Synthesis and characteristics of poly(methyl methacrylate‐co‐methacrylic acid)/poly(methacrylic acid‐co‐N‐isopropylacrylamide) thermosensitive semi‐hollow latex particles and their application to drug carriers

In this work, the poly(methyl methacrylate‐co‐methacrylic acid)/poly(methacrylic acid‐co‐N‐isopropylacrylamide) thermosensitive composite semi‐hollow latex particles was synthesized by three processes. The first process was to synthesize the poly(methyl methacrylate‐co‐methacrylic acid) (poly (MMA‐MAA)) copolymer latex particles by the method of soapless emulsion polymerization. The second process was to polymerize methacrylic acid (MAA), N‐isopropylacrylamide (NIPAAm), and crosslinking agent, N,N′‐methylenebisacrylamide, in the presence of poly(MMA‐MAA) latex particles to form the linear poly(methyl methacrylate‐co‐methacrylic acid)/crosslinking poly(methacrylic acid‐co‐N‐isopropylacrylamide) (poly(MMA‐MAA)/poly(MAA‐NIPAAm)) core–shell latex particles with solid structure. In the third process, part of the linear poly(MMA‐MAA) core of core–shell latex particles was dissolved by ammonia to form the poly(MMA‐MAA)/poly(MAA‐NIPAAm) thermosensitive semi‐hollow latex particles. The morphologies of the semi‐hollow latex particles show that there is a hollow zone between the linear poly(MMA‐MAA) core and the crosslinked poly(MAA‐NIPAAm) shell. The crosslinking agent and shell composition significantly influenced the lower critical solution temperature of poly(MMA‐MAA)/poly(MAA‐NIPAAm) semi‐hollow latex particles. Besides, the poly(MMA‐MAA)/poly(MAA‐NIPAAm) thermosensitive semi‐hollow latex particles were used as carriers to load with the model drug, caffeine. The processes of caffeine loaded into the semi‐hollow latex particles appeared four situations, which was different from that of solid latex particles. In addition, the phenomenon of caffeine released from the semi‐hollow latex particles was obviously different from that of solid latex particles. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 3441–3451     

Synthesis and characteristics of poly(methacrylic acid‐co‐N‐isopropylacrylamide) thermosensitive composite hollow latex particles and their application as drug carriers

In this work, the poly(methacrylic acid‐co‐N‐isopropylacrylamide) thermosensitive composite hollow latex particles was synthesized by a three‐step reaction. The first step was to synthesize the poly(methyl methacrylate‐co‐methacrylic acid) (poly(MMA‐MAA)) copolymer latex particles by the method of soapless emulsion polymerization. The second step was to polymerize methacrylic acid (MAA), N‐isopropylacrylamide (NIPAAm), and N,N′‐methylenebisacrylamide in the presence of poly(MMA‐MAA) latex particles to form the linear poly(methyl methacrylate‐co‐methacrylic acid)/crosslinking poly(methacrylic acid‐co‐N‐isopropylacrylamide) (poly(MMA‐MAA)/poly(MAA‐NIPAAm)) core–shell latex particles. In the third step, the core–shell latex particles were heated in the presence of ammonia solution to form the crosslinking poly(MAA‐NIPAAm) thermosensitive hollow latex particles. The morphologies of poly(MMA‐MAA)/poly(MAA‐NIPAAm) core–shell latex particles and poly(MAA‐NIPAAm) hollow latex particles were observed. The influences of crosslinking agent and shell composition on the lower critical solution temperature of poly(MMA‐MAA)/poly(MAA‐NIPAAm) core–shell latex particles and poly(MAA‐NIPAAm) hollow latex particles were, respectively, studied. Besides, the poly(MAA‐NIPAAm) thermosensitive hollow latex particles were used as carriers to load with the model drug, caffeine. The effect of various variables on the amount of caffeine loading and the efficiency of caffeine release was investigated. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 5203–5214     

In situ polymerization and morphology of polypyrrole obtained in water‐soluble polymer templates

Several water‐soluble polymers were used as templates for the in situ polymerization of pyrrole to determine their effect on the generation of nanosized polypyrrole (PPy) particles. The polymers used include: polyvinyl alcohol (PVA), polyethylene oxide (PEO), poly(vinyl butyral), polystyrene sulfonic acid, poly(ethylene‐alt‐maleic anhydride) (PEMA), poly(octadecene‐alt‐maleic anhydride), poly(N‐vinyl pyrrolidone), poly(vinyl butyral‐co‐vinyl alcohol‐co‐vinyl acetate), poly(N‐isopropyl acrylamide), poly(ethylene oxide‐block‐propylene oxide), hydroxypropyl methyl cellulose, and guar gum. The oxidative polymerization of pyrrole was carried out with FeCl₃ as an oxidant. The morphology of PPy particles obtained after drying the resulting aqueous dispersions was examined by optical microscopy, and selected samples were further analyzed via atomic force microscopy. Among the template polymers, PVA was the most efficient in generating stable dispersions of PPy nanospheres in water, followed by PEO and PEMA. The average size of PPy nanospheres was in the range of 160 nm and found to depend on the molecular weight and concentration of PVA. Model reactions and kinetics of the polymerization reaction of pyrrole in PVA were carried out by hydrogen ¹H NMR spectroscopy using ammonium persulfate as an oxidant. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis and Characterization of pH‐sensitive Poly(IA‐co‐AAc‐co‐AAm) Hydrogels via Frontal Polymerization

In this work, we report a series of poly(itaconic acid‐co‐acrylic acid‐co‐acrylamide) (poly(IA‐co‐AAc‐co‐AAm)) hydrogels via frontal polymerization (FP). FP starts on the top of the reaction mixture with aid of heating provided from soldering iron gun. Once polymerization initiated, no further energy is required to complete the process. The influences of IA/AAc weight ratios on frontal velocities, temperatures, and conversions on the reaction time are thoroughly investigated and discussed where the amount of AAm monomer remains constant. Fourier transform‐infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), scanning electron microscope (SEM), dynamic mechanical analysis, and the swelling measurement are applied to characterize the as‐synthesized poly(IA‐co‐AAc‐co‐AAm) hydrogels. Interestingly, the swelling ratios of the hydrogels are changed with different IA/AAc contents, and the maximum swelling ratios are ~4439% in water. SEM images describe highly porous morphologies and explain good swelling capabilities. Moreover, the poly(IA‐co‐AAc‐co‐AAm) hydrogels exhibit superior pH‐responsive ability. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 2214–2221     

Stimuli‐Responsive A‐b‐(B‐co‐C) Diblock Terpolymers Bearing Polyampholyte Sequences

Summary: Diblock terpolymers that consist of homopolymer and statistical copolymer (polyampholyte) building blocks are synthesized by group transfer polymerization. Two types of block tepolymers are explored in aqueous media: the amphiphilic poly{[(diethylamino)ethyl methacrylate]‐co‐(methacrylic acid)}‐block‐poly(methyl methacrylate) and the double hydrophilic poly[oligo(ethylene glycol) methacrylate]‐block‐poly{[(diethylamino)ethyl methacrylate]‐co‐(methacrylic acid)}. The first terpolymer self‐assembles in aqueous media to form responsive micelles that change their corona charge sign upon switching pH. The second terpolymer exhibits a multi‐responsive behavior. It forms neutral, positive, or negative micelles depending on a combination of different environmental conditions such as temperature, pH, and ionic strength.

P(DEAEMA‐co‐MAA)‐b‐PMMA pH‐sensitive micelles.     

Biobased poly(2,5‐furandimethylene succinate‐co‐butylene succinate) crosslinked by reversible Diels–Alder reaction

We synthesized biobased poly(2,5‐furandimethylene succinate‐co‐butylene succinate) [P(FS‐co‐BS)] copolymers by polycondensation of 2,5‐bis(hydroxymethyl)furan, 1,4‐butanediol, and succinic acid. These copolymers could be crosslinked to form network polymers by means of a reversible Diels–Alder reaction with bis‐maleimide. The thermal properties, mechanical properties, and healing abilities of the P(FS‐co‐BS)s and the network polymers were investigated. The mechanical properties of the network polymers depended on the comonomer composition of the P(FS‐co‐BS)s and the maleimide/furan ratio in the network polymers. Some of the copolymers exhibited healing ability at room temperature, and their healing efficiency was enhanced by solvent or heat. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 216–222     

One‐stage synthesis of narrowly dispersed polymeric core‐shell microspheres

A method of one‐stage soap‐free emulsion polymerization to synthesize narrowly dispersed core‐shell microspheres is proposed. Following this method, core‐shell microspheres of poly(styrene‐co‐4‐vinylpyridine), poly(styrene‐co‐methyl acrylic acid), and poly[styrene‐co‐2‐(acetoacetoxy)ethyl methacrylate‐co‐methyl acrylic acid] are synthesized by one‐stage soap‐free emulsion polymerization of a mixture of one or two hydrophobic monomers and a suitable hydrophilic monomer in water. The effect of the molar ratio of the hydrophobic monomer to the hydrophilic one on the size, the core thickness, and the shell thickness of the core‐shell microspheres is discussed. The molar ratio of the hydrophobic and hydrophilic monomers and the hydrophilicity of the resultant oligomers of the hydrophilic monomer are optimized to synthesize narrowly dispersed core‐shell microspheres. A possible mechanism of one‐stage soap‐free emulsion polymerization to synthesize core‐shell microspheres is suggested and coagglutination of the oligomers of the hydrophilic monomers on the hydrophobic core is considered to be the key to form core‐shell microspheres. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1192–1202, 2008     

Photovoltaic devices using semiconducting polymers containing head‐to‐tail‐structured bithiophene,pyrene, and benzothiadiazole derivatives

An alternating copolymer composed of heal‐to‐tail‐structured 3,4′‐dihexyl‐2,2′‐bithiophene (DHBT) and pyrene units [poly(DHBT‐alt‐PYR)] was synthesized using a Stille coupling reaction for use in photovoltaic devices as a p‐type donor. For the reduction of the bandgap energy of poly(DHBT‐alt‐PYR), 4,7‐bis(3′‐hexyl‐2,2′‐bithiophen‐5‐yl)benzo[c][1,2,5]thiadiazole (BHBTBT) units were introduced into the polymer. Poly(DHBT‐co‐PYR‐co‐BHBTBT)s were synthesized using the same polymerization reaction. The synthesized polymers were soluble in common organic solvents and formed smooth thin films after spin casting. The optical bandgap energies of the polymers were obtained from the onset absorption wavelengths. The measured optical bandgap energy of poly(DHBT‐alt‐PYR) was 2.47 eV. As the BHBTBT content in the ter‐polymers increased, the optical bandgap energies of the resulting polymers decreased. The bandgap energies of poly(50DHBT‐co‐40PYR‐co‐10BHBTBT) and poly(50DHBT‐co‐20PYR‐co‐30BHBTBT) were 1.84 and 1.73 eV, respectively. Photovoltaic devices were fabricated with a typical sandwich structure of ITO/PEDOT:PSS/active layer/LiF/Al using the polymers as electron donors and [6,6]‐phenyl C₇₁‐butyric acid methyl ester as the electron acceptor. The device using poly(50DHBT‐co‐20PYR‐co‐30BHBTBT) showed the best performance among the fabricated devices, with an open‐circuit voltage, short‐circuit current, fill factor, and maximum power conversion efficiency of 0.68 V, 5.54 mA/cm², 0.35, and 1.31%, respectively. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Volume phase transition of methacryloyl‐L‐alanine copolymer hydrogels controlled by the terminal groups in the side chains

The volume phase transition of nonionic hydrogels was controlled with a very small amount of variation (pinpoint variation) of the side chains far from the main chain. The copolymer hydrogels poly(methacryloyl‐alanine methyl ester‐co‐methacryloyl‐alanine ethyl ester) [poly(MA‐Ala‐OMe‐co‐MA‐Ala‐OEt)] and poly(methacryloyl‐alanine alkylamide‐co‐methacryloyl‐alanine ethyl ester) [poly(MA‐Ala‐NR₂‐co‐MA‐Ala‐OEt)] were studied to investigate how pinpoint variation controls the volume phase transition. All copolymer hydrogels showed a volume phase transition from a swollen phase to a collapsed phase at a definite MA‐Ala‐OEt content at a specific temperature. The MA‐Ala‐OEt content at the midpoint of the transition linearly decreased with elevation of the temperature, and the decrease was larger for poly(MA‐Ala‐OMe‐co‐MA‐Ala‐OEt) than for poly(MA‐Ala‐NR₂‐co‐MA‐Ala‐OEt). These results suggest that the association of the side chains controlling the swelling character of the hydrogels depends on the interacting ester–ester or ester–amide groups, and the former is larger than the latter. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 56–62, 2001     

Micelle formation and sol–gel transition behavior of comb‐like amphiphilic poly((PLGA‐b‐PEG)MA) copolymers

Comb‐like amphiphilic poly(poly((lactic acid‐co‐glycolic acid)‐block‐poly(ethylene glycol)) methacrylate (poly((PLGA‐b‐PEG)MA)) copolymers were synthesized by radical polymerization. (PLGA‐b‐PEG)MA macromonomer was prepared by ring‐opening bulk polymerization of DL ‐lactide and glycolide using purified poly(ethylene glycol) monomethacrylate (PEGMA) as an initiator. (PLGA‐b‐PEG)MA macromonomer was copolymerized with PEGMA and/or acrylic acid (AA) by radical polymerization to produce comb‐like amphiphilic block copolymers. The molecular weight and chemical structure were investigated by GPC and ¹H NMR. Poly((PLGA‐b‐PEG)MA) copolymer aqueous solutions showed gel–sol transition behavior with increasing temperature, and gel‐to‐sol transition temperature decreased as the compositions of the hydrophilic PEGMA and AA increased. The gel‐to‐sol transition temperature of the terpolymers of the poly((PLGA‐b‐PEG)MA‐co‐PEGMA‐co‐AA) also decreased when the pH was increased. The effective micelle diameter obtained from dynamic light scattering increased with increasing temperature and with increasing pH. The critical micelle concentration increased as the composition of the hydrophilic monomer component, PEGMA and AA, were increased. The spherical shape of the hyperbranched polymers in aqueous environment was observed by atomic force microscopy. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1954–1963, 2008     

Synthesis of poly[(2‐oxo‐1,3‐dioxolane‐4‐yl) methyl methacrylate‐co‐ethyl acrylate] by incorporation of carbon dioxide into epoxide polymer and the miscibility behavior of its blends with poly(methyl methacrylate) or poly(vinyl chloride)

This study was related to the investigation of the chemical fixation of carbon dioxide to a copolymer bearing epoxide and the application of the cyclic carbonate group containing copolymer‐to‐polymer blends. In the synthesis of poly[(2‐oxo‐1,3‐dioxolane‐4‐yl) methyl methacrylate‐co‐ethyl acrylate] [poly(DOMA‐co‐EA)] from poly(glycidyl methacrylate‐co‐ethyl acrylate) [poly(GMA‐co‐EA)] and CO₂, quaternary ammonium salts showed good catalytic activity. The films of poly(DOMA‐co‐EA) with poly(methyl methacrylate) (PMMA) or poly(vinyl chloride) (PVC) blends were cast from N,N′‐dimethylformamide solution. The miscibility of the blends of poly(DOMA‐co‐EA) with PMMA or PVC have been investigated both by DSC and visual inspection of the blends. The optical clarity test and DSC analysis showed that poly(DOMA‐co‐EA) containing blends were miscible over the whole composition range. The miscibility behaviors were discussed in terms of Fourier transform infrared spectra and interaction parameters based on the binary interaction model. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 1472–1480, 2001     

A novel poly(p‐phenylene) containing alternating poly(perfluorooctylethyl acrylate‐co‐methyl methacrylate) and polystyrene grafts by combination of atom transfer radical polymerization and Suzuki coupling processes

A poly(p‐phenylene) (PP), carrying perfectly alternating, well‐defined poly(perfluorooctylethyl acrylate‐co‐methyl methacrylate) [P(FEA‐co‐MMA)] and polystyrene (PS) side chain grafts, was synthesized by the combination of atom transfer radical polymerization (ATRP) and Suzuki cross‐coupling processes. First, dibromobenzene and diboronic ester functional macromonomers of P(FEA‐co‐MMA) and PS, respectively, were prepared by ATRP. In the second step, PP with lateral alternating P(FEA‐co‐MMA) and PS chains was synthesized by a Suzuki coupling reaction in the presence of Pd(PPh₃)₄ catalyst. The wetting behavior of the polymers was studied by measurements of the static contact angle θ of thin films (200?400 nm thickness) using water and n‐hexadecane as wetting liquids. The obtained fluorinated PP showed high static contact angles with both interrogating liquids, exhibiting simultaneously hydrophobic (θ_w = 111°) and lipophobic (θ_h = 67°) properties. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Preparation of co‐polymethyl(alkoxy)siloxanes by acid‐catalyzed controlled hydrolytic copolycondensation of methyl(trialkoxy)silane and tetraalkoxysilane

Polymethyl(alkoxy)siloxane copolymers, poly(MTES‐co‐TEOS), and poly(MTMS‐co‐TMOS), are prepared by acid‐catalyzed controlled hydrolytic co‐polycondensation of methyl(trialkoxy)silane MeSi(OR)₃ (R = Et (MTES) and Me (MTMS)) and tetra‐alkoxysilane Si(OR)₄ (R = Et (TEOS) and Me (TMOS)), respectively. The products are purified by fractional precipitation to provide polymethyl(alkoxy)siloxane copolymers with molecular weight 1000–10,000 (poly(MTES‐co‐TEOS)) or 1700–100,000 (poly(MTMS‐co‐TMOS)) that are stable to self‐condensation. These polymers are soluble in common organic solvents except for hexane, and form flexible and transparent free‐standing films with a tensile strength of 4.0–10.0 MPa. The structure of the polymethyl(alkoxy)siloxane copolymers is thought to be a random or a block co‐polymer. They are found to provide coating films with an adhesive strength up to 10, a refractive index of 1.36–1.40, and a dielectric constant of 3.5–3.6. The products also show better weathering stability than polyethoxysiloxane due to the hydrolytic polycondensation of TEOS. Field emission‐scanning electron micrography analysis reveals that coating films are composed of a micro‐phase separated structure. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4732–4741     

Structures and photoactive properties of poly(styrene‐co‐vinylbenzophenone)

Poly(styrene‐co‐vinylbenzophenone) prepared by a graft reaction on polystyrene revealed photoactive properties under irradiation of UVA. The photoactive structural features of the polymer were examined via electron paramagnetic resonance (EPR) under irradiation of UVA and fluorescent light. The photoactive functions of the polymer such as antimicrobial performance and dye decolorization ability were investigated. The results revealed that the poly(styrene‐co‐vinylbenzophenone) could generate radicals under fluorescent and UVA irradiation, and some radicals could stay alive for about 30 min in a dark chamber. The photoexcited polymer showed excellent antibacterial ability and decolorization effect on methylene blue and methyl orange dye under both daylight and UVA light. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2423–2430, 2008     

Synthesis and characterization of novel biodegradable block copolymer poly(ethylene glycol)‐block‐poly(L‐lactide‐co‐2‐methyl‐2‐carboxyl‐propylene carbonate)

An amphiphilic block copolymer, poly(ethylene glycol)‐block‐poly(L ‐lactide‐co‐2‐methyl‐2‐benzoxycarbonyl‐propylene carbonate) [PEG‐b‐P(LA‐co‐MBC)], was synthesized in bulk by the ring‐opening polymerization of L ‐lactide with 2‐methyl‐2‐benzoxycarbonyl‐propylene carbonate (MBC) in the presence of poly(ethylene glycol) as a macroinitiator with diethyl zinc as a catalyst. The subsequent catalytic hydrogenation of PEG‐b‐P(LA‐co‐MBC) with palladium hydroxide on activated charcoal (20%) as a catalyst was carried out to obtain the corresponding linear copolymer poly(ethyleneglycol)‐block‐poly(L ‐lactide‐co‐2‐methyl‐2‐carboxyl‐propylenecarbonate) [PEG‐b‐P(LA‐co‐MCC)] with pendant carboxyl groups. DSC analysis indicated that the glass‐transition temperature (T_g) of PEG‐b‐P(LA‐co‐MBC) decreased with increasing MBC content in the copolymer, and T_g of PEG‐b‐P(LA‐co‐MCC) was higher than that of the corresponding PEG‐b‐P(LA‐co‐MBC). The in vitro degradation rate of PEG‐b‐P(LA‐co‐MCC) in the presence of proteinase K was faster than that of PEG‐b‐P(LA‐co‐MBC), and the cytotoxicity of PEG‐b‐P(LA‐co‐MCC) to chondrocytes from human fetal arthrosis was lower than that of poly(L ‐lactide). © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4771–4780, 2005     

Poly(methacrylamide‐co‐2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid) hydrogels: Investigation of pH‐ and temperature‐dependent swelling characteristics and their characterization

Novel poly(methacrylamide‐co‐2‐acrylamido‐2‐methyl‐ 1‐propanesulfonic acid) (poly(MAAm‐co‐AMPS)) hydrogels were synthesized by free radical polymerization of methacrylamide (MAAm) and 2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid (AMPS) in deionized water at 60 °C by using ammonium peroxydisulfate (APS), N,N′‐methylenebisacrylamide (MBAAm) and N,N,N′,N′‐tetramethylethylenediamine (TEMED) as initiator, crosslinker, and activator, respectively. To investigate the effects of feed content on the pH‐ and temperature‐dependent swelling behavior of poly(MAAm‐co‐AMPS), molar ratio of MAAm to AMPS in feed was varied from 90/10 to 10/90. Structural characterization of gels was performed by Fourier transform infrared (FTIR) spectroscopy using attenuated total reflectance (ATR) technique. Thermal and morphological characterizations of gels were performed by thermogravimetric analysis (TGA) and scanning electron microscopy (SEM), respectively. Although an apparent pH‐sensitivity was not observed for the poly(MAAm‐co‐AMPS) gels during the swelling in different buffer solutions, their temperature‐sensitivity became more evident with the increase in AMPS content of copolymer. Thermal stability of poly(MAAm‐co‐AMPS) gels increased with MAAm content. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Spectroscopic studies of interactions in poly(N‐acryloyl‐N′‐methylpiperazine)/acidic polymer complexes

Poly(N‐acryloyl‐N′‐methylpiperazine) (PAMP) forms complexes with four strong acidic polymers, namely, poly(styrenesulfonic acid), poly(vinylphosphonic acid), poly(acrylic acid) and poly(methacrylic acid) in ethanol/water (1:1) solution. The nature of interpolymer interactions in various complexes was studied by Fourier transform infrared (FTIR) spectroscopy and X‐ray photoelectron spectroscopy (XPS). Both the carbonyl oxygen and the amide nitrogen of PAMP are involved in hydrogen‐bonding interactions. Some of the amine nitrogens of PAMP are protonated and therefore PAMP also interacts with the acidic polymers through ionic interactions. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 501–508, 2000     

Upper critical solution temperature type phase behavior of poly(styrene‐co‐acrylonitrile) blends with poly(styrene‐co‐n‐phenyl maleimide) and their interaction energies

To enhance the heat resistance of poly(styrene‐co‐acrylonitrile‐co‐butadiene), ABS, miscibility of poly(styrene‐co‐acrylonitrile), SAN, with poly(styrene‐co‐n‐phenyl maleimide), SNPMI, having a higher glass transition temperature than SAN was explored. SAN/SNPMI blends casted from solvent were immiscible regardless of copolymer compositions. However, SNPMI copolymer forms homogeneous mixtures with SAN copolymer within specific ranges of copolymer composition upon heating caused by upper critical solution temperature, UCST, type phase behavior. Since immiscibility of solvent casting samples can be driven by solvent effects even though SAN/SNPMI blends are miscible, UCST‐type phase behavior was confirmed by exploring phase reversibility. When copolymer composition of SNPMI was fixed, the phase homogenization temperature of SAN/SNPMI blends was increased as AN content in SAN copolymer increased. To understand the observed phase behavior of SAN/SNPMI blend, interaction energies of blends were calculated from the UCST‐type phase boundaries by using the lattice‐fluid theory combined with a binary interaction model. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 1131–1139, 2008     

Propylene sorption and coordinative interactions for poly(N‐vinyl pyrrolidone‐co‐vinyl acetate)/silver salt complex membranes

When poly(N‐vinyl pyrrolidone‐co‐vinyl acetate) (PVP‐co‐PVAc) containing amide and ester groups were complexed with silver salts to form silver polymer electrolyte membranes, their separation performance of propylene/propane mixtures showed the high selectivity of propylene over propane of 55 and the high mixed gas permeance of 12 GPU (1 GPU = 1.0 × 10^?6 cm³(STP) cm^?2 s^?1 cmHg^?1). The separation performance strongly depends on the composition of the copolymer: the higher concentration of PVP in the copolymer, the better separation performance was achieved. These results suggest that the amide group is more effective in facilitated propylene transport than the ester group, primarily due to the stronger interaction of the silver ions with the amide than the ester oxygens, as demonstrated by FT‐IR and FT‐Raman spectroscopies. In‐situ FT‐IR spectra upon propylene sorption also demonstrate that the interaction strength of the silver ions with the ligands is arranged: amide > C?C > ester. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2263–2269, 2007     

Layer‐by‐layer ionomer films made from poly(styrene‐co‐styrenesulfonic acid) and poly(methyl methacrylate‐co‐4‐vinylpyridine) in tetrahydrofuran

Thin films were fabricated layer‐by‐layer (LbL) via ionic bonds formed between a cationic ionomer and an anionic ionomer, which were produced via proton transfer from poly(styrene‐co‐styrenesulfonic acid) to poly(methyl methacrylate‐co‐4‐vinylpyridine) in an organic solvent, tetrahydrofuran. Ionic contents of the ionomers were very low down to 5.6 mol %, much lower than usual polyelectrolytes. The build up of the LbL films was demonstrated by UV/vis spectroscopy: the absorbance of the phenyl rings in styrene residues increased with the number of depositions (thus the number of layers). Transmission electron microscopy observation of strained thin films showed unique deformation mode, involving many bands that developed both in the parallel and perpendicular directions to the stress axis. This is quite different from the deformation modes seen for ionomer blend films and for coextruded polystyrene/poly(methyl methacrylate) multilayer tapes. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 50: 101–105, 2012