Ni/SiO2-ZrO2催化剂焙烧温度对其催化愈创木酚加氢脱氧性能的影响简

采用化学沉淀法合成了SiO₂-ZrO₂复合氧化物载体,并以浸渍法制备了Ni/SiO₂-ZrO₂双功能催化剂,考察了焙烧温度对催化剂结构及其催化愈创木酚加氢脱氧制环己烷性能的影响. 结果表明,经500℃焙烧催化剂的加氢脱氧活性最高,在Ni金属中心和SiO₂-ZrO₂载体材料的协同作用下,愈创木酚转化率为100%,环己烷选择性为96.8%. 对催化剂进行N₂物理吸附、H₂化学吸附、X射线衍射分析、H₂程序升温还原、NH₃程序升温脱附与Raman光谱等表征后发现,合成的SiO₂-ZrO₂为无定形的酸碱两性氧化物;经500℃焙烧的催化剂样品的有效比表面积和孔体积均明显增大,表面酸量最多,硝酸镍分解成小颗粒的NiO较易被H₂还原,这些特性是该催化剂样品具有高效加氢脱氧活性的原因.     

Preparation and characterization of SiO2/TiO2 composite microspheres with microporous SiO2 core/mesoporous TiO2 shell

SiO₂/TiO₂ composite microspheres with microporous SiO₂ core/mesoporous TiO₂ shell structures were prepared by hydrolysis of titanium tetrabutylorthotitanate (TTBT) in the presence of microporous silica microspheres using hydroxypropyl cellulose (HPC) as a surface esterification agent and porous template, and then dried and calcined at different temperatures. The as-prepared products were characterized with differential thermal analysis and thermogravimetric (DTA/TG), scanning electron microscopy (SEM), X-ray diffraction (XRD), nitrogen adsorption. The results showed that composite particles were about 1.8 μm in diameter, and had a spherical morphology and a narrow size distribution. Uniform mesoporous titania coatings on the surfaces of microporous silica microspheres could be obtained by adjusting the HPC concentration to an optimal concentration of about 3.2 mmol L⁻¹. The anatase and rutile phase in the SiO₂/TiO₂ composite microspheres began to form at 700 and 900 °C, respectively. At 700 °C, the specific surface area and pore volume of the SiO₂/TiO₂ composite microspheres were 552 and 0.652 mL g⁻¹, respectively. However, at 900 °C, the specific surface area and pore volume significantly decreased due to the phase transformation from anatase to rutile.     

Regioselective bromination of aromatic compounds with Br2/SO2Cl2 over microporous catalysts

A new selective brominating system Br₂/SO₂Cl₂/zeolite, has been discovered. Partially cation-exchanged Ca²⁺-Y zeolite efficiently catalyzes the selective para-bromination of neat chlorobenzene (CB) by Br₂/SO₂Cl₂ affording a CB conversion of ∼89% and a para-selectivity of ∼97%. During the bromination reaction, SO₂Cl₂ oxidizes HBr, prevents its accumulation within the zeolite pores and yields a more active brominating species. The Ca²⁺-Y catalyst was found to be stable under the bromination conditions, and can easily be regenerated by calcination. The Br₂/SO₂Cl₂/Ca²⁺-Y brominating system could be applicable to other activated aromatic compounds such as o-xylene, toluene and fluorobenzene.     

CeO2-ZrO2复合氧化物的制备及协同抛光性能

Sub-micrometer ultra fine CeO₂-ZrO₂ mixed oxides have been prepared by milling solid cerium carbonate and zirconium oxy-chloride with ammonia and followed by filtering, drying and calcining procedures. The effects of Ce/Zr molar ratio, milling time and calcining temperature on the phase composition, particle size and morphology, surface charge, as well as the polishing property were investigated. The results show that the mixed oxide calcined at 1 000 ℃ is composed of cubic ceria doped with zirconium and tetragonal zirconia doped with cerium, and the phase composition varies with calcination temperature and the Ce/Zr molar ratio. The monoclinic zirconia is observed when decreasing calcination temperature and shortening milling time, demonstrating that milling and calcining can force the phase transformation from monoclinic zirconia to cerium stabilized tetragonal zirconia and zirconium doped cubic ceria solid solutions. The removal rate for the optical glass polishing varies with Ce/Zr molar ratio. A synergetic polishing effect is found when Ce/Zr molar ratio below 4, and the optimal Ce/Zr molar ratio is 1∶1. At the same time, the cubic ceria content, density, particle size and surface charge all increase when calcination temperature increasing from 800 ℃ to 1 100 ℃. However, the particle morphology changes from disperse quasi-sphere to irregular aggregation and the maximal removal rate for optical glass polishing lies at 1 000 ℃.These facts show that the polishing property of the synthesized ceria-zirconia mixed oxide is affected by the particle physical characteristics comprehensively.     

Al2O3-ZrO2复合膜的制备与表征

以异丙醇铝和氧氯化锆为原料,用溶胶-凝胶法在Al₂O₃中空纤维上制备了Al₂O₃-ZrO₂复合膜。应用TG、DTA、XRD、SEM等测试手段对复合膜的热稳定性、结构、形貌进行了表征。结果表明复合膜的热稳定性比单一由氧化铝或氧化锆制成的膜有显著的提高,在1100℃之前,复合膜以t-ZrO₂存在,1200℃时,出现了m-ZrO₂和α-Al₂O₃相。扫描电镜分析表明,膜表面完整、无缺陷。气体渗透实验进一步表明所得膜具有一定的气体选择性,0.3MPa和0.5MPa下对氮气和氩气的分离因子α分别为1.191和1.185,和氮气与氩气的理论分离因子(α=1.194)相当,说明气体通过膜的扩散以Knudsen扩散传质为主。用等温氮气吸附实验测定了非担载膜的孔径大小和分布,最可几孔径约为4.3nm。     

Synthesis and characterization of Fe2O3/SiO2 nanocomposites

Fe₂O₃/SiO₂ nanocomposites based on fumed silica A-300 (S_BET = 337 m²/g) with iron oxide deposits at different content were synthesized using Fe(III) acetylacetonate (Fe(acac)₃) dissolved in isopropyl alcohol or carbon tetrachloride for impregnation of the nanosilica powder at different amounts of Fe(acac)₃ then oxidized in air at 400–900 °C. Samples with Fe(acac)₃ adsorbed onto nanosilica and samples with Fe₂O₃/SiO₂ including 6–17 wt% of Fe₂O₃ were investigated using XRD, XPS, TG/DTA, TPD MS, FTIR, AFM, nitrogen adsorption, Mössbauer spectroscopy, and quantum chemistry methods. The structural characteristics and phase composition of Fe₂O₃ deposits depend on reaction conditions, solvent type, content of grafted iron oxide, and post-reaction treatments. The iron oxide deposits on A-300 (impregnated by the Fe(acac)₃ solution in isopropanol) treated at 500–600 °C include several phases characterized by different nanoparticle size distributions; however, in the case of impregnation of A-300 by the Fe(acac)₃ solution in carbon tetrachloride only α-Fe₂O₃ phase is formed in addition to amorphous Fe₂O₃. The Fe₂O₃/SiO₂ materials remain loose (similar to the A-300 matrix) at the bulk density of 0.12–0.15 g/cm³ and S_BET = 265–310 m²/g.     

大尺寸TiO2/SiO2大孔材料的制备及光降解性能

先以三维骨架聚合物为整体型模板,利用硅酸酯原位溶胶-凝胶过程并结合高温烧结的方法制备出大尺寸大孔径的SiO2载体,然后通过钛酸丁酯溶液浸渍、原位水解、煅烧制备出大尺寸的TiO2/SiO2大孔材料并用SEM、TEM、FTIR、XRD和XPS对其表征,结果表明SiO2载体具有三维连续的超薄层,TiO2以纳米薄层方式均匀地沉积在SiO2的三维超薄层上,形成TiO2/SiO2/TiO2三层夹心结构,层与层界面存在Si-O-Ti键,同时复合结构提高了TiO2由锐钛矿相向金红石相的转变温度.以甲基橙为目标降解物考察不同条件下制备的复合材料的光催化活性,采用复合材料吸入甲基橙溶液的方式,并借助甲醇萃取手段研究光降解动力学过程.结果表明,该复合材料具有较好的光降解催化活性,当焙烧温度为600℃和TiO2的负载量为54.5wt%时,其活性最大且降解速率常数达到1.78 h-1.     

稀土掺杂SiO2与SiO2@Au纳米球

By using EDTA-lanthanide (Eu³⁺， Tb³⁺) coordination compound as precursor， multicolor luminescent SiO₂ nanoshperes were prepared. Also， without any pre-treatment to the surface of SiO₂ nanosphere， a facile strategy was developed for the synthesis of SiO₂@Au core-shell nanospheres.     

水热法制备高纯超细CeO2-ZrO2复合氧化物

Superfine composite powders of CeO₂-ZrO₂ (CZ) and CeO₂-ZrO₂-La₂O₃ (CZL) were prepared by hydrothermal method. The effects of pH、temperature and time for hydrothermal process on the performance of the resulting powders were studied. The optimized reaction parameters were on follows: the precursor′s pH≈9.0, hydrothermal temperature of 200 ℃ holding for 2 h. Thermal stable powders with average particle size smaller than 10 nm and specific surface area of 171 m²·g^-1 were obtained. A BET specific surface area was still at 44 m²·g^-1 after calcination at 1 000 ℃ for 6 hours.     

Preparation of uniform rhodamine B-doped SiO2/TiO2 composite microspheres

Uniform rhodamine B (RB)-doped SiO₂/TiO₂ composite microspheres with catalytic and fluorescent properties were prepared by an easy and economical method in this paper. The composite microspheres were built up with well-dispersed silica particles as the cores, RB as both the doped agent and stabilizer, and the TiO₂ shells were obtained through the hydrolysis of TiCl₄ in water bath. The morphology and structure of the particles were characterized by scanning electron microscopy (SEM) and X-ray powder diffraction (XRD). The characterization results indicate that composite particles are all in spherical shape and have a narrow size distribution. The composite particles calcined above 500 °C reveal clear crystalline reflection peaks of the rutile TiO₂ which exhibits well catalytic property. The photocatalytic experiment was carried out in order to examine the catalytic property of composite microspheres. The fluorescent property of particles was also investigated. Dye-leakage test indicates that RB molecules entrapped in the composite particles by this method are stable inside the particles.     

A Simple Approach to Fabricate CdS-SiO2 Hybrid Microspheres by Producing CdS Nanoparticles on the Surface of Thiolated SiO2 Microspheres

IntroductionSemiconductor nanoparticles show a quantum sizeeffect and have attracted much attention because oftheir unique photochemical and photophysical proper-ties[1—4].In recent years,quantumdots of CdS and in-organic nanoparticles hybrid composites …     

SiO2-CeO2复合氧化物的制备及抛光性能

采用正硅酸乙酯溶胶-凝胶法制备纳米SiO₂，并与氯化铈溶液混合，用氨水沉淀法制备了SiO₂-CeO₂复合氧化物。利用XRD、SEM等手段对其物相类型、外观形貌、颗粒大小、表面电位等物理性能进行了表征，测定了它们对3种光学玻璃的抛光速率。结果表明：合成复合氧化物具有立方萤石型结构，由Sherrer方程计算的晶粒D_XRD(200)小于100 nm甚至10 nm。随着SiO₂复配量的增加和煅烧温度的降低，晶粒度减小，比表面增大；激光粒度分析仪测定的中位粒径D₅₀在2～3 μm之间，且随SiO₂复配量的增加呈增大趋势，但随煅烧温度的变化在800 ℃时出现极小值，而此时的ζ电位的负值最大，对3种玻璃的抛光速率也最大。证明抛光速率与表面电位及相应的悬浮性、颗粒大小有直接关系。随着SiO₂复配量的增加，复合氧化物的ζ电位负值及对3种玻璃的抛光速率均增大。因此，在CeO₂中复配SiO₂是提高抛光速率的有效方法，此时，最佳的煅烧温度为800 ℃。     

表面覆盖SiO2用于提高Pt-Pd/CeO2-ZrO2-Al2O3商用柴油机氧化型催化剂的抗硫性

向Pt-Pd/CeO₂-ZrO₂-Al₂O₃ （Pt-Pd/CZA）商用柴油机氧化型催化剂（DOC）中加入多孔SiO₂以提高其抗硫性. 使用多层涂覆法在Pt-Pd/CZA 催化剂表面覆盖一层多孔SiO₂,从而制得SiO₂/Pt-Pd/CeO₂-ZrO₂-Al₂O₃（SiO₂/Pt-Pd/CZA）抗硫DOC. 并使用扫描电子显微镜（SEM）,H₂程序升温还原（H₂-TPR）,氮气吸脱附,X射线能谱（EDX）和热重分析（TGA）等对其进行表征. SEM结果显示,SiO₂层以多孔形式均匀覆盖在催化剂表面. 氮气吸脱附结果表明,所添加的SiO₂的织构性质与Pt-Pd/CZA 催化剂的织构性质相似,因而表面覆盖的SiO₂并未明显改变Pt-Pd/CZA催化剂的比表面积和孔结构. H₂-TPR结果证实表面覆盖的SiO₂不影响Pt-Pd/CZA催化剂的还原性能. EDX和TGA结果说明表面覆盖SiO₂可以抑制硫物种在催化剂表面的形成及累积. 最终,本文所制备的SiO₂/Pt-Pd/CZA催化剂在保持Pt-Pd/CZA商用DOC的高活性及耐久性的同时有效提高了其抗硫性.     

Preparation, characterization, and infrared emissivity property of optically active polyurethane/TiO2/SiO2 multilayered microspheres

Optically active polyurethane/titania/silica (LPU/TiO₂/SiO₂) multilayered core–shell composite microspheres were prepared by the combination of titania deposition on the surface of silica spheres and subsequent polymer grafting. LPU/TiO₂/SiO₂ was characterized by FT-IR, UV–vis spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), SEM and TEM, and the infrared emissivity value (8–14 μm) was investigated in addition. The results indicated that titania and polyurethane had been successfully coated onto the surfaces of silica microspheres. LPU/TiO₂/SiO₂ exhibited clearly multilayered core–shell construction. The infrared emissivity values reduced along with the increase of covering layers thus proved that the interfacial interactions had direct influence on the infrared emissivity. Besides, LPU/TiO₂/SiO₂ multilayered microspheres based on the optically active polyurethane took advantages of the orderly secondary structure and strengthened interfacial synergistic actions. Consequently, it possessed the lowest infrared emissivity value.     

SiO2负载氮掺杂TiO2可见光响应光催化剂的制备及性能

以四氯化钛为钛源,尿素为氮源,采用液相水解-沉淀法制得SiO2负载N掺杂TiO2可见光响应TiO2-xNy/SiO2光催化剂(TSN)。以苯酚为模型物,考察了TSN在可见光区、紫外光区及太阳光下的光催化活性,以及催化剂的使用寿命、分离性能。采用XPS、FTIR、UV-Vis DRS、XRD、TEM和低温氮物理吸附等对催化剂的结构进行表征。结果表明,N以阴离子形式进入TiO2体相并置换晶格中的O,适量N掺杂的TSN在紫外光区、可见光区及太阳光下均表现出较高的活性。SiO2与TiO2界面间有Ti-O-Si键形成,结合牢固。N掺杂在TiO2表面生成Ti-O-N键,形成新的能级结构,使催化剂的吸收红移至450~500 nm,诱发TiO2可见光催化活性。SiO2负载可减小TiO2颗粒平均尺寸,增加催化剂比表面积;同时SiO2负载还可改善催化剂的分离性能,提高催化剂使用寿命。     

SiO2 /Au核壳结构纳米粒子的制备及表征

通过以金纳米粒子为表面晶种和壳生长的方法制备了金纳米壳包覆二氧化硅的复合纳米粒子。采用TEM 和UV-Vis对复合粒子进行了表征和研究，结果表明所得到的复合粒子粒径均匀、金纳米壳光滑完整，且壳厚度可通过反应物的用量来控制。当核半径与壳厚度之比在4到13之间变化时,复合粒子的光学共振峰在可见光区到近红外光区范围内可发生大于500 nm波长的移动。     

Preparation and characterization of highly dispersed V2O5/SiO2prepared by a CVD method

Highly dispersed V₂O₅/SiO₂(CVD catalyst) was prepared by the reaction of vaporized VO(OPrⁱ)₃ with silica at 293 K, whose process was followed by an IR technique. The rate of propylene photooxidation increased with an increase in V₂O₅ loading for CVD catalysts, but leveled off for impregnated ones. The CVD catalysts were characterized by XAFS and photoluminescence spectroscopy.     

SiO2/ZnO复合纳米粒子的制备及表征

采用双注控制沉积法(Controlled Double-Jet Precipitation,CDJP)将反应物添加到含有SiO₂的溶液中,通过直接的表面反应来制备单分散的SiO₂/ZnO复合纳米粒子,并对其进行了表征。透射电镜(TEM)观察表明,SiO₂表面有一层ZnO纳米颗粒或薄层。对复合纳米粒子SiO₂/ZnO进行X射线衍射(XRD)分析,复合颗粒的衍射峰与单独的氧化锌的衍射峰完全一致。能量弥散X射线法(EDX)分析表明,复合颗粒中含有Zn、Si、O元素。荧光光谱表明有ZnO的吸收峰。     

静电自组装制备纳米TiO2/SiO2光催化材料

采用静电自组装方法制备了纳米TiO2/SiO2光催化材料。采用巯丙基三甲氧基硅烷偶联剂对SiO2进行干法改性,采用双氧水/冰醋酸将偶联剂巯基基团氧化为磺酸基基团。在正负电荷的吸引下,带负电荷的SiO2与带正电荷的钛聚合阳离子自发地组装在一起,经一定温度热处理得到纳米TiO2/SiO2光催化材料。采用XRD、FTIR、PL、UV-Vis DRS、SEM和ICP等对材料进行了分析和表征。采用甲基橙溶液评价材料的光催化性能。结果表明:SiO2促使锐钛矿的形成,抑制锐钛矿向金红石的转变,减小TiO2的晶粒尺寸,使得TiO2光吸收波长发生蓝移。TiO2与SiO2通过Si-O-Ti键发生结合。采用静电自组装方法制备的材料中TiO2的含量高于传统方法,导致材料的光催化性能有所提高。