Synthesis of Gd3PO7:Eu nanospheres via a facile combustion method and optical properties

Eu³⁺-doped Gd₃PO₇ nanospheres with an average diameter of ∼300 nm and a narrow size distribution have been prepared by a facile combustion method and structurally characterized by X-ray diffraction and field emission scanning electron microscopy. The luminescent properties were systemically studied by the measurement of excitation/emission spectra, and emission spectra under different temperatures, as well as by photostability. The strong red-emission intensity peaking at 614 nm originates the ⁵D₀→⁷F₂ transition and is observed under 254-nm irradiation, indicating that Eu³⁺ ions in Gd₃PO₇ mainly occupied non-centrosymmetry sites. The CIE1931 XY chromaticity coordinates of Gd₃PO₇:Eu³⁺ nanospheres are (x=0.654, y=0.345) in the red area, which is near the National Television Standard Committee standard chromaticity coordinates for red. Thus, Gd₃PO₇:Eu³⁺ nanospheres may be potential red-emitting phosphors for PDP and Xe-based mercury-free lamps.     

A novel red emitting phosphor Ca2SnO4: Eu

A novel red emitting phosphor, Eu³⁺-doped Ca₂SnO₄, was prepared by the solid-state reaction. X-ray powder diffraction (XRD) analysis confirmed the formation of Ca₂SnO₄: Eu³⁺. Field-emission scanning electron-microscopy (FE-SEM) observation indicated a narrow size-distribution of about 500 nm for the particles with spherical shape. Photoluminescence measurements indicated that the phosphor exhibits bright red emission at about 615 nm under UV excitation. The excellent luminescence properties make it possible as a good candidate for plasma display panels (PDP) application. Splitting of the ⁵D₀-⁷F_J transitions of Ca₂SnO₄: Eu³⁺ suggests that the Eu³⁺ ions occupied two nonequivalent sites in the crystallite. The luminescence lifetime measurement showed a bi-exponential decay, providing other evidence for the existence of two different environments for Eu³⁺ ions.     

A new phosphor with flower-like structure and luminescent properties of Sr<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript>: Eu<Superscript>2+</Superscript>, Dy<Superscript>3+</Superscript> long afterglow materials by sol–gel method

The flower-like phosphors of Sr₂MgSi₂O₇: Eu²⁺, Dy³⁺ with high brightness and long afterglow were obtained by sol–gel method. X-ray diffraction pattern (XRD) shows that single-phased Sr₂MgSi₂O₇ phosphor is prepared by sol–gel method under 1250 °C. Scanning electron microscope (SEM) indicates that the phosphor consists of nano-sized whiskers which are detected for the first time in Eu²⁺ and Dy³⁺ co-doped long-lasting phosphorescence silicates. Furthermore, the investigation on the mechanism indicates that the internal structure and gas, liquid and solid phase effect play important roles in the formation of flower-like Sr₂MgSi₂O₇: Eu²⁺, Dy³⁺ nanostructure. Finally, the optical properties of flower-like Sr₂MgSi₂O₇ nanostructure have been characterized by photoluminescence (PL) spectra.     

A new promising phosphor, Na3La2(BO3)3:Ln (Ln=Eu, Tb)

We present an efficient way to search a host for ultraviolet (UV) phosphor from UV nonlinear optical (NLO) materials. With the guidance, Na₃La₂(BO₃)₃ (NLBO), as a promising NLO material with a broad transparency range and high damage threshold, was adopted as a host material for the first time. The lanthanide ions (Tb³⁺ and Eu³⁺)-doped NLBO phosphors have been synthesized by solid-state reaction. Luminescent properties of the Ln-doped (Ln=Tb³⁺, Eu³⁺) sodium lanthanum borate were investigated under UV ray excitation. The emission spectrum was employed to probe the local environments of Eu³⁺ ions in NLBO crystal. For red phosphor, NLBO:Eu, the measured dominating emission peak was at 613 nm, which is attributed to ⁵D₀-⁷F₂ transition of Eu³⁺. The luminescence indicates that the local symmetry of Eu³⁺ in NLBO crystal lattice has no inversion center. Optimum Eu³⁺ concentration of NLBO:Eu³⁺ under UV excitation with 395 nm wavelength is about 30 mol%. The green phosphor, NLBO:Tb, showed bright green emission at 543 with 252 nm excited light. The measured concentration quenching curve demonstrated that the maximum concentration of Tb³⁺ in NLBO was about 20%. The luminescence mechanism of Ln-doped NLBO (Tb³⁺ and Eu³⁺) was analyzed. The relative high quenching concentration was also discussed.     

Efficient photoluminescence of Dy at low concentrations in nanocrystalline ZrO2

Nanocrystalline ZrO₂:Dy³⁺ were prepared by sol-gel and the structural and photoluminescence properties characterized. The crystallite size ranges from 20 to 50 nm and the crystalline phase is a mixture of tetragonal and monoclinic structure controlled by dopant concentration. Strong white light produced by the host emission band centered at ∼460 nm and two strong Dy³⁺ emission bands, blue (488 nm) and yellow (580 nm), under direct excitation at 350 nm were observed. The highest efficiency was obtained for 0.5 mol% of Dy³⁺. Emission is explained in terms of high asymmetry of the host suggesting that Dy³⁺ are substituted mainly into Zr⁴⁺ lattice sites at the crystallite surface. Luminescence quenching is explained in terms of cross-relaxation of intermediate Dy³⁺ levels.     

Preparation and optical properties of SrF2:Eu nanospheres

SrF₂:Eu³⁺ nanospheres with homogeneous diameter have been synthesized by a microemulsion-mediated hydrothermal method for the first time, in which quaternary microemulsion of CTAB/water/cyclohexane/n-pentanol was used. The possible reaction mechanism and the luminescent properties of SrF₂:Eu³⁺ nanospheres were also investigated in this paper. The morphology and grain sizes of final products were characterized by field emission scanning electron microscopy and transmission electron microscopy, indicating that most of the products were nanospheres with an average diameter of ∼50 nm. Room-temperature emission spectra, recorded under 394-nm excitation, showed that the transition of ⁵D₀ → ⁷F₁ emission be dominating in SrF₂:Eu³⁺ nanospheres. From the dependence of the luminescence intensity on the concentration of Eu³⁺ ions, the optimal dopant concentration is 2 mol%.     

Synthesis, vacuum ultraviolet and near ultraviolet-excited luminescent properties of GdCaAl3O7: RE (RE=Eu, Tb)

Vacuum ultraviolet (VUV) excitation and photoluminescent (PL) properties of Eu³⁺ and Tb³⁺ ion-doped aluminate phosphors, GdCaAl₃O₇:Eu³⁺ and GdCaAl₃O₇:Tb³⁺ have been investigated. X-ray diffraction (XRD) patterns indicate that the phosphor GdCaAl₃O₇ forms without impurity phase at 900 °C. Field emission scanning electron microscopy (FE-SEM) images show that the particle size of the phosphor is less than 3 μm. Upon excitation with VUV irradiation, the phosphors show a strong emission at around 619 nm corresponding to the forced electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺, and at around 545 nm corresponding to the ⁵D₄→⁷F₅ transition of Tb³⁺. The results reveal that both GdCaAl₃O₇:RE³⁺ (RE=Eu, Tb) are potential candidates as red and green phosphors, respectively, for use in plasma display panel (PDP).     

Enhanced ultraviolet up-conversion emissions of Tm/Yb codoped YF3 nanocrystals

Tm³⁺/Yb³⁺ codoped rod-like YF₃ nanocrystals were synthesized through a facile hydrothermal method. After annealing in an argon atmosphere, the nanocrystals emitted bright blue and intense ultraviolet (UV) light under a 980-nm continuous wave diode laser excitation. Up-conversion emissions centered at ∼291 nm (¹I₆ → ³H₆), ∼347 nm (¹I₆ → ³F₄), ∼362 nm (¹D₂ → ³H₆), ∼452 nm (¹D₂ → ³F₄), ∼476 nm (¹G₄ → ³H₆), ∼642 nm (¹G₄ → ³F₄), and ∼805 nm (³H₄ → ³H₆) were recorded using a fluorescence spectrophotometer. Especially, enhanced UV emissions were studied by changing Yb³⁺/Tm³⁺ doping concentrations, the annealing temperatures, and the excitation power densities. A possible mechanism, energy transfer-cross relaxation-energy transfer (ET-CR-ET), was proposed based on a simple rate-equation model to elucidate the process of the enhanced UV emissions.     

A novel blue-emitting phosphor LiSrPO4:Eu for white LEDs

A novel blue-emitting phosphor, LiSrPO₄:Eu²⁺, was prepared by the solid-state reaction and X-ray powder diffraction (XRD) analysis confirmed the formation of LiSrPO₄:Eu²⁺. Photoluminescence (PL) results showed that the phosphor can be efficiently excited by UV-visible light from 250 to 440 nm, and exhibited bright blue emission. The effects of the doped-Eu²⁺ concentration in LiSrPO₄:Eu²⁺ on the PL were investigated in detail. The results showed that the relative PL intensity increases with Eu²⁺-concentration increasing until a maximum intensity is reached, and then it decreases due to concentration quenching and a red-shift appears, which are explained satisfactorily with the luminescent theory. Upon excited with 396 nm light, the present synthesized phosphor has higher emission intensity than that from the commercial blue phosphor, BaMgAl₁₀O₁₇:Eu²⁺. Bright blue light-emitting diodes were fabricated by the combination of the synthesized LiSrPO₄:Eu²⁺ with ∼397 nm emitting InGaN-based chips.     

Tb3+在MO(M=Ca,Sr)中的长余辉发光

长余辉发光材料的研究与应用，已有近100年的历史，目前仍在许多领域中有着重要应用。此类材料与其他光致发光材料具有相同的发光性能．只是更注重其发光的衰减过程和热释光性能。如．ZnS：Cu作为黄绿色的长余辉发光材料，在1992年以前是余辉性能最好的长余辉发光材料，一直处于发光研究工作的中心。     

Photoluminescence of Eu-doped triple phosphate Ca8MgR(PO4)7 (R=La, Gd, Y)

Eu³⁺-doped triple phosphate Ca₈MgR(PO₄)₇ (R=La, Gd, Y) was synthesized by the general high-temperature solid-state reaction. Excitation and emission spectra as well as luminescence decay were used to characterize the phosphors. Photoluminescence excitation and emission spectra showed that the phosphor could be efficiently excited by UV-vis light from 260 to 450 nm to give bright red emission assigned to the transition (⁵D₀→⁷F₂) at 612 nm. The richness of the red color has been verified by determining their color coordinates (X, Y) from the CIE standard.     

The dependence of persistent phosphorescence on annealing temperatures in CaTiO3:Pr nanoparticles prepared by a coprecipitation technique

Red emitting phosphors of CaTiO₃:Pr³⁺ nanoparticles with size ranging from 6 to 95 nm have been prepared by a coprecipitation technique and structurally characterized by X-ray diffraction, energy dispersive spectroscopy and scanning electron microscopy. The fluorescence and phosphorescence of CaTiO₃:Pr³⁺ nanoparticles as a function of annealing temperature are investigated. It is found that fluorescence intensities monotonously increase with increasing temperature. However, a maximum in phosphorescence with the increase of annealing temperature occurs for the sample prepared at 700 °C. Based on the measurement of fluorescence emission, fluorescence excitation and reflectance spectra as well as time decay patterns of fluorescence and phosphorescence, it is demonstrated that the dependence of fluorescence and phosphorescence on annealing temperature originates from the decrease of surface defects with the increase of temperature.     

Fabrication and luminescent properties of rare earths-doped Gd2(WO4)3 thin film phosphors by Pechini sol-gel process

Rare earth ions (Eu³⁺ and Dy³⁺)-doped Gd₂(WO₄)₃ phosphor films were prepared by a Pechini sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), atomic force microscopy (AFM) and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting powders and films. The results of XRD indicate that the films begin to crystallize at 600°C and the crystallinity increases with the elevation of annealing temperatures. The film is uniform and crack-free, mainly consists of closely packed fine particles with an average grain size of 80 nm. Owing to an energy transfer from WO₄²⁻ groups, the rare earth ions show their characteristic emissions in crystalline Gd₂(WO₄)₃ phosphor films, i.e., (J=0, 1, 2, 3; J′=0, 1, 2, 3, 4, not in all cases) transitions for Eu³⁺ and (J=13/2, 15/2) transitions for Dy³⁺, with the hypersensitive transitions (Eu³⁺) and (Dy³⁺) being the most prominent groups, respectively. Both the lifetimes and PL intensity of the Eu³⁺ () and Dy³⁺ () increase with increasing the annealing temperature from 500°C to 800°C, and the optimum doping concentrations for Eu³⁺ and Dy³⁺ are determined to be 30 and 6 at% of Gd³⁺ in Gd₂(WO₄)₃ film host lattices, respectively.     

Hydrothermal synthesis and luminescent properties of LuBO3:Tb microflowers

Hexagonal vaterite-type LuBO₃:Tb³⁺ microflower-like phosphors have been successfully prepared by an efficient surfactant- and template-free hydrothermal process directly without further sintering treatment. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectrometry, transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), photoluminescence (PL) and cathodoluminescence (CL) spectra as well as kinetic decays were used to characterize the samples. The as-obtained phosphor samples present flowerlike agglomerates composed of nanoflakes with thickness of 40 nm and high crystallinity in spite of the moderate reaction temperature of 200 °C. The reaction mechanism has been considered as a dissolution/precipitation mechanism; the self-assembly evolution process has been proposed on homocentric layer-by-layer growth style. Under ultraviolet excitation into the 4f⁸→4f⁷5d transition of Tb³⁺ at 248 nm (or 288 nm) and low-voltage electron beam excitation, LuBO₃:Tb³⁺ samples show the characteristic green emission of Tb³⁺ corresponding to ⁵D₄→⁷F_{6, 5, 4, 3} transitions with the ⁵D₄→⁷F₅ transition (542 nm) being the most prominent group, which have potential applications in fluorescent lamps and field emission displays.     

ZnO-B2O3∶Tb3+长余辉玻璃的发光性质

通过还原方法制备了Tb³⁺离子掺杂的硼酸锌玻璃，并观察到在254 nm紫外光激发后有明亮的绿色长余辉发光现象，余辉时间达6 h。通过激发与发射光谱、余辉光谱、余辉衰减曲线、热释光谱、热释光释出速率衰减曲线等得到的信息，研究了Tb³⁺离子掺杂的硼酸锌玻璃的发光性质。     

Size-dependent upconversion luminescence in YF3:Yb/Tm nanobundles

The upconversion luminescent properties of YF₃:Yb³⁺(20%)/Tm³⁺(1%) nanobundles with different sizes (240-500 nm in length) were studied under 980-nm excitation. Ultraviolet (¹I₆ → ³F₄/³H₆ and ¹D₂ → ³H₆), blue (¹D₂ → ³F₄ and ¹G₄ → ³H₆), red (¹D₂ → ³H₄, ¹G₄ → ³F₄, and ³F₃ → ³H₆), and near infrared (³H₄ → ³H₆) emissions were observed. The results indicated that the relative intensity of the ultraviolet to the blue as well as the blue to the near infrared increased with decreasing the size of nanobundles. Especially, the position of the dominant red emission peak varied with the size of nanobundles. As the length of nanobundles increased to 500 nm, unusual ³F₃ → ³H₆ transition was observed, which was theoretically explained considering the decrease of the nonradiative transition rate of ³F₃ → ³H₄.     

Thermoluminescent Properties of Tridymite SiO2 : Al3+, Eu3+

SiO₂ crystals have been used in electroluminescence devices and thermoluminescence (TL) dosimeters. However, their emission mechanisms have not yet been clearly explained. Recently, it has become possible to obtain amorphous, highly pure, SiO₂ prepared by the sol-gel method. The emission mechanism of TL was investigated using Al³⁺ and/or Eu³⁺-doped SiO₂ crystalline samples prepared by heat-treating under much lower temperature than the melting point of SiO₂. The TL spectrum of Eu³⁺-doped sample had main peaks due to the electron transitions from ⁵D₂ to ⁷F₅ (ca. 570 nm, yellow peak) and from ⁵D₀ to ⁷F₂ (ca. 610 nm, red peak). The yellow peak intensity has a maximum value in the SiO₂ doped with near 1 mmol% of Eu₂O₃, while the red peak intensity was almost constant. These facts suggest that bright yellow emission of SiO₂TL phosphor is synthesized by the diffusion of Eu³⁺ ion in SiO₂ matrix prepared by sol-gel method.     

Luminescence enhancement of Eu, Ce co-doped Ba3Si5O13−δNδ phosphors

Host lattice Ba₃Si₅O_13−δN_δ oxonitridosilicates have been synthesized by the traditional solid state reaction method. The lattice structure is based on layers of vertex-linked SiO₄ tetrahedrons and Ba²⁺ ions, where each Ba²⁺ ion is coordinated by eight oxygen atoms forming distorted square antiprisms. Under an excitation wavelength of 365 nm, Ba₃Si₅O_13−δN_δ:Eu²⁺ and Ba₃Si₅O_13−δN_δ:Eu²⁺,Ce³⁺ show broad emission bands from about 400-620 nm, with maxima at about 480 nm and half-peak width of around 130 nm. The emission intensity is strongly enhanced by co-doping Ce³⁺ ions into the Ba₃Si₅O_13−δN_δ:Eu²⁺ phosphor, which could be explained by energy transfer. The excitation band from the near UV to the blue light region confirms the possibility that Ba₃Si₅O_13−δN_δ:Eu²⁺, Ce³⁺ could be used as a phosphor for white LEDs.     

Photoluminescence of new red phosphor SrZnO2:Eu

SrZnO₂:Eu³⁺ has been synthesized by solid-state reaction and its photoluminescence in ultraviolet (UV)-vacuum ultraviolet (VUV) range was investigated. The broad bands around 254 nm are assigned to CT band of Eu³⁺-O²⁻. With the increasing of Eu³⁺ concentration, Eu³⁺ could occupy different sites, which leads to the broadening of CT band. A sharp band is observed in the region of 110-130 nm, which is related to the host absorption. The phosphors emit red luminescence centered at about 616 nm due to Eu³⁺⁵D₀→⁷F₂ both under 254 and 147 nm, but none of Eu²⁺ blue emission can be observed.     

Rietveld refinement and photoluminescent properties of a new blue-emitting material: Eu activated SrZnP2O7

A new efficient blue phosphor, Eu²⁺ activated SrZnP₂O₇, has been synthesized at 1000 °C under reduced atmosphere and the crystal structure and photoluminescence properties have been investigated. The crystal structure of SrZnP₂O₇ was obtained via Rietveld refinement of powder X-ray diffraction (XRD) pattern. It was found that SrZnP₂O₇ crystallizes in space group of P2₁/n (no. 14), Z=4, and the unit cell dimensions are: a=5.30906(2) Å, b=8.21392(3) Å, c=12.73595(5) Å, β=90.1573(3)°, and V=555.390(3) Å³. Under ultraviolet excitation (200-400 nm), efficient Eu²⁺ emission peaked at 420 nm was observed, of which the luminescent efficiency at the optimal concentration of Eu²⁺ (4 mol%) was estimated to be 96% as that of BaMgAl₁₀O₁₇:Eu²⁺. Hence, the SrZnP₂O₇:Eu²⁺ exhibit great potential as a phosphor in different applications, such as ultraviolet light emitting diode and photo-therapy lamps.