Soft magnetic properties of FeCo films with Co underlayer

Bilayered Fe₆₅Co₃₅ (=FeCo)/Co films were prepared by facing targets sputtering with 4πM_s∼24 kg. The soft magnetic properties of FeCo films were induced by a Co underlayer. H_c decreased rapidly when the Co underlayer was 2 nm or more. The films showed well-defined in-plane uniaxial anisotropy with the typical values of H_ce=10 Oe and H_ch=3 Oe, respectively. High frequency characteristics of the films show the films can work at 0.8 GHz with real permeability as high as 250.     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

In-plane magnetization with high coercivity in terbium iron garnet thin films deposited on Pt/Si substrate by PLD

We report on the growth of terbium iron garnet (TbIG, Tb₃Fe₅O₁₂) thin films having anomalously large coercivity and in-plane easy axis of magnetization. The TbIG thin films were prepared at room temperature (RT) on Pt/Si(1 0 0) substrates by pulsed laser deposition technique. The films deposited at RT were X-ray amorphous and do not show any magnetic order. Annealing of the RT deposited film at 900 °C resulted into fully textured (532) TbIG film. Atomic force microscopy and cross-sectional scanning electron microscopy studies of the TbIG films showed good surface quality with an average surface roughness of 5.0 nm and thickness of about 300 nm, respectively. The M-H loops measured at 20 K for TbIG films, exhibit about an order of magnitude enhancement in the coercivity value (H_c) than the single crystal. In-plane and out-of-plane M-H loops revealed that the easy axis of the magnetization lies within the film’s plane. In-plane magnetization combining with large H_c value of the TbIG thin film may be of scientific interest for the possible applications.     

The influence of substrate temperature and annealing on the properties of pulsed laser-deposited YIG films on fused quartz substrate

Yttrium iron garnet (YIG) thin films were deposited on fused quartz substrate at different substrate temperatures (T_s) varying from room temperature (RT) to 850 °C using pulsed laser deposition (PLD) technique. All the films in the as-deposited state were X-ray amorphous and non-magnetic at RT. The film deposited at RT after annealing at temperatures T_a?700 °C showed both X-ray peaks and the magnetic order. The films deposited at higher T_s (500–850 °C) and then annealed at 700 °C resulted in better-quality films with higher 4πM_s value. The highest value of magnetization was for the sample deposited at 850 °C and annealed at 700 °C, which is 68% of the bulk 4πM_s value.     

The tuning of quantum magnetization for organic/inorganic hybrid materials composed of Mn12-acetate and azobenzene casted into PMMA films on PVA films

In order to examine the effects of polymer matrix substituting crystalline solvents and photoisomerization of azobenzene in photo-modulation of AC susceptibility discovered recently, we have compared various quantum magnetic properties of new organic/inorganic hybrid materials composed of Mn₁₂-acetate (a typical single-molecule magnet, [Mn₁₂(CH₃COO)₁₆(H₂O)₄O₁₂]·2CH₃COOH·4H₂O) containing or not containing azobenzene casted into polymethylmethacrylate (PMMA) films on Polyvinylalchol (PVA) films. The M-H hysteresis loops below blocking temperature for both materials exhibited distinct differences of the dM/dH vs. H plots, which suggested azobenzene as well as crystalline solvents resulted in tuning of magnetic properties. Moreover, the AC susceptibility at 0.1-1000 Hz frequencies provided activation energy U_eff=87 K from Arrhenius law for both materials, albeit Cole-Cole plots indicated perturbation of quantum magnetization for both hybrid materials in polymer matrix.     

Synthesis of α-Fe2O3 nanobelts and nanoflakes by thermal oxidation and study to their magnetic properties

α-Fe₂O₃ nanobelts and nanoflakes have been successfully synthesized by oxidation of iron-coated ITO glass in air. The X-ray diffraction, Raman spectrum and scanning electron microscopy are carried out to characterize the nanobelts and nanoflakes. The formation mechanism has been presented. Significantly, the magnetic investigations show that the magnetic properties are strongly shape-dependent. The magnetization measurements of belt-like and flake-like α-Fe₂O₃ in perpendicular exhibit ferromagnetic feature with the coercivity (H_c) and saturation magnetization (M_s) of 334.5 Oe and 1.35 emu/g, 239.5 Oe and 0.12 emu/g, respectively. For the parallel, belt-like and flake-like α-Fe₂O₃ also exhibit ferromagnetic feature with the H_c and M_s of 205.5 Oe and 1.44 emu/g, 159.6 Oe and 0.15 emu/g, respectively.     

The electrodeposition behaviors and magnetic properties of Ni-Co films

Ni-Co films with different compositions and microstructures were produced on ITO glasses by electrodeposition from sulphate bath at 25 °C. Cyclic voltammograms give a result that the increase in the Co²⁺ concentration displaces Ni-Co alloy oxidation peaks to negative potential with high Co current distributions. It is observed that the content of cobalt in the films increases from 22.42% to 56.09% as the molar ratio of CoSO₄/NiSO₄ varying from 0.015/0.085 to 0.045/0.055 in electrolyte. XRD patterns reveal that the structure of the films strongly depends on the Co content in the deposited films. The saturation magnetization (M_s) moves up from 144.84 kA m⁻¹ to 342.35 kA m⁻¹ and coercivity (H_c) falls from 15.27 kA m⁻¹ to 7.27 kA m⁻¹ with the heat treatment temperature increasing from 25 °C to 450 °C. The saturation magnetization (M_s) and coercivity (H_c) move up from 340.97 kA m⁻¹ and 7.98 kA m⁻¹ to 971.58 kA m⁻¹ and 18.62 kA m⁻¹ with the Co content increasing from 22.42% to 56.09% after annealing at 450.     

Effect of a high magnetic field on the morphology and magnetic properties of the MnBi compound during the Mn1.08Bi-MnBi phase transformation process

Effect of a 10 T high magnetic field on the morphology and magnetic properties of the MnBi compounds during the Mn_1.08Bi-MnBi phase transformation has been investigated. Results indicate that the field has split the MnBi crystal along the (0 0 1)-crystal plane during the Mn_1.08Bi-MnBi phase transformation process and the split MnBi crystals align and aggregate along the magnetic field direction. Along with the change of the MnBi phase morphology, the magnetic property changes greatly. Indeed, with the alignment and aggregation of the spit MnBi phases, the saturation magnetization M_s and the magnetic susceptibility χ increase, and the coercive field H_c and the remnant magnetization M_r decrease. This implies that a high magnetic field may have caused the magnetic property of the MnBi phase to transform towards soft magnetism. Above results may be attributed to the enhancement of the magnetization and the Mn_1.08Bi-MnBi phase transformation in a high magnetic field.     

Magnetic properties of strontium hexaferrite films prepared by pulsed laser deposition

The magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films fabricated by pulsed laser deposition on the Si(100) substrate with Pt(111) underlayer have been studied as a function of film thickness (50–700 nm). X-ray diffraction patterns confirm that the films have c-axis perpendicular orientation. The coercivities in perpendicular direction are higher than those for in-plane direction which indicates the films have perpendicular magnetic anisotropy. The coercivity was found to decrease with increasing of thickness, due to the increasing of the grain size and relaxation in lattice strain. The 200 nm thick film exhibits hexagonal shape grains of 150 nm and optimum magnetic properties of M_s=298 emu/cm³ and H_c=2540 Oe.     

Heat treatment effects on microstructure and magnetic properties of Mn-Zn ferrite powders

Mn-Zn ferrite powders (Mn_0.5Zn_0.5Fe₂O₄) were prepared by the nitrate-citrate auto-combustion method and subsequently annealed in air or argon. The effects of heat treatment temperature on crystalline phases formation, microstructure and magnetic properties of Mn-Zn ferrite were investigated by X-ray diffraction, thermogravimetric and differential thermal analysis, scanning electron microscopy and vibrating sample magnetometer. Ferrites decomposed to Fe₂O₃ and Mn₂O₃ after annealing above 550 °C in air, and had poor magnetic properties. However, Fe₂O₃ and Mn₂O₃ were dissolved after ferrites annealing above 1100 °C. Moreover, the 1200 °C annealed sample showed pure ferrite phase, larger saturation magnetization (M_s=48.15 emu g⁻¹) and lower coercivity (H_c=51 Oe) compared with the auto-combusted ferrite powder (M_s=44.32 emu g⁻¹, H_c=70 Oe). The 600 °C air annealed sample had the largest saturation magnetization (M_s=56.37 emu g⁻¹) and the lowest coercivity (H_c=32 Oe) due to the presence of pure ferrite spinel phase, its microstructure and crystalline size.     

Synthesis of goethite from Fe(OH)2 precipitates: Influence of Fe(II) concentration and stirring speed

Magnetic methods are efficient tools in soil and environmental science. But in such natural environments, several magnetic minerals are generally present. So, synthetic standard samples are necessary for calibration of laboratory techniques. The aim of this study was to synthesise goethite free of magnetic impurities (concentration <∼1 μg kg⁻¹) with different crystal sizes. Goethite was prepared by oxidation of aqueous suspensions of Fe(OH)₂ precipitates. Final products were characterised by X-ray diffraction, infrared spectroscopy, scanning and transmission electron microscopy and magnetic methods. Goethite could be obtained in the absence of any trace of strong magnetic minerals using FeSO₄·7H₂O and NaOH as reactants with the following experimental conditions: temperature=45 °C, [FeSO₄·7H₂O]=0.50 mol L⁻¹, [NaOH]=0.20 mol L⁻¹, stirring speed=760 rpm. The Fe(II) concentration and the stirring speed were varied. It proved possible to modify the size of the goethite crystals by varying the Fe(II) concentration and the stirring speed, but important changes of these parameters induced the formation of other phases, lepidocrocite when the oxidation reaction was drastically accelerated and Fe₃O₄ when the reaction was slowed down. In any case, for weak magnetic fields, a low-coercivity magnetic mineral saturating at weak magnetic fields was observed. It may correspond to traces of δ-FeOOH or to domains structurally similar to δ-FeOOH inside the multidomainic crystals of δ-FeOOH.     

Effect of Co underlayer on soft magnetic properties and microstructure of FeCo thin films

High saturation magnetization soft magnetic FeCo (=Fe₆₅Co₃₅) films were prepared using a thin Co underlayer. The FeCo/Co films exhibited a well-defined in-plane uniaxial anisotropy with easy axis coercivity (H_ce) of 10 Oe and hard axis coercivity (H_ch) of 3 Oe, and a half reduction of H_c with H_ce=4.8 Oe and H_ch=1.0 Oe was obtained when the composition was adjusted to 25 at% Co. The effective permeability of the films remains flat around 250 to 800 MHz. The saturation magnetostriction was 5.2×10⁻⁵ and the intrinsic stress was 0.8 GPa in FeCo single layer, both were slightly reduced by Co underlayer. The Co underlayer changed the preferred orientation of the FeCo films from (2 0 0) to (1 1 0) but more significantly, reduced the average grain size from ∼74 to ∼8.2 nm. It also reduced the surface roughness from 2.351 to 0.751 nm. The initial stage and interface diffusion properties were examined by TEM and XPS.     

Synthesis and surface modified hard magnetic properties in Co0.5Pt0.5 nanocrystallites from a rheological liquid precursor

Small crystallites of a metastable phase Co_0.5Pt_0.5 are precipitated by heating a rheological liquid precursor of cobalt–hydrazine complex and platinum chloride H₂PtCl₆·xH₂O in polymer molecules of poly(vinylpyrrolidone) (PVP) in ethylene glycol. The hydrazine co-reduces nascent atoms from the Co²⁺ and Pt⁴⁺ that recombine and grow as Co_0.5Pt_0.5. The PVP molecules cap a growing Co_0.5Pt_0.5 as it achieves a critical size so that it stops growing further in given conditions. X-ray diffraction pattern of a recovered powder reveals a crystalline Co_0.5Pt_0.5 phase (average crystallite size D∼8 nm) of a well-known Fm3m-fcc crystal structure with the lattice parameter a=0.3916 nm (density ρ=14.09 g/cm³). A more ordered L1₀ phase (ρ=15.91 g/cm³) transforms (D≥25 nm) upon annealing the powder at temperature lesser than 700 °C (in vacuum). At room temperature, the virgin crystallites bear only a small saturation magnetization M_s=5.54 emu/g (D=8 nm) of a soft magnet and it hardly grows on bigger sizes (D≤31 nm) in a canted ferromagnetic structure. A rectangular hysteresis loop is markedly expanded on an optimally annealed L1₀ phase at 800 °C for 60 min, showing a surface modified coercivity H_c=7.781 kOe with remnant ratio M_r/M_s=0.5564, and M_s=39.75 emu/g. Crystallites self-assembled in an acicular shape tailor large H_c from ideal single domains and high magnetocrystalline anisotropy of a hard magnet L1₀ phase.     

The effect of different chemical compositions caused by the variation of deposition potential on properties of Ni-Co films

The magnetic and microstructural properties of Ni-Co films electrodeposited at different cathode potentials were investigated. The compositional analysis revealed that the Ni content increases from 13 at.% to 44 at.% in the films with increasing deposition potential. Magnetic measurements showed that the saturation magnetization, M_s of the films decreased with increase of Ni content as the deposition potential increased. M_s values changed between 1160 emu/cm³ and 841 emu/cm³. The X-ray diffraction revealed that the crystalline structure of the films is a mixture of the predominant face-centered cubic (fcc) and hexagonal closed packed. However, the mixture phase turns to the fcc because of increasing Ni content up to 44 at.% at the highest (−1.9 V) potential by enhancing the intensity of reflections from the fcc phase. The changes observed in the magnetic and microstructural properties were ascribed to the changes observed in the chemical composition caused by the applied different deposition potentials.     

Microstructural,dielectric and magnetic behavior of spin-deposited nanocrystalline nickel–zinc ferrite thin films for microwave applications

Nanocrystalline nickel ferrite and zinc doped nickel ferrite thin films with general composition Ni_1−xZn_xFe₂O₄; x=0.0, 0.2 and 0.5 were fabricated by the spin-deposition technique. Citrate precursor method was adopted to prepare coating solution used for film deposition. This method resulted in single phase, transparent, homogeneous and crack-free nanocrystalline ferrite thin films at annealing temperature as low as 400 °C. The substrates used for film deposition were ITO-coated 7059 glass, fused quartz and Si (1 0 0). The thickness of films was found to be in the range ∼1000–5500 Å. The surface microstructure and morphology investigated by atomic force microscopy (AFM) confirmed the grain size of nickel–zinc ferrite films to be in nanometer range indicating nanocrystalline nature of the films. Dielectric properties such as the real (∈′) and imaginary parts (∈″) of complex permittivity were measured in the X-band microwave frequency region (8–12 GHz) by employing extended cavity perturbation technique. The M–H hysteresis measurements on the films annealed at 650 °C revealed narrow hysteresis curves with H_c and M_s varying for different compositions.     

Synthesis of Fe3O4 nanoparticles without inert gas protection used as precursors of magnetic fluids

Fe₃O₄ nanoparticles were hydrothermally synthesized under continuous microwave irradiation from FeCl₃·6H₂O and FeSO₄·7H₂O aqueous solutions, using NH₄OH as precipitating reagent and N₂H₄·H₂O as oxidation-resistant reagent. The results of X-ray powder diffraction (XRD), FT–IR spectroscopy and scanning electron microscopy (SEM) measurements showed that the synthesized magnetite (Fe₃O₄) nanoparticles had an average diameter of 10 nm. The magnetic properties of the Fe₃O₄ nanoparticles were measured using a vibrating sample magnetometer (VSM), indicating that the nanoparticles possessed high saturation magnetization at room temperature. The Fe₃O₄ nanoparticles were used to prepare magnetic fluids (MFs) based on water, and the properties of the MFs were characterized by a Gouy magnetic balance, a capillary rheometer and a rotating rheometer, respectively.     

Effect of magnetic field on the TC and magnetic properties for the aligned MnBi compound

In the compound MnBi, a first-order transition from the paramagnetic to the ferromagnetic state can be triggered by an applied magnetic field and the Curie temperature increases nearly linearly with an increase in magnetic field by ∼2 K/T. Under a field of 10 T, T_C increases by 20 and 22 K during heating and cooling, respectively. Under certain conditions a reversible magnetic field or temperature induced transition between the paramagnetic and ferromagnetic states can occur. A magnetic and crystallographic H-T phase diagram for MnBi is given. Magnetic properties of MnBi compound aligned in a Bi matrix have been investigated. In the low temperature phase MnBi, a spin-reorientation takes place during which the magnetic moments rotate from being parallel to the c-axis towards the basal plane at ∼90 K. A measuring Dc magnetic field applied parallel to the c-axis of MnBi suppresses partly the spin-reorientation transition. Interestingly, the fabricated magnetic field increases the temperature of spin-reorientation transition T_s and the change in magnetization for MnBi. For the sample solidified under 0.5 T, the change in magnetization is ∼70% and T_s is ∼91 K.     

Effect of Co layer thickness on the magnetic properties of Tb30Co70/SiNx/Co thin films

The SiN_x (20 nm)/Tb₃₀Co₇₀ (90 nm)/SiN_x (5 nm)/Co (3–37 nm)/SiN_x (10 nm)/Si multilayer films are deposited on naturally oxidized Si wafer by magnetron sputtering. The saturation magnetization (M_s) of the multilayer films is increased with the thickness of high M_s ferromagnetic Co layer. The perpendicular coercivity (_Hc⊥$H_{{\mathrm{c}}^{\perp }}$) value is increased with Co layer thickness as the thickness of the Co layer is lower than 15 nm and then decreases drastically when the thickness of the Co layer further increased. The increase of the _Hc⊥$H_{{\mathrm{c}}^{\perp }}$ value is owing to the interlayer exchange effect [Li Zhang, Physica B 390 (2007) 373] between TbCo and Co layers. Co under-layer with in-plane magnetic anisotropy would pin the magnetic moment of the TbCo layer near by the Co layer and cause the value of _Hc⊥$H_{{\mathrm{c}}^{\perp }}$ to increase. However, as the Co layer is thicker than a critical thickness, the _Hc⊥$H_{{\mathrm{c}}^{\perp }}$ value of the multilayer film would decrease. Therefore, the Co layer with in-plane magnetic anisotropy and soft magnetic properties is expected to dominate the magnetic properties of the multilayer films.     

Synthesis, structural and magnetic properties of the nanocomposite Fe63B23Nd7Y3Nb3Cr1 magnets

The Fe₆₃B₂₃Nd₇Y₃Nb₃Cr₁ nanocomposite magnets in the form of sheets have been prepared by copper mold casting technique. The phase evolution, crystal structure, microstructural and magnetic properties have been investigated in the as-cast and annealed states. The as-cast sheets show magnetically soft behaviors which become magnetically hard by thermal annealing. The optimal annealed microstructure was composed of nanosize soft magnetic α-Fe (19-29 nm) and hard magnetic Nd₂Fe₁₄B (45-55 nm) grains. The best hard magnetic properties such as intrinsic coercivity, _jH_c of 1119 kA/m, remanence, B_r of 0.44 T, magnetic induction to saturation magnetization ratio, M_r/M_s=0.61 and maximum energy product, (BH)_max of 55 kJ/m³ was obtained after annealing at 680 °C for 15 min. The annealing treatment above 680 °C results in non-ideal phase grains growth, which degrade the magnetic properties.     

Synthesis, magnetic and dielectric properties of Er-Ni doped Sr-hexaferrite nanomaterials for applications in High density recording media and microwave devices

A sol-gel combustion method has been successfully employed for the synthesis of Sr-hexaferrite nanomaterials doped with Er³⁺ and Ni²⁺ at strontium and iron sites, respectively. The X-ray diffraction analysis confirmed the single magnetoplumbite phase and the crystallite size was found to be in the range of 14-16 nm, suitable for obtaining signal-to-noise ratio in the high density recording media. The magnetic properties such as saturation magnetization (M_s), remanence (M_r) and coercivity (H_c) were calculated from hysteresis loops. M_s, M_r and H_c are observed to increase with the Er-Ni content. The dielectric constant (ε´) and dielectric loss (tan δ) is found to decrease with the increase in frequency and is explained on the basis of Maxwell-Wagner and Koops theory. The decrease in dielectric constant and dielectric loss but increase in saturation magnetization and remanence with Er-Ni content suggests that the materials are suitable for applications in microwave devices and high density recording media .