Optical properties of MgxZn1−xO thin films deposited on silicon and sapphire substrate by rf magnetron sputtering

The index dispersion at UV–VIS range for polycrystalline Mg_xZn_1−xO films on silicon with different Mg concentration was obtained by spectroscopic ellipsometry (SE) method. It decreases with the increase of the Mg content. Above the relative peak wavelength, they are well fitted by the first-order Sellmeier relation. The band gap of films on sapphire of different Mg content was determined from transmission measurements. Photoluminescence (PL) illustrated that for Mg_xZn_1−xO films every PL peak corresponded to a special excitation wavelength. The wavelength of the PL peak was proportional to the special excitation wavelength. A strong peak was obtained in the blue band for the films due to the large amount of oxygen vacancies caused by excess Zn and Mg atoms, while weak peak at ultraviolet band.     

Role of carbon in the formation of hard Ge1−xCx thin films by reactive magnetron sputtering

We have deposited germanium carbide (Ge_1−xC_x) films on Si(1 0 0) substrate via radio-frequency (RF) reactive magnetron sputtering in a CH₄/Ar mixture discharge, and explored the effects of carbon content (x) on the chemical bonding and hardness for the obtained films. We find that x significantly influences the chemical bonding, which leads to a pronounced change in the hardness of the film. To reveal the relationship between the chemical bonding and hardness, first-principles calculations have been carried out. It is shown that as x increases from 0 to 0.33, the fraction of sp³ C-Ge bonds in the film increases at the expense of Ge-Ge bonds, which promotes formation of a strong covalently bonded network, and thus enhances the hardness of the film. However, as x further increases from 0.33 to 0.59, the fraction of sp³ C-Ge bonds in the film gradually reduces, while that of sp³ C-H and graphite-like sp² C-C bonds increases, which damages the compact network structure, resulting in a sharp decrease in the hardness. This investigation suggests that the medium x (0.17<x<0.40) is most favorable to the preparation of hard Ge_1−xC_x films due to the formation of dominant sp³ C-Ge bonds.     

Structural and electrical characterization of SxSe100−x thin films

Thin films of samples of the glassy S_xSe_100−x system with 0 ≤ x ≤ 7.28 have been prepared by thermal evaporation technique at room temperature (300 K). X-ray investigations show that the structure of pure selenium (Se) does change seriously by the addition of small amount of sulphur S ≤7.28%. The lattice parameters were determined as a function of sulphur content. Results of differential thermal analysis (DTA) of the glassy compositions of the system S_xSe_100−x were discussed. The characteristic temperatures (T_g, T_c and T_m) were evaluated. Dark electrical resistivities, ρ, of S_xSe_100−x thin films with different thicknesses from 100 to 500 nm, were measured in the temperature range from 300 to 423 K. Two distinct linear parts with different activation energies were observed. The variation of electrical resistivity of examined compositions has been discussed as a function of the film thickness, temperature and the sulphur content. The application of Mott model for the phonon assisted hopping of small polarons gave the same two activation energies obtained from the resistivity temperature calculations.     

Fabrication of FeSe1−x superconducting films with bulk properties

We have fabricated high-quality FeSe_1−x superconducting films with a bulk T_c of 11–12 K on different substrates, Al₂O₃(0 0 0 1), SrTiO₃(1 0 0), MgO(1 0 0), and LaAlO₃(1 0 0), by using a pulsed laser deposition technique. All the films were grown at a high substrate temperature of 610 °C, and were preferentially oriented along the (1 0 1) direction, the latter being to be a key to fabricating of FeSe_1−x superconducting thin films with high T_c. According to the energy dispersive spectroscopy data, the Fe:Se composition ratio was 1:0.90 ± 0.02. The FeSe_1−x film grown on a SrTiO₃ substrate showed the best quality with a high upper critical magnetic field [H_c2(0)] of 56 T.     

BiFeO3/Zn1−xMnxO bilayered thin films

BiFeO₃/Zn_1−xMn_xO (x = 0-0.08) bilayered thin films were deposited on the SrRuO₃/Pt/TiO₂/SiO₂/Si(1 0 0) substrates by radio frequency sputtering. A highly (1 1 0) orientation was induced for BiFeO₃/Zn_1−xMn_xO. BiFeO₃/Zn_1−xMn_xO thin films demonstrate diode-like and resistive hysteresis behavior. A remanent polarization in the range of 2P_r ∼ 121.0-130.6 μC/cm² was measured for BiFeO₃/Zn_1−xMn_xO. BiFeO₃/Zn_1−xMn_xO (x = 0.04) bilayer exhibits a highest M_s value of ∼15.2 emu/cm³, owing to the presence of the magnetic Zn_0.96Mn_0.04O layer with an enhanced M_s value.     

Short-range order analysis and some physical properties of InxSe1−x glasses

Bulk In_xSe_1−x (with x=5-25 at%) glasses were prepared using the melt-quench technique. Short range order(SRO) was examined by the X-ray diffraction using Cu(k_α) radiation in the wave vector interval 0.28≤k≤6.5 A⁰⁻¹.The SRO parameters have been obtained from the radial distribution function. The inter-atomic distance obtained from the first and second peak are r₁=0.263 and r₂=0.460 nm, which is equivalent In-Se and Se-Se bond length. The fundamental structural unit for the studied glasses is In₂Se₃ pyramid. Using the differential scanning calorimetry (DSC), the crystallization mechanism of In_xSe_1−x chalcogenide glass has been studied. The glass transition activation energy (E_g) is 289±0.3 kj/mol.There is a correlation amongst the glass forming ability, bond strength and the number of lone pair electrons. The utility of the Gibbs-Di Marzio relation was achieved by estimating T_g theoretically.     

Electronic structure and optical properties of CdSexTe1−x mixed crystals

The band structure and optical properties of the CdSe_xTe_1−x ternary mixed crystals have been studied using the pseudopotential formalism under an improved virtual crystal approximation approach. Quantities such as, energy gaps, band-gap bowing parameters, electron effective mass and dielectric constants are calculated. Our results agree well with the available data in the literature. The composition dependence of all studied quantities has been expressed by quadratic polynomial forms.     

Optoelectronic properties of GaAs1−xPx alloys under the influence of temperature and pressure

This work is concerned with the dependence of the electronic energy band structures for GaAs_1−xP_x alloys on temperature and pressure that is based on local empirical pseudo-potential method. The band structures of GaAs_1−xP_x alloys were calculated in the virtual crystal approximation using the EPM which incorporates compositional disorder as an effective potential.     

Growth of cubic MgxZn1−xO alloy films by electron beam evaporation

We report the growth of cubic Mg_xZn_1−xO alloy thin films on quartz by electron beam evaporation. It can be found that all the samples have sharp absorption edges by the absorption measurements. X-ray diffraction measurements indicate the Mg_xZn_1−xO films are cubic phase with preferred orientation along the (1 1 1) direction. Energy dispersive spectrometry (EDS) demonstrates that the Mg concentration in Mg_xZn_1−xO films is much higher than the ceramic target used, and the composition can be tuned in a small scope by varying the substrate temperature and the beam electric current. The reasons of this phenomenon are also discussed.     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

Structure and electrical properties of Bi5GexSe95−x thin films

Bi₅Ge_xSe_95−x (30, 35, 40 and 45 at.%) thin films of thickness 200 nm were prepared on glass substrates by the thermal evaporation technique. The influence of composition and annealing temperature, on the structural and electrical properties of Bi₅Ge_xSe_95−x films was investigated systematically using X-ray diffraction (XRD), energy dispersive X-ray analysis (EDX). The XRD patterns showed that the as-prepared films were amorphous in nature with few tiny crystalline peaks of relatively low intensity for 30 and 45 at.% and the Bi₅Ge₄₀Se₅₅ annealed film was polycrystalline. The chemical composition of the Bi₅Ge₃₀Se₆₅ film has been checked using energy dispersive X-ray spectroscopy (EDX). The electrical conductivity was measured in the temperature range 300-430 K for the studied compositions. The effect of composition on the activation energy (ΔE) and the density of localized states at the Fermi level N(E_F) were studied, moreover the electrical conductivity was found to increase with increasing the annealing temperature and the activation energy was found to decrease with increasing the annealing temperature. The results were discussed on the basis of amorphous-crystalline transformations.     

Theoretical research on optical properties and quantum efficiency of Ga1−xAlxN photocathodes

In order to design the optimal component structure of transmission-mode (t-mode) Ga_1−xAl_xN photocathode, the optical properties and quantum efficiency of Ga_1−xAl_xN photocathodes are simulated. Based on thin film principle, optical model of t-mode Ga_1−xAl_xN photocathodes is built. And the quantum efficiency formula is put forward. Results show that Ga_1−xAl_xN photocathodes can satisfy the need of detectors with “solar blind” property when the Al component is bigger than 0.375. There is an optimal thickness of Ga_1−xAl_xN layer to get highest quantum efficiency, and the optimal thickness is 0.3 μm. There is close relation between absorptivity and quantum efficiency, which is in good agreement with the “three-step” model. This work gives a reference for the experimental research on the Ga_1−xAl_xN photocathodes.     

Structural, optical and electrical properties of Zn1−xCdxO thin films prepared by PLD

Ternary polycrystalline Zn_1−xCd_xO semiconductor films with cadmium content x ranging from 0 to 0.23 were obtained on quartz substrate by pulse laser deposited (PLD) technique. X-ray diffraction measurement revealed that all the films were single phase of wurtzite structure grown on c-axis orientation with its c-axis lattice constant increasing as the Cd content x increasing. Atomic force microscopy observation revealed that the grain size of Zn_1−xCd_xO films decreases continuously as the Cd content x increases. Both photoluminescence and optical measurements showed that the band gap decreases from 3.27 to 2.78 eV with increasing the Cd content x. The increase in Cd content x also leads to the broadening of the emission peak. The resistivity of Zn_1−xCd_xO films decreases evidently for higher values of Cd content x. The shift of PL emission to visible light as well as the decrease of resistivity makes the Zn_1−xCd_xO films potential candidate for optoelectronic device.     

Study on the electronic structure and optical properties of different Al constituent Ga1−xAlxAs

Using quantum mechanics GASTEP software package based on the first principle density function theory, the electronic structure and optical properties of Ga_1−xAl_xAs at different Al constituent are calculated. Result shows that with the increase of Al constituent, the band gap of Ga_1−xAl_xAs increases and varies from direct band gap to indirect band gap; the absorption band edge and the absorption peak move to high-energy side; the static reflectivity decreases. With the increasing of the incident photon energy, Ga_1−xAl_xAs shows metal reflective properties in certain energy range. With the increasing of Al constituent, static dielectric constant decreases and the intersection of dielectric function and the x-axis move towards high-energy side; the peak of energy loss function move to low-energy side and the peak value reduces.     

Effect of substrate temperature on the morphology, structural and optical properties of Zn1−xCoxO thin films

Zn_1−xCo_xO thin films with c-axis preferred orientation were deposited on sapphire (0 0 0 1) by pulsed laser deposition (PLD) technique at different substrate temperatures in an oxygen-deficient ambient. The effect of substrate temperature on the microstructure, morphology and the optical properties of the Zn_1−xCo_xO thin films was studied by means of X-ray diffraction (XRD), atomic force microscopy (AFM), UV-visible-NIR spectrophotometer, fluorescence spectrophotometer. The results showed that the crystallization of the films was promoted as substrate temperature rose. The structure of the samples was not distorted by the Co incorporating into ZnO lattice. The surface roughness of all samples decreased as substrate temperature increased. The Co concentration in the film was higher than in the target. Emission peak near band edge emission of ZnO from the PL spectra of the all samples was quenched because the dopant complexes acted as non-radiative centers. While three emission bands located at 409 nm (3.03 eV), 496 nm (2.5 eV) and 513 nm (2.4 eV) were, respectively, observed from the PL spectra of the four samples. The three emission bands were in relation to Zn interstitials, Zn vacancies and the complex of V_O and Zn_i (V_OZn_i). The quantity of the Zn interstitials maintained invariable basically, while the quantity of the V_OZn_i slightly decreased as substrate temperature increased.     

Properties of MgxZn1−xO thin films sputtered in different gases

Mg_xZn_1−xO alloy films were prepared on sapphire substrates using Ar and N₂ as the sputtering gases. The effect of the sputtering gas on the structural, optical and electrical properties of the Mg_xZn_1−xO films was studied. By using N₂ as the sputtering gas, the Mg_xZn_1−xO film shows p-type conductivity and the band gap is larger than that employing Ar as the sputtering gas. The reason for this phenomenon is thought to be related to the reaction between N-O or N-Zn, and the N-doping.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Development of structural and optical properties of WOx films upon increasing oxygen partial pressure during reactive sputtering

WO_x films were prepared by reactive dc magnetron sputtering using tungsten target. Sputtering was carried out at a total pressure of 1.2 Pa using a mixture of argon plus oxygen in an effort to determine the influence of the oxygen partial pressure on structural and optical properties of the films. The deposition rate decreases significantly as the surface of the target is oxidized. X-Ray diffraction revealed the amorphous nature of all the films prepared at oxygen partial pressures higher than 1.71×10⁻³ Pa. For higher oxygen partial pressures, fully transparent films were deposited, which showed a slight increase in optical band gap with increasing oxygen partial pressure, while the refractive index was simultaneously decreased.     

Population analysis solution to hardness enhancement in TiCxN1−x

We investigated the hardness enhancement in titanium carbonitrides (TiC_xN_1−x) by the population analysis method based on first-principles calculations. Populations for bonds TiC and TiN in TiC_xN_1−x (0.25<x<0.75) are all positive. The enhanced hardness for titanium carbonitrides is well explained by overlap population analysis. Intrinsic hardness of TiC_xN_1−x has been calculated based on the obtained overlap populations. The calculated results are in good agreement with the available experimental data.     

A study of TaxC1−x coatings deposited on biomedical 316L stainless steel by radio-frequency magnetron sputtering

In this paper, Ta_xC_1−x coatings were deposited on 316L stainless steel (316L SS) by radio-frequency (RF) magnetron sputtering at various substrate temperatures (T_s) in order to improve its corrosion resistance and hemocompatibility. XRD results indicated that T_s could significantly change the microstructure of Ta_xC_1−x coatings. When T_s was <150 °C, the Ta_xC_1−x coatings were in amorphous condition, whereas when T_s was ≥150 °C, TaC phase was formed, exhibiting in the form of particulates with the crystallite sizes of about 15-25 nm (T_s = 300 °C). Atomic force microscope (AFM) results showed that with the increase of T_s, the root-mean-square (RMS) values of the Ta_xC_1−x coatings decreased. The nano-indentation experiments indicated that the Ta_xC_1−x coating deposited at 300 °C had a higher hardness and modulus. The scratch test results demonstrated that Ta_xC_1−x coatings deposited above 150 °C exhibited good adhesion performance. Tribology tests results demonstrated that Ta_xC_1−x coatings exhibited excellent wear resistance. The results of potentiodynamic polarization showed that the corrosion resistance of the 316L SS was improved significantly because of the deposited Ta_xC_1−x coatings. The platelet adhesion test results indicated that the Ta_xC_1−x coatings deposited at T_s of 150 °C and 300 °C possessed better hemocompatibility than the coating deposited at T_s of 25 °C. Additionally, the hemocompatibility of the Ta_xC_1−x coating on the 316L SS was found to be influenced by its surface roughness, hydrophilicity and the surface energy.