La0.7Ca0.3−xSrxCrO3 (0≤x≤0.3): The relationship between thermodynamic behavior and crystal structure changes at the phase transition

The crystal structure of the La_0.7Ca_0.3−xSr_xCrO₃ series, including the compositional and temperature dependence of the structural parameters, has been studied by variable temperature neutron diffraction measurements. The extent of the distortions from the ideal cubic perovskite structure has been evaluated quantitatively using the average bond lengths and the mean volumes of the [CrO₆] octahedron and [(La/Ca/Sr)O₁₂] polyhedron, and has been shown to decrease with increase of Sr content or temperature. At the structural phase transition from the orthorhombic (Pnma) structure to the rhombohedral one, the volume of the [CrO₆] octahedron decreases whereas that of the [(La/Ca/Sr)O₁₂] polyhedron shows little difference, resulting in an overall decrease in the level of distortion. The change in the degree of distortion at the phase transition decreases with increase of Sr content, in agreement with the smaller variation of the enthalpy and volume for the specimens with higher Sr content.     

Local environment in Ba2In2−xWxO5+3x/2 oxide ion conductors

The actual oxygen environment of the tungsten dopant in the Ba₂In_2−xW_xO_5+3x/2 solid solution was revealed by combining X-ray absorption spectroscopy at the tungsten L_I and L_III edges and at the indium L_I edge. Whatever the substitution ratio, the tungsten atoms exhibit a regular octahedral environment. When the substitution ratio increases, the oxygen vacancies are progressively filled until their total occupancy for x=2/3. For x?0.3, the perovskite structure is stabilised; the tungsten atoms are randomly distributed in the structure. Although X-ray diffraction revealed a cubic symmetry for these compositions, a local distortion of the indium environment is observed when a tungsten atom is in its surrounding.     

Evolution of structure and magnetic properties in electron-doped double perovskites, Sr2−xLaxMnWO6 (0?x?1)

Powder neutron and X-ray diffraction studies show that the double perovskites in the region 0?x?1 exhibit two crystallographic modifications at room temperature: monoclinic P2₁/n and tetragonal I4/m, with a boundary at 0.75<x<0.9. Magnetic susceptibility measurements indicate that for x=0 and 0.5 Sr_2−xLa_xMnWO₆ orders antiferromagnetically (AFM) at 15 and 25 K, respectively, for 0.75?x<1.0, a contribution of weak ferromagnetism (FM), probably due to canted-AFM order, increases with increasing x. The end point compound SrLaMnWO₆ shows the strongest FM cluster effect; however, no clear evidence of magnetic order is discernable down to 4.2 K. X-ray absorption spectroscopy (XAS) confirms Mn²⁺ and mixed-valent W^6+/5+ formal oxidation states in Sr_2−xLa_xMnWO₆.     

A novel route to synthesize cubic ZrW2−xMoxO8 (x=0-1.3) solid solutions and their negative thermal expansion properties

Cubic ZrW_2−xMo_xO₈ (c-ZrW_2−xMo_xO₈) (x=0-1.3) solid solutions were prepared by a novel polymorphous precursor transition route. X-ray diffraction (XRD) analysis reveals that the solid solutions are single phase with α- and β-ZrW₂O₈ structure for 0?x?0.8 and 0.9?x?1.3, respectively. The optimum synthesis conditions of ZrWMoO₈ are obtained from differential scanning calorimetry-thermal gravimetric analysis (DSC-TGA), XRD and mass loss-temperature/time curves. Following the above experience, the stoichiometric solid solutions of c-ZrW_2−xMo_xO₈ (x=0-1) are obtained within 1 wt% of mass loss. The relationships of lattice parameters (a), phase transition temperatures (T_c) and instantaneous coefficients of thermal expansion (α_i) against the content x of Mo are discussed based on the variation of order degree parameters of ZrW_2−xMo_xO₈.     

Zr1−xLnxW2O8−x/2 (Ln=Eu, Er, Yb): Solid solutions of negative thermal expansion-synthesis, characterization and limited solid solubility

Zr_1−xLn_xW₂O_8−x/2 solid solutions (Ln=Eu, Er, Yb) of different substitution fractions x have been synthesized. Their X-ray diffraction (XRD) patterns have been indexed and lattice parameters calculated based on the α-ZrW₂O₈ structure. The coefficients of thermal expansion (CTEs) of these solid solutions were estimated to be −10.3×10⁻⁶ K⁻¹ in temperature range of 30-100 °C. The solubility of lanthanide ions in these solid solutions decreases linearly with the increase in the radius of substituted lanthanide ions. Based on the concentration dependence of phase transition temperatures, a novel method for determination of solubility of the lanthanide ions in Zr_1−xLn_xW₂O_8−x/2 solid solutions has been developed. This method seems to be more sensitive as compared with that based on XRD technique.     

A novel boron-rich quaternary scandium borocarbosilicide Sc3.67−xB41.4−y−zC0.67+zSi0.33−w

A novel quaternary scandium borocarbosilicide Sc_3.67−xB_41.4−y−zC_0.67+zSi_0.33−w was found. Single crystallites were obtained as an intergrowth phase in the float-zoned single crystal of Sc_0.83−xB_10.0−yC_0.17+ySi_0.083−z that has a face-centered cubic crystal structure. Single crystal structure analysis revealed that the compound has a hexagonal structure with lattice constants a = b = 1.43055(8) nm and c = 2.37477(13) nm and space group (No. 187). The crystal composition calculated from the structure analysis for the crystal with x = 0.52, y = 1.42, z = 1.17, and w = 0.02 was ScB_12.3C_0.58Si_0.10 and that agreed rather well with the composition of ScB_11.5C_0.61Si_0.04 measured by EPMA. In the crystal structure that is a new structure type of boron-rich borides, there are 79 structurally independent atomic sites, 69 boron and/or carbon sites, two silicon sites and eight scandium sites. Boron and carbon form seven structurally independent B₁₂ icosahedra, one B₉ polyhedron, one B₁₀ polyhedron, one irregularly shaped B₁₆ polyhedron in which only 10.7 boron atoms are available because of partial occupancies and 10 bridging sites. All polyhedron units and bridging site atoms interconnect each other forming a three-dimensional boron framework structure. Sc atoms reside in the open spaces in the boron framework structure.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.