环型聚苯乙烯的凝胶渗透行为和环型聚合物中线型成份相对含量的计算

根据理论推导,通过凝胶渗透行为和粘度研究,探讨了大环产物中线型成分与有关参数之间的定量处理方法,导出并验证了环型大分子与线型大分子GPC差异的定量关系式为g_c=exp[-2.303b⊿V_c];(M_w)_GPC)与(M_w)_LS的关系为(M_w)_GPC/(M_w)_LS=g_c^1/(a+1),并提出了线型大分子相对含量为=(g_c^'-g_c)/[(1-g_c^1/(a+1))(ag_c^'+g_c^a/(a+1))]。     

溶胶-凝胶法合成聚甲基丙烯酸甲酯/二氧化钛杂化聚合物材料

由共聚合在PMMA聚合物链段上引入了－Si(OR)₃功能团,通过溶胶－凝胶过程合成了PMMA/TiO₂杂化聚合物材料.溶剂抽提结果表明有化学键存在的杂化材料体系中凝胶的含量很高.通过FTIR测试对材料结构进行了分析,由TGA、DSC测试分析了杂化材料体系中无机组份的含量对材料性能的影响.     

溶胶-凝胶法制备硅系有机-无机杂化分离膜

以α-Al₂O₃多孔陶瓷片为载体,用溶胶-凝胶法制备有机-无机杂化分离膜.通过考察前驱物的组成及杂化溶胶的合成条件对制膜工艺过程的影响,得到了制备有机-无机杂化分离膜的各种适宜性参数.红外光谱(FTIR)分析结果表明,杂化溶胶的性能不仅决定分离膜的性能,而且对膜热处理过程中的龟裂有很大影响.膜层的厚度为1～2μm;在膜两侧压差为0.10MPa、n(PTMOS)/n(TEOS)=1.16时,膜对O₂/N₂,CO₂/N₂和CO₂/O₂的分离因子分别为2.30,4.31和1.17,渗透系数为75.81×10^-17,75.28×10^-17和72.78×10^-17m₃(STP)·m/(m₂·s·Pa).     

溶胶凝胶法制备杯[6]芳烃乙酸/二氧化钛杂化材料

采用溶胶-凝胶法制备了不同TiO₂含量的杯[6]芳烃乙酸/TiO₂ (CA/TiO₂)杂化材料. 通过溶剂抽提实验和FT-IR测试表明杂化材料中有机无机两相间存在着化学键. 通过XRD, SEM, TGA对材料的结构和性能进行表征. 结果表明: 当TiO₂的含量w为60%时, 材料表面均匀光滑, 有机无机两相相容性和材料的热稳定性能最好, 但w(TiO₂)≤40%时, 难以获得两相均一的杂化材料.     

UV光引发表面接枝两性离子水凝胶层的制备及抗细菌黏附性能

采用聚合和交联的SiO₂有机/无机杂化溶胶作为基材, 通过与两性离子单体层之间的过渡层, 在紫外光作用下引发杂化溶胶和两性离子单体溶液中的双键反应, 使生成的杂化层在基材和表面的两性离子聚合物之间形成辅助性黏接作用, 从而在基材表面构筑两性离子水凝胶层. 通过傅里叶红外光谱(FTIR)、 原子力显微镜(AFM)和接触角测试等方法对所制备的两性离子水凝胶层和杂化层的表面进行了表征. 以空白玻璃片为对照样品, 以金黄色葡萄球菌和大肠杆菌为试验菌, 研究了用两性离子凝胶层修饰的玻璃表面的抗细菌黏附性能. 结果表明, 在SiO₂杂化过渡层中引入线型-Si-(CH₂)₂-O-链段可有效提高杂化过渡层对基材的附着力, 并改善其柔韧性. 与对照样品相比, 用两性离子凝胶层修饰的玻璃表面具有优异的抗菌黏附性能.     

溶胶-凝胶法构筑介孔二氧化硅纳微结构

基于硅酸脂水解/缩合的溶胶-凝胶法是目前制备SiO₂胶体最为常用的化学方法. 在溶胶-凝胶反应过程中, 引入介孔导向剂(通常是表面活性剂)可以得到具有介孔结构的SiO₂胶体. 通过对硅酸脂在多相体系界面水解/缩合过程的调控, 可以构筑具有不同纳微结构的介孔SiO₂材料, 为拓展介孔SiO₂材料的应用领域提供了新机遇, 同时也丰富了对溶胶-凝胶法的理解和认识. 本文综述了利用溶胶-凝胶法构筑介孔SiO₂纳微结构的最新研究进展, 并介绍了其在生物医药、 催化、 吸附分离等领域的应用前景, 最后对这一领域所面临的问题和未来发展方向进行了总结和展望.     

溶胶-凝胶法制备聚醚砜-二氧化硅复合材料

以聚醚砜(PES)为基体,通过溶胶-凝胶过程,得到了分散均匀的PES/SiO₂杂化材料,用扫描电镜、透射电镜、傅里叶红外及差示扫描量热法研究不同SiO₂含量的PES/SiO₂杂化材料材料性能.结果表明,当PES/SiO₂杂化材料中SiO₂的质量分数大于10%时可获得有机聚合物链段与无机网络互穿的均匀分散的复合材料.此材料的玻璃化转变温度(Tg)明显提高.     

P123重水溶液的物理凝胶化及凝胶结构

利用 1H NMR方法, 研究了高浓度的P123(PEO20PPO70PEO20)在重水溶液中的溶胶-凝胶转变过程. 升高温度使得体系发生溶胶-凝胶转变, 进一步升高温度, 体系发生凝胶-溶胶转变. 通过对不同质子基团的谱线宽度和化学位移偏移的分析, 同时结合流变学频率扫描和同步辐射(SR)研究, 发现质量分数为30%的P123的重水溶液在凝胶化过程中, 结构经历了由立方相(cubic)-六角柱状相(hcp)-层状相(lamellar)的转变过程, 其中立方相为面心立方(fcc)和六角密堆积球状相(hcps)的混合相. 高温时从凝胶到溶胶的转变主要体现为P123形成富集区与水发生相分离的过程.     

PEO-PPO-PEO水溶液体系胶束化及凝胶化行为的耗散粒子动力学模拟

采用耗散粒子动力学(Dissipative particle dynamics, DPD)模拟方法研究了三嵌段共聚物聚氧乙烯-聚氧丙烯-聚氧乙烯(PEO-PPO-PEO)的胶束化和凝胶化行为. 通过模拟得到了F127(EO₉₉PO₆₅EO₉₉)水溶液的临界胶束浓度和临界凝胶浓度. 结果发现, 在298 K、 质量分数低于40%时, F127水溶液中形成的胶束形状均为球形. 此外,进一步研究了亲水嵌段长度对胶束结构及凝胶形成浓度的影响, 结果发现, 亲水嵌段越短, 越有利于长椭球状胶束的形成, 而临界凝胶浓度随着亲水嵌段PEO长度的增加而降低.     

F68和F108水溶液溶胶-凝胶转变过程的流变学研究

采用流变学方法研究了具有高PEO质量分数(80%)的两亲性三嵌段共聚物Pluronic F68(PEO₈₀-PPO₃₀-PEO₈₀)和F108(PEO₁₃₃-PPO₅₀-PEO₁₃₃)的水溶液在升温过程中的溶胶-凝胶转变过程, 发现对于特定浓度的嵌段共聚物水溶液, 在溶胶-凝胶转变过程中会出现一个“软凝胶”区域, 通过对F68进行区域的频率扫描实验, 推测了相应的内部结构.     

固体酸催化醇酸树脂的分子量分布及其与性能关系的研究

本文用HPGPC法等研究了固体酸催化醇酸树脂合成中MWD及其与性能的关系。结果表明,固体酸催化醇酸树脂化过程的MWD等物性变化规律与未加催化剂的相似,logM_w和logd与p、M_w与分散度d及logη_G与M_w之间均呈线性关系。然而在达到同样M_w和MWD时,催化新工艺所需时间大大缩短,所需温度也有较大下降,而所得树脂粘度较低,贮存稳定性更好,其成膜干性更好,漆膜硬度也较高。     

Influence of molecular weight and polydispersity on phase behaviour of polyesters with laterally fixed or cross-shaped mesogens

To supplement previous studies of polyesters with laterally attached and cross-shaped mesogens the influence of molecular weight and molecular weight distribution on the phase behaviour has been investigated. For that purpose two polyesters have been fractionated by preparative gel permeation chromatography under high pressure and observed by polarizing microscopy and DSC measurements. A monotropic nematic polyester with laterally attached mesogens shows changing phase transitions up to a molecular weight of 10 000 (M_w); at higher molecular weight only the clearing transition is still slightly influenced. The molecular weight distribution at an average molecular weight of 15 000 (M_w) has no influence on the melting and clearing temperatures, but does effect recrystallization. The tendency to recrystallize decreases with increasing polydispersity, with increasing aberration from a monomodal molecular weight distribution. The recrystallization and the melting enthalpy are most distinguished at molecular weights around 12 000 (M_w) and crystallization disappears at molecular weights under about 5000 (M_w). In this way, fractions with stable nematic phases are obtained. Additionally, the broadness of the biphasic region shows a distinct dependence on molecular weight. Clearing temperatures show the most significant dependence on the molecular weight of an enantiotropic polyester with crossshaped mesogens dropping significantly below a molecular weight of about 20 000 (M_w). Oligomers with molecular weights below 10 000 (M_w) do not exhibit a mesophase. Polyesters with laterally attached mesogens as well as with crossshaped mesogens show no new liquid-crystalline phases by varying the molecular weight or the molecular weight distribution.     

Binding of Pyrene to Different Molecular Weight Fractions of Dissolved Organic Matter: Effects of Chemical Composition and Steric Conformation

The binding constant(K_DOM) of pyrene onto different molecular weight(M_w) fractions of a dissolved organic matter(DOM) extract from an estuarine sediment was measured via a fluorescence quenching method, and the possible binding mechanisms were discussed. The influence of water chemical parameters on pyrene binding was studied to elucidate the effects of DOM steric conformation. DOM fraction with larger M_w(>14000) showed a greater K_DOM(2.02×10⁵) than that with smaller M_w did, and the K_DOMs were 1.16×10⁵ and 1.13×10⁵ for the fractions with M_w of 1000-14000 and <1000, respectively. The K_DOMs of different M_w DOM fractions were correlated positively with the atomic ratio of C/H and absorbance at 280 nm; while a negative correlation existed between K_DOM and (O+C)/N (atomic ratio), and K_DOM and O-containing groups. These correlations indicate the positive influence of aromatic structure and the negative effect of polarity on DOM binding capacity. Infrared spectroscopy revealed that specific interactions existed between pyrene and the DOM fraction with larger M_W besides hydrophobic partition, i.e., NH-π interaction in DOM moiety(1000-14000) and π-π electron donor acceptor(EDA) forces in DOM moiety (>14000). K_DOM varied in a complex pattern with increasing cation concentration and pH, which could be explained by the change in DOM steric conformation. Formed aggregates favored the lipophilic partition of pyrene. However, the accessibility to some interior binding sites became low when the aggregate was too large, leading to a reduced K_DOM.     

香菇多糖的成分及其分子量研究

从香菇子实体中用0.9%NaCl水溶液、85%乙醇、热水、1%草酸铵、5%NaOH/0.05%NaBH₄和2%NaOH/2%尿素分别提取出四种杂多糖(L-FⅠ-L-FⅣn)和两种葡聚糖(L-FⅤ和L-FⅥn).红外光谱和高效液相色谱分析结果表明杂多糖主要由葡萄糖、葡萄糖醛酸、木糖、甘露糖、半乳糖和鼠李糖组成,而且按照分离过程的进行多糖中葡萄糖含量递增.由光散射和膜渗透压法研究了多糖的重均分子量Mw、均方根旋转半径2>^1/2、第二维利系数A₂及数均分子量M_n.L-FⅡ、L-FⅢ、L-FⅤ及L-FⅥn的M_w值依次为19.7×10⁴、192.3×10⁴、136.4×10⁴和136.7×10⁴,它们的多分散系数-Mw/-Mn在3～5范围.     

Studies on molecular weight distribution of carbon fiber polymer precursors synthesized using mixed solvents

The molecular weight distributions were estimated for carbon fiber polymer precursors such as poly（acrylonitrile-co -itaconic acid） synthesized by semi batch solution polymerization in mixed solvents media with the azonitrile compounds as initiator under the different ratios of solvent and non solvent from 0.75 to 2.5 in weight.The copolymer was characterized by using Fourier transform infrared spectroscopy（FTIR） and nuclear magnetic resonance（¹H-NMR） analyses.The molecular weight distributions were evaluated by M_v/M_n ratios estimated from viscosity and osmotic measurements,and M_w/M_n estimated from size exclusion chromatography.The molecular weight distributions of these polymers as determined from M_v/M_n and M_w/M_n are 2.9 to 3.2 and 2.0 to 2.5 respectively.The molecular distributions were close to a narrow distribution of 2.0 when the solvent/non-solvent ratio was varied between 1.4 and 2.0.Intrinsic viscosity[?]as a function of molecular weight of poly（acrylonitrile-co-itaconic acid） was evaluated by means of low angle laser light scattering with size exclusion chromatography（SEC-LALLS） and viscometry with SEC（SEC-VISCO）.The relationship between[?]and M_w for poly（acrylonitrile-co-itaconic acid） in DMF at 50℃was[?]= 1.1×10^-5M_w^0.79,where[?]is obtained in dL/g.     

聚硅芳撑硅氧烷的研究(Ⅱ)——聚四甲基对硅苯撑硅氧烷的合成

本文以具有硅苯撑结构的环状有机硅氧烷--十二甲基环三对硅笨撑硅氧烷为单体,用开环聚合方法合成了聚四甲基对硅苯撑硅氧烷.选用硅醇钾催化,环单体有较高的开环聚合活性.通过IR、¹H NMR和¹³C NMR等证明了聚合物的化学结构.聚合物在空气中的热失重温度较聚二甲基硅氧烷约高110℃,因此热稳定性更好.     

溴化铜对异丙醇铝存在下原子转移自由基聚合的影响

研究了以2-溴异丁酸乙酯为引发剂、溴化亚铜(CuX)/联二吡啶(bPy)/异丙醇铝[Al(OPrⁱ)₃]为三元复合催化体系,40℃下甲基丙烯酸甲酯(MMA)在环己酮中的原子转移自由基聚合,详细研究了溴化酮对聚合反应的影响.实验结果表明,以异丙醇铝为助催化剂,MMA可在较低温度下进行活性聚合;随着CuBr₂浓度的提高,自由基浓度降低,终止反应受到抑制;不加CuBr₂时,聚合物的分子量分布较宽(M_w/Mn);加入CuBr₂时,聚合物的分子量分布较窄(M_w/Mn=1.2～1.5),而且对数转化率与时间呈线性关系.     

以TiCl4为共引发剂的阳离子聚合体系的络合竞争

通过聚合物的GPC谱图分析以及紫外光谱测试证明了以TiCl₄为共引发剂的阳离子聚合体系中微量水与引发剂和TiCl₄之间存在着络合竞争,提出了抑制水对阳离子聚合影响的方法.     

丙烯酰胺-丙烯酸钠共聚物的键结构和光散射研究

用溶液聚合方法制备了一组单体含量相同、分子量不同的丙烯酰胺-丙烯酸钠(AM-AA)共聚物样品,用¹³CNMR和常规光散射方法进行了表征。该组样品的化学组成是均一的(AA摩尔含量16.9±1.1%),AA单体在大分子链中的序列分布为孤立、无规的,聚电解质在盐水体系中的光散射理论适用于共聚物在0.12mol/LNaCl水溶液体系。用恒化学位下的折光指数增量代替恒盐组成的折光指数增量,可从一次常规光散射实验分别求得共聚物样品的真实、第二维利系数A₂和均方旋转半径〈R²〉_z,其关系为:A₂=0.0619M_w^-0.21,〈R²〉_z^1/2=0.0210M_w^0.54.