Fabrication,characterization, and performance evaluation of polyethersulfone/TiO2 nanocomposite ultrafiltration membranes for produced water treatment

In the present work, development of neat and nanocomposite polyethersulfone membranes composed of TiO₂ nanoparticles is presented. Membranes are fabricated using nonsolvent phase inversion process with the objective of improving antifouling, hydrophilicity, and mechanical properties for real and synthetic produced water treatment. Membranes are characterized using scanning electron microscopy, Fourier‐transform infrared, contact angle, porosity measurement, compaction factor, nanoparticles stability, and mechanical strength. The performance of prepared membranes was also characterized using flux measurement and oil rejection. Fourier‐transform infrared spectra indicated that noncovalence bond formed between Ti and polyethersulfone chains. The contact angle results confirmed the improved hydrophilicity of nanocomposite membranes upon addition of TiO₂ nanoparticles owing to the strong interactions between fillers and water molecules. The increased water flux for nanocomposite membranes in comparison with neat ones can be due to coupling effects of improved surface hydrophilicity, higher porosity, and formation of macrovoids in the membrane structure. The membrane containing 7 wt% of TiO₂ nanoparticles was the best nanocomposite membrane because of its high oil rejection, water flux, antifouling properties, and mechanical stability. The pure water flux for this membrane was twice greater than that of neat membrane without any loss in oil rejection. The hydrophilicity and antifouling resistance against oil nominates developed nanocomposite membranes for real and synthetic produced water treatment applications with high performance and extended life span.     

Improving surface structure of photocatalytic self‐cleaning membrane by WO3/PANI nanoparticles

To create a self‐cleaning feature and improve antifouling property, polysulfone (PSf) membranes were modified with WO₃ and polyaniline (PANI) nanoparticles (0–2 wt%) via phase inversion method for ultrafiltration of landfill leachate. The mass ratio of WO₃ nanoparticles was varied between 0, 40 and 60 wt% in different loadings. All synthesized membranes were tested with and without UV irradiation to evaluate the self‐cleaning feature. The synthesized PANI was analyzed with scanning electron morphology (SEM), atomic force microscopy (AFM) and Fourier transform infrared spectroscopy (FTIR). The surface hydrophilicity of the modified membranes increases with increasing the nanoparticle loadings (0–2 wt%). The membrane morphology indicated higher porosity and more finger like pores for the modified membranes. The porosity of 86.8% was achieved for the membrane containing 2 wt% PANI. The flux recovery ratio (FR) of membranes without UV radiation was increased by increasing the ratio of PANI to WO₃ nanoparticles, while the antifouling ability of membranes including WO₃ nanoparticles improved and reached to 98.87% after UV radiation. The highest COD removal before (76.65 %) and after (78.42%) UV radiation was obtained for the membrane containing 2 wt% nanoparticle loading. Copyright © 2016 John Wiley & Sons, Ltd.     

Thermo-responsive and antifouling PVDF nanocomposited membranes based on PNIPAAm modified TiO2 nanoparticles

A novel hydrophilic nanocomposite additive(TiO2-g-PNIPAAm) was synthesized by the surface modification of titanium dioxide(TiO2) with N-isopropylacrylamide(NIPAAm) via "graft-from" technique. And the nanocomposite membrane of poly(vinylidene fluoride)(PVDF)/TiO2-g-PNIPAAm was fabricated by wet phase inversion. The graft degree was obtained by thermo-gravimetric analysis(TGA). Fourier transform infrared attenuated reflection spectroscopy(FTIR-ATR) and X-ray photoelectronic spectroscopy(XPS) characterization results suggested that TiO2-g-PNIPAAm nanoparticles segregated on membrane surface during the phase separation process. Scanning electron microscopy(SEM) was conducted to investigate the surface and cross-section of the modified membranes. The water contact angle measurements confirmed that TiO2-g-PNIPAAm nanoparticles endowed PVDF membranes better hydrophlilicity and thermo-responsive properties compared with those of the pristine PVDF membrane. The water contact angle decreased from 92.8° of the PVDF membrane to 61.2° of the nanocompostie membrane. Bovine serum albumin(BSA) static and dynamic adsorption experiments suggested that excellent antifouling properties of membranes was acquired after adding TiO2-gPNIPAAm. The maximum BSA adsorption at 40 °C was about 3 times than that at 23 °C. The permeation experiments indicated the water flux recover ratio and BSA rejection ratio were improved at different temperatures.     

Formation of appropriate sites on nanofiltration membrane surface for binding TiO2 photo-catalyst: Performance, characterization and fouling-resistant capability

Titanium dioxide (TiO₂) nanoparticles were assembled on the surface of nanofiltration blend membrane. For settling TiO₂ on the membrane surface, two membrane categories were used: (i) unmodified polyethersulfone (PES)/polyimide (PI) blend membrane, and (ii) –OH functionalized PES/PI blend membrane with different concentrations of diethanolamine (DEA). These membranes were radiated by UV light after TiO₂ depositing with different concentrations. 15 min immersion in colloidal suspension and 15 min UV irradiation with 160 W lamps were used for modification. The modification resulted in the formation of a photo-catalytic property with enhanced membrane hydrophilicity. The self-assembly of TiO₂ nanoparticles was established through coordinance bonds with –OH functional groups on the membrane surface. A comparison between the UV irradiated TiO₂ deposited blend membrane and deposited-functionalized blend membranes showed that –OH groups originate excellent adhesion of TiO₂ nanoparticles on the membrane surface, increase reversible deposition, and diminish irreversible fouling. The membranes were characterized using SEM, FTIR, EDX, contact angle, cross flow filtration, and antifouling measurements. SEM images show that the presence of –OH groups on the DEA-modified membrane surface is the main parameter for extra uniformly settlement of TiO₂ nanoparticles on the membrane surface. This procedure is a superior technique for modification of PES/PI nanofiltration membranes to enhance water flux and minimization membrane fouling.     

Preparation and properties of amorphous titania-coated zinc oxide nanoparticles

Amorphous TiO₂-coated ZnO nanoparticles were prepared by the solvothermal synthesis of ZnO nanoparticles in ethanol and the followed by sol-gel coating of TiO₂ nanolayer. The analyses of X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that the resultant ZnO nanoparticles were hexagonal with a wurtzite structure and a mean diameter of about 60 nm. Also, after TiO₂ coating, the TEM images clearly indicated the darker ZnO nanoparticles being surrounded by the lighter amorphous TiO₂ layers. The zeta potential analysis revealed the pH dependence of zeta potentials for ZnO nanoparticles shifted completely to that for TiO₂ nanoparticles after TiO₂ coating, confirming the formation of core-shell structure and suggesting the coating of TiO₂ was achieved via the adhesion of the hydrolyzed species Ti-O⁻ to the positively charged surface of ZnO nanoparticles. Furthermore, the analyses of Fourier transform infrared (FTIR) and Raman spectra were also conducted to confirm that amorphous TiO₂ were indeed coated on the surface of ZnO nanoparticles. In addition, the analyses of ultraviolet-visible (UV-VIS) and photoluminescence (PL) spectra revealed that the absorbance of amorphous TiO₂-coated ZnO nanoparticles at 375 nm gradually decreased with an increase in the Ti/Zn molar ratio and the time for TiO₂ coating, and the emission intensity of ZnO cores could be significantly enhanced by the amorphous TiO₂ shell.     

Evaluation of in vitro bioactivity and MG63 Oesteoblast cell response for TiO2 coated magnesium alloys

The present investigation reports TiO₂ coating on magnesium alloy AZ31 by sol–gel method via dip coating technique. TiO₂ coated surface was characterized by thin film X-ray diffraction (TF-XRD), Fourier transform infrared red (FT-IR) spectroscopy, scanning electron microscopy (SEM) with energy-dispersive X-ray (EDX) spectroscopy, atomic force microscopy (AFM) and transmission electron microscopy (TEM) techniques. From TF-XRD results, the peaks at 2θ values of 25.14, 32.12, 68.73 and 70.11 confirm the presence of TiO₂. The TiO₂ is crystalline in nature and the crystallite size is about 32.4 nm. SEM-EDX, TEM and AFM show that the coated surface is uniform and nanoporous. FT-IR analysis shows that the peak in the range of 692 cm^?1 is assigned to Ti–O–Ti stretching vibration. Contact angle measurements show that the coating is hydrophilic in nature. Bioactivity of the coating in simulated body fluid (SBF) was also examined, the hydroxyl functionalized surface greatly enhances the hydroxyapatite growth. The potentiodynamic polarization studies prove that the corrosion resistance of the TiO₂ coated surface after immersion in SBF for 7 days is improved dramatically. Cell adhesion studies confirm the increased cell attachment on TiO₂ coated surface when compared to uncoated alloy, due to less amount of Mg ion release from the substrate in the culture medium.     

Using PDMS coated TFC-RO membranes for CO2/N2 gas separation: Experimental study,modeling and optimization

Thin film composite (TFC) reverse osmosis (RO) membranes are semipermeable membranes that are utilized in water purification or water desalination systems. Discarding these membranes after end-of-life leads to environmental problems. Reusing old TFC-RO membranes is one way to solve this problem. For this reason, in this study, used TFC-RO membranes were coated with polydimethylsiloxane (PDMS) for CO₂/N₂ gas separation application. Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) was utilized to confirm the crosslinking of coated PDMS. The morphology of PDMS/TFC-RO membranes was characterized using scanning electron microscopy (SEM). The parameters that can affect performance of prepared membranes (N₂ permeance and CO₂/N₂ selectivity) are concentration of PDMS solution, coating time, solvent evaporation time and curing temperature and time. Given that the used membranes don't have uniform surfaces, the first step of this study was to investigate the effect of the above mentioned factors on virgin membranes using fractional factorial design (FFD) of experiments. The results obtained showed that PDMS concentration is the most significant factor that has a negative effect on N₂ permeance and positive effect on CO₂/N₂ selectivity. The reported CO₂/N₂ selectivity of PDMS membranes was 11–12, but this selectivity for prepared PDMS/TFC-RO membranes was in the range of 6.7–22.5. After determining optimum conditions, the gas separation performance of PDMS coated used TFC-RO membrane under these conditions was finally determined. The results showed that the used membranes had a better performance than virgin membranes.     

Virus and bacterial removal ability of TiO2 nanowire-based self-supported hybrid membranes

Development and application of hybrid membranes containing multi-component materials are increasing day by day in the fields of environmental protection and water treatment. In this research, the efficiency of titania nanowire (TiO₂ NW)-based self-supported hybrid membranes was investigated in the removal of Escherichia coli (E. coli) bacteria and MS2 bacteriophages from contaminated water mimicking the microorganism suspension. Furthermore, toxicology tests on the as-prepared membranes were also performed. TiO₂ NWs were coated with iron(III) oxide (Fe₂O₃) and copper(II) oxide (CuO) nanoparticles, respectively, and cellulose was used as reinforcement material. It was found that, the functionalisation strongly affected the MS2 removal ability of as-prepared membranes, which can be due to the electrostatic interactions between the surface of hybrid membrane and the bacteriophages. The most efficient removal (greater than or equal to 99.99%) was obtained with the TiO₂ NW-CuO-cellulose membrane at pH 7.0. The fabricated hybrid membranes were characterized by micro computed tomography (μCT), Raman spectroscopy, Fourier transform infrared spectroscopy (FT-IR), dynamic light scattering (DLS), contact angle measurement and inductively coupled optical emission spectrometry (ICP-OES) techniques. This study shows a simple route of the usage of novel and effective inorganic nanowire-based hybrid membranes for bacteria and virus removal, providing new pathways in the field of water filtration technologies.     

Pebax/TSIL blend thin film composite membranes for CO_2 separation

In this study a thin film composite (TFC) membrane with a Pebax/Task-specific ionic liquid (TSIL) blend selective layer was prepared. Defect-free Pebax/TSIL layers were coated successfully on a polysulfone ultrafiltration porous support with a polydimethylsiloxane (PDMS) gutter layer. Different parameters in the membrane preparation (e.g. concentration, coating time) were investigated and optimized. The morphology of the membranes was studied by scanning electron microscopy (SEM), while the thermal properties and chemical structures of the membrane materials were investigated by thermo-gravimetric analyzer (TGA), differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR). The CO₂ separation performance of the membrane was evaluated using a mixed gas permeation test. Experimental results show that the incorporation of TSIL into the Pebax matrix can significantly increase both CO₂ permeance and CO₂/N₂ selectivity. With the presence of water vapor, the membrane exhibits the best CO₂/N₂ selectivity at a relative humidity of around 75%, where a CO₂ permeance of around 500 GPU and a CO₂/N₂ selectivity of 46 were documented. A further increase in the relative humidity resulted in higher CO₂ permeance but decreased CO₂/N₂ selectivity. Experiments also show that CO₂ permeance decreases with a CO₂ partial pressure increase, which is considered a characteristic in facilitated transport membranes.     

LB技术制备SnO2-TiO2无机交替纳米薄膜

采用LB技术将SnO₂纳米粒子和TiO₂纳米粒子组装进花生酸的交替多层膜，通过热处理除去膜中的有机成分后，采用红外光谱、紫外可见光谱、X-光电子能谱、低角X-射线衍射、原子力显微镜以及扫描电子显微镜等手段对处理后的膜进行了形貌、组成和结构表征，表明制得的是SnO₂纳米粒子-TiO₂纳米粒子无机-无机交替的均匀的纳米薄膜。     

Development of polyaniline – TiO2 nano composite films and its application in corrosion inhibition of oil pipelines

Oil and gas industries are the driving force of Oman’s economy and have a relatively diversified wealth among Gulf Cooperation Council Countries. Oil pipelines play an important role in transporting oil and gas from the wellheads to the processing facilities. Corrosion normally results in the deterioration of the pipe material with exposure to the surrounding environment and complete control of corrosion is difficult. Corrosion in oil transmission pipeline would be effectively addressed by introducing conventional corrosion control practices. Most of the conventional techniques are either less effective or too expensive in controlling the deterioration rate of the pipe materials. However, preventative measures may be taken to protect the metal surface from corrosion is a possible way to reduce corrosion. This research work aimed to develop a novel technique utilizing Polyaniline (PANI) and Titanium dioxide (TiO₂) nanocomposites to assess its corrosion inhibition effect on mild steel. TiO₂ was synthesized by sol-gel process. Polyaniline-Titanium dioxide (PANI/TiO₂) nanocomposites were coated on mild steel specimen by dip coating technique. The coated specimen was subjected to stability studies at different environmental conditions and exposure time. The stable thin film coated specimen was employed in the corrosion inhibition studies at various processing environments. The characteristics of TiO₂ nanoparticles and PANI-TiO₂ thin films were analyzed using Fourier Transform Infra-Red Spectroscopy (FTIR), Energy Dispersive X-Ray analysis (EDX) and X-Ray Diffraction (XRD) and Dynamic Light scattering (DLS). Scanning Electron Microscopy (SEM) was used to visualize the surface morphology and micro structural characteristics of the preformed thin layer. Potentio dynamic test, Atmosphere test and Wet/Dry tests were carried out to investigate the corrosion behaviour of coated and uncoated specimen. The study demonstrates that the Polyaniline – TiO₂ composite thin films fabricated using dip coating technique with minimum film thickness could be a feasible solution in controlling the corrosion in oil pipelines with good film stability, high durability, with a cost effective and environmentally friendly approach.     

Sol–Gel Derived Rh/TiO<Subscript>2</Subscript>/SiO<Subscript>2</Subscript> Nanocomposite Membranes

A porous borosilicate substrate has been coated with base catalysed SiO₂ sol–gel nanoparticles. Onto these were deposited the vapour of titanium isopropoxide, where it reacted with the surface OH groups to give a TiO₂-overcoat. This nanocomposite sol–gel derived TiO₂/SiO₂ membrane was then doped with 1%Rh giving Rh/TiO₂/SiO₂ membranes. These are shown to be coherent and crack-free, to have good permeability and activity in the isomerisation of butanes. It appears that sol–gel chemistry will allow such membranes to be totally engineered at a nm level.     

Nanocomposites of poly(l-lactide) and surface-grafted TiO2 nanoparticles: Synthesis and characterization

A new method of surface modification of TiO₂ nanoparticles by surface-grafting l-lactic acid oligomer was developed. The surface-grafting reaction was evaluated by Fourier transformation infrared (FTIR) and thermal gravimetric analysis (TGA). The results showed that l-lactic acid oligomer could be easily grafted onto the TiO₂ nanoparticles surface in the presence of stannous octanoate and the highest amount of grafted polymer was about 8.5% in weight. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) results showed that grafted TiO₂ (g-TiO₂) in chloroform or PLLA matrix approximated to uniform, while unmodified TiO₂ nanoparticles tended to aggregate. The tensile strength of this material was greatly improved by the addition of g-TiO₂ nanoparticles in poly(l-lactide) (PLLA) matrix. The tensile strength of the g-TiO₂/PLLA nanocomposite containing 5 wt.% of g-TiO₂ was 72 MPa, which was 23.1% higher than that of pure PLLA. Even though the incorporation of the TiO₂ nanoparticles into PLLA led to the deterioration of its elongation at break, the g-TiO₂/PLLA nanocomposite also exhibited better ductility than that of TiO₂/PLLA nanocomposite.     

Impact of TiO2 nanoparticles on morphology and performance of crosslinked polyimide organic solvent nanofiltration (OSN) membranes

Chemically crosslinked polyimide organic–inorganic composite nanofiltration membranes suitable for application in harsh organic solvents were successfully prepared by phase inversion of dope solutions. TiO₂ nanoparticles were dispersed in these dope solutions, comprising polyimide (PI) in N,N-dimethylformamide/1,4-dioxane. The impact of TiO₂ on the resulting PI membranes was investigated using SEM, TGA, water contact angle, dope viscosity measurements and mechanical strength. The presence of TiO₂ nanoparticles within the membrane matrix was proved by the detection of a peak characteristic of TiO₂ in the WAXS pattern. SEM pictures of the cross-section of the PI/TiO₂ membranes showed dramatically changed morphology compared to reference membranes with no TiO₂ addition. Macrovoids present in reference membranes were suppressed by increasing loading of TiO₂ nanoparticles, and eventually disappeared completely at a TiO₂ loading above 3 wt.%. Decreasing water contact angle and an increase in ethanol flux indicated that hydrophilicity increased as nanoparticle loading increased. The effect of TiO₂ on the functional performance of the membranes was evaluated by measuring flux and rejection using cross-flow filtration. Perhaps surprisingly, the presence of TiO₂ improved the compaction resistance of the membranes, whereas rejection and steady flux were almost unaltered.     

ZIF-8 based polysulfone hollow fiber membranes for natural gas purification

Mixed matrix membranes (MMMs) have received worldwide attention for natural gas purification due to their superior performance in terms of permeability and selectivity. The zeolitic imidazole framework-8 (ZIF-8) blended polysulfone (PSf) membranes have been fabricated for natural gas purification. ZIF-8 was selected due to its low cost, remarkable thermal and chemical stabilities, and tunable microporous structure. The neat PSf hollow fiber membrane and mixed matrix hollow fiber membranes incorporated with the various ZIF-8 loadings up to 1.25% were fabricated. The prepared membranes were evaluated using field emission scanning electron microscopy (FESEM), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), atomic force microscopy (AFM), and gas separation performance. The low loading of ZIF-8 nanoparticles to the MMM improved thermal stability and glass transition temperature and yielded low surface roughness. MMMs were tested using pure gases with a significant improvement of 36% in CO₂ permeability and 28% in CO₂/CH₄ selectivity compared to the neat membrane. However, the high ZIF-8 loading reduced the separation performances. Moreover, CO₂/CH₄ selectivity decreased at elevated pressure (8 and 10 bar) due to CO₂-induced plasticization. Previously, the incorporation of ZIF-8 particles has primarily been subjected to the fabrication of flat sheet membranes, whereas this work focused on hollow fiber membranes which are rarely investigated. Hence, the promising results obtained at low feed pressure in this study demonstrated the potential of ZIF-8 based hollow fiber membrane for natural gas purification.     

Surface modification of sulfonated polyvinylchloride cation-exchange membranes by using chitosan polymer containing Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles

Sulfonated polyvinylchloride (SPVC) cation-exchange membranes were coated using chitosan solutions comprising different amounts of Fe₃O₄ nanoparticles. Influence of chitosan immobilization as well as nanofiller concentration on the electrochemical performance of the membranes was investigated. Electrochemical properties of the membranes including permselectivity, ionic permeability, and areal resistance were studied using an equipped electrodialysis setup and NaCl solution as model electrolyte. Scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) were employed for membrane characterization. Electrochemical performance of the SPVC membranes was improved by coating chitosan polymer. In addition, ionic permeability and permselectivity of the membranes were initially raised by increasing nanoparticles concentration from nil to 2 wt% and then decreased by further insertion of the nanofiller. The areal resistance of the plain SPVC membrane was decreased from 9.4 to 2.9 (ohm) by coating of chitosan solution including optimum value of nano-Fe₃O₄ due to electrical potential field enhancement across the membrane.

Open image in new window

Graphical Abstract Chitosan-coated cation-exchange membranes for electrodialysis process

     

Synthesis and Ex-situ Characterization of Nafion/TiO2 Composite Membranes for Direct Ethanol Fuel Cell

Nafion/TiO₂ composite membranes for different loadings of TiO₂ were prepared by casting method for the possible application in direct ethanol fuel cell (DEFC). The properties of the composite membranes were investigated by scanning electron microscopy (SEM), x-ray diffraction (XRD), thermogravimetric analyser (TGA), ion exchange capacity, water and alcohol uptake, swelling ratio, proton conductivity, and ethanol crossover. The observed characteristics of the membranes were evaluated for DEFC and compared with the direct methanol fuel cell (DMFC) membrane. The analysis reveales a significant influence on the TiO₂ surface characteristics, water and alcohol uptake, and swelling of the membrane. The TiO₂ composite membranes exhibited a sharp decrease in methanol and ethanol crossover for 5% TiO₂ and the proton conductivity was heighest for 1% TiO₂ loading. The best compromise between proton conductivity and crossover has been found out with the help of the characteristic factor ϕ. The optimum loading of 5% TiO₂ composite membrane has shown the maximum characteristic factor.     

Effect of TiO2 nanoparticles on structure and properties of high density polyethylene membranes prepared by thermally induced phase separation method

Polyethylene/TiO₂ membranes were fabricated via thermally induced phase separation (TIPS) method. A set of characterization tests including FE‐SEM, EDX, XRD, DSC, TGA, DMA, mechanical test and relative pure water flux for characterization of membranes were carried out to investigate the effect of TiO₂ nanoparticles on membrane properties. The results of EDX, XRD and TGA analyses confirmed the presence of TiO₂ nanoparticles in the polymer matrix. The results of DSC analysis revealed that the melting point as well as the crystallinity of the membranes increased slightly with increasing TiO₂ content. However, the glass transition temperature of the membranes was not affected by the presence of particles. Addition of nanoparticles also increased storage modulus, loss modulus and tensile strength at break of the membranes due to the stiffness improvement effect of inorganic TiO₂. Finally, it was observed that incorporation of the nanoparticles improved pure water flux of the membranes. Copyright © 2015 John Wiley & Sons, Ltd.     

Preparation,photocatalytic activity and mechanism of nano-Titania/Nafion hybrid membrane

Nano-Titania/Nafion (TiO₂/Nafion) hybrid membranes were prepared by recasting, using Nafion solution and TiO₂ anatase hydrosol as the raw materials. The microstructure of the hybrid membrane was characterized by X-ray diffraction, high-resolution transmission electron microscopy (HR-TEM), X-ray Photoelectron Spectroscopy and Fourier Transform Infrared Spectroscopy (FT-IR). The photocatalytic properties of TiO₂/Nafion hybrid membranes were evaluated. Furthermore, endurance of photocatalytic activity of the hybrid membrane was investigated. The results indicate that the TiO₂ Nanoparticles are bounded to Nafion molecule via Ti-O-S bonds and the formed flocculates are distributed homogeneously throughout the recasting Nafion membrane, while the initial pure anatase TiO₂ nanoparticles remain intact in re-crystallized membrane. The hybrid membranes possessed excellent photocatalytic activities with and without H₂O₂. Moreover, the degradation of photocatalytic activities has been better controlled with the presence of H₂O₂.     

Casting of poly (vinyl alcohol)/glycidyl methacrylate reinforced with titanium dioxide nanoparticles for proton exchange fuel cells

Gamma irradiation was used for cross-linking poly (vinyl alcohol) (PVA) and glycidyl methacrylate (GMA) mixtures of different compositions. Specifically, 0.5 wt% titanium dioxide (TiO₂) nanoparticles were added and blended well with the casting mixture prior to exposure to the irradiation dose. Next, 10 kGy was found to be the optimum dose for achieving the desired physical and chemical properties of the membrane. Characterizations of the cast membranes were carried out by Fourier transformer infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and positron annihilation lifetime spectroscopy (PALS). The properties of the membrane were also characterized by ion exchange capacity (IEC), water uptake, and tensile strength and were assessed in relation to application in proton exchange membrane fuel cells (PEMFCs). A maximum proton conductivity of 7.3 × 10^?2 S cm^?1 was obtained for the membrane having 20 % GMA, 80 % PVA, and 0.5 % TiO₂, and its activity and durability in a membrane electrode assembly (MEA) were compared to those of a commercial Nafion® 1350.