Improvement in magnetic properties of La substituted BaFe12O19 particles prepared with an unusually low Fe/Ba molar ratio

In this study, effect of lanthanum substitution on the phase composition, lattice parameters and magnetic properties of barium hexaferrite has been studied in samples synthesized in ammonium nitrate melt. Samples, prepared with different lanthanum amount and having various initial Fe/(Ba+La) ratios in between 12 and 2 {(Ba_1−xLa_x)·n Fe₂O₃, where 0≤x≤1 and 1≤n≤6)}, are sintered at temperatures from 800 to 1200 °C. The lattice parameters, both a and c, decreases with increasing La amount which results in a decrease of the unit cell volume. The scanning electron microscope micrographs show that the pure and La-substituted sample with x=0.3, both calcinated at 1000 °C, have grain sizes smaller than 1 μm. The coercivities of the La-substituted samples increase with increasing La amount and reaches to a maximum value of 5.73 kOe, when x=0.3. Sintering at higher temperatures (above 1000 °C) decreases the coercivity, resembling a transition from single to multi-domain behavior of the particles, while saturation magnetization of the samples continues to increase due to the increasing grain size. Magnetization measurements of the samples prepared with different Fe/(Ba+La) molar ratios, n's, revealed that the specific saturation magnetization slightly increases with decreasing n, while coercivities fluctuates around 5.5 kOe. However, a sharp increase in the saturation magnetization has been observed in the sample having n=1 and washed in HCl. It was measured as 59.2 emu/g at 15 kOe, which is higher than that of the pure sample (57.5 emu/g). Thus, the magnetic parameters are optimized in the sample Ba_0.7La_0.3Fe₁₂O₁₉ so as to maximize both coercivity and specific saturation magnetization in the HCl-washed sample synthesized by starting with an unusually low Fe/(Ba+La) molar ratio of 2 (or n=1).     

Low temperature synthesis and superconducting properties of polycrystalline T′-(La,Sm)2CuO4

La_2−xSm_xCuO_4+δ with the Nd₂CuO₄ structure was synthesized by precipitation from fused alkaline hydroxide, CsOH, at 400 °C. The as-sintered polycrystalline samples showed no diamagnetic signal, but after post-annealing in vacuum of ≈10⁻⁸ atm at 650–700 °C, the samples with x = 0.1 and 0.3 exhibited superconductivity at T_c on = 25 K. The volume fraction of the superconducting phase estimated from the slope of the Zero-Field-Cooled magnetization data was over 30% for x = 0.3, which confirmed that the La_1.7Sm_0.3CuO_4+δ is a bulk superconductor.     

Dielectric properties of valence compensated Ca1−xBixTi1−xCrxO3 perovskite prepared using the sol-gel process

Ca_1−xBi_xNb_1−xCr_xO₃ (x=0.01-0.5) ceramic powders were synthesized using the sol-gel process. The single-phase solids can be presented at x=0.01 and 0.03. The coexistence of orthorhombic perovskite and the secondary phase of BiCrO₃ was verified, as presented for x=0.05-0.5. Grains with a micro-cube topography were obtained for x=0.3-0.5. The average grain size is about 0.4 and 1.1 μm for x=0.3 and 0.5, respectively. The highest dielectric constant peak was measured at around 55 °C for x=0.5 and at 75 °C for x=0.3. The high dielectric constant was caused by the formation of barrier layers at the interface of the bi-phase mixed ceramics. Space charge polarization contributed to the observed behavior.     

Electromagnetic properties of samarium-substituted NiCuZn ferrite prepared by auto-combustion method

Ni_0.25Cu_0.2Zn_0.55Sm_xFe_2−xO₄ ferrite with x=0.00, 0.025, 0.05 and 0.075 compositions were synthesized through the nitrate-citrate auto-combustion method. These powders were calcined, compacted and sintered at 900 °C for 4 h. Effect of Sm substitution on phase composition, microstructure and relative density were studied. Permeability, magnetic loss and AC resistivity were measured in the frequency range of 1 kHz-10 MHz. Permeability and AC resistivity were found to increase and loss decreased with Sm substitution up to x=0.05. Saturation magnetization also increased up to that substitution limit. Observed variations in electromagnetic properties have been explained.     

Study on electro-magnetic properties of La substituted Ni–Cu–Zn ferrite synthesized by auto-combustion method

(Ni_0.25Cu_0.20Zn_0.55)La_xFe_2−xO₄ ferrite with x=0.00, 0.025, 0.050 and 0.075 compositions were synthesized through nitrate–citrate auto-combustion method. Crystalline spinel ferrite phase with about 16–19 nm crystallite size was present in the as-burnt ferrite powder. These powders were calcined, compacted and sintered at 950 °C for 4 h. Initial permeability, magnetic loss and AC resistivity of different compositions were measured in the frequency range from 10 Hz to 10 MHz. Saturation magnetization and hysteresis parameters were measured at room temperature with a maximum magnetic field of 10 kOe. Permeability and AC resistivity were found to increase and magnetic loss decreased with La substitution for Fe, up to x=0.025. Saturation magnetization and coercive field also increases up to that limit. The electromagnetic properties were found best in the ferrite composition of x=0.025, which would be better for more miniaturized multi layer chip inductor.     

Structure and magnetic properties of SmCoxTi0.4-1:7 ribbons

SmCo_xTi_0.4 (x=6.6, 7.1, 7.6, 8.1) ribbons have been prepared by melt spinning at a wheel speed of 42 m/s, followed by annealing at 750 °C for 2 h. Both as-spun and as-annealed ribbons possess the disordered TbCu7-type (1:7) phase even when the Sm/(Co,Ti) atomic ratio deviates from 1/7. The c/a ratio increases with increasing Co concentration x, but the unit cell volume decreases. The Curie temperatures show above 700 °C, increasing from 707 °C for x=6.6 to 782 °C for x=8.1. The saturation magnetizations increase almost linearly with increasing Co content. The observed magnetic hardening is believed to arise from the high magnetocrystalline anisotropy of the 1:7 phase and the fine nanograin structure. The intrinsic coercivity of 9797 Oe has been obtained in the melt-spun SmCo_7.1Ti_0.4 ribbons.     

Influence of manganese substitution and annealing temperature on the formation,microstructure and magnetic properties of Mn–Zn ferrites

The effects of annealing temperature and manganese substitution on the formation, microstructure and magnetic properties of Mn_xZn_1−xFe₂O₄ (with x varying from 0.3 to 0.9) through a solid-state method have been investigated. The correlation of the microstructure and the grain size with the magnetic properties of Mn–Zn ferrite powders was also reported. X-ray diffraction (XRD), a scanning electron microscope (SEM) and a vibrating sample magnetometer (VSM) were utilized in order to study the effect of variation of manganese substitution and its impact on crystal structure, crystalline size, microstructure and magnetic properties of the ferrite powders formed. The XRD analysis showed that pure single phases of Mn–Zn ferrites were obtained by increasing the annealing temperature to 1200–1300 °C. Increasing the annealing temperature to ?1300 °C led to abnormal grain growth with inter-granular pores and this led to a decrease in the saturation magnetization. Moreover, an increase in the Mn²⁺ ion substitution up to x=0.8 increased the lattice parameter of the formed powders due to the high ionic radii of the Mn²⁺ ion. Mn–Zn ferrites phases were formed and the positions of peaks were shifted by substituting manganese. The average crystalline size was increased by increasing the annealing temperature and decreased by increasing the substitution by manganese up to 0.8. The average crystalline size was in the range 95–137.3 nm. The saturation magnetization of the Mn–Zn-substituted ferrite powders increased continuously with an increase in the Mn concentration up to 0.8 at annealing temperatures of 1200–1300 °C. Further increase of Mn substitution up to 0.9 led to a decrease of saturation magnetization. The saturation magnetization increased from 17.3 emu/g for the Mn_0.3Zn_0.7Fe₂O₄ phase particles produced to 59.08 emu/g for Mn_0.8Mn_0.2Fe₂O₄ particles.     

Magnetoelectric characterization of xNi0.75Co0.25Fe2O4-(1−x)BiFeO3 nanocomposites

Magnetoelectric (ME) nanocomposites containing Ni_0.75Co_0.25Fe₂O₄-BiFeO₃ phases were prepared by citrate sol-gel process. X-ray diffraction (XRD) analysis showed phase formation of xNi_0.75Co_0.25Fe₂O₄-(1−x)BiFeO₃ (x=0.1, 0.2, 0.3 and 0.4) composites on heating at 700 °C. Transmission electron microscopy revealed the formation of powders of nano order size and the crystal size was found to vary from 30 to 85 nm. Dispersion in dielectric constant (ε) and dielectric loss (tan δ) in the low-frequency range have been observed. It is seen that nanocomposites exhibit strong magnetic properties and a large ME effect. On increasing Ni_0.75Co_0.25Fe₂O₄ contents in the nanocomposites, the saturation magnetization (M_S) and coercivity (H_C) increased after annealing at 700 °C. The large ME output in the nanocomposites exhibits strong dependence on magnetic bias and magnetic field frequency. The large value of ME output can be attributed to small grain size of ferrite phase of nanocomposite being prepared by citrate precursor process.     

Preference orientation and magnetic properties of CoxFe3−xO4 nanocrystalline thin films on quartz substrate

Nanocrystalline spinel ferrite thin films of Co_xFe_3−xO₄ (x=0.3$x=0.3$, 0.5, 0.8, and 1.0) have been prepared by RF sputtering on quartz substrate without a buffer layer at room temperature and annealed at the temperature range from 200 to 600 °C in air. The as-sputtered films exhibit the preferred orientation and the high magnetization and coercivity. After annealing, the preferred orientations become poor, but the magnetization and coercivity increase. The sample with a magnetization of 455 emu/cm³, a coercivity of 2.8 kOe, a remanence ratio of 0.72, and a maximum energy product of 2.4 MGOe has been obtained. The influence of Co ions and annealing temperature on the magnetic properties has been discussed.     

Effect of Fe substitution on magnetocaloric effect in La0.7Sr0.3Mn1−xFexO3 (0.05≤x≤0.20)

We have studied the effect of Fe substitution on magnetic and magnetocaloric properties in La_0.7Sr_0.3Mn_1−xFe_xO₃ (x=0.05, 0.07, 0.10, 0.15, and 0.20) over a wide temperature range (T=10-400 K). It is shown that substitution by Fe gradually decreases the ferromagnetic Curie temperature (T_C) and saturation magnetization up to x=0.15 but a dramatic change occurs for x=0.2. The x=0.2 sample can be considered as a phase separated compound in which both short-range ordered ferromagnetic and antiferromagnetic phases coexist. The magnetic entropy change (−ΔS_m) was estimated from isothermal magnetization curves and it decreases with increase of Fe content from 4.4 J kg⁻¹ K⁻¹ at 343 K (x=0.05) to 1.3 J kg⁻¹ K⁻¹ at 105 K (x=0.2), under ΔH=5 T. The La_0.7Sr_0.3Mn_0.93Fe_0.07O₃ sample shows negligible hysteresis loss, operating temperature range over 60 K around room temperature with refrigerant capacity of 225 J kg⁻¹, and magnetic entropy of 4 J kg⁻¹ K⁻¹ which will be an interesting compound for application in room temperature refrigeration.     

Zn- and Cu-substituted Co2Y hexagonal ferrites: Sintering behavior and permeability

Y-type polycrystalline hexagonal ferrites Ba₂Co_2−x−yZn_xCu_yFe₁₂O₂₂ with 0≤x≤2 and 0≤y≤0.8 were prepared by the mixed-oxide route. Single phase Y-type ferrite powders were obtained after calcinations at 1000 °C. Samples sintered at 1200 °C show a permeability that increases with the substitution of Zn for Co and display maximum permeability of μ′=35 at 1 MHz for x=1.6 and y=0.4. A resonance frequency f_r=500 MHz is observed for Zn-rich ferrites with y=0 and 0.4. The saturation magnetization increases with substitution of Zn for Co. Addition of Bi₂O₃ shifts the temperature of maximum shrinkage down to T≤950 °C. Moreover, an increase of the Cu-concentration further lowers the sintering temperature to T≤900 °C, enabling co-firing of the ferrites with Ag metallization for multilayer technologies. However, low-temperature firing reduces the permeability to μ′=10 and the resonance frequency is shifted to 1 GHz. Thus substituted hexagonal Y-type ferrites can be used as soft magnetic materials for multilayer inductors for high frequency applications.     

The structure and magnetic properties of Zn1−xNixFe2O4 ferrite nanoparticles prepared by sol–gel auto-combustion

Zn_1−xNi_xFe₂O₄ ferrite nanoparticles were prepared by sol–gel auto-combustion and then annealed at 700 °C for 4 h. The results of differential thermal analysis indicate that the thermal decomposition temperature is about 210 °C and Ni–Zn ferrite nanoparticles could be synthesized in the self-propagating combustion process. The microstructure and magnetic properties were investigated by means of X-ray diffraction, scanning electron microscope, and Vibrating sample magnetometer. It is observed that all the spherical nanoparticles with an average grain size of about 35 nm are of pure spinel cubic structure. The crystal lattice constant declines gradually with increasing x from 0.8435 nm (x=0.20) to 0.8352 nm (x=1.00). Different from the composition of Zn_0.5Ni_0.5Fe₂O₄ for the bulk, the maximum M_s is found in the composition of Zn_0.3Ni_0.7Fe₂O₄ for nanoparticles. The H_c of samples is much larger than the bulk ferrites and increases with the enlarging x. The results of Zn_0.3Ni_0.7Fe₂O₄ annealed at different temperatures indicate that the maximum M_s (83.2 emu/g) appears in the sample annealed at 900 °C. The H_c of Zn_0.3Ni_0.7Fe₂O₄ firstly increases slightly as the grain size increases, and presents a maximum value of 115 Oe when the grains grow up to about 30 nm, and then declines rapidly with the grains further growing. The critical diameter (under the critical diameter, the grain is of single domain) of Zn_0.3Ni_0.7Fe₂O₄ nanoparticles is found to be about 30 nm.     

Structural and magnetic properties of MnxCo1−xFe2O4 ferrite nanoparticles

We report on the structural and magnetic properties of nanoparticles of Mn_xCo_1−xFe₂O₄ (x=0.1, 0.5) ferrites produced by the glycothermal reaction. From the analysis of XRD spectra and TEM micrographs, particle sizes of the samples have been found to be about 8 nm (for x=0.1) and 13 nm (for x=0.5). The samples were characterized by DC magnetization in the temperature range 5-380 K and in magnetic fields of up to 40 kOe using a SQUID magnetometer. Mössbauer spectroscopy results show that the sample with higher Mn content has enhanced hyperfine fields after thermal annealing at 700 °C. There is a corresponding small reduction in hyperfine fields for the sample with lower Mn content. The variations of saturation magnetization, remnant magnetization and coercive fields as functions of temperature are also presented. Our results show evidence of superparamagnetic behaviour associated with the nanosized particles. Particle sizes appear to be critical in explaining the observed properties.     

Preparation of five-layered Si/SixGe1−x nano-films by RF helicon magnetron sputtering

Five-layered Si/Si_xGe_1−x films on Si(1 0 0) substrate with single-layer thickness of 30 nm, 10 nm and 5 nm, respectively were prepared by RF helicon magnetron sputtering with dual targets of Si and Ge to investigate the feasibility of an industrial fabrication method on multi-stacked superlattice structure for thin-film thermoelectric applications. The fine periodic structure is confirmed in the samples except for the case of 5 nm in single-layer thickness. Fine crystalline Si_xGe_1−x layer is obtained from 700 °C in substrate temperature, while higher than 700 °C is required for Si good layer. The composition ratio (x) in Si_xGe_1−x is varied depending on the applied power to Si and Ge targets. Typical power ratio to obtain x = 0.83 was 7:3, Hall coefficient, p-type carrier concentration, sheet carrier concentration and mobility measured for the sample composed of five layers of Si (10 nm)/Si_0.82Ge_0.18 (10 nm) are 2.55 × 10⁶ /°C, 2.56 × 10¹² cm⁻³, 1.28 × 10⁷ cm⁻², and 15.8 cm⁻²/(V s), respectively.     

The influence of substrate temperature and annealing on the properties of pulsed laser-deposited YIG films on fused quartz substrate

Yttrium iron garnet (YIG) thin films were deposited on fused quartz substrate at different substrate temperatures (T_s) varying from room temperature (RT) to 850 °C using pulsed laser deposition (PLD) technique. All the films in the as-deposited state were X-ray amorphous and non-magnetic at RT. The film deposited at RT after annealing at temperatures T_a?700 °C showed both X-ray peaks and the magnetic order. The films deposited at higher T_s (500–850 °C) and then annealed at 700 °C resulted in better-quality films with higher 4πM_s value. The highest value of magnetization was for the sample deposited at 850 °C and annealed at 700 °C, which is 68% of the bulk 4πM_s value.     

Magnetic properties of nanocrystalline Co1−xZnxFe2O4 prepared by forced hydrolysis method

Nanocrystalline zinc-substituted cobalt ferrite powders, Co_1−xZn_xFe₂O₄ (x=0, 0.2, 0.4), were for the first time prepared by forced hydrolysis method. Magnetic and structural properties in these specimens were investigated. The average crystallite size is about 3.0 nm. When the zinc substitution increases from x=0 to x=0.4, at 4.2 K, the saturation magnetization increases from 72.1 to 99.7 emu/g and the coercive field decreases from 1.22 to 0.71 T. All samples are superparamagnetic at room temperature and ferrimagnetic at temperatures below the blocking temperature. The high value of the saturation magnetization and the very thin thickness of the disorder surface layer of all samples suggests that this forced hydrolysis method is suitable not only for preparing two metal element systems but also for three or more ones.     

Effect of Bi substitution on the magnetic and dielectric properties of epitaxially grown BaFe0.3Zr0.7O3−δ thin films on SrTiO3 substrates

The structural, dielectric and magnetic properties of single crystalline Ba_1−xBi_xFe_0.3Zr_0.7O_3−δ (x=0.0-0.29) thin films have been studied. The pseudotetragonal epitaxial thin films were obtained by pulsed laser-beam deposition (PLD) on (0 0 1) SrTiO₃ (STO) single-crystal substrates. The Bi substitution for the Ba ions up to an extent of x=0.18 caused a slight improvement in the leakage current properties, as well as an enhancement of the apparent dielectric constant. The saturation magnetization of the films was significantly decreased following Bi substitution. These changes were thought to be related to the increase in oxygen deficiencies in the films. The effect of the Bi substitution on the dielectric and magnetic properties was analyzed in conjunction with the change in valence value of the Fe ions.     

Some studies about the green and red light emitting structures in NaCl1−xBrx:Mn

In this work we present the results obtained from the luminescence spectra and X-ray diffraction as well as transmission electron microscopy, at room temperature on crystals of NaCl_1−xNaBr_x:MnCl₂:0.3% (x=0.00, 0.05, 0.25, and 0.50). The results suggest the existence of structures between the crystal planes (1 1 1) and (2 0 0), which may be associated with different types of Mn²⁺ arrangements, such as dipole complexes, octahedral and rhombohedral structures as well as other possible nanostructures that include mixtures of bromine/chlorine ions. These are responsible for the emission spectra of “as grown” crystals consisting of maxima around 500 nm and 600 nm. The green emission has been usually attributed to rhombohedral/tetrahedral symmetry sites; the present results point out that this is due to Mn–Cl/Br nanostructures with rhombohedral structure. On the other hand when the crystals are thermally quenched from 500 °C to room temperature the structures previously detected present changes. Only a red band appears around 620 nm if the samples are later annealed at 80 °C.     

Doping effect of Mn on the magnetic behavior in Ni-Zn ferrite nanoparticles prepared by sol-gel auto-combustion

The ferrite samples of a chemical formula Ni_0.5−xMn_xZn_0.5Fe₂O₄ (where x=0.0, 0.1, 0.2, 0.3, 0.4, and 0.5) were synthesized by sol-gel auto-combustion method. The synthesized samples were annealed at 600 °C for 4 h. An analysis of X-ray diffraction patterns reveals the formation of single phase cubic spinel structure. The lattice parameter increases linearly with increase in Mn content x. An initial increase followed by a subsequent decrease in saturation magnetization with increase in Mn content is observed showing inverse trend of coercivity (H_c). Curie temperature decreases with increase in Mn content x. The initial permeability is observed to increase with increase in Mn content up to x=0.3 followed by a decrease, the maximum value being 362. Possible explanation for the observed structural, magnetic, and changes of permeability behavior with various Mn content are discussed.     

Room-temperature ferromagnetism in Sn1−xMnxO2 nanocrystalline thin films prepared by ultrasonic spray pyrolysis

Sn_1−xMn_xO₂ (x=0.01-0.05) thin films were synthesized on quartz substrate using an inexpensive ultrasonic spray pyrolysis technique. The influence of doping concentration and substrate temperature on structural and magnetic properties of Sn_1−xMn_xO₂ thin films was systematically investigated. X-ray diffraction (XRD) studies of these films reflect that the Mn³⁺ ions have substituted Sn⁴⁺ ions without changing the tetragonal rutile structure of pure SnO₂. A linear increase in c-axis lattice constant has been observed with corresponding increase in Mn concentration. No impurity phase was detected in XRD patterns even after doping 5 at% of Mn. A systematic change in magnetic behavior from ferromagnetic to paramagnetic was observed with increase in substrate temperature from 500 to 700 °C for Sn_1−xMn_xO₂ (x=0.01) films. Magnetic studies reveal room-temperature ferromagnetism (RTFM) with 3.61×10⁻⁴ emu saturation magnetization and 92 Oe coercivity in case of Sn_1−xMn_xO₂ (x=0.01) films deposited at 500 °C. However, paramagnetic behavior was observed for the films deposited at a higher substrate temperature of 700 °C. The presence of room-temperature ferromagnetism in these films was observed to have an intrinsic origin and could be obtained by controlling the substrate temperature and Mn doping concentration.