High-field electron emission of carbon nanotubes grown on carbon fibers

Carbon nanotubes with uniform density were synthesized on carbon fiber substrate by the floating catalyst method. The morphology and microstructure were characterized by scanning electron microscopy and Raman spectroscopy. The results of field emission showed that the emission current density of carbon nanotubes/carbon fibers was 10 μA/cm² and 1 mA/cm² at the field of 1.25 and 2.25 V/μm, respectively, and the emission current density could be 10 and 81.2 mA/cm² with the field of 4.5 and 7 V/μm, respectively. Using uniform and sparse density distribution of carbon nanotubes on carbon fiber substrate, the tip predominance of carbon nanotubes can be exerted, and simultaneously the effect of screening between adjacent carbon nanotubes on field emission performance can also be effectively decreased. Therefore, the carbon nanotubes/carbon fibers composite should be a good candidate for a cold cathode material.     

Vertically aligned carbon nanotubes from natural precursors by spray pyrolysis method and their field electron emission properties

Vertically aligned carbon nanotubes have been synthesized from botanical hydrocarbons: Turpentine oil and Eucalyptus oil on Si(100) substrate using Fe catalyst by simple spray pyrolysis method at 700°C and at atmospheric pressure. The as-grown carbon nanotubes were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), thermogravimetric analysis (TGA), differential thermal analysis (DTA), and Raman spectroscopy. It was observed that nanotubes grown from turpentine oil have better degree of graphitization and field emission performance than eucalyptus oil grown carbon nanotubes. The turpentine oil and eucalyptus oil grown carbon nanotubes indicated that the turn-on field of about 1.7 and 1.93 V/μm, respectively, at 10 μA/cm². The threshold field was observed to be about 2.13 and 2.9 V/μm at 1 mA/cm² of nanotubes grown from turpentine oil and eucalyptus oil respectively. Moreover, turpentine oil grown carbon nanotubes show higher current density in relative to eucalyptus oil grown carbon nanotubes. The maximum current density of 15.3 mA/cm² was obtained for ∼3 V/μm corresponding to the nanotubes grown from turpentine oil. The improved field emission performance was attributed to the enhanced crystallinity, fewer defects, and greater length of turpentine oil grown carbon nanotubes.     

丝网印刷制备碳纳米管阴极的强流脉冲发射特性研究

采用丝网印刷法制备了一种大面积的碳纳米管阴极,表征了阴极表面碳纳米管的形貌及分布.研究了该阴极在不同脉冲条件下的高压脉冲发射特性,分析了发射时阴极面等离子体产生和发射点的分布.研究表明：碳纳米管阴极的脉冲发射机制为爆炸电子发射,在平均场强为16.7V/μm的单脉冲电场下,阴极的最高发射电流密度为99 A/cm².在平均场强为15.4 V/μm的双脉冲电场下,阴极的最高发射电流密度为267 A/cm².碳纳米管阴极可以作为强流电子束源在高能微波器件中得到应用. 关键词： 强流脉冲电子束 碳纳米管 阴极 丝网印刷     

一种平行栅碳纳米管阵列阴极的场发射特性研究

建立一种平行栅碳纳米管阵列阴极,利用悬浮球模型和镜像电荷法进行计算,给出碳纳米管顶端表面电场与电场增强因子的解析式. 在此基础上,进一步分析器件各类参数以及接触电阻对阴极电子发射性能的影响. 分析表明,碳纳米管间距大约为2倍碳纳米管高度时阵列阴极的分布密度最佳,靠边缘部位的碳纳米管发射电子能力比其中心部位的大;除碳纳米管的长径比之外,栅极宽度和栅极间距也对电场增强因子有一定作用;接触电阻的存在大幅度降低碳纳米管顶端表面电场与发射电流,而接触电阻高于800 kΩ时,器件对阳极驱动电压的要求更高. 关键词： 平行栅碳纳米管阵列 悬浮球 场增强因子 接触电阻     

太赫兹源场致发射电子源

通过粒子模拟(PIC)软件模拟计算了在ps级别下二极与三极结构碳纳米管场致发射的电流密度与电子注聚焦性能。阳极电压在2 kV时,二极结构下电流密度达到1.85 A/cm2;三极结构下,栅压700 V时发射电流密度达到2.3 A/cm2,且在一定的三极结构参数与电极电压下,可以获得较好的电子注聚束效果。通过碳纳米管二极管发射实验,获得了6.6 A/cm2的发射电流密度,总发射电流达到52.1 mA,可以为太赫兹器件提供连续发射的电子注。     

Improving the field-emission properties of carbon nanotubes by magnetically controlled nickel-electroplating treatment

A novel magnetically controlled Ni-plating method has been developed to improve the field-emission properties of carbon nanotubes (CNTs). The effect of the magnetic field and Ni-electroplating on CNT field-emission properties was investigated, and the results are demonstrated using scanning electron microscopy, J-E and the duration test. After treatment, the turn-on electric field declines from 1.55 to 0.91 V/μm at an emission current density of 100 μA/cm², and the emission current density increases from 0.011 to 0.34 mA/cm² at an electric field of 1.0 V/μm. Both the brightness and uniformity of the CNT emission performance are improved after treatment.     

碳纳米管阴极的强流脉冲发射性能研究

采用丝网印刷和涂敷方法制备了两种碳纳米管阴极，并研究了两种阴极的强流脉冲发射特性，表征了阴极表面碳纳米管的形貌及分布.研究结果表明在脉冲宽度为100 ns、电压为1.64×10⁶ V的脉冲电场下，涂敷法制备阴极的场发射电流最高达5.11 kA，最高发射电流密度达260 A/cm².丝网印刷法制备阴极的场发射稳定性优于涂敷法制备阴极，但其发射电流低.阴极表面发射体的形貌与分布影响了阴极的脉冲发射性能.碳纳米管阴极的脉冲发射机理为爆炸电子发射.碳纳米管阴极可以作为强 关键词： 碳纳米管 阴极 脉冲发射 强电流     

碳、碳氮和硼碳氮纳米管场发射性能的比较研究

采用高温热解法在860℃分别制备出了碳、碳氮和硼碳氮纳米管，提纯后利用丝网印刷工艺分别将它们制备成薄膜，并测试了它们的场发射性能.结果表明：碳纳米管、碳氮纳米管和硼碳氮纳米管薄膜的开启电场分别为2.22，1.1和4.4V/μm，当电场增加到5.7V/μm时，它们的电流密度分别达到1400，3000μA/cm²和小于50μA/cm².碳和碳氮纳米管薄膜的场增强因子分别为10062和11521.可见，碳氮纳米管的场发射性能优于碳纳米管，而硼碳氮纳米管的场发射性能比前两者要差.解释了这三种纳米管场发射性能差别的原因. 关键词： 碳纳米管 碳氮纳米管 硼碳氮纳米管 场发射     

Electrodeposition of Ag nanoparticles onto bamboo-type TiO2 nanotube arrays to improve their lithium-ion intercalation performance

Bamboo-type TiO₂ nanotube arrays prepared via anodic oxidation are modified with Ag nanoparticles by pulsed electrochemical deposition, for improved lithium-ion intercalation property as the anode material in lithium-ion batteries. Heat treatment converts as-formed nanotubes into anatase for Ag deposition. Bare and Ag-modified nanotubes are cycled at a current density of 800 μA?cm^?2 between 1.0 and 2.6 V (vs. Li/Li⁺). All Ag-modified nanotubes exhibit significantly improved or even doubled areal discharge capacities and better cycleability compared to bare nanotubes. Particularly, the nanotubes modified using 100 Ag deposition cycles deliver the highest initial discharge capacity of 199.6 μA?h cm^?2 and the largest final discharge capacity of 131.7 μA?h cm^?2 after 50 electrochemical cycles, while bare nanotubes exhibit an initial capacity of 93.5 μA?h cm^?2 and a final discharge capacity of 54.8 μA?h cm^?2. The former also exhibits 10 % higher capacity retention efficiency than the latter. In addition, an increase in the capacity of modified nanotubes is observed with more Ag deposition, but superfluous Ag content yields reduced capacities due to slower Li-ion transfer inside. Finally, kinetic characteristics of TiO₂ nanotubes are explored using cyclic voltammetry to understand the origin of improvements in electrochemical properties of Ag-modified nanotubes.     

Field emission performances of CNTs bundles array

The field emission performances of normal-gate cold cathode, which is composed of different multi-wall carbon nanotubes (MWCNTs) bundles array are calculated. The device parameters such as the arrangement of bundles, array density, gate location, gate voltage, anode voltages and anode–cathode distance affect the field emission properties, which is discussed in detail. The results reveal that the hexagon bundles array needs a lower threshold voltage than square array to reach high field enhancement factor and large emission current density. The emission current density is two orders larger than that of the oxide emitter. The optimal bundles array densities of hexagon and square array to get field enhancement factor are 0.0063 and 0.00375 μm⁻², respectively. Meanwhile, the field emission performances are impacted critically by gate location and gate voltage. Field emission properties changed little while the anode–cathode distance varies within tens of micrometers, which increases the process-friendliness of CNTs field emission devices.     

Electron field emission properties of conducting polymer coated multi walled carbon nanotubes

The present work describes the field emission characteristics of conducting polymer coated multi walled carbon nanotubes (MWNTs) field emitters fabricated over flexible graphitized carbon cloth. Nanocomposites involving the combination of MWNTs and conducting polymers polyaniline (PANI) and polypyrrole (PPy) have been prepared by in-situ polymerization method and have been characterized using scanning electron microscopy and transmission electron microscopy. Using spin coating method, field emitters based on PANI/MWNTs and PPy/MWNTs over flexible graphitized carbon cloth have been prepared. The field emission characteristics have been studied using an indigenously fabricated set up in a vacuum chamber with a base pressure of 2 × 10⁻⁵ Pa and the results are discussed. Our results display that the field emission performance of the emitters depends strongly on the work function of the emitting material. Low turn on emission field of 2.12 V/μm at 10 μA/cm² and high emission current density of 1 mA/cm² at 3.04 V/μm have been observed for PANI/MWNTs field emitter.     

Ultrasonic preparation of tetraoxalyl ethylenediamine melamine resin-coated multiwalled carbon nanotubes for trace Ni(II) sensing

Under an aid of ultrasonic, tetraoxalyl ethylenediamine melamine resin-coated multiwalled carbon nanotubes were prepared for Ni(II) sensing in aqueous solution. The processes involved the fabrication of tetraoxalyl ethylenediamine melamine resin by one pot way, the coating of tetraoxalyl ethylenediamine melamine resin at multiwalled carbon nanotubes (MWCNTs), and the determination of Ni(II). The present materials were carefully examined by Fourier transform infrared spectroscopy, field emission scanning electron microscope, and electrochemistry techniques. A great deal of amorphous microsphere could be observed for tetraoxalyl ethylenediamine melamine resin with an average diameter of 1.2 μm, and MTE could evenly adhere at the surface of MWCNTs by the ultrasonic. Tetraoxalyl ethylenediamine melamine resin-coated multiwalled carbon nanotube-modified paraffin-impregnated graphite electrode was successfully used for the determination of Ni(II) by differential pulse adsorptive anodic stripping voltammetry. The current responses (?0.3 V) were linearly increased depending on the concentration from 1?×?10^?11 to 3?×?10^?10 M (i (μA)?=?11.1?+?7.9 c (1?×?10^?12 M); R?=?0.9901, 3σ?=?7?×?10^?12 M).     

Microtopography and field emission properties of carbon films grown in a microwave gas discharge plasma

Graphite-like carbon films are grown in an ethanol vapor plasma in a microwave gas discharge. The electrical parameters controlling the microtopography and electronic properties of carbon films are determined. It is shown that electron bombardment affects the fine structure of graphite-like nanocrystallites and their emissive power with characteristics close to those of carbon nanotubes. The emission properties of layered graphite-like films can be improved by metal (cadmium) impurity doping. For nanocrystalline graphite-like films, emission currents with a density of 0.3 A/cm² are induced at an electric field strength of less than 7 V/μ m in the gap. __________ Translated from Fizika Tverdogo Tela, Vol. 46, No. 2, 2004, pp. 367–371. Original Russian Text Copyright ? 2004 by Suzdal’tsev, Yafarov.     

An improved planar-gate triode with CNTs field emitters by electrophoretic deposition

An improved planar-gate triode with carbon nanotubes (CNTs) field emitters has been successfully fabricated by conventional photolithography, screen printing and electrophoretic deposition (EPD). In this structure, cathode electrodes and ITO arrays linked with gate electrodes were interdigitated and paralleled on the same plane although the gate electrodes and cathode electrodes were isolated by dielectric layer, a so-called improved planar-gate triode structure. An electrophoretic process was developed to selectively deposit CNTs field emitters onto cathode electrodes in the CNTs suspension by an applied voltage between the gate electrodes and cathode electrodes. The optical microscopy and FESEM image showed that the CNTs emitters with the uniform packing density were selectively defined onto the cathode electrodes. In addition, field emission characteristics of an improved planar-gate triode with CNTs field emitters were investigated. The experiment results indicated that the turn-on voltage of this triode structure at current density of 1 μA/cm² was approximately 55 V. The anode current and gate current came to 396 μA and 325 μA, at gate voltage and anode voltage of 100 V and 4000 V, respectively and at the anode-cathode spacing of 2000 μm. The emission image became brighter and the luminous image with dot matrix on the anode plate obviously increased with the increase of the gate voltage. Moreover, the emission current fluctuation was smaller than 5% for 11 h, which indicated that the improved planar-gate triode has a good field emission performance and long lifetime.     

Investigating carbon materials for use as the electron emission source in a parallel electron-beam lithography system

A microelectronic parallel electron-beam lithography system using an array of field emitting microguns is currently being developed. This paper investigates the suitability of various carbon based materials for the electron source in this device, namely tetrahedrally bonded amorphous carbon (ta-C), nanoclustered carbon and carbon nanotubes.Ta-C was most easily integrated into a gated field emitter structure and various methods, such as plasma and heavy ion irradiation, were used to induce emission sites in the ta-C. However, the creation of such emission sites at desired locations appeared to be difficult/random in nature and thus the material was unsuitable for this application. In contrast, nanoclustered carbon material readily field emits with a high site density but the by-products from the deposition process create integration issues when using the material in a microelectronic gated structure.Carbon nanotubes are currently the most promising candidate for use as the emission source. We have developed a high yield and clean (amorphous carbon by-product free) PECVD process to deposit single free standing nanotubes at desired locations with exceptional uniformity in terms of nanotube height and diameter. Field emission from an array of nanotubes was also obtained.     

Multiwalled carbon nanotubes mass-produced by dc arc discharge in He–H2 gas mixture

Uniform cathode deposits (longer than 15 mm), containing multiwalled carbon nanotubes (MWNTs) inside, were produced by dc arc discharge evaporation with a computer-controlled feeder of a pure-carbon electrode without a metal catalyst in a He–H₂ gas mixture. The purification of MWNTs was carried out to remove amorphous carbon and carbon nanoparticles. High-resolution transmission electron microscopy observations and Raman scattering studies show that the MWNTs possess a high crystallinity and a mean outermost diameter of ∼ ∼10 nm. It has been confirmed that the current density in the electron field emission from a purified MWNT mat can reach 77.92 mA/cm², indicating that the purified MWNTs are a promising candidate electron source in a super high-luminance light-source tube or a miniature X-ray source.     

Synthesis, characterization and low field emission of CNx nanotubes

Aligned CN_x nanotubes were fabricated by pyrolyzing ethylenediamine on p-type Si(1 1 1) substrates using iron as the catalyst. Scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectrum (XPS) and Raman spectroscopy were used to characterize the CN_x nanotubes. The CN_x nanotubes with the average length of 20 μm and diameters in the range of 50–100 nm have the “bamboo-like” structure and worse crystalline order. The low-field emission measurements of the CN_x nanotubes indicated that 20 μA/cm² current densities were observed at an electric field of 1.4 V/μm and 1.280 mA/cm² were obtained at 2.54 V/μm. The CN_x nanotubes exhibit better field emission properties than the carbon nanotubes and the BCN nanotubes. The emission mechanism of CN_x nanotubes is also discussed.     

Conducting polymer based hybrid structure as transparent and flexible field electron emitter

An efficient cathode material with high transparency (93%) based on conducting polymer poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) and single wall carbon nanotubes (SWCNTs) has been developed for the fabrication of highly transparent and flexible field electron emitters (FEE). This kind of material showed superior field emission (FE) performance with very high current density (10^–3A/cm²) at very low electric field. The FE performance of the hybrid materials was dramatically improved compared to either SWCNTs and PEDOT:PSS. Thus the hybrid structures of conducting polymer and SWCNTs might be a good choice for use as a cathode material to enhance the FE performance and for potential application in future portable displays. (© 2013 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Mechanism of field emission from carbon materials

Field emission in diamond and graphite-like polycrystalline films is investigated experimentally. It is shown that the emission efficiency increases as the nondiamond carbon phase increases; for graphite-like films the threshold electric field is less than 1.5 V/μm, and at 4 V/μm the emission current reaches 1 mA/cm², while the density of emission centers exceeds 10⁶ cm⁻². A general mechanism explaining the phenomenon of electron field emission from materials containing graphite-like carbon is proposed. Pis’ma Zh. éksp. Teor. Fiz. 68, No. 1, 56–60 (10 July 1998)     

High-performance electric double-layer capacitors using mass-produced multi-walled carbon nanotubes

Mass-produced multi-walled carbon nanotubes (MWNTs, which have the trademark VGNF®) have been investigated for their potential for use in electric double-layer capacitors (EDLCs). The variation aspects of these MWNTs by KOH activation showed quite interesting features. The gravimetric capacitance enhancement and specific surface area on KOH activation increased linearly. However, the capacitance per unit surface area has a maximum at 200 wt.?% of KOH addition. The VGNF-KOH 500 sample exhibits a capacitance enhancement as much as 13 times greater (28.3 F/g) than that of the as-grown materials (2.2 F/g), under the conditions of charging up to 3.5 V and discharging at a current density of 10 mA/cm². Interestingly, for this MWNT (VGNF®), selective attack on its amorphous carbon impurity has also been observed, as demonstrated from both scanning electron microscopy observations and Raman spectra. Consequently, the results of this study will provide insight into the potentiality of using MWNTs for EDLC electrodes, which would enable the cheapest production cost among the various types of carbon nanotubes.