The structure and luminescence properties of a novel orange emitting phosphor Y3MnxAl5−2xSixO12

A series of phosphors with the composition Y₃Mn_xAl_5−2xSi_xO₁₂ (x=0, 0.05, 0.1, 0.15, 0.2, 0.3, 0.4, 0.5, 0.6) was prepared through solid state reactions. X-ray powder diffraction analysis of samples shows that when co-doping content does not exceed 16% of Al³⁺, equimolar co-doping of Mn²⁺ and Si⁴⁺ does not change the garnet structure of phosphors, but makes the interplanar distance to decrease a certain extent. However, if the co-doping content exceeds 16%, new phases will form in the samples. The excitation and emission spectra of samples show that Mn²⁺ in Y₃Mn_xAl_5−2xSi_xO₁₂ emits broadband orange light (peak wavelength varies from 586 to 593 nm). With an increment in co-doping content, the emission intensity of the phosphors increases when the value of x is lower than 0.1 while it decreases when it is higher than 0.1 and the emission peak moves to a longer wavelength.     

Oxide coatings on Y3Al5O12:Tb particles

A coating method with precipitating process was developed to reduce the particle size and to improve the particle dispersion of Y₃Al₅O₁₂:Tb³⁺ phosphor prepared by sol-gel method. The particle morphology was observed by using SEM and TEM; and the particle size and its dispersion was measured by using laser scattering technique. Several coating materials were tested. Among them, Al₂(SiO₃)₃ coating not only reduced the particle size from several micrometers to ∼1 μm and improved the particle dispersion, but also well kept luminescent intensities and improved the duration of the phosphor under the bombardment of cathode ray. The mechanism of the particle size reduction was proposed.     

Energy transfer and luminescent properties of Ce, Cr co-doped Y3Al5O12

The phosphors in the system Y_3−xAl_5-yO₁₂:xCe³⁺,yCr³⁺ were synthesized by solid-state reactions and their photoluminescence properties were investigated. These phosphors have absorption in the visible light region and give luminescence in the far-red region (∼688 nm), which are suitable for the application in the device of luminescent solar concentrator (LSC). In these phosphors, Ce³⁺ located at Y³⁺ site can effectively transfer its absorbed energy to Cr³⁺ at Al³⁺ site.     

The structure and luminescence properties of long afterglow phosphor Y3−xMnxAl5−xSixO12

A series of phosphors with the composition Y_3−xMn_xAl_5−xSi_xO₁₂ (x=0, 0.025, 0.050, 0.075, 0.150, 0.225, 0.300) were prepared with solid state reactions. The X-ray powder diffraction analysis of samples shows that the substitution of Mn²⁺ and Si⁴⁺ does not change the garnet structure of phosphors, but makes the interplanar distance decrease to a certain extent. The emission spectra show that Mn²⁺ in Y₃Al₅O₁₂ emits yellow-orange light in a broad band. With the increment of substitution content, the emission intensity of the phosphors increases firstly then decreases subsequently, and the emission peak moves to longer wavelength. Afterglow spectra and decay curves show that all the Mn²⁺ and Si⁴⁺ co-doped samples emit yellow-orange light with long afterglow after the irradiation of ultraviolet light. The longest afterglow time is 18 min. Thermoluminescence measurement shows that there exist two kinds of traps with different depth of energy level and their depth decreases with the increment of substitution content.     

The up-conversion properties of Yb and Er doped Y4Al2O9 phosphors

Er³⁺ doped and Yb³⁺/Er³⁺ co-doped Y₄Al₂O₉ phosphors are prepared by the sol-gel method. The effect of dopant concentration on the structure and up-conversion properties is investigated by X-ray diffraction (XRD) and photoluminescence, respectively. XRD pattern indicates that the sample structure belongs to monoclinic. Under 980 nm excitation, the green and red up-conversion emissions are observed and the emission intensities depended on the Yb³⁺ ion concentration. The green up-conversion emissions decrease with the increase of Yb³⁺ concentration, while red emission increases as Yb³⁺ concentration increases from 0 to 8 at% and then decreases at high Yb³⁺ concentration. The mechanisms of the up-conversion emissions are discussed and results shows that in Er³⁺ and Yb³⁺/Er³⁺ co-doped system, cross-relaxation (CR) and energy transfer (ET) processes play an important role for the green and red up-conversion emissions.     

超声喷雾共沉淀法制备的Lu3Al5O12∶Eu3+ 纳米粉体发光特性

采用新型超声喷雾共沉淀法技术,以Lu₂O₃、Eu₂O₃、Al(NO₃)₃·9H₂O为原料,制备了不同浓度Eu³⁺离子掺杂的Lu₃Al₅O₁₂纳米粉体.用X射线粉末衍射表征了获得纳米粉体的相,用扫描电镜观察了纳米粒子的形貌.测定了粉体的激发光谱、⁷F₀-⁵D₂声子边带谱与发射光谱.研究了不同高温烧结温度与Eu³⁺掺杂浓度对纳米粒子的发光强度与粒子形貌的影响规律.研究表明,当烧结温度高于900 ℃时,粉体发光强度明显增强,并且随着煅烧温度的增加,发光强度有所增强.Eu³⁺离子的最佳掺杂浓度为5~7 mol%.根据稀土离子Eu³⁺光学跃起矩阵元的特点,从发射光谱获得Eu³⁺光学跃起的J-O参量Ω₂与Ω₄.在Eu³⁺掺杂浓度均为5 mol%时,其强度参量达最小,电-声子耦合最强.然后随着掺杂浓度的进一步提高,强度参量略有增加,电-声子耦合减弱.说明Eu-O键强增加,共价性增强,Eu³⁺的局域环境对称性降低.Ω₂值低于Eu³⁺在玻璃与晶体基质中的情况,这是由于纳米粒子中存在着大量的缺陷以及晶体的结构畸变导致纳米粒子的对称性下降所致.     

Energy transfer in Y3Al5O12:Ce, Pr and CaMoO4:Sm, Eu phosphors

Non-radiative energy transfers (ET) from Ce³⁺ to Pr³⁺ in Y₃Al₅O₁₂:Ce³⁺, Pr³⁺ and from Sm³⁺ to Eu³⁺ in CaMoO₄:Sm³⁺, Eu³⁺ are studied based on photoluminescence spectroscopy and fluorescence decay patterns. The result indicates an electric dipole-dipole interaction that governs ET in the LED phosphors. For Ce³⁺ concentration of 0.01 in YAG:Ce³⁺, Pr³⁺, the rate constant and critical distance are evaluated to be 4.5×10⁻³⁶ cm⁶ s⁻¹ and 0.81 nm, respectively. An increase in the red emission line of Pr³⁺ relative to the yellow emission band of Ce³⁺, on increasing Ce³⁺ concentration is observed. This behavior is attributed to the increase of spectral overlap integrals between Ce³⁺ emission and Pr³⁺ excitation due to the fact that the yellow band shifts to the red spectral side with increasing Ce³⁺ concentration. In CaMoO₄:Sm³⁺, Eu³⁺, Sm³⁺-Eu³⁺ transfer occurs from ⁴G_5/2 of Sm³⁺ to ⁵D₀ of Eu³⁺. The rate constant of 8.5×10⁻⁴⁰ cm⁶ s⁻¹ and the critical transfer distance of 0.89 nm are evaluated.     

Enhanced photoluminescence of Sm/Bi co-doped Gd2O3 phosphors by combustion synthesis

Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ powders were prepared by a combustion method. Their structures were determined using X-ray diffraction. UV-visible absorption and photoluminescence spectra were investigated for Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ at different annealing temperatures and different doping concentrations. The emission spectra of all samples presented the characteristic emission narrow lines arising from the ⁴G_5/2→⁶H_J transitions (J=5/2, 7/2, and 9/2) of Sm³⁺ ions upon excitation with UV irradiation. The emission intensity of Sm³⁺ ions was largely enhanced with introducing Bi³⁺ ions into Gd₂O₃:Sm³⁺ and the maximum occurred at a Bi³⁺ concentration of 0.5 mol%. The relevant mechanisms were discussed with the sensitization theory by Dexter and the aggregation behavior of Bi³⁺ ions.     

Luminescence spectroscopy of the Bi single and dimer centers in Y3Al5O12:Bi single crystalline films

Luminescence of the Bi³⁺ single and dimer centers in UV and visible ranges is studied in YAG:Bi (0.13 and 0.27 at% of Bi, respectively) single crystalline films (SCFs), grown by liquid phase epitaxy from a Bi₂O₃ flux. The cathodoluminescence spectra, photoluminescence decays, and time-resolved spectra are measured under the excitation by accelerated electrons and synchrotron radiation with energies of 3.7 and 12 eV, respectively. The energy level structure of the Bi³⁺ single and dimer centers was determined. The UV luminescence of YAG:Bi SCF in the bands that peaked at 4.045 and 3.995 eV at 300 K is caused by radiative transitions of Bi³⁺ single and dimer centers, respectively. The excitation spectra of UV luminescence of Bi³⁺ single and dimer centers consist of two dominant bands, peaked at 4.7/4.315 and 5.7/6.15 eV, related to the ¹S₀→³P₁ (A band) and ¹S₀→ ¹P₁ (C-band) transitions of Bi³⁺ ions, respectively. The excitation bands that peaked at 7.0 and 7.09 eV are ascribed to excitons bound with the Bi³⁺ single and dimer centers, respectively. The visible luminescence of YAG:Bi SCF presents superposition of several wide emission bands peaking within the 3.125-2.57 eV range and is ascribed to different types of excitons localized around the Bi³⁺ single and dimer centers. Apart from the above mentioned A and C bands the excitation spectra of visible luminescence contain wide bands at 5.25, 5.93, and 6.85 eV ascribed to the O²⁻→Bi³⁺ and Bi³⁺→Bi⁴⁺ + e charge transfer transition (CTT) in Bi³⁺ single and dimer centers. The observed significant differences in the decay kinetics of visible luminescence under excitation in A and C bands of Bi³⁺ ions, CTT bands, and in the exciton and interband transitions confirm the radiative decay of different types of excitons localized around Bi³⁺ ions in the single and dimer centers.     

Enhanced luminescence of Ca3B2O6:Dy phosphors by Na-codoping for LED applications

The Ca_2.95−yDy_0.05B₂O₆:yNa⁺ (0≤y≤0.20) phosphors were synthesized at 1100 °C in air by the solid-state reaction route. The as-synthesized phosphors were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE), photoluminescence (PL) spectra and thermoluminescence (TL) spectra. The PLE spectra show the excitation peaks from 300 to 400 nm due to the 4f-4f transitions of Dy³⁺. This mercury-free excitation is useful for solid-state lighting and light-emitting diodes (LEDs). The emission of Dy³⁺ ions on 350 nm excitation was observed at 480 nm (blue) due to the ⁴F_9/2→⁶H_15/2 transitions, 575 nm (yellow) due to ⁴F_9/2→⁶H_13/2 transitions and 660 nm (red) due to weak ⁴F_9/2→⁶H_11/2 emissions. The PL results from the investigated Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors show that Dy³⁺ emissions increase with the increase of the Na⁺ codoping ions. The integral intensity of yellow to blue (Y/B) can be tuned by controlling Na⁺ content. By the simulation of white light, the optimal CIE value (0.328, 0.334) can be achieved when the content of Na⁺-codoping ions is y=0.2. The results imply that the Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors could be potentially used as white LEDs.     

Preparation and luminescent properties of cubic Eu:Y2O3 nanocrystals and comparison to bulk Eu:Y2O3

Y₂O₃:Eu³⁺ nanocrystals were prepared by combustion synthesis. The particle size estimated by X-ray powder diffraction (XRD) was about 10 nm. A blue-shift of the charge-transfer (CT) band in excitation spectra was observed in Y₂O₃:Eu³⁺ nanocrystals compared with bulk Y₂O₃:Eu³⁺. The electronic structure of Y₂O₃ is calculated by density functional method and exchange and correlation have been treated by the generalized gradient approximation (GGA) within the scheme due to Perdew-Burke-Ernzerhof (PBE). The calculated results show that the energy centroid of 5d orbital in nanocrystal has increasing trend compared with that in the bulk material. The bond length and bond covalency are calculated by chemical bond theory. The bond lengths of Y₂O₃:Eu³⁺ nanocrystal are shorter than those of the bulk counterpart and the bond covalency of Y₂O₃:Eu³⁺ nanocrystal also has an increasing trend. By combining centroid shift and crystal-field splitting, the blue-shift of the CT band is interpreted.     

Size-effect on concentration quenching in Yb-doped Y3Al5O12 nano-crystals

Ytterbium-doped nano-crystalline powders of yttrium aluminium garnet Y₃Al₅O₁₂ (Yb³⁺-doped YAG) have been prepared by a modified Pechini method. The morphology of the annealed materials was observed using SEM images. The structure and the average crystalline grain sizes have been determined by X-ray powder diffraction measurements. An increase in elongated spherical crystalline grain sizes from 20 to 50 nm has been observed with annealing temperature increasing from 800 to 1200 °C. The Yb³⁺ concentration dependence of both luminescence spectra and lifetimes has been investigated and compared with those reported for the Yb³⁺-doped YAG bulk single crystals. Decays of Yb^{3+ 2}F_5/2 excited state, much longer in nano-crystalline powders than in bulk single crystals, are discussed in terms of refractive index dependence.     

Unified calculations of the optical and electron paramagnetic resonance spectral data for Ce ion in Y3Ga5O12 crystal

Seven crystal field energy levels (obtained from the optical spectra) and three g factors g_x, g_y and g_z (obtained from electron paramagnetic resonance (EPR) spectra) for Ce³⁺ ion in Y₃Ga₅O₁₂ crystal are calculated together by diagonalizing a complete energy matrix. The Hamiltonian of this energy matrix includes all the interactions for 4f¹ ion Ce³⁺ in rhombic crystal field and under an external magnetic field, and so the optical and EPR data can be studied in a unified way. The calculated crystal field energy levels are in better agreement with the experimental values than the calculated values in the previous paper, and the g factors (which have not been calculated previously) are explained reasonably. The results are discussed.     

Effect of Eu,Tb codoping on the luminescent properties of Y2O3 nanorods

Red-emitting Y₂O₃:Eu³⁺ and green-emitting Y₂O₃:Tb³⁺ and Y₂O₃:Eu³⁺, Tb³⁺ nanorods were synthesized by hydrothermal method. Their structure and micromorphology have been analyzed by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The photoluminescence (PL) property of Y₂O₃:Eu³⁺,Tb³⁺ phosphor was investigated. In the same host (Y₂O₃), upon excitation with ultraviolet (UV) irradiation, it is shown that there are strong emissions at around 610 and 545 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺ and ⁵D₄-⁷F₅ transition of Tb³⁺, respectively. Different qualities of Eu³⁺and Tb³⁺ ions are induced into the Y₂O₃ lattice. From the excitation spectrum, we speculate that there exists energy transfer from Tb³⁺ to Eu³⁺ ions .The emission color of powders reveals regular change in the separation of light emission. These powders can meet with the request of optical display material for different colors or can be potentially used as labels for biological molecules.     

Highly water resistant surface coating by fluoride on long persistent Sr4Al14O25:Eu/Dy phosphor

A novel and efficient method of providing moisture resistance of inorganic particles such as divalent europium activated strontium aluminate phosphors (Sr₄Al₁₄O₂₅:Eu²⁺/Dy³⁺) was developed by firing the phosphor in the presence of appropriate amount of ammonium fluoride at a temperature of 600-700 °C. Scanning electron microscopy, X-ray diffraction, FT-IR, EDAX and Photoluminescence measurements were carried out to characterize the uncoated and coated samples. The pH measurements were carried out for the water resistivity measurements. The phosphor particles became coated with a moisture-impervious thin coating that did not suppress the luminescence of the phosphor and can withstand complete immersion in water for long periods of time, showing very high water resistivity.     

Y2O3:Yb3+,Tm3+纳米材料的可见及紫外上转换发光

通过燃烧法制备了Yb³⁺-Tm³⁺共掺的Y₂O₃纳米粉体,并对样品在980 nm激光照射下的上转换发光特性进行了研究.实验发现,样品在可见光区域能够产生强烈的蓝色发光(476 nm和487 nm)和较弱的红色发光(约650 nm),而且同时观察到了两个紫外发光峰¹I₆→³H₆ (~297 nm)和^{1关键词： 2O₃:Yb3+')" href="#">Y₂O₃:Yb3+ 3+}')" href="#">Tm³⁺ 上转换光谱 敏化 紫外发光     

Luminescence of Mn ions in Tb3Al5O12 garnet

The paper is dedicated to investigation of the Mn²⁺ luminescence in Tb₃Al₅O₁₂ (TbAG) garnet, as well as the processes of excitation energy transfer between host cations (Tb³⁺ ions) and activators (Mn²⁺ and Mn²⁺-Ce³⁺ pair ions) in single crystalline films of TbAG:Mn and TbAG:Mn,Ce garnets which can be considered as promising luminescent materials for conversion of LED's radiation. Due to the effective energy transfer between TbAG host and activator, Mn²⁺ ions in TbAG possess the bright orange luminescence in the bands peaked at 595 nm with a lifetime of 0.64 ms which are caused by the ⁴T₁→⁶A₁ radiative transitions. The simultaneous process of energy transfer is realized in TbAG:Mn,Ce: (i) from Tb³⁺ to Mn²⁺ ions; (ii) from Tb³⁺ cations to Ce³⁺ ions and then partly to Mn²⁺ ions through Tb³⁺ ion sublattice and Ce-Mn dipole-dipole interaction.     

Characterization of Y2O3 gate dielectric on n-GaAs substrates

Physical and electrical properties of sputtered deposited Y₂O₃ films on NH₄OH treated n-GaAs substrate are investigated. The as-deposited films and interfacial layer formation have been analyzed by using X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). It is found that directly deposited Y₂O₃ on n-GaAs exhibits excellent electrical properties with low frequency dispersion (<5%), hysteresis voltage (0.24 V), and interface trap density (3 × 10¹² eV⁻¹ cm⁻²). The results show that the deposition of Y₂O₃ on n-GaAs can be an effective way to improve the interface quality by the suppression on native oxides formation, especially arsenic oxide which causes Fermi level pinning at high-k/GaAs interface. The Al/Y₂O₃/n-GaAs stack with an equivalent oxide thickness (EOT) of 2.1 nm shows a leakage current density of 3.6 × 10⁻⁶ A cm⁻² at a V_FB of 1 V. While the low-field leakage current conduction mechanism has been found to be dominated by the Schottky emission, Poole-Frenkel emission takes over at high electric fields. The energy band alignment of Y₂O₃ films on n-GaAs substrate is extracted from detailed XPS measurements. The valence and conduction band offsets at Y₂O₃/n-GaAs interfaces are found to be 2.14 and 2.21 eV, respectively.     

Optical spectroscopy of Ca3Sc2Si3O12, Ca3Y2Si3O12 and Ca3Lu2Si3O12 doped with Pr

The silicates Ca₃Sc₂Si₃O₁₂, Ca₃Y₂Si₃O₁₂ and Ca₃Lu₂Si₃O₁₂, both undoped and doped with Pr³⁺ ions, have been synthesized by solid-state reaction at high temperature. The luminescence spectroscopy and the excited state dynamics of the materials have been studied upon VUV and X-ray excitation using synchrotron radiation. All doped samples have shown efficient 5d-4f emission upon direct VUV excitation of 5d levels, but only Ca₃Sc₂Si₃O₁₂:Pr³⁺ shows luminescence upon interband VUV or X-ray excitation. The VUV excited emission spectra of Ca₃Y₂Si₃O₁₂:Pr³⁺ and Ca₃Lu₂Si₃O₁₂:Pr³⁺ show features attributed to emission from two distinct sites accommodating the Pr³⁺ dopant. The decay kinetics of the Pr³⁺ 5d-4f emission in Ca₃Sc₂Si₃O₁₂:Pr³⁺ upon VUV excitation across the band gap are characterized by decay times in the range 25-28 ns with no significant rise after the excitation pulse. They appear to be faster upon X-ray irradiation than for VUV excitation. Weak afterglow components are attributed to defect luminescence.     

Solid state reaction synthesis and luminescence properties of Dy-doped Gd2Mo3O9 phosphor

Gd₂Mo₃O₉ phosphors with various Dy³⁺ concentrations were synthesized by a traditional solid-state reaction using Na₂CO₃ as a flux. The influence of reaction temperature and Dy³⁺-doping concentration on the crystal structure of the phosphors was examined by XRD (X-ray diffraction). The effect of Dy³⁺-doping concentration on the emissions of Mo-O bond and Dy³⁺ was experimentally investigated. The energy transfers between host and Dy³⁺ ions, and between Dy³⁺ ions were analyzed based on both the Van Uitert and I-H models. The chromatic properties of the phosphors were also discussed.