Luminescence and EPR studies of Mn-activated SrAl12O19 phosphor prepared by facile combustion approach

Manganese-activated strontium hexa-aluminate (SrAl₁₂O₁₉) phosphor has been prepared at low temperature (500 °C) and in a very short time (<5 min) by urea combustion route. Powder X-ray diffraction pattern showed the presence of hexagonal SrAl₁₂O₁₉ phase. Scanning electron microscopy (SEM) indicated the presence of several particles with sizes of 200 nm. The luminescence of Mn²⁺ activated SrAl₁₂O₁₉ exhibits a strong green emission peak around 515 nm from the synthesized phosphor particles under excitation (451 nm). The luminescence is assigned to a transition from the upper ⁴T₁→⁶A₁ ground state of Mn²⁺ ions. EPR investigations also indicated the presence of Mn²⁺ ions in the prepared material. From the observed EPR spectrum, the spin-Hamiltonian parameters have been evaluated. The magnitude of the hyperfine splitting (A) constant indicates that there exists a moderately covalent bonding between Mn²⁺ ions and the surrounding ligands. The variation of zero-field splitting parameter (D) with temperature is measured and discussed. The mechanism involved in the generation of a green emission has been explained in detail.     

Enhanced blue emission and EPR study of LaMgAl11O19:Eu phosphors

Europium doped LaMgAl₁₁O₁₉ phosphor was prepared by the combustion method. The as-prepared and post-treated (1350 °C 10 h 5% H₂+95% N₂) phosphors were investigated by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), scanning electron microscopy (SEM), photoluminescence (PL) and electron paramagnetic resonance (EPR) techniques. XRD patterns show that LaMgAl₁₁O₁₉:Eu phosphors have hexagonal structure. FT-IR spectrum exhibits absorption bands corresponding to the stretching vibration of AlO₄ and AlO₆. Morphological studies reveal that this phosphor has faceted plates of varying sizes and shapes. The as-prepared LaMgAl₁₁O₁₉:Eu phosphor consists of both Eu³⁺ and Eu²⁺ ions. The phosphor exhibits a bright blue emission at 450 nm (4f⁶5d→4f⁷ transition of Eu²⁺). On post-treating the phosphor we are able to enhance the blue emission efficiency by 330%. The process was detected from the evolution of excitation, emission and EPR spectra and the results are discussed.     

EPR and luminescence properties of LiGa5O8:Mn green emitting phosphor

Green emitting LiGa₅O₈:Mn powder phosphor has been prepared in a short time by solution combustion method. Powder X-ray diffraction pattern indicated a dominant phase of LiGa₅O₈ with another secondary LiGaO₂ phase. Morphology aspects were studied by using field emission scanning electron microscopy. Upon UV light excitation (296 nm), the phosphor exhibits a strong green luminescence (510 nm), which corresponds to the ⁴T₁→⁶A₁ transition of Mn²⁺ ions in an environment close to tetrahedral symmetry. EPR spectrum exhibits resonance signals characteristic of Mn²⁺ ions. It is observed that the spin-Hamiltonian parameters g and A do not vary with temperature. The magnitude of the hyperfine splitting constant (A) in the present study indicates that there exists a moderately covalent bonding between Mn²⁺ ions and the surrounding ligands. The zero-field splitting parameter (D), spin concentration (N) and paramagnetic susceptibility (χ) have also been evaluated.     

Characterization, EPR and luminescence studies of ZnAl2O4:Mn phosphors

ZnAl₂O₄:Mn green light emitting powder phosphors have been prepared by urea combustion technique involving furnace temperatures about 500 °C in a short time (<5 min). The prepared powders were characterized by X-ray diffraction, scanning electron microscopy, Fourier-transform infrared spectrometry and the surface area measurements by a Brunauer-Emmet-Teller (BET) adsorption isotherms. The EPR spectrum exhibits a resonance signal at g≈2.0, which shows a six-line hyperfine structure (hfs). From the EPR spectra the spin-Hamiltonian parameters have been evaluated at room temperature as well as at 110 K. EPR and photoluminescence (PL) studies revealed that manganese ions were present in divalent state and the site symmetry around Mn²⁺ ions is distorted tetrahedral. The spin concentration (N), the paramagnetic susceptibility (χ) and the zero-field splitting parameter (D) have been evaluated and discussed. The green emission at 511 nm in ZnAl₂O₄:Mn phosphor is assigned to a transition from the upper ⁴T₁→⁶A₁ ground state of Mn²⁺ ions.     

Luminescence spectroscopy of Eu in Ca3Sc2Si3O12

Ca₃Sc₂Si₃O₁₂ doped with 1 mol% Eu³⁺ and having a cubic garnet structure was prepared by a solid state reaction. The low temperature luminescence spectrum shows no measurable ⁵D₀→⁷F₀ band, in agreement with the location of the lanthanide dopant in a site of D₂ symmetry, i.e. with a Ca²⁺ substitution. On the other hand, the spectrum is clearly dominated by the ⁵D₀→⁷F₄ band, which is significantly stronger than that for the other transitions originating from the ⁵D₀ level. This unusual behavior is explained on the basis of a model describing the distortion of the EuO₈ coordination polyhedron from a cubic geometry to the actual D₂ one.     

EPR and photoluminescence properties of green light emitting LaAl11O18:Mn phosphors

The LaAl₁₁O₁₈:Mn²⁺ powder phosphor has been prepared using a self-propagating synthesis. Formation and homogeneity of the LaAl₁₁O₁₈:Mn²⁺ phosphor has been verified by X-ray diffraction and energy dispersive X-ray analysis respectively. The EPR spectra of Mn²⁺ ions exhibit resonance signals with effective g values at g≈4.8 and g≈1.978. The signal at g≈1.978 exhibits six-line hyperfine structure and is due to Mn²⁺ ions in an environment close to tetrahedral symmetry, whereas the resonance at g≈4.8 is attributed to the rhombic surroundings of the Mn²⁺ ions. It is observed that the number of spins participating in resonance for g≈1.978 increases with decreasing temperature obeying the Boltzmann law. Upon 451 nm excitation, the photoluminescence spectrum exhibits a green emission peak at 514 nm due to ⁴T₁ (G)→⁶A₁ (S) transition of Mn²⁺ ions. The crystal field parameter Dq and Racah inter-electronic repulsion parameters B and C have been evaluated from the excitation spectrum.     

Luminescence studies on ZnO-P2O5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Zinc phosphate glasses doped with Gd₂O₃:Eu nanoparticles and Eu₂O₃ were prepared by conventional melt-quench method and characterized for their luminescence properties. Binary ZnO-P₂O₅ glass is characterized by an intrinsic defect centre emission around 324 nm. Strong energy transfer from these defect centres to Eu³⁺ ions has been observed when Eu₂O₃ is incorporated in ZnO-P₂O₅ glasses. Lack of energy transfer from these defect centres to Eu³⁺ in Gd₂O₃:Eu nanoparticles doped ZnO-P₂O₅ glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between the luminescent centre and Eu³⁺ ions. Both doped and undoped glasses have the same glass transition temperature, suggesting that the phosphate network is not significantly affected by the Gd₂O₃:Eu nanoparticles or Eu₂O₃ incorporation.     

Photoluminescence and EPR studies of BaMgAl10O17:Eu phosphor with blue-emission synthesized by the solution combustion method

A blue phosphor, BaMgAl₁₀O₁₇:Eu²⁺, has been synthesized in the furnace at a temperature of 500 °C by solution combustion method. The formation of the as-prepared BaMgAl₁₀O₁₇:Eu²⁺ phosphor was confirmed by the powder X-ray diffraction technique. The EPR spectrum exhibited an intense resonance signal centered at g=4.63 at 150 mT along with a number of resonances in the vicinity of g>2.0 and g<2.0. The number of spins participating in resonance (N) and the susceptibility (c) for the resonance signal at g=4.63 have been calculated as a function of temperature. The excitation spectrum of BaMgAl₁₀O₁₇:Eu²⁺ phosphor showed a strong peak near 336 nm (4f⁷ (⁸S)→5d¹(t_2g) transition) with a staircase like structure in the region 376-400 nm owing to crystal field splitting of the Eu²⁺ d-orbital. The 336 nm excitation produced a broad blue emission at 450 nm corresponding to 4f⁶5d→4f⁷ transition. PL studies reveal the two emission centers one at 450 nm and the other at 490 nm in this phosphor.     

Photoluminescence of Eu in SrGa2S4

A photoluminescence (PL) study of the green-emitting SrGa₂S₄:Eu²⁺ phosphor is reported. Diffuse reflectance, excitation, and emission spectra were examined with the aim to enlarge the fundamental knowledge about the emission of the Eu²⁺ ion in this lattice. The thermal dependence of the radiative properties was investigated. In particular, the Stokes shift, the crystal field splitting and the activation energy of the thermal quenching were determined. By combining these results with the information presented in literature, we discussed the location of the Eu²⁺ levels relative to the valence and conduction bands of SrGa₂S₄.     

Luminescence of BaAl2O4:Mn,Ce phosphor

Powder samples of barium aluminate doped with Mn²⁺ and Ce³⁺ were prepared by solid-state reaction method and their photoluminescence and thermoluminescence properties were studied. Substitution of Ca/Sr in place of Ba resulted in enhanced emission from Ce³⁺ ions without changing the spectral profile. Cerium efficiently sensitized the manganese luminescence in barium aluminate. Photoluminescence and thermo luminescence observations have indicated the presence of V_k³⁺ defects in undoped barium aluminate. However, Barium aluminate (either undoped or doped with manganese) did not exhibit long afterglow.     

Energy transfers between Sm and Eu in YPO4, LaP5O14 and LaP3O9 phosphates. Potential quantum cutters for red emitting phosphors

This work concerns the studies of energy transfers between Sm³⁺ and Eu³⁺ ions in some phosphates as new luminescent materials emitting in the orange-red color. The choose of ions is based on the possibility of quantum cutting process and the matrices are selected according to the 5d bands position of Sm³⁺ ion. The Sm³⁺ and Eu³⁺ doped YPO₄, LaP₅O₁₄ and LaP₃O₉ are synthesized and spectroscopic studies in ultraviolet and vacuum ultraviolet ranges have been achieved.     

Electronic energy relaxation and luminescence decay dynamics of Eu in Zn2SiO4:Eu phosphors

Electronic energy relaxation and decay dynamics of Eu³⁺ in Zn₂SiO₄:Eu³⁺ phosphors display evidence of intra-ion energy transfer from the ⁵D₁ to the ⁵D₀ manifold. The energy transfer timescale does not depend on Eu³⁺ concentration, or the addition of Mn²⁺ as a co-dopant and is estimated to be about 11 μs in Zn₂SiO₄. Evidence for intra-ion Eu³⁺ electronic energy transfer has also been observed in Eu-doped MgS as well as Eu³⁺ encapsulated in zeolite-Y. The energy transfer timescale in these other materials is shorter than in Zn₂SiO₄, most likely due to differences in Eu³⁺ surroundings or site symmetry.     

Combustion synthesized MgAl2O4:Cr phosphors—An EPR and optical study

Magnesium aluminate (MgAl₂O₄) doped with trivalent chromium (Cr³⁺) was synthesized by the combustion method. The prepared sample was characterized by X-ray powder diffraction, Brunauer-Emmet-Teller (BET) adsorption isotherms and diffuse-reflectance UV-vis spectroscopy techniques. Electron paramagnetic resonance (EPR) and photoluminescence (PL) studies have been performed at room temperature and at 110 K. The EPR spectrum exhibit resonance signals at g=5.37, 4.53, 3.82, 2.26 and 1.96 characteristic of Cr³⁺ ions. The luminescence of Cr³⁺-activated MgAl₂O₄ exhibits a red emission peak around 686 nm from the synthesized phosphor particles upon 551 nm excitation. The luminescence is assigned to a transition from the upper ²E_g→⁴A_2g ground state of Cr³⁺ ions. By correlating EPR and optical data the crystal field splitting parameter (D_q), Racah inter-electronic repulsion parameter (B) and the bonding parameters have been evaluated and discussed. The bonding parameters suggests that the ionic nature of Cr³⁺ ions with the ligands and the Cr³⁺ ions are in distorted octrahedral environment.     

Red, green and blue (RGB) emission doped Y3Al5O12 (YAG) phosphors prepared by non-hydrolytic sol-gel route

An evolutionary optimization process involving combination chemistry was employed in an attempt to develop Y₃Al₅O₁₂ (YAG). The combination chemistry process utilized here consisted the doping of the YAG host with appropriate amounts of red (R), green (G), and blue (B) dopants in a single layer, for use in tricolor white light. The doped YAG was acieved by means of the non-hydrolytic sol-gel route. Four samples were prepared, three of which were mono-doped samples containing 1.0% of a certain lanthanide (Eu³⁺, Tb³⁺, or Tm³⁺) ion, while the fourth contained the three ions. The samples were characterized by X-ray diffractometry and photoluminescence. The diffraction pattern of the mono-doped samples synthered at 800 °C for 16 h displayed peaks corresponding to the Y₃Al₅O₁₂ (YAG) phase, while the sample doped with the three ions revealed the presence of a mixture of Y₃Al₅O₁₂ (YAG) and Y₄Al₂O₉ (YAM) phases. The emission spectra of the three mono-doped YAG samples displayed the typical bands of the blue, green, and red emission of the corresponding lanthanide ions. As for the sample doped with the three lanthanide ions; it simultaneously emitted R, G and B lights. The green emission (546 nm) was more intense and narrow in relation to the red and blue emissions, which may be due to differences in the size of the three incorporated ions.     

Investigation on Eu doped Sr2MgSi2O7 red-emitting phosphors for white-light-emitting diodes

In this work, we report the high temperature solid-state synthesis of red phosphors Sr₂MgSi₂O₇: Eu³⁺ with various Eu³⁺ concentrations. Their luminescent properties at room temperature are investigated. The X-ray diffraction patterns indicate that the red phosphors powder conforms to the tetragonal Sr₂MgSi₂O₇. Impurity structure appears when more than 20% Eu³⁺ is doped. The samples show a strong emission line at 615 nm and the intensity increases with the increase of Eu³⁺ concentration until concentration quenching occurs. Charge compensation assists in the reduction of the impurity structure and vacancies; hence the luminescent intensity is enhanced. The decay measurement indicates that the lifetime of Eu³⁺ emission is about 2-3 ms. Some of the Eu³⁺ can be reduced to Eu²⁺; this is also discussed.     

Combustion synthesis of Sr3MgSi2O8:Eu and Sr2MgSi2O7:Eu phosphors

Sr₃MgSi₂O₈:Eu²⁺ and Sr₂MgSi₂O₇:Eu²⁺ phosphors find uses in applications such as plasma display panel (PDP), solid-state lighting, longafter glow. Preparation of these phosphors by a modified combustion synthesis is described in this paper. As-prepared samples did not show photoluminescence. After reducing the samples at 900 °C, characteristic Eu²⁺ emission was observed. Preparation of these phosphors by using similar methods helped clarifying various results obtained for Sr₃MgSi₂O₈:Eu²⁺ by different investigators.     

Thermoluminescence spectroscopy of Eu and Mn doped BaMgAl10O17

Thermoluminescence (TL) studies of Eu²⁺ and Mn²⁺ doped BaMgAl₁₀O₁₇ (BAM) are reported and discussed. The TL spectra that are measured after irradiation with ultraviolet (120-) show a series of TL peaks between 100 and . The TL spectra are similar for BAM with the two dopants, which suggest that the shallow traps are typical for the BAM host lattice. Using the Hoogstraaten analysis trap depths between 0.1 and are determined. A model is proposed based on thermally activated recombination in local TL centres (not via the conduction band). Further support for this model is obtained from the observation that the TL signal is strongest for excitation around the band edge of BAM . Upon heating the samples in air all low temperature TL peaks decrease in intensity. In addition a new peak appears in the TL spectrum, which is connected with a deeper trap and also a partial oxidation of Eu²⁺ to Eu³⁺ is observed. The luminescence efficiency is lower and the UV induced degradation is faster after annealing in air. These results indicate that the shallow traps are related to oxygen vacancies. The shallow traps do not have a negative influence on performance (efficiency and degradation) of BAM as a lighting phosphor. The luminescence efficiency and stability are strongly influenced by the formation of Eu³⁺ and a deeper trap during annealing in air. Subsequent annealing in a reducing atmosphere restores the original properties.     

PL and CL degradation and characteristics of SrAl2O4: Eu,Dy phosphors

Strontium aluminate phosphors are ideal for luminescent infrastructure materials. Their brightness and persistent glow time are much higher than previously used sulphide phosphors. Strontium aluminates prepared by the sol–gel and combustion methods are compared with commercially available strontium aluminate. High luminescent efficient SrAl₂O₄:Eu²⁺,Dy³⁺ pulsed laser deposited (PLD) thin films were also produced using the commercially available powder. Photoluminescence (PL) degradation studies showed that the phosphor intensity decreased about 20% over a period of 2 weeks under ultraviolet (UV) irradiation. Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) showed that cathodoluminescence (CL) degradation is due to the formation of SrO due to electron stimulated surface reactions. The light output mechanism of the phosphor is also discussed in more detail.     

Luminescence of BaBr2:Eu under hydrostatic pressure

Luminescence spectra of BaBr₂:Eu²⁺ have been measured under pressures up to 27 GPa at room temperature. In the low-pressure range a red-shift of the 5d-4f transition of −225 cm⁻¹/GPa is observed. From 3 to 10 GPa a phase mixture of the original orthorhombic phase and the high-pressure monoclinic phase gives rise to two luminescence bands. Above 10 GPa the crystal is completely transformed to its high-pressure phase where two different Eu²⁺ sites exist of which, however, only one 5d-4f transition is detected. This transition exhibits a red-shift of −200 cm⁻¹/GPa. The shifts are compared with other literature data.